ISO 6998:1984

Carbonaceous materials for the production of aluminium — Pitch for electrodes — Determination of coking value

Produits carbonés utilisés pour la production de l'aluminium — Brai pour électrodes — Détermination du résidu de cokéfaction

General Information

• Status: Withdrawn
• Publication Date: 31-Mar-1984
• Withdrawal Date: 31-Mar-1984
• ICS: 71.100.10 - Materials for aluminium production
• Technical Committee: ISO/TC 226 - Materials for the production of primary aluminium
• Drafting Committee: ISO/TC 226 - Materials for the production of primary aluminium
• Current Stage: 9599 - Withdrawal of International Standard
• Completion Date: 11-Dec-1997

Relations

• Revised: ISO 6998:1997 - Carbonaceous materials for the production of aluminium — Pitch for electrodes — Determination of coking value
• Effective Date: 15-Apr-2008
• Revised: SIST ISO 6998:1998 - Carbonaceous materials for the production of aluminium -- Pitch for electrodes -- Determination of coking value
• Effective Date: 12-May-2008

Standards Content (Sample)

International Standard 6998
INTERNATIONAL ORGANIZATION FOR STANDARDlZATlON*MEWYHAPOflHAR OPTAHMJAUMR no CTAHAAPTM3AUMM.ORGANlSATlON INTERNATIONALE DE NORMALISATION
Carbonaceous materials for the production of
aluminium - Pitch for electrodes - Determination of
coking value
Produits carbonés utilisés pour la production de l'aluminium - Brai pour électrodes - Détermination du résidu de cokéfaction
First edition - 1984-04-15
UDC 665.m : 669.713 : 66.092.89 Ref. NO. IS0 6998-1984 (E)
Descriptors : aluminium, production, pitch (materials), electrodes, tests, determination, coking.
Price based on 3 pages

---------------------- Page: 1 ----------------------
Foreword
IS0 (the International Organization for Standardization) is a worldwide federation of
national standards bodies (IS0 member bodies). The work of developing International
Standards is carried out through IS0 technical committees. Every member body
interested in a subject for which a technical committee has been authorized has the
right to be represented on that committee. International organizations, governmental
ISO, also take part in the work.
and non-governmental, in liaison dth
Draft International Standards adopted by the technical committees are circulated to
I the member bodies for approval before their acceptance as International Standards by
the IS0 Council.
International Standard IS0 6998 was developed by Technical Committee ISO/TC 47,
Chemistry, and was circulated to the member bodies in August 1982.
I
It has been approved by the member bodies of the following countries :
I
India Romania
Australia
Austria Italy South Africa, Rep. of
Korea, Dem. P. Rep. of Spain
Canada
China Korea, Rep. of Sweden
Mexico Switzerland
Czechoslovakia
Egypt, Arab Rep. of Netherlands United Kingdom
New Zealand USSR
France
Germany, F.R. Poland
Portugal
Hungary
No member body expressed disapproval of the document.
0 International Organization for Standardization, 1984 O
I Printed in Switzerland

---------------------- Page: 2 ----------------------
IS0 6998-1984 (E)
INTERN ATlON AL STAN DARD
Carbonaceous materials for the production of
aluminium - Pitch for electrodes - Determination of
coking value
1 Scope and field of application 5.3 Stainless steel wire supports (see figure 1). to locate
the porcelain crucibles (5.1) correctly in the nickel crucibles
This International Standard specifies a method for determina- (5.2) and allowing a separation of 10 k 1 mm between the
tion of the coking value of pitches used for the production of bases of each crucible.
aluminium.
5.4 Support for the nickel crucibles (see figure 21, made
from 1 mm thick stainless steel plate, which contains four
2 References
holes. The support is bent over the edges, welded at the cor-
ners and fitted with four welded legs which allow, when holes
IS0 565, Test sieves - Woven metal wire cloth, perforated
are used to nest the nickel crucibles, to hold its bottom at least
plate and electroformed sheet - Nominal sizes of openings. 7 mm above the base of the furnace.
The support is intended for four determinations (two duplicate
IS0 5725, Precision of test methods - Determination of
determinations), but for reference testing, only two of the holes
repeatability and reproducibility by inter-laboratory tests.
should be used.
IS0 6257, Carbonaceous materials used in the production of
aluminium - Pitch for electrodes - Sampling.
5.5 Sieves, of 1 mm, 300 pm and 212 pm nominal mesh size
(see IS0 565).
3 Principle
5.6 Electric furnace, capable of being controlled at 550
f looc.
Heating of a test portion under defined conditions at 550
f 10 OC and weighing the coke residue.
6 Sampling and sample
4 Material 6.1 Sampling
Sampling should be carried out according to the procedure
Calcined petroleum coke, sieved,
specified in IS0 6257.
Use the fraction which passes a 1 mm mesh sieve and is re-
6.2 Preparation of test sample
tained by a 212 pm mesh sieve (see IS0 565).
If the sample is sufficiently hard, crush with a small jaw crusher
and grind it in a mortar to pass at least a 300 pm mesh sieve
5 Apparatus
and, if possible, a 212 pm mesh sieve. If the ambient
temperature is high, the operation will be facilitated by chilling
Ordinary laboratory apparatus and
the sample beforehand.
If the pitch is too soft to crush, melt the sample and take suf-
5.1 Porcelain crucibles, tall form, of capacity approxi-
ficient of the molten mass for the test. The
...

Norme internationale @ 6998
~~ ~~~~ ~~ ~
INTERNATIONAL ORGANIZATION FOR STANDARDIZATlON*MEMYHAPOAHAR OPTAHH3AUkiR no CTAHLlAPTM3AUHM*ORGANlSATlON INTERNATIONALE DE NORMALISATION
Produits carbonés utilisés pour la production de
* l'aluminium - Brai pour électrodes - Détermination du
résidu de cokéfaction
Carbonaceous materials for the production of aluminium - Pitch for electrodes - Determination of coking value
Première édition - 1984-04-15
CDU 665.777 : 669.713 : 66.092.89
Réf. no : IS0 6998-1984 (FI
k
Descripteurs : aluminium, production, brai, électrode, essai, détermination, cokéfaction.
f
Prix basé sur 3 pages

---------------------- Page: 1 ----------------------
Avant-propos
L‘ISO (Organisation internationale de normalisation) est une fédération mondiale
d’organismes nationaux de normalisation (comités membres de I’ISO). L‘élaboration
des Normes internationales est confiée aux comités techniques de I’ISO. Chaque
comité membre intéressé par une étude a le droit de faire partie du comité technique
correspondant. Les organisations internationales, gouvernementales et non gouverne-
mentales, en liaison avec I’ISO, participent également aux travaux.
Les projets de Normes internationales adoptés par les comités techniques sont soumis
aux comités membres pour approbation, avant leur acceptation comme Normes inter-
nationales par le Conseil de I’ISO.
La Norme internationale IS0 6998 a été élaborée par le comité technique ISO/TC 47,
Chimie, et a été soumise aux comités membres en août 1982.
Les comités membres des pays suivants l’ont approuvée :
Afrique du Sud, Rép. d’ Espagne Portugal
Allemagne, R.F. France Roumanie
Australie Hongrie Royaume-Uni
Autriche Inde Suède
Canada Italie Suisse
Chine Mexique Tchécoslovaquie
Corée, Rép. de Nouvelle-Zélande URSS
Pays-Bas
Corée, Rép. dém. p. de
Égypte, Rép. arabe d‘ Pologne
Aucun comité membre ne l‘a désapprouvée.
O Organisation internationale de normalisation, 1984 0
Imprimé en Suisse

---------------------- Page: 2 ----------------------
NORM E I NTERNATION ALE IS0 6998-1984 (F)
Produits carbonés utilisés pour la production de
l'aluminium - Brai pour électrodes - Détermination du
résidu de cokéfaction
5.3 Supports en fil d'acier inoxydable (voir figure I), pour
1 Objet et domaine d'application
maintenir en place à l'intérieur des creusets en nickel (5.2) les
*
La présente Norme internationale spécifie une méthode de creusets en porcelaine (5.1) en assurant une distance entre les
détermination du résidu de cokéfaction des brais utilisés pour la fonds des deux creusets de 10 f 1 mm.
production de l'aluminium.
5.4 Support pour les creusets en nickel (voir figure 21,
formé par une tôle en acier inoxydable d'épaisseur 1 mm avec
quatre trous. Le support est replié aux bords, soudé aux coins
2 Références
et muni de quatre supports soudés qui maintiennent les fonds
des creusets en nickel, lorsqu'ils sont logés dans les trous, à
IS0 565, Tamis de contrôle - Tissus métalliques, tôles perfo-
7 mm au moins de distance de la sole du four.
rées et feuilles électro formées - Dimensions nominales des
ouvertures.
Le support est conqu pour effectuer quatre essais à la fois
(deux déterminations en double), mais, lorsqu'il est utilisé pour
IS0 5725, Fidélité des méthodes d'essai - Détermination de la
des analyses d'arbitrage, deux trous seulement doivent être uti-
répétabilité et de la reproductibilité par essais interlaboratoires.
lisés.
IS0 6257, Produits carbonés utilisés pour la production de
Tamis, de 1 mm, 300 pm et 212 pm d'ouvertures nomi-
5.5
I'aluminium - Brais pour électrodes - Échantillonnage.
nales de maille (voir IS0 565).
5.6 Four électrique, réglable à 550 f 10 OC.
3 Principe
Chauffage d'une prise d'essai, dans des conditions définies, à
6 Échantillonnage et échantillon
0
550 f 10 OC et pesée du résidu cokéfié.
6.1 Échantillonnage
4 Produit
L'échantillonnage doit être effectué selon les modalités spéci-
fiées dans I'ISO 6257.
Coke de pétrole calciné, tamisé.
6.2 Préparation de l'échantillon pour essai
la partie qui passe à travers un tamis de 1 mm d'ouver-
Utiliser
ture de maille et est retenue par un tamis de 212 pm d'ouverture
Si l'échantillon est suffisamment dur, le broyer avec un petit
de maille (voir IS0 565).
concasseur à mâchoires et compléter le broyage dans un mor-
tier jusqu'à passage à travers un tamis de 300 I.im d'ouverture
de maille et, si possible, jusqu'à passage à travers un tamis de
5 Appareillage 212 pm d'ouverture de maille. Si la température ambiante est
élevée, l'opération sera facilitée par un refroidissement préala-
Matériel courant de laboratoire, et
ble de l'échantillon.
Si le brai est trop mou pour pouvoir le broyer, faire fondre
5.1 Creusets en porcelaine, forme haute, de capacité 50 ml
l'échantillon et prélever pour l'essai une quantité suffisante de
environ, munis chacun d'un couvercle à rebord emboîtant le
la masse fondue. La température de fusion ne do
...