ISO/FDIS 11997-2

Paints and varnishes — Determination of resistance to cyclic corrosion conditions — Part 2: Wet (salt fog)/dry/humid/UV light

ISO 11197-2:2013 specifies a test method of determining resistance of coatings to a defined cycle of wet (salt fog)/dry/humidity/UV light conditions using a specified solution.

Peintures et vernis — Détermination de la résistance aux conditions de corrosion cyclique — Partie 2: Brouillard salin/sécheresse/humidité/lumière UV

L'ISO 11997-2:2013 spécifie une méthode d'essai permettant de déterminer la résistance des revêtements à un cycle comprenant brouillard salin/sécheresse/humidité/lumière UV et utilisant une solution saline spécifique.

General Information

• Status: Not Published
• ICS: 87.040 - Paints and varnishes
• Technical Committee: ISO/TC 35/SC 9 - General test methods for paints and varnishes
• Drafting Committee: ISO/TC 35/SC 9 - General test methods for paints and varnishes
• Current Stage: 5020 - FDIS ballot initiated: 2 months. Proof sent to secretariat
• Start Date: 08-Aug-2025
• Completion Date: 08-Aug-2025

Relations

• Revises: ISO 11997-2:2013 - Paints and varnishes — Determination of resistance to cyclic corrosion conditions — Part 2: Wet (salt fog)/dry/humidity/UV light
• Effective Date: 17-Jun-2023

Standards Content (Sample)

FINAL DRAFT
International
Standard
ISO/TC 35/SC 9
Paints and varnishes —
Secretariat: BSI
Determination of resistance to
Voting begins on:
cyclic corrosion conditions —
2025-08-08
Part 2:
Voting terminates on:
2025-10-03
Wet (salt fog)/dry/humid/UV light
RECIPIENTS OF THIS DRAFT ARE INVITED TO SUBMIT,
WITH THEIR COMMENTS, NOTIFICATION OF ANY
RELEVANT PATENT RIGHTS OF WHICH THEY ARE AWARE
AND TO PROVIDE SUPPOR TING DOCUMENTATION.
IN ADDITION TO THEIR EVALUATION AS
BEING ACCEPTABLE FOR INDUSTRIAL, TECHNO-
ISO/CEN PARALLEL PROCESSING LOGICAL, COMMERCIAL AND USER PURPOSES, DRAFT
INTERNATIONAL STANDARDS MAY ON OCCASION HAVE
TO BE CONSIDERED IN THE LIGHT OF THEIR POTENTIAL
TO BECOME STAN DARDS TO WHICH REFERENCE MAY BE
MADE IN NATIONAL REGULATIONS.
Reference number
FINAL DRAFT
International
Standard
ISO/TC 35/SC 9
Paints and varnishes —
Secretariat: BSI
Determination of resistance to
Voting begins on:
cyclic corrosion conditions —
Part 2:
Voting terminates on:
Wet (salt fog)/dry/humid/UV light
RECIPIENTS OF THIS DRAFT ARE INVITED TO SUBMIT,
WITH THEIR COMMENTS, NOTIFICATION OF ANY
RELEVANT PATENT RIGHTS OF WHICH THEY ARE AWARE
AND TO PROVIDE SUPPOR TING DOCUMENTATION.
© ISO 2025
IN ADDITION TO THEIR EVALUATION AS
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
BEING ACCEPTABLE FOR INDUSTRIAL, TECHNO-
ISO/CEN PARALLEL PROCESSING
LOGICAL, COMMERCIAL AND USER PURPOSES, DRAFT
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting on
INTERNATIONAL STANDARDS MAY ON OCCASION HAVE
the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address below
TO BE CONSIDERED IN THE LIGHT OF THEIR POTENTIAL
or ISO’s member body in the country of the requester.
TO BECOME STAN DARDS TO WHICH REFERENCE MAY BE
MADE IN NATIONAL REGULATIONS.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: [phone]
Email: [e-mail]
Website: www.iso.org
Published in Switzerland Reference number
ii
Contents Page
Foreword .iv
Introduction .v
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 2
4 Principle . 2
5 Salt fog test solution . 2
6 Apparatus . 2
7 Sampling . 3
8 Test panels . 3
8.1 Material and dimensions .3
8.2 Preparation and coating of panels .3
8.3 Drying and conditioning .3
8.4 Thickness of coating .3
8.5 Scribing of panels .3
9 Procedure . 3
10 Examination of test panels . 4
11 Test report . 4
Annex A (informative) Alternative test procedures . 6
Bibliography . 8

iii
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out through
ISO technical committees. Each member body interested in a subject for which a technical committee
has been established has the right to be represented on that committee. International organizations,
governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely
with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are described
in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the different types
of ISO document should be noted. This document was drafted in accordance with the editorial rules of the
ISO/IEC Directives, Part 2 (see www.iso.org/directives).
ISO draws attention to the possibility that the implementation of this document may involve the use of (a)
patent(s). ISO takes no position concerning the evidence, validity or applicability of any claimed patent
rights in respect thereof. As of the date of publication of this document, ISO had not received notice of (a)
patent(s) which may be required to implement this document. However, implementers are cautioned that
this may not represent the latest information, which may be obtained from the patent database available at
www.iso.org/patents. ISO shall not be held responsible for identifying any or all such patent rights.
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and expressions
related to conformity assessment, as well as information about ISO's adherence to the World Trade
Organization (WTO) principles in the Technical Barriers to Trade (TBT), see www.iso.org/iso/foreword.html.
This document was prepared by Technical Committee ISO/TC 35, Paints and varnishes, Subcommittee
SC 9, General test methods for paints and varnishes in collaboration with the European Committee for
Standardization (CEN) Technical Committee CEN/TC 139, Paints and varnishes, in accordance with the
Agreement on technical cooperation between ISO and CEN (Vienna Agreement).
This third edition cancels and replaces the second edition (ISO 11997-2:2013), which has been technically
revised.
The main changes are as follows:
— Clause 3, Terms and definitions, has been added;
— in A.3.2.2, the designation of the fluorescent UV lamps has been updated;
— the normative references have been updated.
A list of all parts in the ISO 11997 series can be found on the ISO website.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www.iso.org/members.html.

iv
Introduction
Coatings of paints, varnishes and similar materials are exposed to cyclic wet and dry corrosion and UV
exposure conditions using specified salt solutions in cabinets in order to simulate, in the laboratory, processes
occurring in aggressive outdoor conditions. Generally, valid correlations between such outdoor weathering
and laboratory testing cannot be expected because of the large number of factors influencing the breakdown
process. Certain relationships can only be expected if the effect on the coating of the important parameters
(e.g. nature of the pollutant, spectral distribution of the incident irradiance in the relevant photochemical
region, temperature of the specimen, type and cycle of wetting and relative humidity) is known. In contrast
to outdoor weathering, laboratory testing in a cabinet is performed with a reduced number of variables,
which can be controlled and therefore the effects are more reproducible.
The method described can give a means of checking that the quality of a paint or paint system is being
maintained. The method is intended to provide a more realistic simulation of these factors than is found
in traditional tests with continuous exposure to a static set of corrosive conditions. The method has been
found to be useful in comparing the cyclic salt spray resistance of different coatings. It is most useful in
providing relevant ratings for a series of coated panels exhibiting significant differences in cyclic salt spray/
UV exposure resistance tested at the same time and to the same test cycle.
The cycle specified in this document has been found useful for air-drying industrial maintenance coatings
on steel; other cycles may be used as required.

v
FINAL DRAFT International Standard ISO/FDIS 11997-2:2025(en)
Paints and varnishes — Determination of resistance to cyclic
corrosion conditions —
Part 2:
Wet (salt fog)/dry/humid/UV light
1 Scope
This document specifies a test method to determine the resistance of coatings to a specified cycle of wet
(salt fog)/dry/humidity/UV light conditions using a specified solution.
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content constitutes
requirements of this document. For dated references, only the edition cited applies. For undated references,
the latest edition of the referenced document (including any amendments) applies.
ISO 1513, Paints and varnishes — Examination and preparation of test samples
ISO 1514, Paints and varnishes — Standard panels for testing
ISO 2808, Paints and varnishes — Determination of film thickness
ISO 3270, Paints and varnishes and their raw materials — Temperatures and humidities for conditioning and testing
ISO 3696, Water for analytical laboratory use — Specification and test methods
ISO 4618, Paints and varnishes — Vocabulary
ISO 4628-1, Paints and varnishes — Evaluation of degradation of coatings — Designation of quantity and size of
defects, and of intensity of uniform changes in appearance — Part 1: General introduction and designation system
ISO 4628-2, Paints and varnishes — Evaluation of degradation of coatings — Designation of quantity and size of
defects, and of intensity of uniform changes in appearance — Part 2: Assessment of degree of blistering
ISO 4628-3, Paints and varnishes — Evaluation of quantity and size of defects, and of intensity of uniform
changes in appearance — Part 3: Assessment of degree of rusting
ISO 4628-4, Paints and varnishes — Evaluation of degradation of coatings — Designation of quantity and size of
defects, and of intensity of uniform changes in appearance — Part 4: Assessment of degree of cracking
ISO 4628-5, Paints and varnishes — Evaluation of quantity and size of defects, and of intensity of uniform
changes in appearance — Part 5: Assessment of degree of flaking
ISO 4628-6, Paints and varnishes — Evaluation of quantity and size of defects, and of intensity of uniform
changes in appearance — Part 6: Assessment of degree of chalking by tape method
ISO 4628-8, Paints and varnishes — Evaluation of degradation of coatings — Designation of quantity and size of
defects, and of intensity of uniform changes in appearance — Part 8: Assessment of degree of delamination and
corrosion around a scribe or other artificial defect
ISO 4628-10, Paints and varnishes — Evaluation of quantity and size of defects, and of intensity of uniform
changes in appearance — Part 10: Assessment of degree of filiform corrosion

© ISO 2
...

ISO/FDIS 11997--2:2025(en)
Style Definition: Heading 1
Style Definition: Heading 2
ISO/TC 35/SC 9
Style Definition: Heading 3
Secretariat: BSI
Style Definition: Heading 4
Style Definition: Heading 5
Date: 2025-0307-24
Style Definition: Heading 6
Paints and varnishes — Determination of resistance to cyclic corrosion conditions — Part 2:
Style Definition: Default Paragraph Font
Wet (salt fog)/dry/humid/UV light
Style Definition: ANNEX
Style Definition: zzCopyright
Style Definition: AMEND Terms Heading
Style Definition: AMEND Heading 1 Unnumbered
Style Definition: IneraTableMultiPar: Font: Don't adjust
space between Latin and Asian text, Don't adjust space
between Asian text and numbers, Tab stops: 0.7 cm,
Left + 1.4 cm, Left + 2.1 cm, Left + 2.8 cm, Left + 3.5
cm, Left + 4.2 cm, Left + 4.9 cm, Left + 5.6 cm, Left +
6.3 cm, Left + 7 cm, Left
Formatted: French (Switzerland)

ISO/DISFDIS 11997-2:2025(en)
Formatted: Font: 11.5 pt
Formatted: Font: 11.5 pt
Formatted: Adjust space between Latin and Asian text,
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part
Adjust space between Asian text and numbers
of this publication may be reproduced or utilized otherwise in any form or by any means, electronic or
Formatted: Default Paragraph Font
mechanical, including photocopying, or posting on the internet or an intranet, without prior written
permission. Permission can be requested from either ISO at the address below or ISO’sISO's member Formatted: Default Paragraph Font
body in the country of the requester.
ISO copyright officeCopyright Office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Formatted: Adjust space between Latin and Asian text,
Adjust space between Asian text and numbers
Phone: + 41 22 749 01 11
Email: [e-mail]
Email: [e-mail]
Website: www.iso.orgwww.iso.org
Formatted: Adjust space between Latin and Asian text,
Adjust space between Asian text and numbers
Published in Switzerland.
Formatted: Font: Bold
ii
ISO/DISFDIS 11997-2:2025(en)
Formatted: Font: 11.5 pt
Formatted: Font: 11.5 pt
Contents
Foreword . iv
Introduction . v
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 2
4 Principle . 2
5 Salt fog test solution . 2
6 Apparatus . 2
7 Sampling . 3
8 Test panels . 3
8.1 Material and dimensions . 3
8.2 Preparation and coating of panels . 3
8.3 Drying and conditioning . 3
8.4 Thickness of coating . 3
8.5 Scribing of panels . 3
9 Procedure . 3
10 Examination of test panels . 4
11 Test report . 4
Annex A (informative) Alternative test procedures . 6
A.1 General . 6
A.2 Procedure . 6
A.3 Test conditions . 6
A.3.1 General . 6
A.3.2 Exposure to light . 6
A.3.2.1 Xenon arc lamp . 6
A.3.2.2 Fluorescent UV lamp . 6
A.3.2.3 Open-flame carbon arc lamp . 7
A.3.3 Corrosion . 7
A.3.3.1 Salt spray . 7
A.3.3.2 Salt spray/dry/wet . 7
A.3.3.3 Salt spray/wet/hot dry/warm dry . 7
A.3.3.4 Acidified salt spray/dry/wet . 7
Bibliography . 8Foreword i
v
Introduction . v
1 Scope . 1
2 Normative references . 1
Formatted: Font: Bold
iii
ISO/DISFDIS 11997-2:2025(en)
Formatted: Font: 11.5 pt
Formatted: Font: 11.5 pt
3 Terms and definitions . 2
4 Principle . 2
5 Salt fog test solution . 2
6 Apparatus . 2
7 Sampling . 3
8 Test panels . 3
8.1 Material and dimensions . 3
8.2 Preparation and coating of panels . 3
8.3 Drying and conditioning . 3
8.4 Thickness of coating . 3
8.5 Scribing of panels . 3
9 Procedure . 3
10 Examination of test panels . 4
11 Test report . 4
Annex A (informative) Alternative test procedures . 6
A.1 General . 6
A.2 Procedure . 6
A.3 Test conditions . 6
A.3.1 General . 6
A.3.2 Exposure to light . 6
A.3.2.1 Xenon arc lamp . 6
A.3.2.2 Fluorescent UV lamp . 6
A.3.2.3 Open-flame carbon arc lamp . 7
A.3.3 Corrosion . 7
A.3.3.1 Salt spray . 7
A.3.3.2 Salt spray/dry/wet . 7
A.3.3.3 Salt spray/wet/hot dry/warm dry . 7
A.3.3.4 Acidified salt spray/dry/wet . 7
Bibliography . 8
Formatted: Font: Bold
iv
ISO/DISFDIS 11997-2:2025(en)
Formatted: Font: 11.5 pt
Formatted: Font: 11.5 pt
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out through
ISO technical committees. Each member body interested in a subject for which a technical committee has been
established has the right to be represented on that committee. International organizations, governmental and
non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the
International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are described
in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the different types of
ISO document should be noted. This document was drafted in accordance with the editorial rules of the
ISO/IEC Directives, Part 2 (see www.iso.org/directiveswww.iso.org/directives).
ISO draws attention to the possibility that the implementation of this document may involve the use of (a)
patent(s). ISO takes no position concerning the evidence, validity or applicability of any claimed patent rights
in respect thereof. As of the date of publication of this document, ISO had not received notice of (a) patent(s)
which may be required to implement this document. However, implementers are cautioned that this may not
represent the latest information, which may be obtained from the patent database available at
www.iso.org/patents.www.iso.org/patents. ISO shall not be held responsible for identifying any or all such
patent rights.
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
...

PROJET FINAL
Norme
internationale
ISO/TC 35/SC 9
Peintures et vernis —
Secrétariat: BSI
Détermination de la résistance aux
Début de vote:
conditions de corrosion cyclique —
2025-08-08
Partie 2:
Vote clos le:
2025-10-03
Brouillard salin/sécheresse/
humidité/lumière UV
Paints and varnishes — Determination of resistance to cyclic
corrosion conditions —
Part 2: Wet (salt fog)/dry/humid/UV light
LES DESTINATAIRES DU PRÉSENT PROJET SONT
INVITÉS À PRÉSENTER, AVEC LEURS OBSERVATIONS,
NOTIFICATION DES DROITS DE PROPRIÉTÉ DONT ILS
AURAIENT ÉVENTUELLEMENT CONNAISSANCE ET À
FOURNIR UNE DOCUMENTATION EXPLICATIVE.
OUTRE LE FAIT D’ÊTRE EXAMINÉS POUR
ÉTABLIR S’ILS SONT ACCEPTABLES À DES FINS
INDUSTRIELLES, TECHNOLOGIQUES ET COM-MERCIALES,
AINSI QUE DU POINT DE VUE DES UTILISATEURS, LES
PROJETS DE NORMES
TRAITEMENT PARALLÈLE ISO/CEN
INTERNATIONALES DOIVENT PARFOIS ÊTRE CONSIDÉRÉS
DU POINT DE VUE DE LEUR POSSI BILITÉ DE DEVENIR DES
NORMES POUVANT
SERVIR DE RÉFÉRENCE DANS LA RÉGLEMENTATION
NATIONALE.
Numéro de référence
PROJET FINAL
Norme
internationale
ISO/TC 35/SC 9
Peintures et vernis —
Secrétariat: BSI
Détermination de la résistance aux
Début de vote:
conditions de corrosion cyclique —
2025-08-08
Partie 2:
Vote clos le:
2025-10-03
Brouillard salin/sécheresse/
humidité/lumière UV
Paints and varnishes — Determination of resistance to cyclic
corrosion conditions —
Part 2: Wet (salt fog)/dry/humid/UV light
LES DESTINATAIRES DU PRÉSENT PROJET SONT
INVITÉS À PRÉSENTER, AVEC LEURS OBSERVATIONS,
NOTIFICATION DES DROITS DE PROPRIÉTÉ DONT ILS
AURAIENT ÉVENTUELLEMENT CONNAISSANCE ET À
FOURNIR UNE DOCUMENTATION EXPLICATIVE.
DOCUMENT PROTÉGÉ PAR COPYRIGHT
OUTRE LE FAIT D’ÊTRE EXAMINÉS POUR
ÉTABLIR S’ILS SONT ACCEPTABLES À DES FINS
© ISO 2025 INDUSTRIELLES, TECHNOLOGIQUES ET COM-MERCIALES,
AINSI QUE DU POINT DE VUE DES UTILISATEURS, LES
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
PROJETS DE NORMES
TRAITEMENT PARALLÈLE ISO/CEN
INTERNATIONALES DOIVENT PARFOIS ÊTRE CONSIDÉRÉS
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
DU POINT DE VUE DE LEUR POSSI BILITÉ DE DEVENIR DES
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
NORMES POUVANT
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
SERVIR DE RÉFÉRENCE DANS LA RÉGLEMENTATION
NATIONALE.
ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: [phone]
E-mail: [e-mail]
Web: www.iso.org
Publié en Suisse Numéro de référence
ii
Sommaire Page
Avant-propos .iv
Introduction .v
1 Domaine d’application . 1
2 Références normatives . 1
3 Termes et définitions . 2
4 Principe. 2
5 Solution pour l’essai de brouillard salin. 2
6 Appareillage . 3
7 Échantillonnage . 3
8 Panneaux d’essai . 3
8.1 Matériaux et dimensions .3
8.2 Préparation et revêtement des panneaux .3
8.3 Séchage et conditionnement .3
8.4 Épaisseur du revêtement .3
8.5 Scarification des panneaux .4
9 Mode opératoire . 4
10 Examen des panneaux d’essai . 4
11 Rapport d’essai . 5
Annexe A (informative) Modes opératoires alternatifs . 6
Bibliographie . 8

iii
Avant-propos
L’ISO (Organisation internationale de normalisation) est une fédération mondiale d’organismes nationaux
de normalisation (comités membres de l’ISO). L’élaboration des Normes internationales est en général
confiée aux comités techniques de l’ISO. Chaque comité membre intéressé par une étude a le droit de faire
partie du comité technique créé à cet effet. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec l’ISO participent également aux travaux. L’ISO collabore étroitement avec
la Commission électrotechnique internationale (IEC) en ce qui concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier, de prendre note des différents
critères d’approbation requis pour les différents types de documents ISO. Le présent document
a été rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2
(voir www.iso.org/directives).
L’ISO attire l’attention sur le fait que la mise en application du présent document peut entraîner l’utilisation
d’un ou de plusieurs brevets. L’ISO ne prend pas position quant à la preuve, à la validité et à l’applicabilité de
tout droit de brevet revendiqué à cet égard. À la date de publication du présent document, l’ISO n’avait pas
reçu notification qu’un ou plusieurs brevets pouvaient être nécessaires à sa mise en application. Toutefois,
il y a lieu d’avertir les responsables de la mise en application du présent document que des informations
plus récentes sont susceptibles de figurer dans la base de données de brevets, disponible à l’adresse
www.iso.org/brevets. L’ISO ne saurait être tenue pour responsable de ne pas avoir identifié tout ou partie de
tels droits de brevet.
Les appellations commerciales éventuellement mentionnées dans le présent document sont données pour
information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l’ISO liés à l’évaluation de la conformité, ou pour toute information au sujet de l’adhésion de
l’ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles techniques au
commerce (OTC), voir www.iso.org/iso/fr/avant-propos.html.
Le présent document a été élaboré par le comité technique ISO/TC 35, Peintures et vernis, sous-comité SC 9,
Méthodes générales d’essais des peintures et vernis, en collaboration avec le comité technique CEN/TC 139,
Peintures et vernis, du Comité européen de normalisation (CEN), conformément à l’Accord de coopération
technique entre l’ISO et le CEN (Accord de Vienne).
Cette troisième édition annule et remplace la deuxième édition (ISO 11997-2:2013), qui a fait l’objet d’une
révision technique.
Les principales modifications sont les suivantes:
— l’Article 3, Termes et définitions, a été ajouté;
— en A.3.2.2, la désignation des lampes fluorescentes UV a été mise à jour;
— les références normatives ont été mises à jour.
Une liste de toutes les parties de la série ISO 11997 se trouve sur le site web de l’ISO.
Il convient que l’utilisateur adresse tout retour d’information ou toute question concernant le présent
document à l’organisme national de normalisation de son pays. Une liste exhaustive desdits organismes se
trouve à l’adresse www.iso.org/fr/members.html.

iv
Introduction
Des revêtements de peintures, vernis et produits similaires sont exposés dans des enceintes climatiques à
des cycles de corrosion sèche et humide et au rayonnement UV en présence de solutions salines spécifiques
afin de simuler en laboratoire des processus simulant l’agressivité naturelle du milieu. En général, il n’est
pas possible d’établir de corrélations pertinentes entre le vieillissement naturel et des essais de laboratoire
à cause du grand nombre de paramètres intervenant dans le processus de dégradation. On ne peut prévoir
de corrélation que si l’on connaît l’effet sur le revêtement de paramètres importants comme la nature du
polluant, la distribution spectrale du rayonnement incident dans la zone de sensibilité photochimique, la
température de l’échantillon, le type et le cycle d’aspersion et l’humidité relative. Contrairement à l’exposition
naturelle, les essais de laboratoire en enceinte climatique sont réalisés avec un nombre limité de variables
contrôlables et dont les effets sont donc plus reproductibles.
La méthode décrite peut permettre de vérifier la constance de la qualité d’une peinture ou d’un système
de peinture. Cette méthode est destinée à simuler ces facteurs de façon plus réaliste que par des essais
traditionnels d’exposition continue à une suite de conditions de corrosion. La méthode s’est montrée
utile pour comparer la résistance de revêtements à l’exposition cyclique au brouillard salin. Elle est
particulièrement utile pour classer de façon pertinente une série de panneaux revêtus présentant des
différences significatives de résistance à l’exposition cyclique au brouillard salin et aux UV, lorsqu’on les
évalue simultanément dans le même cycle d’essai.
Le cycle spécifié dans le présent document s’est avéré approprié à des revêtements industriels séchant
naturellement pour la maintenance de l’acier; il est sinon possible d’utiliser d’autres cycles.

v
PROJET FINAL Norme internationale ISO/FDIS 11997-2:2025(fr)
Peintures et vernis — Détermination de la résistance aux
conditions de corrosion cyclique —
Partie 2:
Brouillard salin/sécheresse/humidité/lumière UV
1 Domaine d’application
Le présent document spécifie une méthode d’essai permettant de déterminer la résistance des revêtements
à un cycle spécifié comprenant brouillard salin/sécheresse/humidité/lumière UV et utilisant une solution
spécifique.
2 Références normatives
Les documents suivants sont cités dans le texte de sorte qu’ils constituent, pour tout ou partie de leur
contenu, des exigences du présent document. Pour les références datées, seule l’édition citée s’applique. Pour
les références non datées, la dernière édition du document de référence s’applique (y compris les éventuels
amendements).
ISO 1513, Peintures et vernis — Examen et préparation des échantillons pour essai
ISO 1514, Peintures et vernis — Panneaux normalisés pour essai
ISO 2808, Peintures et vernis — Détermination de l'épaisseur du feuil
ISO 3270, Peintures et vernis et leurs matières premières — Températures et humidités pour le conditionnement
et l'essai
ISO 3696, Eau pour laboratoire à usage analytique — Spécification et méthodes d'essai
ISO 4618, Peintures et vernis — Vocabulaire
ISO 4628-1, Peintures et vernis — Évaluation de la dégradation des revêtements — Désignation de la quantité
et de la dimension des défauts, et de l'intensité des changements uniformes d'aspect — Partie 1: Introduction
générale et système de désignation
ISO 4628-2, Peintures et vernis — Évaluation de la dégradation des revêtements — Désignation de la quantité
et de la dimension des défauts, et de l'intensité
...