Standard Test Method for Gel Time of Thermosetting Coating Powder

Standard Test Method for Gel Time of Thermosetting Coating Powder

SIGNIFICANCE AND USE
4.1 This test method is useful for selecting coating powders that gel in the desired time at the specified temperature. The method is not useful for determination of cure time.
SCOPE
1.1 This test method determines the length of time a thermosetting coating powder takes to gel on a polished metal surface at a specified temperature, such as 204°C (400°F). The determination of the gel time is a very simple method for the characterization and quality control of coating powders. However, the gel time determined by this method is not directly related to the time for the coating powder to cure in practical applications.  
1.2 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

General Information

Status
Published
Publication Date
31-May-2017
ICS
83.080.10 - Thermosetting materials
Technical Committee
D01 - Paint and Related Coatings, Materials, and Applications
Drafting Committee
D01.51 - Powder Coatings
Current Stage
Ref Project

Relations

Replaces
ASTM D4217-07(2013) - Standard Test Method for Gel Time of Thermosetting Coating Powder
Effective Date
01-Jun-2017
Referred By
ASTM D3451-06(2017) - Standard Guide for Testing Coating Powders and Powder Coatings
Effective Date
01-Jun-2017
Referred By
ASTM D4242-07(2017) - Standard Test Method for Inclined Plate Flow for Thermosetting Coating Powders
Effective Date
01-Jun-2017

Buy Standard

ASTM D4217-07(2017) - Standard Test Method for Gel Time of Thermosetting Coating PowderASTM D4217-07(2017) - Standard Test Method for Gel Time of Thermosetting Coating Powder
PreviousNext
Standard
ASTM D4217-07(2017) - Standard Test Method for Gel Time of Thermosetting Coating Powder
English language
2 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)


This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the
Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
Designation: D4217 − 07 (Reapproved 2017)
Standard Test Method for
Gel Time of Thermosetting Coating Powder
This standard is issued under the fixed designation D4217; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope 3.1.2 cure time of a coating powder—the time required for
a thermosetting coating powder to sufficiently chemically
1.1 This test method determines the length of time a
crosslink at a given temperature to provide the required coating
thermosetting coating powder takes to gel on a polished metal
properties.
surface at a specified temperature, such as 204°C (400°F). The
3.1.3 gel time of a coating powder—the interval required at
determination of the gel time is a very simple method for the
a given temperature for a coating powder to be transformed
characterization and quality control of coating powders.
from a dry solid to a gel-like state.
However, the gel time determined by this method is not
directly related to the time for the coating powder to cure in
3.1.4 powder coating, n—coatings which are protective or
practical applications.
decorative, or both, formed by the application of a coating
powder to a substrate and fused in a continuous film by the
1.2 This standard does not purport to address all of the
application of heat or radiant energy.
safety concerns, if any, associated with its use. It is the
responsibility of the user of this standard to establish appro-
3.1.5 thermosetting, adj—describing a material that, when
priate safety and health practices and determine the applica-
heated per a minimum recommended cure condition, under-
bility of regulatory limitations prior to use.
goes a chemical reaction and a permanent change to a more
1.3 This international standard was developed in accor-
durable state capable of specific properties as designed for
dance with internationally recognized principles on standard-
substrate protection or decoration, or both.
ization established in the Decision on Principles for the
Development of International Standards, Guides and Recom- 4. Significance and Use
mendations issued by the World Trade Organization Technical
4.1 This test method is useful for selecting coating powders
Barriers to Trade (TBT) Committee.
that gel in the desired time at the specified temperature. The
method is not useful for determination of cure time.
2. Referenced Documents
5. Apparatus
2.1 ISO Standards:
5.1 Hot Plate, having an electrically heated metal block
ISO 8130–6:1992 Coating powders—Part 6: Determination
with a polished surface capable of being maintained at tem-
of gel time of thermosetting coating powders at a given
peratures between range 130 to 230°C (266 to 466°F) to within
temperature
62°C (64°F). The temperature should be controlled by means
of a thermoregulator.
3. Terminology
3.1 Definitions: NOTE 1—There are expected differences in results between this method
and ISO 8130–6 which requires a heating block with small depressions.
3.1.1 coating powder, n—finely divided particles of resin,
either thermoplastic or thermosetting, generally incorporating
5.2 Stopwatch or Timer, accurate to at least 1 s.
pigments, fillers, and additives and remaining finely divided
5.3 Stirrer, of very low heat capacity and of suitable size.
during storage under suitable conditions, which, after fusing
Woodenstirrerswithdimensionsof2mmby6mmby130mm
and possibly curing, give a continuous film.
1 1
or ( ⁄16 in. by ⁄4 in. by 5 in.) have been found suitable.
5.4 Surface Contact Thermocouple, suitable for use at 150
to 250°C (300 to 480°F) and reading no greater than 1°C (2°F).
This test method is under the jurisdiction of ASTM Committee D01 on Paint
and Related Coatings, Materials, andApplications and is the direct responsibility of
Subcommittee D01.51 on Powder Coatings.
Current edition approved June 1, 2017. Published June 2017. Originally The sole source of supply of the Model SS-200 hot plate known to the
approved in 1982. Last previous edition approved in 2013 as D4217 – 07 (2013). committee at this time is Thermo-Electric Co., 455 Route 30, Imperial, PA 15126.
DOI: 10.1520/D4217-07R17. If you are aware of alternative suppliers, please provide this information to ASTM
Available from American National Standards Institute (ANSI), 25 W. 43rd St., International Headquarters. Your comments will receive careful consideration at a
4th Floor, New York, NY 10036, http://www.ansi.org. meeting of the responsible technical committee, which you may attend
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

ASTM
ASTM D6902-04(2023)(Test Method)
Standard Test Method for Laboratory Measurement of Formaldehyde Evolved During the Curing of Melamine-Formaldehyde-Based Coatings

SIGNIFICANCE AND USE
5.1 This test method measures the amount of formaldehyde that is evolved from a coating containing melamine-formaldehyde resin(s) during cure at elevated temperature. Cure formaldehyde results from a side-reaction during cross-linking of functionalized polymers with melamine-formaldehyde resins. Cure formaldehyde is evolved in the final bake or cure oven, when the coating temperature is high enough to initiate cross-linking. Formaldehyde can be released from a coating during application, solvent flash-off and cure. Free formaldehyde is primarily evolved during coating application and solvent flash-off. Test Method D1979 measures “free formaldehyde” in amino resins and Test Method D6191 measures formaldehyde evolved from coatings at ambient temperature. This method measures only the formaldehyde released during heat cure, which is primarily “cure formaldehyde.”  
5.2 This test method is not intended to duplicate the evolved formaldehyde from an industrial process, but serves as a reproducible comparative laboratory evaluation.  
5.3 This test method has not been evaluated with catalyzed coating systems that cure at or below 40 °C, such as those used by the wood-finishing industry, and would likely require special adaptation for this application.
SCOPE
1.1 This test method is for the determination of formaldehyde evolved from melamine-formaldehyde-based coatings during the cure step. The results may be used to determine the “cure formaldehyde” evolved from a sample under controlled laboratory conditions.  
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.3 This test method is capable of measuring from 500 μg/g to 22 000 μg formaldehyde/g dry coating under the test conditions specified (3 000 ml/min total flow, 50 ml/min DNPH tube flow). The ratio of total flow to DNPH tube flow could be adjusted to extend the range of the method.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    7 pages
    English language
    sale 15% off
ASTM
ASTM D4640-86(2022)(Test Method)
Standard Test Method for Determining Stroke Cure Time of Thermosetting Phenol-Formaldehyde Resins

SIGNIFICANCE AND USE
4.1 This method is significant as a process control for polymerization time.  
4.2 When the cure times are determined at several temperatures and plotted as time versus temperature, different resins can be compared for curing characteristics.
SCOPE
1.1 This test method covers the determination of the cure rate at any specified temperature for a thermosetting phenol-formaldehyde resin. The time at that temperature required to make a fluid mixture change into a hard immovable mass indicates speed of cure.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    2 pages
    English language
    sale 15% off
ASTM
ASTM D4142-89(2022)(Guide)
Standard Guide for Testing Epoxy Resins

SIGNIFICANCE AND USE
3.1 This guide directs the user to test methods that determine properties generally accepted as standard test items for classification of epoxy resins.
SCOPE
1.1 This guide covers methods for testing epoxy resins as listed in Table 1. All of the methods were tested by interlaboratory participation in accordance with usual ASTM guidelines. Each method specifies a recommended amount of sample for starting a separate analysis, but several of the procedures can be conducted on the same starting material if so desired. For example, viscosity, color, and density could be run on the same specimen.  
1.2 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Guide
    2 pages
    English language
    sale 15% off
ASTM
ASTM D5165-12(2020)(Practice)
Standard Practice for Laboratory Preparation of Gelled Vehicles Using a Resin Kettle

SIGNIFICANCE AND USE
5.1 This practice provides a means of preparing gel vehicles in laboratory equipment that most closely resembles production reactors. It can be used to predict the performance of gel vehicle components (resins, gellants, alkyds, etc.) in the user's equipment.  
5.2 An ample amount of gel vehicle can be prepared for use in preparing inks for press testing.
SCOPE
1.1 This practice covers a laboratory procedure for the gelation of a resin solution, ink varnish, or vehicle using a resin kettle.  
1.2 Guidance in preparing gelled vehicle samples suitable for use in laboratory sample quantity oil-based printing inks is provided.  
1.3 The procedure outlined is not intended as a means of rating or evaluating resin or vehicle gelability, and is applicable only if the solutions, varnishes, or vehicles produced are of a rheology that is measurable by conventional ink and varnish industry viscometers or rheometers.  
1.4 The values stated in SI units of measurement are to be regarded as the standard. The values given in parentheses are for information only.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    3 pages
    English language
    sale 15% off
ASTM
ASTM D4301-05(2019)(Test Method)
Standard Test Method for Total Chlorine in Epoxy Resins and Compounds

SIGNIFICANCE AND USE
5.1 The presence of residual chlorine in epoxy resins is deleterious to final product properties. This test method has been found to be applicable to resins or ethers with chlorine contents ranging from 50 ppm to 35 % by weight. Other halogen compounds react with the reagent but are distinguished from chlorine by the final potentiometric titration. Epoxy and other functional groups will consume reagent but do not affect the results.
SCOPE
1.1 This test method describes a procedure for the determination of total chlorine in epoxy resins and glycidyl ethers.  
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. For specific hazard statements, see Section 8.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    2 pages
    English language
    sale 15% off
ASTM
ASTM D1726-11(2019)(Test Method)
Standard Test Methods for Hydrolyzable Chloride Content of Liquid Epoxy Resins

SIGNIFICANCE AND USE
5.1 The hydrolyzable chloride content of liquid epoxy resins is an important variable in determining their reactivity and the properties of coatings made from them. These test methods may be used to determine the hydrolyzable chloride content of manufactured epoxy resins and confirm the stated hydrolyzable chloride content of purchased epoxy resins.
SCOPE
1.1 These test methods cover the determination of the easily hydrolyzable chloride content of liquid epoxy resins which are defined as the reaction product of a chlorohydrin and a di- or polyfunctional phenolic compound.
Note 1: There is no known ISO equivalent to this standard.  
1.1.1 In Test Method A, the easily hydrolyzable chloride is saponified with potassium hydroxide and directly titrated with hydrochloric acid. This test method can be used for concentrations of 1 weight % and below.  
1.1.2 In Test Method B, the easily hydrolyzable chloride is again saponified with potassium hydroxide, then titrated potentiometrically with silver nitrate. This test method can be used for concentrations of 5 to 2500 ppm hydrolyzable chloride.  
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. For specific hazard statements see Sections 10 and 16.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    4 pages
    English language
    sale 15% off
ASTM
ASTM D1652-11(2019)(Test Method)
Standard Test Method for Epoxy Content of Epoxy Resins

SIGNIFICANCE AND USE
4.1 The epoxy content of epoxy resins is an important variable in determining their reactivity and the properties of coatings made from them. These test methods may be used to determine the epoxy content of manufactured epoxy resins and confirm the stated epoxy content of purchased epoxy resins.
SCOPE
1.1 This test method covers the procedure for manual and automatic titration of epoxy resins for the quantitative determination of the percent epoxide content from 0.1 to 26 % epoxide.  
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. For specific hazard statements, see Section 6.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    4 pages
    English language
    sale 15% off
ASTM
ASTM D1259-06(2018)(Test Method)
Standard Test Methods for Nonvolatile Content of Resin Solutions

SIGNIFICANCE AND USE
3.1 The nonvolatile content of resin solutions is useful to coatings producers and users for the determination of the total solids available for film formation and for the estimation of the volatile organic content.
SCOPE
1.1 These test methods cover the determination of nonvolatile content of solutions of resins in volatile organic solvents.  
1.2 Two test methods are included as follows:  
1.2.1 Test Method A—For solutions of non-heat-reactive resins. These solutions contain resins that remain stable and release the solvent under conditions of the test. Examples are ester gums and alkyds.  
1.2.2 Test Method B—For two types of solutions:
1.2.2.1 Solutions of heat-reactive resins. These solutions contain resins that undergo condensation or other reactions under the influence of heat. Examples include the formaldehyde reaction products of urea, melamine, and phenols.
1.2.2.2 Solutions that release solvent slowly. Examples include epoxy resin solutions.  
1.3 Test Methods A and B differ primarily in the drying times and types of oven used.  
1.4 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    4 pages
    English language
    sale 15% off
ASTM
ASTM D4242-07(2017)(Test Method)
Standard Test Method for Inclined Plate Flow for Thermosetting Coating Powders

SIGNIFICANCE AND USE
5.1 This test method is useful for selecting coating powders of similar characteristics of melt flow under minimal shear. It is not recommended as an absolute measurement, but rather as a comparative measurement of samples on the same panel measured at the same time.
SCOPE
1.1 This test method specifies a method for determining the flow characteristics of a fused thermosetting coating powder down a plane inclined at a set angle to the horizontal. The test gives an indication of the degree of melt flow that may occur during the curing of the coating powder. This characteristic contributes to the coherence of the coating, to its surface appearance and to the degree of coverage over sharp edges (see Test Method D2967), however, it should not be used as the sole factor for judgment. The test acts as a useful method for checking for batch to batch variation in the behavior of a given coating powder. Correlation between the results from coating powders of differing composition is not to be expected. This method is unlikely to yield meaningful results with coating powders which have gel times of less than one minute at the test temperature (see Test Method D4217). Oven drafts, angle of inclination and pellet variations significantly affect results making inter-lab reproducibility somewhat difficult to correlate.  
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and to determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    3 pages
    English language
    sale 15% off
ASTM
ASTM D7487-24(Practice)
Standard Practice for Polyurethane Raw Materials: Polyurethane Foam Cup Test

SIGNIFICANCE AND USE
5.1 General Utility:  
5.1.1 It is useful to verify catalyst levels in a resin blend or a polyurethane system.  
5.1.2 This practice is suitable for research, quality control, specification testing, and process control.  
5.2 Limitations:  
5.2.1 Several of the measured parameters are subjective. Therefore, operator-to-operator variability and lab-to-lab variability can be much higher than that of a single operator.  
5.2.2 The variability of this practice is dependent on the consistency of mixing of the reactants.  
5.2.3 The estimation of precision in this practice is based on typical formulations for rigid and flexible foams. Formulations with faster reaction times will likely have greater variability, particularly cream time (initiation time). Formulations with slower reaction times will likely have greater variability in the measurement of free rise time.  
5.2.4 It is possible that low-level (ppm, ppb) ingredient contamination will not be detectable using this practice. Confirmation of such contamination will potentially require large-scale (~20 L) tests and is out of the scope of this practice.
SCOPE
1.1 This practice covers the determination of cream time (initiation time), top of cup time, free rise time, free rise height, string gel time (pull time), tack free time, settle back, and free rise density of polyurethane foam formulations using a cup foam test.  
1.2 Typical definitions, terms, and techniques are described; including procedures for mixing and transferring samples to the foaming container; and data gathering and evaluation. However, agreement between the customer and the testing laboratory for all these items must be obtained prior to use.  
1.3 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
Note 1: There is no known ISO equivalent to this standard.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    5 pages
    English language
    sale 15% off
  • Standard
    5 pages
    English language
    sale 15% off