ASTM A562/A562M-06

Standard Specification for Pressure Vessel Plates, Carbon Steel, Manganese-Titanium for Glass or Diffused Metallic Coatings

ABSTRACT
This specification covers standard requirements for titanium-bearing carbon steel plates intended for welded glass lined pressure vessels or other applications where the presence of free-iron carbide would be deleterious to the coating. The steel shall be killed and thermally treated to produce the required grain refinement specification. Heat and product analyses shall be performed wherein the material shall conform to the required chemical composition for carbon, manganese, phosphorus, sulfur, silicon, copper, and titanium. The steel plate shall conform to tensile requirements such as tensile strength, yield strength, and elongation.
SCOPE
1.1 This specification covers titanium-bearing carbon steel plates intended for welded glass lined pressure vessels or other applications where the presence of free-iron carbide would be deleterious to the coating. A minimum specific ratio of titanium to carbon is specified.
1.2 The maximum thickness of plates is limited to 2 in. [50 mm].
1.3 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with the specification.

General Information

• Status: Historical
• Publication Date: 28-Feb-2006
• ICS: 77.140.30 - Steels for pressure purposes
• Technical Committee: A01 - Steel, Stainless Steel and Related Alloys
• Drafting Committee: A01.11 - Steel Plates for Boilers and Pressure Vessels

Relations

• Replaces: ASTM A562/A562M-90(2001) - Standard Specification for Pressure Vessel Plates, Carbon Steel, Manganese-Titanium for Glass or Diffused Metallic Coatings
• Effective Date: 01-Mar-2006
• Replaced By: ASTM A562/A562M-10 - Standard Specification for Pressure Vessel Plates, Carbon Steel, Manganese-Titanium for Glass or Diffused Metallic Coatings
• Effective Date: 01-Oct-2010
• Referred By: ASTM A20/A20M-20 - Standard Specification for General Requirements for Steel Plates for Pressure Vessels
• Effective Date: 01-Mar-2006

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation: A562/A562M – 06
Standard Specification for
Pressure Vessel Plates, Carbon Steel, Manganese-Titanium
1
for Glass or Diffused Metallic Coatings
This standard is issued under the fixed designationA562/A562M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope 3.2 Specification A20/A20M also establishes the rules for
2 the ordering information which should be complied with when
1.1 This specification covers titanium-bearing carbon steel
purchasing material to this specification.
plates intended for welded glass lined pressure vessels or other
3.3 In addition to the basic requirements of this specifica-
applications where the presence of free-iron carbide would be
tion, certain supplementary requirements are available when
deleterioustothecoating.Aminimumspecificratiooftitanium
additional control, testing, or examination is required to meet
to carbon is specified.
end use requirements. These include:
1.2 The maximum thickness of plates is limited to 2 in. [50
3.3.1 Vacuum treatment,
mm].
3.3.2 Additional or special tension testing,
1.3 The values stated in either inch-pound units or SI units
3.3.3 Impact testing, and
are to be regarded separately as standard. Within the text, the
3.3.4 Nondestructive examination.
SI units are shown in brackets. The values stated in each
3.4 The purchaser is referred to the listed supplementary
system are not exact equivalents; therefore, each system must
requirements in this specification and to the detailed require-
be used independently of the other. Combining values from the
ments in Specification A20/A20M.
two systems may result in nonconformance with the specifi-
3.5 If the requirements of this specification are in conflict
cation.
with the requirements of SpecificationA20/A20M, the require-
2. Referenced Documents
ments of this specification shall prevail.
3
2.1 ASTM Standards:
4. Manufacture
A20/A20M Specification for General Requirements for
4.1 Steelmaking Practice—The steel shall be killed.
Steel Plates for Pressure Vessels
5. Heat Treatment
3. General Requirements and Ordering Information
5.1 Plates shall be thermally treated to produce grain refine-
3.1 Material supplied to this material specification shall
ment, either by normalizing or heating uniformly for hot
conform to Specification A20/A20M. These requirements out-
forming at a minimum temperature of 1600°F [870°C] or some
line the testing and retesting methods and procedures, permis-
higher agreed temperature, and held at this temperature for a
sible variations in dimensions, and mass, quality and repair of
minimum of 1 h/in. [2.4 min/mm] of thickness.
defects, marking, loading, etc.
6. Chemical Requirements
1
This specification is under the jurisdiction of ASTM Committee A01 on Steel,
6.1 The steel shall conform to the chemical requirements
Stainless Steel and Related Alloys and is the direct responsibility of Subcommittee
shown inTable 1 unless otherwise modified in accordance with
A01.11 on Steel Plates for Boilers and Pressure Vessels.
Current edition approved March 1, 2006. Published March 2006. Originally Supplementary Requirement S17, Vacuum Carbon-Deoxidized
approved in 1966. Last previous edition approved in 2001
...