ISO 7326:2016

Rubber and plastics hoses - Assessment of ozone resistance under static conditions

ISO 7326:2016 specifies five methods for determining the ozone resistance of the outer covers of hoses: - method 1, for bore sizes up to and including 25 mm, carried out on the hose itself; - method 2, for bore sizes greater than 25 mm, carried out on a test piece from the hose wall; - method 3, for bore sizes greater than 25 mm, carried out on a test piece from the cover; - method 4, for all bore sizes, carried out on the hose itself; - method 5, for all bore sizes, carried out on hoses that are expandable, for example textile-reinforced hoses. NOTE For hoses with built-in fittings from which it is not possible to take test pieces, the ozone resistance can be assessed on slabs in accordance with ISO 1431‑1, using test sheets of the appropriate polymeric compound vulcanized to the same degree.

Tuyaux en caoutchouc et en plastique — Évaluation de la résistance à l'ozone dans des conditions statiques

ISO 7326:2016 spécifie cinq méthodes pour la détermination de la résistance à l'ozone des revêtements extérieurs des tuyaux: - méthode 1, pour des dimensions d'alésage inférieures ou égales à 25 mm, réalisée sur le tuyau lui-même; - méthode 2, pour des dimensions d'alésage supérieures à 25 mm, réalisée sur une éprouvette prélevée dans la paroi du tuyau; - méthode 3, pour des dimensions d'alésage supérieures à 25 mm, réalisée sur une éprouvette prélevée dans le revêtement du tuyau; - méthode 4, pour toutes les dimensions d'alésage, réalisée sur le tuyau lui-même; - méthode 5, pour toutes les dimensions d'alésage, réalisée sur des tuyaux qui sont extensibles, par exemple des tuyaux renforcés textile. NOTE Pour des tuyaux ayant des raccords intégrés sur lesquels il n'est pas possible de prélever des éprouvettes, la résistance à l'ozone peut être évaluée sur des plaques conformément à l'ISO 1431‑1, en utilisant des plaques du mélange polymérique approprié, vulcanisées au même degré.

General Information

• Status: Published
• Publication Date: 06-Oct-2016
• ICS: 23.040.70 - Hoses and hose assemblies
• Technical Committee: ISO/TC 45/SC 1 - Rubber and plastics hoses and hose assemblies
• Drafting Committee: ISO/TC 45/SC 1/WG 4 - Hose test methods
• Current Stage: 9093 - International Standard confirmed
• Start Date: 17-Jun-2021
• Completion Date: 27-Dec-2025

Relations

• Consolidates: ISO 11119-4:2016 - Gas cylinders - Refillable composite gas cylinders - Design, construction and testing - Part 4: Fully wrapped fibre reinforced composite gas cylinders up to 150 l with load-sharing welded metallic liners
• Effective Date: 06-Jun-2022
• Revises: ISO 7326:2006 - Rubber and plastics hoses - Assessment of ozone resistance under static conditions
• Effective Date: 04-Nov-2015

Overview

ISO 7326:2016 - Rubber and plastics hoses: Assessment of ozone resistance under static conditions specifies standardized methods to assess the resistance of hose outer covers to atmospheric ozone. The standard defines five test methods, required apparatus, conditioning and exposure protocols, inspection intervals and reporting requirements to evaluate ozone cracking on hose covers and assemblies.

Key topics and requirements

• Five test methods (scope):
  • Method 1: For bore sizes ≤ 25 mm - test carried out on the hose itself.
  • Method 2: For bore sizes > 25 mm - test on a strip from the hose wall.
  • Method 3: For bore sizes > 25 mm - test on a strip from the hose cover.
  • Method 4: For all bore sizes - hose wound on a cylinder for testing.
  • Method 5: For expandable hoses (e.g., textile-reinforced) - test with an inserted rod.
• Apparatus: Ozone cabinet with ozone generation and control (per ISO 1431-1), appropriate holders/jigs, cylinder and round rod for methods 4 and 5.
• Test pieces & conditioning: Three test pieces per test; no test within 24 h of manufacture; condition test pieces 48 h in an ozone‑free atmosphere following ISO 23529.
• Exposure conditions: Default exposure in ozone cabinet to (50 ± 5) pphm ozone at (40 ± 2) °C for up to 72 h, with inspections at 2, 4, 24, 48 and 72 h under ×2 magnification.
• Reporting: Test report must reference ISO 7326:2016, describe the hose, state the method used, list test conditions and elongation, record any cracks (nature and time observed) and test date.
• Comparability note: Results from different methods may not be directly comparable; the product standard should specify the method to use.

Applications and who uses it

• Manufacturers of rubber and plastics hoses: validate cover compound formulations and production quality for ozone resistance.
• Quality control and test laboratories: perform routine acceptance and conformance testing.
• Product designers and materials engineers: compare candidate materials and predict service life in ozone-prone environments.
• Procurement and regulatory bodies: specify and verify compliance with ozone-resistance requirements in product standards.
• Failure analysis teams: determine whether ozone cracking contributed to hose deterioration.

Practical uses include material selection, batch acceptance testing, end‑use risk assessment (outdoor or ozone-rich environments), and supporting product standards or warranty claims.

Related standards

• ISO 1431-1: Resistance to ozone cracking - static and dynamic strain testing (referred for ozone cabinet and test details).
• ISO 23529: Preparation and conditioning of rubber test pieces.
• ISO 8330: Vocabulary for hoses and hose assemblies (terms and definitions referenced).

Keywords: ISO 7326, ozone resistance, rubber and plastics hoses, hose testing, static ozone test, ozone cracking, ISO 1431-1, ISO 23529.

Standards Content (Sample)

INTERNATIONAL ISO
STANDARD 7326
Fourth edition
2016-10-15
Rubber and plastics hoses —
Assessment of ozone resistance under
static conditions
Tuyaux en caoutchouc et en plastique — Évaluation de la résistance à
l’ozone dans des conditions statiques
Reference number
©
ISO 2016
© ISO 2016, Published in Switzerland
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized otherwise in any form
or by any means, electronic or mechanical, including photocopying, or posting on the internet or an intranet, without prior
written permission. Permission can be requested from either ISO at the address below or ISO’s member body in the country of
the requester.
ISO copyright office
Ch. de Blandonnet 8 • CP 401
CH-1214 Vernier, Geneva, Switzerland
Tel. [phone]
Fax [phone]
[e-mail]
www.iso.org
ii © ISO 2016 – All rights reserved

Contents Page
Foreword .iv
Introduction .v
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 General considerations . 1
5 Apparatus . 2
6 Test pieces . 2
6.1 Type of test piece . 2
6.1.1 Method 1 . 2
6.1.2 Method 2 . 2
6.1.3 Method 3 . 2
6.1.4 Method 4 . 3
6.1.5 Method 5 . 3
6.2 Number of test pieces . 3
7 Conditioning of test pieces . 3
8 Test conditions . 3
9 Procedure. 3
9.1 Method 1. 3
9.2 Method 2. 4
9.3 Method 3. 4
9.4 Method 4. 5
9.5 Method 5. 6
10 Test report . 7
Bibliography . 8
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www.iso.org/directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www.iso.org/patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation on the meaning of ISO specific terms and expressions related to conformity assessment,
as well as information about ISO’s adherence to the World Trade Organization (WTO) principles in the
Technical Barriers to Trade (TBT) see the following URL: www.iso.org/iso/foreword.html.
The committee responsible for this document is ISO/TC 45, Rubber and rubber products, Subcommittee
SC 1, Rubber and plastics hoses and hose assemblies.
This fourth edition cancels and replaces the third edition (ISO 7326:2006), which has been technically
revised with the following changes:
— in Clause 2, the latest edition of ISO 1431-1 has been cited;
— 5.5 and 9.4.1 have been amended;
— in 6.1.1, the formula has been amended.
iv © ISO 2016 – All rights reserved

Introduction
The methods described in this document provide a means of assessing the resistance of hoses to the
deleterious effects of atmospheric ozone under static conditions.
INTERNATIONAL STANDARD ISO 7326:2016(E)
Rubber and plastics hoses — Assessment of ozone
resistance under static conditions
1 Scope
This document specifies five methods for determining the ozone resistance of the outer covers of hoses:
— method 1, for bore sizes up to and including 25 mm, carried out on the hose itself;
— method 2, for bore sizes greater than 25 mm, carried out on a test piece from the hose wall;
— method 3, for bore sizes greater than 25 mm, carried out on a test piece from the cover;
— method 4, for all bore sizes, carried out on the hose itself;
— method 5, for all bore sizes, carried out on hoses that are expandable, for example textile-
reinforced hoses.
NOTE For hoses with built-in fittings from whi
...

NORME ISO
INTERNATIONALE 7326
Quatrième édition
2016-10-15
Tuyaux en caoutchouc et en
plastique — Évaluation de la
résistance à l’ozone dans des
conditions statiques
Rubber and plastics hoses — Assessment of ozone resistance under
static conditions
Numéro de référence
©
ISO 2016
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2016, Publié en Suisse
Droits de reproduction réservés. Sauf indication contraire, aucune partie de cette publication ne peut être reproduite ni utilisée
sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique, y compris la photocopie, l’affichage sur
l’internet ou sur un Intranet, sans autorisation écrite préalable. Les demandes d’autorisation peuvent être adressées à l’ISO à
l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Ch. de Blandonnet 8 • CP 401
CH-1214 Vernier, Geneva, Switzerland
Tel. [phone]
Fax [phone]
[e-mail]
www.iso.org
ii © ISO 2016 – Tous droits réservés

Sommaire Page
Avant-propos .iv
Introduction .v
1 Domaine d’application . 1
2 Références normatives . 1
3 Termes et définitions . 1
4 Considérations générales . 2
5 Appareillage . 2
6 Éprouvettes . 2
6.1 Type d’éprouvette. 2
6.1.1 Méthode 1 . 2
6.1.2 Méthode 2 . 3
6.1.3 Méthode 3 . 3
6.1.4 Méthode 4 . 3
6.1.5 Méthode 5 . 3
6.2 Nombre d’éprouvettes . 3
7 Conditionnement des éprouvettes . 3
8 Conditions d’essai . 3
9 Mode opératoire. 4
9.1 Méthode 1 . 4
9.2 Méthode 2 . 5
9.3 Méthode 3 . 5
9.4 Méthode 4 . 6
9.5 Méthode 5 . 6
10 Rapport d’essai . 7
Bibliographie . 8
Avant-propos
L’ISO (Organisation internationale de normalisation) est une fédération mondiale d’organismes
nationaux de normalisation (comités membres de l’ISO). L’élaboration des Normes internationales est
en général confiée aux comités techniques de l’ISO. Chaque comité membre intéressé par une étude
a le droit de faire partie du comité technique créé à cet effet. Les organisations internationales,
gouvernementales et non gouvernementales, en liaison avec l’ISO participent également aux travaux.
L’ISO collabore étroitement avec la Commission électrotechnique internationale (IEC) en ce qui
concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier de prendre note des différents
critères d’approbation requis pour les différents types de documents ISO. Le présent document a été
rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir www.
iso.org/directives).
L’attention est appelée sur le fait que certains des éléments du présent document peuvent faire l’objet de
droits de propriété intellectuelle ou de droits analogues. L’ISO ne saurait être tenue pour responsable
de ne pas avoir identifié de tels droits de propriété et averti de leur existence. Les détails concernant
les références aux droits de propriété intellectuelle ou autres droits analogues identifiés lors de
l’élaboration du document sont indiqués dans l’Introduction et/ou dans la liste des déclarations de
brevets reçues par l’ISO (voir www.iso.org/brevets).
Les appellations commerciales éventuellement mentionnées dans le présent document sont données
pour information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un
engagement.
Pour une explication de la signification des termes et expressions spécifiques de l’ISO liés à l’évaluation
de la conformité, ou pour toute information au sujet de l’adhésion de l’ISO aux principes de l’Organisation
mondiale du commerce (OMC) concernant les obstacles techniques au commerce (OTC), voir le lien
suivant: www.iso.org/iso/fr/avant-propos.html
Le comité chargé de l’élaboration du présent document est l’ISO/TC 45, Élastomères et produits à base
d’élastomères, sous-comité SC 1, Tuyaux et flexibles en caoutchouc et en matière plastique.
Cette quatrième édition annule et remplace la troisième édition (ISO 7326:2006), qui a fait l’objet d’une
révision technique avec les principales modifications suivantes:
— à l’Article 2, la dernière édition de l’ISO 1431-1 a été citée;
— les paragraphes 5.5 et 9.4.1 ont été révisés;
— en 6.1.1, la formule a été modifiée.
iv © ISO 2016 – Tous droits réservés

Introduction
Les méthodes décrites dans le présent document permettent d’évaluer la résistance des tuyaux aux
effets délétères d’une atmosphère ozonisée dans des conditions statiques.
NORME INTERNATIONALE ISO 7326:2016(F)
Tuyaux en caoutchouc et en plastique — Évaluation de la
résistance à l’ozone dans des conditions statiques
1 Domaine d’application
Le présent document spécifie cinq méthodes pour la détermination de la résistance à l’ozone des
revêtements extérieurs des tuyaux:
— méthode 1, pour des dimensions d’alésage inférieures ou égales à 25 mm, réalisée sur le tuyau
lui-même;
— méthode 2, pour des dimensions d’alésage supérieures à 25 mm, réalisée sur une éprouvette
prélevée dans la paroi du tuyau;
— méthode 3, pour des dimensions d’alésage supérieures à 25 mm, réalisée sur une éprouvette
prélevée dans le revêtement du tuyau;
— méthode 4, pour toutes les dimensions d’alésage, réalisée sur le tuyau lui-même;
— méthode 5, pour toutes les dimensions d’alésage, réalisée sur des tuyaux qui sont extensibles, par
exemple des tuyaux renforcés textile.
NOTE Pour des tuyaux ayant des raccords intégrés sur lesquels il n’est pas possible de prélever des
éprouvettes, la résistance à l’ozone peut être évaluée sur des plaques conformément à l’ISO 1431-1, en utilisant
des plaques du mélange polymérique approprié, vulcanisées au même degré.
2 Références normatives
Les documents suivants sont référencés dans le texte de so
...