ISO 3651-1:1998

Determination of resistance to intergranular corrosion of stainless steels — Part 1: Austenitic and ferritic-austenitic (duplex) stainless steels — Corrosion test in nitric acid medium by measurement of loss in mass (Huey test)

Détermination de la résistance à la corrosion intergranulaire des aciers inoxydables — Partie 1: Aciers inoxydables austénitiques et austéno-ferritiques (duplex) — Essai de corrosion en milieu acide nitrique par mesurage de la perte de masse (essai de Huey)

General Information

• Status: Published
• Publication Date: 12-May-1998
• ICS: 77.060 - Corrosion of metals
• Technical Committee: ISO/TC 17/SC 7 - Methods of testing (other than mechanical tests and chemical analysis)
• Drafting Committee: ISO/TC 17/SC 7 - Methods of testing (other than mechanical tests and chemical analysis)
• Current Stage: 9093 - International Standard confirmed
• Completion Date: 12-Mar-2021

Relations

• Consolidates: ISO 11689:1996 - Acoustics — Procedure for the comparison of noise-emission data for machinery and equipment
• Effective Date: 06-Jun-2022
• Revises: ISO 3651-1:1976 - Austenitic stainless steels — Determination of resistance to intergranular corrosion — Part 1: Corrosion test in nitric acid medium by measurement of loss in mass (Huey test)
• Effective Date: 15-Apr-2008

Standards Content (Sample)

INTERNATIONAL ISO
STANDARD 3651-1
Second edition
1998-05-15
Determination of resistance to intergranular
corrosion of stainless steels —
Part 1:
Austenitic and ferritic-austenitic (duplex)
stainless steels — Corrosion test in nitric acid
medium by measurement of loss in mass
(Huey test)
Détermination de la résistance à la corrosion intergranulaire des aciers
inoxydables —
Partie 1: Aciers inoxydables austénitiques et austéno-ferritiques (duplex) —
Essai de corrosion en milieu acide nitrique par mesurage de la perte de
masse (essai de Huey)
A
Reference number
ISO 3651-1:1998(E)

---------------------- Page: 1 ----------------------
ISO 3651-1:1998(E)
Contents Page
1 Scope . 1
2 Purpose of the test . 1
2.1 Verification of the intrinsic resistance of
the alloy to intergranular corrosion . 1
2.2 Inspection of the efficiency of the solution
treatment . 1
Heat treatment of sensitization .
3 2
4 Corrosion test . 2
4.1 Principle . 2
4.2 Test pieces . 2
5 Apparatus . 3
6 Corrosive solution . 5
7 Procedure . 5
8 Calculation . 5
9 Test report . 6
©  ISO 1998
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced
or utilized in any form or by any means, electronic or mechanical, including photocopying and
microfilm, without permission in writing from the publisher.
International Organization for Standardization
Case postale 56 • CH-1211 Genève 20 • Switzerland
Internet [e-mail]
Printed in Switzerland
ii

---------------------- Page: 2 ----------------------
©
ISO ISO 3651-1:1998(E)
Foreword
ISO (the International Organization for Standardization) is a
worldwide federation of national standards bodies (ISO member
bodies). The work of preparing International Standards is normally
carried out through ISO technical committees. Each member body
interested in a subject for which a technical committee has been
established has the right to be represented on that committee.
International organizations, governmental and non-governmental, in
liaison with ISO, also take part in the work. ISO collaborates closely
with the International Electrotechnical Commission (IEC) on all
matters of electrotechnical standardization.
Draft International Standards adopted by the technical committees
are circulated to the member bodies for voting. Publication as an
International Standard requires approval by at least 75 % of the
member bodies casting a vote.
International Standard ISO 3651-1 was prepared by Technical
Committee ISO/TC 17, Steel, Subcommittee SC 7, Methods of
testing (other than mechanical tests and chemical analysis)
.
This second edition cancels and replaces the first edition
(ISO 3651-1:1976), which has been technically revised.
ISO 3651 consists of the following parts, under the general title
Determination of resistance to intergranular corrosion of stainless
steels:
— Part 1: Austenitic and ferritic-austenitic (duplex) stainless steels
— Corrosion test in nitric acid medium by measurement of loss
in mass (Huey test)
— Part 2: Ferritic, austenitic and ferritic-austenitic (duplex) stainless
steels — Corrosion test in media containing sulfuric acid
iii

---------------------- Page: 3 ----------------------
©
ISO 3651-1:1998(E) ISO
Introduction
The term “intergranular corrosion test” denotes the corrosion test
carried out by means of preferential attack of the grain boundaries.
Austenitic and ferritic-austenitic (duplex) stainless steels may be
subject to such attack when they are held at a temperature between
about 500 °C and 1 000 °C. This heat cycle, which may provoke
sensitization to intergranular corrosion, may occur during hot
forming (forging, rolling) as the result of incorrect solution treatment
or during a welding operation.
NOTE —  Intergranular corrosion in nitric acid may be associated with one or
more of the following:
— precipitation of chromium carbides;
— precipitation of intermetallic compounds such as sigma phase, in
molybdenum-bearing grades;
— segregation of impurity elements to the grain boundaries.
The interpretation of the result (for example, maximum rate of
corrosion) shall form the subject of an agreement between the
interested parties.
iv

---------------------- Page: 4 ----------------------
©
INTERNATIONAL STANDARD  ISO ISO 3651-1:1998(E)
Determination of resistance to intergranular corrosion of stainless
steels —
Part 1:
Austenitic and ferritic-austenitic (duplex) stainless steels — Corrosion
test in nitric acid medium by measurement of loss in mass (Huey test)
1 Scope
This part of ISO 3651 specifies a method for the determination of the resistance to intergranular
corrosion of austenitic and ferritic-austenitic (duplex) stainless steels in a nitric acid medium by
measurement of the loss in mass (Huey test). It also specifies the purpose which may be assigned to
the test.
The method is applicable only to austenitic and ferritic-austenitic (duplex) stainless steels supplied in the
form of rolled or forged products, tubes and cast products and intended for use in a strongly oxidizing
medium (for example, relatively concentrated nitric acid). In general the Huey test should not be used for
grades containing molybdenum unless the material tested is to be used in nitric acid service.
NOTE —  It is important to note that the result of the corrosion test is only strictly valid for the corrosive medium used in the
test. It constitutes a basis for estimating the resistance to intergranular corrosion but may not be used to check resistance to
other forms of corrosion (general corrosion, pitting, stress corrosion, etc.). It is necessary for the user to adapt the specified
corrosion test to the use which will be made of the alloy. This test should, in no case, be considered as an absolute criterion of
the quality of the alloy.
2 Purpose of the test
This intergranular corrosion test may have either of the purposes given in 2.1 or 2.2. If an order specifies
this corrosion test, the purpose of the test shall be stated at the time of ordering.
2.1 Verification of the intrinsic resistance of the alloy to intergranular corrosion
This verification applies only to austenitic steel grades which are specially produced for resistance to
intergranular corrosion in strongly oxidizing media. The specimen is inspected after having undergone a
heat treatment for sensitization (see clause 3).
2.2 Inspection of the efficiency of the solution treatment
This inspection is only carried out on thin products for which the cooling speed may be made sufficiently
rapid. The specimen is inspected in the state in which it is delivered to the user, without heat treatment
for sensitization.
1

---------------------- Page: 5 ---------
...

NORME ISO
INTERNATIONALE 3651-1
Deuxième édition
1998-05-15
Détermination de la résistance
à la corrosion intergranulaire des aciers
inoxydables —
Partie 1:
Aciers inoxydables austénitiques et austéno-
ferritiques (duplex) — Essai de corrosion en
milieu acide nitrique par mesurage de la perte
de masse (essai de Huey)
Determination of resistance to intergranular corrosion of stainless steels —
Part 1: Austenitic and ferritic-austenitic (duplex) stainless steels —
Corrosion test in nitric acid medium by measurement of loss in mass
(Huey test)
A
Numéro de référence
ISO 3651-1:1998(F)

---------------------- Page: 1 ----------------------
ISO 3651-1:1998(F)
Sommaire Page
1 Domaine d'application . 1
2 Objectif de l'essai . 1
2.1 Vérification de la résistance intrinsèque de
l’acier à la corrosion intergranulaire . 1
2.2 Contrôle de l'efficacité du traitement
d'hypertrempe . 1
Traitement thermique de sensibilisation .
3 2
4 Essai de corrosion . 2
4.1 Principe . 2
4.2 Éprouvettes . 2
5 Appareillage . 3
6 Solution corrosive . 5
7 Mode opératoire . 5
8 Calcul . 5
9 Rapport d'essai . 6
©  ISO 1998
Droits de reproduction réservés. Sauf prescription différente, aucune partie de cette publi-
cation ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun pro-
cédé, électronique ou mécanique, y compris la photocopie et les microfilms, sans l'accord
écrit de l'éditeur.
Organisation internationale de normalisation
Case postale 56 • CH-1211 Genève 20 • Suisse
Internet [e-mail]
Imprimé en Suisse
ii

---------------------- Page: 2 ----------------------
©
ISO ISO 3651-1:1998(F)
Avant-propos
L'ISO (Organisation internationale de normalisation) est une
fédération mondiale d'organismes nationaux de normalisation
(comités membres de l'ISO). L'élaboration des Normes interna-
tionales est en général confiée aux comités techniques de l'ISO.
Chaque comité membre intéressé par une étude a le droit de faire
partie du comité technique créé à cet effet. Les organisations
internationales, gouvernementales et non gouvernementales, en
liaison avec l'ISO, participent également aux travaux. L'ISO
collabore étroitement avec la Commission électrotechnique interna-
tionale (CEI) en ce qui concerne la normalisation électrotechnique.
Les projets de Normes internationales adoptés par les comités
techniques sont soumis aux comités membres pour vote. Leur
publication comme Normes internationales requiert l'approbation de
75 % au moins des comités membres votants.
La Norme internationale ISO 3651-1 a été élaborée par le comité
technique ISO/TC 17, Acier, sous-comité SC 7, Méthodes d'essais
(autres que les essais mécaniques et les analyses chimiques).
Cette deuxième édition annule et remplace la première édition
(ISO 3651-1:1976), dont elle constitue une révision technique.
L'ISO 3651 comprend les parties suivantes, présentées sous le titre
Détermination de la résistance à la corrosion inter-
général
granulaire des aciers inoxydables:
— Partie 1: Aciers inoxydables austénitiques et austéno-ferritiques
(duplex) — Essai de corrosion en milieu acide nitrique par
mesurage de la perte de masse (essai de Huey)
— Partie 2: Aciers inoxydables ferritiques, austénitiques et
austéno-ferritiques (duplex) — Essais de corrosion en milieux
contenant de l'acide sulfurique
iii

---------------------- Page: 3 ----------------------
©
ISO 3651-1:1998(F) ISO
Introduction
L'expression «essai de corrosion intergranulaire» désigne un essai
de corrosion effectué par attaque préférentielle des joints de grains.
Les aciers inoxydables austénitiques et austéno-ferritiques (duplex),
maintenus à une température comprise entre 500 °C et 1 000 °C,
peuvent être soumis à ce genre d'attaque. Ce cycle thermique,
provoquant éventuellement une sensibilisation à la corrosion inter-
granulaire, peut intervenir lors d'une transformation à chaud
(forgeage ou laminage), par suite d'une hypertrempe incorrecte ou
durant le soudage.
NOTE —  Dans le domaine d'application de cet essai, la corrosion intergranulaire
dans l’acide nitrique peut être associée à un ou plusieurs des facteurs suivants:
 précipitation de carbures de chrome;
 précipitation de composés intermétalliques tels que phase sigma dans les
nuances d’acier pour roulements au molybdène;
 ségrégation en impuretés dans les joints de grains.
L'interprétation des résultats de l'essai (par exemple vitesse de
corrosion maximale) doit faire l'objet d'un accord entre les parties
intéressées.
iv

---------------------- Page: 4 ----------------------
©
NORME INTERNATIONALE  ISO ISO 3651-1:1998(F)
Détermination de la résistance à la corrosion intergranulaire
des aciers inoxydables —
Partie 1:
Aciers inoxydables austénitiques et austéno-ferritiques (duplex) —
Essai de corrosion en milieu acide nitrique par mesurage de la perte
de masse (essai de Huey)
1 Domaine d'application
La présente partie de l'ISO 3651 spécifie une méthode d'essai pour déterminer la résistance à la
corrosion intergranulaire, en milieu acide nitrique, des aciers inoxydables austénitiques et austéno-
ferritiques (duplex), par mesurage de la perte de masse (essai de Huey). Elle spécifie également les
objectifs qu'il est possible d'assigner à l'essai.
La méthode n'est applicable qu'aux aciers inoxydables austénitiques et austéno-ferritiques (duplex)
livrés sous forme de produits moulés, laminés ou forgés, et de tubes, et destinés à être utilisés dans un
milieu fortement oxydant (par exemple acide nitrique relativement concentré). En général l'essai de
Huey ne doit pas être utilisé pour les nuances au molybdène, à moins que le matériel contrôlé ne soit
utilisé en milieu acide nitrique.
NOTE —  Il est important de noter que le résultat de l'essai de corrosion n'est strictement valable que pour le milieu corrosif
utilisé dans l'essai. Il constitue une base d'estimation de la résistance à la corrosion intergranulaire, mais ne peut pas servir à
vérifier la résistance à d'autres formes de corrosion (corrosion générale, corrosion par piqûres, corrosion sous contrainte etc.).
L'utilisateur devra nécessairement adapter l'essai de corrosion spécifié à l'usage qu'il désire faire de l’acier. Il ne faut en aucun
cas considérer cet essai comme un critère absolu de la qualité du métal.
2 Objectif de l'essai
Le présent essai de corrosion intergranulaire peut avoir l'un des objectifs énoncés en 2.1 et 2.2. Dans le
cas où la commande spécifie cet essai de corrosion, l'objectif de l'essai doit être prescrit lors de la
commande.
2.1 Vérification de la résistance intrinsèque de l’acier à la corrosion intergranulaire
Cette vérification s'applique uniquement aux aciers austénitiques spécialement élaborés pour résister à
la corrosion intergranulaire en milieu fortement oxydant. L’échantillon est contrôlé après avoir subi un
traitement thermique de sensibilisation (voir 3).
2.2 Contrôle de l'efficacité du traitement d'hypertrempe
Ce contrôle ne s'effectue que sur les produits minces dont la vitesse de refroidissement peut être
rendue suffisamment rapide. L’échantillon est contrôlé à l'état de livraison à l'utilisateur, sans traitement
thermique de sensibilisation.
1

---------------------- Page: 5 ----------------------
©
ISO
ISO 3651-1:1998(F)
3 Traitement thermique de sensibilisation
En vue de vérifier la résistance intrinsèque à
...