CR 13933:2000
(Main)Masonry cement - Testing for workability (cohesivity)
Masonry cement - Testing for workability (cohesivity)
The adaption of existing test methods and equipment to provide a repeatable and reproducible means of assessing the workability ("cohesivity") imparted to mortar by masonry cements.
Zidarski cement - Preskušanje obdelavnosti (kohezivnost)
General Information
Relations
Standards Content (Sample)
SLOVENSKI STANDARD
01-februar-2001
Zidarski cement - Preskušanje obdelavnosti (kohezivnost)
Masonry cement - Testing for workability (cohesivity)
Ta slovenski standard je istoveten z: CR 13933:2000
ICS:
91.100.10 Cement. Mavec. Apno. Malta Cement. Gypsum. Lime.
Mortar
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.
---------------------
...
This May Also Interest You
This document specifies two equivalent test methods to assess the chemical reactivity of a pozzolanic or latent hydraulic cement constituent or concrete addition by measurements of heat of hydration (see Clause 5 and 8.3 Method A, Heat of Hydration) or bound water content (see Clause 5 and 8.4 Method B, Bound Water Content) of hydrated pastes composed of the cement constituent or concrete addition, calcium hydroxide, calcium carbonate, potassium sulfate, and potassium hydroxide cured at 40 °C for 72 h and 168 h (3 days and 7 days).
These two test methods measure chemical reactivity of test specimens intended for use as cementitious materials, such as cement constituents and concrete additions. The test methods do not distinguish between latent hydraulic and pozzolanic reactivity.
The test methods are used for qualification purposes if the cement constituents or concrete additions are tested at the fineness as specified by the respective product standards. In the absence of a product standard or a specification in the product standard, the constituents are tested at the fineness of the intended use.
NOTE In case the test methods are used for purposes of comparison of intrinsic reactivity, cement constituents are tested at similar fineness, where possible.
The test methods are also used for testing other new constituents that are latent hydraulic or pozzolanic and that are not covered by EN 197 series product standards. However, for such new constituents the validity of the underlying correlations with strength development have not been verified; in consequence the test results can only be used for informative and indicative purposes.
Furthermore, these test methods are used in manufacturing control of cement constituents for assessing their latent hydraulic or pozzolanic reactivity.
- Draft13 pagesEnglish languagesale 10% offe-Library read for×1 day
This document deals with the adaption of existing test methods and equipment to provide a repeatable and reproducible means of assessing the workability ("cohesivity") imparted to mortar by masonry cements.
- Technical report26 pagesEnglish languagesale 10% offe-Library read for×1 day
This document specifies cement with recycled concrete fines whose intended use is the preparation of concrete, mortar, grout, etc.
- Standard12 pagesEnglish languagesale 10% offe-Library read for×1 day
The general scope of the core product category rules (PCR) is given in EN 15804:2012+A2:2019, Clause 1.
This PCR is primarily intended for the creation of cradle-to-gate EPDs of cement and building lime.
In other respects, the scope is as in EN 15804:2012+A2:2019.
- Standard27 pagesEnglish languagesale 10% offe-Library read for×1 day
This document specifies the test methods for all building limes covered by EN 459 1. They can also be applied to other lime materials, the standards for which call up these methods.
This document specifies in Table 2 the methods used for the chemical analyses and the determination of physical properties of building limes.
This document specifies the reference methods and, in certain cases, an alternative method which can be considered to be equivalent. In the case of a dispute, only the reference methods are used.
Any other methods may be used provided they are calibrated, either against the reference methods or against internationally accepted reference materials, in order to demonstrate their equivalence.
- Standard74 pagesEnglish languagesale 10% offe-Library read for×1 day
This document deals with Portland-composite cement CEM II/C-M, not covered by EN 197-1, and a different type of Composite cement CEM VI, also not covered by EN 197-1, whose intended use is the preparation of concrete, mortar, grout etc.
This document does not cover:
- common cement covered by EN 197-1;
- very low heat special cement covered by EN 14216;
- supersulfated cement covered by EN 15743;
- calcium aluminate cement covered by EN 14647;
- masonry cement covered by EN 413-1.
- Standard10 pagesEnglish languagesale 10% offe-Library read for×1 day
This document specifies the scheme for the assessment and verification of constancy of performance (AVCP) of cements, including certification of constancy of performance.
The document provides technical rules for factory production control, further testing of samples taken at the manufacturing plant (autocontrol testing) and assessment of the performance of the cement, initial inspection of the manufacturing plant and of factory production control, continuing surveillance, assessment and evaluation of factory production control and audit-testing of samples. It also provides rules for actions to be followed in the event of non-conformity and requirements for depots.
In this document, the word “cement” is used to refer both to common cements as defined in EN 197 1 and to other cements and binders for which the relevant product specification standard makes reference to this document and which are submitted for certification. Such a cement is produced at a given factory and belongs to a particular type and a particular strength class, as defined and specified in the relevant product specification standard.
The guidelines given in the Technical Report CEN/TR 14245 contain information for the application of this document.
This document is linked with Annexes ZA of European Standards covering cements and binders, i.e. EN 197 1, EN 14216, EN 14647, EN 413 1 and EN 15743.
NOTE The reason for having drafted this separate document is that the provisions it includes are applicable to different products covered by different European Standards.
Guidance
EN 197 2 deals with the assessment and verification of constancy of performance (AVCP) of cements and binders that are submitted for certification. It deals in particular with cases where “further testing” of the product is undertaken, as is the case for attestation system 1+ under the Construction Products Regulation. The products for which EN 197 2 is applicable are: the common cement products and the low heat cements and the sulfate resisting cements, refer to EN 197 1, the very low heat special cements, refer to EN 14216, the supersulfated cements, refer to EN 15743, the calcium aluminate cements, refer to EN 14647, and the masonry cements, refer to EN 413 1.
- Technical report40 pagesEnglish languagesale 10% offe-Library read for×1 day
This document specifies the scheme for the assessment and verification of constancy of performance (AVCP) of cements, including certification of constancy of performance.
The document provides technical rules for factory production control, further testing of samples taken at the manufacturing plant (autocontrol testing) and assessment of the performance of the cement, initial inspection of the manufacturing plant and of factory production control, continuing surveillance, assessment and evaluation of factory production control and audit-testing of samples. It also provides rules for actions to be followed in the event of non-conformity and requirements for depots.
In this document, the word "cement" is used to refer both to common cements as defined in EN 197 1 and to other cements and binders for which the relevant product specification standard makes reference to this document and which are submitted for certification. Such a cement is produced at a given factory and belongs to a particular type and a particular strength class, as defined and specified in the relevant product specification standard.
The guidelines given in the Technical Report CEN/TR 14245 [1] contain information for the application of this document.
This document is linked with the Annexes ZA of European Standards covering cements and binders, i.e. EN 197 1, EN 14216, EN 14647, EN 413 1 and EN 15743.
NOTE The reason for having drafted this separate document is that the provisions it includes are applicable to different products covered by different European Standards.
- Standard21 pagesEnglish languagesale 10% offe-Library read for×1 day
This document describes the analytical procedures used to determine the content of C3A in the clinker starting from a chemical analysis on cement. The method can be applied to CEM type I and IV for the determination of the requirement of C3A, as defined on EN 197 1.
This document describes two methods, traditional wet and XRF analysis (EN 196 2), which can be considered to be equivalent, in the scope of this CEN/TR 17365, for the determination of Al2O3, Fe2O3 and SO3.
The same methods are described in EN 196 2, but for the scope of this document, the X-ray fluorescence (XRF) is the preferred method to be used for the determination of Al2O3, Fe2O3 and SO3.
- Technical report19 pagesEnglish languagesale 10% offe-Library read for×1 day
This document specifies the apparatus and procedure for determining the heat of hydration of cements and other hydraulic binders at different test ages by isothermal conduction calorimetry.
This test procedure is intended for measuring the heat of hydration of cement up to 7 days in order to obtain correspondence between Isothermal Conduction Calorimetry (ICC) and EN 196 8 and EN 196 9. Nevertheless this test duration may be critical for some apparatus, even if they can work properly at shorter test ages.
Contrary to EN 196 8 this method gives the heat of hydration continuously over the time. Additionally, the heat flow versus time is given.
- Standard17 pagesEnglish languagesale 10% offe-Library read for×1 day
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.