ISO 4608:1998

Plastics — Homopolymer and copolymer resins of vinyl chloride for general use — Determination of plasticizer absorption at room temperature

Plastiques — Résines d'homopolymères et de copolymères de chlorure de vinyle à usages généraux — Détermination de la prise de plastifiant à température ambiante

General Information

• Status: Withdrawn
• Publication Date: 22-Apr-1998
• ICS: 83.080.20 - Thermoplastic materials
• Technical Committee: ISO/TC 61/SC 9 - Thermoplastic materials
• Drafting Committee: ISO/TC 61/SC 9/WG 20 - Poly(vinyl chloride)
• Current Stage: 9599 - Withdrawal of International Standard
• Completion Date: 10-Nov-2023

Relations

• Consolidates: ISO 5832-5:1978 - Implants for surgery — Metallic materials — Part 5: Wrought cobalt-chromium-tungsten- nickel alloy
• Effective Date: 06-Jun-2022
• Revised: ISO 4608:2023 - Plastics — Homopolymer and copolymer resins of vinyl chloride for general use — Determination of plasticizer absorption at room temperature
• Effective Date: 06-Jun-2022
• Revised: SIST ISO 4608:1996 - Plastics -- Homopolymer and copolymer resins of vinyl chloride for general use -- Determination of plasticizer absorption at room temperature
• Effective Date: 12-May-2008
• Revises: ISO 4608:1984 - Plastics — Homopolymer and copolymer resins of vinyl chloride for general use — Determination of plasticizer absorption at room temperature
• Effective Date: 15-Apr-2008

Standards Content (Sample)

INTERNATIONAL ISO
STANDARD 4608
Third edition
1998-05-01
Plastics — Homopolymer and copolymer
resins of vinyl chloride for general use —
Determination of plasticizer absorption
at room temperature
Plastiques — Résines d'homopolymères et de copolymères de chlorure
de vinyle à usages généraux — Détermination de la prise de plastifiant
à température ambiante
A
Reference number
ISO 4608:1998(E)

---------------------- Page: 1 ----------------------
ISO 4608:1998(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide
federation of national standards bodies (ISO member bodies). The work of
preparing International Standards is normally carried out through ISO
technical committees. Each member body interested in a subject for which
a technical committee has been established has the right to be represented
on that committee. International organizations, governmental and non-
governmental, in liaison with ISO, also take part in the work. ISO
collaborates closely with the International Electrotechnical Commission
(IEC) on all matters of electrotechnical standardization.
Draft International Standards adopted by the technical committees are
circulated to the member bodies for voting. Publication as an International
Standard requires approval by at least 75 % of the member bodies casting
a vote.
International Standard ISO 4608 was prepared by Technical Committee
ISO/TC 61, Plastics, Subcommittee SC 9, Thermoplastic materials.
This third edition cancels and replaces the second edition (ISO 4608:1984),
which has been technically revised.
©  ISO 1998
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced
or utilized in any form or by any means, electronic or mechanical, including photocopying and
microfilm, without permission in writing from the publisher.
International Organization for Standardization
Case postale 56 • CH-1211 Genève 20 • Switzerland
Internet [e-mail]
X.400 c=ch; a=400net; p=iso; o=isocs; s=central
Printed in Switzerland
ii

---------------------- Page: 2 ----------------------
©
INTERNATIONAL STANDARD  ISO ISO 4608:1998(E)
Plastics — Homopolymer and copolymer resins of vinyl chloride
for general use — Determination of plasticizer absorption at room
temperature
1  Scope
This International Standard specifies a method for determining plasticizer absorption at room temperature. It is
applicable to PVC general-purpose resins and filler resins (designated "G" and "F" in ISO 1060-1:1998, Plastics —
Homopolymer and copolymer resins of vinyl chloride — Part 1: Designation system and basis for specifications).
The object of the test is to determine the quantity of plasticizer absorbed by a resin at room temperature to give a
dry mixture.
The results give a general indication of the plasticizer absorption of a resin at room temperature. They indicate the
usefulness of resins for the manufacture of plasticized dry blends, particularly when taken in conjunction with the
results of plasticizer absorption tests under hot conditions.
2  Normative reference
The following standard contains provisions which, through reference in this text, constitute provisions of this
International Standard. At the time of publication, the edition indicated was valid. All standards are subject to
revision, and parties to agreements based on this International Standard are encouraged to investigate the
possibility of applying the most recent edition of the standard indicated below. Members of IEC and ISO maintain
registers of currently valid International Standards.
ISO 1385-1:1977, Phthalate esters for industrial use — Methods of test — Part 1: General.
3  Principle
An excess of bis-(2-ethylhexyl) phthalate (DOP) is added to a specified amount of resin. The mixture is then
centrifuged under defined conditions and the amount of plasticizer retained by the resin determined.
4  Apparatus and materials
Ordinary laboratory apparatus, plus the following:
4.1  Balance, capable of weighing to 0,1 mg.
3 3
4.2  Burette, for example 50 cm , graduated at 0,1 cm intervals.
1

---------------------- Page: 3 ----------------------
©
ISO
ISO 4608:1998(E)
4.3  Centrifuge, whose rotor turns in a horizontal plane and which has an acceleration under the test conditions of
–2 –2
24 500 m⋅s to 29 500 m⋅s measured at the bottoms of the tubes, with, if necessary, a cooling system to prevent
the temperature of the mixture from exceeding 30 °C at the end of centrifuging for 60 min.
NOTE —  It is permissible to use different centrifuging conditions, i.e. a different acceleration, a different time and smaller
centrifuge tubes (see 4.4), provided that it has been verified that the results obtained are equivalent.
4.4  Centrifuge tubes, to fit the centrifuge used, each consisting either of a tube, made of glass or another
material, with a conical bottom pierced by a hole of about 0,8 mm diameter (see figure 1) or of a cylindrical tube
fitted at one end with a sieve plate o
...

NORME ISO
INTERNATIONALE 4608
Troisième édition
1998-05-01
Plastiques — Résines d'homopolymères
et de copolymères de chlorure de vinyle
à usages généraux — Détermination de
la prise de plastifiant à température
ambiante
Plastics — Homopolymer and copolymer resins of vinyl chloride for
general use — Determination of plasticizer absorption at room temperature
A
Numéro de référence
ISO 4608:1998(F)

---------------------- Page: 1 ----------------------
ISO 4608:1998(F)
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération
mondiale d'organismes nationaux de normalisation (comités membres de
l'ISO). L'élaboration des Normes internationales est en général confiée aux
comités techniques de l'ISO. Chaque comité membre intéressé par une
étude a le droit de faire partie du comité technique créé à cet effet. Les
organisations internationales, gouvernementales et non gouvernementales,
en liaison avec l'ISO, participent également aux travaux. L'ISO collabore
étroitement avec la Commission électrotechnique internationale (CEI) en
ce qui concerne la normalisation électrotechnique.
Les projets de Normes internationales adoptés par les comités techniques
sont soumis aux comités membres pour vote. Leur publication comme
Normes internationales requiert l'approbation de 75 % au moins des
comités membres votants.
La Norme internationale ISO 4608 a été élaborée par le comité technique
ISO/TC 61, Plastiques, sous-comité SC 9, Matériaux thermoplastiques.
Cette troisième édition annule et remplace la deuxième édition
(ISO 4608:1984), dont elle constitue une révision technique.
©  ISO 1998
Droits de reproduction réservés. Sauf prescription différente, aucune partie de cette publi-
cation ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun pro-
cédé, électronique ou mécanique, y compris la photocopie et les microfilms, sans l'accord
écrit de l'éditeur.
Organisation internationale de normalisation
Case postale 56 • CH-1211 Genève 20 • Suisse
Internet [e-mail]
X.400 c=ch; a=400net; p=iso; o=isocs; s=central
Imprimé en Suisse
ii

---------------------- Page: 2 ----------------------
©
NORME INTERNATIONALE  ISO ISO 4608:1998(F)
Plastiques — Résines d'homopolymères et de copolymères de
chlorure de vinyle à usages généraux — Détermination de la prise
de plastifiant à température ambiante
1  Domaine d'application
La présente Norme internationale prescrit une méthode pour la détermination de la prise de plastifiant à
température ambiante des résines PVC à usages généraux et des résines renforcées par des fibres «G» et «F»
dans la désignation selon l'ISO 1060-1:1998, Plastiques — Résines d'homopolymères et de copolymères de
chlorure de vinyle — Partie 1: Système de désignation et base de spécification.
L'essai a pour but de déterminer la quantité de plastifiant qu'une résine absorbe à température ambiante pour
donner un mélange sec.
Les résultats donnent une indication générale de l'absorption de plastifiant par les résines à la température
ambiante. Ils indiquent l'aptitude des résines à la fabrication de mélanges plastifiés secs, en particulier en liaison
avec les résultats des essais d'absorption de plastifiant à haute température.
2  Référence normative
La norme suivante contient des dispositions qui, par suite de la référence qui en est faite, constituent des
dispositions valables pour la présente Norme internationale. Au moment de la publication, l'édition indiquée était en
vigueur. Toute norme est sujette à révision et les parties prenantes des accords fondés sur la présente Norme
internationale sont invitées à rechercher la possibilité d'appliquer l'édition la plus récente de la norme indiquée ci-
après. Les membres de la CEI et de l'ISO possèdent le registre des Normes internationales en vigueur à un
moment donné.
ISO 1385-1:1977,
Phtalates à usage industriel — Méthodes d'essai — Partie 1: Généralités.
3  Principe
Un excès de di-(2-éthylhexyl) phtalate (DOP) est ajouté à une masse prescrite de résine. Le mélange est centrifugé
dans des conditions définies et la quantité de plastifiant retenue par la résine est déterminée.
4  Appareillage et matériaux
Matériel courant de laboratoire, et
4.1  Balance, permettant d'effectuer des pesées à 0,1 mg près.
3 3
4.2  Burette, par exemple de 50 cm , graduée en 0,1 cm .
1

---------------------- Page: 3 ----------------------
©
ISO
ISO 4608:1998(F)
4.3  Centrifugeuse, avec étoile de centrifugation horizontale, permettant d'exercer, dans les conditions d'essai,
–2 –2
une accélération de 24 500 m⋅s à 29 500 m⋅s au niveau du fond du tube, et munie, si nécessaire, d'un dispositif
de refroidissement empêchant la température du mélange de dépasser 30 °C à la fin d'une centrifugation de
60 min.
NOTE —  Il est admis d'utiliser des conditions de centrifugation différentes, c'est-à-dire une accélération et une durée
différentes ainsi que des tubes de centrifugation plus petits (voir 4.4), à condition d'avoir vérifié que
...