ISO 636:2015
(Main)Welding consumables — Rods, wires and deposits for tungsten inert gas welding of non-alloy and fine-grain steels — Classification
Welding consumables — Rods, wires and deposits for tungsten inert gas welding of non-alloy and fine-grain steels — Classification
ISO 636:2015 specifies requirements for classification of rods and wires in the as-welded condition and in the post-weld heat-treated condition for tungsten inert gas welding of non-alloy and fine-grain steels with a minimum yield strength of up to 500 MPa or a minimum tensile strength of up to 570 MPa. This International Standard is a combined specification providing classification utilizing a system based upon the yield strength and the average impact energy of 47 J of all-weld metal or utilizing a system based upon the tensile strength and the average impact energy of 27 J of all-weld metal. a) Paragraphs and tables which carry the suffix letter "A" are applicable only to rods and wires classified to the system based upon the yield strength and the average impact energy of 47 J of all-weld metal in accordance with this International Standard. b) Paragraphs and tables which carry the suffix letter "B" are applicable only to rods and wires classified to the system based upon the tensile strength and the average impact energy of 27 J of all-weld metal in accordance with this International Standard. c) Paragraphs and tables which have neither the suffix letter "A" nor the suffix letter "B" are applicable to all rods and wires classified in accordance with this International Standard.
Produits consommables pour le soudage — Baguettes et fils pour dépôts par soudage TIG des aciers non alliés et des aciers à grains fins — Classification
ISO 636:2015 spécifie les exigences relatives à la classification des baguettes et des fils à l'état brut de soudage et à l'état traité thermiquement après soudage, en soudage TIG (soudage à l'arc sous protection de gaz inerte avec électrode de tungstène) des aciers non alliés et des aciers à grains fins ayant une limite d'élasticité minimale pouvant atteindre 500 MPa ou une résistance à la traction minimale pouvant atteindre 570 MPa. La présente Norme internationale propose une spécification mixte permettant une classification utilisant un système fondé soit sur la limite d'élasticité et l'énergie de rupture moyenne de 47 J pour le métal fondu hors dilution, soit sur la résistance à la traction et l'énergie de rupture moyenne de 27 J pour le métal fondu hors dilution. Les paragraphes et les tableaux qui portent le suffixe «A» ne sont applicables qu'aux baguettes et fils classifiés d'après le système basé sur la limite d'élasticité et l'énergie de rupture moyenne de 47 J pour le métal fondu hors dilution conformément à la présente Norme internationale. Les paragraphes et les tableaux qui portent le suffixe «B» ne sont applicables qu'aux baguettes et fils classifiés d'après le système basé sur la résistance à la traction et l'énergie de rupture moyenne de 27 J pour le métal fondu hors dilution conformément à la présente Norme internationale. Les paragraphes et les tableaux ne comportant ni le suffixe «A» ni le suffixe «B» sont applicables à toutes les baguettes et à tous les fils classifiés conformément à la présente Norme internationale.
General Information
Relations
Buy Standard
Standards Content (Sample)
INTERNATIONAL ISO
STANDARD 636
Fourth edition
2015-11-15
Welding consumables — Rods, wires
and deposits for tungsten inert gas
welding of non-alloy and fine-grain
steels — Classification
Produits consommables pour le soudage — Baguettes et fils pour
dépôts par soudage TIG des aciers non alliés et des aciers à grains fins
— Classification
Reference number
ISO 636:2015(E)
©
ISO 2015
---------------------- Page: 1 ----------------------
ISO 636:2015(E)
COPYRIGHT PROTECTED DOCUMENT
© ISO 2015, Published in Switzerland
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized otherwise in any form
or by any means, electronic or mechanical, including photocopying, or posting on the internet or an intranet, without prior
written permission. Permission can be requested from either ISO at the address below or ISO’s member body in the country of
the requester.
ISO copyright office
Ch. de Blandonnet 8 • CP 401
CH-1214 Vernier, Geneva, Switzerland
Tel. +41 22 749 01 11
Fax +41 22 749 09 47
copyright@iso.org
www.iso.org
ii © ISO 2015 – All rights reserved
---------------------- Page: 2 ----------------------
ISO 636:2015(E)
Contents Page
Foreword .iv
Introduction .v
1 Scope . 1
2 Normative references . 1
3 Classification . 1
4 Symbols and requirements . 2
4.1 Symbol for the product/process . 2
4.2 Symbol for strength and elongation of all-weld metal . 3
4.3 Symbol for impact properties of all-weld metal . 4
4.4 Symbol for the chemical composition of rods or wires . 4
5 Mechanical tests . 9
5.1 Preheating and interpass temperatures . 9
5.2 Welding conditions and pass sequence .10
5.3 PWHT condition .10
6 Chemical analysis .10
7 Rounding procedure .11
8 Retests .11
9 Technical delivery conditions .11
10 Designation .11
© ISO 2015 – All rights reserved iii
---------------------- Page: 3 ----------------------
ISO 636:2015(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www.iso.org/directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www.iso.org/patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation on the meaning of ISO specific terms and expressions related to conformity
assessment, as well as information about ISO’s adherence to the WTO principles in the Technical
Barriers to Trade (TBT) see the following URL: Foreword - Supplementary information
The committee responsible for this document is ISO/TC 44, Welding and allied processes, Subcommittee
SC 3, Welding consumables.
This fourth edition cancels and replaces the third edition (ISO 636:2004), which has been
technically revised.
Requests for official interpretations of any aspect of this International Standard should be directed to
the Secretariat of ISO/TC 44/SC 3, through your national standards body, a complete listing of which
can be found at www.iso.org.
iv © ISO 2015 – All rights reserved
---------------------- Page: 4 ----------------------
ISO 636:2015(E)
Introduction
This International Standard provides a classification for the designation of rods and wires in terms of
their chemical composition and, where required, in terms of the yield strength, tensile strength, and
elongation of the all-weld metal. The ratio of yield to tensile strength of weld metal is generally higher
than that of parent metal. Matching weld metal yield strength to parent metal yield strength will not
necessarily ensure that the weld metal tensile strength matches that of the parent material. Where
the application requires matching tensile strengths, selection of consumables is made by reference to
column 3 of Table 1A or Table 1B.
Of note is that the mechanical properties of all-weld metal test specimens used to classify the rods and
wires vary from those obtained in production joints because of differences in welding procedure such
as diameter, width of weave, welding position, and material composition.
The classification according to system A is mainly based on EN 1668:1997. The classification according
to system B is mainly based upon standards used around the Pacific Rim.
© ISO 2015 – All rights reserved v
---------------------- Page: 5 ----------------------
INTERNATIONAL STANDARD ISO 636:2015(E)
Welding consumables — Rods, wires and deposits for
tungsten inert gas welding of non-alloy and fine-grain
steels — Classification
1 Scope
This International Standard specifies requirements for classification of rods and wires in the as-
welded condition and in the post-weld heat-treated condition for tungsten inert gas welding of non-
alloy and fine-grain steels with a minimum yield strength of up to 500 MPa or a minimum tensile
strength of up to 570 MPa.
This International Standard is a combined specification providing classification utilizing a system
based upon the yield strength and the average impact energy of 47 J of all-weld metal or utilizing a
system based upon the tensile strength and the average impact energy of 27 J of all-weld metal.
a) Paragraphs and tables which carry the suffix letter “A” are applicable only to rods and wires
classified to the system based upon the yield strength and the average impact energy of 47 J of all-
weld metal in accordance with this International Standard.
b) Paragraphs and tables which carry the suffix letter “B” are applicable only to rods and wires
classified to the system based upon the tensile strength and the average impact energy of 27 J of
all-weld metal in accordance with this International Standard.
c) Paragraphs and tables which have neither the suffix letter “A” nor the suffix letter “B” are applicable
to all rods and wires classified in accordance with this International Standard.
2 Normative references
The following documents, in whole or in part, are normatively referenced in this document and are
indispensable for its application. For dated references, only the edition cited applies. For undated
references, the latest edition of the referenced document (including any amendments) applies.
ISO 544, Welding consumables — Technical delivery conditions for filler materials and fluxes — Type of
product, dimensions, tolerances and markings
ISO 13916, Welding — Guidance on the measurement of preheating temperature, interpass temperature
and preheat maintenance temperature
ISO 14175, Welding consumables — Gases and gas mixtures for fusion welding and allied processes
ISO 14344, Welding consumables — Procurement of filler materials and fluxes
ISO 15792-1:2000, Welding consumables — Test methods — Part 1: Test methods for all-weld metal test
specimens in steel, nickel and nickel alloys. Amended by ISO 15792-1:2000/Amd 1:2011
ISO 80000-1:2009, Quantities and units — Part 1: General. Corrected by ISO 80000-1:2009/Cor 1:2011
3 Classification
Classification designations are based upon two approaches to indicate the tensile properties and the
impact properties of the all-weld metal obtained with rods or wires. The two designation approaches
include additional designators for some other classification requirements, but not all as will be
clear from the following sections. In most cases, a given commercial product can be classified to the
© ISO 2015 – All rights reserved 1
---------------------- Page: 6 ----------------------
ISO 636:2015(E)
classification requirements in both systems. Then, either or both classification designations can be
used for the product.
Rods or wires shall be classified according to their chemical composition in accordance with
Table 3A or Table 3B.
3A Classification by yield strength and 47 J 3B Classification according to alloy type
impact energy
The classification is divided into four parts. The classification is divided into four parts.
1) The first part gives a symbol indicating the 1) The first part gives a symbol indicating the
product/process to be identified. product/process to be identified.
2) The second part gives a symbol indicating 2) The second part gives a symbol indicating
the strength and elongation of the all-weld the strength and elongation of the all-weld
metal (see Table 1A). metal in either the as-welded or post-weld
heat-treated condition (see Table 1B).
3) The third part gives a symbol indicating the
impact properties of all-weld metal (see 3) The third part gives a symbol indicating
Table 2). the impact properties of all-weld metal in
the same condition as specified for the
4) The fourth part gives a symbol indicating
tensile strength (see Table 2). The letter
the chemical composition of the rods or
“U” after this designator indicates that the
wires used (see Table 3A).
deposit meets an average optional
requirement of 47 J at the designated
Charpy test temperature.
4) The fourth part gives a symbol indicating
the chemical composition of the rods or
wires used (see Table 3B).
4 Symbols and requirements
4.1 Symbol for the product/process
The symbol of weld deposit by the tungsten inert gas welding process shall be the letter “W” placed at
the beginning of the designation.
The symbol of rods or wires for the tungsten inert gas welding shall be the letter “W” placed at the
beginning of the rod or wire designation.
2 © ISO 2015 – All rights reserved
---------------------- Page: 7 ----------------------
ISO 636:2015(E)
4.2 Symbol for strength and elongation of all-weld metal
4.2A Classification by yield strength and 4.2B Classification by tensile strength and
47 J impact energy 27 J impact energy
The symbol in Table 1A indicates yield The symbol in Table 1B indicates yield
strength, tensile strength, and elongation of strength, tensile strength, and elongation of the
the all-weld metal in the as-welded condition all-weld metal in the as-welded condition or in
determined in accordance with Clause 5. the post-weld heat-treated condition
determined in accordance with Clause 5.
Table 1A — Symbol for strength and elonga- Table 1B — Symbol for strength and elongation
tion of all-weld metal of all-weld metal
Minimum Minimum
Tensile Minimum Tensile Minimum
yield yield
b c
strength elongation a strength elongation
Symbol Symbol
a b
strength strength
MPa MPa % MPa MPa %
35 355 440 to 570 22 43X 330 430 to 600 20
38 380 470 to 600 20 49X 390 490 to 670 18
42 420 500 to 640 20 55X 460 550 to 740 17
46 460 530 to 680 20
57X 490 570 to 770 17
50 500 560 to 720 18
a a
For yield strength, the lower yield (R ) is used X is “A” or “P”. Where “A” indicates testing in the
eL
when yielding occurs. Otherwise, the 0,2 % proof as-welded condition and “P” indicates testing in the
strength (R ) is used. post weld heat-treated condition.
p0,2
b b
Gauge length is equal to five times the test speci- For yield strength, the lower yield (R ) is used
eL
men diameter. when yielding occurs. Otherwise, the 0,2 % proof
strength (R ) is used.
p0,2
c
Gauge length is equal to five times the test specimen
diameter.
© ISO 2015 – All rights reserved 3
---------------------- Page: 8 ----------------------
ISO 636:2015(E)
4.3 Symbol for impact properties of all-weld metal
4.3A Classification by yield strength and 4.3B Classification by tensile strength and
47 J impact energy 27 J impact energy
The symbols in Table 2 indicate the temperature The symbol in Table 2 indicates the temperature
at which impact energy of 47 J is achieved under at which impact energy of 27 J is achieved in the
the conditions given in Clause 5. as-welded condition or in the post-weld
heat-treated condition under the conditions
Three test specimens shall be tested. Only one
given in Clause 5.
individual value can be lower than 47 J, but not
lower than 32 J. The average of the three values Five test specimens shall be tested. The lowest
shall be at least 47 J. and highest values obtained shall be disregarded.
Two of the three remaining values shall be equal
or greater than the specified 27 J level. One of the
three can be lower, but shall not be less than
20 J. The average of the three remaining values
shall be at least 27 J.
The addition of the optional symbol U
immediately after the symbol for condition of
heat treatment indicates that the supplemental
requirement of 47 J impact energy at the normal
27 J impact test temperature has also been
satisfied. For the 47 J impact requirement, the
number of specimens tested and values obtained
shall meet the requirement of 4.3A.
Table 2 — Symbol for impact properties of all-weld metal
Temperature for minimum average impact
a b
energy of 47 J or 27 J
Symbol
°C
Z No requirements
a b
A or Y +20
0 0
2 −20
3 −30
4 −40
5 −50
6 −60
7 −70
8 −80
9 −90
...
DRAFT INTERNATIONAL STANDARD
ISO/DIS 636
ISO/TC 44/SC 3 Secretariat: ANSI
Voting begins on: Voting terminates on:
2013-09-12 2014-02-12
Welding consumables — Rods, wires and deposits for
tungsten inert gas welding of non-alloy and fine-grain
steels — Classification
Produits consommables pour le soudage — Baguettes et fils pour dépôts par soudage TIG des aciers non
alliés et des aciers à grains fins — Classification
[Revision of third edition (ISO 636:2004)]
ICS: 25.160.20
ISO/CEN PARALLEL PROCESSING
This draft has been developed within the International Organization for
Standardization (ISO), and processed under the ISO lead mode of collaboration
as defined in the Vienna Agreement.
This draft is hereby submitted to the ISO member bodies and to the CEN member
bodies for a parallel five month enquiry.
Should this draft be accepted, a final draft, established on the basis of comments
received, will be submitted to a parallel two-month approval vote in ISO and
THIS DOCUMENT IS A DRAFT CIRCULATED
formal vote in CEN.
FOR COMMENT AND APPROVAL. IT IS
THEREFORE SUBJECT TO CHANGE AND MAY
NOT BE REFERRED TO AS AN INTERNATIONAL
STANDARD UNTIL PUBLISHED AS SUCH.
To expedite distribution, this document is circulated as received from the
IN ADDITION TO THEIR EVALUATION AS
committee secretariat. ISO Central Secretariat work of editing and text
BEING ACCEPTABLE FOR INDUSTRIAL,
composition will be undertaken at publication stage.
TECHNOLOGICAL, COMMERCIAL AND
USER PURPOSES, DRAFT INTERNATIONAL
STANDARDS MAY ON OCCASION HAVE TO
BE CONSIDERED IN THE LIGHT OF THEIR
POTENTIAL TO BECOME STANDARDS TO
WHICH REFERENCE MAY BE MADE IN
Reference number
NATIONAL REGULATIONS.
ISO/DIS 636:2013(E)
RECIPIENTS OF THIS DRAFT ARE INVITED
TO SUBMIT, WITH THEIR COMMENTS,
NOTIFICATION OF ANY RELEVANT PATENT
RIGHTS OF WHICH THEY ARE AWARE AND TO
©
PROVIDE SUPPORTING DOCUMENTATION. ISO 2013
---------------------- Page: 1 ----------------------
ISO/DIS 636:2013(E)
Copyright notice
This ISO document is a Draft International Standard and is copyright-protected by ISO. Except as
permitted under the applicable laws of the user’s country, neither this ISO draft nor any extract
from it may be reproduced, stored in a retrieval system or transmitted in any form or by any means,
electronic, photocopying, recording or otherwise, without prior written permission being secured.
Requests for permission to reproduce should be addressed to either ISO at the address below or ISO’s
member body in the country of the requester.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail copyright@iso.org
Web www.iso.org
Reproduction may be subject to royalty payments or a licensing agreement.
Violators may be prosecuted.
ii © ISO 2013 – All rights reserved
---------------------- Page: 2 ----------------------
ISO/DIS 636
Contents Page
Foreword . iv
Introduction . v
1 Scope . 1
2 Normative references . 1
3 Classification . 2
4 Symbols and requirements . 2
4.1 Symbol for the product/process . 2
4.2 Symbol for strength and elongation of all-weld metal . 2
4.3 Symbol for impact properties of all-weld metal . 3
4.4 Symbol for the chemical composition of rods or wires . 4
5 Mechanical tests . 8
5.1 Preheating and interpass temperatures . 8
5.2 Welding conditions and pass sequence . 9
5.3 PWHT condition . 9
6 Chemical analysis . 9
7 Retests . 10
8 Technical delivery conditions . 10
9 Designation . 11
© ISO 2013 – All rights reserved iii
---------------------- Page: 3 ----------------------
ISO/DIS 636
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies
(ISO member bodies). The work of preparing International Standards is normally carried out through ISO
technical committees. Each member body interested in a subject for which a technical committee has been
established has the right to be represented on that committee. International organizations, governmental and
non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the
International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2.
The main task of technical committees is to prepare International Standards. Draft International Standards
adopted by the technical committees are circulated to the member bodies for voting. Publication as an
International Standard requires approval by at least 75 % of the member bodies casting a vote.
Attention is drawn to the possibility that some of the elements of this document may be the subject of patent
rights. ISO shall not be held responsible for identifying any or all such patent rights.
ISO 636 was prepared by Technical Committee ISO/TC 44, Welding and allied processes, Subcommittee
SC 3, Welding consumables.
This fourth edition cancels and replaces the third edition which has been technically revised.
iv © ISO 2013 – All rights reserved
---------------------- Page: 4 ----------------------
ISO/DIS 636
Introduction
This International Standard provides a classification for the designation of rods and wires in terms of their
chemical composition and, where required, in terms of the yield strength, tensile strength and elongation of
the all-weld metal. The ratio of yield to tensile strength of weld metal is generally higher than that of parent
metal. Users should note that matching weld metal yield strength to parent metal yield strength will not
necessarily ensure that the weld metal tensile strength matches that of the parent material. Where the
application requires matching tensile strengths, selection of consumable should be made by reference to
column 3 of Table 1A or Table 1B.
It should be noted that the mechanical properties of all-weld metal test specimens used to classify the rods
and wires vary from those obtained in production joints because of differences in welding procedure such as
diameter, width of weave, welding position and material composition.
The classification according to system A is mainly based on EN 1668:1997, Welding consumables — Rods,
wires and deposits for tungsten inert gas welding of non alloy and fine grain steels — Classification. The
classification according to system B is mainly based upon standards used around the Pacific Rim.
Requests for official interpretations of any aspect of this International Standard should be directed to the
Secretariat of ISO/TC 44/SC 3, via your national standards body, a complete listing of which can be found at
www.iso.org.
© ISO 2013 – All rights reserved v
---------------------- Page: 5 ----------------------
DRAFT INTERNATIONAL STANDARD ISO/DIS 636
Welding consumables — Rods, wires and deposits for tungsten
inert gas welding of non-alloy and fine-grain steels —
Classification
1 Scope
This International Standard specifies requirements for classification of rods and wires in the as-welded
condition and in the post-weld heat-treated condition for tungsten inert gas welding of non-alloy and fine grain
steels with a minimum yield strength of up to 500 MPa or a minimum tensile strength of up to 570 MPa.
This International Standard is a combined specification providing classification utilizing a system based upon
the yield strength and the average impact energy of 47 J of all-weld metal, or utilizing a system based upon
the tensile strength and the average impact energy of 27 J of all-weld metal.
1) Paragraphs and tables which carry the suffix letter “A” are applicable only to rods and wires classified
to the system based upon the yield strength and the average impact energy of 47 J of all-weld metal
in accordance with this International Standard.
2) Paragraphs and tables which carry the suffix letter “B” are applicable only to rods and wires classified
to the system based upon the tensile strength and the average impact energy of 27 J of all-weld
metal in accordance with this International Standard.
3) Paragraphs and tables which have neither the suffix letter “A” nor the suffix letter “B” are applicable
to all rods and wires classified in accordance with this International Standard.
2 Normative references
The following referenced documents are indispensable for the application of this document. For dated
references, only the edition cited applies. For undated references, the latest edition of the referenced
document (including any amendments) applies.
ISO 544, Welding consumables – Technical delivery conditions for filler materials and fluxes – Type of product,
dimensions, tolerances and markings
ISO 13916, Welding — Guidance on the measurement of preheating temperature, interpass temperature and
preheat maintenance temperature
ISO 14175, Welding consumables – Gases and gas mixtures for fusion welding and allied processes
ISO 14344, Welding consumables – Procurement of filler materials and fluxes
ISO 15792-1:2000/Amd 1:2011, Welding consumables — Test methods — Part 1: Test methods for all-weld
metal test specimens in steel, nickel and nickel alloys
ISO 80000-1:2009, Quantities and units — Part 1: General
© ISO 2013 – All rights reserved 1
---------------------- Page: 6 ----------------------
ISO/DIS 636
3 Classification
Classification designations are based upon two approaches to indicate the tensile properties and the impact
properties of the all-weld metal obtained with rods or wires. The two designation approaches include
additional designators for some other classification requirements, but not all, as will be clear from the following
sections. In most cases, a given commercial product can be classified to the classification requirements in
both systems. Then either or both classification designations can be used for the product.
Rods or wires shall be classified according to their chemical composition in accordance with Table 3A or
Table 3B.
3A Classification by yield strength and 3B Classification by tensile strength and
47 J impact energy 27 J impact energy
The classification is divided into four parts: The classification is divided into four parts:
1) the first part gives a symbol indicating the 1) the first part gives a symbol indicating the
product/process to be identified; product/process to be identified;
2) the second part gives a symbol indicating
2) the second part gives a symbol indicating
the strength and elongation of the all-weld
the strength and elongation of the all-weld
metal in either the as-welded or post-weld
metal (see Table 1A);
heat-treated condition (see Table 1B);
3) the third part gives a symbol indicating the
3) the third part gives a symbol indicating the
impact properties of all-weld metal (see
impact properties of all-weld metal in the
Table 2);
same condition as specified for the tensile
strength (see Table 2). The letter “U” after
4) the fourth part gives a symbol indicating
this designator indicates that the deposit
the chemical composition of the rods or
meets an average optional requirement of
wires used (see Table 3A).
47 J at the designated Charpy test
temperature;
4) the fourth part gives a symbol indicating
the chemical composition of the rods or
wires used (see Table 3B).
4 Symbols and requirements
4.1 Symbol for the product/process
The symbol of weld deposit by the tungsten inert gas welding process shall be the letter “W” placed at the
beginning of the designation.
The symbol of rods or wires for the tungsten inert gas welding shall be the letter “W” placed at the beginning
of the rod or wire designation.
4.2 Symbol for strength and elongation of all-weld metal
4.2A Classification by yield strength and 47 J 4.2B Classification by tensile strength and
impact energy 27 J impact energy
The symbol in Table 1A indicates yield strength, The symbol in Table 1B indicates yield strength,
tensile strength and elongation of the all-weld metal tensile strength and elongation of the all-weld metal
in the as-welded condition determined in in the as-welded condition or in the post-weld heat-
accordance with Clause 5. treated condition determined in accordance with
Clause 5.
2 © ISO 2013 – All rights reserved
---------------------- Page: 7 ----------------------
ISO/DIS 636
Table 1A — Symbol for strength and elongation Table 1B — Symbol for strength and elongation
of all-weld metal of all-weld metal
Minimum Minimum
Tensile Minimum Tensile Minimum
yield yield
b c
strength elongation strength elongation
a
a b
Symbol Symbol
strength strength
MPa MPa % MPa MPa %
35 355 440 to 570 22 43X 330 430 to 600 20
38 380 470 to 600 20 49X 390 490 to 670 18
42 420 500 to 640 20 55X 460 550 to 740 17
46 460 530 to 680 20 57X 490 570 to 770 17
a
50 500 560 to 720 18
X is “A” or “P”. Where “A” indicates testing in the as-welded
condition and “P” indicates testing in the post-weld heat-treated
a
For yield strength the lower yield (R ) is used when
eL condition.
yielding occurs, otherwise the 0,2 % proof strength (R ) is
p0,2
b
For yield strength the lower yield (R ) is used when
used.
eL
yielding occurs, otherwise the 0,2 % proof strength (R ) is
p0,2
b
Gauge length is equal to five times the test specimen used.
diameter.
c
Gauge length is equal to five times the test specimen
diameter.
4.3 Symbol for impact properties of all-weld metal
4.3A Classification by yield strength and 47 J 4.3B Classification by tensile strength and
impact energy 27 J impact energy
The symbols in Table 2 indicates the temperature at The symbol in Table 2 indicates the temperature at
which an impact energy of 27 J is achieved in the
which an impact energy of 47 J is achieved under
as-welded condition or in the post-weld heat-treated
the conditions given in Clause 5.
condition under the conditions given in Clause 5.
Three test specimens shall be tested. Only one
Five test specimens shall be tested. The lowest and
individual value may be lower than 47 J but not
highest values obtained shall be disregarded. Two
lower than 32 J. The average of the three values
of the three remaining values shall be equal or
shall be at least 47J.”
greater than the specified 2
...
NORME ISO
INTERNATIONALE 636
Quatrième édition
2015-11-15
Produits consommables pour le
soudage — Baguettes et fils pour
dépôts par soudage TIG des aciers
non alliés et des aciers à grains fins —
Classification
Welding consumables — Rods, wires and deposits for tungsten inert
gas welding of non-alloy and fine-grain steels — Classification
Numéro de référence
ISO 636:2015(F)
©
ISO 2015
---------------------- Page: 1 ----------------------
ISO 636:2015(F)
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2015, Publié en Suisse
Droits de reproduction réservés. Sauf indication contraire, aucune partie de cette publication ne peut être reproduite ni utilisée
sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique, y compris la photocopie, l’affichage sur
l’internet ou sur un Intranet, sans autorisation écrite préalable. Les demandes d’autorisation peuvent être adressées à l’ISO à
l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Ch. de Blandonnet 8 • CP 401
CH-1214 Vernier, Geneva, Switzerland
Tel. +41 22 749 01 11
Fax +41 22 749 09 47
copyright@iso.org
www.iso.org
ii © ISO 2015 – Tous droits réservés
---------------------- Page: 2 ----------------------
ISO 636:2015(F)
Sommaire Page
Avant-propos .iv
Introduction .v
1 Domaine d’application . 1
2 Références normatives . 1
3 Classification . 2
4 Symboles et exigences. 2
4.1 Symbole du produit et/ou du procédé . 2
4.2 Symbole de la résistance et de l’allongement du métal fondu hors dilution . 3
4.3 Symbole de la résistance à la flexion par choc du métal fondu hors dilution . 4
4.4 Symbole pour la composition chimique des baguettes et des fils . 4
5 Essais mécaniques . 9
5.1 Températures de préchauffage et entre passes . 9
5.2 Conditions de soudage et séquence des passes .10
5.3 Conditions de traitement thermique après soudage .10
6 Analyse chimique .11
7 Procédure d’arrondissage .11
8 Contre-essais .11
9 Conditions techniques de livraison .11
10 Désignation .11
© ISO 2015 – Tous droits réservés iii
---------------------- Page: 3 ----------------------
ISO 636:2015(F)
Avant-propos
L’ISO (Organisation internationale de normalisation) est une fédération mondiale d’organismes
nationaux de normalisation (comités membres de l’ISO). L’élaboration des Normes internationales est
en général confiée aux comités techniques de l’ISO. Chaque comité membre intéressé par une étude
a le droit de faire partie du comité technique créé à cet effet. Les organisations internationales,
gouvernementales et non gouvernementales, en liaison avec l’ISO participent également aux travaux.
L’ISO collabore étroitement avec la Commission électrotechnique internationale (IEC) en ce qui
concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier de prendre note des différents
critères d’approbation requis pour les différents types de documents ISO. Le présent document a été
rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir www.
iso.org/directives).
L’attention est appelée sur le fait que certains des éléments du présent document peuvent faire l’objet de
droits de propriété intellectuelle ou de droits analogues. L’ISO ne saurait être tenue pour responsable
de ne pas avoir identifié de tels droits de propriété et averti de leur existence. Les détails concernant
les références aux droits de propriété intellectuelle ou autres droits analogues identifiés lors de
l’élaboration du document sont indiqués dans l’Introduction et/ou dans la liste des déclarations de
brevets reçues par l’ISO (voir www.iso.org/brevets).
Les appellations commerciales éventuellement mentionnées dans le présent document sont données
pour information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer
un engagement.
Pour une explication de la signification des termes et expressions spécifiques de l’ISO liés à
l’évaluation de la conformité, ou pour toute information au sujet de l’adhésion de l’ISO aux principes
de l’OMC concernant les obstacles techniques au commerce (OTC), voir le lien suivant: Avant-propos —
Informations supplémentaires.
Le comité chargé de l’élaboration du présent document est l’ISO/TC 44, Soudage et techniques connexes,
sous-comité SC 3, Produits consommables pour le soudage.
Cette quatrième édition annule et remplace la troisième édition (ISO 636:2004), qui fait l’objet d’une
révision technique.
Il convient d’adresser les demandes d’interprétation officielle de tout aspect de la présente Norme
internationale au secrétariat de l’ISO/TC 44/SC 3, via votre organisme national de normalisation; une
liste complète des organismes nationaux de normalisation peut être obtenue à l’adresse www.iso.org.
iv © ISO 2015 – Tous droits réservés
---------------------- Page: 4 ----------------------
ISO 636:2015(F)
Introduction
La présente Norme internationale définit un système de classification permettant la désignation des
baguettes et des fils en fonction de leur composition chimique et, suivant les exigences, en fonction de
la limite d’élasticité, de la résistance à la traction et de l’allongement du métal fondu hors dilution. Le
rapport entre la limite d’élasticité à la résistance à la traction du métal fondu est généralement plus
élevé que celui du métal de base. Il convient que les utilisateurs notent qu’une bonne correspondance
des limites d’élasticité du métal fondu et du métal de base ne garantit pas nécessairement que la
résistance à la traction du métal fondu correspondra à celle du métal de base. Ainsi, lorsque l’application
exige la correspondance de la résistance à la traction, il convient de choisir le produit consommable en
référence à la colonne 3 du Tableau 1A ou du Tableau 1B.
Il convient de noter que les caractéristiques mécaniques des éprouvettes en métal fondu hors dilution
utilisées pour classifier les baguettes et les fils varient de celles obtenues sur des assemblages réalisés
en production par suite de différences dans le mode opératoire de soudage telles que le diamètre, la
largeur du balayage, la position de soudage et la composition chimique du métal de base.
La classification suivant le système A est principalement fondée sur l’EN 1668:1997. La classification
suivant le système B est principalement fondée sur les normes utilisées dans la Zone Pacifique.
© ISO 2015 – Tous droits réservés v
---------------------- Page: 5 ----------------------
NORME INTERNATIONALE ISO 636:2015(F)
Produits consommables pour le soudage — Baguettes et
fils pour dépôts par soudage TIG des aciers non alliés et
des aciers à grains fins — Classification
1 Domaine d’application
La présente Norme internationale spécifie les exigences relatives à la classification des baguettes et
des fils à l’état brut de soudage et à l’état traité thermiquement après soudage, en soudage TIG (soudage
à l’arc sous protection de gaz inerte avec électrode de tungstène) des aciers non alliés et des aciers à
grains fins ayant une limite d’élasticité minimale pouvant atteindre 500 MPa ou une résistance à la
traction minimale pouvant atteindre 570 MPa.
La présente Norme internationale propose une spécification mixte permettant une classification
utilisant un système fondé soit sur la limite d’élasticité et l’énergie de rupture moyenne de 47 J pour
le métal fondu hors dilution, soit sur la résistance à la traction et l’énergie de rupture moyenne de 27 J
pour le métal fondu hors dilution.
a) Les paragraphes et les tableaux qui portent le suffixe «A» ne sont applicables qu’aux baguettes et
fils classifiés d’après le système basé sur la limite d’élasticité et l’énergie de rupture moyenne de
47 J pour le métal fondu hors dilution conformément à la présente Norme internationale.
b) Les paragraphes et les tableaux qui portent le suffixe «B» ne sont applicables qu’aux baguettes et
fils classifiés d’après le système basé sur la résistance à la traction et l’énergie de rupture moyenne
de 27 J pour le métal fondu hors dilution conformément à la présente Norme internationale.
c) Les paragraphes et les tableaux ne comportant ni le suffixe «A» ni le suffixe «B» sont applicables à
toutes les baguettes et à tous les fils classifiés conformément à la présente Norme internationale.
2 Références normatives
Les documents de référence suivants sont indispensables pour l’application du présent document. Pour
les références datées, seule l’édition citée s’applique. Pour les références non datées, la dernière édition
du document de référence s’applique (y compris les éventuels amendements).
ISO 544, Produits consommables pour le soudage — Conditions techniques de livraison des matériaux
d’apport et des flux — Type de produit, dimensions, tolérances et marquage
ISO 13916, Soudage — Lignes directrices pour le mesurage de la température de préchauffage, de la
température entre passes et de la température de maintien du préchauffage
ISO 14175, Produits consommables pour le soudage — Gaz et mélanges gazeux pour le soudage par fusion
et les techniques connexes
ISO 14344, Produits consommables pour le soudage — Approvisionnement en matériaux d’apport et flux
ISO 15792-1:2000, Produits consommables pour le soudage — Méthodes d’essai — Partie 1: Méthodes
d’essai pour les éprouvettes de métal fondu hors dilution pour le soudage de l’acier, du nickel et des alliages
de nickel. Amendé par ISO 15792-1:2000/Amd 1:2011
ISO 80000-1:2009, Grandeurs et unités — Partie 1: Généralités. Corrigé par ISO 80000-1:2009/Cor 1:2011
© ISO 2015 – Tous droits réservés 1
---------------------- Page: 6 ----------------------
ISO 636:2015(F)
3 Classification
Les désignations classifiées sont fondées sur deux systèmes pour indiquer les caractéristiques de
traction et de résistance à la flexion par choc du métal fondu hors dilution obtenu avec une baguette
ou un fil donnés. Les deux systèmes de désignation comportent des indicateurs supplémentaires pour
certaines autres exigences de classification, mais pas toutes, comme précisé ci-après. Dans la plupart
des cas, un produit commercial donné peut être classifié dans les deux systèmes. Il est alors possible
d’utiliser pour le produit l’un des deux systèmes, ou les deux systèmes.
Les baguettes et les fils doivent être classifiés suivant leur composition chimique conformément au
Tableau 3A ou au Tableau 3B.
3A Classification d’après la limite d’élasticité 3B Classification d’après le type d’alliage
et l’énergie de rupture de 47 J
La classification est divisée en quatre parties: La classification est divisée en quatre parties:
1) la première partie donne le symbole du 1) la première partie donne le symbole du
produit et/ou du procédé à identifier. produit et/ou du procédé à identifier.
2) la deuxième partie donne le symbole de la 2) la deuxième partie donne le symbole de la
résistance à la traction et de l’allongement du résistance à la traction et de l’allongement
métal fondu hors dilution (voir Tableau 1A). du métal fondu hors dilution soit à l’état brut
de soudage, soit à l’état traité thermiquement
3) la troisième partie donne le symbole de la
après soudage (voir Tableau 1B).
résistance à la flexion par choc du métal
fondu hors dilution (voir Tableau 2). 3) la troisième partie donne le symbole de la
résistance à la flexion par choc du métal
4) la quatrième partie donne le symbole de la
fondu hors dilution pour le même état que
composition chimique des baguettes et des
celui spécifié pour la résistance à la traction
fils utilisés (voir Tableau 3A).
(voir Tableau 2). La lettre «U» placée après
cet indicateur indique que le dépôt satisfait à
une exigence optionnelle moyenne de 47 J à la
température désignée de l’essai de flexion par
choc.
4) la quatrième partie donne le symbole de la
composition chimique des baguettes et des
fils utilisés (voir Tableau 3B).
4 Symboles et exigences
4.1 Symbole du produit et/ou du procédé
Le symbole du dépôt par procédé de soudage à l’arc sous protection de gaz inerte avec électrode de
tungstène doit être la lettre «W» placée au début de la désignation.
Le symbole pour les baguettes et les fils pour le soudage à l’arc sous protection de gaz inerte avec
électrode de tungstène doit être la lettre «W» placée au début de la désignation des baguettes ou des fils.
2 © ISO 2015 – Tous droits réservés
---------------------- Page: 7 ----------------------
ISO 636:2015(F)
4.2 Symbole de la résistance et de l’allongement du métal fondu hors dilution
4.Classification d’après la limite d’élasticité 4.2B Classification d’après la résistance à la
et l’énergie de rupture de 47 J traction et l’énergie de rupture de 27 J
Le symbole du Tableau 1A indique la limite Le symbole du Tableau 1B indique la limite
d’élasticité, la résistance à la traction et l’allonge- d’élasticité, la résistance à la traction et l’allonge-
ment du métal fondu hors dilution à l’état brut de ment du métal fondu hors dilution à l’état brut de
soudage, déterminés conformément à l’Article 5. soudage ou à l’état traité thermiquement après
soudage, déterminés conformément à l’Article 5.
Table 1A — Symboles de la résistance Table 1B — Symboles de la résistance
à la traction et de l’allongement à la traction et de l’allongement
du métal fondu hors dilution du métal fondu hors dilution
Limite Résistance Allonge- Limite Allonge-
Résistance
d’élasticité à la trac- ment mini- d’élasticité ment mini-
à la traction
a
Symbole a b Symbole b c
minimale tion mal minimale mal
MPa MPa % MPa MPa %
35 355 440 à 570 22 43X 330 430 à 600 20
38 380 470 à 600 20 49X 390 490 à 670 18
42 420 500 à 640 20 55X 460 550 à 740 17
46 460 530 à 680 20
57X 490 570 à 770 17
50 500 560 à 720 18
a a
Lorsqu’un écoulement se produit, la limite d’élas- X est «A» ou «P». La lettre «A» signifie que l’essai a
ticité utilisée est la limite inférieure d’écoulement été effectué sur des éprouvettes à l’état brut de sou-
(R ); dans le cas contraire, c’est la limite apparente dage, et la lettre «P» indique que l’essai a été effectué
eL
d’élasticité à 0,2 % (R ). sur des éprouvettes traitées thermiquement après
p0,2
soudage.
b
La longueur entre repères est égale à cinq fois le
b
diamètre de l’éprouvette. Lorsqu’un écoulement se produit, la limite d’élasti-
cité utilisée est la limite inférieure d’écoulement (R );
eL
dans le cas contraire, c’est la limite apparente d’élasti-
cité à 0,2 % (R ).
p0,2
c
La longueur entre repères est égale à cinq fois le
diamètre de l’éprouvette.
© ISO 2015 – Tous droits réservés 3
---------------------- Page: 8 ----------------------
ISO 636:2015(F)
4.3 Symbole de la résistance à la flexion par choc du métal fondu hors dilution
4.3A Classification d’après la limite d’élasti- 4.3B Classification d’après la résistance à la
cité et l’énergie de rupture de 47 J traction et l’énergie de rupture de 27 J
Les symboles du Tableau 2 indiquent la tempéra- Le symbole du Tableau 2 indique la température
ture à laquelle une énergie de rupture de 47 J est à laquelle une énergie de rupture de 27 J est
obtenue dans les conditions données à l’Article 5. obtenue à l’état brut de soudage ou à l’état traité
thermiquement après soudage, dans les condi-
Trois éprouvettes doivent être soumises aux
tions données à l’Article 5.
essais. Une seule valeur individuelle peut être
inférieure à 47 J, sans être inférieure à 32 J. La Cinq éprouvettes doivent être soumises aux
moyenne des trois valeurs doit être au moins de essais. Les valeurs maximale et minimale doivent
47 J. être ignorées. Deux des trois valeurs restantes
doivent être supé
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.