CEN/TS 15418:2006

Methods of test for dense refractory products - Guidelines for testing the corrosion of refractories caused by liquids

These guidelines introduce the principles, testing and assessment of corrosion of refractories by liquids (molten metals, metallurgical slags, glasses, fluxes etc.) and describe four commonly used test methods.
-   Method A: Corrosion testing by the crucible test;
-   Method B: Corrosion testing by the finger-dip test;
-   Method C: Corrosion testing by the rotary slag test;
-   Method D: Corrosion testing by the induction crucible test.

Prüfverfahren für dichte feuerfeste Erzeugnisse - Leitlinien zur Prüfung von durch Flüssigkeiten hervorgerufene Korrosion an feuerfesten Erzeugnissen

Die in dieser Technischen Spezifikation gegebenen Leitlinien führen für vier üblicherweise verwendete
Verfahren jeweils in die Grundlagen, Prüfung und die Bewertung der durch Flüssigkeiten (Metallschmelzen,
metallurgische Schlacke, Gläser, Flussmittel usw.) verursachten Korrosion von feuerfesten Erzeugnissen ein:
- Verfahren A: Korrosionsprüfung mittels Tiegeltest;
- Verfahren B: Korrosionsprüfung mittels Finger-Eintauchprüfung;
- Verfahren C: Korrosionsprüfung mittels Prüfung an rotierender Schlacke;
- Verfahren D: Korrosionsprüfung mittels Induktionstiegeltest.

Méthodes d'essai pour produits réfractaires denses - Lignes directrices pour la conduite sur réfractaires d'essais de corrosion provoquée par des liquides

Ces lignes directrices présentent les principes, les essais et l’évaluation de la corrosion des réfractaires
provoquée par des liquides (métaux en fusion, laitiers métallurgiques, verres, flux, etc.) et décrivent quatre
méthodes d’essai d’usage courant :
- Méthode A : Essais de corrosion au creuset ;
- Méthode B : Essais de corrosion au doigt (Procédé d’immersion) ;
- Méthode C : Essais de corrosion par les laitiers au four rotatif ;
- Méthode D : Essais de corrosion au creuset dans un four à induction.

Metode za preskušanje gostih ognjevzdržnih izdelkov – Navodila za preskušanje odpornosti ognjevzdržnih materialov proti koroziji zaradi tekočin

General Information

• Status: Published
• Publication Date: 13-Jun-2006
• ICS: 81.080 - Refractories
• Technical Committee: CEN/TC 187 - Refractory products and materials
• Drafting Committee: CEN/TC 187/WG 5 - Chemical attack on refractory products
• Current Stage: 9093 - Decision to confirm - Review Enquiry
• Start Date: 07-May-2009
• Completion Date: 07-May-2009
• Ref Project: SIST-TS CEN/TS 15418:2006 - Methods of test for dense refractory products - Guidelines for testing the corrosion of refractories caused by liquids

Standards Content (Sample)

SLOVENSKI STANDARD
01-oktober-2006
0HWRGH]DSUHVNXãDQMHJRVWLKRJQMHY]GUåQLKL]GHONRY±1DYRGLOD]DSUHVNXãDQMH
RGSRUQRVWLRJQMHY]GUåQLKPDWHULDORYSURWLNRUR]LML]DUDGLWHNRþLQ
Methods of test for dense refractory products - Guidelines for testing the corrosion of
refractories caused by liquids
Prüfverfahren für dichte feuerfeste Erzeugnisse - Leitlinien zur Prüfung von durch
Flüssigkeiten hervorgerufene Korrosion an feuerfesten Erzeugnissen
Méthodes d'essai pour produits réfractaires denses - Lignes directrices pour la conduite
sur réfractaires d'essais de corrosion provoquée par des liquides
Ta slovenski standard je istoveten z: CEN/TS 15418:2006
ICS:
81.080 Ognjevzdržni materiali Refractories
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.

TECHNICAL SPECIFICATION
CEN/TS 15418
SPÉCIFICATION TECHNIQUE
TECHNISCHE SPEZIFIKATION
June 2006
ICS 81.080
English Version
Methods of test for dense refractory products - Guidelines for
testing the corrosion of refractories caused by liquids
Méthodes d'essai pour produits réfractaires denses - Prüfverfahren für dichte feuerfeste Erzeugnisse - Leitlinien
Lignes directrices pour la conduite sur réfractaires d'essais zur Prüfung von durch Flüssigkeiten hervorgerufene
de corrosion provoquée par des liquides Korrosion an feuerfesten Erzeugnissen
This Technical Specification (CEN/TS) was approved by CEN on 25 March 2006 for provisional application.
The period of validity of this CEN/TS is limited initially to three years. After two years the members of CEN will be requested to submit their
comments, particularly on the question whether the CEN/TS can be converted into a European Standard.
CEN members are required to announce the existence of this CEN/TS in the same way as for an EN and to make the CEN/TS available
promptly at national level in an appropriate form. It is permissible to keep conflicting national standards in force (in parallel to the CEN/TS)
until the final decision about the possible conversion of the CEN/TS into an EN is reached.
CEN members are the national standards bodies of Austria, Belgium, Cyprus, Czech Republic, Denmark, Estonia, Finland, France,
Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania,
Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom.
EUROPEAN COMMITTEE FOR STANDARDIZATION
COMITÉ EUROPÉEN DE NORMALISATION
EUROPÄISCHES KOMITEE FÜR NORMUNG
Management Centre: rue de Stassart, 36  B-1050 Brussels
© 2006 CEN All rights of exploitation in any form and by any means reserved Ref. No. CEN/TS 15418:2006: E
worldwide for CEN national Members.

Contents Page
1 Scope .3
2 Normative references .4
3 General.4
4 Method A: Crucible test .7
5 Method B: Finger-dip corrosion test. 10
6 Method C: Rotary slag test . 12
7 Method D : Induction furnace test. 17
Bibliography. 19

Foreword
This Technical Specification (CEN/TS 15418:2006) has been prepared by Technical Committee CEN/TC 187
“Refractory products and materials”, the secretariat of which is held by BSI.
According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following
countries are bound to announce this Technical Specification: Austria, Belgium, Cyprus, Czech Republic,
Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania,
Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden,
Switzerland and United Kingdom.
1 Scope
These guidelines introduce the principles, testing and assessment of corrosion of refractories by liquids
(molten metals, metallurgical slags, glasses, fluxes etc.) and describe four commonly used test methods.
 Method A: Corrosion testing by the crucible test;
 Method B: Corrosion testing by the finger-dip test;
 Method C: Corrosion testing by the rotary slag test;
 Method D: Corrosion testing by the induction crucible test.
2 Normative references
The following referenced documents are indispensable for the application of this document. For dated
references, only the edition cited applies. For undated references, the latest edition of the referenced
document (including any amendments) applies.
EN 1402-5 Unshaped refractory products — Preparation and treatment of test pieces
EN ISO 12677 Chemical analysis of refractory products by XRF— Fused cast bead method (ISO 12677:2003)
ISO 3611 Micrometer callipers for external measurement
3 General
3.1 Principles
Industrial refractories are mainly used for the inner linings of operational units in combustion, chemical,
metallurgical and materials manufacturing processes. Because of the thermal, chemical, mechanical and
physical gradients encountered in these refractory linings, their service life is limited by corrosion phenomena,
which often involve a combination of different mechanisms such as dissolution, invasive penetration,
oxidation-reduction reactions, mass transport, acid-base reaction and spalling of reacted layers.
Because of the complexity of the phenomena, a simple, all-encompassing, general theory of corrosion of
refractory materials does not exist, but some basic principles can be applied.
A fundamental and long considered principle is the acid-base relationship between the refractory and the
corroding liquid so that an acid refractory such as silica is chosen for an acidic liquid and a basic refractory
such as magnesia or doloma for a basic liquid. For example, commonly used acid-base ranking of various
compounds are:
most acidic < N O (g) < SO (g) < SO (g)< CO (g) < B O (g or l) < V O (g or l) < SiO (s) 2 5 3 2 2 2 3 2 5 2 2
ZrO (s) < Fe O (s) < Cr O (s) < Al O (s) < FeO (s) < NiO (s) < MnO (s) < MgO (s) < CaO (s) < Na O (s
2 2 3 2 3 2 3 2
or g) < K O (s or g) < most basic.
However, whilst this approach provides a starting point for refractory selection, it has limited value in
comparing actual behaviour.
A second approach is to make appropriate thermodynamic calculations for the thermal stability of each
constituent (free energy of formation); red-ox potentials and possible reactions (free energy change) between
reactants (solid, liquid and gas) with the help of the Ellingham diagrams; and the volume changes caused by
phase transformations inducing microcracks in the matrix.
Finally, the kinetics of the corrosion are also governed by several other phenomena:
 wetting or non-wetting behaviour of the liquid reactant on a solid surface and the capillary forces
controlling its penetration in the porous volume of the refractory (slag penetration inducing structural
spalling);
 dissolution of the solid into the liquid;
 condensation of a gas to form a liquid or a solid into the pores that may react chemically and create a
thermal-expansion mismatch (for instance, alkali vapours causing the formation of high thermal
expansion aluminosilicates).
In practice, for porous solids such as refractories, with open porosity and with fine and highly reactive matrix
materials, both dissolution and penetration occur. Hence, most corrosion situations involve chemical attack of
the matrix or low-melting constituent phases, which disrupts the structure and allows the coarse-grained
aggregates to be carried away by movement of the liquid.
When penetration is more important than dissolution, another mechanism of degradation, structural spalling,
needs to be considered.
NOTE Structural spalling is the general term for the cracking or fracture caused by stress produced between the
altered (e.g. slag impregnated) zone and the original zone in a refractory under service.
Major factors like chemical reaction rate, viscosity, diffusion constant are highly temperature dependent.
Information about the maximum service temperature for normal durability as a function of refractory materials
and corrosion reactants can be found in the literature (see e.g. [1]).
3.2 Corrosion testing
Corrosion resistance data obtained in a laboratory environment rarely simulate the actual conditions that
prevail in service. The size and geometry, thermal gradient and cycling, mechanical load, as well as operation
time are difficult to scale down to laboratory conditions. Moreover, accelerated tests in more severe conditions
to reduce testing time can lead to erroneous predictions of service performance.
As full-size testing in industrial conditions or at the scale of small panels are more costly and not always
possible to perform, numerous laboratory test procedures have been developed but only a few of these have
reached the status of an international standard because each industrial application requires specific conditions.
Nevertheless, there is a need for corrosion test standards, describing general procedures and reasonable
expectations in terms of data and reliability, leaving full freedom for the choice of the temperature and the
nature of the reactant.
On the other hand, when the reactant is a pure chemical compound, acting under readily definable conditions,
a standard has already been developed (for instance, the CO attack procedure in the EN ISO 12676 [2]).
In the case of liquid corrodent (e.g. molten metal, molten salt, slag), different approaches have been adopted
for corrosion testing in the laboratory:
 Static
The crucible test, the immersion test or the pill test deal with the thermodynamic aspect for the appraisal
of chemical attack.
 Dynamic
The drip test and the finger-dip test with movement and/or rotation add a kinetic aspect; for immersion
and finger-dip tests, weight changes can be recorded. More application oriented tests are the basin test,
the rotary slag test and the induction crucible test, which are performed on a larger scale, closer to the
service conditions but, as a consequence, involve a high degree of setting up and expense.
Finally, it is emphasised that corrosion resistance is not an intrinsic material property, but that of a "three-
component" system (i.e. material-corrodent-environment). Accordingly, the results will be largely dependent
upon the test method used and any comparison between results obtained by different methods should be
done with great care.
3.3 Assessment of the extent of corrosion
The extent of chemical attack may be ascertained using a number of simple criteria:
 Depth of penetration and formation of an altered layer;
 Change of mass (gain or loss);
 Change of cross-section (contraction or expansion);
 Change of mechanical strength;
 Change in the chemical composition of the corroding medium.
In addition, microscopic examination and microanalysis techniques can be used to study the nature of the
attack.
3.4 Overview
An overview of the main characteristics of the 4 methods covered by the present guidelines is shown in Table
1 and is meant to assist in the selection of the most pertinent method for a given practical situation.
Table 1 — Overview of the various test methods
Factors Crucible Finger-dip Rotary slag Induction furnace
Metals (M) X X - X
Technical Slags (S) X X X -
(Materials)
M + S X X (X) X
Glasses X X (X) -
Static X X - -
Dynamic - X X X
Isothermal X X - -
Temp. gradient - - X X
Technical Vol
corrodent
low high medium medium
Surf
(Parameters)
refrac
Renewal of corrodent - - X X
Possible interaction
- X X X
between samples
Control of the atmosphere X X X X
Visual/Microscopy X X X X
Technical Dimensional X X X X
(Assessment)
Change of composition possible possible possible possible
Mechanical - - - -
Scale small medium large large
Economical Ease ++++ +++ ++ +
Cost low medium high high
4 Method A: Crucible test
4.1 Scope
This clause describes a method of determining the relative resistance of refractory products to a given liquid
corrodent under static conditions when heated to specified temperatures, by melting the corrodent in crucibles
formed from the products to be tested.
It is applicable to fired or unfired products and to monolithic materials including concrete, gun mixes, ram
mixes, plastics, etc. A variation of the test allows assessment of jointing material.
The method enables the relative resistance of various refractory products to a specified corrodent to be
established by comparing the erosion and penetration occurring under static conditions and a uniform
temperature.
4.2 Principle
Crucibles together with lids are cut or fabricated from the products to be tested. The crucibles are filled with a
quantity of the corrodent and heated to the test temperature for a specified period.
The test conditions (temperature and corrodent composition) may reflect expected service conditions, but in
some situations, a more aggressive corrodent and/or high temperature may be used to speed up the attack to
determine the resistance of the refractory to the corrosive liquid in a relatively short time.
After cooling the crucibles are cut open, examined and measured for penetration or erosion and photographed
if required.
4.3 Advantages/disadvantages
4.3.1 Advantages
The method is an easy and simple test to perform, merely a standard furnace and a crucible of the re
...