ASTM B502/B502M-10(2017)
(Specification)Standard Specification for Aluminum-Clad Steel Core Wire for Use in Overhead Electrical Aluminum Conductors
Standard Specification for Aluminum-Clad Steel Core Wire for Use in Overhead Electrical Aluminum Conductors
ABSTRACT
This specification covers round, aluminum-clad steel core wire used for mechanical reinforcement in the manufacture of aluminum conductors, aluminum-clad steel reinforced. The base metal shall be steel produced by the openhearth, electric-furnace, or basic-oxygen process and shall be of such composition that the finished clad wire shall have the properties and characteristics prescribed in this specification. The aluminum used for cladding shall have a purity and quantity sufficient to meet thickness and resistance requirements of this specification. The material shall conform to the required tensile properties such as stress, tensile strength, and elongation. The aluminum-clad steel core shall undergo elongation test, tension test, and torsion test. The elongation test shall be determined by an extensometer equipped with a vernier or other instrument reading. In the torsion test, a small tensile load shall be applied to the specimen during testing. The specimen shall be twisted by rotating one of the vises in the same direction until fracture occurs.
SCOPE
1.1 This specification covers round, aluminum-clad steel core wire with two designations of tensile strengths, AW2 (Normal Strength) and AW3 (High Strength).
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.
1.2.1 For conductor sizes designated by AWG, the requirements in SI units have been numerically converted from corresponding values stated or derived in inch-pound units. For conductor sizes designated by SI units only, the requirements are stated or derived in SI units.
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
General Information
Relations
Buy Standard
Standards Content (Sample)
NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation:B502/B502M −10 (Reapproved 2017)
Standard Specification for
Aluminum-Clad Steel Core Wire for Use in Overhead
1
Electrical Aluminum Conductors
This standard is issued under the fixed designation B502/B502M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope 3. Ordering Information
3.1 Orders for material under this specification shall include
1.1 This specification covers round, aluminum-clad steel
the following information:
core wire with two designations of tensile strengths, AW2
3.1.1 Quantity of each size,
(Normal Strength) and AW3 (High Strength).
3.1.2 Wire size: diameter in inches (see 6.1),
1.2 The values stated in either SI units or inch-pound units
3.1.3 Core Wire Strength, AW2 (Normal Strength) or AW3
are to be regarded separately as standard. The values stated in
(High Strength) (see Table 1 and Table 2),
each system may not be exact equivalents; therefore, each
3.1.4 Package size: (see 17.1),
system shall be used independently of the other. Combining
3.1.5 Special packaging and package marking if required
values from the two systems may result in non-conformance
(see 16.1), and
with the standard.
3.1.6 Place of inspection if other than place of manufacture
1.2.1 For conductor sizes designated by AWG, the require-
(see 14.1).
ments in SI units have been numerically converted from
4. Materials and Manufacture
correspondingvaluesstatedorderivedininch-poundunits.For
conductor sizes designated by SI units only, the requirements
4.1 The base metal shall be steel produced by the open-
are stated or derived in SI units.
hearth, electric-furnace, or basic-oxygen process and shall be
of such composition that the finished clad wire shall have the
1.3 This international standard was developed in accor-
properties and characteristics prescribed in this specification.
dance with internationally recognized principles on standard-
ization established in the Decision on Principles for the
4.2 The aluminum used for cladding shall have a purity and
Development of International Standards, Guides and Recom-
quantity sufficient to meet thickness and resistance require-
mendations issued by the World Trade Organization Technical
ments of this specification (see 7.1 and 9.1).
Barriers to Trade (TBT) Committee.
5. Tensile Properties
2. Referenced Documents
5.1 Requirements—The aluminum-clad steel core wire shall
conform to the tensile requirements prescribed in Table 1 and
2.1 The following documents of the issue in effect on date
Table 2. Purchasers of core intended for use in conductor
of material purchase form a part of this specification to the
constructions with annealed aluminum wires, such as ACSS/
extent referenced herein.
AW3, ACSS/TW/AW3 may request the stranded steel core be
2
2.2 ASTM Standards:
compliant only with ultimate tensile strength and may waive
B193 Test Method for Resistivity of Electrical Conductor
compliance with the 1 % extension tensile requirement. This
Materials
use of the ultimate tensile requirement as an alternate to the 1
E8 Test Methods for Tension Testing of Metallic Materials
% extension requirement shall be by agreement between the
purchaser and producer and shall be noted on product compli-
ance documentation. In computing stress at 1 % extension and
ultimate tensile strength, the actual diameter of the finished
1
This specification is under the jurisdiction of ASTM Committee B01 on
wire shall be used.
Electrical Conductors and is the direct responsibility of Subcommittee B01.06 on
Bi-Metallic Conductors.
5.2 ElongationTest—The elongation shall be determined by
Current edition approved April 1, 2017. Published April 2017. Originally
ɛ2
an extensometer suitable for measuring elongation in 10.0 in.
approved in 1970. Last previous edition approved in 2010 as B502/B502M – 10 .
DOI: 10.1520/B0502_B0502M-10R17.
[250 mm] and equipped with a vernier or other instrument
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
reading to 0.001 in. [0.025 mm]. It shall be attached to the test
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
specimen at a load equal to the initial tensile stress shown in
Standards volume information, refer to the standard’s Document Summary page on
the ASTM website. Table 3 and Table 4. At this load the extensometer shall be
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1
---------------------- Page: 1 ----------------------
B502/B502M−10 (2017)
TABLE 1 Tensile Requirements for Normal Strength (AW2) For
elongation thus determin
...
This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
´2
Designation: B502/B502M − 10 B502/B502M − 10 (Reapproved 2017)
Standard Specification for
Aluminum-Clad Steel Core Wire for Use in Overhead
1
Electrical Aluminum Conductors
This standard is issued under the fixed designation B502/B502M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1
ε NOTE—Designation was corrected editorially in October 2013.
2
ε NOTE—Editorial corrections were made in Section 9.1 in January 2016.
1. Scope
1.1 This specification covers round, aluminum-clad steel core wire with two designations of tensile strengths, AW2 (Normal
Strength) and AW3 (High Strength).
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each
system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the
two systems may result in non-conformance with the standard.
1.2.1 For conductor sizes designated by AWG, the requirements in SI units have been numerically converted from
corresponding values stated or derived in inch-pound units. For conductor sizes designated by SI units only, the requirements are
stated or derived in SI units.
1.3 This international standard was developed in accordance with internationally recognized principles on standardization
established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued
by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
2. Referenced Documents
2.1 The following documents of the issue in effect on date of material purchase form a part of this specification to the extent
referenced herein.
2
2.2 ASTM Standards:
B193 Test Method for Resistivity of Electrical Conductor Materials
E8 Test Methods for Tension Testing of Metallic Materials
3. Ordering Information
3.1 Orders for material under this specification shall include the following information:
3.1.1 Quantity of each size,
3.1.2 Wire size: diameter in inches (see 6.1),
3.1.3 Core Wire Strength, AW2 (Normal Strength) or AW3 (High Strength) (see Table 1 and Table 2),
3.1.4 Package size: (see 17.1),
3.1.5 Special packaging and package marking if required (see 16.1), and
3.1.6 Place of inspection if other than place of manufacture (see 14.1).
4. Materials and Manufacture
4.1 The base metal shall be steel produced by the open-hearth, electric-furnace, or basic-oxygen process and shall be of such
composition that the finished clad wire shall have the properties and characteristics prescribed in this specification.
1
This specification is under the jurisdiction of ASTM Committee B01 on Electrical Conductors and is the direct responsibility of Subcommittee B01.06 on Bi-Metallic
Conductors.
Current edition approved April 1, 2010April 1, 2017. Published May 2010April 2017. Originally approved in 1970. Last previous edition approved in 20072010 as
ɛ2
B502 – 02B502/B502M – 10 (2007). . DOI: 10.1520/B0502_B0502M-10E02.10.1520/B0502_B0502M-10R17.
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1
---------------------- Page: 1 ----------------------
B502/B502M − 10 (2017)
TABLE 1 Tensile Requirements for Normal Strength (AW2) For
ACSR/AW2, ACSR/TW/AW2 and ACSS/AW2, ACSR/TW/AW2 Type
Conductors
Nominal Stress at 1.0 % Ultimate Tensile Elongation,
Diameter, Extension min, Strength, min, min, %, 10 in.
in. [mm] psi (MPa) psi (MPa) [250 mm]
0.0770 to 0.1289 175 000 (1206) 195 000 (1344) 1.5
[1.956 to 3.274], incl
0.1290 to 0.1369 170 000 (1172) 190 000 (1310) 1.5
[3.275 to 3.477], incl
0.1370 to 0.1443 165 000 (1137) 185 000 (1275) 1.5
[3.478 to 3.665], incl
0.1444 to 0.1549 160 000 (1103) 180 000 (1241) 1.5
[3.666 to 3.934], incl
0.1550 to 0.1620 160 000 (1103) 175 000 (1206) 1.5
[3.935 to 4.115], incl
0.1621 to 0.1729 155 000 (1068) 170 000 (1172) 1.5
[4.116 to 4.392], incl
0.1730 to 0.1819 150 000 (1034) 165 000 (1137) 1.5
[4.393 to 4.620], incl
0.1820 to 0.1880 145 000 (1000) 160 000 (1103) 1.5
[4.621 to 4.775], incl
TABLE 2
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.