ISO 9073-4:1989
(Main)Textiles — Test methods for nonwovens — Part 4: Determination of tear resistance
Textiles — Test methods for nonwovens — Part 4: Determination of tear resistance
Textiles — Méthodes d'essai pour nontissés — Partie 4: Détermination de la résistance à la déchirure
General Information
Relations
Buy Standard
Standards Content (Sample)
IS0
INTER NATIONAL
9073-2
STANDARD
First edition
1989-07-01 .
Textiles - Test methods for nonwovens -
Part 2 :
Determination of thickness
Textiles - Méthodes d'essai pour nontisses -
Partie 2 : Détermination de l'épaisseur
Reference number
IS0 9073-2 : 1989 (E)
---------------------- Page: 1 ----------------------
IS0 9073-2 : 1989 (E)
Foreword
IS0 (the International Organization for Standardization) is a worldwide federation of
national standards bodies (IS0 member bodies). The work of preparing International
Standards is normally carried out through IS0 technical committees. Each member
body interested in a subject for which a technical committee has been established has
the right to be represented on that committee. International organizations, govern-
mental and non-governmental, in liaison with ISO, also take part in the work. IS0
collaborates closely with the International Electrotechnical Commission (IEC) on all
matters of electrotechnical standardization.
Draft International Standards adopted by the technical committees are circulated to
the member bodies for approval before their acceptance as International Standards by
the IS0 Council. They are approved in accordance with IS0 procedures requiring at
least 75 % approval by the member bodies voting.
International Standard IS0 9073-2 was prepared by Technical Committee ISO/TC 38,
Textiles.
IS0 9073 consists of the following parts, under the general title Textiles - Test
methods for nonwovens :
-
Part I: Determination of mass per unit area
-
Part 2: Determination of thickness
-
Part 3: Determination of tensile strength and elongation
-
Part 4: Determination of tear resistance
O IS0 1989
All rights reserved. No part of this publication may be reproduced or utilized in any form or by any
means, electronic or mechanical, including photocopying and microfilm, without permission in
writing from the publisher.
International Organization for Standardization
Case postale 56 O CH-1211 Genève 20 O Switzerland
Printed in Switzerland
ii
---------------------- Page: 2 ----------------------
IS0 9073-2 : 1989 (E)
Introduction
Although nonwovens are classified within the textile industry, it should be recognized
that nonwovens technologically share characteristics not only with textile products but
also with paper and/or plastic products. There is an existing international textile,test,
IS0 5084. However, in order to meet the specific needs of nonwovens, alternative
requirements to those listed in IS0 5084 are specified in this part of IS0 9073. These
are
a) a different sampling procedure;
b) specific pressures at which to test normal and bulky nonwovens;
c) a specific area for the size of the presser-foot;
d) a shorter time to note the gauge reading.
---------------------- Page: 3 ----------------------
~
IS0 9073-2 : 1989 (E)
INTERNATIONAL STANDARD
Textiles - Test methods for nonvvovens -
Part 2:
Determination of thickness
1 Scope 5 Apparatus
This part of IS0 9073 specifies methods for the determination
5.1 For normal nonwovens
of the thickness, when under a specific pressure, for normal
e
and bulky nonwovens.
5.1.1 Two circular horizontal plates, attached to a stand.
The upper plate, or presser-foot, shall be capable of moving
vertically and shall have an area of approximately 2 500 mm2.
2 Normative references
The reference plate shall have a plane surface of diameter at
The following standards contain provisions which, through
least 50 mm greater than that of the presser-foot.
reference in this text, constitute provisions of this part of
IS0 9073. At the time of publication, the editions indicated
5.1.2 Measuring device, having a scale with 0,Ol mm
were valid. All standards are subject to revision, and parties to
graduations.
agreements based on this part of IS0 9073 are encouraged to
investigate the possibility of applying the most recent editions
of the standards listed below. Members of IEC and IS0 main-
5.2 For bulky nonwovens with a maximum
tain registers of currently valid International Standards.
thickness of 20 mm
IS0 139 : 1973, Textiles - Standard atmospheres for con-
5.2.1 Vertical reference plate, with an area of 1 O00 mm2,
ditioning and testing.
presser-foot with an area of 2 500 mm2, and equipment to
IS0 186 : 1985, Paper and board - Sampling to determine suspend the test piece vertically between them.
average quality.
5.2.2 Elbow lever, attached to the reference plate and
IS0 5084 : 1977, Textiles - Determination of thickness of
so that it
capable of being balanced using a counterweight
woven and knitted fabrics (other than textile floor covering).
@
exerts a very small force to the left when the balance weight is
not in position.
3 Definitions
5.2.3 Electrical contacts, which, when closed, cause a
For the purposes of this part of IS0 9073, the following defi-
small bulb to become illuminated.
nitions apply.
5.2.4 Balance weight, with a mass of 2,05 g k 0,05 g,
3.1 bulky nonwovens : Nonwovens which are compressible
which, when in position, causes the contacts to separate and
by 20 % or more when the pressure applied changes from
extinguish the bulb. This gives a measuring pressure of
0.1 kPa to 0,5 kPa.
0,02 kPa.
3.2 thickness : The distance between the face and back of a
nonwoven measured as the distance between a reference plate
5.2.5 Screw, which, when turned, drives the presser-foot to
on which the nonwoven rests and a parallel presser-foot that is
the left and presses the test piece with increasing pressure
applying a pressure to the nonwoven.
against the reference plate until the force on the balance is
overcome and the bulb becomes illuminated again.
4 Principle
5.2.6 Dial-gauge, to indicate the distance between the
Measurement of the thickness of a nonwoven as the distance reference plate and the presser-foot corresponding to the
between the reference plate on which the nonwoven rests and thickness of the test piece at the pressure applied.
a parallel presser-foot that exerts a specified pressure on the
area under test. NOTE - An example of suitable apparatus is shown in figure 1.
1
---------------------- Page: 4 ----------------------
IS0 9073-2 : 1989 (E)
NOTE - The vertical probe T should be above the centre of the
5.3 For bulky nonwovens with a thickness greater
measuring plate P when in use (see 9.3.2) so that its distance from the
than 20 mm
vertical scale is slightly more than 100 mm and the measuring plate is
not in contact with the scale.
5.3.1 Testing area, of 200 mm x 200 mm.
5.3.2.2 Square measuring plate P, with a side length of
5.3.2 Testing apparatus (see figure 21, consisting of the
200 mm f 0,2 mm and a mass of 82 g f 2 g. The plate is made
following.
of glass with a thickness of 0,7 mm which can be brought to
the required mass by the addition of weight-pieces. The
5.3.2.1 Horizontal square base plate with a side length of
measuring pressure
...
NORME
IS0
I N T E R N AT I O NA LE
9073-4
Première édition
1989-04-1 5
Textiles - Méthodes d'essai pour nontissés -
Partie 4 :
Détermination de la résistance à la déchirure
Textiles - Test methods for nonwovens -
Part 4: Determination of tear resistance
Numéro de référence
IS0 9073-4 : 1989 (FI
---------------------- Page: 1 ----------------------
IS0 9073-4 : 1989 (FI
Avant- propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale
d'organismes nationaux de normalisation (comités membres de I'ISO). L'élaboration
des Normes internationales est en général confiée aux comités techniques de I'ISO.
Chaque comité membre intéressé par une étude a le droit de faire partie du comité
technique créé à cet effet. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec I'ISO participent également aux travaux. L'ISO col-
labore étroitement avec la Commission électrotechnique internationale (CEI) en ce qui
concerne la normalisation électrotechnique.
Les projets de Normes internationales adoptés par les comités techniques sont soumis
aux comités membres pour approbation, avant leur acceptation comme Normes inter-
nationales par le Conseil de I'ISO. Les Normes internationales sont approuvées confor-
mément aux procédures de 1'1S0 qui requièrent l'approbation de 75 YO au moins des
comités membres votants.
La Norme internationale IS0 9073-4 a été élaborée par le comité technique ISO/TC 38,
Textiles.
CIS0 9073 comprend les parties suivantes, présentées sous le titre général Textiles -
Méthodes d'essai pour nontissés :
-
Partie I: Détermination de la masse surfacique
- Partie 2: Détermination de l'épaisseur
- Partie 3: Détermination de la résistance à la traction et de l'allongement
-
Partie 4: Détermination de la résistance à la déchirure
O IS0 1989
Droits de reproduction réservés. Aucune partie de cette publication ne peut être reproduite ni
utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie et les microfilms, sans l'accord écrit de l'éditeur.
Organisation internationale de normalisation
Case postale 56 0 CH-121 1 Genève 20 O Suisse
Imprimé en Suisse
ii
---------------------- Page: 2 ----------------------
IS0 9073-4 : 1989 (FI
Introduction
Bien que les nontissés soient classés avec les produits de l'industrie textile, il convient
à la fois les caracté-
de reconnaître que, d'un point de vue technologique, ils présentent
ristiques des produits textiles et celles des papiers et/ou matières plastiques. II n'existe
pas actuellement de Norme internationale pour la détermination de la résistance à la
déchirure des textiles, mais des travaux sont en cours sur la détermination de la résis-
tance à la déchirure (méthode du pendule tombant, IS0 9290; méthode d'essai de
a
déchirement avec déchirure amorcée).
Cette méthode, qui utilise une déchirure trapézoïdale, est un essai de traction au cours
duquel la force est déterminée principalement par les fibres de la structure composite et
leurs liaisons entre elles. Elle sert à estimer la facilité relative de déchirement des nontis-
sés. Pour les nontissés, le mécanisme de déchirement dépend des forces de friction
entre les fibres et diffère de celui relevé pour les tissus pour lesquels le déchirement cor-
respond essentiellement à une rupture en chaîne des fils sous tension.
II est prouvé que cet essai peut ne pas être applicable à des nontissés d'une certaine
masse surfacique et d'une certaine rigidité. Des travaux complémentaires sont en
cours dans ce domaine.
e
iii
---------------------- Page: 3 ----------------------
NORM E I NTE RN AT1 ON ALE IS0 9073-4 : 1989 (FI
Textiles - Méthodes d'essai pour nontissés -
Partie 4:
Détermination de la résistance à la déchirure
3 Principe
1 Domaine d'application
Marquage d'un trapézoïde sur une éprouvette.
La présente partie de I'ISO 9073 prescrit une méthode pour la
détermination de la résistance à la déchirure des nontissés par
Fixation des bords non parallèles du trapézoïde entre les
@ le procédé du trapézoïde.
mâchoires d'une machine d'essai de traction.
Application d'une force en augmentation constante sur I'éprou-
2 Références normatives
vette de telle sorte que la déchirure se propage sur toute la lar-
geur.
Les normes suivantes contiennent des dispositions qui, par
suite de la référence qui en est faite, constituent des disposi- Détermination de la résistance maximale moyenne à la déchi-
tions valables pour la présente partie de I'ISO 9073. Au moment
rure, en newtons.
de la publication, les éditions indiquées étaient en vigueur.
Toute norme est sujette à révision et les parties prenantes des
4 Appareillage
accords fondés sur la présente partie de 1'60 9073 sont invi-
tées à rechercher la possibilité d'appliquer les éditions les plus
4.1 Machine d'essai de traction, de type à allongement à
récentes des normes indiquées ci-après. Les membres de la CE1
vitesse constante ou à déplacement transversal à vitesse cons-
et de I'ISO possèdent le registre des Normes internationales en
tante, dotée d'un dispositif autographique permettant d'enre-
vigueur à un moment donné.
gistrer la for
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.