Advanced technical ceramics - Mechanical properties of ceramic composites at high temperature under inert atmosphere - Determination of tensile properties

Advanced technical ceramics - Mechanical properties of ceramic composites at high temperature under inert atmosphere - Determination of tensile properties

This part of ENV is to specify the conditions for determination of tensile properties of ceramic matrix composite materials with continuous fibre reinforcement for temperatures up to 2 000 °C under vacuum or a gas atmosphere which is inert to the material under test. Note: The use of these environments is aimed at avoiding changes of the material to be tested due to chemical reaction with its environment during the test.

Hochleistungskeramik - Mechanische Eigenschaften von keramischen Verbundwerkstoffen bei hoher Temperatur in inerter Atmosphäre - Bestimmung der Eigenschaften unter Zug

Céramiques techniques avancées - Propriétés mécaniques des céramiques composites a haute température sous atmosphere neutre - Détermination des caractéristiques en traction

Advanced technical ceramics - Mechanical properties of ceramic composites at high temperature under inert atmosphere - Determination of tensile properties

General Information

Status
Withdrawn
Publication Date
30-Nov-2000
Withdrawal Date
31-Aug-2005
ICS
81.060.30 - Advanced ceramics
Technical Committee
SS SPL - Technical Board for the general field
Current Stage
9900 - Withdrawal (Adopted Project)
Start Date
01-Sep-2005
Due Date
01-Sep-2005
Completion Date
01-Sep-2005
Mandate
M/076 - Mandate to CEN/CENELEC for standardization in the field of advanced ceramics
Ref Project
ENV 1892:1996 - Advanced technical ceramics - Mechanical properties of ceramic composites at high temperature under inert atmosphere - Determination of tensile properties

Relations

Replaced By
SIST EN 1892:2005 - Advanced technical ceramics - Mechanical properties of ceramic composites at high temperature under inert atmosphere - Determination of tensile properties
Effective Date
01-Sep-2005

Buy Standard

ENV 1892:2000ENV 1892:2000
PreviousNext
Standardization document
ENV 1892:2000
English language
19 pages
sale 10% off
Preview
sale 10% off
Preview
e-Library read for
1 day

Standards Content (Sample)

SLOVENSKI STANDARD
SIST ENV 1892:2000
01-december-2000
Advanced technical ceramics - Mechanical properties of ceramic composites at
high temperature under inert atmosphere - Determination of tensile properties
Advanced technical ceramics - Mechanical properties of ceramic composites at high
temperature under inert atmosphere - Determination of tensile properties
Hochleistungskeramik - Mechanische Eigenschaften von keramischen
Verbundwerkstoffen bei hoher Temperatur in inerter Atmosphäre - Bestimmung der
Eigenschaften unter Zug
Céramiques techniques avancées - Propriétés mécaniques des céramiques composites
a haute température sous atmosphere neutre - Détermination des caractéristiques en
traction
Ta slovenski standard je istoveten z: ENV 1892:1996
ICS:
81.060.30 Sodobna keramika Advanced ceramics
SIST ENV 1892:2000 en
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.

---------------------- Page: 1 ----------------------

SIST ENV 1892:2000

---------------------- Page: 2 ----------------------

SIST ENV 1892:2000

---------------------- Page: 3 ----------------------

SIST ENV 1892:2000

---------------------- Page: 4 ----------------------

SIST ENV 1892:2000

---------------------- Page: 5 ---
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

SIST
SIST EN 13235:2007(Main)
Advanced technical ceramics - Mechanical properties of ceramic composites at high temperature under inert atmosphere - Determination of creep behaviour
EN 13235:2006

This European Standard specifies the conditions for the determination of the tensile creep deformation and failure behaviour of ceramic matrix composite materials with continuous fibre reinforcement for temperatures up to 2 000 °C under vacuum or in a gas atmosphere which is inert to the material under test. The purpose of these test conditions is to prevent changes to the material as a result of chemical reaction with the test environment.
This European Standard applies to all ceramic matrix composites with a continuous fibre reinforcement, unidirectional (1 D), bidirectional (2 D), and tridirectional (x D, where 2 ? x ? 3), loaded along one principal axis of reinforcement.

  • Standard
    15 pages
    English language
    sale 10% off
    e-Library read for
    1 day
SIST
SIST EN 15158:2007(Main)
Advanced technical ceramics - Mechanical properties of ceramic composites at high temperature under inert atmosphere - Determination of fatigue properties at constant amplitude
EN 15158:2006

This European Standard specifies the conditions for the determination of constant-amplitude of load or strain in uniaxial tension/tension or in uniaxial tension/compression cyclic fatigue properties of ceramic matrix composite materials (CMCs) with fibre reinforcement for temperature up to 2 000 °C under vacuum or a gas atmosphere which is inert to the material under test.
NOTE   Test environments are specified which are intended to prevent the material under test from chemically reacting with them.
This European Standard applies to all ceramic matrix composites with fibre reinforcement, unidirectional (1D), bi-directional (2D), and tri-directional (xD, where 2 < x ? 3).

  • Standard
    18 pages
    English language
    sale 10% off
    e-Library read for
    1 day
SIST
SIST EN 623-1:2007(Main)
Advanced technical ceramics - Monolithic ceramics - General and textural properties - Part 1: Determination of the presence of defects by dye penetration
EN 623-1:2006

This part of EN 623 specifies qualitative methods for determination of the presence of defects in advanced technical ceramics by dye penetration tests. The results are reported as visual observations of dye penetration.
Three methods are described:
Method A:  A fuchsine dye test which is suitable for white or pale-coloured ceramic products, performed using an evacuation test.
Method B:  A fluorescent dye test which is suitable particularly for those products where the purple fuchsine has insufficient visual contrast with the ceramic material, performed using a proprietary test kit.
Method C:  A fuchsine dye test which is performed by simple immersion in or spraying with a dye solution, suitable for routine testing for major defects.

  • Standard
    7 pages
    English language
    sale 10% off
    e-Library read for
    1 day
SIST
SIST EN 12788:2005(Main)
Advanced technical ceramics - Mechanical properties of ceramic composites at high temperature under inert atmosphere - Determination of flexural strength
EN 12788:2005

TThis document specifies the conditions for determination of the flexural strength of ceramic matrix composite materials with continuous fibre reinforcement under three-point or four-point bending for temperatures up to 2 000 °C under vacuum or a gas atmosphere which is inert to the material under test.
NOTE 1   The use of these environments is aimed at avoiding changes of the material affecting its flexural strength caused by chemical reaction with its environment during the test.
This European document applies to all ceramic matrix composites with a continuous fibre reinforcement, unidirectional (1D), bidirectional (2D), and tridirectional (xD, with 2 < x L 3), loaded along one principal axis of reinforcement.
NOTE 2   The method outlined in this document should not be used to obtain values of flexural strength for design purposes.

  • Standard
    12 pages
    English language
    sale 10% off
    e-Library read for
    1 day
SIST
SIST EN ISO 15732:2005(Main)
Fine ceramics (advanced ceramics, advanced technical ceramics) - Test method for fracture toughness of monolithic ceramics at room temperature by single edge precracked beam (SEPB) method (ISO 15732:2003)
EN ISO 15732:2005

ISO 15732:2003 describes a test method for the determination of fracture toughness of monolithic ceramic materials at room temperature by the Single-Edge-Precracked-Beam (SEPB) method.
This International Standard is intended for use with monolithic ceramics and whisker- or particulate-reinforced ceramics which are regarded as macroscopically homogeneous. It does not include continuous-fiber-reinforced ceramic composites.
ISO 15732:2003 is for material development, material comparison, quality assurance, characterization, reliability and design data generation.
Fracture toughness values determined with other test methods cannot be interchanged with KIpb as defined in this International Standard, and may not be interchangeable with each other.

  • Standard
    27 pages
    English language
    sale 10% off
    e-Library read for
    1 day
SIST
SIST EN ISO 18756:2005(Main)
Fine ceramics (advanced ceramics, advanced technical ceramics) - Determination of fracture toughness of monolithic ceramics at room temperature by the surface crack in flexure (SCF) method (ISO 18756:2003)
EN ISO 18756:2005

ISO 18756:2003 describes a test method that covers the determination of fracture toughness of monolithic ceramic materials at room temperature by the surface crack in flexure (SCF) method.
This International Standard is intended for use with monolithic ceramics and whisker- or particulate-reinforced ceramics that are regarded as macroscopically homogeneous. It does not include continuous-fiber reinforced ceramic composites.
The test method is applicable to materials with either flat or rising crack growth resistance curves.

  • Standard
    36 pages
    English language
    sale 10% off
    e-Library read for
    1 day
SIST
SIST EN 12289:2005(Main)
Advanced technical ceramics - Mechanical properties of ceramic composites at ambient temperature - Determination of in-plane shear properties
EN 12289:2005

This European Standard specifies the conditions for the determination of the in-plane shear properties at ambient temperature of ceramic matrix composite materials with continuous fibre reinforcement.
This European Standard applies to ceramic matrix composites with a continuous fibre reinforcement, bi-directional (2D) and tri-directional (xD, with 2 < x < 3).

  • Standard
    17 pages
    English language
    sale 10% off
    e-Library read for
    1 day
SIST
SIST EN 1894:2005(Main)
Advanced technical ceramics - Mechanical properties of ceramic composites at high temperature under inert atmosphere - Determination of shear strength by compression loading of notched specimens
EN 1894:2005

This document specifies the conditions for determination of the inter-laminar shear strength of ceramic matrix composite materials with continuous fibre reinforcement for temperatures up to 2 000 °C under a vacuum, or a gas atmosphere, which is inert to the material under test, by loading of notched specimens in compression.
NOTE 1   The use of a vacuum or a gas atmosphere is aimed at avoiding changes of the material to be tested due to chemical reaction with its environment during the test.
This document applies to all ceramic matrix composites with continuous fibre reinforcement, unidirectional (1D), bidirectional (2D), and tridirectional (xD, with 2 < x < 3), loaded along one principal axis of reinforcement.
NOTE 2   Care should be exercised in interpreting the results of the test method to obtain absolute values of the inter-laminar shear strength of ceramic matrix composites for design purposes.
.

  • Standard
    11 pages
    English language
    sale 10% off
    e-Library read for
    1 day
SIST
SIST EN 821-3:2005(Main)
Advanced technical ceramics - Monolithic ceramics. Thermo-physical properties - Part 3: Determination of specific heat capacity
EN 821-3:2005

This document specifies two methods for the determination of specific heat capacity of advanced monolithic technical ceramic materials based on drop calorimetry (Method A) and differential scanning calorimetry (DSC, Method B) over a temperature range from room temperature upwards, depending on the design of the equipment.
NOTE 1   The methods described apply in the case of test materials free from phase transformations, annealing effects or partial melting. If any such effect occurs in a material over the temperature range of the test, spurious results will be obtained unless the data are carefully analysed. In such cases it is usually necessary to conduct repeat tests at a number of temperatures close to the discontinuity, in order to estimate correctly its contribution to the apparent heat capacity.
NOTE 2   Care should be exercised in both methods over the selection of the cell or crucible material and in the selection of the test atmosphere, especially at high temperatures. Test pieces can react with the crucible or the atmosphere, leading to spurious results. In general, an awareness of such problems should be maintained at all times. Especially with regard to Method B, awareness should also be maintained of radiation effects at temperatures above 1000 °C, and of the reproducibility of the output signal.

  • Standard
    18 pages
    English language
    sale 10% off
    e-Library read for
    1 day
SIST
SIST EN 623-4:2005(Main)
Advanced technical ceramics - Monolithic ceramics - General and textural properties - Part 4: Determination of surface roughness
EN 623-4:2004

This part of EN 623 concerns the use of conventional stylus type instruments for the measurement of surface texture of advanced monolithic technical ceramics, sets the test machine measuring parameters, and recommends the adoption of certain precautions and conditions of measurement.
NOTE   Non-contact optical methods of surface texture measurement employ a different concept using a narrow laser beam. The interaction of the beam with the surface is influenced by the angle of the surface to the beam and the reflectivity/translucence of the surface. The reflected beam is detected in a number of ways based on spot focus or beam deflection and converted into a height profile. Results from such a test are not directly equivalent to those obtained by the stylus method.

  • Standard
    13 pages
    English language
    sale 10% off
    e-Library read for
    1 day