Standard Specification for Self-Adhering Polymer Modified Bituminous Sheet Materials Used as Steep Roofing Underlayment for Ice Dam Protection

ABSTRACT
This specification covers the standards for polymer modified bituminous sheet materials proposed for use as underlayment on roof eaves, or valleys, or both, to prevent leakage of shingle, tile or metal roofs from water back-up due to ice dams. The underlayment sheet shall comply with the physical requirements which include thickness, maximum load, elongation, adhesion to plywood, thermal stability, flexibility, tear resistance, moisture vapor permeance, sealability, and slip resistance. The underlayment sheet shall not crack, as well, nor be too sticky as to cause damage upon being unrolled.
SCOPE
1.1 This specification covers polymer modified bituminous sheet materials intended for use as underlayment on roof eaves, or valleys, or both, to prevent leakage of shingle, tile, or metal roofs from water back-up due to ice dams.  
1.2 These underlayment sheets have a sticky adhesive layer which is exposed by removal of a protective sheet. The top surface is suitable to work on during the application of the exposed roofing.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

General Information

Status
Historical
Publication Date
31-Oct-2016
Current Stage
Ref Project

Relations

Buy Standard

Technical specification
ASTM D1970/D1970M-16 - Standard Specification for Self-Adhering Polymer Modified Bituminous Sheet Materials Used as Steep Roofing Underlayment for Ice Dam Protection
English language
6 pages
sale 15% off
Preview
sale 15% off
Preview
Technical specification
REDLINE ASTM D1970/D1970M-16 - Standard Specification for Self-Adhering Polymer Modified Bituminous Sheet Materials Used as Steep Roofing Underlayment for Ice Dam Protection
English language
6 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation:D1970/D1970M −16
Standard Specification for
Self-Adhering Polymer Modified Bituminous Sheet Materials
Used as Steep Roofing Underlayment for Ice Dam
1
Protection
This standard is issued under the fixed designation D1970/D1970M; the number immediately following the designation indicates the
year of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last
reapproval. A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope Nonrigid Thermoplastic Sheeting or Film at Elevated
Temperature
1.1 This specification covers polymer modified bituminous
D2523Practice for Testing Load-Strain Properties of Roof-
sheetmaterialsintendedforuseasunderlaymentonroofeaves,
ing Membranes
or valleys, or both, to prevent leakage of shingle, tile, or metal
D4073TestMethodforTensile-TearStrengthofBituminous
roofs from water back-up due to ice dams.
Roofing Membranes
1.2 These underlayment sheets have a sticky adhesive layer
D5147/D5147MTest Methods for Sampling and Testing
which is exposed by removal of a protective sheet. The top
Modified Bituminous Sheet Material
surface is suitable to work on during the application of the
D7349/D7349MTest Method for Determining the Capabil-
exposed roofing.
ityofRoofingandWaterproofingMaterialstoSealaround
1.3 The values stated in either SI units or inch-pound units Fasteners
E96/E96MTest Methods for Water Vapor Transmission of
are to be regarded separately as standard. The values stated in
each system may not be exact equivalents; therefore, each Materials
system shall be used independently of the other. Combining
3. Terminology
values from the two systems may result in non-conformance
3.1 Definitions—For definitions of terms used in this
with the standard.
specification, refer to Terminology D1079.
1.4 This standard does not purport to address all of the
safety concerns, if any, associated with its use. It is the 3.2 Definitions of Terms Specific to This Standard:
responsibility of the user of this standard to establish appro-
3.2.1 lot—for the purpose of sampling, a lot shall consist of
priate safety and health practices and determine the applica-
all material manufactured in one production run (not to exceed
bility of regulatory limitations prior to use.
24 h) using the same source of raw materials.
4. Workmanship, Finish, and Appearance
2. Referenced Documents
2
4.1 The underlayment sheet shall be supplied in roll form.
2.1 ASTM Standards:
D228/D228MTest Methods for Sampling, Testing, and
4.2 The underlayment sheet shall be substantially uniform
Analysis of Asphalt Roll Roofing, Cap Sheets, and
in thickness and appearance. It shall be free of visible defects
Shingles Used in Roofing and Waterproofing
such as holes, ragged or untrue edges, breaks, cracks, tears,
D903Test Method for Peel or Stripping Strength of Adhe-
protuberances, and indentations, except for those perforations
sive Bonds
or protuberances which are intentional.
D1079Terminology Relating to Roofing and Waterproofing
4.3 Thesurfaceoftheunderlaymentsheetshallbedesigned
D1204Test Method for Linear Dimensional Changes of
to provide traction and slip resistance to the applicator.
NOTE 1—The intent of 4.3 is to recognize that surface slipperiness is
1 important when working on a roof and, while no test method is specified
This specification is under the jurisdiction of ASTM Committee D08 on
in this standard, several methods for assessing the relative slipperiness of
RoofingandWaterproofingandisthedirectresponsibilityofSubcommitteeD08.02
surfaces are available. It is the further intent of this paragraph to ensure
on Steep Roofing Products and Assemblies.
Current edition approved Nov. 1, 2016. Published November 2016. Originally that, whatever method is used, the friction coefficient or resistance to
approvedin1990.Lastpreviouseditionapprovedin2015asD1970/D1970M–15a. slipping of the surface of these products should be at least as great as
DOI: 10.1520/D1970_D1970M-16.
asphalt-saturated felt shingle underlayment tested under the same condi-
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
tions of temperature and wetness as agreed between purchaser and seller.
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
4.4 Sheet sections shall be suitable for joining by the
Standards volume information, refer to the standard’s Document Summary page on
the ASTM website. manufacturer’s recommended procedure. The entire lower
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
D1970/D1970M−16
surface of the underlayment sheet shall be capable of being 7.3.2.1 Condition each specimen at least2hat23 6 2°C
fully adhered t
...

This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation: D1970/D1970M − 15a D1970/D1970M − 16
Standard Specification for
Self-Adhering Polymer Modified Bituminous Sheet Materials
Used as Steep Roofing Underlayment for Ice Dam
1
Protection
This standard is issued under the fixed designation D1970/D1970M; the number immediately following the designation indicates the
year of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last
reapproval. A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope
1.1 This specification covers polymer modified bituminous sheet materials intended for use as underlayment on roof eaves, or
valleys, or both, to prevent leakage of shingle, tile, or metal roofs from water back-up due to ice dams.
1.2 These underlayment sheets have a sticky adhesive layer which is exposed by removal of a protective sheet. The top surface
is suitable to work on during the application of the exposed roofing.
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each
system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the
two systems may result in non-conformance with the standard.
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility
of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory
limitations prior to use.
2. Referenced Documents
2
2.1 ASTM Standards:
D228D228/D228M Test Methods for Sampling, Testing, and Analysis of Asphalt Roll Roofing, Cap Sheets, and Shingles Used
in Roofing and Waterproofing
D903 Test Method for Peel or Stripping Strength of Adhesive Bonds
D1079 Terminology Relating to Roofing and Waterproofing
D1204 Test Method for Linear Dimensional Changes of Nonrigid Thermoplastic Sheeting or Film at Elevated Temperature
D2523 Practice for Testing Load-Strain Properties of Roofing Membranes
D4073 Test Method for Tensile-Tear Strength of Bituminous Roofing Membranes
D5147D5147/D5147M Test Methods for Sampling and Testing Modified Bituminous Sheet Material
D7349D7349/D7349M Test Method for Determining the Capability of Roofing and Waterproofing Materials to Seal around
Fasteners
E96/E96M Test Methods for Water Vapor Transmission of Materials
3. Terminology
3.1 Definitions—For definitions of terms used in this specification, refer to Terminology D1079.
3.2 Definitions of Terms Specific to This Standard:
3.2.1 lot—for the purpose of sampling, a lot shall consist of all material manufactured in one production run (not to exceed 24
h) using the same source of raw materials.
4. Workmanship, Finish, and Appearance
4.1 The underlayment sheet shall be supplied in roll form.
1
This specification is under the jurisdiction of ASTM Committee D08 on Roofing and Waterproofing and is the direct responsibility of Subcommittee D08.02 on Steep
Roofing Products and Assemblies.
Current edition approved June 15, 2015Nov. 1, 2016. Published July 2015November 2016. Originally approved in 1990. Last previous edition approved in 2015 as
D1970/D1970M – 15.D1970/D1970M – 15a. DOI: 10.1520/D1970_D1970M-15A.10.1520/D1970_D1970M-16.
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
D1970/D1970M − 16
4.2 The underlayment sheet shall be substantially uniform in thickness and appearance. It shall be free of visible defects such
as holes, ragged or untrue edges, breaks, cracks, tears, protuberances, and indentations, except for those perforations or
protuberances which are intentional.
4.3 The surface of the underlayment sheet shall be designed to provide traction and slip resistance to the applicator.
NOTE 1—The intent of 4.3 is to recognize that surface slipperiness is important when working on a roof and, while no test method is specified in this
standard, several methods for assessing the relative slipperiness of surfaces are available. It is the further intent of this paragraph to ensure that, whatever
method is used, the friction coefficient or resistance to slipping of the surface of
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.