ISO 10893-10:2011
(Main)Non-destructive testing of steel tubes — Part 10: Automated full peripheral ultrasonic testing of seamless and welded (except submerged arc-welded) steel tubes for the detection of longitudinal and/or transverse imperfections
Non-destructive testing of steel tubes — Part 10: Automated full peripheral ultrasonic testing of seamless and welded (except submerged arc-welded) steel tubes for the detection of longitudinal and/or transverse imperfections
ISO 10893-10:2011 specifies requirements for automated full peripheral ultrasonic shear wave (generated by conventional or phased array technique) testing of seamless and welded [except submerged arc-welded (SAW)] steel tubes, for the detection of longitudinal and/or transverse imperfections. In the case of testing on longitudinal imperfections, Lamb wave testing can be applied at the discretion of the manufacturer. For seamless tubes, by agreement between the purchaser and manufacturer, testing principles of ISO 10893-10:2011 can be applied to detect imperfections having other orientations. ISO 10893-10:2011 is applicable to the inspection of tubes with an outside diameter greater than or equal to 10 mm, normally with an outside diameter-to-thickness ratio greater than or equal to 5. It can also be applicable to the testing of circular hollow sections.
Essais non destructifs des tubes en acier — Partie 10: Contrôle automatisé par ultrasons sur toute la circonférence des tubes en acier sans soudure et soudés (sauf à l'arc immergé sous flux en poudre) pour la détection des imperfections longitudinales et/ou transversales
L'ISO 10893-10:2011 spécifie les exigences relatives au contrôle automatisé par ultrasons, avec ondes de cisaillement (générées par une technique conventionnelle ou la technique des réseaux à commande de phase), sur toute la circonférence des tubes en acier sans soudure et soudés [sauf à l'arc immergé sous flux en poudre (SAW)], pour la détection des imperfections longitudinales et/ou transversales. Dans le cas du contrôle d'imperfections longitudinales, un contrôle par ondes de Lamb peut être appliqué au choix du producteur. Pour les tubes sans soudure, par accord entre l'acheteur et le producteur, les principes de contrôle de l'ISO 10893-10:2011 peuvent être appliqués pour détecter des imperfections ayant d'autres orientations. L'ISO 10893-10:2011 s'applique au contrôle des tubes ayant un diamètre extérieur supérieur ou égal à 10 mm et, normalement, un rapport diamètre extérieur/épaisseur supérieur ou égal à 5. Elle est également applicable au contrôle des profils creux circulaires.
General Information
Relations
Standards Content (Sample)
INTERNATIONAL ISO
STANDARD 10893-10
First edition
2011-04-01
Non-destructive testing of steel tubes —
Part 10:
Automated full peripheral ultrasonic
testing of seamless and welded (except
submerged arc-welded) steel tubes for
the detection of longitudinal and/or
transverse imperfections
Essais non destructifs des tubes en acier —
Partie 10: Contrôle automatisé par ultrasons sur toute la circonférence
des tubes en acier sans soudure et soudés (sauf à l'arc immergé sous
flux en poudre) pour la détection des imperfections longitudinales et/ou
transversales
Reference number
ISO 10893-10:2011(E)
©
ISO 2011
---------------------- Page: 1 ----------------------
ISO 10893-10:2011(E)
PDF disclaimer
This PDF file may contain embedded typefaces. In accordance with Adobe's licensing policy, this file may be printed or viewed but
shall not be edited unless the typefaces which are embedded are licensed to and installed on the computer performing the editing. In
downloading this file, parties accept therein the responsibility of not infringing Adobe's licensing policy. The ISO Central Secretariat
accepts no liability in this area.
Adobe is a trademark of Adobe Systems Incorporated.
Details of the software products used to create this PDF file can be found in the General Info relative to the file; the PDF-creation
parameters were optimized for printing. Every care has been taken to ensure that the file is suitable for use by ISO member bodies. In
the unlikely event that a problem relating to it is found, please inform the Central Secretariat at the address given below.
COPYRIGHT PROTECTED DOCUMENT
© ISO 2011
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means,
electronic or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address below or
ISO's member body in the country of the requester.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail copyright@iso.org
Web www.iso.org
Published in Switzerland
ii © ISO 2011 – All rights reserved
---------------------- Page: 2 ----------------------
ISO 10893-10:2011(E)
Contents Page
Foreword .iv
1 Scope.1
2 Normative references.1
3 Terms and definitions .2
4 General requirements .3
5 Test method .3
6 Reference tube.4
6.1 General .4
6.2 Types of reference notches.4
6.3 Dimensions of reference notches.5
7 Equipment calibration and checking.6
7.1 General .6
7.2 Adjustment of trigger/alarm level .6
7.3 Calibration check and recalibration .7
8 Acceptance .7
9 Test report.8
Annex A (normative) Testing on longitudinal imperfections of tubes with a ratio of the specified
outside diameter to the average of the specified thickness range less than 5 .9
Annex B (normative) Manual/semi-automated testing of untested ends and suspect areas .11
© ISO 2011 – All rights reserved iii
---------------------- Page: 3 ----------------------
ISO 10893-10:2011(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies
(ISO member bodies). The work of preparing International Standards is normally carried out through ISO
technical committees. Each member body interested in a subject for which a technical committee has been
established has the right to be represented on that committee. International organizations, governmental and
non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the
International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2.
The main task of technical committees is to prepare International Standards. Draft International Standards
adopted by the technical committees are circulated to the member bodies for voting. Publication as an
International Standard requires approval by at least 75 % of the member bodies casting a vote.
Attention is drawn to the possibility that some of the elements of this document may be the subject of patent
rights. ISO shall not be held responsible for identifying any or all such patent rights.
ISO 10893-10 was prepared by Technical Committee ISO/TC 17, Steel, Subcommittee SC 19, Technical
delivery conditions for steel tubes for pressure purposes.
This first edition cancels and replaces ISO 9303:1989 and ISO 9305:1989, which have been technically
revised.
ISO 10893 consists of the following parts, under the general title Non-destructive testing of steel tubes:
⎯ Part 1: Automated electromagnetic testing of seamless and welded (except submerged arc-welded) steel
tubes for the verification of hydraulic leaktightness
⎯ Part 2: Automated eddy current testing of seamless and welded (except submerged arc-welded) steel
tubes for the detection of imperfections
⎯ Part 3: Automated full peripheral flux leakage testing of seamless and welded (except submerged
arc-welded) ferromagnetic steel tubes for the detection of longitudinal and/or transverse imperfections
⎯ Part 4: Liquid penetrant inspection of seamless and welded steel tubes for the detection of surface
imperfections
⎯ Part 5: Magnetic particle inspection of seamless and welded ferromagnetic steel tubes for the detection of
surface imperfections
⎯ Part 6: Radiographic testing of the weld seam of welded steel tubes for the detection of imperfections
⎯ Part 7: Digital radiographic testing of the weld seam of welded steel tubes for the detection of
imperfections
⎯ Part 8: Automated ultrasonic testing of seamless and welded steel tubes for the detection of laminar
imperfections
⎯ Part 9: Automated ultrasonic testing for the detection of laminar imperfections in strip/plate used for the
manufacture of welded steel tubes
⎯ Part 10: Automated full peripheral ultrasonic testing of seamless and welded (except submerged
arc-welded) steel tubes for the detection of longitudinal and/or transverse imperfections
iv © ISO 2011 – All rights reserved
---------------------- Page: 4 ----------------------
ISO 10893-10:2011(E)
⎯ Part 11: Automated ultrasonic testing of the weld seam of welded steel tubes for the detection of
longitudinal and/or transverse imperfections
⎯ Part 12: Automated full peripheral ultrasonic thickness testing of seamless and welded (except
submerged arc-welded) steel tubes
© ISO 2011 – All rights reserved v
---------------------- Page: 5 ----------------------
INTERNATIONAL STANDARD ISO 10893-10:2011(E)
Non-destructive testing of steel tubes —
Part 10:
Automated full peripheral ultrasonic testing of seamless
and welded (except submerged arc-welded) steel tubes
for the detection of longitudinal and/or transverse imperfections
1 Scope
This part of ISO 10893 specifies requirements for automated full peripheral ultrasonic shear wave (generated
by conventional or phased array technique) testing of seamless and welded [except submerged arc-welded
(SAW)] steel tubes, for the detection of longitudinal and/or transverse imperfections.
Unless otherwise specified in the purchase order, the testing method is applicable to the detection of
predominantly longitudinal imperfections.
In the case of testing on longitudinal imperfections, Lamb wave testing can be applied at the discretion of the
manufacturer.
For seamless tubes, by agreement between the purchaser and manufacturer, testing principles of this part of
ISO 10893 can be applied to detect imperfections having other orientations.
This part of ISO 10893 is applicable to the inspection of tubes with an outside diameter greater than or equal
to 10 mm, normally with an outside diameter-to-thickness ratio greater than or equal to 5.
This part of ISO 10893 can also be applicable to the testing of circular hollow sections.
NOTE For options for testing tubes with an outside diameter-to-thickness ratio less than 5 on longitudinal
imperfections, see Annex A.
2 Normative references
The following referenced documents are indispensable for the application of this document. For dated
references, only the edition cited applies. For undated references, the latest edition of the referenced
document (including any amendments) applies.
ISO 5577, Non-destructive testing — Ultrasonic inspection — Vocabulary
ISO 9712, Non-destructive testing — Qualification and certification of personnel
ISO 11484, Steel products — Employer's qualification system for non-destructive testing (NDT) personnel
© ISO 2011 – All rights reserved 1
---------------------- Page: 6 ----------------------
ISO 10893-10:2011(E)
3 Terms and definitions
For the purposes of this document, the terms and definitions given in ISO 5577 and ISO 11484 and the
following apply.
3.1
reference standard
standard for the calibration of non-destructive testing equipment (e.g. drill holes, notches, recesses)
3.2
reference tube
tube or length of tube containing the reference standard(s)
3.3
reference sample
sample (e.g. segment of tube, plate or strip) containing the reference standard(s)
NOTE Only the term “reference tube” is used in this part of ISO 10893, also covering the term “reference sample”.
3.4
tube
hollow long product open at both ends, of any cross-sectional shape
3.5
seamless tube
tube made by piercing a solid product to obtain a tube hollow, which is further processed, either hot or cold,
into its final dimensions
3.6
welded tube
tube made by forming a hollow profile from a flat product and welding adjacent edges together, and which
after welding can be further processed, either hot or cold, into its final dimensions
3.7
manufacturer
organization that manufactures products in accordance with the relevant standard(s) and declares the
compliance of the delivered products with all applicable provisions of the relevant standard(s)
3.8
agreement
contractual arrangement between the manufacturer and purchaser at the time of enquiry and order
3.9
average of the specified thickness range
average of the specified thickness range given by:
TT+
max min
2
where T and T are the maximum and the minimum thicknesses allowed by the standard when taking
max min
into account the wall thickness tolerances
2 © ISO 2011 – All rights reserved
---------------------- Page: 7 ----------------------
ISO 10893-10:2011(E)
4 General requirements
4.1 Unless otherwise specified by the product standard or agreed on by the purchaser and manufacturer,
this ultrasonic testing shall be carried out on tubes after completion of all the primary production process
operations (rolling, heat treating, cold and hot working, sizing and straightening, etc.).
4.2 The tubes under test shall be sufficiently straight to ensure the validity of the test. The surfaces shall be
sufficiently free of foreign matter which can interfere with the validity of the test.
4.3 This test shall be carried out by suitable trained operators qualified in accordance with ISO 9712,
ISO 11484 or equivalent and supervised by competent personnel nominated by the manufacturer. In the case
of third-party inspection, this shall be agreed on by the purchaser and manufacturer.
The operating authorization issued by the employer shall be according to a written procedure. Non-destructive
testing (NDT) operations shall be authorized by a level 3 NDT individual approved by the employer.
NOTE The definition of levels 1, 2 and 3 can be found in appropriate International Standards, e.g. ISO 9712 and
ISO 11484.
5 Test method
5.1 The tubes shall be tested by using an ultrasonic shear wave technique for the detection of longitudinal
and transverse imperfections. Lamb wave technique may be applied for the detection of longitudinal
imperfections.
5.2 During testing, the tubes and the transducer assembly shall be moved relative to each other such that
the whole of the tube surface is scanned, with coverage calculated on the dimension of the transducer(s). The
relative speed of movement during testing shall not vary by more than ±10 %. There can be a short length at
both tube ends which cannot be tested. Any untested ends shall be dealt with in accordance with the
requirements of the appropriate product standard (see Annex B).
5.3 Unless otherwise agreed on by the purchaser and manufacturer, testing shall be carried out in two
opposite directions of sound propagation for the requested type of inspection, clockwise and anticlockwise for
the detection of longitudinal defects and forward and backward for the detection of transversal defects.
5.4 For the detection of longitudinal imperfections, the maximum width of each individual transducer,
measured parallel to the major axis of the tube, shall be 25 mm. For U1 category tubes with an outside
diameter equal to or less than 50 mm, the width of any one transducer unit shall normally be restricted to a
maximum of 12,5 mm.
In the case of use of the Lamb wave technique or phased array technique, the maximum width of transducer
or active aperture, measured parallel to the major axis of the tube, shall be limited to 35 mm.
For the detection of transversal imperfections, the maximum width of each individual transducer, measured
perpendicular to the major axis of the tube, shall be 25 mm.
5.5 The ultrasonic test frequency of transducers that shall be used
...
NORME ISO
INTERNATIONALE 10893-10
Première édition
2011-04-01
Essais non destructifs des tubes en
acier —
Partie 10:
Contrôle automatisé par ultrasons sur
toute la circonférence des tubes en acier
sans soudure et soudés (sauf à l'arc
immergé sous flux en poudre) pour la
détection des imperfections
longitudinales et/ou transversales
Non-destructive testing of steel tubes —
Part 10: Automated full peripheral ultrasonic testing of seamless and
welded (except submerged arc-welded) steel tubes for the detection of
longitudinal and/or transverse imperfections
Numéro de référence
ISO 10893-10:2011(F)
©
ISO 2011
---------------------- Page: 1 ----------------------
ISO 10893-10:2011(F)
PDF – Exonération de responsabilité
Le présent fichier PDF peut contenir des polices de caractères intégrées. Conformément aux conditions de licence d'Adobe, ce fichier
peut être imprimé ou visualisé, mais ne doit pas être modifié à moins que l'ordinateur employé à cet effet ne bénéficie d'une licence
autorisant l'utilisation de ces polices et que celles-ci y soient installées. Lors du téléchargement de ce fichier, les parties concernées
acceptent de fait la responsabilité de ne pas enfreindre les conditions de licence d'Adobe. Le Secrétariat central de l'ISO décline toute
responsabilité en la matière.
Adobe est une marque déposée d'Adobe Systems Incorporated.
Les détails relatifs aux produits logiciels utilisés pour la création du présent fichier PDF sont disponibles dans la rubrique General Info
du fichier; les paramètres de création PDF ont été optimisés pour l'impression. Toutes les mesures ont été prises pour garantir
l'exploitation de ce fichier par les comités membres de l'ISO. Dans le cas peu probable où surviendrait un problème d'utilisation,
veuillez en informer le Secrétariat central à l'adresse donnée ci-dessous.
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2011
Droits de reproduction réservés. Sauf prescription différente, aucune partie de cette publication ne peut être reproduite ni utilisée sous
quelque forme que ce soit et par aucun procédé, électronique ou mécanique, y compris la photocopie et les microfilms, sans l'accord écrit
de l'ISO à l'adresse ci-après ou du comité membre de l'ISO dans le pays du demandeur.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail copyright@iso.org
Web www.iso.org
Publié en Suisse
ii © ISO 2011 – Tous droits réservés
---------------------- Page: 2 ----------------------
ISO 10893-10:2011(F)
Sommaire Page
Avant-propos .iv
1 Domaine d'application .1
2 Références normatives.1
3 Termes et définitions .2
4 Exigences générales.3
5 Méthode de contrôle .3
6 Étalons de référence .4
6.1 Généralités .4
6.2 Types d'entailles de référence .4
6.3 Dimensions des entailles de référence.5
7 Étalonnage et vérification de l'équipement .6
7.1 Généralités .6
7.2 Réglage du seuil de déclenchement et d'alarme .6
7.3 Vérification de l'étalonnage et réétalonnage .7
8 Acceptation .7
9 Rapport de contôle.8
Annexe A (normative) Contrôle des imperfections longitudinales de tubes ayant un rapport
diamètre extérieur spécifié/moyenne de plage d'épaisseur spécifiée inférieur à 5 .9
Annexe B (normative) Contrôle manuel/semi-automatisé des extrémités non contrôlées et des
zones douteuses .11
© ISO 2011 – Tous droits réservés iii
---------------------- Page: 3 ----------------------
ISO 10893-10:2011(F)
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes nationaux de
normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est en général confiée
aux comités techniques de l'ISO. Chaque comité membre intéressé par une étude a le droit de faire partie du
comité technique créé à cet effet. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec l'ISO participent également aux travaux. L'ISO collabore étroitement avec
la Commission électrotechnique internationale (CEI) en ce qui concerne la normalisation électrotechnique.
Les Normes internationales sont rédigées conformément aux règles données dans les Directives ISO/CEI,
Partie 2.
La tâche principale des comités techniques est d'élaborer les Normes internationales. Les projets de Normes
internationales adoptés par les comités techniques sont soumis aux comités membres pour vote. Leur
publication comme Normes internationales requiert l'approbation de 75 % au moins des comités membres
votants.
L'attention est appelée sur le fait que certains des éléments du présent document peuvent faire l'objet de
droits de propriété intellectuelle ou de droits analogues. L'ISO ne saurait être tenue pour responsable de ne
pas avoir identifié de tels droits de propriété et averti de leur existence.
L'ISO 10893-10 a été élaborée par le comité technique ISO/TC 17, Acier, sous-comité SC 19, Conditions
techniques de livraison des tubes d'acier pour appareils à pression.
Cette première édition annule et remplace l'ISO 9309:1989 et l'ISO 9305:1989, qui ont fait l'objet d'une
révision technique.
L'ISO 10893 comprend les parties suivantes, présentées sous le titre général Essais non destructifs des tubes
en acier:
⎯ Partie 1: Contrôle automatisé électromagnétique pour vérification de l'étanchéité hydraulique des tubes
en acier sans soudure et soudés (sauf à l'arc immergé sous flux en poudre)
⎯ Partie 2: Contrôle automatisé par courants de Foucault pour la détection des imperfections des tubes en
acier sans soudure et soudés (sauf à l'arc immergé sous flux en poudre)
⎯ Partie 3: Contrôle automatisé par flux de fuite sur toute la circonférence des tubes en acier
ferromagnétique sans soudure et soudés (sauf à l'arc immergé sous flux en poudre) pour la détection des
imperfections longitudinales et/ou transversales
⎯ Partie 4: Contrôle par ressuage des tubes en acier sans soudure et soudés pour la détection des
imperfections de surface
⎯ Partie 5: Contrôle par magnétoscopie des tubes en acier ferromagnétique sans soudure et soudés pour
la détection des imperfections de surface
⎯ Partie 6: Contrôle radiographique du cordon de soudure des tubes en acier soudés pour la détection des
imperfections
⎯ Partie 7: Contrôle radiographique numérique du cordon de soudure des tubes en acier soudés pour la
détection des imperfections
⎯ Partie 8: Contrôle automatisé par ultrasons pour la détection des dédoublures des tubes en acier sans
soudure et soudés
iv © ISO 2011 – Tous droits réservés
---------------------- Page: 4 ----------------------
ISO 10893-10:2011(F)
⎯ Partie 9: Contrôle automatisé par ultrasons pour la détection des dédoublures dans les bandes/tôles
fortes utilisées pour la fabrication des tubes en acier soudés
⎯ Partie 10: Contrôle automatisé par ultrasons sur toute la circonférence des tubes en acier sans soudure
et soudés (sauf à l'arc immergé sous flux en poudre) pour la détection des imperfections longitudinales
et/ou transversales
⎯ Partie 11: Contrôle automatisé par ultrasons du cordon de soudure des tubes en acier soudés pour la
détection des imperfections longitudinales et/ou transversales
⎯ Partie 12: Contrôle automatisé de l'épaisseur par ultrasons sur toute la circonférence des tubes en acier
sans soudure et soudés (sauf à l'arc immergé sous flux en poudre)
© ISO 2011 – Tous droits réservés v
---------------------- Page: 5 ----------------------
NORME INTERNATIONALE ISO 10893-10:2011(F)
Essais non destructifs des tubes en acier —
Partie 10:
Contrôle automatisé par ultrasons sur toute la circonférence
des tubes en acier sans soudure et soudés (sauf à l'arc
immergé sous flux en poudre) pour la détection des
imperfections longitudinales et/ou transversales
1 Domaine d'application
La présente partie de l'ISO 10893 spécifie les exigences relatives au contrôle automatisé par ultrasons, avec
ondes de cisaillement (générées par une technique conventionnelle ou la technique des réseaux à commande
de phase), sur toute la circonférence des tubes en acier sans soudure et soudés [sauf à l'arc immergé sous
flux en poudre (SAW)], pour la détection des imperfections longitudinales et/ou transversales.
Sauf spécification contraire à la commande, la méthode d'essai est appliquée pour la détection des
imperfections essentiellement longitudinales.
Dans le cas du contrôle d'imperfections longitudinales, un contrôle par ondes de Lamb peut être appliqué au
choix du producteur.
Pour les tubes sans soudure, par accord entre l'acheteur et le producteur, les principes de contrôle de la
présente partie de l'ISO 10893 peuvent être appliqués pour détecter des imperfections ayant d'autres
orientations.
La présente partie de l'ISO 10893 s'applique au contrôle des tubes ayant un diamètre extérieur supérieur ou
égal à 10 mm et, normalement, un rapport diamètre extérieur/épaisseur supérieur ou égal à 5.
La présente partie de l'ISO 10893 est également applicable au contrôle des profils creux circulaires.
NOTE L'Annexe A spécifie les options permettant de contrôler les imperfections longitudinales des tubes ayant un
rapport diamètre extérieur/épaisseur inférieur à 5.
2 Références normatives
Les documents de référence suivants sont indispensables pour l'application du présent document. Pour les
références datées, seule l'édition citée s'applique. Pour les références non datées, la dernière édition du
document de référence s'applique (y compris les éventuels amendements).
ISO 5577, Essais non destructifs — Contrôle par ultrasons — Vocabulaire
ISO 9712, Essais non destructifs — Qualification et certification du personnel
ISO 11484, Produits en acier — Système de qualification, par l'employeur, du personnel pour essais non
destructifs (END)
© ISO 2011 – Tous droits réservés 1
---------------------- Page: 6 ----------------------
ISO 10893-10:2011(F)
3 Termes et définitions
Pour les besoins du présent document, les termes et définitions donnés dans l'ISO 5577 et l'ISO 11484 ainsi
que les suivants s'appliquent.
3.1
étalon de référence
étalon conçu pour l'étalonnage des équipements de contrôle non destructif (par exemple trous percés,
entailles, gorges)
3.2
tube de référence
tube ou longueur de tube contenant l'étalon ou les étalons de référence
3.3
échantillon de référence
échantillon (par exemple tronçon de tube, de tôle forte ou de bande) contenant l'étalon ou les étalons de
référence
NOTE Seule l'expression «tube de référence» est utilisée dans la suite de la présente partie de l'ISO 10893; elle
signifie également «échantillon de référence».
3.4
tube
produit long et creux, ouvert à ses deux extrémités, ayant toute forme de section
3.5
tube sans soudure
tube fabriqué à partir d'un produit plein que l'on perce en vue d'obtenir une ébauche creuse, qui est soumise à
une transformation ultérieure, à chaud ou à froid, pour lui donner ses dimensions définitives
3.6
tube soudé
tube fabriqué par formage d'un produit plat en profil creux et par soudage des rives adjacentes, et qui, après
soudage, peut être soumis à une transformation supplémentaire, à chaud ou à froid, pour lui donner ses
dimensions définitives
3.7
producteur
organisation qui fabrique des produits conformément à la norme ou aux normes pertinentes et déclare la
conformité des produits livrés à toutes les dispositions applicables de la norme ou des normes pertinentes
3.8
accord
arrangement contractuel entre le producteur et l'acheteur au moment de l'appel d'offres et de la commande
3.9
moyenne de la plage d'épaisseur spécifiée
la moyenne de la plage d'épaisseur spécifiée est donnée par
TT+
max min
2
où T et T sont les épaisseurs maximale et minimale autorisées par la norme lorsque l'on prend en
max min
compte les tolérances d'épaisseur
2 © ISO 2011 – Tous droits réservés
---------------------- Page: 7 ----------------------
ISO 10893-10:2011(F)
4 Exigences générales
4.1 Sauf spécification contraire dans la norme de produit ou accord contraire entre l'acheteur et le
producteur, le contrôle par ultrasons doit être effectué sur les tubes après exécution de toutes les opérations
principales du processus de fabrication (laminage, traitement thermique, formage à chaud ou à froid,
calibrage, dressage initial, etc.).
4.2 Les tubes à contrôler doivent être suffisamment droits pour garantir la validité de l'essai. Les surfaces
doivent être suffisamment exemptes de corps étrangers pouvant perturber la validité de l'essai.
4.3 Le contrôle doit être effectué par des opérateurs formés, qualifiés conformément à l'ISO 9712, à
l'ISO 11484 ou à une norme équivalente, et supervisés par un personnel compétent désigné par le producteur.
Lorsque le contrôle est effectué par une tierce partie, cela doit faire l'objet d'un accord entre l'acheteur et le
producteur.
L'autorisation d'opérer doit être délivrée par l'employeur conformément à une procédure écrite. Les opérations
d'essais non destructifs (END) doivent être autorisées par un personnel END de niveau 3 approuvé par
l'employeur.
NOTE La définition des niveaux 1, 2 et 3 peut être trouvée dans des Normes internationales appropriées, par
exemple l'ISO 9712 et l'ISO 11484.
5 Méthode de contrôle
5.1 Les tubes doivent être contrôlés par une technique ultrasonore avec ondes de cisaillement pour la
détection des imperfections longitudinales et/ou transversales. La technique des ondes de Lamb peut être
utilisée pour le contrôle des imperfections longitudinales.
5.2 Lors du contrôle, les tubes et l'ensemble des palpeurs doivent être déplacés l'un par rapport à l'autre de
manière à permettre un balayage de toute la surface du tube, la couverture étant calculée en fonction de la
taille du(des) palpeur(s). La vitesse relative de déplacement ne doit pas varier de plus de ±10 % pendant le
contrôle. Il est reconnu qu'il peut exister aux deux extrémités du tube une courte longueur qui ne peut être
contrôlée. Toute extrémité non contrôlée doit être traitée selon les exigences de la norme de produit
appropriée (voir l'Annexe B).
5.3 Sauf accord contraire entre acheteur et producteur, le contrôle doit être réalisé par passage du faisceau
ultrasonore selon deux directions opposées de propagation des ondes pour le type de contrôle demandé,
dans le sens horaire et antihoraire pour les imperfections longitudinales et avant/arrière pour les imperfections
transversales.
5.4 Pour la détection des imperfections longitudinales, la largeur maximale de chaque palpeur individuel,
mesurée parallèlement à l'axe longitudinal du tube, doit être de 25 mm. Pour les tubes de catégorie U1, de
diamètre extérieur inférieur ou égal à 50 mm, la largeur d'un palpeur est normalement limitée à 12,5 mm au
maximum.
Lorsque la technique des ondes de Lamb ou la technique des réseaux à commande de phase est utilisée, la
largeur maximale du palpeur/palpeur virtuel, mesurée parallèlement à l'axe longitudinal du tube, doit être
limitée à 35 mm.
Pour la détection des imperfections transversales, la largeur maximale de chaque palpeur/palpeur virtuel
individuel, mesurée perpendiculairement à l'axe longitudinal du tube, doit être de 25 mm.
5.5 La fréquence de contrôle par ultrasons des palpeurs devant être utilisés doit se situer dans l'intervalle
de 1 MHz à 15 MHz pour la technique des ondes de cisaillement et dans l'intervalle de 0,3 MHz à 1 MHz pour
la technique des ondes de Lamb, selon l'état et les propriétés du produit, l'épaisseur et le fini de surface des
tubes à contrôler.
5.6 L'équipement doit être capable de différencier les tubes acceptables et douteux au moyen d'un seuil
automatique de déclenchement et d'alarme, combiné ave
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.