ASTM D1212-91(2020)
(Test Method)Standard Test Methods for Measurement of Wet Film Thickness of Organic Coatings
Standard Test Methods for Measurement of Wet Film Thickness of Organic Coatings
SIGNIFICANCE AND USE
4.1 Wet film thickness measurements aid in the prediction of dry film thickness. In instances where dry film thickness cannot be measured nondestructively, wet film thickness is frequently specified. Also, the ability to determine wet film thickness during application can provide the opportunity to correct the application procedures.
SCOPE
1.1 These test methods cover the determination of wet film thickness of organic coatings such as paint, varnish, and lacquer. Two methods are described as follows:
1.1.1 In Test Method A, the Wet Film Thickness Gage (English or Metric graduation (see 5.1)) is used to measure wet film thicknesses up to 60 mils on the English scale series, and up to 700 μm on the metric scale series (Sections 5 – 8).
1.1.2 In Test Method B, the Pfund Gage is used to measure wet film thicknesses up to 14.2 mils (360 μm) (Sections 9 – 13).
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
General Information
Relations
Standards Content (Sample)
This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the
Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
Designation: D1212 − 91 (Reapproved 2020)
Standard Test Methods for
1
Measurement of Wet Film Thickness of Organic Coatings
This standard is issued under the fixed designation D1212; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope film thickness is determined as quickly as possible to reduce
shrinkage due to solvent loss.
1.1 These test methods cover the determination of wet film
thickness of organic coatings such as paint, varnish, and 3.2 In Test Method A, a gage with one eccentric and two
lacquer. Two methods are described as follows: concentricwheelsisrolledoverthesurfaceandthepointwhere
1.1.1 In Test Method A, the Wet Film Thickness Gage the eccentric wheel first touches the wet film is determined.
(English or Metric graduation (see 5.1)) is used to measure wet
3.3 InTest Method B, a gage with a convex lower surface is
film thicknesses up to 60 mils on the English scale series, and
pushed into the wet film until the center touches the substrate.
up to 700 µm on the metric scale series (Sections5–8).
The diameter of the spot of wet coating left on the convex
1.1.2 In Test Method B, the Pfund Gage is used to measure
surface is measured and the film thickness calculated from the
wet film thicknesses up to 14.2 mils (360 µm) (Sections9–
diameter of the spot and the radius of curvature.
13).
4. Significance and Use
1.2 The values stated in SI units are to be regarded as the
standard. The values given in parentheses are for information
4.1 Wet film thickness measurements aid in the prediction
only.
of dry film thickness. In instances where dry film thickness
1.3 This standard does not purport to address all of the cannot be measured nondestructively, wet film thickness is
frequently specified. Also, the ability to determine wet film
safety concerns, if any, associated with its use. It is the
responsibility of the user of this standard to establish appro- thickness during application can provide the opportunity to
correct the application procedures.
priate safety, health, and environmental practices and deter-
mine the applicability of regulatory limitations prior to use.
1.4 This international standard was developed in accor-
TEST METHOD A
dance with internationally recognized principles on standard-
ization established in the Decision on Principles for the
5. Apparatus
Development of International Standards, Guides and Recom-
5.1 WetFilmThicknessGage—Two versions of the gage are
mendations issued by the World Trade Organization Technical
3
now in use: The original design as shown in Fig. 1 and a later
Barriers to Trade (TBT) Committee.
designasshowninFig.2.Bothdesignsconsistsofaneccentric
2. Referenced Documents
center wheel supported by two concentric wheels so as to
2
provide two scales that are bilaterallysymmetrical.As the gage
2.1 ASTM Standards:
is rolled on the film, there is a change in clearance between the
D823 Practices for Producing Films of Uniform Thickness
wet film and the eccentric wheel. The point at which the film
of Paint, Coatings and Related Products on Test Panels
first touches the center wheel measures the thickness of the
3. Summary of Test Methods
film.
3.1 The material is applied in the laboratory to plane, rigid
5.2 The later design shown in Fig. 2, moves the eccentric
test panels or in the field to the surface being coated. The wet
wheel from between the concentric wheels, as shown in Fig. 1,
to the outside of the gage and closer to one of the concentric
1
These test methods are under the jurisdiction of ASTM Committee D01 on
wheels. Gage reading errors of parallax across the gage are
Paint and Related Coatings, Materials, and Applications and are the direct
eliminatedasthetwoscalesareplaceddirectlyontheeccentric
responsibility of Subcommittee D01.23 on Physical Properties of Applied Paint
Films.
Current edition approved June 1, 2020. Published June 2020. Originally
3
approved in 1952. Last previous edition approved in 2013 as D1212 – 91 (2013). Both versions of this gage (Interchemical (INMONT) and Model “C”) are
DOI: 10.1520/D1212-91R20. covered by U.S. Patents 2 507 592 and 3 128 558 and are issued to Maynard R.
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or Euverard. Interested parties are invited to submit information regarding the
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM identification of acceptable alternatives to this patented item to the Committee on
Standards
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.