ISO 2713:1973

Copper and copper alloys — Rockwell hardness test (B, F and G scales)

Cuivre et alliages de cuivre — Essai de dureté Rockwell (Échelles B, F, G)

General Information

• Status: Withdrawn
• Publication Date: 31-Oct-1973
• Withdrawal Date: 31-Oct-1973
• ICS: 77.040.10 - Mechanical testing of metals
• Technical Committee: ISO/TC 164/SC 3 - Hardness testing
• Drafting Committee: ISO/TC 164/SC 3 - Hardness testing
• Current Stage: 9599 - Withdrawal of International Standard
• Completion Date: 01-Nov-1986

Relations

• Revised: ISO 6508:1986 - Metallic materials — Hardness test — Rockwell test (scales A - B - C - D - E - F - G - H - K)
• Effective Date: 15-Apr-2008
• Revised: SIST ISO 6508:1995 - Metallic materials -- Hardness test -- Rockwell test (scales A - B - C - D - E - F - G - H - K)
• Effective Date: 12-May-2008

Standards Content (Sample)

@ 2713
INTERNATIONAL STANDARD
‘ax&
INTERNATIONAL ORGANIZATION FOR STANDARDIZATION *MEX~YHAPOLIHAR OPTAHM3AUAR IT0 CTAHAAPTA3AUMH .ORGANISATION INTERNATIONALE DE NORMALISATION
Copper and copper alloys - Rockwell hardness test
(B, F and G scales)
First edition - 1973-1 1-01
-
UDC 669.3 : 620.178.152.42 Ref. No. IS0 2713-1973 (E)
w
-
p>
r-
Descriptors : copper, copper alloys, tests, hardness tests, Rockwell hardness
...
1,
c
IC
F1
Price based on 5 pages
z

---------------------- Page: 1 ----------------------
FOREWORD
IS0 (the International Organization for Standardization) is a worldwide federation
of national standards institutes (IS0 Member Bodies). The work of developing
International Standards is carried out through IS0 Technical Committees. Every
Member Body interested in a subject for which a Technical Committee has been set
up has the right to be represented on that Committee. International organizations,
governmental and non-governmental, in liaison with ISO, also take part in the work.
Draft International Standards adopted by the Technical Committees are circulated
to the Member Bodies for approval before their acceptance as International
Standards by the IS0 Council.
International Standard IS0 2713 was drawn up by Technical Committee
ISO/TC26, Copper and copper a//oys, and circulated to the Member Bodies in
June 1972.
It has been approved by the Member Bodies of the following countries :
Hungary Romania
Austria
India South Africa, Rep. of
Belgium
Brazil Ireland Sweden
Morocco Switzerland
Chile
Czechoslovakia Netherlands Turkey
New Zealand United Kingdom
Denmark
Egypt, Arab Rep. of Norway U.S.A.
Poland U.S.S.R.
Finland
Portugal
France
The Member Body of the following country expressed disapproval of the document
on technical grounds :
Austra I i a
O International Organization for Standardization, 1973
Printed in Switzerland

---------------------- Page: 2 ----------------------
___
INTERNATIONAL STANDARD IS0 2713-1973 (E)
Copper and copper alloys - Rockwell hardness test
(€3, F and G scales)
1 SCOPE AND FIELD OF APPLICATION
This International Standard specifies the method for carrying out the Rockwell hardness test (B, F and G scales) for copper
and copper alloys using a steel ball indenter.
For C scale tests using a diamond cone indenter reference should be made to ISO/R 80.
2 REFERENCES
ISOIR 80, Rockwell hardness test f5 and C scales) for steel.
ISOIR 286, IS0 System of limits and fits - Part 1 : General, tolerances and deviations.
ISOIR 674, Calibration of standardized blocks to be used for Rockwell B and C scale hardness testing machines.
ISOIR 7 16, Verification of Rockwell B and C scale hardness testing machines.
3 PRINCIPLE
The test consists in forcing a ball into the surface of a test piece in two operations and measuring the permanent increase e of
the depth of indentation by means of a depth gauge under defined conditions.
The unit of measurement for e is 0,002 mm; from the measurement of e, a number, known as the Rockwell hardness, is
deduced.
The test is carried out at ambient temperature, unless otherwise specified.
1

---------------------- Page: 3 ----------------------
IS0 2713-1973 (E)
4 SYMBOLS AND DESIGNATIONS
I l
- Surface of test piece
eo Datum line
130
t I t
II
Symbol
Diameter of ball = 1,587 5 mm (1116 in)
Preliminary load = 98,06 N ( 10 kgf)
Additional load = 882,52 N ( 90 kgf) for the B scale, or
= 490,33 N ( 50 kgf) for the F scale, or
= 1 3759 N (140 kgf) for the G scale
F Total load = Fo + F, = 98,06 t 882,52 = 98458 N (100 kgf) for the B scale, or
= 98,06 + 490,33 = 588,s N ( 60 kgf) for the F scale, or
=98,06 + 1 372,9 = 1 470,96 N (150 kgf) for the G scale
Depth of indentation under preliminary load before application of additional load
h0
Increase in depth of indentation under additional load
h,
e
Permanent increase of depth of indentation under preliminary load after removalof additional load,
the increase being expressed in units of 0,002 mm
HRB Rockwell hardness
HRF
HRG Rockwell hardness
NOTE -- The Rockwell hardness is denoted by the symbol HRB, HRF or HRG, preceded by the hardness value.
Exampie : 70 HRF = a Rockwell hardness of 70 measured on the F-scale.
2

---------------------- Page: 4 ----------------------
IS0 2713-1973 (E)
5 TESTING EQUIPMENT 6.3 Bring the indenter into contact with the test surface,
and apply the preliminary load FO = 98,06 f 1,96 N
(IO 1: 0,2 kgf) in a direction normal to the test surface,
5.1 Testing machines
without shock or vibration. Care shall be taken that this
The testing machine shall be verified in accordance with the
load is not exceeded.
principles of ISO/R 716.
6.4 Set the dial of the indicator at the initial position and
5.2 Standardized blocks for verification of testing
increase the load, without shock or vibration, within a
machines period of 4 to 8 s by the value of the additional load FI,
thus obtaining a total load :
Standardized blocks shall be calibrated in accordance with
ISO/R 674 except that, if copper or copper alloy blocks F = Fo + FI = 980,58 f 6,37 N (100 f 0,65 kgf)
are used, the duration of the application of the additional for the B scale:
load (section 8 of ISO/R 674) shall be in accordance with
...

NORME INTERNATIONALE 2713
INTERNATIONAL ORGANIZATION FOR STANDAROIZATION .MEEAYHAPOfiHAR OPrAHHOAUHII Il0 CTAHlTAPTH3AUm.ORGANISATlON INTERNATIONALE DE NORMALISATION
Cuivre et alliages de cuivre - Essai de dureté Rockwell
0
(Échelles B, F, G)
Première édition - 1973-1 1-01
~
Réf. NO : IS0 2713-1973 (F)
CDU 669.3 : 620.178.152.42
Descripteurs : cuivre, alliage de cuivre, essai, essai de dureté. dureté Rockwell.
Prix bad sur 5 pages

---------------------- Page: 1 ----------------------
AVANT-PROPOS
IS0 (Organisation Internationale de Normalisation) est une fédération mondiale
d'organismes nationaux de normalisation (Comités Membres ISO). L'élaboration de
Normes Internationales est confiée aux Comités Techniques ISO. Chaque Comité
Membre intéressé par une étude a le droit de faire partie du Comité Technique
correspondant. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec i'IS0, participent également aux travaux.
les Comités Techniques sont
Les Projets de Normes Internationales adoptés par
soumis aux Comités Membres pour approbation, avant leur acceptation comme
Normes Internationales par le Conseil de I'ISO.
La Norme Internationale IS0 2713 a été établie par le Comité Technique
ISO/TC26, Cuivre et alliages de cuivre, et soumise aux Comités Membres en
juin 1972.
Elle a été approuvée par les Comités Membres des pays suivants :
Afrique du Sud, Rép. d' Hongrie Roumanie
Autriche Inde Royaume-Uni
Belgique Irlande Suède
Brésil Maroc Suisse
Chili Norvège Tchécoslovaquie
Danemark
Nouvelle-Zélande Turquie
Egypte, Rép. arabe d' U.R.S.S.
Pays- Bas
Finlande U.S.A.
Pologne
France Portugal
Le Comité Membre du pays suivant a désapprouvé le document pour des raisons
techniques :
Australie
@ Or(#inisation Internationale de Normalisation, 1973 O
Imprimé en Suisse.

---------------------- Page: 2 ----------------------
NORME INTERNATIONALE IS0 2713-1973 (FI
Cuivre et alliages de cuivre - Essai de dureté Rockwell
(Échelles B, F, G)
1 OBJET ET DOMAINE D'APPLICATION
La présente Norme Internationale spécifie la méthode d'essai de la dureté Rockwell (échelles B, F et G) pour le cuivre et les
alliages de cuivre, effectué avec une bille en acier.
Pour les essais à l'échelle C effectués avec un cône de diamant, se référer à I'ISOIR 80.
z RÉFÉRENCES
ISOIR 00, Essai de dureté Rockwell (Échelles 6 et CI pour l'acier.
ISOIR 286, Système IS0 de tolérances et d'ajustements - Première partie : Généralités, tolérances et écarts.
ISOIR 674, Etalonnage des blocs de référence 2 utiliser pour les machines d'essai de dureté Rockwell (Échelles B et C).
ISOIR 716, ContrBle des machines d'essai de dureté Rockwell (Échelles B et CI.
3 PRINCIPE
L'essai consiste à imprimer une bille en acier, en deux temps, dans la surface de l'éprouvette, et à mesurer l'accroissement
rémanent e de la profondeur de l'empreinte de ce pénétrateur au moyen d'un indicateur d'enfoncement dans des conditions
déterminées.
L'unité de mesure de e est de 0,002 mm; le nombre représentant la valeur e est appelé dureté Rockwell.
Sauf spécification contraire, l'essai est effectué à la température ambiante.
1

---------------------- Page: 3 ----------------------
~ IS0 2713-1973 (F)
4 SYMBOLES ET DÉSIGNATIONS
T
-Surface de la pièce A essayer
de la mesure
FIGURE
Symbole
Désignation
D
Diamètre de la bille = 1,587 5 mm (1/16 in)
Charge initiale =
98,06 N ( 10 kgf)
FO
Surcharge = 882,52 N ( 90 kgf) pour l'échelle B, ou
FI ,
= 490,33 N ( 50 kgfl pour l'échelle F, ou
= 1 372,9 N (140 kgf) pour l'échelle G
F
Charge totale = Fo + F, = 98,06 + 882,52 = 980,58 N (100 kgf) pour I'6chelle B, ou
= 98.06 + 490,33 = 588,39 N ( 60 kgf) pour l'échelle F, ou
= 98,06 + 1 372,9 = 1 470.96 N (150 kgf) pour l'échelle G
Profondeur de l'empreinte sous la charge initiale avant application de la surcharge
h0
Accroissement de la profondeur de l'empreinte sous l'effet de la surcharge
hl
e
Accroissement rémanent de la profondeur de l'empreinte sous la charge initiale après retrait de la surcharge,
exprid en unités 0,002 mm
HRB
Dureté Rockwell B
HRF Dureté Rockwell F = 130-e
HRG Dureté Rockwell G 3
NOTE - La dureté Rockwell est désignée par le symbole HRB,HRF ou HRG, précédé par la valeur de la dureté.
Exemple : 70 HRF = dureté Rockwell de 70 mesurée sur l'échelle F.
2

---------------------- Page: 4 ----------------------
IS0 2713-1973 (F)
6.3 La bille doit être amenée au contact de la surface à
5 ÉQUIPEMENT D'ESSAI
essayer, et la charge initiale Fo = 98,06 f 1,96 N:
(IO f 0.2 kgf) doit être appliquée perpendiculairement
5.1 Machines d'essai
à cette surface, sans choc ni vibration. Prendre bien soin de
La machine d'essai doit être contrôlée conformément aux ne pas dépasser cette charge.
principes de I'ISO/R 716.
6.4 Le cadran de l'indicateur de profondeur doit être
ajusté à position initiaie de l'échelle et la charge augmentée,
5.2 Blocs de référence pour le contrôle des machines
sans choc ni vibration, en 4 à 8 s, de la valeur de la
d'essai
surcharge F,, jusqu'à la charge totale :
Les blocs de référence doivent être tarés conformément à
F = Fo + F, = 980,58 f 6,37 N (1 O0 f 0,65 kgf)
I'ISO/R 674, sauf en cas d'utilisation d'étalons en cuivre ou
pour 1,'échelle B;
en alliages de cuivre, auquel cas la durée d'application de la
588.39 f 4,41 N (60 f 0,45 kgf)
charge additionnelle (chapitre 8 de I'ISO/R 674) doit être
pour l'échelle F;
conforme à 6.5 a) de la présente Norme Internationale.
1 470,96 f 8,82 N (150 I: 0,90 kgf)
G.
pour l'échelle
5.3
...