WG 3 - TC 90/WG 3

IEC 61788-26:2020 specifies a test method for determining the DC critical current of short RE (rare earth)-Ba-Cu-O (REBCO) composite superconductor specimens that have a shape of straight flat tape. This document applies to test specimens shorter than 300 mm and having a rectangular cross section with an area of 0,03 mm2 to 7,2 mm2, which corresponds to tapes with width ranging from 1,0 mm to 12,0 mm and thickness from 0,03 mm to 0,6 mm.
This method is intended for use with superconductor specimens that have critical current less than 300 A and n-values larger than 5 under standard test conditions: the test specimen is immersed in liquid nitrogen bath at ambient pressure without external magnetic field during the testing. Deviations from this test method that are allowed for routine tests and other specific restrictions are given in this document.

IEC 61788-24:2018 describes a test method for determining the retained critical current after double bending at room temperature of short and straight Ag- and/or Ag alloy-sheathed Bi-2223 superconducting wires that have the shape of a flat or square tape containing mono- or multicores of oxides. The wires can be laminated with copper alloy, stainless steel or Ni alloy tapes.
The test method is intended for use with superconductors that have a critical current less than 300 A and an n-value larger than 5.

This part of IEC 61788 covers a test method for the determination of the dc critical current of short and straight Ag- and/or Ag alloy-sheathed Bi-2212 and Bi-2223 oxide superconductors that have a monolithic structure and a shape of round wire or flat or square tape containing mono- or multicores of oxides. This method is intended for use with superconductors that have critical currents less than 500 A and n-values larger than 5. The test is carried out with and without an applying external magnetic field. For all tests in a magnetic field, the magnetic field is perpendicular to the length of the specimen. In the test of a tape specimen in a magnetic field, the magnetic field is parallel or perpendicular to the wider tape surface (or one surface if square). The test specimen is immersed either in a liquid helium bath or a liquid nitrogen bath during testing. Deviations from this test method that are allowed for routine tests and other specific restrictions are given in this standard.