ASTM A285/A285M-17
(Specification)Standard Specification for Pressure Vessel Plates, Carbon Steel, Low- and Intermediate-Tensile Strength
Standard Specification for Pressure Vessel Plates, Carbon Steel, Low- and Intermediate-Tensile Strength
ABSTRACT
This specification covers carbon steel plates of low- and intermediate-tensile strengths which may be made by killed, semi-killed, capped, or rimmed steel. These plates are intended for fusion-welded pressure vessels. Plates are normally supplied in the as-rolled condition. The steel shall conform to the required chemical compositions. The plates, as represented by the tension test specimens, shall conform to the mechanical property requirements.
SCOPE
1.1 This specification2 covers carbon steel plates of low- and intermediate-tensile strengths which may be killed or semi-killed at the producer’s option. These plates are intended for fusion-welded pressure vessels.
1.2 Plates under this specification are available in three grades having different strength levels as follows:
Grade
Tensile Strength, ksi [MPa]
A
45–65 [310–450]
B
50–70 [345–485]
C
55–75 [380–515]
1.3 The maximum thickness of plates is limited by the capacity of the composition to meet the specified mechanical property requirements.
Note 1: For killed carbon steels only, refer to the following ASTM specifications:3
A299/A299M Specification for Pressure Vessel Plates, Carbon Steel, Manganese-Silicon
A515/A515M Specification for Pressure Vessel Plates, Carbon Steel, for Intermediate- and Higher-Temperature Service
A516/A516M Specification for Pressure Vessel Plates, Carbon Steel, for Moderate- and Lower-Temperature Service
1.4 For plates produced from coil and furnished without heat treatment or with stress relieving only, the additional requirements, including additional testing requirements and the reporting of additional test results, of Specification A20/A20M apply.
1.5 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with the specification.
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
General Information
Relations
Buy Standard
Standards Content (Sample)
This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the
Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
Designation:A285/A285M −17
Standard Specification for
Pressure Vessel Plates, Carbon Steel, Low- and
1
Intermediate-Tensile Strength
This standard is issued under the fixed designationA285/A285M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the U.S. Department of Defense.
1. Scope* system are not exact equivalents; therefore, each system must
2 be used independently of the other. Combining values from the
1.1 This specification covers carbon steel plates of low-
two systems may result in nonconformance with the specifi-
and intermediate-tensile strengths which may be killed or
cation.
semi-killed at the producer’s option. These plates are intended
for fusion-welded pressure vessels. 1.6 This international standard was developed in accor-
dance with internationally recognized principles on standard-
1.2 Plates under this specification are available in three
ization established in the Decision on Principles for the
grades having different strength levels as follows:
Development of International Standards, Guides and Recom-
Grade Tensile Strength, ksi [MPa]
mendations issued by the World Trade Organization Technical
A 45–65 [310–450]
B 50–70 [345–485] Barriers to Trade (TBT) Committee.
C 55–75 [380–515]
1.3 The maximum thickness of plates is limited by the 2. Referenced Documents
capacity of the composition to meet the specified mechanical
3
2.1 ASTM Standards:
property requirements.
A20/A20M SpecificationforGeneralRequirementsforSteel
NOTE 1—For killed carbon steels only, refer to the following ASTM Plates for Pressure Vessels
3
specifications:
A299/A299M Specification for Pressure Vessel Plates, Car-
A299/A299M Specification for Pressure Vessel Plates, Carbon Steel,
bon Steel, Manganese-Silicon
Manganese-Silicon
A435/A435M Specification for Straight-Beam Ultrasonic
A515/A515M Specification for Pressure Vessel Plates, Carbon Steel,
Examination of Steel Plates
for Intermediate- and Higher-Temperature Service
A516/A516M Specification for Pressure Vessel Plates, Carbon Steel,
A515/A515M Specification for Pressure Vessel Plates, Car-
for Moderate- and Lower-Temperature Service
bon Steel, for Intermediate- and Higher-Temperature Ser-
1.4 For plates produced from coil and furnished without vice
heat treatment or with stress relieving only, the additional A516/A516M Specification for Pressure Vessel Plates, Car-
requirements,includingadditionaltestingrequirementsandthe bon Steel, for Moderate- and Lower-Temperature Service
reporting of additional test results, of Specification A20/A20M A577/A577M Specification for Ultrasonic Angle-Beam Ex-
apply. amination of Steel Plates
A578/A578M Specification for Straight-Beam Ultrasonic
1.5 The values stated in either inch-pound units or SI units
Examination of Rolled Steel Plates for Special Applica-
are to be regarded separately as standard. Within the text, the
tions
SI units are shown in brackets. The values stated in each
3. General Requirements and Ordering Information
1
This specification is under the jurisdiction ofASTM Committee A01 on Steel,
3.1 Material supplied to this material specification shall
Stainless Steel and Related Alloys and is the direct responsibility of Subcommittee
conform to Specification A20/A20M. These requirements out-
A01.11 on Steel Plates for Boilers and Pressure Vessels.
line the testing and retesting methods and procedures, permit-
Current edition approved Nov. 1, 2017. Published November 2017. Originally
approved in 1946. Last previous edition approved in 2012 as A285/A285M – 12.
ted variations in dimensions, and mass, quality and repair of
DOI: 10.1520/A0285_A0285M-17.
defects, marking, loading, and ordering information.
2
For ASME Boiler and Pressure Vessel Code applications, see related Specifi-
cation SA-285/SA-285M in Section II of that Code.
3.2 In addition to the basic requirements of this
3
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
specification, certain supplementary requirements are available
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
when additional control, testing, or examination is required to
Standards volume information, refer to the standard’s Document Summary page on
the ASTM website. meet end use requirements. The purchaser is referred to the
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM International, 100 Barr Harbor Drive, PO
...
This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation: A285/A285M − 12 A285/A285M − 17
Standard Specification for
Pressure Vessel Plates, Carbon Steel, Low- and
1
Intermediate-Tensile Strength
This standard is issued under the fixed designation A285/A285M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the U.S. Department of Defense.
1. Scope*
2
1.1 This specification covers carbon steel plates of low- and intermediate-tensile strengths which may be made by killed,
semi-killed, capped, or rimmed steel practices at the producer’skilled or semi-killed at the producer’s option. These plates are
intended for fusion-welded pressure vessels.
1.2 Plates under this specification are available in three grades having different strength levels as follows:
Grade Tensile Strength, ksi [MPa]
A 45–65 [310–450]
B 50–70 [345–485]
C 55–75 [380–515]
1.3 The maximum thickness of plates under this specification, for reasons of internal soundness, is limited to a maximum
thickness of 2 in. [50 mm] for all grades. is limited by the capacity of the composition to meet the specified mechanical property
requirements.
3
NOTE 1—For killed carbon steels only, refer to the following ASTM specifications:
A 299/A 299M Pressure Vessel Plates, Carbon Steel, Manganese-
Silicon.
A299/A299M Specification for Pressure Vessel Plates, Carbon Steel, Manganese-Silicon
A515/A515M Specification for Pressure Vessel Plates, Carbon Steel, for Intermediate- and Higher-Temperature Service
A516/A516M Specification for Pressure Vessel Plates, Carbon Steel, for Moderate- and Lower-Temperature Service
A 515/A 515M Pressure Vessel Plates, Carbon Steel, for
Intermediate- and Higher-Temperature Service
A 516/A 516M Pressure Vessel Plates, Carbon Steel, for Moderate-
and Lower-Temperature Service.
1.4 For plates produced from coil and furnished without heat treatment or with stress relieving only, the additional requirements,
including additional testing requirements and the reporting of additional test results, of Specification A20/A20M apply.
1.5 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units
are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used
independently of the other. Combining values from the two systems may result in nonconformance with the specification.
1.6 This international standard was developed in accordance with internationally recognized principles on standardization
established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued
by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
2. Referenced Documents
3
2.1 ASTM Standards:
A20/A20M Specification for General Requirements for Steel Plates for Pressure Vessels
A299/A299M Specification for Pressure Vessel Plates, Carbon Steel, Manganese-Silicon
1
This specification is under the jurisdiction of ASTM Committee A01 on Steel, Stainless Steel and Related Alloys and is the direct responsibility of Subcommittee A01.11
on Steel Plates for Boilers and Pressure Vessels.
Current edition approved May 1, 2012Nov. 1, 2017. Published June 2012November 2017. Originally approved in 1946. Last previous edition approved in 20072012 as
A285/A285M – 03 (2007). 12. DOI: 10.1520/A0285_A0285M-12.10.1520/A0285_A0285M-17.
2
For ASME Boiler and Pressure Vessel Code applications, see related Specification SA-285/SA-285M in Section II of that Code.
3
For referenced ASTM standards, visit the ASTM website, www.astm.org, or contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1
---------------------- Page: 1 ----------------------
A285/A285M − 17
A435/A435M Specification for Straight-Beam Ultrasonic Examination of Steel Plates
A515/A515M Specification for Pressure Vessel Plates, Carbon Steel, for Intermediate- and Higher-Temperature Service
A516/A516M Specification for Pressure Vessel Plates, Carbon Steel, for Moderate- an
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.