ISO 7267-3:2017

Rubber-covered rollers — Determination of apparent hardness — Part 3: Pusey and Jones method

ISO 7267-3:2017 specifies a method for the determination of the apparent hardness of vulcanized- or thermoplastic-rubber roller covers, expressed as the Pusey and Jones indentation value. The Pusey and Jones plastometer apparatus is used to measure the depth of indentation of an indentor under a specified force into the surface of the rubber. The indentation value should not be confused with hardness as measured by the international rubber hardness test method ISO 48,[1] since in this method the rubber immediately adjacent to the indentor is precompressed. The Pusey and Jones indentation value is an inverse measurement of hardness, i.e. the harder the rubber the lower the Pusey and Jones indentation value.

Cylindres revêtus de caoutchouc — Détermination de la dureté apparente — Partie 3: Méthode Pusey et Jones

ISO 7267-3:2017 spécifie une méthode de détermination de la dureté apparente des cylindres revêtus de caoutchouc vulcanisé ou thermoplastique, exprimée en valeur de pénétration Pusey et Jones. Le plastomètre Pusey et Jones est utilisé pour mesurer la profondeur de pénétration d'un pénétrateur sous une force spécifiée dans la surface d'un caoutchouc. La valeur de la pénétration n'est pas à confondre avec la dureté mesurée par la méthode d'essai de détermination du degré international de dureté du caoutchouc (DIDC) décrite dans l'ISO 48[1], étant donné que, dans cette méthode, le caoutchouc immédiatement en contact avec le pénétrateur est précompressé. La valeur de pénétration Pusey et Jones est une mesure inverse de la dureté, c'est-à-dire que plus le caoutchouc est dur, plus la valeur de pénétration Pusey et Jones est faible.

General Information

• Status: Withdrawn
• Publication Date: 17-Aug-2017
• Withdrawal Date: 17-Aug-2017
• ICS: 83.140.99 - Other rubber and plastics products
• Technical Committee: ISO/TC 45/SC 2 - Testing and analysis
• Drafting Committee: ISO/TC 45/SC 2/WG 1 - Physical properties
• Current Stage: 9599 - Withdrawal of International Standard
• Completion Date: 20-Aug-2018

Relations

• Revised: ISO 48-8:2018 - Rubber, vulcanized or thermoplastic — Determination of hardness — Part 8: Apparent hardness of rubber-covered rollers by Pusey and Jones method
• Effective Date: 15-Dec-2017
• Revises: ISO 7267-3:2011 - Rubber-covered rollers — Determination of apparent hardness — Part 3: Pusey and Jones method
• Effective Date: 10-Dec-2016

Standards Content (Sample)

INTERNATIONAL ISO
STANDARD 7267-3
Fourth edition
2017-08
Rubber-covered rollers —
Determination of apparent
hardness —
Part 3:
Pusey and Jones method
Cylindres revêtus de caoutchouc — Détermination de la dureté
apparente —
Partie 3: Méthode Pusey et Jones
Reference number
ISO 7267-3:2017(E)
©
ISO 2017

---------------------- Page: 1 ----------------------
ISO 7267-3:2017(E)

COPYRIGHT PROTECTED DOCUMENT
© ISO 2017, Published in Switzerland
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized otherwise in any form
or by any means, electronic or mechanical, including photocopying, or posting on the internet or an intranet, without prior
written permission. Permission can be requested from either ISO at the address below or ISO’s member body in the country of
the requester.
ISO copyright office
Ch. de Blandonnet 8 • CP 401
CH-1214 Vernier, Geneva, Switzerland
Tel. [phone]
Fax [phone]
[e-mail]
www.iso.org
ii © ISO 2017 – All rights reserved

---------------------- Page: 2 ----------------------
ISO 7267-3:2017(E)

Contents Page
Foreword .iv
Introduction .v
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Time-interval between vulcanization/finished grinding and testing.2
5 Conditioning and temperature of test . 2
6 Apparatus . 2
7 Calibration . 4
8 Procedure. 4
9 Expression of results . 4
10 Test report . 4
Annex A (normative) Calibration schedule . 6
Bibliography . 8
© ISO 2017 – All rights reserved iii

---------------------- Page: 3 ----------------------
ISO 7267-3:2017(E)

Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www.iso.org/directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www.iso.org/patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation on the voluntary nature of standards, the meaning of ISO specific terms and
expressions related to conformity assessment, as well as information about ISO's adherence to the
World Trade Organization (WTO) principles in the Technical Barriers to Trade (TBT) see the following
URL: www.iso.org/iso/foreword.html.
This document was prepared by Technical Committee ISO/TC 45, Rubber and rubber products,
Subcommittee SC 2, Testing and analysis.
This fourth edition cancels and replaces the third edition (ISO 7267-3:2011), of which it constitutes a
minor revision to update the normative references in Clause 2.
A list of all parts in the ISO 7267 series can be found on the ISO website.
iv © ISO 2017 – All rights reserved

---------------------- Page: 4 ----------------------
ISO 7267-3:2017(E)

Introduction
The hardness of a roller covering has traditionally been determined on the finished roller, since it is this
hardness that is critical to the correct functioning of the roller in its end application. Values of hardness,
determined by whichever method is chosen, are therefore dependent not only on the method employed
and on the rubber, but also on the diameter of the roller, on the thickness of the covering and, in the
case of thin coverings, on the nature of the roller core. For this reason the term “apparent hardness” is
used to distinguish between the values obtained by the methods described in the various parts of this
document and those that would be obtained for the rubber if it was possible to use the standard test
methods for standard test pieces forming the subjects of other International Standards.
Since rollers vary considerably in size, construction and end use, and in view of the fact that hardness
determinations are made for such different purposes as specification and factory process control, it has
not been possible to standardize one test method. Consequently, three methods are described in the
ISO 7267 series, each capable of standing alone.
© ISO 2017 – All rights reserved v

---------------------- Page: 5 ----------------------
INTERNATIONAL STANDARD ISO 7267-3:2017(E)
Rubber-covered rollers — Determination of apparent
hardness —
Part 3:
Pusey and Jones method
WARNING 1 — Persons using this document should be familiar with normal laboratory practice.
This document does not purport to address all of the safety problems, if any, associated with its
use. It is the responsibility of the user to establish appropriate safety and health practices and to
determine the applicability of any other restrictions.
WARNING 2 — Certain procedures specified in this document might involve the use or generation
of substances, or the generation of waste, that could constitute a local environmental hazard.
Reference should be made to appropriate documentation on safe handling and disposal after use.
1 Scope
This document specifies a method for the determination of the apparent hardness of vulcanized- or
thermoplastic-rubber roller covers, expressed as the Pusey and Jones indentation value.
The Pusey and Jones plastometer apparatus is used to measure the depth of indentation of an indentor
under a specified force into the surface of the rubber. The indentation value should not be confused with
[1]
hardness as measured by the international rubber hardness test method ISO 48, since in this method
the rubber immediately adjacent to the indentor is precompressed. The Pusey and Jones indentation
value is an inverse measurement of hardness, i.e. the harder the rubbe
...

NORME ISO
INTERNATIONALE 7267-3
Quatrième édition
2017-08
Cylindres revêtus de caoutchouc —
Détermination de la dureté
apparente —
Partie 3:
Méthode Pusey et Jones
Rubber-covered rollers — Determination of apparent hardness —
Part 3: Pusey and Jones method
Numéro de référence
ISO 7267-3:2017(F)
©
ISO 2017

---------------------- Page: 1 ----------------------
ISO 7267-3:2017(F)

DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2017, Publié en Suisse
Droits de reproduction réservés. Sauf indication contraire, aucune partie de cette publication ne peut être reproduite ni utilisée
sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique, y compris la photocopie, l’affichage sur
l’internet ou sur un Intranet, sans autorisation écrite préalable. Les demandes d’autorisation peuvent être adressées à l’ISO à
l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Ch. de Blandonnet 8 • CP 401
CH-1214 Vernier, Geneva, Switzerland
Tel. [phone]
Fax [phone]
[e-mail]
www.iso.org
ii © ISO 2017 – Tous droits réservés

---------------------- Page: 2 ----------------------
ISO 7267-3:2017(F)

Sommaire Page
Avant-propos .iv
Introduction .v
1 Domaine d'application . 1
2 Références normatives . 1
3 Termes et définitions . 1
4 Délai entre vulcanisation/rectification et essai . 2
5 Conditionnement et température d'essai . 2
6 Appareillage . 2
7 Étalonnage . 4
8 Mode opératoire. 4
9 Expression des résultats. 4
10 Rapport d'essai . 4
Annexe A (normative) Programme d'étalonnage. 6
Bibliographie . 8
© ISO 2017 – Tous droits réservés iii

---------------------- Page: 3 ----------------------
ISO 7267-3:2017(F)

Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes
nationaux de normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est
en général confiée aux comités techniques de l'ISO. Chaque comité membre intéressé par une étude
a le droit de faire partie du comité technique créé à cet effet. Les organisations internationales,
gouvernementales et non gouvernementales, en liaison avec l'ISO participent également aux travaux.
L'ISO collabore étroitement avec la Commission électrotechnique internationale (IEC) en ce qui
concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier de prendre note des différents
critères d'approbation requis pour les différents types de documents ISO. Le présent document a été
rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir www.
iso.org/directives).
L'attention est attirée sur le fait que certains des éléments du présent document peuvent faire l'objet de
droits de propriété intellectuelle ou de droits analogues. L'ISO ne saurait être tenue pour responsable
de ne pas avoir identifié de tels droits de propriété et averti de leur existence. Les détails concernant
les références aux droits de propriété intellectuelle ou autres droits analogues identifiés lors de
l'élaboration du document sont indiqués dans l'Introduction et/ou dans la liste des déclarations de
brevets reçues par l'ISO (voir www.iso.org/brevets).
Les appellations commerciales éventuellement mentionnées dans le présent document sont données
pour information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un
engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l'ISO liés à l'évaluation de la conformité, ou pour toute information au sujet de l'adhésion
de l'ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles
techniques au commerce (OTC), voir le lien suivant: www.iso.org/avant-propos.
Le présent document a été élaboré par le comité technique ISO/TC 45, Élastomères et produits à base
d'élastomères, sous-comité SC 2, Essais et analyses.
Cette quatrième édition annule et remplace la troisième édition (ISO 7267-3:2011), dont elle constitue
une révision mineure afin de mettre à jour les références normatives à l’Article 2.
Une liste de toutes les parties de l’ISO 7267 peut être trouvée sur le site internet de l’ISO.
iv © ISO 2017 – Tous droits réservés

---------------------- Page: 4 ----------------------
ISO 7267-3:2017(F)

Introduction
Traditionnellement, la dureté d'un revêtement de cylindre est déterminée sur le cylindre fini, étant
donné que c'est cette dureté qui est essentielle au bon fonctionnement du cylindre en service. Quelle
que soit la méthode choisie, les valeurs de la dureté déterminées dépendent donc non seulement de la
méthode utilisée et du caoutchouc, mais aussi du diamètre du cylindre et de l'épaisseur du revêtement
et, dans le cas de revêtements minces, de la nature du noyau du cylindre. C'est pourquoi le terme «dureté
apparente» est utilisé pour faire la distinction entre les valeurs obtenues par les méthodes décrites
dans les diverses parties du présent document et celles qui seraient obtenues pour le caoutchouc s'il
était possible d'utiliser les méthodes d'essai normalisées pour des éprouvettes normalisées faisant
l'objet d'autres Normes internationales.
Étant donné que les cylindres varient considérablement au point de vue taille, construction et utilisation
finale, et que les déterminations de dureté sont faites à des fins aussi différentes que la spécification et
le contrôle d'usine, il n'a pas été possible de normaliser une seule méthode d'essai. Par conséquent, trois
méthodes sont décrites dans la série ISO 7267, chacune étant auto-portante.
© ISO 2017 – Tous droits réservés v

---------------------- Page: 5 ----------------------
NORME INTERNATIONALE ISO 7267-3:2017(F)
Cylindres revêtus de caoutchouc — Détermination de la
dureté apparente —
Partie 3:
Méthode Pusey et Jones
AVERTISSEMENT 1 — Il convient que l'utilisateur du présent document connaisse bien les
pratiques courantes de laboratoire. Le présent document n'a pas pour but de traiter tous les
problèmes de sécurité qui sont, le cas échéant, liés à son utilisation. Il incombe à l'utilisateur
d'établir des pratiques appropriées en matière d'hygiène et de sécurité, et de déterminer
l'applicabilité de toute autre restriction.
AVERTISSEMENT 2 — Certains modes opératoires spécifiés dans le présent document peuvent
impliquer l'utilisation ou la génération de substances, ou la génération de déchets, susceptibles
de constituer un danger environnemental localisé. Il convient de se référer à la documentation
appropriée relative à la manipulation et à l'élimination de ces substances en toute sécurité après
utilisation.
1 Domaine d'application
Le présent document spécifie une méthode de détermination de la dureté apparente des cylindres
revêtus de caoutchouc vulcanisé ou thermoplastique, exprimée en valeur de pénétration Pusey et Jones.
Le plastomètre Pusey et Jones est utilisé pour mesurer la profondeur de pénétration d'un pénétrateur
sous une force spécifiée dans la surface d'un caoutchouc. La valeur de la pénétration n'est pas à
confondre avec la dureté mesurée par la méthode d'essai de détermination du degré international
[1]
de dureté du caoutchouc (DIDC) décrite dans l'ISO 48 , étant donné que, dans cette méthode, le
caoutchouc immédiatement en contact avec le pénétrateur est précompressé. La valeur de pénétration
Pusey et Jones est une mesure inverse de la dureté, c'est-à-dire que plus le caoutchouc est dur, plus la
valeur de pénétration Pusey et Jones est faible.
...