ASTM A299/A299M-09
(Specification)Standard Specification for Pressure Vessel Plates, Carbon Steel, Manganese-Silicon
Standard Specification for Pressure Vessel Plates, Carbon Steel, Manganese-Silicon
ABSTRACT
This specification covers manganese-silicon carbon steel plates for use in welded boilers and other pressure vessels. Plates under this specification are produced in two grades. The steel shall be killed and shall conform to the fine austenitic grain size requirement. Tension test shall be made to conform to the requirements specified.
SCOPE
1.1 This specification covers manganese-silicon carbon steel plates for use in welded boilers and other pressure vessels.
1.2 Plates under this specification are produced in two grades. The specified minimum yield strength decreases for thicknesses over 1 in. [25 mm].
1.3 The maximum thickness of plates is limited only by the capacity of the composition to meet the specified mechanical property requirements; however, current practice normally limits the maximum thickness of plates furnished under this specification to 8 in. [200 mm].
1.4 For plates produced from coil and furnished without heat treatment or with stress relieving only, the additional requirements, including additional testing requirements and the reporting of additional test results, of Specification A20/A20M apply.
1.5 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with the specification.
General Information
Relations
Buy Standard
Standards Content (Sample)
NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation: A299/A299M −09
StandardSpecification for
1
Pressure Vessel Plates, Carbon Steel, Manganese-Silicon
This standard is issued under the fixed designationA299/A299M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope* amination of Steel Plates
2
A578/A578M Specification for Straight-Beam Ultrasonic
1.1 This specification covers manganese-silicon carbon
Examination of Rolled Steel Plates for Special Applica-
steelplatesforuseinweldedboilersandotherpressurevessels.
tions
1.2 Plates under this specification are produced in two
grades. The specified minimum yield strength decreases for
3. General Requirements and Ordering Information
thicknesses over 1 in. [25 mm].
3.1 Plates supplied to this product specification shall con-
1.3 The maximum thickness of plates is limited only by the
form to Specification A20/A20M, which outlines the testing
capacity of the composition to meet the specified mechanical
and retesting methods and procedures, permitted variations in
property requirements; however, current practice normally
dimensions and mass, quality and repair of defects, marking,
limits the maximum thickness of plates furnished under this
loading, and ordering information.
specification to 8 in. [200 mm].
3.2 In addition to the basic requirements of this
1.4 For plates produced from coil and furnished without
specification, certain supplementary requirements are available
heat treatment or with stress relieving only, the additional
where additional control, testing, or examination is required to
requirements,includingadditionaltestingrequirementsandthe
meet end use requirements. The purchaser is referred to the
reporting of additional test results, of Specification A20/A20M
listed supplementary requirements in this specification and to
apply.
the detailed requirements in Specification A20/A20M.
1.5 The values stated in either inch-pound units or SI units
3.3 Coils are excluded from qualification to this specifica-
are to be regarded separately as standard. Within the text, the
tion until they are processed into finished plates. Plates
SI units are shown in brackets. The values stated in each
produced from coil means plates that have been cut to
system are not exact equivalents; therefore, each system must
individuallengthsfromcoil.Theprocessordirectlycontrols,or
be used independently of the other. Combining values from the
is responsible for, the operations involved in the processing of
two systems may result in nonconformance with the specifi-
coils into finished plates. Such operations include decoiling,
cation.
leveling, cutting to length, testing, inspection, conditioning,
heat treatment (if applicable), packaging, marking, loading for
2. Referenced Documents
shipment, and certification.
3
2.1 ASTM Standards:
NOTE 1—For plates produced from coil and furnished without heat
A20/A20M SpecificationforGeneralRequirementsforSteel
treatment or with stress relieving only, three test results are reported for
Plates for Pressure Vessels each qualifying coil. Additional requirements regarding plates from coil
are described in Specification A20/A20M.
A435/A435M Specification for Straight-Beam Ultrasonic
Examination of Steel Plates
3.4 If the requirements of this specification are in conflict
A577/A577M Specification for Ultrasonic Angle-Beam Ex-
with the requirements of Specification A20/A20M, the require-
ments of this specification shall prevail.
1
This specification is under the jurisdiction of ASTM Committee A01 on Steel,
4. Materials and Manufacture
Stainless Steel and Related Alloys and is the direct responsibility of Subcommittee
4.1 Steelmaking Practice—The steel shall be killed and
A01.11 on Steel Plates for Boilers and Pressure Vessels.
Current edition approved Oct. 1, 2009. Published November 2009. Originally
shall conform to the fine austenitic grain size requirement of
approved in 1947. Last previous edition approved in 2004 as A299/A299M – 04.
Specification A20/A20M.
DOI: 10.1520/A0299_A0299M-09.
2
For ASME Boiler and Pressure Vessel Code applications, see related Specifi-
5. Heat Treatment
cation SA-299/SA-299M in Section II of that Code.
3
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
5.1 Plates2in.[50mm]andunderinthicknessarenormally
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
supplied in the as-rolled condition. Plates may be ordered
Standards volume information, refer to the standard’s Document Summary page on
the ASTM website. normalized or stress relieved, or both.
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM Inte
...
This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation:A299/A299M–04 Designation: A299/A299M – 09
Standard Specification for
1
Pressure Vessel Plates, Carbon Steel, Manganese-Silicon
This standard is issued under the fixed designationA299/A299M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
Note—Grades A and B were added editorially to the entry for Carbon in Table 1 and the year date changed on Feb. 2, 2004.
1. Scope*
2
1.1 This specification covers manganese-silicon carbon steel plates for use in welded boilers and other pressure vessels.
1.2 Plates under this specification are produced in two grades. The specified minimum the yield strength decreases onfor
thicknesses over 1 in. [25 mm].
1.3 The maximum thickness of plates is limited only by the capacity of the composition to meet the specified mechanical
property requirements; however, current practice normally limits the maximum thickness of plates furnished under this
specification to 8 in. [200 mm].
1.4 Forplatesproducedfromcoilandfurnishedwithoutheattreatmentorwithstressrelievingonly,theadditionalrequirements,
including additional testing requirements and the reporting of additional test results, of Specification A20/A20M apply.
1.5 Thevaluesstatedineitherinch-poundunitsorSIunitsaretoberegardedseparatelyasstandard.Withinthetext,theSIunits
are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used
independently of the other. Combining values from the two systems may result in nonconformance with the specification.
2. Referenced Documents
3
2.1 ASTM Standards:
A20/A20M Specification for General Requirements for Steel Plates for Pressure Vessels Specification for General Require-
ments for Steel Plates for Pressure Vessels
A435/A435M Specification for Straight-Beam Ultrasonic Examination of Steel Plates
A577/A577M Specification for Ultrasonic Angle-Beam Examination of Steel Plates
A578/A578M Specification for Straight-Beam Ultrasonic Examination of Rolled Steel Plates for Special Applications
3. General Requirements and Ordering Information
3.1 Plates supplied to this product specification shall conform to Specification A20/A20M, which outlines the testing and
retesting methods and procedures, permissible variations in dimensions and mass, quality and repair of defects, marking, loading,
and so forth.
3.2Specification , which outlines the testing and retesting methods and procedures, permitted variations in dimensions and mass,
quality and repair of defects, marking, loading, and ordering information.
3.2 Inadditiontothebasicrequirementsofthisspecification,certainsupplementaryrequirementsareavailablewhereadditional
control, testing, or examination is required to meet end use requirements. The purchaser is referred to the listed supplementary
requirements in this specification and to the detailed requirements in Specification A20/A20Malso establishes the rules for the
ordering information that should be complied with when purchasing plates to this specification.
3.3In addition to the basic requirements of this specification, certain supplementary requirements are available where additional
control, testing, or examination is required to meet end use requirements.
3.4The purchaser is referred to the listed supplementary requirements in this specification and to the detailed requirements in
Specification A20/A20M.
3.5Coils3.3 Coils are excluded from qualification to this specification until they are processed into finished plates. Plates
1
This specification is under the jurisdiction ofASTM CommitteeA01 on Steel, Stainless Steel and RelatedAlloys and is the direct responsibility of SubcommitteeA01.11
on Steel Plates for Boilers and Pressure Vessels.
´1
Current edition approved Feb. 2, 2004. Published February 2004. Originally approved in 1947. Last previous edition approved in 2003 as A299/A299M–03 . DOI:
10.1520/A0299_A0299M-04.
Current edition approved Oct. 1, 2009. Published November 2009. Originally approved in 1947. Last previous edition approved in 2004 as A299/A299M – 04. DOI:
10.1520/A0299_A0299M-09.
2
For ASME Boiler and Pressure Vessel Code applications, see related Specification SA-299/SA-299M in Section II of that Code.
3
For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at service@astm.org. For Annual Book ofASTM Standar
...
This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation:A299/A299M–04 Designation: A299/A299M – 09
Standard Specification for
1
Pressure Vessel Plates, Carbon Steel, Manganese-Silicon
This standard is issued under the fixed designationA299/A299M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
Note—Grades A and B were added editorially to the entry for Carbon in Table 1 and the year date changed on Feb. 2, 2004.
1. Scope*
2
1.1 This specification covers manganese-silicon carbon steel plates for use in welded boilers and other pressure vessels.
1.2 Plates under this specification are produced in two grades. The specified minimum the yield strength decreases onfor
thicknesses over 1 in. [25 mm].
1.3 The maximum thickness of plates is limited only by the capacity of the composition to meet the specified mechanical
property requirements; however, current practice normally limits the maximum thickness of plates furnished under this
specification to 8 in. [200 mm].
1.4 Forplatesproducedfromcoilandfurnishedwithoutheattreatmentorwithstressrelievingonly,theadditionalrequirements,
including additional testing requirements and the reporting of additional test results, of Specification A20/A20M apply.
1.5 Thevaluesstatedineitherinch-poundunitsorSIunitsaretoberegardedseparatelyasstandard.Withinthetext,theSIunits
are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used
independently of the other. Combining values from the two systems may result in nonconformance with the specification.
2. Referenced Documents
3
2.1 ASTM Standards:
A20/A20M Specification for General Requirements for Steel Plates for Pressure Vessels Specification for General Require-
ments for Steel Plates for Pressure Vessels
A435/A435M Specification for Straight-Beam Ultrasonic Examination of Steel Plates
A577/A577M Specification for Ultrasonic Angle-Beam Examination of Steel Plates
A578/A578M Specification for Straight-Beam Ultrasonic Examination of Rolled Steel Plates for Special Applications
3. General Requirements and Ordering Information
3.1 Plates supplied to this product specification shall conform to Specification A20/A20M, which outlines the testing and
retesting methods and procedures, permissible variations in dimensions and mass, quality and repair of defects, marking, loading,
and so forth.
3.2Specification , which outlines the testing and retesting methods and procedures, permitted variations in dimensions and mass,
quality and repair of defects, marking, loading, and ordering information.
3.2 Inadditiontothebasicrequirementsofthisspecification,certainsupplementaryrequirementsareavailablewhereadditional
control, testing, or examination is required to meet end use requirements. The purchaser is referred to the listed supplementary
requirements in this specification and to the detailed requirements in Specification A20/A20Malso establishes the rules for the
ordering information that should be complied with when purchasing plates to this specification.
3.3In addition to the basic requirements of this specification, certain supplementary requirements are available where additional
control, testing, or examination is required to meet end use requirements.
3.4The purchaser is referred to the listed supplementary requirements in this specification and to the detailed requirements in
Specification A20/A20M.
3.5Coils3.3 Coils are excluded from qualification to this specification until they are processed into finished plates. Plates
1
This specification is under the jurisdiction ofASTM CommitteeA01 on Steel, Stainless Steel and RelatedAlloys and is the direct responsibility of SubcommitteeA01.11
on Steel Plates for Boilers and Pressure Vessels.
´1
Current edition approved Feb. 2, 2004. Published February 2004. Originally approved in 1947. Last previous edition approved in 2003 as A299/A299M–03 . DOI:
10.1520/A0299_A0299M-04.
Current edition approved Oct. 1, 2009. Published November 2009. Originally approved in 1947. Last previous edition approved in 2004 as A299/A299M – 04. DOI:
10.1520/A0299_A0299M-09.
2
For ASME Boiler and Pressure Vessel Code applications, see related Specification SA-299/SA-299M in Section II of that Code.
3
For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at service@astm.org. For Annual Book ofASTM Standar
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.