ISO 1079:1989

Metallic materials — Hardness test — Verification of Rockwell superficial hardness testing machines (scales 15N, 30N, 45N, 15T, 30T and 45T)

Matériaux métalliques — Essai de dureté — Contrôle des machines d'essai de dureté superficielle Rockwell (échelles 15N, 30N, 45N, 15T, 30T et 45T)

General Information

• Status: Withdrawn
• Publication Date: 18-Oct-1989
• Withdrawal Date: 18-Oct-1989
• ICS: 77.040.10 - Mechanical testing of metals
• Technical Committee: ISO/TC 164/SC 3 - Hardness testing
• Drafting Committee: ISO/TC 164/SC 3 - Hardness testing
• Current Stage: 9599 - Withdrawal of International Standard
• Completion Date: 16-Sep-1999

Relations

• Revised: ISO 6508-2:1999 - Metallic materials — Rockwell hardness test — Part 2: Verification and calibration of testing machines (scales A, B, C, D, E, F, G, H, K, N, T)
• Effective Date: 15-Apr-2008

Standards Content (Sample)

INTERNATIONAL Is0
STANDARD 1079
First edition
1989-l l-01
Metallic materials - Hardness test -
Verification of Rockwell superficial hardness
testing machines (scales 15N, 30N, 45N, 15T, 30T
and 45T)
Contr6le des machines d’essai de
Matbriaux m&alligues - Essai de durete -
duretb superficiele Rockwell (tkhelles 75N, 3ON, 45N, 15T, 301 et 45T)
Reference number
IS0 1079 : 1989 (El

---------------------- Page: 1 ----------------------
ISO1079:1989 (El
Foreword
IS0 (the International Organization for Standardization) is a worldwide federation of
national standards bodies (IS0 member bodies). The work of preparing International
Standards is normally carried out through IS0 technical committees. Each member
body interested in a subject for which a technical committee has been established has
the right to be represented on that committee. International organizations, govern-
mental and non-governmental, in liaison with ISO, also take part in the work. IS0
collaborates closely with the International Electrotechnical Commission (IEC) on all
matters of electrotechnical standardization.
Draft International Standards adopted by the technical committees are circulated to
the member bodies for approval before their acceptance as International Standards by
the IS0 Council. They are approved in accordance with IS0 procedures requiring at
least 75 % approval by the member bodies voting.
International Standard IS0 1079 was prepared by Technical Committee ISO/TC 164,
Mechanical testing of metals.
It cancels and replaces IS0 Recommendation R 1079: 1969, of which it constitutes a
technical revision.
Annexes A and B form an integral part of this International Standard.
0 IS0 1989
All rights reserved. No part of this publication may be reproduced or utilized in any form or by any
means, electronic or mechanical, including photocopying and microfilm, without permission in
writing from the publisher.
International Organization for Standardization
Case postale 56 l CH-1211 Geneve 20 l Switzerland
Printed in Switzerland

---------------------- Page: 2 ----------------------
IS0 1079: 1989 (E)
INTERNATIONAL STANDARD
Metallic materials - Hardness test - Verification
superficial hardness testing machines.
of Rockwell
(scales 15N, 30N, 45N, 15T, 30T and 45T)
3 General conditions
1 Scope
Before a Rockwell superficial hardness testing machine is
This International Standard specifies a method of verification of
verified, it shall be checked to ensure that
testing machines for determining Rockwell superficial hardness
(scales 15N, 30N, 45N, 15T, 30T and 45T) in accordance with
a) the machine is properly set up;
IS0 1024.
b) the plunger holding the indenter is capable of sliding in
its guide, by its own weight, but without any appreciable
It describes a direct verification method for checking the main
clearance;
functions of the machine, and an indirect verification method
suitable for the overall checking of the machine. The indirect
c) the indenter-holder is firmly mounted in the plunger;
verification method may be used on its own for periodic routine
d) the test force can be applied and removed without
checking of the machine in service.
shock or vibration and in such a manner that the readings
are not influenced;
If a testing machine is also to be used for other methods of
e) the readings are not affected either by movements of
hardness testing, it shall be verified independently for each
method. the test piece or by deformations of the frame. When a
device is supplied which locks the test piece against the up-
per part of the frame, the locking force shall exceed the total
test force. The influence of deformations may be checked
2 Normative references
by using a plain plunger instead of the indenter, bearing
directly against the anvil and using the locking device (when
it is supplied). The readings of the measuring device before
The following standards contain provisions which, through
application and after removal of the additional test force
reference in this text, constitute provisions of this International
shall not differ by more than 1,0 Rockwell superficial unit.
Standard. At the time of publication, the editions indicated
were valid. All standards are subject to revision, and parties to
agreements based on this International Standard are encour-
4 Direct verification
aged to investigate the possibility of applying the most recent
editions of the standards indicated below. Members of IEC and
Direct verification involves
IS0 maintain registers of currently valid International Stan-
dards.
-
verification of the test force;
-
IS0 1024 : 1989, Metallic materials - Hardness test - verification of the indenter;
Rockwell superficial test (scales 75N, 3ON, 45N, 75T, 30T
-
verification of the measuring device.
and 45TI.
4.1 Verification of the test force
IS0 1355 : 1989, Metallic materials - Hardness test - Calibra-
tion of standardized blocks to be used for Rockwell superficial
hardness testing machines (scales 75N, 3ON, 45N, 15T, 3OTand 4.1.1 The preliminary test force F0 (see 4.1.4) and each total
45TI. test force F used (see 4.1.5) shall be measured, and, whenever
applicable, this shall be done at not less than three positions of
IS0 6507-l : 1982, Metallic materials - Hardness test - the plunger spaced throughout its range of movement during
Vickers test - Part 7; HV 5 to HV 100. testing.
1

---------------------- Page: 3 ----------------------
ISO1079:1989 EI
crystallographic axes of the diamond, and the seating of the
4.12 The forces shall be measured by one of the following
diamond in its holder.
two methods :
For this reason, an indirect verification is considered necessary.
a) measurement by means of an elastic proving device
The performance of the test indenter shall be compared in a
previously calibrated to an accuracy of + 0,2 %,
standardizing machine with the performance of the standardiz-
ing machine indenter. The test shall be in accordance with IS0
1355.
balancing against a force, accurate to + 0,2 %, applied
b)
by means of standardized masses with mechanical advan-
Tests shall be made on a minimum of two blocks in the 30N
tage. ’
scale, one at a hardness level near the lower limit, the second
near the upper limit of the field of application of this scale. For
4.1.3 Three readings shall be taken for each force at each
each block the mean hardness value of three indentations made
position of the plunger. Immediately before each reading is
using the indenter to be verified shall not differ from the mean
taken, the plunger shall have been moved in the same direction
hardness of the three indentations obtained with the standar-
as during testing.
dizing indenter by more than k 0,8 Rockwell superficial hard-
ness units. The indentations with the indenter to be verified and
with the standardizing indenter shall be located so that the in-
4.1.4 The tolerance on the preliminary test force F0 before ap-
dentations of the two indenters are in each case adjacent. The
plication and after removal of the additional test force FI shall
test shall be made in accordance with IS0 1355.
be & 2,0 %.
NOTE - The standardizing indenter is the indenter or the indenters
4.1.5 The tolerance on the total test force Fshall be * 0,7 %.
recognized as the reference indenter(s) at national level.
4.2 Verification of the indenter
4.2.2 Steel ball indenters (scales 15T, 30T and 45T) shall be
verified following the procedure given in 4.2.2.1 to 4.2.2.3.
4.2.1 Diamond cone indenters (scales 15N, 30N and 45N)
shall ‘be verified following the procedure given in 4.2.1.1
to 4.2.1.6.
4.2.2.1 For the purpose of verifying the size and the hardness
of the steel balls it is considered sufficient to test a sample ball
4.2.1.1 The surface of the diamond cone and spherical tip
selected at random from a batch. The ball verified for hardness
shall be positioned for a penetration depth
...

NORME
IS0
I NTE R NAT1 O NALE
1079
Première édition
1989-11-01
'L
Matériaux métalliques - Essai de dureté -
Contrôle des machines d'essai de dureté
superficielle Rockwell (échelles 15N, 30N, 45N,
15T, 30T et 45T)
Metallic materials - Hardness test - Verification of Rochell suDedicial hardness
testing machines (scales 15N, 30N, 45N, 15T, 30T and 45T)
Numéro de référence
IS0 1079 : 1989 (Fi

---------------------- Page: 1 ----------------------
IS0 1079 : 1989 (FI
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale
d'organismes nationaux de normalisation (comités membres de I'ISO). L'élaboration
des Normes internationales est en général confiée aux comités techniques de I'ISO.
Chaque comité membre intéressé par une étude a le droit de faire partie du comité
technique créé à cet effet. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec I'ISO participent également aux travaux. L'ISO col-
labore étroitement avec la Commission électrotechnique internationale (CE11 en ce qui
concerne la normalisation électrotechnique.
Les projets de Normes internationales adoptés par les comités techniques sont soumis
aux comités membres pour approbation, avant leur acceptation comme Normes inter-
nationales par le Conseil de I'ISO. Les Normes internationales sont approuvées confor-
mément aux procédures de I'ISO qui requièrent l'approbation de 75 % au moins des
comités membres votants.
La Norme internationale IS0 1079 a été élaborée par le comité technique ISO/TC 164,
Essais mécaniques des métaux.
Elle annule et remplace la Recommandation ISO/R 1079: 1969, dont elle constitue une
révision technique.
Les annexes A et B font partie intégrante de la présente Norme internationale.
O IS0 1989
Droits de reproduction réservés. Aucune partie de cette publication ne peut être reproduite ni
utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie et les microfilms, sans l'accord écrit de l'éditeur.
Organisation internationale de normalisation
Case postale 56 0 CH-1211 Genève 20 0 Suisse
Imprimé en Suisse

---------------------- Page: 2 ----------------------
IS0 1079 : 1989 (FI
NORM E I NTER NATIONALE
Matériaux métalliques - Essai de dureté - Contrôle
des machines d'essai de dureté superficielle Rockwell
(échelles 15N, 30N, 45N, 15T, 30T et 45T)
L 1 Domaine d'application 3 Conditions générales
Avant de contrôler une machine d'essai de dureté Rockwell,
La présente Norme internationale prescrit une méthode pour le
celle-ci doit être vérifiée pour s'assurer que
contrôle des machines d'essai utilisées en vue de la détermina-
tion de la dureté superficielle Rockwell (échelles 15N. 30N. 45N.
a) la machine est correctement installée;
15T, 30T et 45T) conformément à I'ISO 1024.
b) le plongeur portant le pénétrateur peut glisser dans son
Elle décrit une méthode de contrôle direct pour la vérification guide sous son propre poids sans aucun jeu appréciable;
des principales fonctions de la machine, et une méthode de
c) la monture du pénétrateur est solidement fixée sur le
contrôle indirect utilisée pour une vérification globale de la
plongeur;
machine. La méthode de contrôle indirect peut être utilisée
d) la charge peut être appliquée et enlevée sans choc ni
seule lorsqu'il s'agit d'une vérification périodique de routine des
vibration et de telle facon que les lectures n'en soient pas
machines en service.
affectées;
Si une machine d'essai est généralement utilisée pour d'autres
e) les lectures ne sont pas affectées par des déplacements
méthodes de dureté, elle doit être contrôlée séparément pour de l'éprouvette ou des déformations du bâti de la machine.
chaque méthode. Lorsqu'une machine est fournie avec un système de blocage
maintenant solidement l'éprouvette contre le dessus du
bâti, la force de blocage doit être supérieure à la charge
totale. II est possible de déterminer l'influence des déforma-
2 Références normatives
tions en remplacant le pénétrateur par une touche prenant
1v
appui directement sur l'enclume et en utilisant le dispositif
Les normes suivantes contiennent des dispositions qui, par
de blocage (lorsqu'il est fourni). Les lectures du dispositif de
suite de la référence qui en est faite, constituent des disposi-
mesure, avant et après application de la charge addition-
tions valables pour la présente Norme internationale. Au
nelle, ne doivent pas différer de plus de 1 ,O unité de dureté
moment de la publication, les éditions indiquées étaient en
superficielle Rockwell.
vigueur. Toute norme est sujette à révision et les parties pre-
nantes des accords fondés sur la présente Norme internationale
sont invitées à rechercher la possibilité d'appliquer les éditions
4 Contrôle direct
les plus récentes des normes indiquées ci-après. Les membres
de la CE1 et de 1'1S0 possèdent le registre des Normes interna- Le contrôle direct comprend
tionales en vigueur à un moment donné.
-
le contrôle de la charge d'essai;
IS0 1024 1 1989, Matériaux métalliques - Essai de dureté -
- le contrôle du pénétrateur;
Essai superficiel Rockwell (échelles 15N, 30N, &N, 15T, 30T
-
le contrôle du dispositif de mesure.
et &Ti.
4.1
IS0 1355 1 1989, Matériaux métalliques - Essai de dureté - Contrôle de la charge d'essai
Étalonnage des blocs de référence à utiliser pour les machines
d'essai de dureté superficielle Rockwell (échelles 15N, 30N,
4.1.1 La charge initiale F, (voir 4.1.4) et chaque charge totale
45N, 15T, 30T et &Ti.
F utilisée (voir 4.1.5) doivent être mesurées et, chaque fois que
possible, ces mesures doivent être effectuées pour au moins
IS0 6507-1 : 1982, Matériaux métalliques - Essai de dureté - trois positions de l'équipage mobile réparties sur toute I'éten-
Essai Vickers - Partie 1 : HV 5 à HV 1 00. due de sa course.
1

---------------------- Page: 3 ----------------------
IS0 1079 : 1989 (FI
Pour cette raison, il est considéré comme nécessaire d’effec-
4.1.2 Les charges doivent être mesurées par l‘une des deux
tuer un contrôle indirect. Le comportement du pénétrateur sur
méthodes suivantes:
une machine d’étalonnage doit être comparé avec le comporte-
ment du pénétrateur propre à la machine d’étalonnage. L‘essai
a) soit à l‘aide d’un dynamomètre étalonné donnant une
doit être effectué conformément à 1‘1S0 1355.
précision de f 0.2 %,
b) soit par comparaison avec la force, précise à f 0.2 %,
Des essais doivent être effectués sur un minimum de deux
produite à l’aide de masses étalonnées avec un système
blocs dans l‘échelle 30N. le niveau de dureté du premier bloc
mécanique.
étant situé près de la limite inférieure du domaine d‘application
de cette échelle et le second près de la limite supérieure de ce
domaine. Pour chaque bloc, la dureté moyenne de trois
4.1.3 Trois lectures doivent être faites pour chaque charge et
empreintes faites avec le pénétrateur à vérifier ne doit pas diffé-
pour chaque position de l’équipage mobile. Immédiatement
rer de f 0,8 unité de dureté superficielle Rockwell de la dureté
avant chaque lecture, l’équipage mobile doit avoir été déplacé
moyenne de trois empreintes obtenue avec le pénétrateur éta-
dans le même sens qu’au cours de l‘essai.
lon. Les empreintes réalisées avec le pénétrateur à vérifier et
celles faites avec le pénétrateur étalon doivent être exécutées
4.1.4 La tolérance sur la charge initiale Fo avant application et
de façon qu‘elles soient adjacentes dans chaque cas. L’essai
après retrait de la surcharge FI doit être de f 2,O %.
doit être effectué conformément à I’ISO 1355.
4.1.5 La tolérance sur la charge totaleFdoit être de f 0.7 YO.
NOTE - Le pénétrateur étalon est le (ou les) pénétrateUr(?.) qui a (ou
-
ont) été reconnuis) comme le pénétrateur de référence sur le plan
national.
4.2 Contrôle du pénétrateur
4.2.2 Les pénétrateurs bille d’acier (échelles 15T, 30T et 45T)
4.2.1 Les pénétrateurs coniques en diamant (échelles 15N,
doivent être contrôlés selon la procédure décrite en 4.2.2.1
30N et 45N) doivent être contrôlés selon la procédure décrite en
à 4.2.2.3.
4.2.1.1 à 4.2.1.6.
4.2.2.1 Pour les besoins du contrôle de la dimension et de la
4.2.1.1 La surface du cône en diamant et de la pointe sphéri-
dureté des bille
...