ISO 15876-2:2017

Plastics piping systems for hot and cold water installations — Polybutene (PB) — Part 2: Pipes

ISO 15876-2:2017 specifies the characteristics of pipes for polybutene-1 (PB-1) piping systems intended to be used for hot and cold water installations within buildings for the conveyance of water whether or not intended for human consumption (domestic systems), and for heating systems, under design pressures and temperatures appropriate to the class of application (see ISO 15876‑1). The designation polybutene is used together with the abbreviation PB throughout this document. ISO 15876-2:2017 covers a range of service conditions (application classes), design pressures and pipe dimension classes. For values of TD, Tmax and Tmal in excess of those in ISO 15876‑1, this document does not apply. NOTE 1 It is the responsibility of the purchaser or specifier to make the appropriate selections from these aspects, taking into account their particular requirements and any relevant national regulations and installation practices or codes. It also specifies the test parameters for the test methods referred to in this document. In conjunction with the other parts of ISO 15876, this document is applicable to PB pipes, their joints and to joints with components of PB, other plastics and non-plastics materials intended to be used for hot and cold water installations. It is applicable to pipes with or without (a) barrier layer(s). NOTE 2 In the case of plastics pipes provided with a thin barrier layer, e.g. to prevent or greatly diminish the diffusion of gases and the transmission of light into or through the pipe wall, the design stress requirements are totally met by the base polymer (PB).

Systèmes de canalisations en plastique pour les installations d'eau chaude et froide — Polybutène (PB) — Partie 2: Tubes

ISO 15876-2:2017 spécifie les caractéristiques des tubes des systèmes de canalisations en polybutène-1 (PB-1), conçus pour être utilisés dans des installations d'eau chaude et froide à l'intérieur des bâtiments, pour le transport de l'eau destinée ou non à la consommation humaine (systèmes domestiques), et dans des installations de chauffage, à des pressions et des températures de service adaptées à leur classe d'application (voir l'ISO 15876‑1). La désignation polybutène est utilisée conjointement avec l'abréviation PB dans l'ensemble du présent document. ISO 15876-2:2017 couvre une gamme de conditions de service (classes d'application) et de classes de pressions de service et de dimensions des tubes. Pour les valeurs TD, Tmax et Tmal dépassant celles de l'ISO 15876‑1, le présent document ne s'applique pas. NOTE 1 Il est de la responsabilité de l'acheteur ou du prescripteur de sélectionner convenablement ces aspects, en tenant compte des exigences particulières et des éventuelles règles nationales et pratiques ou codes de pose appropriés. Il spécifie également les paramètres d'essai pour les méthodes d'essai auxquelles il est fait référence dans le présent document. Avec les autres parties de l'ISO 15876, le présent document s'applique aux tubes en PB, à leurs assemblages et aux assemblages avec des composants fabriqués en PB et en d'autres matériaux, plastiques ou non plastiques, destinés à des installations d'eau chaude et froide. Il s'applique aux tubes avec ou sans couche(s) barrière. NOTE 2 Dans le cas des tubes plastiques pourvus d'une fine couche barrière, par exemple, pour éviter ou diminuer fortement la diffusion de gaz et la transmission de la lumière dans ou à travers la paroi du tube, les exigences relatives à la contrainte de dimensionnement sont totalement satisfaites par le polymère de base (PB).

General Information

• Status: Published
• Publication Date: 09-Jan-2017
• ICS: 23.040.20 - Plastics pipes
• ICS: 91.140.60 - Water supply systems
• Technical Committee: ISO/TC 138/SC 2 - Plastics pipes and fittings for water supplies
• Drafting Committee: ISO/TC 138/SC 2/WG 1 - Plastics piping systems for hot and cold water applications
• Current Stage: 9093 - International Standard confirmed
• Completion Date: 21-Jul-2022

Relations

• Amended By: ISO 15876-2:2017/Amd 1:2020 - Plastics piping systems for hot and cold water installations — Polybutene (PB) — Part 2: Pipes — Amendment 1
• Effective Date: 09-May-2020
• Consolidates: ISO 9803-1:2007 - Vacuum technology — Mounting dimensions of pipeline fittings — Part 1: Non knife-edge flange type
• Effective Date: 06-Jun-2022
• Revises: ISO 15876-2:2003/Amd 1:2007 - Plastics piping systems for hot and cold water installations — Polybutylene (PB) — Part 2: Pipes — Amendment 1
• Effective Date: 03-Nov-2012
• Revises: ISO 15876-2:2003 - Plastics piping systems for hot and cold water installations — Polybutylene (PB) — Part 2: Pipes
• Effective Date: 03-Nov-2012
• Consolidated By: ISO 19116:2019 - Geographic information — Positioning services
• Effective Date: 06-Jun-2022

Standards Content (Sample)

INTERNATIONAL ISO
STANDARD 15876-2
Second edition
2017-01
Plastics piping systems for hot
and cold water installations —
Polybutene (PB) —
Part 2:
Pipes
Systèmes de canalisations en plastique pour les installations d’eau
chaude et froide — Polybutène (PB) —
Partie 2: Tubes
Reference number
ISO 15876-2:2017(E)
©
ISO 2017

---------------------- Page: 1 ----------------------
ISO 15876-2:2017(E)

COPYRIGHT PROTECTED DOCUMENT
© ISO 2017, Published in Switzerland
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized otherwise in any form
or by any means, electronic or mechanical, including photocopying, or posting on the internet or an intranet, without prior
written permission. Permission can be requested from either ISO at the address below or ISO’s member body in the country of
the requester.
ISO copyright office
Ch. de Blandonnet 8 • CP 401
CH-1214 Vernier, Geneva, Switzerland
Tel. [phone]
Fax [phone]
[e-mail]
www.iso.org
ii © ISO 2017 – All rights reserved

---------------------- Page: 2 ----------------------
ISO 15876-2:2017(E)

Contents Page
Foreword .iv
Introduction .v
1 Scope . 1
2 Normative references . 1
3 Terms and definitions, symbols and abbreviated terms . 2
4 Pipe material . 2
4.1 General . 2
4.2 Evaluation of σ -curves . 2
LPL
4.3 Influence on water intended for human consumption . 5
5 General characteristics . 6
5.1 Appearance . 6
5.2 Opacity . 6
6 Geometrical characteristics . 6
6.1 General . 6
6.2 Dimensions of pipes . 7
6.2.1 Outside diameters . 7
6.2.2 Wall thicknesses and their tolerances . 7
7 Mechanical characteristics .10
8 Physical and chemical characteristics .10
9 Performance requirements .11
10 Marking .11
10.1 General requirements .11
10.2 Minimum required marking .12
Annex A (normative) Derivation of S .13
calc,max
Bibliography .16
© ISO 2017 – All rights reserved iii

---------------------- Page: 3 ----------------------
ISO 15876-2:2017(E)

Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www .iso .org/ directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www .iso .org/ patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation on the meaning of ISO specific terms and expressions related to conformity assessment,
as well as information about ISO’s adherence to the World Trade Organization (WTO) principles in the
Technical Barriers to Trade (TBT) see the following URL: www . i so .org/ iso/ foreword .html.
ISO 15876-2 was prepared by the European Committee Standardization (CEN) Technical Committee
CEN/TC 155, Plastics piping systems and ducting systems, in collaboration with ISO Technical Committee
ISO/TC 138, Plastics pipes, fittings and valves for the transport of fluids, Subcommittee SC 2, Plastics pipes
and fittings for water supplies, in accordance with the Agreement on technical cooperation between ISO
and CEN (Vienna Agreement).
This second edition cancels and replaces the first edition (ISO 15876-2:2003), which has been
technically revised with the following changes:
— introduction of polybutene random copolymer (PB-R) and renaming existing polybutene (PB) into
polybutene homopolymer (PB-H);
— revision of specifications for conditioning of samples.
It also incorporates the Amendment ISO 15876-2:2003/Amd 1:2007.
A list of all parts in the ISO 15876 series can be found on the ISO website.
iv © ISO 2017 – All rights reserved

---------------------- Page: 4 ----------------------
ISO 15876-2:2017(E)

Introduction
The System Standard ISO 15876, of which this document is Part 2, specifies the requirements for a
piping system when made from polybutene (PB). The piping system is intended to be used for hot and
cold water installations.
In respect of potential adverse effects on the quality of water intended for human consumption, caused
by the product covered by ISO 15876 (all parts):
— ISO 15876 (all parts) provides no information as to whether the product may be used without
restriction in any of the Member States of the EU or EFTA;
— it should be noted that, while awaiting the adoption of verifiable European criteria, existing national
regulations concerning the use and/or the characteristics of this product remain in force.
Requirements and test methods for material and components, other than pipes, are specified in
ISO 15876-1 and ISO 15876-3. Characteristics for fitness for purpose (mainly for joints) are covered in
ISO 15876-5. ISO/TS 15876-7 gives guidance for the assessment of conformity.
This document specifies the characteristics of pipes.
At the date of publication of this standard, System Standards for piping systems of other plastics
materials used for the same application include ISO 15874, ISO 15875, ISO 15876, ISO 15877, ISO 21003
and ISO 22391.
© ISO 2017 – All rights reserved v

---------------------- Page: 5 ----------------------
INTERNATIONAL STANDARD ISO 15876-2:2017(E)
Plastics piping systems for hot and cold water
installations — Polybutene (PB) —
Part 2:
Pipes
1 Scope
This document specifies the characteristics of pipes for polybutene-1 (PB-1) piping systems intended to
be used for hot and cold water installations within buildings for the conveyance of water whether or not
intended for human consumption (domestic systems), and for heating systems, under design pressures
and temperatures appropriate to the class of application (see ISO 15876-1).
The designation polybutene is used together with the abbreviation PB throughout this document.
This document covers a range of service conditions (application classes), design pressures and pipe
dimension classes. For values of T , T and T in excess of those in ISO 15876-1, this document does
D max mal
not apply.
NOTE 1 It is the responsibility of the purchaser or specifier to make the appropriate selections from these
aspects, taking into account their particular requirements and any relevant national regulations and installation
practices or codes.
It also specifies the test parameters for the test methods referred to in this document.
In conjunction with the other parts of ISO 15876, this document is applicable to PB pipes, their joints
and to joints with components of PB, other plastics and non-plastics materials intended to be used for
hot and cold water installations.
It is applicable to pipes with or without (a) barrier layer(s).
NOTE 2 In the case of plastics pipes provided with a thin barrier layer, e.g. to prevent or greatly diminish the
diffusion of gases and the transmission of light into or through the pipe wall, the design stress requirements are
totally met by the base polymer (PB).
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content
constitutes requirements of this document. For dated references, only the edition cited applies. For
undated references, the latest edition of the referenced document (including any amendments) applies.
ISO 1133-1, Plastics — Determination of the melt mass-flow rate (MFR) and melt volume-flow rate (MVR)
of thermoplastics — Part 1: Standard method
ISO 1167-1, Thermoplastics pipes, fittings and assemblies for the conveyance of fluids — Determination of
the resistance to internal pressure — Part 1: General method
ISO 1167-2, Thermoplastics pipes, fittings and assemblies for the conveyance of fluids — Determination of
the resistance to internal pressure — Part 2: Preparation of pipe test pieces
ISO 2505, Thermoplastics pipes — Longitudinal reversion — Test method and parameters
ISO 3126, Plastics piping systems — Plastics components — Determination of dimensions
ISO 7686, Plastics pipes and fittings — Determination of opacity
© ISO 2017 – All rights reserved 1

---------------------- Page: 6 ----------------------
ISO 15876-2:2017(E)

ISO 9080, Plastics piping and ducting systems — Determination of the long-term hydrostatic strength of
thermoplastics materials in pipe form by extrapolation
ISO 15876-1:2003, Plastics piping systems for hot and cold water installations — Polybutene (PB) —
Part 1: General
ISO 15876-3, Plastics piping systems for hot and cold water installations — Polybutene (PB) — Part 3:
Fittings
ISO 15876-5, Plastics piping systems for hot and cold water installations — Polybutene (PB) —Part 5:
Fitness for purpose of the system
3 Terms and definitions, symbols and abbreviated terms
For the purposes of this document, the terms and definitions, symbols and abbreviated terms given in
ISO 15876-1 apply.
ISO and IEC maintain terminological databases for use in standardization at the following addresses:
— IEC Electropedia: available at http:// www .electropedia .org/
— ISO Online browsing platform: available at http:// www .iso .org/ obp
4 Pipe material
4.1 General
The pipe material from which the pipe is made shall comply with ISO 15876-1.
After extrusion or moulding, PB undergoes a crystalline phase transition (usually called ageing) before
it develops its final properties. The minimum required transition time depends on temperature and
product characteristics. The same final material performance is obtained once completion of crystalline
phase transition is achieved, irrespective of transition conditions. For quality control purposes,
therefore, test specimens shall be taken immediately after processing and be conditioned in accordance
with recommendations obtained from the compound supplier prior to testing.
The crystalline phase transition is dependent on time and temperature. For guidance a minimum time
of five days for PB-H and one day for PB-R should be allowed at 23 °C, unless accelerated ageing is
performed.
NOTE The crystalline phase transition can be considerably accelerated upon applying higher hydrostatic
pressure of approx. 1 kbar to 2 kbar. Accelerated ageing at higher pressure can be accepted if test results can be
proven reproducible and equal to those obtained at atmospheric pressure.
Because of the slow crystallization, transformation and shrinkage which takes places after PB-H and
PB-R plastics are cooled from the melt, physical testing should be delayed after extrusion or moulding
until this morphological transition is complete.
4.2 Evaluation of σ -curves
LPL
The pipe material shall be evaluated in accordance with ISO 9080 or equivalent where internal pressure
tests are made in accordance with ISO 1167-1 and ISO 1167-2 to find the σ -values. The σ -value
LPL LPL
thus determined shall at least be as high as the corresponding values of the reference curves given in
Figure 1 or Figure 2.
NOTE One equivalent way of evaluation is to calculate the σ -value for each temperature (e.g. 20 °C, 60 °C
LPL
to 70 °C and 95 °C) individually.
2 © ISO 2017 – All rights reserved

---------------------- Page: 7 ----------------------
ISO 15876-2:2017(E)

The reference curves in Figure 1 in the temperature range of 10 °C to 110 °C for PB-H and in Figure 2 in
the temperature range of 10 °C to 95 °C for PB-R are derived from the following formulae:
First branch (i.e. the left-hand portion of the lines as shown in Figure 1 and Figure 2)
for PB-H:
125010⋅lg σ 173892,7
log t =−430,866− ++290,056 9⋅log σ (1)
TT
for PB-R:
104096,,6⋅lg σ 145940 231
log t =−367,8019− ++245,536⋅log σ (2)
TT
Second branch (i. e. the right-hand portion of the lines as shown in Figure 1)
for PB-H:
37262,,75⋅lg σ 2 556 48
log t =−129,895− ++88,56735⋅log σ (3)
TT
To demonstrate conformance to the reference lines, pipe samples shall be tested at following
temperatures and at various hoop stresses such that, at each of the temperatures given, at least three
failure times fall in each of the following time intervals:
— temperatures 20 °C; 60 °C to 70 °C; 95 °C;
— time intervals 10 h to 100 h, 100 h to 1 000 h, 1 000 h to 8 760 h and above 8 760 h.
In tests lasting more than 8 760 h, once failure is reached at a stress and time at least on or above the
reference line, any time after that may be considered as the failure time. Testing should be carried out
in accordance with ISO 1167-1 and ISO 1167-2.
Conformance with the reference lines should be demonstrated by plotting the individual experimental
results on the graph. At least 97,5 % of them should lie on or above the reference line.
© ISO 2017 – All rights reserved 3

---------------------- Page: 8 ----------------------
ISO 15876-2:2017(E)

50
40
30
20
10 ˚C
20 ˚C
30 ˚C
40 ˚C
...

NORME ISO
INTERNATIONALE 15876-2
Deuxième édition
2017-01
Systèmes de canalisations en plastique
pour les installations d’eau chaude et
froide — Polybutène (PB) —
Partie 2:
Tubes
Plastics piping systems for hot and cold water installations —
Polybutene (PB) —
Part 2: Pipes
Numéro de référence
ISO 15876-2:2017(F)
©
ISO 2017

---------------------- Page: 1 ----------------------
ISO 15876-2:2017(F)

DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2017, Publié en Suisse
Droits de reproduction réservés. Sauf indication contraire, aucune partie de cette publication ne peut être reproduite ni utilisée
sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique, y compris la photocopie, l’affichage sur
l’internet ou sur un Intranet, sans autorisation écrite préalable. Les demandes d’autorisation peuvent être adressées à l’ISO à
l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Ch. de Blandonnet 8 • CP 401
CH-1214 Vernier, Geneva, Switzerland
Tel. [phone]
Fax [phone]
[e-mail]
www.iso.org
ii © ISO 2017 – Tous droits réservés

---------------------- Page: 2 ----------------------
ISO 15876-2:2017(F)

Sommaire Page
Avant-propos .iv
Introduction .v
1 Domaine d’application . 1
2 Références normatives . 1
3 Termes et définitions, symboles et abréviations . 2
4 Matière des tubes . 2
4.1 Généralités . 2
4.2 Évaluation des courbes de σ .
LPL 3
4.3 Influence sur l’eau destinée à la consommation humaine . 6
5 Caractéristiques générales . 6
5.1 Aspect . . 6
5.2 Opacité . 6
6 Caractéristiques géométriques . 6
6.1 Généralités . 6
6.2 Dimensions des tubes . 7
6.2.1 Diamètres extérieurs . 7
6.2.2 Épaisseurs de paroi et tolérances . 7
7 Caractéristiques mécaniques .10
8 Caractéristiques physiques et chimiques .10
9 Exigences de performance .11
10 Marquage .11
10.1 Exigences générales .11
10.2 Marquage minimal exigé .12
Annexe A (normative) Détermination de S .13
calc,max
Bibliographie .16
© ISO 2017 – Tous droits réservés iii

---------------------- Page: 3 ----------------------
ISO 15876-2:2017(F)

Avant-propos
L’ISO (Organisation internationale de normalisation) est une fédération mondiale d’organismes
nationaux de normalisation (comités membres de l’ISO). L’élaboration des Normes internationales est
en général confiée aux comités techniques de l’ISO. Chaque comité membre intéressé par une étude
a le droit de faire partie du comité technique créé à cet effet. Les organisations internationales,
gouvernementales et non gouvernementales, en liaison avec l’ISO participent également aux travaux.
L’ISO collabore étroitement avec la Commission électrotechnique internationale (IEC) en ce qui
concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier de prendre note des différents
critères d’approbation requis pour les différents types de documents ISO. Le présent document a été
rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir www
.iso .org/ directives).
L’attention est appelée sur le fait que certains des éléments du présent document peuvent faire l’objet de
droits de propriété intellectuelle ou de droits analogues. L’ISO ne saurait être tenue pour responsable
de ne pas avoir identifié de tels droits de propriété et averti de leur existence. Les détails concernant
les références aux droits de propriété intellectuelle ou autres droits analogues identifiés lors de
l’élaboration du document sont indiqués dans l’Introduction et/ou dans la liste des déclarations de
brevets reçues par l’ISO (voir www .iso .org/ brevets).
Les appellations commerciales éventuellement mentionnées dans le présent document sont données
pour information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un
engagement.
Pour une explication de la signification des termes et expressions spécifiques de l’ISO liés à l’évaluation
de la conformité, ou pour toute information au sujet de l’adhésion de l’ISO aux principes de l’Organisation
mondiale du commerce (OMC) concernant les obstacles techniques au commerce (OTC), voir le lien
suivant: w w w . i s o .org/ iso/ fr/ avant -propos .html
L’ISO 15876-2 a été élaborée par le Comité technique CEN/TC 155, Systèmes de canalisations et de gaines
en plastiques, du Comité européen de normalisation (CEN), en collaboration avec le Comité technique
ISO/TC 138, Tubes, raccords et robinetterie en matières plastiques pour le transport des fluides, de
l’Organisation internationale de normalisation (ISO), Sous-comité SC 2, Tubes et raccords en matières
plastiques pour adduction et distribution d’eau, conformément à l’Accord de coopération technique entre
l’ISO et le CEN (Accord de Vienne).
Cette deuxième édition annule et remplace la première édition (ISO 15876-2:2003) qui a fait l’objet
d’une révision technique avec les modifications suivantes:
— ajout du copolymère statistique de polybutène (PB R) et modification de la désignation polybutène
(PB) actuelle en homopolymère de polybutène (PB-H);
— révision des spécifications relatives au conditionnement des échantillons.
Il comprend également l’amendement ISO 15876-2:2003/Amd 1:2007.
Une liste de toutes les parties de la série ISO 15876 est disponible sur le site web de l’ISO.
iv © ISO 2017 – Tous droits réservés

---------------------- Page: 4 ----------------------
ISO 15876-2:2017(F)

Introduction
La norme de système ISO 15876, dont le présent document constitue la Partie 2, spécifie les exigences
relatives à un système de canalisations en polybutène (PB). Le système de canalisations est destiné aux
installations d’eau chaude et froide.
Pour ce qui concerne les éventuels effets défavorables du produit visé par l’ISO 15876 (toutes les
parties) sur la qualité des eaux destinées à la consommation humaine:
— aucune information n’est fournie par l’ISO 15876 (toutes les parties) sur les restrictions possibles
d’utilisation du produit dans un État membre de l’UE ou de l’AELE;
— il convient de rappeler que, dans l’attente de l’adoption de critères européens vérifiables, les
réglementations nationales existantes concernant l’utilisation et/ou les caractéristiques de ce
produit restent en vigueur.
Les exigences et les méthodes d’essai relatives à la matière et aux composants autres que les tubes sont
spécifiées dans l’ISO 15876-1 et l’ISO 15876-3. Les caractéristiques d’aptitude à l’emploi (principalement
pour les assemblages) sont traitées dans l’ISO 15876-5. L’ISO/TS 15876-7 fournit un guide pour
l’évaluation de la conformité.
Le présent document spécifie les caractéristiques des tubes.
À la date de publication de la présente norme, les normes de système pour les systèmes de canalisations
réalisés à partir d’autres matières plastiques et destinés à la même application comprennent l’ISO 15874,
l’ISO 15875, l’ISO 15876, l’ISO 15877, l’ISO 21003 et l’ISO 22391.
© ISO 2017 – Tous droits réservés v

---------------------- Page: 5 ----------------------
NORME INTERNATIONALE ISO 15876-2:2017(F)
Systèmes de canalisations en plastique pour les
installations d’eau chaude et froide — Polybutène (PB) —
Partie 2:
Tubes
1 Domaine d’application
Le présent document spécifie les caractéristiques des tubes des systèmes de canalisations en
polybutène-1 (PB-1), conçus pour être utilisés dans des installations d’eau chaude et froide à l’intérieur
des bâtiments, pour le transport de l’eau destinée ou non à la consommation humaine (systèmes
domestiques), et dans des installations de chauffage, à des pressions et des températures de service
adaptées à leur classe d’application (voir l’ISO 15876-1).
La désignation polybutène est utilisée conjointement avec l’abréviation PB dans l’ensemble du présent
document.
Le présent document couvre une gamme de conditions de service (classes d’application) et de classes
de pressions de service et de dimensions des tubes. Pour les valeurs T , T et T dépassant celles de
D max mal
l’ISO 15876-1, le présent document ne s’applique pas.
NOTE 1 Il est de la responsabilité de l’acheteur ou du prescripteur de sélectionner convenablement ces aspects,
en tenant compte des exigences particulières et des éventuelles règles nationales et pratiques ou codes de pose
appropriés.
Il spécifie également les paramètres d’essai pour les méthodes d’essai auxquelles il est fait référence
dans le présent document.
Avec les autres parties de l’ISO 15876, le présent document s’applique aux tubes en PB, à leurs
assemblages et aux assemblages avec des composants fabriqués en PB et en d’autres matériaux,
plastiques ou non plastiques, destinés à des installations d’eau chaude et froide.
Il s’applique aux tubes avec ou sans couche(s) barrière.
NOTE 2 Dans le cas des tubes plastiques pourvus d’une fine couche barrière, par exemple, pour éviter ou
diminuer fortement la diffusion de gaz et la transmission de la lumière dans ou à travers la paroi du tube, les
exigences relatives à la contrainte de dimensionnement sont totalement satisfaites par le polymère de base (PB).
2 Références normatives
Les documents suivants cités dans le texte constituent, en tout ou partie de leur contenu, des exigences
du présent document. Pour les références datées, seule l’édition citée s’applique. Pour les références non
datées, la dernière édition du document de référence s’applique (y compris les éventuels amendements).
ISO 1133-1, Plastiques — Détermination de l’indice de fluidité à chaud des thermoplastiques, en masse
(MFR) et en volume (MVR) — Partie 1: Méthode normale
ISO 1167-1, Tubes, raccords et assemblages en matières thermoplastiques pour le transport des fluides —
Détermination de la résistance à la pression interne — Partie 1: Méthode générale
ISO 1167-2, Tubes, raccords et assemblages en matières thermoplastiques pour le transport des fluides —
Détermination de la résistance à la pression interne — Partie 2: Préparation des éprouvettes tubulaires
© ISO 2017 – Tous droits réservés 1

---------------------- Page: 6 ----------------------
ISO 15876-2:2017(F)

ISO 2505, Tubes en matières thermoplastiques — Retrait longitudinal à chaud — Méthode d’essai et
paramètres
ISO 3126, Systèmes de canalisations en plastiques — Composants en plastiques — Détermination des
dimensions
ISO 7686, Tubes et raccords en matières plastiques — Détermination de l’opacité
ISO 9080, Systèmes de canalisations et de gaines en matières plastiques — Détermination de la résistance
hydrostatique à long terme des matières thermoplastiques sous forme de tubes par extrapolation
ISO 15876-1:2003, Systèmes de canalisations en plastique pour les installations d’eau chaude et froide —
Polybutène (PB) — Partie 1: Généralités
ISO 15876-3, Systèmes de canalisations en plastique pour les installations d’eau chaude et froide —
Polybutène (PB) — Partie 3: Raccords
ISO 15876-5, Systèmes de canalisations en plastique pour les installations d’eau chaude et froide —
Polybutène (PB) — Partie 5: Aptitude à l’emploi du système
3 Termes et définitions, symboles et abréviations
Pour les besoins du présent document, les termes, définitions, symboles et abréviations de
l’ISO 15876-1 s’appliquent.
L’ISO et l’IEC tiennent à jour des bases de données terminologiques destinées à être utilisées en
normalisation, consultables aux adresses suivantes:
— IEC Electropedia: disponible à l’adresse http:// www .electropedia .org/
— ISO Online browsing platform: disponible à l’adresse http:// www .iso .org/ obp
4 Matière des tubes
4.1 Généralités
La matière dans laquelle le tube est fabriqué doit être conforme à l’ISO 15876-1.
Après son extrusion ou son moulage, le PB subit une transition de phase cristalline (généralement
appelée vieillissement), avant d’acquérir ses propriétés finales. La durée minimale de transition requise
dépend de la température et des caractéristiques du produit. Les mêmes performances finales de la
matière sont obtenues au terme de la transition de phase cristalline, quelles que soient les conditions
de transition. Pour les besoins du contrôle qualité, les éprouvettes doivent donc être prélevées
immédiatement après le procédé de production et conditionnées conformément aux recommandations
fournies par le fournisseur de la composition avant les essais.
La transition de phase cristalline dépend du temps et de la température. À titre indicatif, il convient de
laisser le PB-H pendant une durée minimale de 5 jours et le PB-R pendant une durée minimale d’une
journée à 23 °C, sauf si l’on procède à un vieillissement accéléré.
NOTE La transition de phase cristalline peut être considérablement accélérée en appliquant une pression
hydrostatique plus élevée, d’environ 1 kbar à 2 kbar. Le vieillissement accéléré à pression plus élevée peut être
accepté s’il est possible de démontrer la reproductibilité des résultats d’essai et leur équivalence avec ceux
obtenus à la pression atmosphérique.
En raison de la lenteur des processus de cristallisation, de transformation et de retrait qui se produisent
suite au refroidissement des plastiques PB-H et PB-R après la fusion, il est nécessaire de retarder
les essais physiques après extrusion ou moulage, jusqu’à ce que cette transition morphologique soit
terminée.
2 © ISO 2017 – Tous droits réservés

---------------------- Page: 7 ----------------------
ISO 15876-2:2017(F)

4.2 Évaluation des courbes de σ
LPL
La matière des tubes doit être évaluée selon l’ISO 9080, ou toute méthode équivalente qui inclut
des essais de pression interne réalisés conformément à l’ISO 1167-1 et l’ISO 1167-2 pour trouver les
valeurs σ . La valeur σ ainsi déterminée doit au moins être égale aux valeurs correspondantes des
LPL LPL
courbes de référence de la Figure 1 ou la Figure 2.
NOTE Une méthode d’évaluation équivalente consiste à calculer la valeur σ pour chacune des
LPL
températures (par exemple, 20 °C, 60 °C à 70 °C et 95 °C).
Les courbes de référence de la Figure 1, données pour le PB-H dans la gamme de température de 10 °C
à 110 °C, et de la Figure 2, données pour le PB-R dans la gamme de température de 10 °C à 95 °C, sont
calculées à l’aide des formules suivantes:
Première branche (c’est-à-dire partie gauche des courbes représentées à la Figure 1 et la Figure 2)
Pour le PB-H:
125010⋅lg σ 173892,7
log t =−430,866− ++290,056 9⋅log σ (1)
TT
Pour le PB-R:
104096,,6⋅lg σ 145940 231
log t =−367,8019− ++245,536⋅log σ (2)
TT
Seconde branche (c’est-à-dire partie droite des courbes représentées à la Figure 1)
Pour le PB-H:
37262,,75⋅lg σ 2 556 48
log t =−129,895− ++88,56735⋅log σ (3)
TT
Pour démontrer la conformité aux courbes de référence, il convient de soumettre à essai les échantillons
de tubes aux températures suivantes et à différentes contraintes de paroi de sorte que, pour chacune
des températures indiquées, au moins trois temps de défaillance se situent dans chacun des intervalles
de temps suivants:
— Températures 20 °C; 60 °C à 70 °C; 95 °C.
— Intervalles de temps 10 h à 100 h, 100 h à 1 000 h, 1 000 h à 8 760 h et au-dessus de 8 760 h.
Pour les essais qui durent plus de 8 760 h, une fois que la défaillance est atteinte à une contrainte et
un temps situés au moins sur ou au-dessus de la courbe de référence, n’importe quel temps ultérieur
peut être considéré comme le temps de défaillance. Il convient de réaliser les essais conformément à
l’ISO 1167-1 et l’ISO 1167-2.
Il convient de démonter la conformité aux courbes de référence en reportant les résultats expérimentaux
individuels sur le graphique. Il convient qu’au moins 97,5 % d’entre eux se situent sur ou au-dessus de la
courbe de référence.
© ISO 2017 – Tous droits réservés 3

---------------------- Page: 8 ----------------------
ISO 15876-2:2017(F)

50
40
30
20
10 ˚C
20 ˚C
30 ˚C
40 ˚C
50 ˚C
60 ˚C
70 ˚C
10
9
80 ˚C
8
90 ˚C
7
95 ˚C
6
5
4
110 ˚C
3
2
15 10 25 50 100
X2
1
1 100000 1000000
10 100 1000 10000
X1
Légende
X1 temps, t , jusqu’à la rupture, en heures
1
X2 temps, t , jusqu’à la rupt
...