Advanced technical ceramics - Methods of test for ceramic powders - Part 3: Determination of the oxygen content of non-oxides by thermal extraction with a carrier gas

Advanced technical ceramics - Methods of test for ceramic powders - Part 3: Determination of the oxygen content of non-oxides by thermal extraction with a carrier gas

This part of EN 725 describes a method for the determination of the oxygen content of non-oxide powders used for advanced technical ceramics, using an inert carrier gas thermal extraction method. The method described is suitable for oxygen contents of less than 3 %.
NOTE   An indication of the limits of determination is usually given by the manufacturers of the gas analysis apparatus used.  However, for a specific measurement procedure, such limits can be determined by experiments conducted by the user.

Hochleistungskeramik - Prüfverfahren für keramische Pulver - Teil 3: Bestimmung des Sauerstoffgehaltes in Nichtoxid-Pulvern mittels Trägergasheißextraktion

Dieser Teil von EN 725 beschreibt ein Verfahren zur Bestimmung des Sauerstoffgehaltes mittels Trägergasheißextraktion in Nichtoxidpulvern, die für Technische Keramik verwendet werden. Das Verfahren ist anwendbar für Sauerstoffgehalte < 3 %.
ANMERKUNG   Die Grenzwerte für die Bestimmung sind von den Geräteherstellern vorgegeben. Für spezielle Messverfahren müssen sie durch eigene Versuche bestimmt werden

Céramiques techniques avancées - Méthodes d'essais pour poudres céramiques - Partie 3: Détermination de la teneur en oxygène de poudres non-oxydes par extraction à chaud sous gaz porteur

La présente partie de l’EN 725 décrit une méthode de détermination de la teneur en oxygène de poudres non-oxydes utilisées dans les céramiques techniques avancées, par extraction à chaud sous gaz porteur inerte. La méthode présentée est applicable aux teneurs en oxygène inférieures à 3 %.
NOTE   Généralement, les fabricants de l’appareil d’analyse du gaz utilisé indiquent les limites de la détermination.  Cependant, pour un mode opératoire de mesure particulier, ces limites peuvent être déterminées au cours des expériences conduites par l’utilisateur.

Sodobna tehnična keramika - Preskusne metode za keramične praške - 3. del: Določevanje kisika v neoksidnih praških s toplotno ekstrakcijo z nosilnim plinom

General Information

Status
Published
Publication Date
16-Jan-2007
Withdrawal Date
30-Jul-2007
ICS
81.060.30 - Advanced ceramics
Technical Committee
CEN/TC 184 - Advanced technical ceramics
Drafting Committee
CEN/TC 184 - Advanced technical ceramics
Current Stage
9020 - Submission to 2 Year Review Enquiry - Review Enquiry
Start Date
15-Jul-2024
Completion Date
15-Jul-2024
Mandate
M/BC/CEN/90/4 - Request concerning the realisation of a standardization programme in the field of advanced technical ceramics
Ref Project
SIST EN 725-3:2007 - Advanced technical ceramics - Methods of test for ceramic powders - Part 3: Determination of the oxygen content of non-oxides by thermal extraction with a carrier gas

Relations

Replaces
EN 725-3:1994 - Advanced technical ceramics - Methods of test for ceramic powders - Part 3: Determination of the oxygen content of non-oxides by thermal extraction with a carrier gas
Effective Date
22-Dec-2008

Buy Standard

EN 725-3:2007EN 725-3:2007
PreviousNext
Standard
EN 725-3:2007
English language
7 pages
sale 10% off
Preview
sale 10% off
Preview
e-Library read for
1 day

Standards Content (Sample)


SLOVENSKI STANDARD
01-maj-2007
1DGRPHãþD
SIST EN 725-3:2000
6RGREQDWHKQLþQDNHUDPLND3UHVNXVQHPHWRGH]DNHUDPLþQHSUDãNHGHO
'RORþHYDQMHNLVLNDYQHRNVLGQLKSUDãNLKVWRSORWQRHNVWUDNFLMR]QRVLOQLPSOLQRP
Advanced technical ceramics - Methods of test for ceramic powders - Part 3:
Determination of the oxygen content of non-oxides by thermal extraction with a carrier
gas
Hochleistungskeramik - Prüfverfahren für keramische Pulver - Teil 3: Bestimmung des
Sauerstoffgehaltes in Nichtoxid-Pulvern mittels Trägergasheißextraktion
Céramiques techniques avancées - Méthodes d'essais pour poudres céramiques - Partie
3: Détermination de la teneur en oxygene de poudres non-oxydes par extraction a chaud
sous gaz porteur
Ta slovenski standard je istoveten z: EN 725-3:2007
ICS:
81.060.30 Sodobna keramika Advanced ceramics
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.

EUROPEAN STANDARD
EN 725-3
NORME EUROPÉENNE
EUROPÄISCHE NORM
January 2007
ICS 81.060.30 Supersedes EN 725-3:1994
English Version
Advanced technical ceramics - Methods of test for ceramic
powders - Part 3: Determination of the oxygen content of non-
oxides by thermal extraction with a carrier gas
Céramiques techniques avancées - Méthodes d'essais Hochleistungskeramik - Prüfverfahren für keramische
pour poudres céramiques - Partie 3: Détermination de la Pulver - Teil 3: Bestimmung des Sauerstoffgehaltes in
teneur en oxygène de poudres non-oxydes par extraction à Nichtoxid-Pulvern mittels Trägergasheißextraktion
chaud sous gaz porteur
This European Standard was approved by CEN on 2 December 2006.
CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European
Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national
standards may be obtained on application to the CEN Management Centre or to any CEN member.
This European Standard exists in three official versions (English, French, German). A version in any other language made by translation
under the responsibility of a CEN member into its own language and notified to the CEN Management Centre has the same status as the
official versions.
CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Finland,
France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal,
Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom.
EUROPEAN COMMITTEE FOR STANDARDIZATION
COMITÉ EUROPÉEN DE NORMALISATION
EUROPÄISCHES KOMITEE FÜR NORMUNG
Management Centre: rue de Stassart, 36  B-1050 Brussels
© 2007 CEN All rights of exploitation in any form and by any means reserved Ref. No. EN 725-3:2007: E
worldwide for CEN national Members.

Contents Page
Foreword.3
1 Scope .4
2 Normative references .4
3 Principle.4
4 Apparatus .4
5 Sample preparation .5
6 Calibration .5
7 Blank determination .5
8 Procedure .5
9 Test report .6
Annex A (informative) Guidance in the selection of test conditions .7

Foreword
This document (EN 725-3:2007) has been prepared by Technical Committee CEN/TC 184 “Advanced
technical ceramics”, the secretariat of which is held by BSI.
This European Standard shall be given the status of a national standard, either by publication of an identical
text or by endorsement, at the latest by July 2007, and conflicting national standards shall be withdrawn at the
latest by July 2007.
This document supersedes EN 725-3:1994.
EN 725 Advanced technical ceramics — Methods of test for ceramic powders was prepared in Parts as
follows:
Part 1: Determination of impurities in alumina
Part 2: Determination of impurities in barium titanate
Part 3: Determination of the oxygen content of non-oxides by thermal extraction with a carrier gas
Part 4: Determination of oxygen content in aluminium nitride by XRF analysis
Part 5: Determination of particle size distribution
Part 6: Determination of the specific surface area [withdrawn]
Part 7: Determination of the absolute density [withdrawn]
Part 8: Determination of tapped bulk density
Part 9: Determination of un-tapped bulk density
Part 10: Determination of compaction properties
Part 11: Determination of densification on natural sintering
Part 12: Chemical analysis of zirconia
Parts 6 and 7 of the series were superseded in 2005 by EN ISO 18757 and EN ISO 18753 respectively.
According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following
countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Cyprus, Czech
Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia,
Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain,
Sweden, Switzerland and United Kingdom.
1 Scope
This part of EN 725 describes a method for the determination of the oxygen content of non-oxide powders
used for advanced technical ceramics, u
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

CEN
EN ISO 21971:2024(Main)
Fine ceramics (advanced ceramics, advanced technical ceramics) - Mechanical properties of ceramic composites at ambient temperature in air atmospheric pressure - Determination of hoop tensile properties of tubes (ISO 21971:2019)
SIST EN ISO 21971:2024

This document specifies the conditions for the determination of hoop tensile properties of ceramic matrix composite (CMC) tubes with continuous fibre-reinforcement at ambient temperature in air atmospheric pressure. This document is specific to the tubular geometries since fibre architecture and specimen geometry factors in composite tubes are distinctly different from those in flat specimens.
This document provides information on the hoop tensile properties and stress-strain response, such as hoop tensile strength, hoop tensile strain at failure and elastic constants. The information can be used for material development, control of manufacturing (quality insurance), material comparison, characterization, reliability and design data generation for tubular components.
This document addresses, but is not restricted to, various suggested test piece fabrication methods. It applies primarily to ceramic and/or glass matrix composite tubes with a continuous fibrous-reinforcement: unidirectional (1D filament winding and tape lay-up), bi-directional (2D braid and weave) and tri-directional (xD, with 2 < x < 3), subjected to an internal pressure.
Values expressed in this document are in accordance with the International System of Units (SI).

  • Standard
    26 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN ISO 22459:2024(Main)
Fine ceramics (advanced ceramics, advanced technical ceramics) - Reinforcement of ceramic composites - Determination of distribution of tensile strength and tensile strain to failure of filaments within a multifilament tow at ambient temperature (ISO 22459:2024)
SIST EN ISO 22459:2024

This document specifies the conditions for the determination of the distribution of strength and rupture strain of ceramic filaments within a multifilament tow at room temperature by performing a tensile test on a multifilament tow.
This document applies to dry tows of continuous ceramic filaments that are assumed to act freely and independently under loading and exhibit linear elastic behaviour up to failure. The outputs of this method are not to be mixed up with the strengths of embedded tows determined by using ISO 24046.

  • Standard
    23 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN ISO 26443:2023(Main)
Fine ceramics (advanced ceramics, advanced technical ceramics) - Rockwell indentation test for evaluation of adhesion of ceramic coatings (ISO 26443:2023)
SIST EN ISO 26443:2024

This document specifies a method for the qualitative evaluation of the adhesion of ceramic coatings up to 20 μm thick by indentation with a Rockwell diamond indenter. The formation of cracks after indentation can also reveal cohesive failure. The indentations are made with a Rockwell hardness test instrument.
The method described in this document can also be suitable for evaluating the adhesion of metallic coatings.
The test is not suitable for elastic coatings on hard substrates.

  • Standard
    13 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN ISO 18755:2023(Main)
Fine ceramics (advanced ceramics, advanced technical ceramics) - Determination of thermal diffusivity of monolithic ceramics by flash method (ISO 18755:2022)
SIST EN ISO 18755:2023

This document specifies the test method for the determination of thermal diffusivity from room temperature to at least 1 700 K by the flash method for homogeneous monolithic ceramics with porosity less than 10 %.
Flash methods, like laser flash, are applicable to homogeneous isotropic materials with thermal diffusivity values ranging from 0,1 to 1 000 mm2 s-1 within the temperature range from approximately 100 K to 2 300 K.
The method described in Annex G describes how to estimate, on the basis of the thermal diffusivity test, the specific heat capacity and the thermal conductivity of homogeneous monolithic ceramics with porosity less than 10 %.

  • Standard
    49 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN ISO 23739:2023(Main)
Fine ceramics (advanced ceramics, advanced technical ceramics) - Methods for chemical analysis of zirconium oxide powders (ISO 23739:2021)
SIST EN ISO 23739:2023

This document specifies methods for the chemical analysis of zirconium oxide powders used as the raw material for fine ceramics.
It stipulates the determination methods of the zirconium, aluminium, barium, calcium, cerium, cobalt, gadolinium, hafnium, iron, magnesium, potassium, silicon, sodium, strontium, titanium and yttrium contents in zirconium oxide powders for fine ceramics. The test sample is decomposed by acid pressure decomposition or alkali fusion. Contents of zirconium and yttrium are determined by using either a precipitation and gravimetric method or an inductively coupled plasma–optical emission spectrometry (ICP–OES) method. Contents of aluminium, barium, calcium, cerium, cobalt, gadolinium, hafnium, iron, magnesium, potassium, silicon, sodium, strontium and titanium are determined by using an ICP–OES method.

  • Standard
    24 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN ISO 17947:2023(Main)
Fine ceramics (advanced ceramics, advanced technical ceramics) - Methods for chemical analysis of fine silicon nitride powders (ISO 17947:2014)
SIST EN ISO 17947:2023

This document specifies the methods for the chemical analysis of fine silicon nitride powders used as the raw material for fine ceramics. It stipulates the determination methods of total silicon, total nitrogen, aluminium, iron, calcium, oxygen, carbon, fluorine, and chlorine in fine silicon nitride powders.

  • Standard
    41 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN ISO 24370:2023(Main)
Fine ceramics (advanced ceramics, advanced technical ceramics) - Test method for fracture toughness of monolithic ceramics at room temperature by chevron-notched beam (CNB) method (ISO 24370:2005)
SIST EN ISO 24370:2023

ISO 24370:2005 specifies a test method for determining the fracture toughness of monolithic ceramic materials at room temperature by the chevron-notched beam (CNB) method.
ISO 24370:2005 is applicable to monolithic ceramics and whisker- or particulate-reinforced ceramics that are regarded as macroscopically homogeneous. It is not applicable to continuous-fibre reinforced ceramic composites.
ISO 24370:2005 is usually applicable to ceramic materials with a fracture toughness less than about 12 megapascal(square root metre). The test method is applicable to materials with a flat crack-growth resistance curve and may be applicable to materials with a rising crack-growth resistance curve (R-curve).

  • Standard
    22 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN ISO 20509:2023(Main)
Fine ceramics (advanced ceramics, advanced technical ceramics) - Determination of oxidation resistance of non-oxide monolithic ceramics (ISO 20509:2003)
SIST EN ISO 20509:2023

ISO 20509:2003 describes the method of test for determining the oxidation resistance of non-oxide monolithic ceramics, such as silicon nitride, sialon and silicon carbide at high temperatures. This International Standard is designed to provide an assessment of the mass and dimensional changes of test pieces following oxidation at high temperature in an oxidizing atmosphere, and to assess whether oxidation has a significant effect on the subsequent strength. This test method may be used for materials development, quality control, characterization, and design data generation purposes.

  • Standard
    19 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN ISO 17092:2023(Main)
Fine ceramics (advanced ceramics, advanced technical ceramics) - Determination of corrosion resistance of monolithic ceramics in acid and alkaline solutions (ISO 17092:2005)
SIST EN ISO 17092:2023

ISO 17092:2005 describes the test method for determining the corrosion resistance of fine ceramics in acid and alkaline solutions, such as sulfuric acid and sodium hydroxide. This International Standard is designed to provide an assessment of the mass changes and dimensional changes of test specimens following the corrosion test immersed in the corrosive liquids, and to assess whether corrosion has a significant effect on the subsequent strength. This test method may be used for development of materials, quality control, characterization, and design-data generation purposes.

  • Standard
    16 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN ISO 20501:2022(Main)
Fine ceramics (advanced ceramics, advanced technical ceramics) - Weibull statistics for strength data (ISO 20501:2019)
SIST EN ISO 20501:2023

This document covers the reporting of uniaxial strength data and the estimation of probability distribution parameters for advanced ceramics which fail in a brittle fashion. The failure strength of advanced ceramics is treated as a continuous random variable. Typically, a number of test specimens with well-defined geometry are brought to failure under well-defined isothermal loading conditions. The load at which each specimen fails is recorded. The resulting failure stresses are used to obtain parameter estimates associated with the underlying population distribution.
This document is restricted to the assumption that the distribution underlying the failure strengths is the two-parameter Weibull distribution with size scaling. Furthermore, this document is restricted to test specimens (tensile, flexural, pressurized ring, etc.) that are primarily subjected to uniaxial stress states. Subclauses 6.4 and 6.5 outline methods of correcting for bias errors in the estimated Weibull parameters, and to calculate confidence bounds on those estimates from data sets where all failures originate from a single flaw population (i.e. a single failure mode). In samples where failures originate from multiple independent flaw populations (e.g. competing failure modes), the methods outlined in 6.4 and 6.5 for bias correction and confidence bounds are not applicable.

  • Standard
    45 pages
    English language
    sale 10% off
    e-Library read for
    1 day