ISO 3312:1987

Sintered metal materials and hardmetals - Determination of Young modulus

This second edition cancels and replaces the first edition (i.e. ISO 3312:1975). Specifies a method for the determination of the dynamic (adiabatic) Young moduls by longitudinal oscillations of sintered metal materials and hardmetals. Gives principle, symbols and units, apparatus, preparation of the pieces, procedure, expression of results and test report.

Matériaux métalliques frittés et métaux-durs — Détermination du module de Young

La présente Norme internationale spécifie une méthode de détermination dynamique (adiabatique) du module de Young par oscillations longitudinales pour les matériaux métalliques frittés et les métaux-durs.

General Information

• Status: Published
• Publication Date: 15-Jul-1987
• ICS: 77.040.10 - Mechanical testing of metals
• ICS: 77.160 - Powder metallurgy
• Technical Committee: ISO/TC 119/SC 3 - Sampling and testing methods for sintered metal materials (excluding hardmetals)
• Drafting Committee: ISO/TC 119/SC 3 - Sampling and testing methods for sintered metal materials (excluding hardmetals)
• Current Stage: 9093 - International Standard confirmed
• Start Date: 10-Dec-2025
• Completion Date: 13-Dec-2025

Relations

• Consolidated By: ISO 13428:2005 - Geosynthetics - Determination of the protection efficiency of a geosynthetic against impact damage
• Effective Date: 06-Jun-2022
• Revises: ISO 3312:1975 - Sintered metal materials and hardmetals - Determination of Young's modulus
• Effective Date: 15-Apr-2008

Overview

ISO 3312:1987 specifies a laboratory method for determining the dynamic (adiabatic) Young’s modulus of sintered metal materials and hardmetals (cemented carbides) by excitation of longitudinal ultrasonic oscillations. This second edition (1987) replaces ISO 3312:1975 and defines the principle, symbols and units, required apparatus, specimen preparation, test procedure, calculation of results and test-report content.

Key topics and requirements

• Test principle: Excite specimens with ultrasonic longitudinal vibrations, identify the resonance frequency corresponding to the fundamental longitudinal mode, and calculate dynamic Young’s modulus from measured parameters.
• Specimen geometry: Minimum length 60 mm; acceptable cross-sections:
  • Cylindrical: diameter 6 ± 0.2 mm
  • Rectangular bar: (6 ± 0.2) mm × (8 ± 0.2) mm
• Surface and dimensional tolerances:
  • Remove surface layer to at least 0.1 mm.
  • Surface roughness Ra < 1.25 µm.
  • End faces planed; parallelism deviation ≤ 0.02 mm.
  • Specimen must be visually free of cracks and cleaned before testing.
• Apparatus:
  • Support/fixture for specimen mounting.
  • Ultrasonic generator adjustable from about 20 kHz to 100 kHz.
  • Device to detect and measure resonance frequency.
• Measurement and accuracy:
  • Density (mass per unit volume) determined per ISO 2738 to 0.01 g/cm3.
  • Length measured to 0.1 mm.
  • Resonance frequency located (fundamental longitudinal) and determined with specified frequency accuracy.
• Result reporting: The standard prescribes the calculation method (Young’s modulus derived from specimen length, density, resonance frequency and geometry), rounding conventions and required test-report items such as reference to ISO 3312, specimen identification, measured values, test result, any non‑standard operations and incidents affecting results.

Applications and users

ISO 3312 is used for:

• Quality control and acceptance testing in powder metallurgy and hardmetal production.
• Material characterization for engineering design and finite element analysis input.
• R&D and comparative testing of sintered alloys and cemented carbides.
• Non-destructive evaluation labs and contract testing laboratories verifying elastic properties.

Typical users include metallurgists, materials engineers, quality assurance teams, test laboratories and manufacturers of sintered components and cutting/tooling materials.

Related standards

• ISO 2738 - referenced for accurate determination of density, oil content and open porosity of sintered metallic materials.

Keywords: ISO 3312, Young’s modulus, dynamic Young modulus, sintered metal materials, hardmetals, ultrasonic resonance, longitudinal oscillations, ISO 2738, specimen preparation, materials testing.

Standards Content (Sample)

INTERNATIONAL STANDARD 3312
Second edition
1987-07-15
INTERNATIONAL ORGANIZATION FOR STANDARDIZATION
ORGANISATION INTERNATIONALE DE NORMALISATION
MEXflYHAPOflHAfi OPrAHM3A~MR I-IO CTAHAAPTM3A~MM
Sintered metal materials and hardmetals - Determination
of Young modulus
Dhtermination du module de Young
Ma tkiaux rnd tafliques fritths et mb taux-durs -
Reference number
ISO 3312: 1987 (E
Fo reword
ISO (the International Organization for Standardization) is a worldwide federation of
national Standards bodies (ISO member bodies). The work of preparing International
Standards is normally carried out through ISO technical committees. Esch member
body interested in a subject for which a technical committee has been established has
the right to be represented on that committee. International organizations, govern-
mental and non-governmental, in liaison with ISO, also take part in the work.
Draft International Standards adopted by the technical committees are circulated to
the member bodies for approval before their acceptance as International Standards by
the ISO Council. They are approved in accordance with ISO procedures requiring at
least 75 % approval by the member bodies voting.
International Standard ISO 3312 was prepared by Technical Committee ISO/TC 119,
Powder metallurg y.
This second edition cancels and replaces the first edition (ISO 3312 : 19751, of which it
constitutes a minor revision.
Users should note that all International Standards undergo revision from time to time
and that any reference made herein to any other International Standard implies its
latest edition, unless otherwise stated.
@ International Organkation for Standardization, 1987 l
Printed in Switzerland
ISO 3312 : 1987 (E)
INTERNATIONAL STANDARD
Determinat-ion
hardmetals -
Sintered metal materials and
of Young modulus
1 Scope and field of application 6 Preparation of test pieces
This International Standard specifies a method for the deter-
6.1 The test pieces shall be at least 60 mm long and may
mination of the dynamic (adiabatic) Young modulus by
have either a round or a rectangular Cross-section. The test
longitudinal oscillations of sintered metal materials and hard-
piece with round Cross-section shall be 6 + 0,2 mm in
meta
...

l
ISO
NORME INTERNATIONALE
Deuxième édition
1987-07-U
.
INTERNATIONAL ORGANIZATION FOR STANDARDIZATION
ORGANISATION INTERNATIONALE DE NORMALISATION
. MEXJIJYHAPOAHAFI OPrAHM3A~MFi Il0 CTAHjJAPTl43A~MM
Matériaux métalliques frittés et métaux-durs -
Détermination du module de Young
.I*
Detefmination of Young modulus
. Sin tered metal materials and hardmetals -
Numéro de référence
ISO 3312: 1987 (F)
Avant-propos
L’ISO (Organisation internationale de normalisation) est une fédération mondiale
d’organismes nationaux de normalisation (comités membres de I’ISO). L’élaboration
des Normes internationales est normalement confiée aux comités techniques de I’ISO.
Chaque comité membre intéressé par une étude a le droit de faire partie du comité
technique créé à cet effet. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec I’ISO participent également aux travaux.
Les projets de Normes internationales adoptés par les comités techniques sont soumis
aux comités membres pour approbation, avant leur acceptation comme Normes inter-
nationales par le Conseil de I’ISO. Les Normes internationales sont approuvées confor-
mément aux procédures de I’ISO qui requièrent l’approbation de 75 % au moins des
comités membres votants.
La Norme internationale ISO 3312 a été élaborée par le comité technique ISO/TC 119,
Métallurgie des poudres.
Cette deuxième édition annule et remplace la première édition (ISO 3312 : 1975), dont
elle constitue une révision mineure.
L’attention des utilisateurs est attirée sur le fait que toutes les Normes internationales
sont de temps en temps soumises à révision et que toute référence faite à une autre
Norme internationale dans le présent document implique qu’il s’agit, sauf indication
contraire, de la dernière édition.
Organisation internationale de normalisation, 1987
Imprimé en Suisse
ISO 3312 : 1987 (F)
NORME INTERNATIONALE
Matériaux métalliques frittés et métaux-durs -
Détermination du module de Young
6 Préparation des éprouvettes
1 Objet et domaine d’application
.,
La présente Norme internationale spécifie une méthode de
6.1 Les éprouvettes doivent avoir une longueur d’au moins
détermination dynamique (adiabatique) du module de Young
60 mm et peuvent avoir une section circulaire ou rectangulaire.
par oscillations longitudinales pour les matériaux métalliques
L’éprouvette cylindrique doit avoir un diamètre de 6
...

l
ISO
NORME INTERNATIONALE
Deuxième édition
1987-07-U
.
INTERNATIONAL ORGANIZATION FOR STANDARDIZATION
ORGANISATION INTERNATIONALE DE NORMALISATION
. MEXJIJYHAPOAHAFI OPrAHM3A~MFi Il0 CTAHjJAPTl43A~MM
Matériaux métalliques frittés et métaux-durs -
Détermination du module de Young
.I*
Detefmination of Young modulus
. Sin tered metal materials and hardmetals -
Numéro de référence
ISO 3312: 1987 (F)
Avant-propos
L’ISO (Organisation internationale de normalisation) est une fédération mondiale
d’organismes nationaux de normalisation (comités membres de I’ISO). L’élaboration
des Normes internationales est normalement confiée aux comités techniques de I’ISO.
Chaque comité membre intéressé par une étude a le droit de faire partie du comité
technique créé à cet effet. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec I’ISO participent également aux travaux.
Les projets de Normes internationales adoptés par les comités techniques sont soumis
aux comités membres pour approbation, avant leur acceptation comme Normes inter-
nationales par le Conseil de I’ISO. Les Normes internationales sont approuvées confor-
mément aux procédures de I’ISO qui requièrent l’approbation de 75 % au moins des
comités membres votants.
La Norme internationale ISO 3312 a été élaborée par le comité technique ISO/TC 119,
Métallurgie des poudres.
Cette deuxième édition annule et remplace la première édition (ISO 3312 : 1975), dont
elle constitue une révision mineure.
L’attention des utilisateurs est attirée sur le fait que toutes les Normes internationales
sont de temps en temps soumises à révision et que toute référence faite à une autre
Norme internationale dans le présent document implique qu’il s’agit, sauf indication
contraire, de la dernière édition.
Organisation internationale de normalisation, 1987
Imprimé en Suisse
ISO 3312 : 1987 (F)
NORME INTERNATIONALE
Matériaux métalliques frittés et métaux-durs -
Détermination du module de Young
6 Préparation des éprouvettes
1 Objet et domaine d’application
.,
La présente Norme internationale spécifie une méthode de
6.1 Les éprouvettes doivent avoir une longueur d’au moins
détermination dynamique (adiabatique) du module de Young
60 mm et peuvent avoir une section circulaire ou rectangulaire.
par oscillations longitudinales pour les matériaux métalliques
L’éprouvette cylindrique doit avoir un diamètre de 6
...