ASTM D494-11(2019)
(Test Method)Standard Test Method for Acetone Extraction of Phenolic Molded or Laminated Products
Standard Test Method for Acetone Extraction of Phenolic Molded or Laminated Products
SIGNIFICANCE AND USE
4.1 For molded phenolic products, acetone extraction shall be considered solely as a quantitative expression of a property normally associated with degree of cure. There is no demonstrably rigorous relation between the optimum mechanical and electrical properties of a well-cured piece and the numerical value of the acetone test. The amount of acetone-soluble matter is affected by: (1) nature of resin and filler, (2) lubricant, (3) molding temperature, (4) length of cure, (5) thickness of the section from which sample is taken, (6) nature of molded piece, (7) technique used in molding, (8) distribution of fines in the material to be extracted, and (9) method of grinding the specimen. These variations under some conditions will cause a difference of 3 to 4 % in acetone-extractable matter. For this reason, the test method shall be used only as a comparative test for measuring undercure.
4.2 For laminated phenolic products, acetone extraction indicates change in stage of cure, change in resin content, change in type of resin used, presence of plasticizers or other acetone-extractable addition agents, and is affected in general by the same factors as stated in 6.1
SCOPE
1.1 This test method covers the determination of the amount of acetone-soluble matter in molded or laminated phenolic products.
1.2 The values stated in SI units are to be regarded as standard. The values given in parentheses are mathematical conversions to inch-pound units that are provided for information only and are not considered standard.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
Note 1: This test method is similar to ISO 308.
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
General Information
Relations
Standards Content (Sample)
This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the
Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
Designation: D494 − 11 (Reapproved 2019)
Standard Test Method for
Acetone Extraction of Phenolic Molded or Laminated
1
Products
This standard is issued under the fixed designation D494; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope content of material in the unmoulded state)
1.1 This test method covers the determination of the amount
3. Terminology
of acetone-soluble matter in molded or laminated phenolic
products.
3.1 All definitions are in accordance with Terminology
D883.
1.2 The values stated in SI units are to be regarded as
standard. The values given in parentheses are mathematical
4. Significance and Use
conversions to inch-pound units that are provided for informa-
tion only and are not considered standard.
4.1 For molded phenolic products, acetone extraction shall
1.3 This standard does not purport to address all of the
be considered solely as a quantitative expression of a property
safety concerns, if any, associated with its use. It is the
normally associated with degree of cure. There is no demon-
responsibility of the user of this standard to establish appro-
strably rigorous relation between the optimum mechanical and
priate safety, health, and environmental practices and deter-
electrical properties of a well-cured piece and the numerical
mine the applicability of regulatory limitations prior to use.
valueoftheacetonetest.Theamountofacetone-solublematter
is affected by: (1) nature of resin and filler, (2) lubricant, (3)
NOTE 1—This test method is similar to ISO 308.
molding temperature, (4) length of cure, (5) thickness of the
1.4 This international standard was developed in accor-
sectionfromwhichsampleistaken,(6)natureofmoldedpiece,
dance with internationally recognized principles on standard-
(7) technique used in molding, (8) distribution of fines in the
ization established in the Decision on Principles for the
material to be extracted, and (9) method of grinding the
Development of International Standards, Guides and Recom-
specimen. These variations under some conditions will cause a
mendations issued by the World Trade Organization Technical
difference of 3 to 4 % in acetone-extractable matter. For this
Barriers to Trade (TBT) Committee.
reason, the test method shall be used only as a comparative test
for measuring undercure.
2. Referenced Documents
2
2.1 ASTM Standards: 4.2 For laminated phenolic products, acetone extraction
D618 Practice for Conditioning Plastics for Testing
indicates change in stage of cure, change in resin content,
D883 Terminology Relating to Plastics
change in type of resin used, presence of plasticizers or other
E11 Specification for Woven Wire Test Sieve Cloth and Test
acetone-extractable addition agents, and is affected in general
Sieves
by the same factors as stated in 6.1
E691 Practice for Conducting an Interlaboratory Study to
Determine the Precision of a Test Method
5. Apparatus
2.2 ISO Standards:
5.1 Sieves—The set of sieves used shall consist of sieves
ISO 308 Plastics—Phenolic moulding materials—
Nos. 40 (425-µm) and 140 (106-µm), with a cover and
Determination of acetone-soluble matter (apparent resin
receiving pan, conforming to the requirements of Specification
E11.
1
This test method is under the jurisdiction ofASTM Committee D20 on Plastics
5.2 Extraction Apparatus—The apparatus may be of the
and is the direct responsibility of Subcommittee D20.70 on Analytical Methods.
type shown in Fig. 1, or a Wiley-Richardson type, as shown in
Current edition approved Nov. 1, 2019. Published November 2019. Originally
Fig. 2. The former type is more suitable for use with small
approved in 1946. Last previous edition approved in 2011 as D494 - 11. DOI:
10.1520/D0494-11R19.
electric hot plates, while the latter is more suitable for use with
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
oil or water baths. In either case, it shall be possible to control
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
the temperature so that the rate of extraction can be regulated
Standards volume information, refer to the standard’s Document Summary page on
the ASTM website. accurately.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1
---------------------- Page: 1 ----------------------
D494 − 11 (2019)
5.3 Drying Dishes—The drying dishes shall be lightweight