ISO 3605:1978

Textile glass reinforced plastics — Composites in the form of rods made from textile glass rovings — Determination of compressive strength

Plastiques renforcés au verre textile — Composites sous forme de joncs à base de stratifils — Détermination de la résistance à la compression

General Information

• Status: Withdrawn
• Publication Date: 31-Jan-1978
• Withdrawal Date: 31-Jan-1978
• ICS: 59.100.10 - Textile glass materials
• Technical Committee: ISO/TC 61/SC 13 - Composites and reinforcement fibres
• Drafting Committee: ISO/TC 61/SC 13 - Composites and reinforcement fibres
• Current Stage: 9599 - Withdrawal of International Standard
• Completion Date: 01-May-1987

Relations

• Revised: ISO 3605:1987 - Textile glass — Rovings — Determination of compressive strength of rod composites
• Effective Date: 15-Apr-2008

Standards Content (Sample)

INTERNATIONAL STANDARD 3605
INTERNATIONAL ORGANIZATION FOR STANDARDIZATlON*MEX,llYHAPOnHAR OPrAHHJAUMR il0 CTAHLlAPTH3AUHH*ORGANlSATlON INTERNATIONALE DE NORMALISATION
0
Textile glass reinforced plastics - Composites in the form of
O
rods made from textile glass rovings - Determination of
compressive strength
Plastiques renforcés au verre textile - Composites sous forme de joncs à base de stratifils - Détermination de la
résistance à la compression
First edition - 1978-02-01
Lu
- UDC 678.5/.8 : 539.4 Ref. No. IS0 3605-1978 (E)
R
z
Descriptors : textile glass reinforced plastics, composite materials, rovings, tests, compression tests.
Price based on 3 pages

---------------------- Page: 1 ----------------------
FOREWORD
IS0 (the International Organization for Standardization) is a worldwide federation
of national standards institutes (IS0 member bodies). The work of developing
International Standards is carried out through IS0 technical committees. Every
member body interested in a subject for which a technical committee has been set
up has the right to be represented on that committee. International organizations,
governmental and non-governmental, in liaison with ISO, also take part in the work.
Draft International Standards adopted by the technical committees are circulated
to the member bodies for approval before their acceptance as International
Standards by the IS0 Council.
International Standard IS0 3605 was developed by Technical Committee
ISO/TC 61, Plastics, and was circulated to the member bodies in January 1975.
It has been approved by the member bodies of the following countries :
India Romania
Austria
Iran South Africa, Rep. of
BelgiÙm
Brazil Israel Sweden
Switzerland
Canada Japan
Mexico Turkey
Czechoslovakia
Finland New Zealand United Kingdom
Germany Netherlands U.S.A.
Hungary Poland U.S.S. R.
No member body expressed disapproval of the document.
O International 0rg.niration for Standardization, 1978
Printed in Switzerland

---------------------- Page: 2 ----------------------
I NTE RNATl ON AL STANDARD IS0 3605-1978 (E)
Textile glass reinforced plastics - Composites in the form of
rods made from textile glass rovings - Determination of
compressive strength
3.6 Two test jigs, as shown, for example, in figure 1, each
1 SCOPE AND FIELD OF APPLICATION
consisting of
This International Standard specifies a method for
a) a base plate X;
determining the compressive strength of textile glass
reinforced resin composite rods of circular cross-section,
b) an elastic compressive pad Y (for example of poly-
made from rovings.
amide);
c) an anti-burst ring 2.
2 REFERENCES
IS0 291, Plastics - Standard atmospheres for conditioning
and testing.
Dimensions in millimetres
IS0 1 172, Textile glass reinforced plastics - Determination
of the loss on ignition.
Test specimen
3 APPARATUS AND MATERIAL
0
3.1 Mould, in the form of a straight rigid cylinder, having
a minimum length of 400mm and a standard internal
diameter of 6 +. 0,1 mm; if other diameters are chosen,
these shall be selected upon agreement between the
interested parties from the range of 4 to 10 mm (with
2
0,î mm).
tolerances off
8
The mould may be constructed of glass, polytetrafluor-
ethylene, or any other suitable material.
3.2 Resin.
Y (polyamide)
Not all resin systems are necessarily suitable and the system
to be used shall be at the discretion of the roving supplier.
In the event of dispute, the system used shall be declared
and shall form the basis for the test, subject to an
agreement between the interested parties. The selected resin
system shall be mixed in accordance with the resin
manufacturer’s detailed instructions.
3.3 Suitable wire, for pulling the roving through the
mould (3.1).
3.4 Oven with air circulation, for curing and/or postcuring
the resin at the recommended temperature.
3.5 Suitable compression testing machine, capable of
FIGURE 1 - Example of a jig for testing textile glass fibre
maintaining a constant speed of 1 mm/min. reinforced plastic rods of 6 mm diameter
1

---------------------- Page: 3 ----------------------
IS0 3605-1978 (E)
4 CONDITIONING AND TESTING ATMOSPHERES
-
The hank of rovings shall be conditioned for at least 16 h
B
in one of the standard laboratory atmospheres defined in
IS0 291.
A
The atmosphere during the test shall be one of those
defined in IS0 291.
-
B
5 PROCEDURE
A
5.1 Preparation of the rovings
-
Take a parallel assembly of rovings, 1 m long and of the
C
correct mass (approximately 15 g) to give a glass content
-
in the moulded rod of 62 f 3 % (m/m).
B
-
5.2 Preparation of rein
...

NORME INTERNATIONALE 3605
INTFRNATI~~NAI ORGANIZATION FOR STANDARDiZATION~ME~AYHAPOAHAR OPCAHM3AUMR no CTAHAAPTH3AUHH*ORGANlSATION INTERNATIONALE DE NORMALISATiOI\.
Plastiques renforcés au verre textile - Composites sous forme
de joncs à base de stratifils - Détermination de la résistance
à la compression
Textile glass reinforced plastics - Composites in the form of rods made from textile glass rovings - Determination of
compressive strength
Première édition - 1978-02-01
Réf. no : IS0 3605-1978 (FI
- U
CDU 678.5f.8 : 539.4
2
q
Descripteus : plastique renforcé au verre textile, maferiau composé, stratifils, essai, essai de compression.
s
m
Prix basé sur 3 pages
s

---------------------- Page: 1 ----------------------
AVANT-PROPOS
L'ISO (Organisation internationale de normalisation) est une fédération mondiale
d'organismes nationaux de normalisation (comités membres de I'ISO). L'élaboration
des Normes internationales est confiée aux comités techniques de I'ISO. Chaque
comité membre intéresse par une étude a le droit de faire partie du comité technique
correspondant. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec I'ISO, participent également aux travaux.
Les projets de Normes internationales adoptés par les comités techniques sont
soumis aux comités membres pour approbation, avant leur acceptation comme
Normes internationales par le Conseil de I'ISO.
La Norme internationale IS0 3605 a été élaborée par le comité technique
ISOTrC 61, Plastiques, et a été soumise aux comités membres en janvier 1975.
Les comités membres des pays suivants l'ont approuvée :
Afrique du Sud, Rép. d' inde Roumanie
Allemagne Iran Royaume-Uni
Autriche Israël Suède
Belgique
Japon Suisse
Brésil Mexique
Tchécoslovaquie
Canada Nouvelle-Zélande Turquie
Finlande Pays-Bas U.R.S.S.
Hongrie Pologne U.S.A.
Aucun comité membre ne l'a désapprouvée.
O Organisation internationale da normalisation, 1978 0
Imprimé en Suisse

---------------------- Page: 2 ----------------------
NORM E I NT E R N AT I ON AL E
Plastiques renforcés au verre textile - Composites sous forme
de joncs à base de stratifils - Détermination de la résistance
à la compression
3.6 Deux dispositifs d'essai, tels que représentés à la
1 OBJET ET DOMAINE D'APPLICATION
figure 1 et comprenant :
a) une plaque de base X;
b) une rondelle compressive élastique Y (par exemple
résine renforcée de çtratifils.
en polyamide);
C) un anneau d'encastrement z.
2 RÉFÉRENCES
IÇO 291, Plastiques - Atmosphères normales de
Dimensions en millimètres
conditionnement et d'essai.
is0 1172, Matières plastiques renforcées au Verre textile -
Détermination de la perte au feu.
Éprouvette
0
3 APPAREILLAGE ET MATÉRIAU
I
Le moule peut être en verre, en polytétrafluoréthylène OU
en toute autre matière convenable.
3.2 Résine.
recommandées.
3.5 Appareil d'essai en compression, capable de travailler
à la vitesse constante de 1 mm/min.
1

---------------------- Page: 3 ----------------------
IS0 3605-1978 (F)
4 ATMOSPHÈRES DE CONDITIONNEMENT ET
D'ESSAI
L'écheveau de stratifils doit être conditionné durant au
moins 16 h dans l'une des atmosphères définies dans
I'ISO 291.
L'atmosphère d'essai doit être conforme à l'une des
atmosphères définies dans I'ISO 291.
5 MODE OPÉRATOIRE
5.1 Préparation du stratifil
Prélever un assemblage parallèle de stratifil de 1 m de long
et de masse convenable (environ 15g) pour donner une
teneur en verre dans le jonc moulé de 62 k 3 % (m/m).
5.2 Préparation des joncs renforcés
Plier l'écheveau de stratifil en son milieu et l'accrocher en
ce point à un morceau du fil de métal (3.3). Le soumettre
au conditionnement durant au moins 16 h dans l'une des
atmosphères normales de laboratoire définies dans
I'ISO 291. Prendre soin de réduire à un minimum les mani-
pulations du stratifil afin d'éviter les souillures.
Imprégner l'écheveau par immersion dans un récipient
contenant la résine catalysée (3.2) ou par tout autre moyen
convenable, Lorsqu'il a été complètement imprégné, tirer
l'écheveau verticalement dans le moule (3.1) au moyen du
fil. Tirer l'extrémité inférieure de l'écheveau à quelques
millimètres à l'intérieur du moule et sceller l'ouverture du
moule en utilisant un bouchon de liège ou de plastique pour
empêcher l'écoulement de la résine.
Préparer ainsi trois joncs.
FIGURE 2 - Découpage des jeux d'éprouvettes dans les joncs
5.3 Cu
...