ISO 6272-1:2002

Paints and varnishes — Rapid-deformation (impact resistance) tests — Part 1: Falling-weight test, large-area indenter

ISO 6272-1:2002 describes a method for evaluating the resistance of a dry film of paint, varnish or related product to cracking or peeling from a substrate when it is subjected to a deformation caused by a falling weight, with a 20-mm-diameter spherical indenter, dropped under standard conditions. The method described can be applied either as a pass/fail test, the test being carried out from one drop height and with a specified mass, so as to test compliance with a particular specification; or as a classification test, to determine the minimum mass and/or drop height for which the coating cracks or peels from its substrate by gradually increasing the drop height and/or the mass.

Peintures et vernis — Essais de déformation rapide (résistance au choc) — Partie 1: Essai de chute d'une masse avec pénétrateur de surface importante

L'ISO 6272 décrit une méthode permettant d'évaluer la résistance d'un feuil sec de peinture, vernis ou produit assimilé au craquelage ou au décollement de son subjectile lorsque celui-ci est soumis à une déformation provoquée par une masse tombante avec un pénétrateur sphérique de 20 mm de diamètre, lâchée dans des conditions normalisées. La méthode est applicable soit en essai tout ou rien, l'essai étant réalisé avec une hauteur de chute et une masse données afin de vérifier la conformité à une spécification particulière, soit en essai de classement, afin de déterminer la masse minimale et/ou la hauteur de chute pour lesquelles le revêtement se craquelle ou se décolle de son subjectile, l'essai étant réalisé en augmentant progressivement la hauteur de chute et/ou la masse.

General Information

• Status: Withdrawn
• Publication Date: 07-Aug-2002
• Withdrawal Date: 07-Aug-2002
• ICS: 87.040 - Paints and varnishes
• Technical Committee: ISO/TC 35/SC 9 - General test methods for paints and varnishes
• Drafting Committee: ISO/TC 35/SC 9 - General test methods for paints and varnishes
• Current Stage: 9599 - Withdrawal of International Standard
• Completion Date: 09-Aug-2011

Relations

• Revised: ISO 6272-1:2011 - Paints and varnishes — Rapid-deformation (impact resistance) tests — Part 1: Falling-weight test, large-area indenter
• Effective Date: 20-Jun-2008
• Revises: ISO 6272:1993 - Paints and varnishes — Falling-weight test
• Effective Date: 15-Apr-2008

Standards Content (Sample)

INTERNATIONAL ISO
STANDARD 6272-1
First edition
2002-07-01
Paints and varnishes — Rapid-deformation
(impact resistance) tests —
Part 1:
Falling-weight test, large-area indenter
Peintures et vernis — Essais de déformation rapide (résistance au choc) —
Partie 1: Essai de chute d'une masse avec pénétrateur de surface
importante

Reference number
ISO 6272-1:2002(E)
©
ISO 2002

---------------------- Page: 1 ----------------------
ISO 6272-1:2002(E)
PDF disclaimer
This PDF file may contain embedded typefaces. In accordance with Adobe's licensing policy, this file may be printed or viewed but shall not be
edited unless the typefaces which are embedded are licensed to and installed on the computer performing the editing. In downloading this file,
parties accept therein the responsibility of not infringing Adobe's licensing policy. The ISO Central Secretariat accepts no liability in this area.
Adobe is a trademark of Adobe Systems Incorporated.
Details of the software products used to create this PDF file can be found in the General Info relative to the file; the PDF-creation parameters
were optimized for printing. Every care has been taken to ensure that the file is suitable for use by ISO member bodies. In the unlikely event
that a problem relating to it is found, please inform the Central Secretariat at the address given below.
© ISO 2002
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means,
electronic or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address below or ISO's
member body in the country of the requester.
ISO copyright office
Case postale 56  CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail [e-mail]
Web www.iso.ch
Printed in Switzerland
©
ii ISO 2002 – All rights reserved

---------------------- Page: 2 ----------------------
ISO 6272-1:2002(E)
Contents Page
1 Scope . 1
2 Normative references . 1
3 Required supplementary information . 2
4 Apparatus . 2
5 Sampling . 2
6 Test panels . 4
7 Procedure . 5
8 Precision . 6
9 Test report . 6
Annex
A Required supplementary information. 7
©
ISO 2002 – All rights reserved iii

---------------------- Page: 3 ----------------------
ISO 6272-1:2002(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO
member bodies). The work of preparing International Standards is normally carried out through ISO technical
committees. Each member body interested in a subject for which a technical committee has been established has
the right to be represented on that committee. International organizations, governmental and non-governmental, in
liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical
Commission (IEC) on all matters of electrotechnical standardization.
International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 3.
Draft International Standards adopted by the technical committees are circulated to the member bodies for voting.
Publication as an International Standard requires approval by at least 75 % of the member bodies casting a vote.
Attention is drawn to the possibility that some of the elements of this part of ISO 6272 may be the subject of patent
rights. ISO shall not be held responsible for identifying any or all such patent rights.
International Standard ISO6272-1 was prepared by Technical Committee ISO/TC35, Paints and varnishes,
Subcommittee SC 9, General test methods for paints and varnishes.
Together with ISO 6272-2, this part of ISO 6272 cancels and replaces ISO 6272:1993. The main change is the
introduction of the option to increase the mass of the weight that is dropped onto the panel, thus enabling a more
severe test to be carried out.
ISO 6272 consists of the following parts, under the general title Paints and varnishes — Rapid-deformation (impact
resistance) tests:
— Part 1: Falling-weight test, large-area indenter
— Part 2: Falling-weight test, small-area indenter
Annex A forms a normative part of this part of ISO 6272.
©
iv ISO 2002 – All rights reserved

---------------------- Page: 4 ----------------------
INTERNATIONAL STANDARD ISO 6272-1:2002(E)
Paints and varnishes — Rapid-deformation (impact resistance)
tests —
Part 1:
Falling-weight test, large-area indenter
WARNING — This part of ISO 6272 does not purport to address the all of the safety problems, if any,
associated with its use. It is the responsibility of the user of this part of ISO 6272 to establish appropriate
safety and health practices and determine the applicability of regulatory limitations prior to use.
1 Scope
This part of ISO 6272 describes a method for evaluating the resistance of a dry film of paint, varnish or related
product to cracking or peeling from a substrate when it is subjected to a deformation caused by a falling weight, with
a 20-mm-diameter spherical indenter, dropped under standard conditions.
NOTE The term “impact resistance” is included in the title of this part of ISO 6272, but one important characteristic of the
apparatus used is that it should produce rapid deformation rather than a true impact.
The method described can be applied
— either as a pass/fail test, the test being carried out from one drop height and with a specified mass, so as to test
compliance with a particular specification;
— or as a classification test, to determine the minimum mass and/or drop height for which the coating cracks or
peels from its substrate by gradually increasing the drop height and/or the mass.
2 Normative references
The following normative documents contain provisions which, through reference in this text, constitute provisions of
this part of ISO 6272. For dated references, subsequent amendments to, or revisions of, any of these publications do
not apply. However, parties to agreements based on this part of ISO 6272 are encouraged to investigate the
possibility of applying the most recent editions of the normative documents indicated below. For undated references,
the latest edition of the normative document referred to applies. Members of ISO and IEC maintain registers of
currently valid International Standards.
ISO 1513, Paints and varnishes — Examination and preparation of samples for testing
ISO 1514, Paints and varnishes — Standard panels for testing
ISO 2808, Paints and varnishes — Determination of film thickness
ISO 3270, Paints and varnishes and their raw materials — Temperatures and humidities for conditioning and testing
ISO 15528, Paints, varnishes and raw materials for paints and varnishes — Sampling
©
ISO 2002 – All rights reserved 1

---------------------- Page: 5 ----------------------
ISO 6272-1:2002(E)
3 Required supplementary information
For any particular application, the test method specified in this part of ISO 6272 needs to be completed by
supplementary information. The items of supplementary information are given in annex A.
4 Apparatus
Ordinary laboratory apparatus and glassware, together with the following:
4.1 Falling-weight apparatus, comprising the elements described in 4.1.1 to 4.1.7.
4.1.1 Base stand, of sufficient mass to support the die (4.1.5).
4.1.2 Primary falling weight (see Figure 1), the head having the shape of a spherical segment of diameter
(20± 0,3) mm, and a total mass of (1 000± 1) g.
4.1.3 Secondary weight(s), which may be added to the primary falling weight in order to increase the severity of
the test. The mass of each weight may be (1 000± 1) g or (2 000± 2) g, and the total load may be 1 kg, 2 kg, 3 kg
or .4kg
4.1.4 Vertical guide tube (see Figures 1 and 2), to direct the primary falling weight (4.1.2) perpendicularly on to the
test panel. The guide tube shall be graduated in millimetres to indicate the distance above the surface of the test
panel.
To avoid excessive friction and to ensure ac
...

NORME ISO
INTERNATIONALE 6272-1
Première édition
2002-07-01
Peintures et vernis — Essais de
déformation rapide (résistance au choc) —
Partie 1:
Essai de chute d'une masse avec
pénétrateur de surface importante
Paints and varnishes — Rapid-deformation (impact resistance) tests —
Part 1: Falling-weight test, large-area indenter

Numéro de référence
ISO 6272-1:2002(F)
©
ISO 2002

---------------------- Page: 1 ----------------------
ISO 6272-1:2002(F)
PDF — Exonération de responsabilité
Le présent fichier PDF peut contenir des polices de caractères intégrées. Conformément aux conditions de licence d'Adobe, ce fichier peut
être imprimé ou visualisé, mais ne doit pas être modifié à moins que l'ordinateur employé à cet effet ne bénéficie d'une licence autorisant
l'utilisation de ces polices et que celles-ci y soient installées. Lors du téléchargement de ce fichier, les parties concernées acceptent de fait la
responsabilité de ne pas enfreindre les conditions de licence d'Adobe. Le Secrétariat central de l'ISO décline toute responsabilité en la
matière.
Adobe est une marque déposée d'Adobe Systems Incorporated.
Les détails relatifs aux produits logiciels utilisés pour la création du présent fichier PDF sont disponibles dans la rubrique General Info du
fichier; les paramètres de création PDF ont été optimisés pour l'impression. Toutes les mesures ont été prises pour garantir l'exploitation de
ce fichier par les comités membres de l'ISO. Dans le cas peu probable où surviendrait un problème d'utilisation, veuillez en informer le
Secrétariat central à l'adresse donnée ci-dessous.
© ISO 2002
Droits de reproduction réservés. Sauf prescription différente, aucune partie de cette publication ne peut être reproduite ni utilisée sous
quelque forme que ce soit et par aucun procédé, électronique ou mécanique, y compris la photocopie et les microfilms, sans l'accord écrit de
l'ISO à l'adresse ci-après ou au comité membre de l'ISO dans le pays du demandeur.
ISO copyright office
Case postale 56  CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail [e-mail]
Web www.iso.ch
Imprimé en Suisse
©
ii ISO 2002 – Tous droits réservés

---------------------- Page: 2 ----------------------
ISO 6272-1:2002(F)
Sommaire Page
1 Domaine d'application . 1
2 Références normatives . 1
3 Informations supplémentaires requises . 2
4 Appareillage . 2
5 Échantillonnage . 2
6 Panneaux d'essai . 4
7 Mode opératoire . 5
8 Fidélité . 6
9 Rapport d'essai . 6
Annexe
A Informations supplémentaires requises . 7
©
ISO 2002 – Tous droits réservés iii

---------------------- Page: 3 ----------------------
ISO 6272-1:2002(F)
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes nationaux de
normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est en général confiée aux
comités techniques de l'ISO. Chaque comité membre intéressé par une étude a le droit de faire partie du comité
technique créé à cet effet. Les organisations internationales, gouvernementales et non gouvernementales, en liaison
avec l'ISO participent également aux travaux. L'ISO collabore étroitement avec la Commission électrotechnique
internationale (CEI) en ce qui concerne la normalisation électrotechnique.
Les Normes internationales sont rédigées conformément aux règles données dans les Directives ISO/CEI, Partie 3.
Les projets de Normes internationales adoptés par les comités techniques sont soumis aux comités membres pour
vote. Leur publication comme Normes internationales requiert l'approbation de 75 % au moins des comités membres
votants.
L'attention est appelée sur le fait que certains des éléments de la présente partie de l'ISO 6272 peuvent faire l'objet
de droits de propriété intellectuelle ou de droits analogues. L'ISO ne saurait être tenue pour responsable de ne pas
avoir identifié de tels droits de propriété et averti de leur existence.
La Norme internationale ISO 6272-1 a été élaborée par le comité technique ISO/TC 35, Peintures et vernis, sous-
comité SC 9, Méthodes générales d'essais des peintures et vernis.
Avec l’ISO 6272-2, la présente partie de l’ISO 6272 annule et remplace l’ISO 6272:1993. La principale modification
réside dans la possibilité d’augmenter la masse du poids que l’on fait tomber sur le panneau, ce qui permet d’obtenir
des conditions d’essai plus dures.
L'ISO 6272 comprend les parties suivantes, présentées sous le titre général Peintures et vernis — Essais de
déformation rapide (résistance au choc):
— Partie 1: Essai de chute d'une masse avec pénétrateur de surface importante
— Partie 2: Essai de chute d'une masse avec pénétrateur de surface réduite
L'annexe A constitue un élément normatif de la présente partie de l'ISO 6272.
©
iv ISO 2002 – Tous droits réservés

---------------------- Page: 4 ----------------------
NORME INTERNATIONALE ISO 6272-1:2002(F)
Peintures et vernis — Essais de déformation rapide (résistance au
choc) —
Partie 1:
Essai de chute d'une masse avec pénétrateur de surface
importante
AVERTISSEMENT — La présente partie de l'ISO 6272 n'est pas censée aborder tous les problèmes de
sécurité qui sont, le cas échéant, liés à son utilisation. Il incombe à l'utilisateur de la présente partie de
l'ISO 6272 d'établir des pratiques appropriées en matière d'hygiène et de sécurité, et de s'assurer du respect
de la réglementation nationale en vigueur.
1 Domaine d'application
La présente partie de l'ISO 6272 décrit une méthode permettant d'évaluer la résistance d'un feuil sec de peinture,
vernis ou produit assimilé au craquelage ou au décollement de son subjectile lorsque celui-ci est soumis à une
déformation provoquée par une masse tombante avec un pénétrateur sphérique de 20 mm de diamètre, lâchée dans
des conditions normalisées.
NOTE Le terme «résistance au choc» est inclus dans le titre de la présente partie de l'ISO 6272, mais une caractéristique
importante de l'appareil utilisé est de produire une déformation rapide plutôt qu'un choc véritable.
La méthode est applicable
— soit en essai tout ou rien, l'essai étant réalisé avec une hauteur de chute et une masse données afin de vérifier
la conformité à une spécification particulière,
— soit en essai de classement, afin de déterminer la masse minimale et/ou la hauteur de chute pour lesquelles le
revêtement se craquelle ou se décolle de son subjectile, l'essai étant réalisé en augmentant progressivement la
hauteur de chute et/ou la masse.
2Références normatives
Les documents normatifs suivants contiennent des dispositions qui, par suite de la référence qui y est faite,
constituent des dispositions valables pour la présente partie de l'ISO6272. Pour les références datées, les
amendements ultérieurs ou les révisions de ces publications ne s'appliquent pas. Toutefois, les parties prenantes
aux accords fondés sur la présente partie de l'ISO 6272 sont invitées à rechercher la possibilité d'appliquer les
éditions les plus récentes des documents normatifs indiqués ci-après. Pour les références non datées, la dernière
édition du document normatif en référence s'applique. Les membres de l'ISO et de la CEI possèdent le registre des
Normes internationales en vigueur.
ISO 1513, Peintures et vernis — Examen et préparation des échantillons pour essais
ISO 1514, Peintures et vernis — Panneaux normalisés pour essais
ISO 2808, Peintures et vernis — Détermination de l'épaisseur du feuil
ISO 3270, Peintures et vernis et leurs matières premières — Températures et humidités pour le conditionnement et
l'essai
©
ISO 2002 – Tous droits réservés 1

---------------------- Page: 5 ----------------------
ISO 6272-1:2002(F)
ISO 15528, Peintures, vernis et matières premières pour peintures et vernis — Échantillonnage
3 Informations supplémentaires requises
Pour toute application particulière, la méthode d'essai spécifiée dans la présente partie de l'ISO 6272 doit être
complétée par des informations supplémentaires. Celles-ci figurent en annexe A.
4 Appareillage
Verrerie et matériel courant de laboratoire, et:
4.1 Appareil à chute de masse, comprenant les éléments décrits de 4.1.1 à 4.1.7.
4.1.1 Plaque de base, d'une masse suffisante pour supporter la matrice (4.1.5).
4.1.2 Masse tombante primaire (voir Figure 1), dont la tête est en forme de calotte sphérique d'un diamètre de
(20± 0,3) mm et d'une masse totale de (1 000± 1) g.
4.1.3 Masse(s) secondaire(s) qui peuvent être ajoutées à la masse tombante primaire pour obtenir des conditions
d'essai plus dures. La masse de chaque masse peut être de (1 000± 1) g ou de (2 000± 2) g et la charge totale
peut être de , , 1kg 2kg 3kgou .4kg
4.1.4 Tube-guide vertical (voir Figures 1 et 2) servant à guider la masse tombante (4.1.2) perpendiculairement au
panneau d'essai. Le tube-guide doit être gradué en millimètres pour indiquer la distance au dessus de la surface du
panneau d'essai.
Afin d'éviter toute friction excessive et pour assurer un guidage précis, la différence entre le rayon intérieur du tube-
guide et
...