ISO 4892-4:1994
(Main)Plastics — Methods of exposure to laboratory light sources — Part 4: Open-flame carbon-arc lamps
Plastics — Methods of exposure to laboratory light sources — Part 4: Open-flame carbon-arc lamps
Specifies methods for exposing to a carbon-arc light source under controlled environmental conditions. The procedure may include measurements of the irradiance and radiant exposure at the surface of the specimen. It is recommended that a similar material of known behaviour be exposed simultaneously with the experimental material as a reference. General guidance is given in ISO 4892-1.
Plastiques — Méthodes d'exposition à des sources lumineuses de laboratoire — Partie 4: Lampes à arc au carbone
Polimerni materiali - Metode izpostave laboratorijskim izvorom svetlobe - 4. del: Ogljikove svetilke z odprtim plamenom
General Information
Relations
Buy Standard
Standards Content (Sample)
INTERNATIONAL
IS0
STANDARD 4892-4
First edition
1994-05-01
Plastics - Methods of exposure to
laboratory light sources -
Part 4:
Open-flame carbon-arc lamps
P/as tiques - M&hodes d’exposition a des sources lumineuses de
labora toire -
Partie 4: Lampes 9 arc au carbone
Reference number
IS0 4892-4: 1994(E)
---------------------- Page: 1 ----------------------
IS0 4892-4: 1994(E)
Foreword
IS0 (the International Organization for Standardization) is a worldwide
federation of national standards bodies (IS0 member bodies). The work
of preparing International Standards is normally carried out through IS0
technical committees. Each member body interested in a subject for
which a technical committee has been established has the right to be
represented on that committee. International organizations, governmental
and non-governmental, in liaison with ISO, also take part in the work. IS0
collaborates closely with the International Electrotechnical Commission
(IEC) on all matters of electrotechnical standardization.
Draft International Standards adopted by the technical committees are
circulated to the member bodies for voting. Publication as an International
Standard requires approval by at least 75 % of the member bodies casting
a vote.
International Standard IS0 4892-4 was prepared by Technical Committee
!SO/TC 61, Plastics, Subcommittee SC 6, Ageing, chemical and environ-
mental resistance.
Together with the other parts of IS0 4892, it cancels and replaces
IS0 4892:1981, of which it constitutes a technical revision.
IS0 4892 consists of the following parts, under the general title
- Methods of exposure to laboratory light sources:
P/as tics
- Part I: General guidance
- Part 2: Xenon-arc sources
- Part 3: Fluorescent lJV lamps
- Part 4: Open-flame carbon-arc lamps
Annex A forms an integral part of this part of IS0 4892. Annexes B and
C are for information only.
0 IS0 1994
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced
or utilized in any form or by any means, electronic or mechanical, including photocopying and
microfilm, without permission in writing from the publisher.
International Organization for Standardization
Case Postale 56 l CH-1211 Geneve 20 l Switzerland
Printed in Switzerland
---------------------- Page: 2 ----------------------
IS0 4892-4: 1994(E)
INTERNATIONAL STANDARD 0 IS0
- Methods of exposure to laboratory light
Plastics
sources -
Part 4:
Open-flame carbon-arc lamps
3.2 The procedure may include measurements of
1 Scope
the irradiance and radiant exposure at the surface of
This part of IS0 4892 specifies methods for exposing
the specimen.
specimens to open-flame carbon-arc lamps. General
guidance is given in IS0 4892-l.
3.3 It is recommended that a similar material of
known behaviour be exposed simultaneously with the
2 Normative references
experimental material as a reference.
The following standards contain provisions which,
through reference in this text, constitute provisions
of this part of IS0 4892. At the time of publication, the
3.4 Intercomparison of results obtained from speci-
editions indicated were valid. All standards are subject
mens exposed in different apparatus should not be
to revision, and parties to agreements based on this
made unless reproducibility has been established
part of IS0 4892 are encouraged to investigate the
among devices for the material to be tested.
possibility of applying the most recent editions of the
standards indicated below. Members of IEC and IS0
maintain registers of currently valid International
4 Apparatus
Standards.
IS0 4582: 1980, Plastics - Determination of changes
in colour and variations in properties after exposure to 4.1 Laboratory light source
daylight under glass, natural weathering or artificial
.
l/ght .
4.1.1 The lamp comprises an arc formed in free air
between carbon rod electrodes. The specifications for
IS0 4892-l :I 994, Plastics - Methods of exposure to
the light source are given in annex A.
labora tory light sources - Part I: General guidance.
3 Principle
4.1.2 The radiation reaching the specimens passes
through filter elements. The different types of filter
3.1 Specimens of the samples to be tested are ex- element used in practice shall have spectral-
posed to a carbon-arc light source under controlled transmittance values as specified in table 1 at the
environmental conditions. wavelengths given in the table.
1
---------------------- Page: 3 ----------------------
IS0 4892=4:1994(E)
Table 1 - Spectral transmittance of glass filters at specific wavelengths prior to use
Type 1 TYPe 2 Type 3
Wavelength Transmittance Wavelength Transmittance Wavelength Transmittance
nm % nm % nm %
295
255
> 40
320 65 to 80 320
302 71 to 86
Information on different types of glass filter is given
4.5 Relative-humidity control equipment
in annex B.
The relative humidity of the air passing over the test
The carbon rods shall be changed in accordance with
specimens shall be controlled at an agreed value if
the manufacturer’s instructions.
required and measured by suitable instruments in-
serted into the test chamber and shielded from the
The characteristics of filters are subject to change
lamp radiation.
during use due to ageing and the formation of de-
posits, and filters shall therefore be replaced at suit-
able intervals (see 7.2.2).
4.6 Spray system
4.2 Test chamber (see also annex B)
4.6.1 The test chamber shall contain a water-spray
The test chamber contains a specimen frame, with
system equipped with nozzles to produce a uniformly
provision for passing air over the specimens for tem-
distributed spray on demand. The system shall be
perature control.
constructed of stainless steel, plastic or another ma-
The frame rotates about the central axis of the
terial that does not react with or contaminate the
carbon-arc holder. A typical frame diameter is 96 cm.
water passing through it.
Other frame diameters may be used if mutually
NOTE 1 Suitable filters and demineralizers may be re-
agreed upon by all interested parties.
quired for use in conjunction with the spray system in order
to meet the requirements for water purity.
The frame shall carry specimens directly as panels
and/or in holders attached to the frame. The frame
may be vertical or inclined.
4.6.2 The spray system shall provide uniform wet-
The upper and lower electrodes, as well as the
ting and rapid cooling. Spray water shall drain freely
filter(s), shall be installed in accordance with the in-
from the wetted surfaces.
structions of the manufacturer of the apparatus.
The apparatus shall be fitted with equipment for pro-
4.6.3 Specimens may be sprayed with distilled or
cycles within the operational Iim-
gramming exposure
demineralized water (having a conductivity below
its of the apparatus,
5 IS/cm) intermittently under specified conditions.
The water shall leave no observable stains or deposits
4.3 Radiometer
and should therefore preferably contain less than
1 ppm of solids. In addition to distillation, a combi-
is used, it shall comply with the
When a radiometer
nation of deionization and reverse-osmosis can be
requirements outlined in IS0 4892-l : 1994, subclause
used to produce water of the required quality. The pH
52 . .
of the water used shall be reported.
4.4 Black-standard/black-panel thermometer
4.6.4 A spray system designed to cool the specimen
The black-standard or black-panel thermometer used by spraying the back surface of the specimen or
shall comply with the requirements outlined in specimen backing may be required when the ex-
IS0 4892-l : 1994, subclause 5.1.5. posure programme specifies periods of condensation.
---------------------- Page: 4 ----------------------
0 IS0 IS0 4892=4:1994(E)
4.7 Specimen holders
Table 2 - Spray cycles
Specimen holders may be in the form of an open
Dry interval between
frame, leaving the back of the specimen exposed, or
Duration of spraying
spraying
they may provide the specimen with
...
SLOVENSKI STANDARD
SIST ISO 4892-2:1996
01-junij-1996
Polimerni materiali - Metode izpostave laboratorijskim izvorom svetlobe - 2. del:
Ksenonska svetilka
Plastics -- Methods of exposure to laboratory light sources -- Part 2: Xenon-arc sources
Plastiques -- Méthodes d'exposition à des sources lumineuses de laboratoire -- Partie 2:
Sources à arc au xénon
Ta slovenski standard je istoveten z: ISO 4892-2:1994
ICS:
83.080.01 Polimerni materiali na Plastics in general
splošno
SIST ISO 4892-2:1996 en
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.
---------------------- Page: 1 ----------------------
SIST ISO 4892-2:1996
---------------------- Page: 2 ----------------------
SIST ISO 4892-2:1996
IS0
INTERNATIONAL
4892-2
STANDARD
First edition
1994-05-01
- Methods of exposure to
Plastics
laboratory light sources -
Part 2:
Xenon-arc sources
P/as tiques - M&hodes d’exposition 2 des sources lumineuses de
labora toire -
Partie 2: Sources 9 arc au x&non
Reference number
IS0 4892-2:1994(E)
---------------------- Page: 3 ----------------------
SIST ISO 4892-2:1996
IS0 4892-2: 1994(E)
Foreword
IS0 (the International Organization for Standardization) is a worldwide
federation of national standards bodies (IS0 member bodies). The work
of preparing International Standards is normally carried out through IS0
technical committees. Each member body interested in a subject for
which a technical committee has been established has the right to be
represented on that committee. International organizations, governmental
and non-governmental, in liaison with ISO, also take part in the work. IS0
collaborates closely with the International Electrotechnical Commission
(IEC) on all matters of electrotechnical standardization.
Draft International Standards adopted by the technical committees are
circulated to the member bodies for voting. Publication as an International
Standard requires approval by at least 75 % of the member bodies casting
a vote.
International Standard IS0 4892-2 was prepared by Technical Committee
!SO/TC 61, Plastics, Subcommittee SC 6, Ageing, chemica/ and environ-
mental resistance.
Together with the other parts of IS0 4892, it cancels and replaces
IS0 4892:1981, of which it constitutes a technical revision.
IS0 4892 consists of the following parts, under the general title
P/as tics - Methods of exposure to laboratory light sources:
- Part 7: General guidance
- Part 2: Xenon-arc sources
- Part 3: Fluorescent UV lamps
- Part 4: Open-flame carbon-arc lamps
Annex A of this part of IS0 4892 is for information only.
0 IS0 1994
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced
or utilized in any form or by any means, electronic or mechanical, including photocopying and
microfilm, without permission in writing from the publisher.
International Organization for Standardization
Case Postale 56 l CH-1211 Geneve 20 l Switzerland
Printed in Switzerland
---------------------- Page: 4 ----------------------
SIST ISO 4892-2:1996
INTERNATIONAL STANDARD 0 IS0 IS0 4892-2: 1994(E)
Plastics - Methods of exposure to laboratory light
sources -
Part 2:
Xenon-arc sources
3 Principle
1 Scope
This part of IS0 4892 specifies methods for exposing
specimens to xenon-arc light sources. General guid-
3.1 A xenon arc, when fitted with suitable filters
ance is given in IS0 4892-l.
and properly maintained, produces radiation with a
spectral energy distribution similar to that of terrestrial
2 Normative references
sunlight in the ultraviolet and visible regions of the
spectrum.
The following standards contain provisions which,
through reference in this text, constitute provisions
of this part of IS0 4892. At the time of publication, the
editions indicated were valid. All standards are subject
3.2 Specimens of the samples to be tested are ex-
to revision, and parties to agreements based on this
posed to the light source under controlled environ-
part of IS0 4892 are encouraged to investigate the
mental conditions.
possibility of applying the most recent editions of the
standards indicated below. Members of IEC and IS0
maintain registers of currently valid International
Standards.
3.3 The procedure may include measurement of the
irradiance and radiant exposure at the surface of the
IS0 4582:1980, Plastics - Determination of changes
specimen.
in colour and variations in properties after exposure to
daylight under glass, natural weathering or artificial
.
light .
3.4 It is recommended that a similar material of
IS0 4892-l : 1994, Plastics - Methods of exposure to
known behaviour be exposed simultaneously with the
labora tory light sources - Part 1: General guidance.
experimental material as a reference.
Cl E Publication No. 20: 1972, Recommendations for
the integrated irradiance and the spectral distribution
of simulated solar radiation for testing purposes. 3.5 Intercomparison of results obtained from speci-
mens exposed in different apparatus should not be
CIE Publication No. 85:1989, Technical Report - So- made unless reproducibility has been established
lar spectral irradiance. among devices for the material to be tested.
1
---------------------- Page: 5 ----------------------
SIST ISO 4892-2:1996
IS0 4892-2: 1994(E) 0 IS0
4 Apparatus
- Relative spectral irradiance for
Table 1
artificial weathering (method A)
I I
Relative spectral
Wavelength, A
irradiancel)
4.1 Laboratory light source
nm %
290 < 1 \< 800 100
R < 290 02)
4.1.1 Quartz-jacketed xenon-arc lamps emit radiation
290 < A. < 320 0,6 + 0,2
in a range that extends from below 270 nm in the -
ultraviolet through the visible region of the spectrum
320 < R < 360 4,2 + 0,5
-
and into the infrared.
360 < A < 400 62 k 1 ,O
To simulate direct natural exposure, the radiant en-
I) The spectral irradiance between 290 nm and
ergy must be filtered to provide a spectral power dis-
800 nm is defined as 100 %.
tribution that closely approximates to that of terrestrial
2) Xenon arcs operating as specified in method A emit
daylight (method A), as described in CIE Publication
a small amount of radiation below 290 nm. In some
No. 85.
cases, this can cause degradation reactions which do
not occur in outdoor exposures.
Filters designed to reduce the irradiance below
320 nm are used to simulate daylight filtered through
window glass (method B).
Table 2 - Relative spectral irradiance for
daylight behind window glass (method B)
Additional filters to reduce the level of non-actinic in-
Relative spectral
frared energy may be desirable when heating of the
Wavelength, R
irradiancel)
specimen adversely influences the photochemical-
reaction rate or causes thermal degradation not ex- nm %
I
perienced during real-time natural exposure.
300 < R \< 800 100
The characteristics of xenon arcs and filters are sub-
0
;1 \< 300
ject to change during use due to ageing, and lamps
300 < A < 320 < 0,l
and filters shall be replaced at suitable intervals. Fur-
thermore, they are subject to change due to the ac- 3,O * 0,5
320 < A. < 360
cumulation of dirt and shall therefore be cleaned at
360 < ;1 < 400 60 k I,0
suitable intervals. Follow the manufacturer’s rec-
I) The spectral irradiance between 300 nm and
ommendations for replacement and cleaning of lamps
800 nm is defined as 100 %.
and filters. I
4.1.4 The irradiance at the test specimen surface
shall not vary by more than & 10 % comparing any
4.1.2 Recommendations for UV-radiation distri-
two points in the sample holder plane parallel to the
butions of filtered xenon-arc sources, together with
lamp axis. If this is not possible, specimens shall be
tolerance limits, are given in table 1 for artificial
periodically repositioned to provide equivalent ex-
weathering (method A) and table2 for simulated ex-
posure periods in each location.
posure to daylight behind window glass (method B).
NOTE 1
Depending on the exact design of test chamber
spectral-irradiance values may be time-
(4.2) used, th e
averaged values.
4.1.3 For reference purposes, an irradiance of
550 W/m* in the 290 nm to 800 nm passband has
been selected (see CIE Publication No. 20). It is not
4.2 Test chamber
necessarily the preferred irradiance. When mutually
agreed upon between interested parties, other
The test chamber contains a frame, carrying specimen
irradiance levels may be selected. Report the
holders if necessary, with provision for passing air
irradiance and the passband selected.
over the specimens for temperature control.
2
---------------------- Page: 6 ----------------------
SIST ISO 4892-2:1996
0 IS0 IS0 4892-2:1994(E)
The source(s) of radiant energy shall be located, with water shall leave no observable stains or deposits and
respect to the specimens, such that the irradiance at should therefore preferably contain less than 1 ppm
the specimen surface complies with 4.1.3 and 4.1.4. of solids. In addition to distillation, a combination of
deionization and reverse osmosis can be used to
Should any ozone be generated from operation of the
produce water of the required quality. The pH of the
lamp(s), the lamp(s) shall be isolated from the test
water used shall be reported.
specimens and operating personnel. If the ozone is in
an air stream, it shall be vented directly to the outside
4.7 Specimen holders
of the building.
Specimen holders may be in the form of an open
To reduce the effect of any eccentricity in the lamp,
frame, leaving the back of the specimen exposed, or
or when more than one lamp is used in a single
they may provide the specimen with a solid backing.
chamber to increase irradiance, the uniformity of ex-
They shall be made from inert materials that will not
posure may be improved by rotating the frame carry-
affect the test results, for example non-oxidizing al-
ing the specimens around the light source(s) and, if
loys of aluminium or stainless steel. Brass, steel or
necessary, by periodically changing the position of
copper shall not be used in the vicinity of the test
each specimen.
specimens. The backing used may affect the results,
particularly with transparent specimens, and shall be
The specimen holders may also rotate about their
agreed on between the interested parties.
own axis, thus exposing directly to the radiation from
the light source the side of the specimen holder that
was previously not directly exposed. 4.8 Apparatus to assess changes in
properties
Programmes may be used which employ a dark cycle
obtained by extinguishing the light source to provide
The apparatus required by the International Standards
controlled exposure conditions without the presence
relating to the determination of the properties chosen
of simulated solar radiation.
for monitoring (see also IS0 4582) shall be used.
When any of these operating modes or programmes
5 Test specimens
are used, they shall be reported in full.
Refer to IS0 4892-l.
4.3 Radiometer
6 Test conditions
When a radiometer is used, it shall comply with the
requirements outlined in IS0 4892-l :1994, subclause
. .
52 6.1 Black-standard/black-panel temperature
Two black-standard temperatures have been selected
4.4 Black-standard/black-panel thermometer
for reference purposes:
The black-standard or black-panel thermometer used
65 “C + 3 “C
shall comply with the requirements outlined in
IS0 4892-l :I 994, subclause 5.1.5.
100 "C + 3 "C
-
NOTE 2 The higher temperature is intended for special
4.5 Relative-humidity control equipment
tests, but will increase the tendency of the specimen to
undergo thermal degradation and influence the test results.
The relative humidity of the air passing over the test
specimens shall be controlled at an agreed value, and
These temperatures are not necessarily the preferred
measured by suitable instruments inserted into the
ones. When mutually agreed upon, another tempera-
test chamber and shielded from the lamp radiation.
ture may be selected, but shall be stated in the ex-
posure report.
Spray system
4.6
If water spray is used, the temperature requirements
Specimens may be sprayed with distilled or apply to the end of the dry period. If the thermometer
demineralized water (having a conductivity below does not attain equilibrium during a short cycle, the
5 pS/cm) intermittently under specified conditions. specified temperature shall be established without
The spray system shall be made from inert materials water spray and the maximum temperature attained
that do not contaminate the water employed. The during the dry cycle shall be reported.
3
---------------------- Page: 7 ----------------------
SIST ISO 4892-2:1996
0 IS0
IS0 4892-2: 1994(E)
Even if the exposure apparatus is operated in an specimen by suitable indelible marking, avoiding areas
alternating mode, measurement by black-standard to be used for subsequent testing. As a check, a plan
thermometer shall be carried out in the continuous of the test-specimen positions may be made.
mode.
If desired, in the case of specimens used to deter-
If a black-panel thermometer is used, then the type mine change in colour and appearance, a portion of
of thermometer, the way in which it is mounted on
each test specimen may be shielded by an opaque
the specimen holder and the selected temperature of cover throughout the test. This gives an unexposed
operation shall be stated in the exposure report. area adjacent to the exposed area for comparison.
This is useful for checking the progress of the ex-
posure, but the data reported shall always be based
...
NORME ISO
INTERNATIONALE 4892-4
Premihe édition
1994-05-01
- Méthodes d’exposition à des
Plastiques
sources lumineuses de laboratoire -
Partie 4:
Lampes à arc au carbone
P/as tics - Methods of exposure to laboratory light sources -
Part 4: Open-flame carbon-arc lamps
Numéro de référence
ISO 4892-4: 1994(F)
---------------------- Page: 1 ----------------------
ISO 4892-4: 1994(F)
Avant-propos
L’ISO (Organisation internationale de normalisation) est une féderation
mondiale d’organismes nationaux de normalisation (comités membres de
I’ISO). L’élaboration des Normes internationales est en général confiée aux
comités techniques de I’ISO. Chaque comite membre intéressé par une
étude a le droit de faire partie du comite technique creé a cet effet. Les
organisations internationales, gouvernementales et non gouvernemen-
tales, en liaison avec I’ISO participent également aux travaux. L’ISO colla-
bore étroitement avec la Commission électrotechnique internationale (CEI)
en ce qui concerne la normalisation électrotechnique.
Les projets de Normes internationales adoptés par les comités techniques
sont soumis aux comités membres pour vote. Leur publication comme
Normes internationales requiert l’approbation de 75 % au moins des co-
mités membres votants.
La Norme internationale ISO 4892-4 a été élaborée par le comité techni-
que lSO/TC 61, Plastiques, sous-comité SC 6, Vieillissement et résistance
aux agents chimiques et environnants.
Conjointement avec les autres parties de I’ISO 4892, elle annule et rem-
place la Norme internationale ISO 4892:1981, dont elle constitue une ré-
vision technique.
L’ISO 4892 comprend les parties suivantes, présentées sous le titre gé-
néral Plastiques - M&hodes d’exposition à des sources lumineuses de
laboratoire:
- Partie 1: Guide général
- Partie 2: Sources à arc au x&on
- Partie 3: Lampes fluorescentes UV
- Partie 4: Lampes à arc au carbone
L’annexe A fait partie intégrante de la présente partie de I’ISO 4892. Les
annexes B et C sont données uniquement a titre d’information.
0 60 1994
Droits de reproduction réservés. Sauf prescription différente, aucune partie de cette publi-
cation ne peut être reproduite ni utilisee sous quelque forme que ce soit et par aucun pro-
cédé, électronique ou mécanique, y compris la photocopie et les microfilms, sans l’accord
écrit de l’editeur.
Organisation internationale de normalisation
Case Postale 56 l CH-l 211 Genéve 20 l Suisse
Imprimé en Suisse
ii
---------------------- Page: 2 ----------------------
ISO 4892-4: 1994(F)
NORME INTERNATIONALE 0 ISO
- Méthodes d’exposition à des sources
Plastiques
lumineuses de laboratoire -
Partie 4:
Lampes à arc au carbone
3 Principe
1 Domaine d’application
La présente partie de I’ISO 4892 prescrit une mé-
3.1 Les éprouvettes des échantillons à essayer sont
thode pour l’exposition d’éprouvettes à des lampes à
exposées a une source de lumiere à arc au carbone
arc au carbone. L’ISO 4892-l donne des recomman-
dans des conditions d’environnement contrôlées.
dations générales.
3.2 Le mode opératoire peut comprendre le mesu-
rage de l’éclairement énergétique et de l’exposition
énergétique sur la surface de l’éprouvette.
3.3 II est conseillé d’exposer, en même temps que
le matériau a essayer, un matériau similaire dont le
2 Références normatives
comportement est connu.
Les normes suivantes contiennent des dispositions
3.4 La comparaison des résultats obtenus avec des
qui, par suite de la référence qui en est faite, consti-
éprouvettes exposées en différents appareils ne de-
tuent des dispositions valables pour la présente partie
vrait pas être faite si la reproductibilité entre les ap-
de I’ISO 4892. Au moment de la publication, les édi-
pareils n’a pas été établie pour le matériau a essayer.
tions indiquées étaient en vigueur. Toute norme est
sujette à révision et les parties prenantes des accords
fondés sur la présente partie de I’ISO 4892 sont invi-
4 Appareillage
tées à rechercher la possibilité d’appliquer les éditions
les plus récentes des normes indiquées ci-aprés. Les
4.1 Source lumineuse de laboratoire
membres de la CEI et de I’ISO possédent le registre
des Normes internationales en vigueur a un moment
4.1.1 La lampe se compose d’un arc formé a l’air li-
donné.
bre entre des électrodes cylindriques en carbone. La
spécification de la source lumineuse est donnée dans
ISO 4582:1980, Plastiques - Ddtermination des
l’annexe A.
changements de coloration et des variations de pro-
priétés après exposition à la lumière naturelle sous
4.1.2 Le rayonnement qui atteint les éprouvettes
verre, aux agents atmosphériques ou à la lumiére ar-
passe à travers des éléments filtrants. Les différents
tificielle.
types d’éléments filtrants utilisés en pratique doivent
P/as tiques - M&hodes avoir, pour des longueurs d’onde données, les fac-
I SO 4892-l : 1994,
teurs spectraux de transmission prescrites dans le
d’exposition à des sources lumineuses de laboratoire
tableau 1.
- Partie 1: Guide général.
1
---------------------- Page: 3 ----------------------
0 ISO
ISO 4892-4: 1994(F)
Des renseignements sur les différents types de filtres
4.3 Radiomètre
en verre sont donnes dans l’annexe B.
Si un radiometre est utilisé, il doit répondre aux pres-
Les électrodes en carbone doivent être remplacées
criptions de I’ISO 4892-l :1994, paragraphe 5.2.
conformément aux instructions du fabricant.
4.4 Thermomètre à étalon noir@ panneau
Les caractéristiques des filtres en service sont sus-
noir
ceptibles de changer en raison du vieillissement et de
la formation de dépôts et, de ce fait, ils doivent être
Le thermomètre à étalon noir ou a panneau noir utilisé
remplaces a intervalles appropriés (voir 7.2.2).
doit répondre aux prescriptions de I’ISO 4892-l :1994,
paragraphe 5.1.5.
4.5 Instruments de mesure de l’humidité
4.2 Enceinte d’essai (voir également
relative
annexe B)
L’humidité relative de l’air passant sur les éprouvettes
L’enceinte d’essai renferme un châssis porte-
doit être régulée a une valeur convenue, si néces-
éprouvettes permettant le passage de l’air sur les
saire, et mesurée au moyen d’instruments appropries
éprouvettes pour le contrôle de la température.
introduits dans l’enceinte d’essai et protégés du
rayonnement de la lampe.
Le châssis a un diamètre de 96 cm et tourne autour
d’un axe central passant par le centre du mecanisme
4.6 Système d’arrosage à l’eau
qui supporte l’arc au carbone. D’autres diamètres
peuvent être utilisés par accord entre les parties inté-
4.6.1 L’enceinte d’essai doit renfermer un circuit
ressées.
d’eau doté de buses destinées a produire un arrosage
Le châssis doit supporter directement les éprouvettes uniformément réparti a la demande. Le circuit doit
sous forme de panneaux et/ou par l’intermédiaire des être realisé en acier inoxydable, en plastique ou tout
porte-éprouvettes assujettis au châssis. Ce dernier
autre matériau qui ni ne réagit avec l’eau qui le par-
peut être vertical ou incliné.
court, ni ne la contamine.
L’électrode supérieure et l’électrode inférieure ainsi
NOTE 1 II peut s’avérer nécessaire d’utiliser des filtres
que le (ou les) filtre(s) doivent être installés confor- et des déminéraliseurs appropriés avec le système d’arro-
sage pour répondre aux prescriptions de pureté de l’eau.
mément aux instructions du constructeur de I’appa-
reillage.
d’arrosage doit assurer un
4.6.2 Le système
L’appareillage doit être doté d’un moyen permettant mouillage uniforme et un refroidissement rapide.
de programmer les cycles d’exposition dans ses limi- L’eau pulvérisée doit évacuer librement la surface ar-
tes de fonctionnement. rosée.
Tableau 1 - Facteur spectral de transmission à l’état neuf, de filtres en verre pour des longueurs d’onde
données
Type 3
Type 1 Type 2
Facteur spectral
Facteur spectral Facteur spectral
Longueur d’onde Longueur d’onde Longueur d’onde
de transmission
de transmission de transmission
nm %
nm % nm %
L
295
255 275 d
0 G2
302 71 à 86 320 65 à 80 320 > 40
3 360 > 91 400 à 700 > 90 400 à 700 > 90
.
2
---------------------- Page: 4 ----------------------
0 ISO
ISO 4892-4: 1994(F)
4.6.3 Les éprouvettes peuvent être arrosées avec température choisie doit être mentionnée dans le
de l’eau distillee ou déminéralisée (ayant une con- rapport d’exposition.
.
ductivité inférieure à 5 @m), de manière intermit-
En cas d’arrosage à l’eau, la prescription de tempéra-
tente et dans des conditions prescrites. L’eau utilisée
ture est applicable à la fin de la période de séchage.
ne doit laisser ni dépôt gênant ni tache visible sur les
éprouvettes et, dans ce but, devrait contenir moins
de 1 ppm de matiere solide. En plus de la distillation,
6.2 Humidité relative
une combinaison de traitements de déionisation et
Sauf prescription contraire, l’humidité relative doit être
d’osmose inverse peut efficacement produire de l’eau
de la qualité requise. Le pH de l’eau utilisée doit être de (50 + 5) %.
mentionné dans le rapport d’essai.
NOTE 2 L’humidité relative de l’air mesurée dans I’en-
ceinte d’essai n’est pas nécessairement équivalente à la
4.6.4 Un système d’arrosage conçu pour assurer le
teneur de l’air en humidité à proximité immédiate de la
refroidissement de l’éprouvette par arrosage de la
surface de l’éprouvette, en raison du fait que des éprou-
surface arrière ou du support de l’éprouvette peut être
vettes de couleur et d’épaisseur différentes n’ont pas la
exige lorsque le programme d’exposition prescrit des
même température.
périodes de condensation.
6.3 Cycle d’arrosage
4.7 Porte-éprouvettes
...
NORME ISO
INTERNATIONALE 4892-4
Premihe édition
1994-05-01
- Méthodes d’exposition à des
Plastiques
sources lumineuses de laboratoire -
Partie 4:
Lampes à arc au carbone
P/as tics - Methods of exposure to laboratory light sources -
Part 4: Open-flame carbon-arc lamps
Numéro de référence
ISO 4892-4: 1994(F)
---------------------- Page: 1 ----------------------
ISO 4892-4: 1994(F)
Avant-propos
L’ISO (Organisation internationale de normalisation) est une féderation
mondiale d’organismes nationaux de normalisation (comités membres de
I’ISO). L’élaboration des Normes internationales est en général confiée aux
comités techniques de I’ISO. Chaque comite membre intéressé par une
étude a le droit de faire partie du comite technique creé a cet effet. Les
organisations internationales, gouvernementales et non gouvernemen-
tales, en liaison avec I’ISO participent également aux travaux. L’ISO colla-
bore étroitement avec la Commission électrotechnique internationale (CEI)
en ce qui concerne la normalisation électrotechnique.
Les projets de Normes internationales adoptés par les comités techniques
sont soumis aux comités membres pour vote. Leur publication comme
Normes internationales requiert l’approbation de 75 % au moins des co-
mités membres votants.
La Norme internationale ISO 4892-4 a été élaborée par le comité techni-
que lSO/TC 61, Plastiques, sous-comité SC 6, Vieillissement et résistance
aux agents chimiques et environnants.
Conjointement avec les autres parties de I’ISO 4892, elle annule et rem-
place la Norme internationale ISO 4892:1981, dont elle constitue une ré-
vision technique.
L’ISO 4892 comprend les parties suivantes, présentées sous le titre gé-
néral Plastiques - M&hodes d’exposition à des sources lumineuses de
laboratoire:
- Partie 1: Guide général
- Partie 2: Sources à arc au x&on
- Partie 3: Lampes fluorescentes UV
- Partie 4: Lampes à arc au carbone
L’annexe A fait partie intégrante de la présente partie de I’ISO 4892. Les
annexes B et C sont données uniquement a titre d’information.
0 60 1994
Droits de reproduction réservés. Sauf prescription différente, aucune partie de cette publi-
cation ne peut être reproduite ni utilisee sous quelque forme que ce soit et par aucun pro-
cédé, électronique ou mécanique, y compris la photocopie et les microfilms, sans l’accord
écrit de l’editeur.
Organisation internationale de normalisation
Case Postale 56 l CH-l 211 Genéve 20 l Suisse
Imprimé en Suisse
ii
---------------------- Page: 2 ----------------------
ISO 4892-4: 1994(F)
NORME INTERNATIONALE 0 ISO
- Méthodes d’exposition à des sources
Plastiques
lumineuses de laboratoire -
Partie 4:
Lampes à arc au carbone
3 Principe
1 Domaine d’application
La présente partie de I’ISO 4892 prescrit une mé-
3.1 Les éprouvettes des échantillons à essayer sont
thode pour l’exposition d’éprouvettes à des lampes à
exposées a une source de lumiere à arc au carbone
arc au carbone. L’ISO 4892-l donne des recomman-
dans des conditions d’environnement contrôlées.
dations générales.
3.2 Le mode opératoire peut comprendre le mesu-
rage de l’éclairement énergétique et de l’exposition
énergétique sur la surface de l’éprouvette.
3.3 II est conseillé d’exposer, en même temps que
le matériau a essayer, un matériau similaire dont le
2 Références normatives
comportement est connu.
Les normes suivantes contiennent des dispositions
3.4 La comparaison des résultats obtenus avec des
qui, par suite de la référence qui en est faite, consti-
éprouvettes exposées en différents appareils ne de-
tuent des dispositions valables pour la présente partie
vrait pas être faite si la reproductibilité entre les ap-
de I’ISO 4892. Au moment de la publication, les édi-
pareils n’a pas été établie pour le matériau a essayer.
tions indiquées étaient en vigueur. Toute norme est
sujette à révision et les parties prenantes des accords
fondés sur la présente partie de I’ISO 4892 sont invi-
4 Appareillage
tées à rechercher la possibilité d’appliquer les éditions
les plus récentes des normes indiquées ci-aprés. Les
4.1 Source lumineuse de laboratoire
membres de la CEI et de I’ISO possédent le registre
des Normes internationales en vigueur a un moment
4.1.1 La lampe se compose d’un arc formé a l’air li-
donné.
bre entre des électrodes cylindriques en carbone. La
spécification de la source lumineuse est donnée dans
ISO 4582:1980, Plastiques - Ddtermination des
l’annexe A.
changements de coloration et des variations de pro-
priétés après exposition à la lumière naturelle sous
4.1.2 Le rayonnement qui atteint les éprouvettes
verre, aux agents atmosphériques ou à la lumiére ar-
passe à travers des éléments filtrants. Les différents
tificielle.
types d’éléments filtrants utilisés en pratique doivent
P/as tiques - M&hodes avoir, pour des longueurs d’onde données, les fac-
I SO 4892-l : 1994,
teurs spectraux de transmission prescrites dans le
d’exposition à des sources lumineuses de laboratoire
tableau 1.
- Partie 1: Guide général.
1
---------------------- Page: 3 ----------------------
0 ISO
ISO 4892-4: 1994(F)
Des renseignements sur les différents types de filtres
4.3 Radiomètre
en verre sont donnes dans l’annexe B.
Si un radiometre est utilisé, il doit répondre aux pres-
Les électrodes en carbone doivent être remplacées
criptions de I’ISO 4892-l :1994, paragraphe 5.2.
conformément aux instructions du fabricant.
4.4 Thermomètre à étalon noir@ panneau
Les caractéristiques des filtres en service sont sus-
noir
ceptibles de changer en raison du vieillissement et de
la formation de dépôts et, de ce fait, ils doivent être
Le thermomètre à étalon noir ou a panneau noir utilisé
remplaces a intervalles appropriés (voir 7.2.2).
doit répondre aux prescriptions de I’ISO 4892-l :1994,
paragraphe 5.1.5.
4.5 Instruments de mesure de l’humidité
4.2 Enceinte d’essai (voir également
relative
annexe B)
L’humidité relative de l’air passant sur les éprouvettes
L’enceinte d’essai renferme un châssis porte-
doit être régulée a une valeur convenue, si néces-
éprouvettes permettant le passage de l’air sur les
saire, et mesurée au moyen d’instruments appropries
éprouvettes pour le contrôle de la température.
introduits dans l’enceinte d’essai et protégés du
rayonnement de la lampe.
Le châssis a un diamètre de 96 cm et tourne autour
d’un axe central passant par le centre du mecanisme
4.6 Système d’arrosage à l’eau
qui supporte l’arc au carbone. D’autres diamètres
peuvent être utilisés par accord entre les parties inté-
4.6.1 L’enceinte d’essai doit renfermer un circuit
ressées.
d’eau doté de buses destinées a produire un arrosage
Le châssis doit supporter directement les éprouvettes uniformément réparti a la demande. Le circuit doit
sous forme de panneaux et/ou par l’intermédiaire des être realisé en acier inoxydable, en plastique ou tout
porte-éprouvettes assujettis au châssis. Ce dernier
autre matériau qui ni ne réagit avec l’eau qui le par-
peut être vertical ou incliné.
court, ni ne la contamine.
L’électrode supérieure et l’électrode inférieure ainsi
NOTE 1 II peut s’avérer nécessaire d’utiliser des filtres
que le (ou les) filtre(s) doivent être installés confor- et des déminéraliseurs appropriés avec le système d’arro-
sage pour répondre aux prescriptions de pureté de l’eau.
mément aux instructions du constructeur de I’appa-
reillage.
d’arrosage doit assurer un
4.6.2 Le système
L’appareillage doit être doté d’un moyen permettant mouillage uniforme et un refroidissement rapide.
de programmer les cycles d’exposition dans ses limi- L’eau pulvérisée doit évacuer librement la surface ar-
tes de fonctionnement. rosée.
Tableau 1 - Facteur spectral de transmission à l’état neuf, de filtres en verre pour des longueurs d’onde
données
Type 3
Type 1 Type 2
Facteur spectral
Facteur spectral Facteur spectral
Longueur d’onde Longueur d’onde Longueur d’onde
de transmission
de transmission de transmission
nm %
nm % nm %
L
295
255 275 d
0 G2
302 71 à 86 320 65 à 80 320 > 40
3 360 > 91 400 à 700 > 90 400 à 700 > 90
.
2
---------------------- Page: 4 ----------------------
0 ISO
ISO 4892-4: 1994(F)
4.6.3 Les éprouvettes peuvent être arrosées avec température choisie doit être mentionnée dans le
de l’eau distillee ou déminéralisée (ayant une con- rapport d’exposition.
.
ductivité inférieure à 5 @m), de manière intermit-
En cas d’arrosage à l’eau, la prescription de tempéra-
tente et dans des conditions prescrites. L’eau utilisée
ture est applicable à la fin de la période de séchage.
ne doit laisser ni dépôt gênant ni tache visible sur les
éprouvettes et, dans ce but, devrait contenir moins
de 1 ppm de matiere solide. En plus de la distillation,
6.2 Humidité relative
une combinaison de traitements de déionisation et
Sauf prescription contraire, l’humidité relative doit être
d’osmose inverse peut efficacement produire de l’eau
de la qualité requise. Le pH de l’eau utilisée doit être de (50 + 5) %.
mentionné dans le rapport d’essai.
NOTE 2 L’humidité relative de l’air mesurée dans I’en-
ceinte d’essai n’est pas nécessairement équivalente à la
4.6.4 Un système d’arrosage conçu pour assurer le
teneur de l’air en humidité à proximité immédiate de la
refroidissement de l’éprouvette par arrosage de la
surface de l’éprouvette, en raison du fait que des éprou-
surface arrière ou du support de l’éprouvette peut être
vettes de couleur et d’épaisseur différentes n’ont pas la
exige lorsque le programme d’exposition prescrit des
même température.
périodes de condensation.
6.3 Cycle d’arrosage
4.7 Porte-éprouvettes
...
Questions, Comments and Discussion