Buildings and civil engineering works — Determination of the staining of porous substrates by sealants used in joints — Part 1: Test with compression

This document specifies a method for determining the staining of porous substrates (e.g. marble, limestone, sandstone or granite) by sealants used in building construction. The method evaluates the likelihood of a sealant causing an early stain on a porous substrate due to exudation of materials from the sealant. The outcome of the test is specific to the tested sealant and tested substrate and cannot be extrapolated to other sealant formulations or other porous substrates. During this accelerated test, if the sealant does not stain or discolour the substrates, it does not mean that the tested sealant will not stain or discolour the tested porous substrate over a longer time period.

Bâtiments et ouvrages de génie civil — Détermination du tachage des supports poreux par les mastics utilisés dans les joints — Partie 1: Essai avec compression

La présente partie de l'ISO 16938 spécifie la méthode pour déterminer le tachage des supports poreux (par exemple marbre, calcaire, grès ou granit) par les mastics utilisés dans la construction des bâtiments. La méthode évalue la probabilité d'apparition d'une coloration précoce, sur un support poreux, due au suintement ou à l'infiltration des matériaux des mastics. Le résultat de l'essai est spécifique du mastic et du support soumis à l'essai et ne peut être extrapolé à d'autres formulations de mastics ou à d'autres supports poreux. Durant cet essai accéléré, si le mastic ne tache pas ou ne décolore pas les supports, cela ne signifie pas que le mastic soumis à l'essai sur une période plus longue ne tachera pas ou ne décolorera pas le support poreux.

General Information

Status
Published
Publication Date
18-Sep-2019
Technical Committee
Drafting Committee
Current Stage
9020 - International Standard under periodical review
Start Date
15-Jul-2024
Completion Date
15-Jul-2024
Ref Project

Relations

Buy Standard

Standard
ISO 16938-1:2019 - Buildings and civil engineering works — Determination of the staining of porous substrates by sealants used in joints — Part 1: Test with compression Released:9/17/2019
English language
9 pages
sale 15% off
Preview
sale 15% off
Preview
Standard
ISO 16938-1:2019 - Buildings and civil engineering works -- Determination of the staining of porous substrates by sealants used in joints
English language
9 pages
sale 15% off
Preview
sale 15% off
Preview
Standard
ISO 16938-1:2019 - Bâtiments et ouvrages de génie civil — Détermination du tachage des supports poreux par les mastics utilisés dans les joints — Partie 1: Essai avec compression Released:10/14/2019
French language
9 pages
sale 15% off
Preview
sale 15% off
Preview
Standard
ISO 16938-1:2019 - Bâtiments et ouvrages de génie civil -- Détermination du tachage des supports poreux par les mastics utilisés dans les joints
French language
9 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)


INTERNATIONAL ISO
STANDARD 16938-1
Second edition
2019-09
Buildings and civil engineering
works — Determination of the
staining of porous substrates by
sealants used in joints —
Part 1:
Test with compression
Bâtiments et ouvrages de génie civil — Détermination du tachage des
supports poreux par les mastics utilisés dans les joints —
Partie 1: Essai avec compression
Reference number
©
ISO 2019
© ISO 2019
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting
on the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address
below or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: +41 22 749 01 11
Fax: +41 22 749 09 47
Email: copyright@iso.org
Website: www.iso.org
Published in Switzerland
ii © ISO 2019 – All rights reserved

Contents Page
Foreword .iv
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Principle . 1
5 Apparatus . 2
5.1 Substrate materials . 2
5.2 Spacers . 2
5.3 Non-adherent substrate . 2
5.4 Masking tape . 2
5.5 Ventilated convection-type oven . 2
5.6 Refrigerated enclosure . 2
5.7 Clamps or other device . 2
5.8 Actinic radiation accelerated aging apparatus . 2
5.8.1 General. 2
5.8.2 Fluorescent ultraviolet radiation/condensation test apparatus . 2
5.8.3 Xenon light test apparatus . 3
5.9 Black standard thermometer . 3
5.10 Measuring device . 3
6 Preparation of test specimens . 3
7 Conditioning . 4
8 Test procedure . 4
8.1 Compression . 4
8.2 Aging procedures . 5
8.2.1 General. 5
8.2.2 Heat aging . 5
8.2.3 Cold aging . 5
8.2.4 Actinic radiation aging . 5
9 Detection of staining . 6
9.1 General . 6
9.2 Detection at the surface of the substrate . 6
9.3 Detection in the depth of the substrate . 6
9.4 Expression of results . 8
10 Test report . 8
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www .iso .org/directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www .iso .org/patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and
expressions related to conformity assessment, as well as information about ISO's adherence to the
World Trade Organization (WTO) principles in the Technical Barriers to Trade (TBT) see www .iso
.org/iso/foreword .html.
This document was prepared by Technical Committee ISO/TC 59, Buildings and civil engineering works,
Subcommittee SC 8, Sealants.
This second edition cancels and replaces the first edition (ISO 16938-1:2008), which has been
technically revised.
The main changes compared to the previous edition are as follows:
— the title of the document has been modified;
— the figures have been modified and notes were added to provide further explanation;
— Figure 4 has been replaced by Table 2.
A list of all parts in the ISO 16938 series can be found on the ISO website.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www .iso .org/members .html.
iv © ISO 2019 – All rights reserved

INTERNATIONAL STANDARD ISO 16938-1:2019(E)
Buildings and civil engineering works — Determination
of the staining of porous substrates by sealants used in
joints —
Part 1:
Test with compression
1 Scope
This document specifies a method for determining the staining of porous substrates (e.g. marble,
limestone, sandstone or granite) by sealants used in building construction. The method evaluates the
likelihood of a sealant causing an early stain on a porous substrate due to exudation of materials from
the sealant. The outcome of the test is specific to the tested sealant and tested substrate and cannot be
extrapolated to other sealant formulations or other porous substrates. During this accelerated test, if
the sealant does not stain or discolour the substrates, it does not mean that the tested sealant will not
stain or discolour the tested porous substrate over a longer time period.
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content
constitutes requirements of this document. For dated references, only the edition cited applies. For
undated references, the latest edition of the referenced document (including any amendments) applies.
ISO 4892-1, Plastics — Methods of exposure to laboratory light sources — Part 1: General guidance
ISO 4892-2:2013, Plastics — Methods of exposure to laboratory light sources — Part 2: Xenon-arc lamps
ISO 4892-3, Plastics — Methods of exposure to laboratory light sources — Part 3: Fluorescent UV lamps
ISO 6927, Buildings and civil engineering works — Sealants — Vocabulary
ISO 11431:2002, Building construction — Jointing products — Determination of adhesion/cohesion
properties of sealants after exposure to heat, water and artificial light through glass
3 Terms and definitions
For the purposes of this document, the terms and definitions given in ISO 6927 apply.
ISO and IEC maintain terminological databases for use in standardization at the following addresses:
— ISO Online browsing platform: available at https: //www .iso .org/obp
— IEC Electropedia: available at http: //www .electropedia .org/
4 Principle
This method measures the visible staining attributed to joint sealants on porous substrates that is a
result of the conditioning specified.
A sealant is applied and cured between two pieces of porous substrate. The test specimens are
compressed and then subjected to heat aging and/or cold aging and/or aging in actinic radiation
accelerated weathering equipment. After aging, the test specimens are evaluated and visible staining is
recorded on the exterior surface and in the interior of the substrate after visual inspection of changes in
surface appearance and measurements of maximum and minimum stain width and stain penetration.
5 Apparatus
5.1 Substrate materials
For the preparation of each test specimen, two substrate pieces of the same material are required with
dimensions as shown in Figure 1.
5.2 Spacers
For the preparation of the test specimens, the spacers shall be of a cross-section 12 mm × 12 mm, with
a non-adherent surface (see Figure 1).
If the spacers are made of a material to which the sealant adheres, their surfaces should be made non-
adherent, e.g. by a thin wax coating.
5.3 Non-adherent substrate
For the preparation of test specimens, the non-adherent substrate can be, for example, a polyethylene
(PE) film or a micro-porous polytetrafluorethylene (PTFE) film, preferably on the advice of the sealant
manufacturer.
5.4 Masking tape
The masking tape shall be suitable for covering the tested surface of the substrates (see Figure 1) to
prevent sealant contamination during specimen preparation.
5.5 Ventilated convection-type oven
The ventilated convection-type oven shall be capable of being maintained at (70 ± 2) °C.
5.6 Refrigerated enclosure
The refrigerated enclosure shall be capable of being maintained at (−20 ± 2) °C.
5.7 Clamps or other device
The cla
...


INTERNATIONAL ISO
STANDARD 16938-1
Second edition
2019-09
Buildings and civil engineering
works — Determination of the
staining of porous substrates by
sealants used in joints —
Part 1:
Test with compression
Bâtiments et ouvrages de génie civil — Détermination du tachage des
supports poreux par les mastics utilisés dans les joints —
Partie 1: Essai avec compression
Reference number
©
ISO 2019
© ISO 2019
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting
on the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address
below or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: +41 22 749 01 11
Fax: +41 22 749 09 47
Email: copyright@iso.org
Website: www.iso.org
Published in Switzerland
ii © ISO 2019 – All rights reserved

Contents Page
Foreword .iv
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Principle . 1
5 Apparatus . 2
5.1 Substrate materials . 2
5.2 Spacers . 2
5.3 Non-adherent substrate . 2
5.4 Masking tape . 2
5.5 Ventilated convection-type oven . 2
5.6 Refrigerated enclosure . 2
5.7 Clamps or other device . 2
5.8 Actinic radiation accelerated aging apparatus . 2
5.8.1 General. 2
5.8.2 Fluorescent ultraviolet radiation/condensation test apparatus . 2
5.8.3 Xenon light test apparatus . 3
5.9 Black standard thermometer . 3
5.10 Measuring device . 3
6 Preparation of test specimens . 3
7 Conditioning . 4
8 Test procedure . 4
8.1 Compression . 4
8.2 Aging procedures . 5
8.2.1 General. 5
8.2.2 Heat aging . 5
8.2.3 Cold aging . 5
8.2.4 Actinic radiation aging . 5
9 Detection of staining . 6
9.1 General . 6
9.2 Detection at the surface of the substrate . 6
9.3 Detection in the depth of the substrate . 6
9.4 Expression of results . 8
10 Test report . 8
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www .iso .org/directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www .iso .org/patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and
expressions related to conformity assessment, as well as information about ISO's adherence to the
World Trade Organization (WTO) principles in the Technical Barriers to Trade (TBT) see www .iso
.org/iso/foreword .html.
This document was prepared by Technical Committee ISO/TC 59, Buildings and civil engineering works,
Subcommittee SC 8, Sealants.
This second edition cancels and replaces the first edition (ISO 16938-1:2008), which has been
technically revised.
The main changes compared to the previous edition are as follows:
— the title of the document has been modified;
— the figures have been modified and notes were added to provide further explanation;
— Figure 4 has been replaced by Table 2.
A list of all parts in the ISO 16938 series can be found on the ISO website.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www .iso .org/members .html.
iv © ISO 2019 – All rights reserved

INTERNATIONAL STANDARD ISO 16938-1:2019(E)
Buildings and civil engineering works — Determination
of the staining of porous substrates by sealants used in
joints —
Part 1:
Test with compression
1 Scope
This document specifies a method for determining the staining of porous substrates (e.g. marble,
limestone, sandstone or granite) by sealants used in building construction. The method evaluates the
likelihood of a sealant causing an early stain on a porous substrate due to exudation of materials from
the sealant. The outcome of the test is specific to the tested sealant and tested substrate and cannot be
extrapolated to other sealant formulations or other porous substrates. During this accelerated test, if
the sealant does not stain or discolour the substrates, it does not mean that the tested sealant will not
stain or discolour the tested porous substrate over a longer time period.
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content
constitutes requirements of this document. For dated references, only the edition cited applies. For
undated references, the latest edition of the referenced document (including any amendments) applies.
ISO 4892-1, Plastics — Methods of exposure to laboratory light sources — Part 1: General guidance
ISO 4892-2:2013, Plastics — Methods of exposure to laboratory light sources — Part 2: Xenon-arc lamps
ISO 4892-3, Plastics — Methods of exposure to laboratory light sources — Part 3: Fluorescent UV lamps
ISO 6927, Buildings and civil engineering works — Sealants — Vocabulary
ISO 11431:2002, Building construction — Jointing products — Determination of adhesion/cohesion
properties of sealants after exposure to heat, water and artificial light through glass
3 Terms and definitions
For the purposes of this document, the terms and definitions given in ISO 6927 apply.
ISO and IEC maintain terminological databases for use in standardization at the following addresses:
— ISO Online browsing platform: available at https: //www .iso .org/obp
— IEC Electropedia: available at http: //www .electropedia .org/
4 Principle
This method measures the visible staining attributed to joint sealants on porous substrates that is a
result of the conditioning specified.
A sealant is applied and cured between two pieces of porous substrate. The test specimens are
compressed and then subjected to heat aging and/or cold aging and/or aging in actinic radiation
accelerated weathering equipment. After aging, the test specimens are evaluated and visible staining is
recorded on the exterior surface and in the interior of the substrate after visual inspection of changes in
surface appearance and measurements of maximum and minimum stain width and stain penetration.
5 Apparatus
5.1 Substrate materials
For the preparation of each test specimen, two substrate pieces of the same material are required with
dimensions as shown in Figure 1.
5.2 Spacers
For the preparation of the test specimens, the spacers shall be of a cross-section 12 mm × 12 mm, with
a non-adherent surface (see Figure 1).
If the spacers are made of a material to which the sealant adheres, their surfaces should be made non-
adherent, e.g. by a thin wax coating.
5.3 Non-adherent substrate
For the preparation of test specimens, the non-adherent substrate can be, for example, a polyethylene
(PE) film or a micro-porous polytetrafluorethylene (PTFE) film, preferably on the advice of the sealant
manufacturer.
5.4 Masking tape
The masking tape shall be suitable for covering the tested surface of the substrates (see Figure 1) to
prevent sealant contamination during specimen preparation.
5.5 Ventilated convection-type oven
The ventilated convection-type oven shall be capable of being maintained at (70 ± 2) °C.
5.6 Refrigerated enclosure
The refrigerated enclosure shall be capable of being maintained at (−20 ± 2) °C.
5.7 Clamps or other device
The cla
...


NORME ISO
INTERNATIONALE 16938-1
Deuxième édition
2019-09
Bâtiments et ouvrages de génie
civil — Détermination du tachage
des supports poreux par les mastics
utilisés dans les joints —
Partie 1:
Essai avec compression
Buildings and civil engineering works — Determination of the
staining of porous substrates by sealants used in joints —
Part 1: Test with compression
Numéro de référence
©
ISO 2019
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2019
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: +41 22 749 01 11
Fax: +41 22 749 09 47
E-mail: copyright@iso.org
Web: www.iso.org
Publié en Suisse
ii © ISO 2019 – Tous droits réservés

Sommaire Page
Avant-propos .iv
1 Domaine d’application . 1
2 Références normatives . 1
3 Termes et définitions . 1
4 Principe . 2
5 Appareillage . 2
5.1 Supports . 2
5.2 Espaceurs . 2
5.3 Support anti-adhérent . 2
5.4 Adhésif de masquage . 2
5.5 Étuve ventilée à convection . 2
5.6 Enceinte réfrigérée . 2
5.7 Dispositif de serrage ou autre dispositif . 2
5.8 Appareil d'essai de vieillissement climatique accéléré par rayonnement . 3
5.8.1 Généralités . 3
5.8.2 Enceinte d’essai à condensation équipée de lampes fluorescentes UV . 3
5.8.3 Enceinte d’essai à lampe au xénon . 3
5.9 Thermomètre à étalon noir/à panneau noir . 3
5.10 Dispositif de mesure. 3
6 Préparation des éprouvettes . 3
7 Conditionnement . 5
8 Mode opératoire d’essai. 5
8.1 Compression . 5
8.2 Modes opératoires de vieillissement . 5
8.2.1 Généralités . 5
8.2.2 Vieillissement par action de la chaleur . 5
8.2.3 Vieillissement par action du froid . 5
8.2.4 Vieillissement climatique accéléré (stabilité à la lumière) . 5
9 Détection du tachage . 6
9.1 Généralités . 6
9.2 Détection à la surface du support . 6
9.3 Détection dans la profondeur du support . 6
9.4 Expression des résultats . 8
10 Rapport d’essai . 8
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes
nationaux de normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est
en général confiée aux comités techniques de l'ISO. Chaque comité membre intéressé par une étude
a le droit de faire partie du comité technique créé à cet effet. Les organisations internationales,
gouvernementales et non gouvernementales, en liaison avec l'ISO participent également aux travaux.
L'ISO collabore étroitement avec la Commission électrotechnique internationale (IEC) en ce qui
concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier, de prendre note des différents
critères d'approbation requis pour les différents types de documents ISO. Le présent document a été
rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir www
.iso .org/ directives).
L'attention est attirée sur le fait que certains des éléments du présent document peuvent faire l'objet de
droits de propriété intellectuelle ou de droits analogues. L'ISO ne saurait être tenue pour responsable
de ne pas avoir identifié de tels droits de propriété et averti de leur existence. Les détails concernant
les références aux droits de propriété intellectuelle ou autres droits analogues identifiés lors de
l'élaboration du document sont indiqués dans l'Introduction et/ou dans la liste des déclarations de
brevets reçues par l'ISO (voir www .iso .org/ brevets).
Les appellations commerciales éventuellement mentionnées dans le présent document sont données
pour information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un
engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l'ISO liés à l'évaluation de la conformité, ou pour toute information au sujet de l'adhésion
de l'ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles
techniques au commerce (OTC), voir www .iso .org/ avant -propos.
Le présent document a été élaboré par le comité technique ISO/TC 59, Bâtiments et ouvrages de génie
civil, sous-comité SC 8, Mastics.
Cette deuxième édition annule et remplace la première édition (ISO 16938-1:2008), qui a fait l’objet
d’une révision technique.
Les principales modifications par rapport à l’édition précédente sont les suivantes:
— le titre du document a été modifié.
— les figures du présent document ont été modifiées et des notes ont été ajoutées à titre explicatif.
— la Figure 4 a été remplacée par le Tableau 2.
Une liste de toutes les parties de la série ISO 16938 se trouve sur le site web de l’ISO.
Il convient que l’utilisateur adresse tout retour d’information ou toute question concernant le présent
document à l’organisme national de normalisation de son pays. Une liste exhaustive desdits organismes
se trouve à l’adresse www .iso .org/ fr/ members .html.
iv © ISO 2019 – Tous droits réservés

NORME INTERNATIONALE ISO 16938-1:2019(F)
Bâtiments et ouvrages de génie civil — Détermination du
tachage des supports poreux par les mastics utilisés dans
les joints —
Partie 1:
Essai avec compression
1 Domaine d’application
La présente partie de l’ISO 16938 spécifie la méthode pour déterminer le tachage des supports poreux
(par exemple marbre, calcaire, grès ou granit) par les mastics utilisés dans la construction des bâtiments.
La méthode évalue la probabilité d’apparition d’une coloration précoce, sur un support poreux, due au
suintement ou à l’infiltration des matériaux des mastics. Le résultat de l’essai est spécifique du mastic
et du support soumis à l’essai et ne peut être extrapolé à d’autres formulations de mastics ou à d’autres
supports poreux. Durant cet essai accéléré, si le mastic ne tache pas ou ne décolore pas les supports,
cela ne signifie pas que le mastic soumis à l’essai sur une période plus longue ne tachera pas ou ne
décolorera pas le support poreux.
2 Références normatives
Les documents suivants sont cités dans le texte de sorte qu’ils constituent, pour tout ou partie de leur
contenu, des exigences du présent document. Pour les références datées, seule l’édition citée s’applique.
Pour les références non datées, la dernière édition du document de référence s'applique (y compris les
éventuels amendements).
ISO 4892-1, Plastiques — Méthodes d'exposition à des sources lumineuses de laboratoire — Partie 1: Lignes
directrices générales
ISO 4892-2:2013, Plastiques — Méthodes d'exposition à des sources lumineuses de laboratoire — Partie 2:
Lampes à arc au xénon
ISO 4892-3, Plastiques — Méthodes d'exposition à des sources lumineuses de laboratoire — Partie 3:
Lampes fluorescentes UV
ISO 6927, Bâtiments et ouvrages de génie civil — Mastics — Vocabulaire
ISO 11431:2002, Construction immobilière — Produits pour joints — Détermination des propriétés
d'adhésivité/cohésion des mastics après exposition à la chaleur, à l'eau et à la lumière artificielle à travers
le verre
3 Termes et définitions
Pour les besoins du présent document, les termes et les définitions de ISO 6927 s’appliquent.
L’ISO et l’IEC tiennent à jour des bases de données terminologiques destinées à être utilisées en
normalisation, consultables aux adresses suivantes:
— ISO Online browsing platform: disponible à l’adresse https:// www .iso .org/ obp
— IEC Electropedia: disponible à l’adresse http:// www .electropedia .org/
4 Principe
Cette méthode mesure le tachage visible attribué à des joints de mastics appliqués sur des supports
poreux résultant de conditions spécifiques.
Le mastic est appliqué entre deux éléments de support poreux. Après son durcissement, les éprouvettes
sont comprimées, puis soumises à un vieillissement par action de la chaleur et/ou à un vieillissement
par action du froid et/ou à un vieillissement climatique accéléré par un équipement d’essai de stabilité
à la lumière. Après vieillissement, les éprouvettes sont évaluées en enregistrant le tachage visible sur
la surface extérieure et à l’intérieur du support, en réalisant un examen visuel des changements de
l’aspect de surface et en mesurant la largeur maximale et minimale ainsi que la pénétration de la tâche.
5 Appareillage
5.1 Supports
La préparation de chaque éprouvette requiert deux supports constitués du même matériau et ayant les
dimensions indiquées à la Figure 1.
5.2 Espaceurs
Pour la préparation des éprouvettes, ils sont de sections transversales 12 mm × 12 mm, avec une
surface anti-adhérente (voir la Figure 1).
NOTE Si les espaceurs sont constitués d’un matériau adhérant au mastic, il convient que leur surface soit
rendue non adhérente, par exemple par application d’une fine c
...


NORME ISO
INTERNATIONALE 16938-1
Deuxième édition
2019-09
Bâtiments et ouvrages de génie
civil — Détermination du tachage
des supports poreux par les mastics
utilisés dans les joints —
Partie 1:
Essai avec compression
Buildings and civil engineering works — Determination of the
staining of porous substrates by sealants used in joints —
Part 1: Test with compression
Numéro de référence
©
ISO 2019
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2019
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: +41 22 749 01 11
Fax: +41 22 749 09 47
E-mail: copyright@iso.org
Web: www.iso.org
Publié en Suisse
ii © ISO 2019 – Tous droits réservés

Sommaire Page
Avant-propos .iv
1 Domaine d’application . 1
2 Références normatives . 1
3 Termes et définitions . 1
4 Principe . 2
5 Appareillage . 2
5.1 Supports . 2
5.2 Espaceurs . 2
5.3 Support anti-adhérent . 2
5.4 Adhésif de masquage . 2
5.5 Étuve ventilée à convection . 2
5.6 Enceinte réfrigérée . 2
5.7 Dispositif de serrage ou autre dispositif . 2
5.8 Appareil d'essai de vieillissement climatique accéléré par rayonnement . 3
5.8.1 Généralités . 3
5.8.2 Enceinte d’essai à condensation équipée de lampes fluorescentes UV . 3
5.8.3 Enceinte d’essai à lampe au xénon . 3
5.9 Thermomètre à étalon noir/à panneau noir . 3
5.10 Dispositif de mesure. 3
6 Préparation des éprouvettes . 3
7 Conditionnement . 5
8 Mode opératoire d’essai. 5
8.1 Compression . 5
8.2 Modes opératoires de vieillissement . 5
8.2.1 Généralités . 5
8.2.2 Vieillissement par action de la chaleur . 5
8.2.3 Vieillissement par action du froid . 5
8.2.4 Vieillissement climatique accéléré (stabilité à la lumière) . 5
9 Détection du tachage . 6
9.1 Généralités . 6
9.2 Détection à la surface du support . 6
9.3 Détection dans la profondeur du support . 6
9.4 Expression des résultats . 8
10 Rapport d’essai . 8
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes
nationaux de normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est
en général confiée aux comités techniques de l'ISO. Chaque comité membre intéressé par une étude
a le droit de faire partie du comité technique créé à cet effet. Les organisations internationales,
gouvernementales et non gouvernementales, en liaison avec l'ISO participent également aux travaux.
L'ISO collabore étroitement avec la Commission électrotechnique internationale (IEC) en ce qui
concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier, de prendre note des différents
critères d'approbation requis pour les différents types de documents ISO. Le présent document a été
rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir www
.iso .org/ directives).
L'attention est attirée sur le fait que certains des éléments du présent document peuvent faire l'objet de
droits de propriété intellectuelle ou de droits analogues. L'ISO ne saurait être tenue pour responsable
de ne pas avoir identifié de tels droits de propriété et averti de leur existence. Les détails concernant
les références aux droits de propriété intellectuelle ou autres droits analogues identifiés lors de
l'élaboration du document sont indiqués dans l'Introduction et/ou dans la liste des déclarations de
brevets reçues par l'ISO (voir www .iso .org/ brevets).
Les appellations commerciales éventuellement mentionnées dans le présent document sont données
pour information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un
engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l'ISO liés à l'évaluation de la conformité, ou pour toute information au sujet de l'adhésion
de l'ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles
techniques au commerce (OTC), voir www .iso .org/ avant -propos.
Le présent document a été élaboré par le comité technique ISO/TC 59, Bâtiments et ouvrages de génie
civil, sous-comité SC 8, Mastics.
Cette deuxième édition annule et remplace la première édition (ISO 16938-1:2008), qui a fait l’objet
d’une révision technique.
Les principales modifications par rapport à l’édition précédente sont les suivantes:
— le titre du document a été modifié.
— les figures du présent document ont été modifiées et des notes ont été ajoutées à titre explicatif.
— la Figure 4 a été remplacée par le Tableau 2.
Une liste de toutes les parties de la série ISO 16938 se trouve sur le site web de l’ISO.
Il convient que l’utilisateur adresse tout retour d’information ou toute question concernant le présent
document à l’organisme national de normalisation de son pays. Une liste exhaustive desdits organismes
se trouve à l’adresse www .iso .org/ fr/ members .html.
iv © ISO 2019 – Tous droits réservés

NORME INTERNATIONALE ISO 16938-1:2019(F)
Bâtiments et ouvrages de génie civil — Détermination du
tachage des supports poreux par les mastics utilisés dans
les joints —
Partie 1:
Essai avec compression
1 Domaine d’application
La présente partie de l’ISO 16938 spécifie la méthode pour déterminer le tachage des supports poreux
(par exemple marbre, calcaire, grès ou granit) par les mastics utilisés dans la construction des bâtiments.
La méthode évalue la probabilité d’apparition d’une coloration précoce, sur un support poreux, due au
suintement ou à l’infiltration des matériaux des mastics. Le résultat de l’essai est spécifique du mastic
et du support soumis à l’essai et ne peut être extrapolé à d’autres formulations de mastics ou à d’autres
supports poreux. Durant cet essai accéléré, si le mastic ne tache pas ou ne décolore pas les supports,
cela ne signifie pas que le mastic soumis à l’essai sur une période plus longue ne tachera pas ou ne
décolorera pas le support poreux.
2 Références normatives
Les documents suivants sont cités dans le texte de sorte qu’ils constituent, pour tout ou partie de leur
contenu, des exigences du présent document. Pour les références datées, seule l’édition citée s’applique.
Pour les références non datées, la dernière édition du document de référence s'applique (y compris les
éventuels amendements).
ISO 4892-1, Plastiques — Méthodes d'exposition à des sources lumineuses de laboratoire — Partie 1: Lignes
directrices générales
ISO 4892-2:2013, Plastiques — Méthodes d'exposition à des sources lumineuses de laboratoire — Partie 2:
Lampes à arc au xénon
ISO 4892-3, Plastiques — Méthodes d'exposition à des sources lumineuses de laboratoire — Partie 3:
Lampes fluorescentes UV
ISO 6927, Bâtiments et ouvrages de génie civil — Mastics — Vocabulaire
ISO 11431:2002, Construction immobilière — Produits pour joints — Détermination des propriétés
d'adhésivité/cohésion des mastics après exposition à la chaleur, à l'eau et à la lumière artificielle à travers
le verre
3 Termes et définitions
Pour les besoins du présent document, les termes et les définitions de ISO 6927 s’appliquent.
L’ISO et l’IEC tiennent à jour des bases de données terminologiques destinées à être utilisées en
normalisation, consultables aux adresses suivantes:
— ISO Online browsing platform: disponible à l’adresse https:// www .iso .org/ obp
— IEC Electropedia: disponible à l’adresse http:// www .electropedia .org/
4 Principe
Cette méthode mesure le tachage visible attribué à des joints de mastics appliqués sur des supports
poreux résultant de conditions spécifiques.
Le mastic est appliqué entre deux éléments de support poreux. Après son durcissement, les éprouvettes
sont comprimées, puis soumises à un vieillissement par action de la chaleur et/ou à un vieillissement
par action du froid et/ou à un vieillissement climatique accéléré par un équipement d’essai de stabilité
à la lumière. Après vieillissement, les éprouvettes sont évaluées en enregistrant le tachage visible sur
la surface extérieure et à l’intérieur du support, en réalisant un examen visuel des changements de
l’aspect de surface et en mesurant la largeur maximale et minimale ainsi que la pénétration de la tâche.
5 Appareillage
5.1 Supports
La préparation de chaque éprouvette requiert deux supports constitués du même matériau et ayant les
dimensions indiquées à la Figure 1.
5.2 Espaceurs
Pour la préparation des éprouvettes, ils sont de sections transversales 12 mm × 12 mm, avec une
surface anti-adhérente (voir la Figure 1).
NOTE Si les espaceurs sont constitués d’un matériau adhérant au mastic, il convient que leur surface soit
rendue non adhérente, par exemple par application d’une fine c
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.