ISO 34-1:2004

Rubber, vulcanized or thermoplastic — Determination of tear strength — Part 1: Trouser, angle and crescent test pieces

ISO 34-1:2004 specifies three test methods for the determination of the tear strength of vulcanized rubber, namely Method A, using a trouser test piece; Method B, using an angle test piece, with or without a nick of specified depth; Method C, using a crescent test piece with a nick. Method A, using the trouser test piece, is preferred because it is not sensitive to the length of the cut, unlike the other two test pieces in which the nick has to be very closely controlled. In addition, the results obtained are more easily related to the fundamental tear properties of the material and are less sensitive to modulus effects (provided that the leg extension is negligible) and the rate of propagation of the tear is directly related to the rate of grip separation. With some rubbers, the propagation of tear is not smooth (knotty tear), and analysis of results may be difficult. Method B, procedure (a), using an angle test piece without a nick, is a combination of tear initiation and propagation. Stress is built up at the point of the angle until it is sufficient to initiate a tear and then further stresses propagate this tear. However, it is only possible to measure the overall force required to rupture the test piece, and, therefore, the force cannot be resolved into two components producing initiation and propagation. Method B, procedure (b), using an angle test piece with a nick, measures the force required to propagate a nick already produced in the test piece. The rate of propagation is not directly related to the jaw speed. Method C, using a crescent test piece, also measures the force required to propagate a nick already produced in the test piece and the rate of propagation is not related to the jaw speed. A separate method for the determination of the tear strength of small test pieces of vulcanized rubber (Delft test pieces) is specified in ISO 34-2.

Caoutchouc vulcanisé ou thermoplastique — Détermination de la résistance au déchirement — Partie 1: Éprouvettes pantalon, angulaire et croissant

L'ISO 34-1:2004 spécifie trois méthodes pour la détermination de la résistance au déchirement du caoutchouc vulcanisé ou thermoplastique, à savoir: La méthode A, utilisant une éprouvette pantalon; La méthode B, utilisant une éprouvette angulaire, avec ou sans entaille de profondeur spécifiée; La méthode C, utilisant une éprouvette croissant entaillée. La méthode A, qui utilise l'éprouvette pantalon, est utilisée de préférence, car elle n'est pas sensible à la longueur de la coupure, à la différence des deux autres éprouvettes dans lesquelles l'entaille doit être très étroitement contrôlée. En outre, les résultats obtenus sont plus facilement reliés aux caractéristiques de déchirement fondamentales du matériau et sont moins sensibles aux effets du module (pourvu que l'extension des jambes soit négligeable), et la vitesse de propagation de la déchirure est directement liée à la vitesse de séparation des mâchoires. Avec certains caoutchoucs, la propagation du déchirement n'est pas régulière et l'analyse des résultats peut être difficile. La méthode B, mode opératoire (a), qui utilise une éprouvette angulaire sans entaille, associe l'initiation de l'amorçage et la propagation de la déchirure. La contrainte est concentrée à la base de l'angle jusqu'à ce qu'elle soit suffisante pour amorcer une déchirure qui se propage sous l'effet de contraintes ultérieures. Cependant, comme il est seulement possible de mesurer la force globale nécessaire pour rompre l'éprouvette, la force ne peut être décomposée en deux composantes dont une produit l'initiation et l'autre la propagation. La méthode B, mode opératoire (b), qui utilise une éprouvette angulaire entaillée, mesure la force nécesaire pour propager une entaille déjà pratiquée dans l'éprouvette et la vitesse de propagation n'est pas directement liée à la vitesse de séparation des mâchoires. La méthode C, qui utilise une éprouvette croissant, mesure la force nécessaire pour propager une entaille déjà pratiquée dans l'éprouvette et la vitesse de propagation n'est pas liée à la vitesse de séparation des mâchoires. Une méthode particulière de détermination de la résistance au déchirement de petites éprouvettes de caoutchouc vulcanisé (éprouvettes de Delft) est spécifiée dans l'ISO 34-2.

General Information

• Status: Withdrawn
• Publication Date: 23-Mar-2004
• Withdrawal Date: 23-Mar-2004
• ICS: 83.060 - Rubber
• Technical Committee: ISO/TC 45/SC 2 - Testing and analysis
• Drafting Committee: ISO/TC 45/SC 2/WG 1 - Physical properties
• Current Stage: 9599 - Withdrawal of International Standard
• Completion Date: 03-Sep-2010

Relations

• Revised: ISO 34-1:2010 - Rubber, vulcanized or thermoplastic — Determination of tear strength — Part 1: Trouser, angle and crescent test pieces
• Effective Date: 15-Apr-2008
• Revises: ISO 34-1:1994 - Rubber, vulcanized or thermoplastic — Determination of tear strength — Part 1: Trouser, angle and crescent test pieces
• Effective Date: 15-Apr-2008
• Revises: ISO 34-1:1994/Cor 1:1999 - Rubber, vulcanized or thermoplastic — Determination of tear strength — Part 1: Trouser, angle and crescent test pieces — Technical Corrigendum 1
• Effective Date: 15-Apr-2008
• Consolidated By: ISO 34101-2:2019 - Sustainable and traceable cocoa — Part 2: Requirements for performance (related to economic, social and environmental aspects)
• Effective Date: 06-Jun-2022

Standards Content (Sample)

INTERNATIONAL ISO
STANDARD 34-1
Second edition
2004-03-15
Rubber, vulcanized or thermoplastic —
Determination of tear strength —
Part 1:
Trouser, angle and crescent test pieces
Caoutchouc vulcanisé ou thermoplastique — Détermination de la
résistance au déchirement —
Partie 1: Éprouvettes pantalon, angulaire et croissant

Reference number
ISO 34-1:2004(E)
©
ISO 2004

---------------------- Page: 1 ----------------------
ISO 34-1:2004(E)
PDF disclaimer
This PDF file may contain embedded typefaces. In accordance with Adobe's licensing policy, this file may be printed or viewed but shall
not be edited unless the typefaces which are embedded are licensed to and installed on the computer performing the editing. In
downloading this file, parties accept therein the responsibility of not infringing Adobe's licensing policy. The ISO Central Secretariat
accepts no liability in this area.
Adobe is a trademark of Adobe Systems Incorporated.
Details of the software products used to create this PDF file can be found in the General Info relative to the file; the PDF-creation
parameters were optimized for printing. Every care has been taken to ensure that the file is suitable for use by ISO member bodies. In the
unlikely event that a problem relating to it is found, please inform the Central Secretariat at the address given below.
© ISO 2004
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means,
electronic or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address below or
ISO's member body in the country of the requester.
ISO copyright office
Case postale 56  CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail [e-mail]
Web www.iso.org
Published in Switzerland
©
ii ISO 2004 – All rights reserved

---------------------- Page: 2 ----------------------
ISO 34-1:2004(E)
Contents Page
1 Scope . 1
2 Normative references . 2
3 Terms and definitions . 2
4 Principle . 2
5 Apparatus . 3
6 Test pieces . 6
7 Number of tests . 7
8 Temperature of test . 7
9 Procedure . 7
10 Expression of results . 7
11 Precision . 8
12 Test report . 8
Annex A (informative) Guidance for using precision results . 10
Annex B (informative) Formulations for compounds A, B and C used in ITP . 11
Bibliography . 12
©
ISO 2004 – All rights reserved iii

---------------------- Page: 3 ----------------------
ISO 34-1:2004(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies
(ISO member bodies). The work of preparing International Standards is normally carried out through ISO
technical committees. Each member body interested in a subject for which a technical committee has been
established has the right to be represented on that committee. International organizations, governmental and
non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the International
Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2.
The main task of technical committees is to prepare International Standards. Draft International Standards
adopted by the technical committees are circulated to the member bodies for voting. Publication as an
International Standard requires approval by at least 75 % of the member bodies casting a vote.
Attention is drawn to the possibility that some of the elements of this document may be the subject of patent
rights. ISO shall not be held responsible for identifying any or all such patent rights.
ISO 34-1 was prepared by Technical Committee ISO/TC 45, Rubber and rubber products, Subcommittee SC 2,
Testing and analyses.
This second edition cancels and replaces the first edition (ISO 34-1:1994), of which it constitutes a minor
revision (a number of corrections have been made in Figure 2). It also incorporates the Technical Corrigendum
ISO 34-1:1994/Cor.1:1999.
ISO34 consists of the following parts, under the general title Rubber, vulcanized or thermoplastic —
Determination of tear strength:
— Part 1: Trouser, angle and crescent test pieces
— Part 2: Small (Delft) test pieces
©
iv ISO 2004 – All rights reserved

---------------------- Page: 4 ----------------------
INTERNATIONAL STANDARD ISO 34-1:2004(E)
Rubber, vulcanized or thermoplastic — Determination of tear
strength —
Part 1:
Trouser, angle and crescent test pieces
1Scope
This part of ISO 34 specifies three test methods for the determination of the tear strength of vulcanized and
thermoplastic rubber, namely
— Method A, using a trouser test piece;
— Method B, using an angle test piece, with or without a nick of specified depth;
— Method C, using a crescent test piece with a nick.
The value of tear strength obtained depends on the shape of the test piece, speed of stretching and
temperature of test. It may also be susceptible to grain effects in rubber.
Method A: Using a trouser test piece
Method A, using the trouser test piece, is preferred because it is not sensitive to the length of the cut, unlike the
other two test pieces in which the nick has to be very closely controlled. In addition, the results obtained are
more easily related to the fundamental tear properties of the material and are less sensitive to modulus effects
(provided that the leg extension is negligible) and the rate of propagation of the tear is directly related to the rate
of grip separation. With some rubbers, the propagation of tear is not smooth (knotty tear), and analysis of
results may be difficult.
Method B, procedure (a): Using an angle test piece without nick
This test is a combination of tear initiation and propagation. Stress is built up at the point of the angle until it is
sufficient to initiate a tear and then further stresses propagate this tear. However it is only possible to measure
the overall force required to rupture the test piece, and, therefore, the force cannot be resolved in two
[1]
components producing initiation and propagation.
Method B, procedure (b): Using an angle test piece with nick
This test measures the force required to propagate a nick already produced in the test piece. The rate of
[2]
propagation is not directly related to the jaw speed.
Method C: Using a crescent test piece
This test also measures the force required to propagate a nick already produced in the test piece and the rate
of propagation is not related to the jaw speed.
NOTE A separate method for the determination of the tear strength of small test pieces of rubber (Delft test pieces) is
[3]
specified in ISO 34-2.
©
ISO 2004 – All rights reserved 1

---------------------- Page: 5 ----------------------
ISO 34-1:2004(E)
2 Normative references
The following referenced documents are indispensable for the application of this document. For dated
references, only the edition cited applies. For undated references, the latest edition of the referenced document
(including any amendments) applies.
ISO 471:1995, Rubber — Temperatures, humidities and times for conditioning and testing
ISO 3383:1985, Rubber — General directions for achieving elevated or subnormal temperatures for test
purposes
ISO 4648:1991, Rubber, vulcanized or thermoplastic — Determination of dimensions of test pieces and
products for test purposes
ISO 5893:2002, Rubber and plastics test equipment — Tensile, flexural and compression types (constant rate
of traverse) — Specification
ISO 6133:1998, Rubber and plastics — Analysis of multi-peak traces obtained in determinations of tear
strength and adhesion strength
ISO/TR 9272:1986, Rubber and rubber products — Determination of precision for test method standards
3 Terms and definitions
For the purposes of this document, the following terms and definitions apply.
3.1
trouser tear strength
median force, calculated in accordance with ISO 6133, required to propagate a cut in a specified trouser-
shaped test piece by tearing, divided by the thickness of the test piece, the force acting in a direction
substantially in the plane of the cut
3.2
unnicked angle tear strength
maximum force required to rupture a specified angle-shaped test piece, divided by the thickness of the test
piece, the force acting in a direction substantially along the length of the test piece
3.3
nicked angle or crescent tear strength
maximum force required to cause a nick cut in a specified angle- or crescent-shaped test piece to extent by
tearing of the rubber, divided by the thickness of the test piece, the force acting in a direction substantially
normal to the plane of the nick
4Principle
The test consists in measuring the force required to tear a specified test piece, in continuation of the cut or nick
already produced in the test piece or, in the case of method B, procedure (a), completely across the width of the
test piece.
The tearing force is applied by means of a tensile testing machine, operated without interruption at a constant
rate of traverse until the test piece breaks. Dependent upon the method employed, the maximum or median
force achieved is used to calculate the tear strength.
No correlation between data obtained by the alternative test pieces is implied.
©
2 ISO 2004 – All rights reserved

---------------------- Page: 6 ----------------------
ISO 34-1:2004(E)
5 Apparatus
5.1 Dies
5.1.1 The die used for cutting trouser test pieces shall have the outline dimensions (length and width) shown
in Figure 1.
5.1.2 The die used for cutting angle test pieces shall have the dimensions shown in Figure 2.
5.1.3 The die used for cutting crescent test pieces shall have the dimensions shown in Figure 3.
5.1.4 The cutting edges of the dies shall be kept sharp and free from ragged edges. Care shall be taken that
the cutting edges are perpendicular to the other surfaces of the die and have a minimum of concavity.
Dimensions in millimetres
a
Direction of cut
Figure 1 — Trouser test piece die
©
ISO 2004 – All rights reserved 3

---------------------- Page: 7 ----------------------
ISO 34-1:2004(E)
Dimensions in millimetres
Key
1 location of nick for method B, procedure (b)
Figure 2 — Angle test piece die
Dimensions in millimetres
Key
1 location of nick
Figure 3 — Crescent test piece die
©
4 ISO 2004 – All rights reserved

---------------------- Page: 8 ----------------------
ISO 34-1:2004(E)
5.2 Nick cutter
A sharp razor blade or a sharp knife free from ragged edges shall be used for producing a cut or a nick in the
test piece.
The apparatus for introducing the nick required for the nicked angle or crescent test piece shall be as follows.
Means shall be provided for clamping the test piece firmly, especially in the region where the nick is to be
introduced. The cutting tool, consisting of a razor blade or similar blade, shall be clamped in a plane
perpendicular to the major axis of the test piece, and positioned so as to introduce the nick in the appropriate
place. The blade clamping device shall permit no lateral movement and shall be fitted in guides to enable the
blade to be moved across the test piece with its edge remaining perpendicular to the plane of the test piece.
Alternatively, the blade may be fixed and the test piece arranged to move in an analogous manner. Means shall
be provided for fine adjustment of the depth of the nick. The adjustment of the position of the blade holder
and/or clamped test piece shall be determined for each blade by cutting one or two preliminary nicks and
measuring these with the aid of a microscope. The blade shall be wetted with water or soap solution prior to
nicking.
[4]
NOTE A suitable apparatus for nicking tear test pieces has been described in detail in the literature.
To check that the depth of the nick is within the specified limits (see 6.4), any suitable means may be used, for
example an optical projection apparatus. A convenient arrangement is a microscope giving at least ×10
magnification fi
...

NORME ISO
INTERNATIONALE 34-1
Deuxième édition
2004-03-15
Caoutchouc vulcanisé ou
thermoplastique — Détermination de la
résistance au déchirement —
Partie 1:
Éprouvettes pantalon, angulaire et
croissant
Rubber, vulcanized or thermoplastic — Determination of tear strength —
Part 1: Trouser, angle and crescent test pieces

Numéro de référence
ISO 34-1:2004(F)
©
ISO 2004

---------------------- Page: 1 ----------------------
ISO 34-1:2004(F)
PDF — Exonération de responsabilité
Le présent fichier PDF peut contenir des polices de caractères intégrées. Conformément aux conditions de licence d'Adobe, ce fichier
peut être imprimé ou visualisé, mais ne doit pas être modifié à moins que l'ordinateur employé à cet effet ne bénéficie d'une licence
autorisant l'utilisation de ces polices et que celles-ci y soient installées. Lors du téléchargement de ce fichier, les parties concernées
acceptent de fait la responsabilité de ne pas enfreindre les conditions de licence d'Adobe. Le Secrétariat central de l'ISO décline toute
responsabilité en la matière.
Adobe est une marque déposée d'Adobe Systems Incorporated.
Les détails relatifs aux produits logiciels utilisés pour la création du présent fichier PDF sont disponibles dans la rubrique General Info du
fichier; les paramètres de création PDF ont été optimisés pour l'impression. Toutes les mesures ont été prises pour garantir l'exploitation
de ce fichier par les comités membres de l'ISO. Dans le cas peu probable où surviendrait un problème d'utilisation, veuillez en informer
le Secrétariat central à l'adresse donnée ci-dessous.
© ISO 2004
Droits de reproduction réservés. Sauf prescription différente, aucune partie de cette publication ne peut être reproduite ni utilisée sous
quelque forme que ce soit et par aucun procédé, électronique ou mécanique, y compris la photocopie et les microfilms, sans l'accord écrit
de l'ISO à l'adresse ci-après ou du comité membre de l'ISO dans le pays du demandeur.
ISO copyright office
Case postale 56  CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail [e-mail]
Web www.iso.org
Publié en Suisse
©
ii ISO 2004 – Tous droits réservés

---------------------- Page: 2 ----------------------
ISO 34-1:2004(F)
Sommaire Page
1 Domaine d'application . 1
2Références normatives . 2
3 Termes et définitions . 2
4 Principe . 2
5 Appareillage . 3
6 Éprouvettes . 6
7 Nombre d'essais . 7
8Température d'essai . 7
9 Mode opératoire . 7
10 Expression des résultats . 7
11 Fidélité . 8
12 Rapport d'essai . 10
Annexe A (informative) Indications pour l'utilisation des résultats de fidélité . 11
Annexe B (informative) Formules d'essai pour les mélanges A, B et C utilisés dans l'ITP . 12
Bibliographie . 13
©
ISO 2004 – Tous droits réservés iii

---------------------- Page: 3 ----------------------
ISO 34-1:2004(F)
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes nationaux de
normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est en général confiée
aux comités techniques de l'ISO. Chaque comité membre intéressé par une étude a le droit de faire partie du
comité technique créé à cet effet. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec l'ISO participent également aux travaux. L'ISO collabore étroitement avec la
Commission électrotechnique internationale (CEI) en ce qui concerne la normalisation électrotechnique.
Les Normes internationales sont rédigées conformément aux règles données dans les Directives ISO/CEI,
Partie 2.
La tâche principale des comités techniques est d'élaborer les Normes internationales. Les projets de Normes
internationales adoptés par les comités techniques sont soumis aux comités membres pour vote. Leur
publication comme Normes internationales requiert l'approbation de 75 % au moins des comités membres
votants.
L'attention est appelée sur le fait que certains des éléments du présent document peuvent faire l'objet de droits
de propriété intellectuelle ou de droits analogues. L'ISO ne saurait être tenue pour responsable de ne pas avoir
identifié de tels droits de propriété et averti de leur existence.
L'ISO 34-1 a été élaborée par le comité technique ISO/TC 45, Élastomères et produits à base d'élastomères,
sous-comité SC 2, Essais et analyses.
Cette deuxième édition annule et remplace la première édition (ISO 34-1:1994), dont elle constitue une révision
mineure (un certain nombre de corrections ont été faites dans la Figure 2). Elle incorpore aussi le Rectificatif
technique ISO 34-1:1994/Cor.1:1999.
L'ISO34 comprend les parties suivantes, présentées sous le titre général Caoutchouc vulcanisé ou
thermoplastique — Détermination de la résistance au déchirement:
— Partie 1: Éprouvettes pantalon, angulaire et croissant
— Partie 2: Petites éprouvettes (éprouvettes de Delft)
©
iv ISO 2004 – Tous droits réservés

---------------------- Page: 4 ----------------------
NORME INTERNATIONALE ISO 34-1:2004(F)
Caoutchouc vulcanisé ou thermoplastique — Détermination de
la résistance au déchirement —
Partie 1:
Éprouvettes pantalon, angulaire et croissant
1 Domaine d'application
La présente partie de l'ISO 34 spécifie trois méthodes pour la détermination de la résistance au déchirement du
caoutchouc vulcanisé ou thermoplastique, à savoir:
— la méthode A, utilisant une éprouvette pantalon;
— la méthode B, utilisant une éprouvette angulaire, avec ou sans entaille de profondeur spécifiée;
— la méthode C, utilisant une éprouvette croissant entaillée.
La valeur de la résistance au déchirement obtenue dépend de la forme de l'éprouvette, de la vitesse d'étirement
et de la température d'essai. Elle peut aussi être sensible au sens du grain du caoutchouc.
Méthode A: avec éprouvette pantalon
La méthode A, qui utilise l'éprouvette pantalon, est utilisée de préférence, car elle n'est pas sensible à la
longueur de la coupure, à la différence des deux autres éprouvettes dans lesquelles l'entaille doit être très
étroitement contrôlée. En outre, les résultats obtenus sont plus facilement reliés aux caractéristiques de
déchirement fondamentales du matériau et sont moins sensibles aux effets du module (pourvu que l'extension
des jambes soit négligeable), et la vitesse de propagation de la déchirure est directement liée à la vitesse de
séparation des mâchoires. Avec certains caoutchoucs, la propagation du déchirement n'est pas régulière et
l'analyse des résultats peut être difficile.
Méthode B, mode opératoire (a): avec une éprouvette angulaire sans entaille
L'essai associe l'initiation de l'amorçage et la propagation de la déchirure. La contrainte est concentrée à la
base de l'angle, jusqu'à ce qu'elle soit suffisante pour amorcer une déchirure qui se propage sous l'effet de
contraintes ultérieures. Cependant, comme il est seulement possible de mesurer la force globale nécessaire
pour rompre l'éprouvette, la force ne peut pas être décomposée en deux composantes dont l'une produit
[1]
l'initiation et l'autre la propagation.
Méthode B, mode opératoire (b): avec une éprouvette angulaire entaillée
Dans cet essai, on mesure la force nécessaire pour propager une entaille déjà pratiquée dans l'éprouvette. La
[2]
vitesse de propagation n'est pas directement liée à la vitesse de séparation des mâchoires.
Méthode C: avec une éprouvette croissant
Dans cet essai, on mesure la force nécessaire pour propager une entaille déjà pratiquée dans l'éprouvette et la
vitesse de propagation n'est pas liée à la vitesse de séparation des mâchoires.
NOTE Une méthode particulière de détermination de la résistance au déchirement des petites éprouvettes de caoutchouc
[3]
(éprouvettes de Delft) est spécifiée dans l'ISO 34-2.
©
ISO 2004 – Tous droits réservés 1

---------------------- Page: 5 ----------------------
ISO 34-1:2004(F)
2Références normatives
Les documents de référence suivants sont indispensables pour l'application du présent document. Pour les
références datées, seule l'édition citée s'applique. Pour les références non datées, la dernière édition du
document de référence s'applique (y compris les éventuels amendements).
ISO 471:1995, Caoutchouc — Températures, humidités et durées pour le conditionnement et l'essai
ISO 3383:1985, Caoutchouc — Directives générales pour l'obtention de températures élevées ou de
températures inférieures à la température normale lors des essais
ISO 4648:1991, Caoutchouc vulcanisé ou thermoplastique — Détermination des dimensions des éprouvettes
et des produits en vue des essais
ISO 5893:2002, Appareils d'essai du caoutchouc et des plastiques — Types pour traction, flexion et
compression (vitesse de translation constante) — Spécifications
ISO 6133:1998, Caoutchouc et plastiques — Analyse des tracés multi-pics obtenus lors des déterminations de
la résistance au déchirement et de la force d'adhérence
ISO/TR 9272:1986, Caoutchouc et produits en caoutchouc — Détermination de la fidélité de méthodes d'essai
normalisées
3 Termes et définitions
Pour les besoins du présent document, les termes et définitions suivants s'appliquent.
3.1
résistance au déchirement de l'éprouvette pantalon
force médiane, calculée conformément à l'ISO 6133, nécessaire pour propager par déchirement une coupure
dans une éprouvette spécifiée en forme de pantalon, divisée par l'épaisseur de l'éprouvette, la force agissant
dans une direction située sensiblement dans le plan de la coupure
3.2
résistance au déchirement de l'éprouvette angulaire sans entaille
force maximale nécessaire pour rompre une éprouvette spécifiée de forme angulaire, divisée par l'épaisseur de
l'éprouvette, la force agissant sensiblement dans le sens de la longueur de l'éprouvette
3.3
résistance au déchirement de l'éprouvette angulaire ou croissant, avec entaille
force maximale nécessaire pour provoquer l'extension, par déchirement du caoutchouc, d'une entaille pratiquée
dans une éprouvette spécifiée, angulaire ou croissant, divisée par l'épaisseur de l'éprouvette, la force agissant
dans une direction sensiblement normale au plan de l'entaille
4Principe
L’essai consiste à mesurer la force nécessaire pour déchirer l’éprouvette spécifiée, dans le prolongement de
l’entaille déjà pratiquée ou, dans le cas de la méthodeB, mode opératoire (a), sur toute la largeur de
l’éprouvette.
La force de déchirement est appliquée au moyen d'une machine d'essai de traction, utilisée sans interruption à
une vitesse de déplacement constante, jusqu'à rupture de l'éprouvette. Selon la méthode employée, la force
maximale ou médiane atteinte est utilisée pour calculer la résistance au déchirement.
On ne peut établir aucune corrélation entre les indications obtenues avec différentes éprouvettes.
©
2 ISO 2004 – Tous droits réservés

---------------------- Page: 6 ----------------------
ISO 34-1:2004(F)
5 Appareillage
5.1 Emporte-pièce
5.1.1 L'emporte-pièce utilisé pour découper les éprouvettes pantalon doit avoir les dimensions générales
(longueur et largeur) indiquées à la Figure 1.
5.1.2 L'emporte-pièce utilisé pour découper les éprouvettes angulaires doit avoir les dimensions indiquées à
la Figure 2.
5.1.3 L'emporte-pièce utilisé pour découper les éprouvettes croissant doit avoir les dimensions indiquées à la
Figure 3.
5.1.4 Le tranchant des emporte-pièce doit être maintenu net et sans la moindre ébréchure. On doit prendre
soin que les bords coupants soient perpendiculaires aux autres faces de l'éprouvette et aient un minimum de
concavité.
Dimensions en millimètres
a
Sens de la coupure
Figure 1 — Emporte-pièce pour éprouvette pantalon
©
ISO 2004 – Tous droits réservés 3

---------------------- Page: 7 ----------------------
ISO 34-1:2004(F)
Dimensions en millimètres
Légende
1 emplacement de l’entaille pour la méthode B, mode opératoire (b)
Figure 2 — Emporte-pièce pour éprouvette angulaire
Dimensions en millimètres
Légende
1 emplacement de l’entaille
Figure 3 — Emporte-pièce pour éprouvette croissant
©
4 ISO 2004 – Tous droits réservés

---------------------- Page: 8 ----------------------
ISO 34-1:2004(F)
5.2 Outil de coupe pour entaille
Pour pratiquer une entaille dans l'éprouvette, une lame de rasoir tranchante ou un couteau tranchant sans
ébréchure doit être utilisé(e).
Le dispositif pour pratiquer l'entaille voulue dans l'éprouvette angulaire ou l'éprouvette croissant avec l'entaille
doit être le suivant:
Un dispositif doit être fourni pour fixer solidement l'éprouvette en la serrant, en particulier dans la région où
devra se trouver l'entaille. L'outil de coupe, constitué par une lame de rasoir ou une lame similaire, doit être fixé
par un serrage dans un plan perpendiculaire au grand axe de l'éprouvette et placé de manière à réaliser
l'entaille à l'endroit approprié. Le dispositif de fixation par serrage de la lame ne doit permettre aucun
déplacement latéral et doit être monté dans des guides permettant à la lame de se déplacer dans l'éprouvette,
son bord demeurant perpendiculaire au plan de cette dernière. On peut aussi maintenir la lame en position fixe
et faire déplacer l'éprouvette d'une manière analogue. On doit disposer d'un moyen permettant d'ajuster avec
précision la profondeur de l'entaille. Le réglage à effectuer pour positionner le support de lame et/ou
l'éprouvette fixée par serrage doit être déterminé pour chaque lame en pratiquant une ou deux entailles
préliminaires et en mesurant celle(s)-ci à l'aide d'un microscope. Mouiller la lame avec de l'eau ou une solution
de savon avant entaillage.
NOTE Un dispositif approprié à l'entaillage des éprouvettes pour essai de déchirement est décrit en détail dans la
[4]
littérature.
Pour vérifier que la profondeur de l'entaille est comprise dans les limites spécifiées (voir 6.4), on peut utiliser
tout moyen approprié, par exemple un appareil de projection optique. Un microscope donnant un
grossissement d'au moins ×10, muni d'une platine mobile convenablement éclairée const
...