Standard Specification for CPT-Fluoropolymer Molding and Extrusion Materials

Standard Specification for CPT-Fluoropolymer Molding and Extrusion Materials

ABSTRACT
This specification addresses the physical properties of copolymers of chlorotrifluoroethylene, perfluoroalkoxy, and tetrafluoroethylene that are suitable for extrusion, compression, and injection molding. It does not cover blended and recycled materials. Covered here is one type of fluoropolymer that is supplied in pellet form and classified according to their melting points, while the resins of each type are divided into four grades according to their melt flow rates. The materials shall be sampled in accordance with an adequate statistical sampling procedure and shall conform to specific gravity, melting point, flow rate, elongation, and tensile strength requirements when tested by the procedures itemized herein.
SCOPE
1.1 This specification covers copolymers of chlorotrifluoroethylene, perfluoroalkoxy, and tetrafluoroethylene and are suitable for extrusion, compression, and injection molding.  
1.2 This specification does not cover blended materials and does not cover recycled materials.  
1.3 The values stated in SI units as detailed in IEEE/ASTM SI-10 are to be regarded as the standard. The values given in parentheses are for information only.  
1.4 The following safety hazards caveat pertains only to the test method portion, Section 11, of this specification.This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.Note 1—There is no known ISO equivalent to this standard.

General Information

Status
Historical
Publication Date
28-Feb-2014
ICS
83.080.20 - Thermoplastic materials
Technical Committee
D20 - Plastics
Drafting Committee
D20.15 - Thermoplastic Materials
Current Stage
Ref Project

Relations

Replaces
ASTM D7471-09 - Standard Specification for CPT-Fluoropolymer Molding and Extrusion Materials
Effective Date
01-Mar-2014
Replaced By
ASTM D7471-19 - Standard Specification for CPT-Fluoropolymer Molding and Extrusion Materials
Effective Date
01-May-2019

Buy Standard

ASTM D7471-09(2014) - Standard Specification for CPT-Fluoropolymer Molding and Extrusion MaterialsASTM D7471-09(2014) - Standard Specification for CPT-Fluoropolymer Molding and Extrusion Materials
PreviousNext
Technical specification
ASTM D7471-09(2014) - Standard Specification for CPT-Fluoropolymer Molding and Extrusion Materials
English language
3 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation:D7471 −09 (Reapproved 2014)
Standard Specification for
1
CPT-Fluoropolymer Molding and Extrusion Materials
This standard is issued under the fixed designation D7471; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope D3892 Practice for Packaging/Packing of Plastics
E177 Practice for Use of the Terms Precision and Bias in
1.1 This specification covers copolymers of
ASTM Test Methods
chlorotrifluoroethylene, perfluoroalkoxy, and tetrafluoroethyl-
IEEE/ASTM SI-10 Use of the International System of Units
ene and are suitable for extrusion, compression, and injection
(SI): The Modem Metric System
molding.
1.2 This specification does not cover blended materials and
3. Terminology
does not cover recycled materials.
3.1 General—The terminology given in Terminology D883
1.3 The values stated in SI units as detailed in IEEE/ASTM
is applicable to this specification.
SI-10 are to be regarded as the standard. The values given in
3.2 Definitions:
parentheses are for information only.
3.3 lot, n—one production run or a uniform blend of two or
1.4 The following safety hazards caveat pertains only to the
more production runs.
test method portion, Section 11, of this specification.This
3.4 General—The abbreviated terms given in Terminology
standard does not purport to address all of the safety concerns,
D1600 are applicable to this specification.
if any, associated with its use. It is the responsibility of the user
of this standard to establish appropriate safety and health
4. Classification
practices and determine the applicability of regulatory limita-
4.1 This specification covers one type of fluoropolymer
tions prior to use.
supplied in pellet form classified according to their melting
NOTE 1—There is no known ISO equivalent to this standard.
point. The resins of each type are divided into four grades
according to their melt flow rate.
2. Referenced Documents
4.2 An one-line system shall be used to specify materials
2
2.1 ASTM Standards:
covered by this specification. The system uses predefined cells
D618 Practice for Conditioning Plastics for Testing
to refer to specific aspects of this specification, as illustrated as
D638 Test Method for Tensile Properties of Plastics
follows:
D792 Test Methods for Density and Specific Gravity (Rela-
Specification ___________________________
tive Density) of Plastics by Displacement
Standard Number : Type : Grade : Special
D883 Terminology Relating to Plastics
Block : : : Notes
D1238 Test Method for Melt Flow Rates of Thermoplastics :: :,:
Example: Specification D7471 - 09, I2
by Extrusion Plastometer
For this example, the line callout shall be, Specification
D1600 Terminology forAbbreviatedTerms Relating to Plas-
D7471 – 09, I2 and shall specify a fluoropolymer that has all of
tics
the properties listed for that type and grade in the appropriate
D3418 Test Method for Transition Temperatures and En-
specified properties, or tables, or both, in the specification
thalpies of Fusion and Crystallization of Polymers by
identified. A comma is used as the separator between the
Differential Scanning Calorimetry
standard number and the type. Separators are not needed
3
between the group and grade.
1
This specification is under the jurisdiction of ASTM Committee D20 on
Plastics and is the direct responsibility of Subcommittee D20.15 on Thermoplastic
5. General Requirements
Materials.
Current edition approved March 1, 2014. Published March 2014. Originally
5.1 The material shall be of uniform composition and so
approved in 2009. Last previous edition approved in 2009 as D7471 – 09. DOI:
prepared as to conform to the requirements of this specifica-
10.1520/D7471-09R14.
tion.
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
Standards volume information, refer to the standard’s Document Summary page on
3
the ASTM website. See the ASTM Form and Style Manual, available from ASTM Headquarters.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
D7471−09 (2014)
5.2 The material described in this specification shall be free apply 2 to 4 MPa (290 to 580 psi) and hold for 1 to 1.5 min.
of foreign matter to such a contamination level as shall be Maintain the press at 320 6 5°C (608 6 9°F) during these
agreed upon between the purchaser and the seller. steps. Remove the assembly from the press and place between
two 20 6 7-mm (0.75 6 0.25-in.) steel plates whose tempera-
6. Performance Requir
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

ASTM
ASTM D1238-23a(Test Method)
Standard Test Method for Melt Flow Rates of Thermoplastics by Extrusion Plastometer

SIGNIFICANCE AND USE
5.1 This test method is particularly useful for quality control tests on thermoplastics.  
5.2 The data produced by this test method serves to indicate the uniformity of the flow rate of the polymer as made by an individual process. It is not to be used as an indication of uniformity of other properties without valid correlation with data from other tests.  
5.3 The flow rate obtained with the extrusion plastometer is not a fundamental polymer property. It is an empirically defined parameter critically influenced by the physical properties and molecular structure of the polymer and the conditions of measurement. The rheological characteristics of polymer melts depend on a number of variables. It is possible that the values of these variables occurring in this test will differ substantially from those in large-scale processes, which would result in data that does not correlate directly with processing behavior.  
5.4 Measure the flow rate of a material using any of the conditions listed for the material in X4.1. For many materials, there are specifications that require the use of this test method, but with some procedural modifications that take precedence when adhering to the specification. Therefore, it is advisable to refer to that material specification before using this test method. Table 1 in Classification D4000 lists the ASTM materials standards that currently exist. An alternative test method for poly (vinyl chloride) (PVC) compounds is found in Test Method D3364.  
5.5 Additional characterization of a material can be obtained if more than one condition is used. In the case that two or more conditions are employed, a Flow Rate Ratio (FRR) is obtained by dividing the flow rate at one condition by the flow rate at another condition. Procedure D provides one method to measure more than one condition in a single charge.  
5.6 Frequently, variations in test technique, apparatus geometry, or test conditions, which defy all but the most careful scrutiny, exist...
SCOPE
1.1 This test method covers the determination of the rate of extrusion of molten thermoplastic resins using an extrusion plastometer.  
1.2 The values stated in SI units are to be regarded as standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
Note 1: This standard and ISO 1133 address the same subject matter, but differ in technical content.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    19 pages
    English language
    sale 15% off
  • Standard
    19 pages
    English language
    sale 15% off
ASTM
ASTM D6040-18(2023)(Guide)
Standard Guide to Standard Test Methods for Unsintered Polytetrafluoroethylene (PTFE) Extruded Film or Tape

ABSTRACT
This guide identifies the standard test methods to use in evaluating unsintered extruded films or tapes manufactured from polytetrafluoroethylene (PTFE). The test methods covered here shall be capable of investigating the following material properties: width; thickness; tensile properties (tensile strength and elongation); specificat gravity (relative density); residual extrusion aids or other volatile components; dielectric constant; volume resistivity; dielectric breakdown voltage; and unit weight.
SCOPE
1.1 This guide identifies test methods to use in evaluating unsintered extruded films or tapes manufactured from polytetrafluoroethylene.  
1.2 The values stated in SI units as detailed in IEEE/ASTM SI 10, are to be regarded as standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
Note 1: This test method is equivalent to ISO 12086-2:2006 in the measurement of tensile properties, specific gravity, and dielectric constant. These are in ISO 12086-2:2006, sections 8.2.2, 10.6 and 8.1.1. It is not equivalent to ISO 12086-2:2006 in any other measurement or section..  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Guide
    3 pages
    English language
    sale 15% off
ASTM
ASTM D8501-23a(Specification)
Standard Classification System for and Basis for Specification for Unfilled Poly(Ether Ketone Ketone) (PEKK) Materials for Molding, Extrusion, Composites, Powder Coating and Additive Manufacturing

SCOPE
1.1 This specification covers poly(ether ketone ketone) materials, commonly referred to as PEKK, which are suitable for molding, extrusion, composites, powder coating and additive manufacturing. Only materials in this Class 6-8 are covered by this specification. This classification system provides requirements for the use of regrind or reprocessed materials.  
1.2 This specification covers thermoplastic resin materials supplied in pellet as well as powder form.  
1.3 This specification applies only to PEKK copolymers, without any additional fillers or inorganic additives, alloys, or treatments for modification of attributes.  
1.4 This classification system and subsequent line callout (specification) are intended to provide means of calling out poly(ether ketone ketone) materials used in the fabrication of end items or parts.  
1.5 Poly(ether ketone ketone) (PEKK) is a member of the poly (aryl ether ketone) or PAEK polymer family. PEKK has a broad range of repeat unit combinations of Isophthaloyl and Terephthaloyl repeat units. This standard classifies the polymer options.  
1.6 The values stated in SI units, as detailed in IEEE/ASTM S-10, are to be regarded as the standard. The values given in parentheses are for information only.  
1.7 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
Note 1: There is no known ISO equivalent to this standard.
Note 2: PEKK is a thermoplastic polymer. Testing conditions can affect the technical results. Specimens prepared by techniques different than prescribed in this specification can have properties that vary from the values specified.  
1.8 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    7 pages
    English language
    sale 15% off
  • Technical specification
    7 pages
    English language
    sale 15% off
ASTM
ASTM D2561-17(2023)(Test Method)
Standard Test Method for Environmental Stress-Crack Resistance of Blow-Molded Polyethylene Containers

SIGNIFICANCE AND USE
5.1 When properly used, these procedures serve to isolate such factors as material, blow-molding conditions, post-treatment, and so forth, on the stress-crack resistance of the container.  
5.2 Environmental stress cracking of blow-molded containers is governed by many factors. Since variance of any of these factors can change the environmental stress-crack resistance of the container, the test results are representative only of a given test performed under defined conditions in the laboratory. The reproducibility of results between laboratories on containers made on more than one machine from more than one mold has not been established.  
5.3 Results can be used for estimating the shelf life of blow-molded containers in terms of their resistance to environmental stress cracking provided this is done against a rigorous background of practical field experience and reproducible test data.
SCOPE
1.1 Under certain conditions of stress, and in the presence of environments such as soaps, wetting agents, oils, or detergents, blow-molded polyethylene containers exhibit mechanical failure by cracking at stresses appreciably below those that would cause cracking in the absence of these environments.  
1.2 This test method measures the environmental stress crack resistance of blow-molded containers, which is the summation of the influence of container design, resin, blow-molding conditions, post treatment, or other factors that can affect this property. Three procedures are provided as follows:  
1.2.1 Procedure A, Stress-Crack Resistance of Containers to Potential Stress-cracking Liquids—This procedure is particularly useful for determining the effect of container design on stress-crack resistance or the stress-crack resistance of a proposed container that contains a liquid product.  
1.2.2 Procedure B, Stress-Crack Resistance of a Specific Container to Polyoxyethylated Nonylphenol (CAS 68412-54-4), a Stress-Cracking Agent—The conditions of test described in this procedure are designed for testing containers made from Class 3 polyethylene Specification D4976. Therefore, this procedure is recommended for containers made from Class 3 polyethylene only. This procedure is particularly useful for determining the effect of resin on the stress-crack resistance of the container.  
1.2.3 Procedure C, Controlled Elevated Pressure Stress-Crack Resistance of a Specific Container to Polyoxyethylated Nonylphenol (CAS 68412-54-4), a Stress-Cracking Agent—The internal pressure is controlled at a constant elevated level.
Note 1: There are environmental concerns regarding the disposal of Polyoxyethylated Nonylphenol (Nonylphenoxy poly(ethyleneoxy) ethanol (CAS 68412-54-4), for example, Igepal CO-630). Users are advised to consult their supplier or local environmental office and follow the guidelines provided for the proper disposal of this chemical.  
1.3 These procedures are not designed to test the propensity for environmental stress cracking in the neck of containers, such as when the neck is subjected to a controlled strain by inserting a plug.  
1.4 The values stated in SI units are to be regarded as standard.  
Note 2: There is no known ISO equivalent to this standard.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. Specific precautionary statements are given in Section 8 and Note 1.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    6 pages
    English language
    sale 15% off
ASTM
ASTM D4440-23(Test Method)
Standard Test Method for Plastics: Dynamic Mechanical Properties Melt Rheology

SIGNIFICANCE AND USE
5.1 This test method provides a simple means of characterizing the important rheological properties and viscosity of thermoplastic polymers using very small amounts of material (approximately 25 to 50 mm in diameter by 1 to 3 mm in thickness ... approximately 3 to 5 g). Data are generally used for quality control, research and development, and establishment of optimum processing conditions.  
5.2 Dynamic mechanical testing provides a sensitive method for determining molten polymer properties by measuring the elastic and loss moduli as a function of frequency, strain, temperature, or time. Plots of viscosity, storage, and loss moduli, and tan delta as a function of the aforementioned process parameters provide graphical representation indicative of molecular weight, molecular weight distribution, effects of chain branching, and melt-processability for specified conditions.  
5.2.1 Observed data are specific to experimental conditions. Reporting in full (as described in this test method) the conditions under which the data was obtained is essential to assist users with interpreting the data an reconciling apparent or perceived discrepancies.  
5.3 Values obtained in this test method can be used to assess the following:  
5.3.1 Complex viscosity of the polymer melt as a function of dynamic oscillation,  
5.3.2 Processing viscosity, minimum as well as changes in viscosity as a function of experimental parameters,  
5.3.3 Effects of processing treatment,  
5.3.4 Relative polymer behavioral properties, including viscosity and damping, and  
5.3.5 Effects of formulation additives that might affect processability or performance.  
5.4 Before proceeding with this test method, refer to the specification for the material being tested. Any test specimen preparation, conditioning, dimensions, or testing parameters, or combination thereof, covered in the relevant ASTM materials specification shall take precedence over those mentioned in the test method. If there are no r...
SCOPE
1.1 This test method outlines the use of dynamic mechanical instrumentation in determining and reporting the rheological properties of thermoplastic resins and other types of molten polymers. The method is useful for determining the complex viscosity and other significant viscoelastic characteristics of such materials as a function of frequency, strain amplitude, temperature, and time. It is known that fillers and other additives influence rheological properties.  
1.2 It incorporates a laboratory test method for determining the relevant rheological properties of a polymer melt subjected to various oscillatory deformations on an instrument of the type commonly referred to as a mechanical or dynamic spectrometer.  
1.3 This test method is intended to provide a means of determining the rheological properties of molten polymers, such as thermoplastics and thermoplastic elastomers over a range of temperatures by nonresonant, forced-vibration techniques. Plots of modulus, viscosity, and tan delta as a function of dynamic oscillation (frequency), strain amplitude, temperature, and time are indicative of the viscoelastic properties of a molten polymer.  
1.4 This test method is valid for a wide range of frequencies, typically from 0.01 Hz to 100 Hz.  
1.5 This test method is intended for homogenous and heterogeneous molten polymeric systems and composite formulations containing chemical additives, including fillers, reinforcements, stabilizers, plasticizers, flame retardants, impact modifiers, processing aids, and other important chemical additives often incorporated into a polymeric system for specific functional properties, and which could affect the processability and functional performance. These polymeric material systems have molten viscosities typically less than 106 Pa·s (107 poise).  
1.6 Test data obtained by this test method are relevant and appropriate for use in engineering design.  
1.7 The values stated in ...

  • Standard
    5 pages
    English language
    sale 15% off
  • Standard
    5 pages
    English language
    sale 15% off
ASTM
ASTM D2463-23(Test Method)
Standard Test Method for Drop Impact Resistance of Blow-Molded Thermoplastic Containers

SIGNIFICANCE AND USE
5.1 These procedures provide a means to assess the drop impact resistance of the group or lot of blown containers from which the test specimens were selected.  
5.2 It is acceptable to use these procedures for routine inspection purposes.  
5.3 These procedures will evaluate the combined effect of construction, materials, and processing conditions on the impact resistance of the blown containers.  
5.4 Before proceeding with this test method, reference the specification of the material being tested. Any test specimen preparation, conditioning, dimensions, or testing parameters, or combination thereof, covered in the materials specification shall take precedence over those mentioned in this test method. If there are no material specifications, then the default conditions apply.
SCOPE
1.1 This test method provides a means to assess the drop impact resistance of water-filled, blow-molded thermoplastic containers, which is a summation of the effects of material, manufacturing conditions, container design, and perhaps other factors.  
1.2 Two procedures are provided as follows:  
1.2.1 Procedure A, Static Drop Height Method—This procedure is particularly useful for quality control since it is quick.  
1.2.2 Procedure B, Bruceton Staircase Method—This procedure is used to determine the mean failure height and the standard deviation of the distribution.  
1.3 The values stated in SI units are to be regarded as standard. The inch-pound units given in parentheses are for information only.  
Note 1: There is no known ISO equivalent to this standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    5 pages
    English language
    sale 15% off
  • Standard
    5 pages
    English language
    sale 15% off
ASTM
ASTM D6835-23(Classification)
Standard Classification System for Thermoplastic Elastomer-Ether-Ester Molding and Extrusion Materials (TEEE)

SCOPE
1.1 This classification system covers segmented block copolyether-ester elastomers suitable for molding and extrusion.  
1.2 This classification system allows for the use of segmented block copolyether-ester elastomers that are recycled provided that the requirements as stated in this classification system are met. The proportions of recycled material used, as well as the nature and amount of any contaminant, however, cannot be covered practically in this specification.  
1.3 The properties included in this classification system are those required to identify the compositions covered. It is possible that there are other requirements necessary to identify particular characteristics important to specialized applications. One way of specifying them is by using the suffixes as given in Section 5.  
1.4 This classification system and subsequent line callout (specification) are intended to provide a means of calling out plastic materials used in the fabrication of end items or parts. It is not intended for the selection of materials. Material selection is best made by those having expertise in the plastic field after careful consideration of the design and the performance required of the part, the environment to which it will be exposed, the fabrication process to be employed, the costs involved, and the inherent properties of the material other than those covered by this classification system.  
1.5 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.6 The following precautionary caveat pertains only to the test methods portion, Section 11, of this classification system. This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
Note 1: This standard, ISO 20029-1, and ISO 20029-2 address the same subject matter, but differ in technical content.  
1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    5 pages
    English language
    sale 15% off
  • Standard
    5 pages
    English language
    sale 15% off
ASTM
ASTM D3030-23(Test Method)
Standard Test Method for Volatile Matter (Including Water) of Vinyl Chloride Resins

SIGNIFICANCE AND USE
5.1 The quantity of volatile components in a vinyl chloride resin can be established by this test method. This test method does not identify the components.
SCOPE
1.1 This test method covers the quantitative determination of the volatile matter (including water) present in vinyl chloride resins.  
1.2 The values stated in SI units are to be regarded as standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
Note 1: This test method is identical ISO 1269.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    3 pages
    English language
    sale 15% off
  • Standard
    3 pages
    English language
    sale 15% off
ASTM
ASTM D4878-23(Test Method)
Standard Test Methods for Polyurethane Raw Materials: Determination of Viscosity of Polyols

SIGNIFICANCE AND USE
4.1 These test methods are suitable for research or as quality control or specification tests.  
4.2 Viscosity measures the resistance of a fluid to uniformly continuous flow without turbulence or other forces.
SCOPE
1.1 These test methods (A and B) determine the viscosity of polyols in the range from 10 to 100 000 mPa·s(cP) at 25°C. Test Method A is a rotational procedure for determining dynamic viscosity. Test Method B is a general procedure for kinematic viscosity of transparent polyols. (See Note 1.)  
1.2 The values stated in SI units are to be regarded as the standard. Other equivalent units are provided because of current common usage.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
Note 1: Test Method A is equivalent to ISO 3219. Test Method B is equivalent to ISO 3104.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    5 pages
    English language
    sale 15% off
  • Standard
    5 pages
    English language
    sale 15% off
ASTM
ASTM D3275-18(2023)(Classification)
Standard Classification System for E-CTFE-Fluoroplastic Molding, Extrusion, and Coating Materials

ABSTRACT
This classification system covers melt processible molding, extrusion, and coating materials of ethylene-chlorotrifluoroethylene (E-CTFE) fluoroplastics. The resin is a copolymer of ethylene and chlorotrifluoroethylene. The classification of ECTFE materials into groups in accordance with their physical appearance, and further into classes based on melt flow rate, is provided. The test specimens shall be subjected to tests to determine their melt flow rate, melting endotherm peak, specific gravity, tensile property, dielectric constant and dissipation factor, and oxygen index.
SCOPE
1.1 This classification system covers melt processible molding, extrusion, and coating materials of ethylene-chlorotrifluoroethylene (E-CTFE) fluoroplastics. The resin is a copolymer of ethylene and chlorotrifluoroethylene containing approximately 80 weight % of chlorotrifluoroethylene.  
1.2 The values stated in SI units, as detailed in IEEE/ASTM SI-10, are to be regarded as standard.  
1.3 The following precautionary statement pertains only to the test methods portion, Section 11 of this classification system. This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
Note 1: Although this classification system and ISO 20568-1 and ISO 20568-2 differ in approach or detail, data obtained using either are technically equivalent.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    4 pages
    English language
    sale 15% off