ISO 16834:2025
(Main)Welding consumables — Wire electrodes, wires, rods and deposits for gas shielded arc welding of high strength steels — Classification
Welding consumables — Wire electrodes, wires, rods and deposits for gas shielded arc welding of high strength steels — Classification
This document specifies requirements for classification of wire electrodes, wires, rods and all-weld metal deposits in the as-welded condition and in the post-weld heat-treated (PWHT) condition for gas shielded metal arc welding and tungsten inert-gas welding of high-strength steels with a minimum yield strength greater than 500 MPa, or a minimum tensile strength greater than 570 MPa. One wire electrode can be tested and classified with different shielding gases. This document is a combined specification providing for classification utilizing a system based upon the yield strength and the average impact energy of 47 J of all-weld metal, or utilizing a system based upon the tensile strength and the average impact energy of 27 J of all-weld metal. a) Clauses, subclauses and tables which carry the suffix “System A” are applicable only to wire electrodes, wires, rods and deposits classified according to the system based upon the yield strength and the average impact energy of 47 J of all-weld metal under this document. b) Clauses, subclauses and tables which carry the suffix “System B” are applicable only to wire electrodes, wires, rods and deposits classified according to the system based upon the tensile strength and the average impact energy of 27 J of all-weld metal under this document. c) Clauses, subclauses and tables which do not have either the suffix “System A” or “System B” are applicable to all wire electrodes, wires, rods and deposits classified under this document. Annex A gives information on the description of composition designations for electrodes in the classification system based upon tensile strength and average impact energy of 27 J – System B.
Produits consommables pour le soudage — Fils-électrodes, fils, baguettes et dépôts pour le soudage à l'arc sous flux gazeux des aciers à haute résistance — Classification
This document specifies requirements for classification of wire electrodes, wires, rods and all-weld metal deposits in the as-welded condition and in the post-weld heat-treated (PWHT) condition for gas shielded metal arc welding and tungsten inert-gas welding of high-strength steels with a minimum yield strength greater than 500 MPa, or a minimum tensile strength greater than 570 MPa. One wire electrode can be tested and classified with different shielding gases. This document is a combined specification providing for classification utilizing a system based upon the yield strength and the average impact energy of 47 J of all-weld metal, or utilizing a system based upon the tensile strength and the average impact energy of 27 J of all-weld metal. a) Clauses, subclauses and tables which carry the suffix “System A” are applicable only to wire electrodes, wires, rods and deposits classified according to the system based upon the yield strength and the average impact energy of 47 J of all-weld metal under this document. b) Clauses, subclauses and tables which carry the suffix “System B” are applicable only to wire electrodes, wires, rods and deposits classified according to the system based upon the tensile strength and the average impact energy of 27 J of all-weld metal under this document. c) Clauses, subclauses and tables which do not have either the suffix “System A” or “System B” are applicable to all wire electrodes, wires, rods and deposits classified under this document. Annex A gives information on the description of composition designations for electrodes in the classification system based upon tensile strength and average impact energy of 27 J – System B.
General Information
Relations
Buy Standard
Standards Content (Sample)
International
Standard
ISO 16834
Third edition
Welding consumables — Wire
2025-02
electrodes, wires, rods and deposits
for gas shielded arc welding of high
strength steels — Classification
Produits consommables pour le soudage — Fils-électrodes, fils,
baguettes et dépôts pour le soudage à l'arc sous flux gazeux des
aciers à haute résistance — Classification
Reference number
© ISO 2025
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting on
the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address below
or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: +41 22 749 01 11
Email: copyright@iso.org
Website: www.iso.org
Published in Switzerland
ii
Contents Page
Foreword .iv
Introduction .v
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 2
4 Classification . 2
4.1 General .2
4.2 Classification systems .2
5 Symbols and requirements . 3
5.1 Symbols for the product/process .3
5.2 Symbols for strength and elongation properties of all-weld metal .3
5.2.1 Classification by yield strength and 47 J impact energy – System A .3
5.2.2 Classification by tensile strength and 27 J impact energy – System B .3
5.3 Symbol for impact properties of all-weld metal .3
5.3.1 Classification by yield strength and 47 J impact energy – System A .3
5.3.2 Classification by tensile strength and 27 J impact energy – System B .4
5.4 Symbol for shielding gas .4
5.5 Symbol for the chemical composition of wire electrodes, wires and rods .5
5.6 Symbol for condition of post-weld heat treatment .5
5.6.1 Classification by yield strength and 47 J impact energy – System A .5
5.6.2 Classification by tensile strength and 27 J impact energy – System B .5
6 Mechanical tests .10
7 Preheating and interpass temperatures .10
8 Welding conditions and pass sequence .10
8.1 General .10
8.2 Post-weld heat-treated condition .11
8.2.1 Classification by yield strength and 47 J impact energy – System A .11
8.2.2 Classification by tensile strength and 27 J impact energy – System B .11
9 Chemical analysis . .11
10 Rounding procedure .11
11 Retest.12
12 Technical delivery conditions .12
13 Examples of designation .12
13.1 General . 12
13.2 Example 1 – Classification by yield strength and 47 J impact energy – System A . 12
13.3 Example 2 - Classification by tensile strength and 27 J impact energy – System B . 13
13.4 Example 3 – Classification by yield strength and 47 J impact energy – System A . 13
13.5 Example 4 - Classification by tensile strength and 27 J impact energy – System B . 13
13.6 Example 5 - Classification by yield strength and 47 J impact energy – System A .14
13.7 Example 6 – Classification by tensile strength and 27 J impact energy – System B .14
Annex A (informative) Description of composition designations for electrodes in the
classification system based upon tensile strength and average impact energy of 27 J –
System B .16
Bibliography . 17
iii
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out through
ISO technical committees. Each member body interested in a subject for which a technical committee
has been established has the right to be represented on that committee. International organizations,
governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely
with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are described
in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the different types
of ISO document should be noted. This document was drafted in accordance with the editorial rules of the
ISO/IEC Directives, Part 2 (see www.iso.org/directives).
ISO draws attention to the possibility that the implementation of this document may involve the use of (a)
patent(s). ISO takes no position concerning the evidence, validity or applicability of any claimed patent
rights in respect thereof. As of the date of publication of this document, ISO had not received notice of (a)
patent(s) which may be required to implement this document. However, implementers are cautioned that
this may not represent the latest information, which may be obtained from the patent database available at
www.iso.org/patents. ISO shall not be held responsible for identifying any or all such patent rights.
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and expressions
related to conformity assessment, as well as information about ISO's adherence to the World Trade
Organization (WTO) principles in the Technical Barriers to Trade (TBT), see www.iso.org/iso/foreword.html.
This document was prepared by Technical Committee ISO/TC 44, Welding and allied processes, Subcommittee
SC 3, Welding consumables, in collaboration with the European Committee for Standardization (CEN)
Technical Committee CEN/TC 121, Welding and allied processes, in accordance with the Agreement on
technical cooperation between ISO and CEN (Vienna Agreement).
This third edition cancels and replaces the second edition (ISO 16834:2012), which has been technically
revised.
The main changes are as follows:
— document has been reformatted in single column showing System A and System B in tables and separate
clauses and subclauses, some which are new;
— In Clause 4, clarification that System A and System B are independent of each other and can produce
different results;
— Table 2 – addition of a new system A symbol 96 for strength and elongation properties of all weld metal;
— Table 3 - addition of new symbols 7 and 8 for impact properties of all-weld metal;
— Table 4 – some classifications have been revised and new classifications, N2M31, N2CM2, N3CM2, N4CM3,
N6C1M41 have been added, and footnotes have been revised;
— Tables 5, 7 and 8 – content has been added to the table and has been revised;
— Clause 13 has been updated to reflect changes.
Any feedback or questions on this document should be directed to the user’s
national standards body. A complete listing of these bodies can be found at
www.iso.org/members.html. Official interpretations of ISO/TC 44 documents, where they exist, are
available from this page: https://committee.iso.org/sites/tc44/home/interpretation.html.
iv
Introduction
This document recognizes that there are two somewhat different approaches in the global market to
classifying a given wire electrode, wire, rod or deposit, and allows for either or both to be used to suit a
particular market need. Application of either type of classification designation (or of both where suitable)
identifies a product as classified in accordance with this document.
The classification in accordance with system A was originally based on EN 12534:1999 which has been
withdrawn and replaced by this document. The classification in accordance with system B is mainly based
upon standards used around the Pacific Rim. Future revisions will aim to merge the two systems into a
single classification system.
This document provides a classification for the designation of wire electrodes, wires, rods and deposits in
terms of their chemical composition and, where required, in terms of the yield strength, tensile strength
and elongation of the all-weld metal. The ratio of yield to tensile strength of weld metal is generally higher
than that of the parent metal. Users should note that matching weld metal yield strength to parent metal
yield strength does not necessarily ensure that the weld metal tensile strength matches that of the parent
material. Thus, where the application requires matching tensile strength, selection of the consumable should
be made by reference to Table 2 System A or System B, as appropriate.
v
International Standard ISO 16834:2025(en)
Welding consumables — Wire electrodes, wires, rods and
deposits for gas shielded arc welding of high strength steels
— Classification
1 Scope
This document specifies requirements for classification of wire electrodes, wires, rods and all-weld metal
deposits in the as-welded condition and in the post-weld heat-treated (PWHT) condition for gas shielded
metal arc welding and tungsten inert-gas welding of high-strengt
...
Norme
internationale
ISO 16834
Troisième édition
Produits consommables pour le
2025-02
soudage — Fils-électrodes, fils,
baguettes et dépôts pour le soudage
à l'arc sous flux gazeux des aciers à
haute résistance — Classification
Welding consumables — Wire electrodes, wires, rods and
deposits for gas shielded arc welding of high strength steels —
Classification
Numéro de référence
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2025
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: +41 22 749 01 11
E-mail: copyright@iso.org
Web: www.iso.org
Publié en Suisse
ii
Sommaire Page
Avant-propos .v
Introduction .vii
1 Domaine d'application . 1
2 Références normatives . 1
3 Termes et définitions . 2
4 Classification . 2
4.1 Généralités .2
4.2 Systèmes de classification .2
5 Symboles et exigences . 3
5.1 Symboles pour le produit/procédé .3
5.2 Symboles des caractéristiques de résistance et d’allongement du métal fondu hors
dilution .3
5.2.1 Classification d’après la limite d’élasticité et l’énergie de rupture de 47 J –
Système A .3
5.2.2 Classification d’après la résistance à la traction et l’énergie de rupture de 27 J –
Système B .3
5.3 Symbole pour la résistance à la flexion par choc du métal fondu hors dilution .4
5.3.1 Classification d’après la limite d’élasticité et l’énergie de rupture de 47 J –
Système A .4
5.3.2 Classification d’après la résistance à la traction et l’énergie de rupture de 27 J –
Système B .4
5.4 Symbole pour le gaz de protection .5
5.5 Symbole pour la composition chimique des fil-électrodes, fils et baguettes .5
5.6 Symbole pour l’état de traitement thermique après soudage .5
5.6.1 Classification d’après la limite d’élasticité et l’énergie de rupture de 47 J –
Système A .5
5.6.2 Classification d’après la résistance à la traction et l’énergie de rupture de 27 J –
Système B .6
6 Essais mécaniques . .10
7 Températures de préchauffage et entre passes . 10
8 Conditions de soudage et séquence des passes . 10
8.1 Généralités .10
8.2 État de traitement thermique après soudage .11
8.2.1 Classification d’après la limite d’élasticité et l’énergie de rupture de 47 J –
Système A .11
8.2.2 Classification d’après la résistance à la traction et l’énergie de rupture de 27 J –
Système B .11
9 Analyse chimique .11
10 Mode opératoire d’arrondissage.12
11 Contre-essai .12
12 Conditions techniques de livraison .12
13 Exemples de désignation .12
13.1 Généralités . 12
13.2 Exemple 1 – Classification d’après la limite d’élasticité et l’énergie de rupture de 47J –
Système A . 12
13.3 Exemple 2 - Classification d’après la résistance à la traction et l’énergie de rupture de
27 J – Système B . 13
13.4 Exemple 3 – Classification d’après la limite d’élasticité et l’énergie de rupture de 47 J –
Système A . 13
iii
13.5 Exemple 4 - Classification d’après la résistance à la traction et l’énergie de rupture de
27 J – Système B .14
13.6 Exemple 5 – Classification d’après la limite d’élasticité et l’énergie de rupture de 47 J –
Système A .14
13.7 Exemple 6 - Classification d’après la résistance à la traction et l’énergie de rupture de
27 J – Système B . 15
Annexe A (informative) Description des désignations de composition pour les électrodes dans
le système de classification basé sur la résistance à la traction et l’énergie de rupture
minimale de 27 J – Système B .16
Bibliographie . 17
iv
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes nationaux
de normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est en général
confiée aux comités techniques de l'ISO. Chaque comité membre intéressé par une étude a le droit de faire
partie du comité technique créé à cet effet. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec l'ISO participent également aux travaux. L'ISO collabore étroitement avec
la Commission électrotechnique internationale (IEC) en ce qui concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier, de prendre note des différents
critères d'approbation requis pour les différents types de documents ISO. Le présent document a
été rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir
www.iso.org/directives).
L’ISO attire l’attention sur le fait que la mise en application du présent document peut entraîner l’utilisation
d’un ou de plusieurs brevets. L’ISO ne prend pas position quant à la preuve, à la validité et à l’applicabilité de
tout droit de propriété revendiqué à cet égard. À la date de publication du présent document, l’ISO n'avait pas
reçu notification qu’un ou plusieurs brevets pouvaient être nécessaires à sa mise en application. Toutefois,
il y a lieu d’avertir les responsables de la mise en application du présent document que des informations
plus récentes sont susceptibles de figurer dans la base de données de brevets, disponible à l'adresse
www.iso.org/brevets. L’ISO ne saurait être tenue pour responsable de ne pas avoir identifié tout ou partie de
tels droits de propriété.
Les appellations commerciales éventuellement mentionnées dans le présent document sont données pour
information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l'ISO liés à l'évaluation de la conformité, ou pour toute information au sujet de l'adhésion de
l'ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles techniques au
commerce (OTC), voir www.iso.org/avant-propos.
Le présent document a été élaboré par le comité technique ISO/TC 44, Soudage et techniques connexes, Sous-
comité SC 3, Produits consommables pour le soudage, en collaboration avec le Comité Technique CEN/TC 121,
Soudage et techniques connexes, du Comité européen de normalisation (CEN) conformément à l’Accord de
coopération technique entre l’ISO et le CEN (Accord de Vienne).
Cette troisième édition annule et remplace la deuxième édition (ISO 16834:2012), qui a fait l’objet d’une
révision technique.
Les principales modifications sont les suivantes:
— le document a été reformaté en une seule colonne montrant le Système A et le Système B dans les tableaux
et des articles et paragraphes séparés, dont certains sont nouveaux;
— dans l'Article 4, clarificat
...
Questions, Comments and Discussion