ISO 1519:2002

Paints and varnishes — Bend test (cylindrical mandrel)

This International Standard specifies an empirical test procedure for assessing the resistance of a coating of paint, varnish or related product to cracking and/or detachment from a metal or plastic substrate when subjected to bending round a cylindrical mandrel under standard conditions. For a multicoat system, each coat may be tested separately or the complete system may be tested. The method specified may be carried out either as a "go/no go" test, by carrying out the test with a single specified size of mandrel, to assess compliance with a particular requirement, or by repeating the procedure using successively smaller mandrels to determine the diameter of the first mandrel over which the coating cracks and/or becomes detached from the substrate. Two types of apparatus are specified, type 1 being appropriate for use on test panels of thickness up to 0,3 mm, and type 2 for use on test panels of thickness up to 1,0 mm. Both types of apparatus have been found to give similar results with the same coating, but normally only one will be used for testing a given product.

Peintures et vernis — Essai de pliage sur mandrin cylindrique

La présente Norme Internationale spécifie une méthode d'essai empirique permettant d'évaluer la résistance d'une couche de peinture, de vernis ou de produit assimilé aux craquelures et/ou au décollement d'un subjectile métallique ou en matière plastique lorsqu'il est plié sur un mandrin cylindrique dans des conditions normalisées. Pour un système multicouche, l'essai peut porter sur chaque couche séparément ou sur le système complet. La méthode spécifiée peut être mise en oeuvre soit comme un essai «tout ou rien», l'essai étant effectué avec une dimension spécifiée unique du mandrin pour évaluer la conformité à une exigence particulière, soit en utilisant des mandrins de plus en plus petits pour déterminer le diamètre du premier mandrin sur lequel la couche se craquelle et/ou se décolle du subjectile. Deux types d'appareils sont spécifiés; le type 1 convient pour des panneaux d'essai dont l'épaisseur est inférieure ou égale à 0,3 mm, le type 2 pour des panneaux d'essai dont l'épaisseur est inférieure ou égale à 1,0 mm. Ces deux types d'appareils donnent des résultats semblables pour le même revêtement, mais normalement un seul sera utilisé pour essayer un produit donné.

General Information

• Status: Withdrawn
• Publication Date: 13-Mar-2002
• Withdrawal Date: 13-Mar-2002
• ICS: 87.040 - Paints and varnishes
• Technical Committee: ISO/TC 35/SC 9 - General test methods for paints and varnishes
• Drafting Committee: ISO/TC 35/SC 9 - General test methods for paints and varnishes
• Current Stage: 9599 - Withdrawal of International Standard
• Completion Date: 06-Jan-2011

Relations

• Revised: ISO 1519:2011 - Paints and varnishes — Bend test (cylindrical mandrel)
• Effective Date: 15-Apr-2008
• Consolidates: ISO 753-7:1981 - Acetic acid for industrial use — Methods of test — Part 7: Determination of dichromate index
• Effective Date: 06-Jun-2022
• Revises: ISO 1519:1973 - Paints and varnishes — Bend test (cylindrical mandrel)
• Effective Date: 15-Apr-2008

Standards Content (Sample)

INTERNATIONAL ISO
STANDARD 1519
Second edition
2002-03-15


Paints and varnishes — Bend test
(cylindrical mandrel)
Peintures et vernis — Essai de pliage sur mandrin cylindrique





Reference number
ISO 1519:2002(E)
©
 ISO 2002

---------------------- Page: 1 ----------------------
ISO 1519:2002(E)
PDF disclaimer
This PDF file may contain embedded typefaces. In accordance with Adobe's licensing policy, this file may be printed or viewed but shall not
be edited unless the typefaces which are embedded are licensed to and installed on the computer performing the editing. In downloading this
file, parties accept therein the responsibility of not infringing Adobe's licensing policy. The ISO Central Secretariat accepts no liability in this
area.
Adobe is a trademark of Adobe Systems Incorporated.
Details of the software products used to create this PDF file can be found in the General Info relative to the file; the PDF-creation parameters
were optimized for printing. Every care has been taken to ensure that the file is suitable for use by ISO member bodies. In the unlikely event
that a problem relating to it is found, please inform the Central Secretariat at the address given below.


©  ISO 2002
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means, electronic
or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address below or ISO's member body
in the country of the requester.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail [e-mail]
Web www.iso.ch
Printed in Switzerland

ii © ISO 2002 – All rights reserved

---------------------- Page: 2 ----------------------
ISO 1519:2002(E)
Contents Page
Foreword.iv
Introduction.v
1 Scope .1
2 Normative references.1
3 Required supplementary information.1
4 Apparatus .2
5 Sampling.4
6 Test panels .5
7 Procedure .5
8 Expression of results .7
9 Precision.7
10 Test report .7
Annex A (normative) Required supplementary information.8

© ISO 2002 – All rights reserved iii

---------------------- Page: 3 ----------------------
ISO 1519:2002(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO
member bodies). The work of preparing International Standards is normally carried out through ISO technical
committees. Each member body interested in a subject for which a technical committee has been established has
the right to be represented on that committee. International organizations, governmental and non-governmental, in
liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical
Commission (IEC) on all matters of electrotechnical standardization.
International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 3.
The main task of technical committees is to prepare International Standards. Draft International Standards adopted
by the technical committees are circulated to the member bodies for voting. Publication as an International
Standard requires approval by at least 75 % of the member bodies casting a vote.
Attention is drawn to the possibility that some of the elements of this International Standard may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights.
ISO 1519 was prepared by Technical Committee ISO/TC 35, Paints and varnishes, Subcommittee SC 9, General
test methods for paints and varnishes.
This second edition cancels and replaces the first edition (ISO 1519:1973), which has been technically revised.
Annex A forms a normative part of this International Standard.
iv © ISO 2002 – All rights reserved

---------------------- Page: 4 ----------------------
ISO 1519:2002(E)
Introduction
This International Standard is one of five standards which specify empirical test procedures for assessing the
resistance of coatings of paints, varnishes and related products to cracking and/or detachment from the substrate
under different conditions of deformation.
The other four documents are:
 ISO 1520, Paints and varnishes — Cupping test
 ISO 6272-1, Paints and varnishes — Rapid-deformation tests — Part 1: Falling-weight test, large area
 ISO 6272-2, Paints and varnishes — Rapid-deformation tests — Part 2: Falling-weight test, small area
 ISO 6860, Paints and varnishes — Bend test (conical mandrel)
The method chosen will depend on the property to be measured and on agreement between the interested parties.
In principle, all these tests differ from each other technically and in their accuracy.
© ISO 2002 – All rights reserved v

---------------------- Page: 5 ----------------------
INTERNATIONAL STANDARD ISO 1519:2002(E)

Paints and varnishes — Bend test (cylindrical mandrel)
1 Scope
This International Standard specifies an empirical test procedure for assessing the resistance of a coating of paint,
varnish or related product to cracking and/or detachment from a metal or plastic substrate when subjected to
bending round a cylindrical mandrel under standard conditions.
For a multicoat system, each coat may be tested separately or the complete system may be tested.
The method specified may be carried out
 either as a “go/no go” test, by carrying out the test with a single specified size of mandrel, to assess
compliance with a particular requirement;
 or by repeating the procedure using successively smaller mandrels to determine the diameter of the first
mandrel over which the coating cracks and/or becomes detached from the substrate.
Two types of apparatus are specified, type 1 being appropriate for use on test panels of thickness up to 0,3 mm,
and type 2 for use on test panels of thickness up to 1,0 mm. Both types of apparatus have been found to give
similar results with the same coating, but normally only one will be used for testing a given product.
2 Normative references
The following normative documents contain provisions which, through reference in this text, constitute provisions of
this International Standard. For dated references, subsequent amendments to, or revisions of, any of these
publications do not apply. However, parties to agreements based on this International Standard are encouraged to
investigate the possibility of applying the most recent editions of the normative documents indicated below. For
undated references, the latest edition of the normative document referred to applies. Members of ISO and IEC
maintain registers of currently valid International Standards.
ISO 1513:1992, Paints and varnishes — Examination and preparation of samples for testing
1)
ISO 1514:— , Paints and varnishes — Standard panels for testing
ISO 2808:1997, Paints and varnishes — Determination of film thickness
ISO 3270:1984, Paints and varnishes and their raw materials — Temperatures and humidities for conditioning and
testing
ISO 15528:2000, Paints, varnishes and raw materials for paints and varnishes — Sampling
3 Required supplementary information
For any particular application, the test method specified in ISO 1519 needs to be completed by supplementary
information.
The items of supplementary information are given in annex A.

1) To be published. (Revision of ISO 1514:1993)
© ISO 2002 – All rights reserved 1

---------------------- Page: 6 ----------------------
ISO 1519:2002(E)
4 Apparatus
4.1 Bend test apparatus
4.1.1 Material
In both types of apparatus specified below, the mandrels shall be made of a rigid and suitably corrosion-resistant
material, for example stainless steel.
4.1.2 Type 1 mandrel tester
An example of a type 1 tester is shown in Figures 1 and 2. This type of tester is used with test panels of thickness
not greater than 0,3 mm. A set of hinges is provided, each incorporating a cylindrical mandrel. The diameters of the
mandrels are 2 mm, 3 mm, 4 mm, 5 mm, 6 mm, 8 mm, 10 mm, 12 mm, 16 mm, 20 mm, 25 mm and 32 mm,
respectively, with a tolerance of ± 0,1 mm. The dimensions of the apparatus are not critical, except that the gap
between the surface of the mandrel and the plates of the hinges shall be (0,55 ± 0,05) mm. The mandrel shall be
free to rotate on its axis and the apparatus shall be provided with a stop to ensure that, when the test panel is bent,
the two parts are parallel.
NOTE Especially with the 2-mm-diameter mandrel, it is important to ensure that no distortion of the mandrel takes place
during the bending process, and not to use any mandrel showing such distortion.

Key
1 Mandrel
2 Stop of similar height to mandrel
Figure 1 — Type 1 bend test apparatus

Figure 2 — Type 1 bend test apparatus in use
2 © ISO 2002 – All rights reserved

---------------------- Page: 7 ----------------------
ISO 1519:2002(E)
4.1.3 Type 2 mandrel tester
An example of a type 2 tester is shown in Figures 3 and 4. Type 2 testers are normally used for panels with a
thickness of up to 1,0 m
...

NORME ISO
INTERNATIONALE 1519
Deuxième édition
2002-03-15


Peintures et vernis — Essai de pliage sur
mandrin cylindrique
Paints and varnishes — Bend test (cylindrical mandrel)





Numéro de référence
ISO 1519:2002(F)
©
 ISO 2002

---------------------- Page: 1 ----------------------
ISO 1519:2002(F)
PDF – Exonération de responsabilité
Le présent fichier PDF peut contenir des polices de caractères intégrées. Conformément aux conditions de licence d'Adobe, ce fichier peut
être imprimé ou visualisé, mais ne doit pas être modifié à moins que l'ordinateur employé à cet effet ne bénéficie d'une licence autorisant
l'utilisation de ces polices et que celles-ci y soient installées. Lors du téléchargement de ce fichier, les parties concernées acceptent de fait la
responsabilité de ne pas enfreindre les conditions de licence d'Adobe. Le Secrétariat central de l'ISO décline toute responsabilité en la
matière.
Adobe est une marque déposée d'Adobe Systems Incorporated.
Les détails relatifs aux produits logiciels utilisés pour la création du présent fichier PDF sont disponibles dans la rubrique General Info du
fichier; les paramètres de création PDF ont été optimisés pour l'impression. Toutes les mesures ont été prises pour garantir l'exploitation de
ce fichier par les comités membres de l'ISO. Dans le cas peu probable où surviendrait un problème d'utilisation, veuillez en informer le
Secrétariat central à l'adresse donnée ci-dessous.


©  ISO 2002
Droits de reproduction réservés. Sauf prescription différente, aucune partie de cette publication ne peut être reproduite ni utilisée sous quelque
forme que ce soit et par aucun procédé, électronique ou mécanique, y compris la photocopie et les microfilms, sans l'accord écrit de l’ISO à
l’adresse ci-après ou du comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax. + 41 22 749 09 47
E-mail [e-mail]
Web www.iso.ch
Imprimé en Suisse

ii © ISO 2002 – Tous droits réservés

---------------------- Page: 2 ----------------------
ISO 1519:2002(F)
Sommaire Page
Avant-propos .iv
Introduction.v
1 Domaine d'application .1
2 Références normatives .1
3 Informations complémentaires requises .1
4 Appareillage .2
5 Échantillonnage .4
6 Panneaux d'essai.5
7 Mode opératoire.5
8 Expression des résultats .7
9 Fidélité .7
10 Rapport d'essai.7
Annexe A (normative) Informations complémentaires requises .8

© ISO 2002 – Tous droits réservés iii

---------------------- Page: 3 ----------------------
ISO 1519:2002(F)
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes nationaux de
normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est en général confiée aux
comités techniques de l'ISO. Chaque comité membre intéressé par une étude a le droit de faire partie du comité
technique créé à cet effet. Les organisations internationales, gouvernementales et non gouvernementales, en
liaison avec l'ISO participent également aux travaux. L'ISO collabore étroitement avec la Commission
électrotechnique internationale (CEI) en ce qui concerne la normalisation électrotechnique.
Les Normes internationales sont rédigées conformément aux règles données dans les Directives ISO/CEI, Partie 3.
La tâche principale des comités techniques est d'élaborer les Normes internationales. Les projets de Normes
internationales adoptés par les comités techniques sont soumis aux comités membres pour vote. Leur publication
comme Normes internationales requiert l'approbation de 75 % au moins des comités membres votants.
L'attention est appelée sur le fait que certains des éléments de la présente Norme internationale peuvent faire
l'objet de droits de propriété intellectuelle ou de droits analogues. L'ISO ne saurait être tenue pour responsable de
ne pas avoir identifié de tels droits de propriété et averti de leur existence.
L'ISO 1519 a été élaborée par le comité technique ISO/TC 35, Peintures et vernis, sous-comité SC 9, Méthodes
générales d'essais des peintures et vernis.
Cette deuxième édition annule et remplace la première édition (ISO 1519:1973) qui a fait l'objet d'une révision
technique.
L’annexe A constitue un élément normatif de la présente Norme internationale.
iv © ISO 2002 – Tous droits réservés

---------------------- Page: 4 ----------------------
ISO 1519:2002(F)
Introduction
La présente Norme internationale est l'une des cinq normes qui spécifient des modes opératoires d’essai
empiriques permettant d’évaluer la résistance aux craquelures et/ou au décollement, dans différentes conditions de
déformation, des couches de peintures, de vernis et de produits assimilés.
Les quatre autres documents sont les suivants:
 ISO 1520, Peintures et vernis — Essai d’emboutissage
 ISO 6272-1, Peintures et vernis — Essais de déformation rapide — Partie 1: Essai de chute d’une masse sur
une surface importante
 ISO 6272-2, Peintures et vernis — Essais de déformation rapide — Partie 2: Essai de chute d’une masse sur
une surface réduite
 ISO 6860, Peintures et vernis — Essai de pliage (mandrin conique)
La méthode choisie dépendra de la propriété à mesurer et sera à convenir entre les parties. En principe, tous ces
essais diffèrent les uns des autres sur le plan technique et ne présentent pas la même exactitude.

© ISO 2002 – Tous droits réservés v

---------------------- Page: 5 ----------------------
NORME INTERNATIONALE ISO 1519:2002(F)

Peintures et vernis — Essai de pliage sur mandrin cylindrique
1 Domaine d'application
La présente Norme Internationale spécifie une méthode d'essai empirique permettant d’évaluer la résistance d'une
couche de peinture, de vernis ou de produit assimilé aux craquelures et/ou au décollement d'un subjectile
métallique ou en matière plastique lorsqu'il est plié sur un mandrin cylindrique dans des conditions normalisées.
Pour un système multicouche, l’essai peut porter sur chaque couche séparément ou sur le système complet.
La méthode spécifiée peut être mise en œuvre:
 soit comme un essai «tout ou rien», l'essai étant effectué avec une dimension spécifiée unique du mandrin
pour évaluer la conformité à une exigence particulière;
 soit en utilisant des mandrins de plus en plus petits pour déterminer le diamètre du premier mandrin sur lequel
la couche se craquelle et/ou se décolle du subjectile.
Deux types d'appareils sont spécifiés; le type 1 convient pour des panneaux d'essai dont l'épaisseur est inférieure
ou égale à 0,3 mm, le type 2 pour des panneaux d'essai dont l'épaisseur est inférieure ou égale à 1,0 mm. Ces
deux types d'appareils donnent des résultats semblables pour le même revêtement, mais normalement un seul
sera utilisé pour essayer un produit donné.
2 Références normatives
Les documents normatifs suivants contiennent des dispositions qui, par suite de la référence qui y est faite,
constituent des dispositions valables pour la présente Norme internationale. Pour les références datées, les
amendements ultérieurs ou les révisions de ces publications ne s'appliquent pas. Toutefois, les parties prenantes
aux accords fondés sur la présente Norme internationale sont invitées à rechercher la possibilité d'appliquer les
éditions les plus récentes des documents normatifs indiqués ci-après. Pour les références non datées, la dernière
édition du document normatif en référence s'applique. Les membres de l'ISO et de la CEI possèdent le registre des
Normes internationales en vigueur.
ISO 1513:1992, Peintures et vernis — Examen et préparation des échantillons pour essais
1)
ISO 1514:— , Peintures et vernis — Panneaux normalisés pour essais
ISO 2808:1997, Peintures et vernis — Détermination de l’épaisseur du feuil
ISO 3270:1984, Peintures et vernis et leurs matières premières — Températures et humidités pour le
conditionnement et l’essai
ISO 15528:2000, Peintures, vernis et matières premières pour peintures et vernis — Échantillonnage
3 Informations complémentaires requises
Dans le cas d’une application particulière, des informations complémentaires doivent compléter la méthode d’essai
spécifiée dans l’ISO 1519.
Ces informations complémentaires figurent en annexe A.

1)
À publier. (Révision de l'ISO 1514:1993)
© ISO 2002 – Tous droits réservés 1

---------------------- Page: 6 ----------------------
ISO 1519:2002(F)
4 Appareillage
4.1 Appareil d'essai de pliage
4.1.1 Matériau
Dans les deux types d'appareils décrits ci-dessous, les mandrins doivent être constitués d’un matériau rigide et
résistant convenablement à la corrosion, par exemple en acier inoxydable.
4.1.2 Dispositif d’essai de mandrin de type 1
Un exemple de dispositif d’essai de type 1 est représenté sur les Figures 1 et 2. Ce type de dispositif est utilisé
avec des panneaux d'essai dont l’épaisseur n’excède pas 0,3 mm. Il est muni d'un jeu de charnières comprenant
chacune un mandrin cylindrique. Les diamètres des mandrins sont respectivement de 2 mm, 3 mm, 4 mm, 5 mm,
6 mm, 8 mm, 10 mm, 12 mm, 16 mm, 20 mm, 25 mm et 32 mm, avec une tolérance de ± 0,1 mm. Les dimensions
de l'appareil ne sont pas très importantes, mais l'écart entre la surface du mandrin et les plaques des charnières
doit être de (0,55 ± 0,05) mm. Le mandrin doit tourner librement sur son axe et l'appareil doit être muni d'une butée
pour que les deux parties restent parallèles lorsque le panneau d'essai est plié.
NOTE Il est important, surtout pour les mandrins de 2 mm de diamètre, que le mandrin ne se déforme pas au cours du
pliage; il est important de ne pas utiliser de mandrin ainsi déformé.

Légende
1 Mandrin
2 Butée de hauteur égale à celle du mandrin
Figure 1 — Appareil d’essai de pliage de type 1


Figure 2 — Appareil d’essai de pliage de type 1 en fonctionnement
2 © ISO 2002 – Tous droits réservés

---------------------- Page: 7 ----------------------
ISO 1519:2002(F)
4.1.3 Dispositif d’essai de mandrin de type 2
Les Figures 3 et 4 montrent un exemple de dispositif d’essai de type 2. Les dispositifs d’essai de type 2 sont
normalement utilisés pour les panneaux dont l’épaisseu
...