ASTM A542/A542M-09
(Specification)Standard Specification for Pressure Vessel Plates, Alloy Steel, Quenched-and-Tempered, Chromium-Molybdenum, and Chromium-Molybdenum-Vanadium
Standard Specification for Pressure Vessel Plates, Alloy Steel, Quenched-and-Tempered, Chromium-Molybdenum, and Chromium-Molybdenum-Vanadium
ABSTRACT
This specification covers pressure vessel plates, alloy steel, quenched-and-tempered, chromium-molybdenum, and chromium-molybdenum-vanadium. As a steel making practice, the steel shall be killed and shall conform to specified fine austenitic grain size requirements. Plate types A, B, C, D, and E shall be heat treated by heating to a suitable austenitizing temperature, holding for a sufficient period of time to attain uniform temperature throughout the thickness, and quenching in a suitable liquid medium by spraying or immersion. The steel shall conform to the required chemical compositions. The required mechanical properties that include tension test requirements and notch toughness requirements are presented in details.
SCOPE
1.1 This specification covers two types of 2¼ Cr-1 Mo and three types of Cr-Mo-V alloy steel plates for use in the quenched-and-tempered condition, intended for the fabrication of welded pressure vessels and components.
1.2 Material under this specification is available in five types, designated “A,” “B,” “C,” “D,” and “E.” Type B is identical to Type A except for restrictive limits for carbon, phosphorus, sulfur, and nickel. The material is also available in five classes having the following strength levels. Type E is available only as Class 4 and 4a.
ClassMinimum Tensile Strength, ksi [MPa] 1 105 [725] 2 115 [795] 3 95 [655] 4 and 4a 85 [585]
1.3 The maximum thickness of plates is limited only by the capacity of the chemical composition to meet the specified mechanical property requirements.
1.4 The minimum thickness of plates is limited to 3/16 in. [5 mm].
1.5 The material is intended to be suitable for fusion welding. Welding technique is of fundamental importance and it is presupposed that welding procedures will be in accordance with approved methods.
1.6 These alloy steel plates in the as-rolled condition are sensitive to cracking during flame cutting, transit, and handling. They should be shipped in the as-rolled condition only with the mutual agreement of the manufacturer and the purchaser or fabricator.
1.7 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents, therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with this specification.
General Information
Relations
Buy Standard
Standards Content (Sample)
NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation:A542/A542M −09
StandardSpecification for
Pressure Vessel Plates, Alloy Steel, Quenched-and-
Tempered, Chromium-Molybdenum, and Chromium-
1
Molybdenum-Vanadium
This standard is issued under the fixed designationA542/A542M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision.Anumber in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope* SI units are shown in brackets. The values stated in each
2 system are not exact equivalents, therefore, each system must
1
1.1 Thisspecification coverstwotypesof2 ⁄4 Cr-1Moand
beusedindependentlyoftheother.Combiningvaluesfromthe
three types of Cr-Mo-V alloy steel plates for use in the
two systems may result in nonconformance with this specifi-
quenched-and-tempered condition, intended for the fabrication
cation.
of welded pressure vessels and components.
2. Referenced Documents
1.2 Material under this specification is available in five
3
types, designated “A,” “B,” “C,” “D,” and “E.” Type B is
2.1 ASTM Standards:
identical to Type A except for restrictive limits for carbon,
A20/A20MSpecificationforGeneralRequirementsforSteel
phosphorus,sulfur,andnickel.Thematerialisalsoavailablein
Plates for Pressure Vessels
five classes having the following strength levels. Type E is
A370Test Methods and Definitions for Mechanical Testing
available only as Class 4 and 4a.
of Steel Products
A387/A387MSpecificationforPressureVesselPlates,Alloy
Class Minimum Tensile Strength, ksi [MPa]
1 105 [725]
Steel, Chromium-Molybdenum
2 115 [795]
A435/A435MSpecification for Straight-Beam Ultrasonic
3 95 [655]
4 and 4a 85 [585] Examination of Steel Plates
A577/A577MSpecification for Ultrasonic Angle-Beam Ex-
1.3 The maximum thickness of plates is limited only by the
amination of Steel Plates
capacity of the chemical composition to meet the specified
A578/A578MSpecification for Straight-Beam Ultrasonic
mechanical property requirements.
Examination of Rolled Steel Plates for Special Applica-
3
1.4 The minimum thickness of plates is limited to ⁄16 in. [5
tions
mm].
3. General Requirements and Ordering Information
1.5 The material is intended to be suitable for fusion
3.1 Material supplied to this material specification shall
welding. Welding technique is of fundamental importance and
conform to Specification A20/A20M. These requirements out-
itispresupposedthatweldingprocedureswillbeinaccordance
line the testing and retesting methods and procedures, permit-
with approved methods.
ted variations in dimensions, and mass, quality and repair of
1.6 These alloy steel plates in the as-rolled condition are
defects, marking, loading, and ordering information.
sensitive to cracking during flame cutting, transit, and han-
3.2 In addition to the basic requirements of this
dling. They should be shipped in the as-rolled condition only
specification,certainsupplementaryrequirementsareavailable
with the mutual agreement of the manufacturer and the
when additional control, testing, or examination is required to
purchaser or fabricator.
meet end use requirements. The purchaser is referred to the
1.7 The values stated in either inch-pound units or SI units
listed supplementary requirements in this specification and to
are to be regarded separately as standard. Within the text, the
the detailed requirements in Specification A20/A20M.
3.3 If the requirements of this specification are in conflict
1
This specification is under the jurisdiction ofASTM Committee A01 on Steel,
withtherequirementsofSpecificationA20/A20M,therequire-
Stainless Steel and RelatedAlloys and is the direct responsibility of Subcommittee
ments of this specification shall prevail.
A01.11 on Steel Plates for Boilers and Pressure Vessels.
Current edition approved Oct. 1, 2009. Published October 2009. Originally
3
approved in 1965. Last previous edition approved in 2004 as A542/ For referenced ASTM standards, visit the ASTM website, www.astm.org, or
´1
A542M–99(2004) . DOI: 10.1520/A0542_A0542M-09. contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
2
For ASME Boiler and Pressure Vessel Code applications, see related Specifi- Standards volume information, refer to the standard’s Document Summary page on
cation SA-542 in Section II of that Code. the ASTM website.
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1
---------------------- Page: 1 ----------------------
A542/A542M−09
TABLE 1 Chemical Requirements
NOTE 1—Where “.” appears there is no requirement.
Composition, %
Element
Type A Type B Type C Type D Type E
Carbon:
Heat analysis 0.15 max 0.11–0.15 0.10–0.15 0
...
This document is not anASTM standard and is intended only to provide the user of anASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
´1
Designation:A542/A542M–99 (Reapproved 2004) Designation: A542/A542M – 09
Standard Specification for
Pressure Vessel Plates, Alloy Steel, Quenched-and-
Tempered, Chromium-Molybdenum, and Chromium-
1
Molybdenum-Vanadium
This standard is issued under the fixed designationA542/A542M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision.Anumber in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1
´ NOTE—Supplementary Requirement S14, Bend Test, was editorially removed in September 2004.
1. Scope*
2
1
1.1 This specification covers two types of 2 ⁄4 Cr-1 Mo and three types of Cr-Mo-V alloy steel plates for use in the
quenched-and-tempered condition, intended for the fabrication of welded pressure vessels and components.
1.2 Material under this specification is available in five types, designated “A,” “B,” “C,” “D,” and “E.” Type B is identical to
TypeAexcept for restrictive limits for carbon, phosphorus, sulfur, and nickel.The material is also available in five classes having
the following strength levels. Type E is available only as Class 4 and 4a.
Class Minimum Tensile Strength, ksi [MPa]
1 105 [725]
2 115 [795]
3 95 [655]
4 and 4a 85 [585]
1.3 The maximum thickness of plates is limited only by the capacity of the chemical composition to meet the specified
mechanical property requirements.
3
1.4 The minimum thickness of plates is limited to ⁄16 in. [5 mm].
1.5 The material is intended to be suitable for fusion welding. Welding technique is of fundamental importance and it is
presupposed that welding procedures will be in accordance with approved methods.
1.6The values stated in either inch-pound units or SI units are to be regarded separately as standard.Within the text, the SI units
are shown in brackets. The values stated in each system are not exact equivalents, therefore, each system must be used
independently of the other. Combining values from the two systems may result in nonconformance with this specification.
1.6 These alloy steel plates in the as-rolled condition are sensitive to cracking during flame cutting, transit, and handling. They
should be shipped in the as-rolled condition only with the mutual agreement of the manufacturer and the purchaser or fabricator.
1.7 Thevaluesstatedineitherinch-poundunitsorSIunitsaretoberegardedseparatelyasstandard.Withinthetext,theSIunits
are shown in brackets. The values stated in each system are not exact equivalents, therefore, each system must be used
independently of the other. Combining values from the two systems may result in nonconformance with this specification.
2. Referenced Documents
3
2.1 ASTM Standards:
A20/A20M Specification for General Requirements for Steel Plates for Pressure Vessels
A370 Test Methods and Definitions for Mechanical Testing of Steel Products
A387/A387M Specification for Pressure Vessel Plates, Alloy Steel, Chromium-Molybdenum
A435/A435M Specification for Straight-Beam Ultrasonic Examination of Steel Plates
A577/A577M Specification for Ultrasonic Angle-Beam Examination of Steel Plates
A578/A578M Specification for Straight-Beam Ultrasonic Examination of Rolled Steel Plates for Special Applications
1
ThisspecificationisunderthejurisdictionofASTMCommitteeA01onSteel,StainlessSteelandRelatedAlloysandisthedirectresponsibilityofSubcommitteeA01.11
on Steel Plates for Boilers and Pressure Vessels.
Current edition approved Sept.Oct. 1, 2004.2009. Published September 2004.October 2009. Originally approved in 1965. Last previous edition approved in 19992004 as
´1
A542/A542M–99(2004) . DOI: 10.1520/A0542_A0542M-99R04E01. DOI: 10.1520/A0542_A0542M-09.
2
For ASME Boiler and Pressure Vessel Code applications, see related Specification SA-542 in Section II of that Code.
3
ForreferencedASTMstandards,visittheASTMwebsite,www.astm.org,orcontactASTMCustomerServiceatservice@astm.org.ForAnnualBookofASTMStandards
volume information, refer to the standard’s Document Summary page on the ASTM website.
*ASummary of Changes section appears at the end of this standard.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
1
---------------------- Page: 1 ----------------------
A542/A542M – 09
3. General Requirements and Ordering Information
3.1 Material supplied to this material specification shall conform to Specification A20/A20M. These requirements outline the
testing and retesting methods and
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.