ISO 21207:2015
(Main)Corrosion tests in artificial atmospheres — Accelerated corrosion tests involving alternate exposure to corrosion-promoting gases, neutral salt-spray and drying
Corrosion tests in artificial atmospheres — Accelerated corrosion tests involving alternate exposure to corrosion-promoting gases, neutral salt-spray and drying
ISO 21207:2015 defines two accelerated corrosion test methods to be used in assessing the corrosion resistance of products with metals in environments where there is a significant influence of chloride ions, mainly as sodium chloride from a marine source or by winter road de-icing salt, and of corrosion-promoting gases from industrial or traffic air pollution. ISO 21207:2015 specifies both the test apparatus and test procedures to be used in executing the accelerated corrosion tests. The methods are especially suitable for assessing the corrosion resistance of sensitive products with metals, e.g. electronic components, used in traffic and industrial environments.
Essais de corrosion en atmosphères artificielles — Essais de corrosion accélérée par expositions alternées à des gaz corrosifs ou au brouillard salin neutre et à un séchage
Ce document définit deux méthodes d’essai de corrosion accélérée à utiliser pour évaluer la résistance à la corrosion de produits contenant des métaux dans des environnements où les facteurs qui jouent un rôle significatif sont les ions chlorure, notamment sous forme de chlorure de sodium provenant d’une source marine ou des sels de déverglaçage des routes en hiver, et les gaz corrosifs résultant de la pollution industrielle ou de la circulation routière. Ce document spécifie à la fois l’appareillage et les modes opératoires d’essai à utiliser pour exécuter les essais de corrosion accélérée. Ces méthodes sont particulièrement appropriées à l’évaluation de la résistance à la corrosion des produits sensibles contenant des métaux, par exemple les composants électroniques, qui sont utilisés dans les environnements industriels et sur le réseau routier.
General Information
Relations
Buy Standard
Standards Content (Sample)
FINAL
INTERNATIONAL ISO/FDIS
DRAFT
STANDARD 21207
ISO/TC 156
Corrosion tests in artificial
Secretariat: SAC
atmospheres — Accelerated corrosion
Voting begins
on: 20150904 tests involving alternate exposure to
corrosion-promoting gases, neutral
Voting terminates
on: 20151104
salt-spray and drying
Essais de corrosion en atmosphères artificielles — Essais de corrosion
accélérée par expositions alternées à des gaz oxydants ou au
brouillard salin neutre et à un séchage
RECIPIENTS OF THIS DRAFT ARE INVITED TO
SUBMIT, WITH THEIR COMMENTS, NOTIFICATION
OF ANY RELEVANT PATENT RIGHTS OF WHICH
THEY ARE AWARE AND TO PROVIDE SUPPOR TING
DOCUMENTATION.
IN ADDITION TO THEIR EVALUATION AS
Reference number
BEING ACCEPTABLE FOR INDUSTRIAL, TECHNO
ISO/FDIS 21207:2015(E)
LOGICAL, COMMERCIAL AND USER PURPOSES,
DRAFT INTERNATIONAL STANDARDS MAY ON
OCCASION HAVE TO BE CONSIDERED IN THE
LIGHT OF THEIR POTENTIAL TO BECOME STAN
DARDS TO WHICH REFERENCE MAY BE MADE IN
©
NATIONAL REGULATIONS. ISO 2015
ISO/FDIS 21207:2015(E)
© ISO 2015, Published in Switzerland
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized otherwise in any form
or by any means, electronic or mechanical, including photocopying, or posting on the internet or an intranet, without prior
written permission. Permission can be requested from either ISO at the address below or ISO’s member body in the country of
the requester.
ISO copyright office
Ch. de Blandonnet 8 • CP 401
CH1214 Vernier, Geneva, Switzerland
Tel. +41 22 749 01 11
Fax +41 22 749 09 47
copyright@iso.org
www.iso.org
ii © ISO 2015 – All rights reserved
ISO/FDIS 21207:2015(E)
Contents Page
Foreword .iv
Introduction .v
1 Scope . 1
2 Normative references . 1
3 Apparatus and reagents . 1
4 Evaluation of the corrosivity of the tests . 2
4.1 Reference test panels . 2
4.2 Arrangement of the reference panels during testing . 3
4.3 Determination of mass loss after testing . 3
4.4 Satisfactory performance of test . 3
5 Test objects . 4
6 Procedure. 4
6.1 Test method A . 4
6.1.1 Test cycle . 4
6.1.2 Salt spray testing followed by drying (step a) . 4
6.1.3 Exposure to corrosive gases followed by drying (step b) . 5
6.1.4 Test duration . 5
6.2 Test method B . 5
6.2.1 Test cycle . 5
6.2.2 Salt spray testing followed by drying (step a or step c) . 6
6.2.3 Exposure to corrosive gases (step b or step d) . 6
6.2.4 Test duration . 6
7 Evaluation of results . 6
8 Test report . 7
Annex A (informative) Recommended test periods . 8
Bibliography . 9
ISO/FDIS 21207:2015(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and nongovernmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www.iso.org/directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www.iso.org/patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation on the meaning of ISO specific terms and expressions related to conformity
assessment, as well as information about ISO’s adherence to the WTO principles in the Technical
Barriers to Trade (TBT) see the following URL: Foreword - Supplementary information.
The committee responsible for this document is ISO/TC 156, Corrosion of metals and alloys.
This second edition cancels and replaces the first edition (ISO 21207:2004), of which it constitutes a
minor revision. It also incorporates the Technical Corrigendum ISO 21207:2004/Cor 1:2008.
iv © ISO 2015 – All rights reserved
ISO/FDIS 21207:2015(E)
Introduction
Corrosion of metallic materials with or without corrosion protection is influenced by many
environmental factors, the importance of which can vary with the type of metallic material and with
the type of environment. Laboratory tests are designed to simulate the effects of the most important
factors that enhance the corrosion of metallic materials.
The accelerated corrosion test methods described in this International Standard, methods A and B,
are designed to simulate and enhance the environmental influence of exposure to an outdoor climate
where salt-contaminated conditions and corrosion-promoting gases from an industrial or a traffic
environment occur which might promote corrosion. Test method A simulates a moderately aggressive
traffic environment while test method B simulates a more severe industrial or traffic environment.
Test method A involves exposure of the test objects to the following test cycle:
a) neutral salt spray testing (ISO 9227) for 2 h in a mist of a salt solution containing a mass fraction of
5 % of sodium chloride at 35 °C, followed by drying for 22 h in a standard laboratory climate;
b) exposure for 120 h in a test atmosphere containing a mixture of corrosionpromoting gases, volume
−6 −6
fraction of NO equal to 1,5 × 10 and of SO equal to 0,5 × 10 , at a relative humidity of 95 % and
2 2
at a temperature of 25 °C, followed by drying for 24 h in a standard laboratory climate.
Test method B involves exposure of the test object to the following test cycle:
a) neutral salt spray testing (ISO 9227) for 2 h in a mist of a sodium chloride salt solution of mass
fraction 5 % at 35 °C, followed by drying for 22 h in a standard laboratory climate;
b) exposure for 48 h in a test atmosphere containing a mixture of corrosionpromoting gases, volume
−6 −6
fraction of NO equal to 10 × 10 and of SO equal to 5 × 10 , at a relative humidity of 95 % and at
2 2
a temperature of 25 °C;
c) neutral salt spray testing (ISO 9227) for 2 h in a mist of a sodium chloride salt solution of mass
fraction 5 % at 35 °C, followed by drying for 22 h in a standard laboratory climate;
d) exposure for 72 h in a test atmosphere containing a mixture of corrosionpromoting gases, volume
−6 −6
fraction of NO equal to 10 × 10 and of SO equal to 5 × 10 , at a relative humidity of 95 % and at
2 2
a temperature of 25 °C.
The results obtained do not permit farreaching conclusions on the corrosion resistance of the tested
product under the whole range of environmental conditions in which it may be used.
FINAL DRAFT INTERNATIONAL STANDARD ISO/FDIS 21207:2015(E)
Corrosion tests in artificial atmospheres — Accelerated
corrosion tests involving alternate exposure to corrosion-
promoting gases, neutral salt-spray and drying
1 Scope
This International Standard defines two accelerated corrosion test methods to be used in assessing the
corrosion resistance of products with metals in environments where there is a significant influence of
chloride ions, mainly as sodium chloride from a marine source or by winter road de-icing salt, and of
corrosion-promoting gases from industrial or traffic air pollution.
This International Standard specifies both the test apparatus and test procedures to be used in
executing the accelerated corrosion tests.
The methods are especially suitable for assessing the corrosion resistance of sensitive products with
metals, e.g. electronic components, used in traffic and industrial environments.
2 Normative references
The following documents, in whole or in part, are normatively referenced in this document and are
indispensable for its application. For dated references, only the edition cited applies. For undated
references, the latest edition of the referenced document (including any amendments) applies.
ISO 8407, Corrosion of metals and alloys — Removal of corrosion products from corrosion test specimens
ISO 9227, Corrosion tests in artificial atmospheres — Salt spray tests
ISO 10062, Corrosion tests in artificial atmosphere at very low concentrations of polluting gas(es)
ISO 10289, Methods for corrosion testing of metallic and other inorganic coatings on metallic substrates —
Rating of test specimens and manufactured articles subjected to corrosion tests
3 Apparatus and reagents
3.1 Exposure of test objects to mixtures of NO and SO at a relative humidity of 95 % and a
2 2
temperature of 25 °C.
The climatic cabinet with inner chamber and gas flow system shall comply with the requirements
of ISO 10062.
The equipment used for testing shall be constructed for the following reasons.
a) The inner chamber and gas flow system consist of inert materials, e.g. PTFE
(polytetrafluoroethylene) or glass, to avoid or minimize adsorption of hostile gases on surfaces
other than of that of the test panels.
b) Airflow and hostile gas injection system are designed to ensure uniform test conditions in the inner
chamber or working space of cabinet.
In the most common design of test equipment, the test atmosphere in the working space is obtained
by continuously introducing the necessary quantity of the mixture of corrosion-promoting gases
into a damp airflow to obtain the required concentration. The corrosion-promoting gases and
conditioned air are mixed outside the cabinet. The conditioned air is taken from the outer chamber
of the climatic cabinet. The airflow after injection of the corrosion-promoting gases is then mixed
ISO/FDIS 21207:2015(E)
with a flow of re-circulated test atmosphere and the resulting gas flow admitt
...
INTERNATIONAL ISO
STANDARD 21207
Second edition
2015-12-15
Corrosion tests in artificial
atmospheres — Accelerated corrosion
tests involving alternate exposure to
corrosion-promoting gases, neutral
salt-spray and drying
Essais de corrosion en atmosphères artificielles — Essais de corrosion
accélérée par expositions alternées à des gaz oxydants ou au
brouillard salin neutre et à un séchage
Reference number
©
ISO 2015
© ISO 2015, Published in Switzerland
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized otherwise in any form
or by any means, electronic or mechanical, including photocopying, or posting on the internet or an intranet, without prior
written permission. Permission can be requested from either ISO at the address below or ISO’s member body in the country of
the requester.
ISO copyright office
Ch. de Blandonnet 8 • CP 401
CH-1214 Vernier, Geneva, Switzerland
Tel. +41 22 749 01 11
Fax +41 22 749 09 47
copyright@iso.org
www.iso.org
ii © ISO 2015 – All rights reserved
Contents Page
Foreword .iv
Introduction .v
1 Scope . 1
2 Normative references . 1
3 Apparatus and reagents . 1
4 Evaluation of the corrosivity of the tests . 2
4.1 Reference test panels . 2
4.2 Arrangement of the reference panels during testing . 3
4.3 Determination of mass loss after testing . 3
4.4 Satisfactory performance of test . 3
5 Test objects . 4
6 Procedure. 4
6.1 Test method A . 4
6.1.1 Test cycle . 4
6.1.2 Salt spray testing followed by drying (step a) . 4
6.1.3 Exposure to corrosive gases followed by drying (step b) . 5
6.1.4 Test duration . 5
6.2 Test method B . 5
6.2.1 Test cycle . 5
6.2.2 Salt spray testing followed by drying (step a or step c) . 6
6.2.3 Exposure to corrosive gases (step b or step d) . 6
6.2.4 Test duration . 6
7 Evaluation of results . 6
8 Test report . 7
Annex A (informative) Recommended test periods . 8
Bibliography . 9
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www.iso.org/directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www.iso.org/patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation on the meaning of ISO specific terms and expressions related to conformity
assessment, as well as information about ISO’s adherence to the WTO principles in the Technical
Barriers to Trade (TBT) see the following URL: Foreword - Supplementary information
The committee responsible for this document is ISO/TC 156, Corrosion of metals and alloys.
This second edition cancels and replaces the first edition (ISO 21207:2004), of which it constitutes a
minor revision. It also incorporates the Technical Corrigendum ISO 21207:2004/Cor 1:2008.
iv © ISO 2015 – All rights reserved
Introduction
Corrosion of metallic materials with or without corrosion protection is influenced by many
environmental factors, the importance of which can vary with the type of metallic material and with
the type of environment. Laboratory tests are designed to simulate the effects of the most important
factors that enhance the corrosion of metallic materials.
The accelerated corrosion test methods described in this International Standard, methods A and B,
are designed to simulate and enhance the environmental influence of exposure to an outdoor climate
where salt-contaminated conditions and corrosion-promoting gases from an industrial or a traffic
environment occur which might promote corrosion. Test method A simulates a moderately aggressive
traffic environment while test method B simulates a more severe industrial or traffic environment.
Test method A involves exposure of the test objects to the following test cycle:
a) neutral salt spray testing (ISO 9227) for 2 h in a mist of a sodium chloride salt solution of mass
fraction 5 % at 35 °C, followed by drying for 22 h in a standard laboratory climate;
b) exposure for 120 h in a test atmosphere containing a mixture of corrosion-promoting gases, volume
−6 −6
fraction of NO equal to 1,5 × 10 and of SO equal to 0,5 × 10 , at a relative humidity of 95 % and
2 2
at a temperature of 25 °C, followed by drying for 24 h in a standard laboratory climate.
Test method B involves exposure of the test objects to the following test cycle:
a) neutral salt spray testing (ISO 9227) for 2 h in a mist of a sodium chloride salt solution of mass
fraction 5 % at 35 °C, followed by drying for 22 h in a standard laboratory climate;
b) exposure for 48 h in a test atmosphere containing a mixture of corrosion-promoting gases, volume
−6 −6
fraction of NO equal to 10 × 10 and of SO equal to 5 × 10 , at a relative humidity of 95 % and at
2 2
a temperature of 25 °C;
c) neutral salt spray testing (ISO 9227) for 2 h in a mist of a sodium chloride salt solution of mass
fraction 5 % at 35 °C, followed by drying for 22 h in a standard laboratory climate;
d) exposure for 72 h in a test atmosphere containing a mixture of corrosion-promoting gases, volume
−6 −6
fraction of NO equal to 10 × 10 and of SO equal to 5 × 10 , at a relative humidity of 95 % and at
2 2
a temperature of 25 °C.
The results obtained do not permit far-reaching conclusions on the corrosion resistance of the tested
product under the whole range of environmental conditions in which it may be used.
INTERNATIONAL STANDARD ISO 21207:2015(E)
Corrosion tests in artificial atmospheres — Accelerated
corrosion tests involving alternate exposure to corrosion-
promoting gases, neutral salt-spray and drying
1 Scope
This International Standard defines two accelerated corrosion test methods to be used in assessing the
corrosion resistance of products with metals in environments where there is a significant influence of
chloride ions, mainly as sodium chloride from a marine source or by winter road de-icing salt, and of
corrosion-promoting gases from industrial or traffic air pollution.
This International Standard specifies both the test apparatus and test procedures to be used in
executing the accelerated corrosion tests.
The methods are especially suitable for assessing the corrosion resistance of sensitive products with
metals, e.g. electronic components, used in traffic and industrial environments.
2 Normative references
The following documents, in whole or in part, are normatively referenced in this document and are
indispensable for its application. For dated references, only the edition cited applies. For undated
references, the latest edition of the referenced document (including any amendments) applies.
ISO 8407, Corrosion of metals and alloys — Removal of corrosion products from corrosion test specimens
ISO 9227, Corrosion tests in artificial atmospheres — Salt spray tests
ISO 10062, Corrosion tests in artificial atmosphere at very low concentrations of polluting gas(es)
ISO 10289, Methods for corrosion testing of metallic and other inorganic coatings on metallic substrates —
Rating of test specimens and manufactured articles subjected to corrosion tests
3 Apparatus and reagents
3.1 Exposure of test objects to mixtures of NO and SO at a relative humidity of 95 % and a
2 2
temperature of 25 °C.
The climatic cabinet with inner chamber and gas flow system shall comply with the requirements
of ISO 10062.
The equipment used for testing shall be constructed for the following reasons.
a) The inner chamber and gas flow system consist of inert materials, e.g. PTFE
(polytetrafluoroethylene) or glass, to avoid or minimize adsorption of hostile gases on surfaces
other than of that of the test panels.
b) Airflow and hostile gas injection system are designed to ensure uniform test conditions in the inner
chamber or working space of cabinet.
In the most common design of test equipment, the test atmosphere in the working space is obtained
by continuously introducing the necessary quantity of the mixture of corrosion-promoting gases
into a damp airflow to obtain the required concentration. The corrosion-promoting gases and
conditioned air are mixed outside the cabinet. The conditioned air is taken from the outer chamber
of the climatic cabinet. The airflow after injection of the corrosion-promoting gases is then mixed
with a flow of re-circulated test atmosphere and the resulting gas flow admitted into the inner
chamber or working space of the cabinet. Half of the flow of the test atmosphere through the inner
chamber may be re-circulated.
To ensure uniform test conditions in the working space, the test atmosphere is normally supplied
to the working space from the bottom and the outlet is placed at the top. Perforated plates are
placed in front of the openings to ensure uniform airflow through the working space.
c) Uniformity of temperature in the working space shall be better than ±1 °C and uniformity of relative
humidity better than ±3 %. In terms of corrosivity, expressed as the corrosion rate of c
...
INTERNATIONAL ISO
STANDARD 21207
Second edition
2015-12-15
Corrosion tests in artificial
atmospheres — Accelerated corrosion
tests involving alternate exposure to
corrosion-promoting gases, neutral
salt-spray and drying
Essais de corrosion en atmosphères artificielles — Essais de corrosion
accélérée par expositions alternées à des gaz oxydants ou au
brouillard salin neutre et à un séchage
Reference number
©
ISO 2015
© ISO 2015, Published in Switzerland
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized otherwise in any form
or by any means, electronic or mechanical, including photocopying, or posting on the internet or an intranet, without prior
written permission. Permission can be requested from either ISO at the address below or ISO’s member body in the country of
the requester.
ISO copyright office
Ch. de Blandonnet 8 • CP 401
CH-1214 Vernier, Geneva, Switzerland
Tel. +41 22 749 01 11
Fax +41 22 749 09 47
copyright@iso.org
www.iso.org
ii © ISO 2015 – All rights reserved
Contents Page
Foreword .iv
Introduction .v
1 Scope . 1
2 Normative references . 1
3 Apparatus and reagents . 1
4 Evaluation of the corrosivity of the tests . 2
4.1 Reference test panels . 2
4.2 Arrangement of the reference panels during testing . 3
4.3 Determination of mass loss after testing . 3
4.4 Satisfactory performance of test . 3
5 Test objects . 4
6 Procedure. 4
6.1 Test method A . 4
6.1.1 Test cycle . 4
6.1.2 Salt spray testing followed by drying (step a) . 4
6.1.3 Exposure to corrosive gases followed by drying (step b) . 5
6.1.4 Test duration . 5
6.2 Test method B . 5
6.2.1 Test cycle . 5
6.2.2 Salt spray testing followed by drying (step a or step c) . 6
6.2.3 Exposure to corrosive gases (step b or step d) . 6
6.2.4 Test duration . 6
7 Evaluation of results . 6
8 Test report . 7
Annex A (informative) Recommended test periods . 8
Bibliography . 9
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www.iso.org/directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www.iso.org/patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation on the meaning of ISO specific terms and expressions related to conformity
assessment, as well as information about ISO’s adherence to the WTO principles in the Technical
Barriers to Trade (TBT) see the following URL: Foreword - Supplementary information
The committee responsible for this document is ISO/TC 156, Corrosion of metals and alloys.
This second edition cancels and replaces the first edition (ISO 21207:2004), of which it constitutes a
minor revision. It also incorporates the Technical Corrigendum ISO 21207:2004/Cor 1:2008.
iv © ISO 2015 – All rights reserved
Introduction
Corrosion of metallic materials with or without corrosion protection is influenced by many
environmental factors, the importance of which can vary with the type of metallic material and with
the type of environment. Laboratory tests are designed to simulate the effects of the most important
factors that enhance the corrosion of metallic materials.
The accelerated corrosion test methods described in this International Standard, methods A and B,
are designed to simulate and enhance the environmental influence of exposure to an outdoor climate
where salt-contaminated conditions and corrosion-promoting gases from an industrial or a traffic
environment occur which might promote corrosion. Test method A simulates a moderately aggressive
traffic environment while test method B simulates a more severe industrial or traffic environment.
Test method A involves exposure of the test objects to the following test cycle:
a) neutral salt spray testing (ISO 9227) for 2 h in a mist of a sodium chloride salt solution of mass
fraction 5 % at 35 °C, followed by drying for 22 h in a standard laboratory climate;
b) exposure for 120 h in a test atmosphere containing a mixture of corrosion-promoting gases, volume
−6 −6
fraction of NO equal to 1,5 × 10 and of SO equal to 0,5 × 10 , at a relative humidity of 95 % and
2 2
at a temperature of 25 °C, followed by drying for 24 h in a standard laboratory climate.
Test method B involves exposure of the test objects to the following test cycle:
a) neutral salt spray testing (ISO 9227) for 2 h in a mist of a sodium chloride salt solution of mass
fraction 5 % at 35 °C, followed by drying for 22 h in a standard laboratory climate;
b) exposure for 48 h in a test atmosphere containing a mixture of corrosion-promoting gases, volume
−6 −6
fraction of NO equal to 10 × 10 and of SO equal to 5 × 10 , at a relative humidity of 95 % and at
2 2
a temperature of 25 °C;
c) neutral salt spray testing (ISO 9227) for 2 h in a mist of a sodium chloride salt solution of mass
fraction 5 % at 35 °C, followed by drying for 22 h in a standard laboratory climate;
d) exposure for 72 h in a test atmosphere containing a mixture of corrosion-promoting gases, volume
−6 −6
fraction of NO equal to 10 × 10 and of SO equal to 5 × 10 , at a relative humidity of 95 % and at
2 2
a temperature of 25 °C.
The results obtained do not permit far-reaching conclusions on the corrosion resistance of the tested
product under the whole range of environmental conditions in which it may be used.
INTERNATIONAL STANDARD ISO 21207:2015(E)
Corrosion tests in artificial atmospheres — Accelerated
corrosion tests involving alternate exposure to corrosion-
promoting gases, neutral salt-spray and drying
1 Scope
This International Standard defines two accelerated corrosion test methods to be used in assessing the
corrosion resistance of products with metals in environments where there is a significant influence of
chloride ions, mainly as sodium chloride from a marine source or by winter road de-icing salt, and of
corrosion-promoting gases from industrial or traffic air pollution.
This International Standard specifies both the test apparatus and test procedures to be used in
executing the accelerated corrosion tests.
The methods are especially suitable for assessing the corrosion resistance of sensitive products with
metals, e.g. electronic components, used in traffic and industrial environments.
2 Normative references
The following documents, in whole or in part, are normatively referenced in this document and are
indispensable for its application. For dated references, only the edition cited applies. For undated
references, the latest edition of the referenced document (including any amendments) applies.
ISO 8407, Corrosion of metals and alloys — Removal of corrosion products from corrosion test specimens
ISO 9227, Corrosion tests in artificial atmospheres — Salt spray tests
ISO 10062, Corrosion tests in artificial atmosphere at very low concentrations of polluting gas(es)
ISO 10289, Methods for corrosion testing of metallic and other inorganic coatings on metallic substrates —
Rating of test specimens and manufactured articles subjected to corrosion tests
3 Apparatus and reagents
3.1 Exposure of test objects to mixtures of NO and SO at a relative humidity of 95 % and a
2 2
temperature of 25 °C.
The climatic cabinet with inner chamber and gas flow system shall comply with the requirements
of ISO 10062.
The equipment used for testing shall be constructed for the following reasons.
a) The inner chamber and gas flow system consist of inert materials, e.g. PTFE
(polytetrafluoroethylene) or glass, to avoid or minimize adsorption of hostile gases on surfaces
other than of that of the test panels.
b) Airflow and hostile gas injection system are designed to ensure uniform test conditions in the inner
chamber or working space of cabinet.
In the most common design of test equipment, the test atmosphere in the working space is obtained
by continuously introducing the necessary quantity of the mixture of corrosion-promoting gases
into a damp airflow to obtain the required concentration. The corrosion-promoting gases and
conditioned air are mixed outside the cabinet. The conditioned air is taken from the outer chamber
of the climatic cabinet. The airflow after injection of the corrosion-promoting gases is then mixed
with a flow of re-circulated test atmosphere and the resulting gas flow admitted into the inner
chamber or working space of the cabinet. Half of the flow of the test atmosphere through the inner
chamber may be re-circulated.
To ensure uniform test conditions in the working space, the test atmosphere is normally supplied
to the working space from the bottom and the outlet is placed at the top. Perforated plates are
placed in front of the openings to ensure uniform airflow through the working space.
c) Uniformity of temperature in the working space shall be better than ±1 °C and uniformity of relative
humidity better than ±3 %. In terms of corrosivity, expressed as the corrosion rate of c
...
NORME ISO
INTERNATIONALE 21207
Deuxième édition
2015-12-15
Essais de corrosion en atmosphères
artificielles — Essais de corrosion
accélérée par expositions alternées à
des gaz corrosifs ou au brouillard salin
neutre et à un séchage
Corrosion tests in artificial atmospheres — Accelerated corrosion
tests involving alternate exposure to corrosion-promoting gases,
neutral salt-spray and drying
Numéro de référence
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2015
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: +41 22 749 01 11
E-mail: copyright@iso.org
Web: www.iso.org
Publié en Suisse
ii
Sommaire Page
Avant‑propos .iv
Introduction .v
1 Domaine d’application . 1
2 Références normatives .1
3 Appareillage et réactifs . 1
4 Évaluation de la corrosivité des essais . 3
4.1 Panneaux d’essai de référence . 3
4.2 Montage des panneaux de référence pendant l’essai . 3
4.3 Détermination de la perte de masse après l’essai . 3
4.4 Bonne exécution de l’essai . 4
5 Objets en essai . 4
6 Mode opératoire . 5
6.1 Méthode d’essai A . 5
6.1.1 Cycle d’essai . 5
6.1.2 Essai au brouillard salin suivi d’un séchage (étape a) . 5
6.1.3 Exposition aux gaz corrosifs suivie d’un séchage (étape b) . 5
6.1.4 Durée de l’essai . 6
6.2 Méthode d’essai B . 6
6.2.1 Cycle d’essai . 6
6.2.2 Essai au brouillard salin suivi d’un séchage (étape a ou étape c) . 6
6.2.3 Exposition aux gaz corrosifs (étape b ou étape d) . 6
6.2.4 Durée de l’essai . 7
7 Évaluation des résultats . 7
8 Rapport d’essai . 7
Annexe A (informative) Durées d’essai recommandées . 9
Bibliographie .11
iii
Avant‑propos
L’ISO (Organisation internationale de normalisation) est une fédération mondiale d’organismes
nationaux de normalisation (comités membres de l’ISO). L’élaboration des Normes internationales est
en général confiée aux comités techniques de l’ISO. Chaque comité membre intéressé par une étude
a le droit de faire partie du comité technique créé à cet effet. Les organisations internationales,
gouvernementales et non gouvernementales, en liaison avec l’ISO participent également aux travaux.
L’ISO collabore étroitement avec la Commission électrotechnique internationale (IEC) en ce qui
concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient en particulier de prendre note des différents
critères d’approbation requis pour les différents types de documents ISO. Le présent document
a été rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2
(voir www.iso.org/directives).
L’attention est appelée sur le fait que certains des éléments du présent document peuvent faire l’objet de
droits de propriété intellectuelle ou de droits analogues. L’ISO ne saurait être tenue pour responsable
de l’identification de ces droits de propriété en tout ou partie. Les détails concernant les références aux
droits de propriété intellectuelle ou autres droits analogues identifiés lors de l’élaboration du document
sont indiqués dans l’Introduction et/ou dans la liste des déclarations de brevets reçues par l’ISO (voir
www.iso.org/brevets).
Les appellations commerciales éventuellement mentionnées dans le présent document sont données
pour information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un
engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l’ISO liés à l’évaluation de la conformité, ou pour toute information au sujet de l’adhésion
de l’ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles
techniques au commerce (OTC), voir le lien suivant : www.iso.org/iso/fr/avant-propos.
Le comité chargé de l’élaboration du présent document est l’ISO/TC 156, Corrosion des métaux et alliages.
Cette deuxième édition annule et remplace la première édition (ISO 21207:2004), dont elle constitue
une révision mineure. Elle intègre également le rectificatif technique ISO 21207:2004/Cor 1:2008.
iv
Introduction
De nombreux facteurs environnementaux influent sur la corrosion des matériaux métalliques qu’ils
soient ou non protégés contre la corrosion. L’importance de ces facteurs peut varier selon le type de
matériau métallique et le type d’environnement. Les essais en laboratoire sont conçus pour simuler les
effets des facteurs les plus importants favorisant la corrosion des matériaux métalliques.
Les méthodes A et B d’essai de corrosion accélérée, décrites dans la présente Norme internationale, sont
conçues pour simuler et mettre en valeur l’influence de l’exposition à un climat extérieur présentant
des conditions où la salinité de l’atmosphère et les gaz corrosifs provenant soit d’un environnement
industriel, soit de la circulation routière, peuvent favoriser la corrosion. La méthode A simule des
conditions de circulation modérément agressives tandis que la méthode B simule un environnement
industriel ou des conditions de trafic routier plus sévères.
La méthode A consiste à exposer les objets en essai au cycle d’essai suivant :
a) essai au brouillard salin neutre (ISO 9227) pendant 2 h avec pulvérisation d’une solution de
chlorure de sodium à 5 % (fraction massique) à 35 °C, suivi d’un séchage pendant 22 h dans une
atmosphère normale de laboratoire ;
b) exposition pendant 120 h à une atmosphère d’essai contenant un mélange de gaz corrosifs et
−6 −6
composé de NO et de SO en fractions volumiques respectivement égales à 1,5 × 10 et 0,5 × 10 ,
2 2
à une humidité relative de 95 % et à une température de 25 °C, suivie d’un séchage pendant 24 h
dans une atmosphère normale de laboratoire.
La méthode B implique d’exposer les objets en essai au cycle d’essai suivant :
a) essai au brouillard salin neutre (ISO 9227) pendant 2 h avec pulvérisation d’une solution de
chlorure de sodium à 5 % (fraction massique) à 35 °C, suivi d’un séchage pendant 22 h dans une
atmosphère normale de laboratoire ;
b) exposition pendant 48 h à une atmosphère d’essai contenant un mélange de gaz corrosifs et
−6 −6
composé de NO et de SO en fractions volumiques respectivement égales à 10 × 10 et 5 × 10 ,
2 2
à une humidité relative de 95 % et à une température de 25 °C ;
c) essai au brouillard salin neutre (ISO 9227) pendant 2 h avec pulvérisation d’une solution de
chlorure de sodium à 5 % (fraction massique) à 35 °C, suivi d’un séchage pendant 22 h dans une
atmosphère normale de laboratoire ;
d) exposition pendant 72 h à une atmosphère d’essai contenant un mélange de gaz corrosifs et
−6 −6
composé de NO et de SO en fractions volumiques respectivement égales à 10 × 10 et 5 × 10 ,
2 2
à une humidité relative de 95 % et à une température de 25 °C.
Les résultats obtenus ne permettent pas de tirer des conclusions définitives sur la résistance à la
corrosion du produit soumis à essai sur toute la gamme des conditions environnementales dans
lesquelles celui-ci est susceptible d’être utilisé.
v
NORME INTERNATIONALE ISO 21207:2015(F)
Essais de corrosion en atmosphères artificielles — Essais
de corrosion accélérée par expositions alternées à des gaz
corrosifs ou au brouillard salin neutre et à un séchage
1 Domaine d’application
La présente Norme internationale définit deux méthodes d’essai de corrosion accélérée à utiliser pour
évaluer la résistance à la corrosion de produits contenant des métaux dans des environnements où
les facteurs qui jouent un rôle significatif sont les ions chlorure, notamment sous forme de chlorure
de sodium provenant d’une source marine ou des sels de déverglaçage des routes en hiver, et les gaz
corrosifs résultant de la pollution industrielle ou de la circulation routière.
La présente Norme internationale spécifie à la fois l’appareillage et les modes opératoires d’essai
à utiliser pour exécuter les essais de corrosion accélérée.
Ces méthodes sont particulièrement appropriées à l’évaluation de la résistance à la corrosion des
produits sensibles contenant des métaux, par exemple les composants électroniques, qui sont utilisés
dans les environnements industriels et sur le réseau routier.
2 Références normatives
Les documents suivants sont cités dans le texte de sorte qu’ils constituent, pour tout ou partie de leur
contenu, des exigences du présent document. Pour les références datées, seule l’édition citée s’applique.
Pour les références non datées, la dernière édition du document de référence s’applique (y compris les
éventuels amendements).
ISO 8407, Corrosion des métaux et alliages — Élimination des produits de corrosion sur les éprouvettes
d'essai de corrosion
ISO 9227, Essais de corrosion en atmosphères artificielles — Essais aux brouillards salins
ISO 10062, Corrosion des métaux et alliages — Essais de corrosion en atmosphère artificielle à très faible
concentration en gaz polluants
ISO 10289, Méthodes d'essai de corrosion des revêtements métalliques et inorganiques sur substrats
métalliques — Cotation des éprouvettes et des articles manufacturés soumis aux essais de corrosion
3 Appareillage et réactifs
3.1 Exposition des objets en essai à des mélanges de NO et SO à une humidité relative de
2 2
95 % et une température de 25 °C
L’enceinte climatique avec chambre intérieure et le système de circulation de gaz doivent être conformes
aux exigences de l’ISO 10062.
L’équipement utilisé pour les essais doit être construit de la manière suivante :
a) la chambre intérieure et le système de circulation de gaz doivent être fabriqués en matériaux
inertes, par exemple du PTFE (polytétrafluoroéthylène) ou du verre, pour éviter ou réduire le plus
possible l’adsorption des gaz corrosifs sur des surfaces autres que celles des panneaux d’essai ;
b) le système de circulation d’air et d’injection de gaz corrosif doit être conçu d
...
ISO/TC 156
Date : 2015-12-15
ISO/TC 156
2015-12-15
Secrétariat : SAC
Essais de corrosion en atmosphères artificielles — Essais de corrosion accélérée
par expositions alternées à des gaz corrosifs ou au brouillard salin neutre et à un
séchage
Corrosion tests in artificial atmospheres— Accelerated corrosion tests involving alternate
exposure to corrosion-promoting gases, neutral salt-spray and drying
ICS : 77.060
Type du document : Norme internationale
Sous-type du document :
Stade du document : (60) Publication
Langue du document : F
NORME INTERNATIONALE ISO 21207:2015(F)
ii
Type du document : Norme internationale
Sous-type du document :
Stade du document : (60) Publication
Langue du document : F
NORME INTERNATIONALE ISO 21207:2015(F)
DOCUMENT PROTÉGÉ PAR COPYRIGHT
Droits de reproduction réservés. Sauf indication contraire, aucune partie de cette publication ne
peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique
ou mécanique, y compris la photocopie, l’affichage sur l’internet ou sur un Intranet, sans
autorisation écrite préalable. Les demandes d’autorisation peuvent être adressées à l’ISO à
l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Ch. de Blandonnet 8 •• CP 401
CH-1214 Vernier, Geneva, Switzerland
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
copyright@iso.org
www.iso.org
www.iso.org
Publié en Suisse
iii© ISO 2015 – Tous droits réservés
Sommaire Page
Avant-propos. iv
Introduction . v
1 Domaine d’application . 1
2 Références normatives . 1
3 Appareillage et réactifs . 1
4 Évaluation de la corrosivité des essais . 3
4.1 Panneaux d’essai de référence . 3
4.2 Montage des panneaux de référence pendant l’essai . 3
4.3 Détermination de la perte de masse après l’essai . 4
4.4 Bonne exécution de l’essai . 4
5 objets en essai . 5
6 Mode opératoire . 5
6.1 Méthode d’essai A . 5
6.1.1 Cycle d’essai . 5
6.1.2 Essai au brouillard salin suivi d’un séchage (étape a) . 5
6.1.3 Exposition aux gaz corrosifs suivie d’un séchage (étape b) . 6
6.1.4 Durée de l’essai . 6
6.2 Méthode d’essai B . 6
6.2.1 Cycle d’essai . 6
6.2.2 Essai au brouillard salin suivi d’un séchage (étape a ou étape c) . 7
6.2.3 Exposition aux gaz corrosifs (étape b ou étape d) . 7
6.2.4 Durée de l’essai . 8
7 Évaluation des résultats . 8
8 Rapport d’essai . 8
Annexe A (informative) Durées d’essai recommandées . 10
Bibliographie . 12
Avant-propos. iv
Introduction . v
1 Domaine d’application . 1
2 Références normatives . 1
3 Appareillage et réactifs . 2
4 Évaluation de la corrosivité des essais . 3
4.1 Panneaux d’essai de référence . 3
4.2 Montage des panneaux de référence pendant l’essai . 4
4.3 Détermination de la perte de masse après l’essai . 4
4.4 Bonne exécution de l’essai . 4
4iv © ISO 2015 – Tous droits réservés
5 Objets en essai . 5
6 Mode opératoire. 5
6.1 Méthode d’essai A . 5
6.1.1 Cycle d’essai . 5
6.1.2 Essai au brouillard salin suivi d’un séchage (étape a) . 6
6.1.3 Exposition aux gaz corrosifs suivie d’un séchage (étape b) . 6
6.1.4 Durée de l’essai . 6
6.2 Méthode d’essai B . 7
6.2.1 Cycle d’essai . 7
6.2.2 Essai au brouillard salin suivi d’un séchage (étape a ou étape c) . 7
6.2.3 Exposition aux gaz corrosifs (étape b ou étape d) . 7
6.2.4 Durée de l’essai . 8
7 Évaluation des résultats . 8
8 Rapport d’essai . 9
Annexe A (informative) Durées d’essai recommandées . 10
Bibliographie . 12
Avant-propos
L’ISO (Organisation internationale de normalisation) est une fédération mondiale d’organismes
nationaux de normalisation (comités membres de l’ISO). L’élaboration des Normes internationales est
en général confiée aux comités techniques de l’ISO. Chaque comité membre intéressé par une étude a le
droit de faire partie du comité technique créé à cet effet. Les organisations internationales,
gouvernementales et non gouvernementales, en liaison avec l’ISO participent également aux travaux.
L’ISO collabore étroitement avec la Commission électrotechnique internationale (IEC) en ce qui
concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient en particulier de prendre note des différents
critères d’approbation requis pour les différents types de documents ISO. Le présent document a été
rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2
(voir www.iso.org/directives). www.iso.org/directives).
L’attention est appelée sur le fait que certains des éléments du présent document peuvent faire l’objet
de droits de propriété intellectuelle ou de droits analogues. L’ISO ne saurait être tenue pour
responsable de l’identification de ces droits de propriété en tout ou partie. Les détails concernant les
références aux droits de propriété intellectuelle ou autres droits analogues identifiés lors de
l’élaboration du document sont indiqués dans l’Introduction et/ou dans la liste des déclarations de
brevets reçues par l’ISO (voir www.iso.org/brevets). www.iso.org/brevets).
Les appellations commerciales éventuellement mentionnées dans le présent document sont données
pour information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un
engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l’ISO liés à l’évaluation de la conformité, ou pour toute information au sujet de l’adhésion
de l’ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles
techniques au commerce (OTC), voir le lien suivant :
www.iso.org/iso/fr/avant-proposwww.iso.org/iso/fr/avant-propos.
Le comité chargé de l’élaboration du présent document est l’ISO/TC 156, Corrosion des métaux
et alliages.
Cette deuxième édition annule et remplace la première édition (ISO 21207:2004), dont elle constitue
une révision mineure. Elle intègre également le rectificatif technique ISO 21207:2004/Cor 1:2008.
6vi © ISO 2015 – Tous droits réservés
Introduction
De nombreux facteurs environnementaux influent sur la corrosion des matériaux métalliques qu’ils
soient ou non protégés contre la corrosion. L’importance de ces facteurs peut varier selon le type de
matériau métallique et le type d’environnement. Les essais en laboratoire sont conçus pour simuler les
effets des facteurs les plus importants favorisant la corrosion des matériaux métalliques.
Les méthodes A et B d’essai de corrosion accélérée, décrites dans la présente Norme internationale,
sont conçues pour simuler et mettre en valeur l’influence de l’exposition à un climat extérieur
présentant des conditions où la salinité de l’atmosphère et les gaz corrosifs provenant soit d’un
environnement industriel, soit de la circulation routière, peuvent favoriser la corrosion. La méthode A
simule des conditions de circulation modérément agressives tandis que la méthode B simule un
environnement industriel ou des conditions de trafic routier plus sévères.
La méthode A consiste à exposer les objets en essai au cycle d’essai suivant :
a) essai au brouillard salin neutre (ISO 9227) pendant 2 h avec pulvérisation d’une solution de
chlorure de sodium à 5 % (fraction massique) à 35 °C, suivi d’un séchage pendant 22 h dans une
atmosphère normale de laboratoire ;
b) exposition pendant 120 h à une atmosphère d’essai contenant un mélange de gaz corrosifs et
−6 −6
composé de NO et de SO en fractions volumiques respectivement égales à 1,5 × 10 et 0,5 × 10 ,
2 2
à une humidité relative de 95 % et à une température de 25 °C, suivie d’un séchage pendant 24 h
dans une atmosphère normale de laboratoire.
La méthode B implique d’exposer les objets en essai au cycle d’essai suivant :
a) essai au brouillard salin neutre (ISO 9227) pendant 2 h avec pulvérisation d’une solution de
chlorure de sodium à 5 % (fraction massique) à 35 °C, suivi d’un séchage pendant 22 h dans une
atmosphère normale de laboratoire ;
b) exposition pendant 48 h à une atmosphère d’essai contenant un mél
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.