ISO 8776:1988
(Main)Photography — Photographic film — Determination of folding endurance
Photography — Photographic film — Determination of folding endurance
Photographie — Film photographique — Détermination de la résistance au pliage
Photography - Photographic film - Determination of folding endurance
General Information
Relations
Buy Standard
Standards Content (Sample)
ISO
INTERNATIONAL STANDARD
8776
First edi tion
19884501
rmy
INTERNATIONAL ORGANIZATION FOR STANDARDKATION
ORGANISATION INTERNATIONALE DE NORMALISATION
ME~YHAPOflHAfl OPrAHl43A~Mfl n0 CTAH~APTM3A~MM
Photographit film - Determination of
Photography -
folding endurante
Film photographique - DtS termina tion de Ia rksistance au pliage
Photographie -
Reference number
ISO 8776 : 1988 (E)
---------------------- Page: 1 ----------------------
ISO 8776: 1988 (El
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of
national Standards bodies (ISO member bodies). The work of preparing International
Standards is normally carried out through ISO technical committees. Esch member
body interested in a subject for which a technical committee has been established has
the right to be represented on that committee. International organizations, govern-
mental and non-governmental, in liaison with ISO, also take part in the work. ISO
collaborates closely with the International Electrotechnical Commission (IEC) on all
matters of electrotechnical standardization.
Draft International Standards adopted by the technical committees are circulated to
the member bodies for approval before their acceptance as International Standards by
the ISO Council. They are approved in accordance with ISO procedures requiring at
least 75 % approval by the member bodies voting.
International Standard ISO 8776 was prepared by Technical Committee ISO/TC 42,
Photograph y.
Users should note that all International Standards undergo revision from time to time
and that any reference made herein to any other International Standard implies its
latest edition, unless otherwise stated.
The annex of this International Standard is for information only.
0 International Organkation for Standardkation, 1988 0
Printed in Switzerland
---------------------- Page: 2 ----------------------
INTERNATIONAL STANDARD ISO 8776 : 1988 (E)
Photography - Photographit film - Determination of
folding endurante
0 Introduction Different types of failure occur when film is flexed. Failure may
consist of very fine Cracks in the emulsion (without a break in
Photographit film should have sufficient folding endurante to the support) which are objectionable when the Photograph is
permit satisfactory Performance when used in the equipment viewed. Failure may also consist of Cracks in the support or a
for which it is intended under the atmospheric conditions likely complete break. The wedge brittleness test, standardized in
ISO 6677, tan generally detect the presence of emulsion Cracks
to be encountered in practice. Folding endurante is a measure
of fatigue resistance in multiple flexing. Photographit film is after a Single flex. However, emulsion Cracks are not visible
during the MIT test. They may occur after relatively few flexes
essentially a laminate of two or more different materials,
generally a plastics support and the photosensitive emulsion. and result in subsequent flexing of only the film base itself with
The latter is usually made of image forming chemicals sus- consequent higher folding endurante. For this reason, the MIT
pended in gelatin or other polymeric binder. fold test may not necessarily be in agreement with ISO 6677.
The two tests may also disagree because the apparent
The folding endurante of photographic film is affected ad- brittleness (or lack of flexibility) and fatigue resistance tan also
versely by both reduced temperature and reduced relative be dependent upon the manner in which the photographic film
humidity. In most applications, folding endurante loss at low is mechanically treated, with respect to both the degree and the
relative humidity is encountered more frequently than loss at Speed of straining. There are a number of folding endurante
low temperature. Moreover, a marked Change in film flexibility tests in addition to the MIT folding endurante test, as
may occur with only a very small Change in relative humidity described in ISO 5626. Films may be rated differently by the
below a level of about 25 %. This means that folding
different tests.
endurante tests on photographic film should be carried out
only in an atmosphere which is accurately controlled with
respect to both temperature and relative humidity.
1 Scope and field of application
The folding endurante of film is very dependent on the Sample
thickness, decreasing with an increase in thickness of either
This International Standard specifies a method for determining
base or emulsion. For this reason, the thickness of the film
and expressing quantitatively the folding endurante of
layers have to be considered when comparing the behaviour of
photographic film. l) lt is an analytical test and is not intended
different films. The temperatures and relative humidities to
to simulate practical use conditions.
which the film has been subjected between manufacture and
testing may also affect the folding endurante even though the
This International Standard is applicable to film with or without
Sample is reconditioned to a Standard temperature and
a gelatin backing, and may also be applied to either raw or pro-
humidity. Gelatin is generally more brittle than film base, so
cessed film, although the flexibility level of a given film may be
that photographic film having a gelatin layer on only one side is
quite different after processing.
usually more brittle if bent with the gelatin-side out (that is,
gelatin under tension). This tan affect the following endurante,
Equipment similar to that described in this International
depending on the direction of the first fold.
Standard may be used provided that a correlation has been
established between the results obtained using such equipment
The folding endurante of photographic film may vary in dif-
and the results obtained using the equipment described.
ferent directions if the base is oriented more in one direction
than another. There is generally no directional effect in the
emulsion.
This International Standard covers the MIT folding endurante 2 References
test in which the film is subjected to a rapid and repeated
folding action until it breaks. This test is used in ISO 4331 ISO 5626, Paper - Determination of folding endurante.
which specifies the requirements for silver-gelatin type archival
film on cellulose base and ISO 8225 which covers the stability ISO 6677, Photography - Determination of brittleness of
pho tographic film - Wedge brittleness test.
requirements for diazo film.
1) The method is based on the MIT folding endurante testet- described in the annex.
---------------------- Page: 3 ----------------------
ISO 8776: 1988 (El
3 Principle direction. If the film has a discrete backing layer, a separate set
of samples shall be tut in at least one of the two principal direc-
ner of a
Folding backwards and fotwards in a standardized man tions to enable the film to be tested with both the emulsion-side
Sample of film subjected to a longitudinal stress, until it breaks.
and the reverse-side in tension on the first fold.3)
5.3 Size of samples
4 Apparatus
The Standard film samples shall be 120 mm long and 15 to
4.1 Test chamber 16 mm wide.
An air-conditioned cabinet or walk-in room shall be used for
both conditioning and testing. The temperature shall be con-
6 Conditioning
trolled to within + 1 OC and the relative humidity to within
Z& 1 % at relative humidities below 30 % and to within + 2 %
6.1 Conditioning of samples
at higher humidities. The linear air velocity shall be at least
150 mm/s. If a walk-in conditioned room is used, the air velo-
Samples shall be conditioned in the test chamber (4.1) until
city shall be adequate to maintain the conditions specified. The
practical moisture equilibrium has been reached. This may be
number of personnel permitted in the room during testing shall
determined by weighing samples at regular intervals and deter-
be limited and precautions taken to prevent the operator’s
mining the time at which further conditioning does not ap-
breath reaching the film.
preciably Change the weight. In many instances this time will be
i
...
SLOVENSKI STANDARD
SIST ISO 8776:1997
01-september-1997
Photography - Photographic film - Determination of folding endurance
Photography -- Photographic film -- Determination of folding endurance
Photographie -- Film photographique -- Détermination de la résistance au pliage
Ta slovenski standard je istoveten z: ISO 8776:1988
ICS:
37.040.20 )RWRJUDIVNLSDSLUILOPLLQ Photographic paper, films
IRWRJUDIVNHSORãþH)LOPVNL and cartridges
]YLWNL
SIST ISO 8776:1997 en
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.
---------------------- Page: 1 ----------------------
SIST ISO 8776:1997
---------------------- Page: 2 ----------------------
SIST ISO 8776:1997
ISO
INTERNATIONAL STANDARD
8776
First edi tion
19884501
rmy
INTERNATIONAL ORGANIZATION FOR STANDARDKATION
ORGANISATION INTERNATIONALE DE NORMALISATION
ME~YHAPOflHAfl OPrAHl43A~Mfl n0 CTAH~APTM3A~MM
Photographit film - Determination of
Photography -
folding endurante
Film photographique - DtS termina tion de Ia rksistance au pliage
Photographie -
Reference number
ISO 8776 : 1988 (E)
---------------------- Page: 3 ----------------------
SIST ISO 8776:1997
ISO 8776: 1988 (El
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of
national Standards bodies (ISO member bodies). The work of preparing International
Standards is normally carried out through ISO technical committees. Esch member
body interested in a subject for which a technical committee has been established has
the right to be represented on that committee. International organizations, govern-
mental and non-governmental, in liaison with ISO, also take part in the work. ISO
collaborates closely with the International Electrotechnical Commission (IEC) on all
matters of electrotechnical standardization.
Draft International Standards adopted by the technical committees are circulated to
the member bodies for approval before their acceptance as International Standards by
the ISO Council. They are approved in accordance with ISO procedures requiring at
least 75 % approval by the member bodies voting.
International Standard ISO 8776 was prepared by Technical Committee ISO/TC 42,
Photograph y.
Users should note that all International Standards undergo revision from time to time
and that any reference made herein to any other International Standard implies its
latest edition, unless otherwise stated.
The annex of this International Standard is for information only.
0 International Organkation for Standardkation, 1988 0
Printed in Switzerland
---------------------- Page: 4 ----------------------
SIST ISO 8776:1997
INTERNATIONAL STANDARD ISO 8776 : 1988 (E)
Photography - Photographit film - Determination of
folding endurante
0 Introduction Different types of failure occur when film is flexed. Failure may
consist of very fine Cracks in the emulsion (without a break in
Photographit film should have sufficient folding endurante to the support) which are objectionable when the Photograph is
permit satisfactory Performance when used in the equipment viewed. Failure may also consist of Cracks in the support or a
for which it is intended under the atmospheric conditions likely complete break. The wedge brittleness test, standardized in
ISO 6677, tan generally detect the presence of emulsion Cracks
to be encountered in practice. Folding endurante is a measure
of fatigue resistance in multiple flexing. Photographit film is after a Single flex. However, emulsion Cracks are not visible
during the MIT test. They may occur after relatively few flexes
essentially a laminate of two or more different materials,
generally a plastics support and the photosensitive emulsion. and result in subsequent flexing of only the film base itself with
The latter is usually made of image forming chemicals sus- consequent higher folding endurante. For this reason, the MIT
pended in gelatin or other polymeric binder. fold test may not necessarily be in agreement with ISO 6677.
The two tests may also disagree because the apparent
The folding endurante of photographic film is affected ad- brittleness (or lack of flexibility) and fatigue resistance tan also
versely by both reduced temperature and reduced relative be dependent upon the manner in which the photographic film
humidity. In most applications, folding endurante loss at low is mechanically treated, with respect to both the degree and the
relative humidity is encountered more frequently than loss at Speed of straining. There are a number of folding endurante
low temperature. Moreover, a marked Change in film flexibility tests in addition to the MIT folding endurante test, as
may occur with only a very small Change in relative humidity described in ISO 5626. Films may be rated differently by the
below a level of about 25 %. This means that folding
different tests.
endurante tests on photographic film should be carried out
only in an atmosphere which is accurately controlled with
respect to both temperature and relative humidity.
1 Scope and field of application
The folding endurante of film is very dependent on the Sample
thickness, decreasing with an increase in thickness of either
This International Standard specifies a method for determining
base or emulsion. For this reason, the thickness of the film
and expressing quantitatively the folding endurante of
layers have to be considered when comparing the behaviour of
photographic film. l) lt is an analytical test and is not intended
different films. The temperatures and relative humidities to
to simulate practical use conditions.
which the film has been subjected between manufacture and
testing may also affect the folding endurante even though the
This International Standard is applicable to film with or without
Sample is reconditioned to a Standard temperature and
a gelatin backing, and may also be applied to either raw or pro-
humidity. Gelatin is generally more brittle than film base, so
cessed film, although the flexibility level of a given film may be
that photographic film having a gelatin layer on only one side is
quite different after processing.
usually more brittle if bent with the gelatin-side out (that is,
gelatin under tension). This tan affect the following endurante,
Equipment similar to that described in this International
depending on the direction of the first fold.
Standard may be used provided that a correlation has been
established between the results obtained using such equipment
The folding endurante of photographic film may vary in dif-
and the results obtained using the equipment described.
ferent directions if the base is oriented more in one direction
than another. There is generally no directional effect in the
emulsion.
This International Standard covers the MIT folding endurante 2 References
test in which the film is subjected to a rapid and repeated
folding action until it breaks. This test is used in ISO 4331 ISO 5626, Paper - Determination of folding endurante.
which specifies the requirements for silver-gelatin type archival
film on cellulose base and ISO 8225 which covers the stability ISO 6677, Photography - Determination of brittleness of
pho tographic film - Wedge brittleness test.
requirements for diazo film.
1) The method is based on the MIT folding endurante testet- described in the annex.
---------------------- Page: 5 ----------------------
SIST ISO 8776:1997
ISO 8776: 1988 (El
3 Principle direction. If the film has a discrete backing layer, a separate set
of samples shall be tut in at least one of the two principal direc-
ner of a
Folding backwards and fotwards in a standardized man tions to enable the film to be tested with both the emulsion-side
Sample of film subjected to a longitudinal stress, until it breaks.
and the reverse-side in tension on the first fold.3)
5.3 Size of samples
4 Apparatus
The Standard film samples shall be 120 mm long and 15 to
4.1 Test chamber 16 mm wide.
An air-conditioned cabinet or walk-in room shall be used for
both conditioning and testing. The temperature shall be con-
6 Conditioning
trolled to within + 1 OC and the relative humidity to within
Z& 1 % at relative humidities below 30 % and to within + 2 %
6.1 Conditioning of samples
at higher humidities. The linear air velocity shall be at least
150 mm/s. If a walk-in conditioned room is used, th
...
IS0
8776
NORME INTERNATIONALE
Première édition
1988-06-01
INTERNATIONAL ORGANIZATION FOR STANDARDIZATION
ORGANISATION INTERNATIONALE DE NORMALISATION
MEXAYHAPOAHAR OPTAHMSAUMR Il0 CTAHAAPTM3AuMM
Photographie - Film photographique - Détermination
de la résistance au pliage
Photography - Photographic film - Determination of folding endurance
Numéro de référence
IS0 8776 : 1988 (F)
---------------------- Page: 1 ----------------------
IS0 8776 : 1988 (FI
L'ISO (Organisation internationale de normalisation) est une fédération mondiale
d'organismes nationaux de normalisation (comités membres de I'ISO). L'élaboration
des Normes internationales est en général confiée aux comités techniques de I'ISO.
Chaque comité membre intéressé par une étude a le droit de faire partie du comité
technique créé à cet effet. Les organisations internationales, gouvernementales et non
I'ISO participent également aux travaux. L'ISO col-
gouvernementales, en liaison avec
labore étroitement avec la Commission électrotechnique internationale (CE11 en ce qui
concerne la normalisation électrotechnique.
Les projets de Normes internationales adoptés par les comités techniques sont soumis
aux comités membres pour approbation, avant leur acceptation comme Normes inter-
nationales par le Conseil de I'ISO. Les Normes internationales sont approuvées confor-
mément aux procédures de I'ISO qui requièrent l'approbation de 75 % au moins des
comités membres votants.
La Norme internationale IS0 8776 a été élaborée par le comité technique ISO/TC 42,
Photographie.
I
L'attention des utilisateurs est attirée sur le fait que toutes les Normes internationales
sont de temps en temps soumises à révision et que toute référence faite à une autre
Norme internationale dans le présent document implique qu'il s'agit, sauf indication
contraire, de la dernière édition.
L'annexe de la présente Norme internationale est donnée uniquement à titre d'informa-
I
tion.
---------------------- Page: 2 ----------------------
NORME INTERNATIONALE IS0 8776 : 1988 (FI
raphie - Film photographique - Détermination
a résistance au pliage
rapide et répété jusqu'à la rupture. Cet essai est préconisé dans
8 introduction
VISO 4331 qui spécifie les conditions requises pour le film
Les films photographiques devraient avoir une résistance au gélatino-argentique sur support en ester de cellulose destiné à
pliage permettant des performances satisfaisantes dans les l'archivage et dans I'ISO 8225 qui établit les conditions de stabi-
équipements destinés à être utilisés dans les conditions atmos- lité requises pour le film diazoïque.
phériques rencontrées ordinairement dans la pratique. La résis-
tance au pliage est la capacité d'un film à endurer la fatigue due Différents types de défauts se produisent lorsqu'un film est
.)
à de multiples pliures. Le film photographique est essentielle-
plié. Ces défauts peuvent consister en de très fines craquelures
ment un produit formé de deux ou plusieurs composants de dif- dans l'émulsion (sans ruptures dans le support), ce qui est inac-
férentes matières, généralement un support en matière plasti-
ceptable lorsque l'on examine les images. II existe également
que et une couche d'émulsion photosensible. Cette dernière est des défauts de craquelureg ou une rupture complète du sup-
à base
ordinairement constituée de gélatine ou d'un autre liant port. La détermination de la fragilité à la flexion, normalisée
de polymères, qui maintient les produits photosensibles. dans I'ISO 6077, permet gdnéralement de détecter la présence
de craquelures dans la couche sensible après une simple pliure.
La résistance au pliage des films photographiques est accrue Toutefois, les craquelures de la couche sensible ne sont pas
par une diminution de la température et/ou par une diminution
visibles pendant l'essai du type ((MIT». Elles peuvent apparaître
de l'humidité relative. Dans la plupart des applications, la résis- après un nombre de pliures relativement faible et résultent uni-
tance au pliage à basse humidité relative se rencontre plus fré-
quement de la flexion du support lui-même entraînant une aug-
quemment que la résistance au pliage à basse température. De mentation de la résistance au pliage. C'est pour cette raison
il peut se produire un changement important de la fragilité que l'essai ((MIT» n'est pas nécessairement en accord avec
plus,
d'un film pour une très faible variation de l'humidité relative I'ISO 6077. On peut trouver des résultats différents entre les
deux types d'essais, qui peqvent être dus à un traitement méca-
au-dessous d'environ 25 %. II en résulte que les essais de fragi-
lité à la flexion sur les films photographiques ne doivent être nique différent du film photographique produisant une fragilité
apparente (ou un manque de flexibilité) et une résistance au
effectués que dans une atmosphère dont la température et
l'humidité relative sont contrôlées avec une grande précision. pliage différente en fonction de l'angle et de la vitesse des pliu-
res. II y a de nombreux essais de résistance au pliage en plus de
I'ISO 5626. Les films peuvent
La résistance au pliage d'un film dépend beaucoup de I'épais- la méthode ((MIT» décrite dans
seur de l'éprouvette et elle croît avec l'épaisseur du support ou être considérés différemment selon les différents essais.
de l'émulsion. Pour cette raison, on doit prendre en considéra-
tion l'épaisseur des couches déposées sur le film lorsque l'on
compare le comportement de différents films. Les conditions
de température et d'humidité auxquelles a été soumis un film
entre sa fabrication et les essais peuvent aussi affecter la fragi-
lité à la résistance au pliage, même si l'éprouvette est recondi- 1 Objet et domaine d'application
tionnée à la température et à l'humidité normales. La gélatine
est généralement plus fragile que le support, de sorte que le La présente Norme internationale spécifie une méthode de
film photographique n'ayant une couche de gélatine que sur détermination et d'expression quantitative de la résistance au
une face est normalement plus fragile lorsqu'il est courbé, le pliage des films photograpHiques. II s'agit d'essais théoriques et
côté gélatine vers l'extérieur (c'est-à-dire la couche de gélatine non d'une simulation des conditions d'utilisation des fi1rns.l)
en tension). En conséquence, la résistance au pliage dépend du
sens du premier pli. La méthode est applicable aux films présentant ou non une dor-
sale à la gélatine; aux film$ vierges ou développés, même si la
La résistance au pliage du film photographique peut varier sui- flexibilité d'un film donné est totalement différente après traite-
vant l'orientation de l'axe de flexion par rapport au support. II ment.
n'y a, en général, pas d'effet directionnel dans l'émulsion.
à celui décrit dans la présente Norme
Un appareillage similaire
La présente Norme internationale couvre l'essai ((MIT» de internationale peut être utilisé si on peut établir une corrélation
résistance au pliage, dans lequel le film est soumis à un pliage entre eux.
La méthode est fondée sur l'appareil d'essai (( MIT )) de la résistance au pliage décrit en annexe.
1)
1
---------------------- Page: 3 ----------------------
IS0 8776 : 1988 (FI
doit être maintenue afin que les arêtes de l'éprouvette soient
2 Références
nettes et dépourvues d'amorces de rupture. L'opérateur doit
porter des gants de caoutchouc pour manipuler les éprouvettes
IS0 5626, Papier - Détermination de la résistance au pliage.
pendant la préparation et les essais.2)
IS0 6077, Photographie - Détermination de la fragilité à la
flexion des films photographiques - Essai par la méthode dite
5.2 Choix des éprouvettes
rrdu coinu.
Un jeu d'au moins dix éprouvettes doit être préparé pour cha-
que essai. Si le format du film le permet, un jeu d'éprouvettes
3 Principe
devrait être coupé dans le sens chaîne et un second jeu dans le
sens trame. Si le film porte une couche dorsale, un jeu distinct
Pliage en avant et en arrière de facon normalisée d'une éprou-
d'éprouvettes doit être coupé dans au moins l'un des deux sens
vette de film soumise à un effort longitudinal, jusqu'à sa rupture.
principaux afin de pouvoir faire des essais soit avec le côté cou-
che image en tension, soit avec la dorsale en tension, pour la
première pliure. 3)
4 Appareillage
5.3 Taille des éprouvettes
4.1 Enceinte d'essai
L'éprouvette de film normalisée doit avoir une longueur de
Utiliser une enceinte ou une salle conditionnée à la fois pour le
120 mm et une largeur de 15 à 16 mm.
conditionnement des films et pour les essais. La température
doit être réglée à f 1 OC et l'humidité relative à f 1 % pour les
valeurs d'humidité inférieures à 30 % et à f2 % pour les
6 Conditionnement
valeurs d'humidité relative plus élevées. La vitesse linéaire de
l'air doit être au moins de 150 mm/s. Si l'on utilise une salle
6.1 Conditionnement des éprouvettes
conditionnée, la vitesse de l'air doit être suffisante pour mainte-
nir les conditions spécifiées. Le personnel admis dans la salle au
Les éprouvettes doivent être conditionnées dans l'enceinte
cours des essais doit être limité et l'on doit prendre les précau-
d'essai jusqu'à ce que l'équilibre d'humidité soit pratiq
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.