Standard Practice for Production and Evaluation of Field Metallographic Replicas

Standard Practice for Production and Evaluation of Field Metallographic Replicas

SIGNIFICANCE AND USE
4.1 Replication is a nondestructive sampling procedure that records and preserves the topography of a metallographically prepared surface as a negative relief on a plastic film (replica). The replica permits the examination and analysis of the metallographically prepared surface on the LM or SEM.  
4.2 Enhancement procedures for improving replica contrast for microscopic examination are utilized and sometimes necessary (see 8.1).Note 1—It is recommended that the purchaser of a field replication service specify that each replicator demonstrate proficiency by providing field prepared replica metallography and direct LM and SEM comparison to laboratory prepared samples of an identical material by grade and service exposure.
SCOPE
1.1 This practice covers recognized methods for the preparation and evaluation of cellulose acetate or plastic film replicas which have been obtained from metallographically prepared surfaces. It is designed for the evaluation of replicas to ensure that all significant features of a metallographically prepared surface have been duplicated and preserved on the replica with sufficient detail to permit both LM and SEM examination with optimum resolution and sensitivity.  
1.2 This practice may be used as a controlling document in commercial situations.  
1.3 The values stated in SI units are to be regarded as the standard. Inch-pound units given in parentheses are for information only.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

General Information

Status
Historical
Publication Date
30-Sep-2012
ICS
77.040.99 - Other methods of testing of metals
Technical Committee
E04 - Metallography
Drafting Committee
E04.01 - Specimen Preparation
Current Stage
Ref Project

Buy Standard

ASTM E1351-01(2012) - Standard Practice for Production and Evaluation of Field Metallographic ReplicasASTM E1351-01(2012) - Standard Practice for Production and Evaluation of Field Metallographic Replicas
PreviousNext
Standard
ASTM E1351-01(2012) - Standard Practice for Production and Evaluation of Field Metallographic Replicas
English language
6 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation: E1351 − 01 (Reapproved 2012)
Standard Practice for
1
Production and Evaluation of Field Metallographic Replicas
This standard is issued under the fixed designation E1351; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision.Anumber in parentheses indicates the year of last reapproval.A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
INTRODUCTION
Replication is a nondestructive sampling procedure which records and preserves the topography of
a metallographic specimen as a negative relief on a plastic film. The microstructural replica can be
examined using a light microscope (LM) or scanning electron microscope (SEM) for subsequent
analysis. Specimens examined in the SEM are vacuum coated with vaporized carbon or a suitable
metal to provide contrast and conductivity. The convenience of the replication process makes it
suitable for obtaining microstructures from field locations for subsequent examination and analysis in
a laboratory. The proper preparation of the test surface and of the replica itself is of paramount
importance and must receive careful attention. Because of the diversity of metallographic equipment
available and the wide range of environments in which replication is conducted, the preparation of
replicas of high quality should be viewed as a skilled process for which there exists a variety of
techniques that achieve satisfactory results.
This practice presents some guidelines on the preparation of metallic surfaces and production of
replicas and guidelines on evaluation of replica quality. It does not attempt to limit the variations in
technique developed by skilled metallographers, each of which may produce acceptable replicas.
1. Scope 2. Referenced Documents
2
1.1 This practice covers recognized methods for the prepa- 2.1 ASTM Standards:
ration and evaluation of cellulose acetate or plastic film A335/A335MSpecification for Seamless Ferritic Alloy-
replicas which have been obtained from metallographically Steel Pipe for High-Temperature Service
prepared surfaces. It is designed for the evaluation of replicas E3Guide for Preparation of Metallographic Specimens
to ensure that all significant features of a metallographically E7Terminology Relating to Metallography
prepared surface have been duplicated and preserved on the E407Practice for Microetching Metals and Alloys
replica with sufficient detail to permit both LM and SEM
3. Terminology
examination with optimum resolution and sensitivity.
3.1 Definitions—For definitions of terms used in this
1.2 This practice may be used as a controlling document in
practice, refer to Terminology E7.
commercial situations.
1.3 The values stated in SI units are to be regarded as the
4. Significance and Use
standard. Inch-pound units given in parentheses are for infor-
4.1 Replication is a nondestructive sampling procedure that
mation only.
records and preserves the topography of a metallographically
1.4 This standard does not purport to address all of the
prepared surface as a negative relief on a plastic film (replica).
safety concerns, if any, associated with its use. It is the
The replica permits the examination and analysis of the
responsibility of the user of this standard to establish appro-
metallographically prepared surface on the LM or SEM.
priate safety and health practices and determine the applica-
4.2 Enhancement procedures for improving replica contrast
bility of regulatory limitations prior to use.
for microscopic examination are utilized and sometimes nec-
essary (see 8.1).
1
This practice is under the jurisdiction of ASTM Committee E04 on Metallog-
raphy and is the direct responsibility of Subcommittee E04.01 on Specimen
2
Preparation. For referenced ASTM standards, visit the ASTM website, www.astm.org, or
Current edition approved Oct. 1, 2012. Published October 2012. Originally contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
approved in 1990. Last previous edition approved in 2006 as E1351–01(2006). Standards volume information, refer to the standard’s Document Summary page on
DOI: 10.1520/E1351-01R12. the ASTM website.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
E1351 − 01 (2012)
NOTE 1—It is recommended that the purchaser of a field replication tester.Areplicamayalsobemadeonthedecarburizedsurface,ifitserves
service specify that each replicator demonstrate proficiency by providing the purpose of the investigation.
field prepared replica metallography and direct LM and SEM comparison
6.4 Do not remove any precipitates, carbides, nonmetallic
to laboratory prepared samples of an identical mate
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

ASTM
ASTM E340-23(Practice)
Standard Practice for Macroetching Metals and Alloys

SIGNIFICANCE AND USE
3.1 Applications of Macroetching:  
3.1.1 Macroetching is used to reveal the heterogeneity of metals and alloys. Metallographic specimens and chemical analyses will provide the necessary detailed information about specific localities, but they cannot give data about variation from one place to another unless an inordinate number of specimens are taken.  
3.1.2 Macroetching, on the other hand, will provide information on variations in (1) structure, such as grain size, flow lines, columnar structure, dendrites, and so forth; (2) variations in chemical composition as evidenced by segregation, carbide and ferrite banding, coring, inclusions, and depth of carburization or decarburization. The information provided about variations in chemical composition is strictly qualitative but the location of extremes in segregation will be shown. Chemical analyses or other means of determining the chemical composition would have to be performed to determine the extent of variation. Macroetching will also show the presence of discontinuities and voids, such as seams, laps, porosity, flakes, bursts, extrusion rupture, cracks, and so forth.  
3.1.3 Other applications of macroetching in the fabrication of metals are the study of weld structure, definition of weld penetration, dilution of filler metal by base metals, entrapment of flux, porosity, and cracks in weld and heat affected zones, and so forth. It is also used in the heat-treating shop to determine location of hard or soft spots, tong marks, quenching cracks, case depth in shallow-hardening steels, case depth in carburization, effectiveness of stop-off coatings in carburization, and so forth. In the machine shop, it can be used for the determination of grinding cracks in tools and dies.  
3.1.4 Macroetching is used extensively for quality control in the steel industry, to determine the tone of a heat in billets with respect to inclusions, segregation, and structure. Forge shops, in addition, use macroetching to reveal flow...
SCOPE
1.1 These procedures describe the methods of macroetching metals and alloys to reveal their macrostructure.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to the International System (SI) units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
For specific warning statements, see 6.2, 7.1, 8.1.3, 8.2.1, 8.8.3, 8.10.1.1, and 8.13.2. It is further recommended to review the guidance in Guide E2014.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    11 pages
    English language
    sale 15% off
  • Standard
    11 pages
    English language
    sale 15% off
ASTM
ASTM E407-23(Practice)
Standard Practice for Microetching Metals and Alloys

SIGNIFICANCE AND USE
5.1 This practice lists recommended methods and solutions for the etching of specimens for metallographic examination. Solutions are listed that highlight the phases and constituents present in most major alloy systems.
SCOPE
1.1 This practice covers chemical solutions and procedures to be used in etching metals and alloys for microscopic examination. Safety precautions and miscellaneous information are also included.  
1.2 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. For specific cautionary statements, see 6.1 and Table 2.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    22 pages
    English language
    sale 15% off
  • Standard
    22 pages
    English language
    sale 15% off
ASTM
ASTM E45-18a(2023)(Test Method)
Standard Test Methods for Determining the Inclusion Content of Steel

SIGNIFICANCE AND USE
4.1 These test methods cover four macroscopic and five microscopic test methods (manual and image analysis) for describing the inclusion content of steel and procedures for expressing test results.  
4.2 Inclusions are characterized by size, shape, concentration, and distribution rather than chemical composition. Although compositions are not identified, Microscopic methods place inclusions into one of several composition-related categories (sulfides, oxides, and silicates—the last as a type of oxide). Paragraph 11.1.1 describes a metallographic technique to facilitate inclusion discrimination. Only those inclusions present at the test surface can be detected.  
4.3 The macroscopic test methods evaluate larger surface areas than microscopic test methods and because examination is visual or at low magnifications, these methods are best suited for detecting larger inclusions. Macroscopic methods are not suitable for detecting inclusions smaller than about 0.40 mm (1/64 in.) in length and the methods do not discriminate inclusions by type.  
4.4 The microscopic test methods are employed to characterize inclusions that form as a result of deoxidation or due to limited solubility in solid steel (indigenous inclusions). As stated in 1.1, these microscopic test methods rate inclusion severities and types based on morphological type, that is, by size, shape, concentration, and distribution, but not specifically by composition. These inclusions are characterized by morphological type, that is, by size, shape, concentration, and distribution, but not specifically by composition. The microscopic methods are not intended for assessing the content of exogenous inclusions (those from entrapped slag or refractories). In case of a dispute whether an inclusion is indigenous or exogenous, microanalytical techniques such as energy dispersive X-ray spectroscopy (EDS) may be used to aid in determining the nature of the inclusion. However, experience and knowledge of the casting proce...
SCOPE
1.1 These test methods cover a number of recognized procedures for determining the nonmetallic inclusion content of wrought steel. Macroscopic methods include macroetch, fracture, step-down, and magnetic particle tests. Microscopic methods include five generally accepted systems of examination. In these microscopic methods, inclusions are assigned to a category based on similarities in morphology, and not necessarily on their chemical identity. Metallographic techniques that allow simple differentiation between morphologically similar inclusions are briefly discussed. While the methods are primarily intended for rating inclusions, constituents such as carbides, nitrides, carbonitrides, borides, and intermetallic phases may be rated using some of the microscopic methods. In some cases, alloys other than steels may be rated using one or more of these methods; the methods will be described in terms of their use on steels.  
1.2 These test methods cover procedures to perform JK-type inclusion ratings using automatic image analysis in accordance with microscopic methods A and D.  
1.3 Depending on the type of steel and the properties required, either a macroscopic or a microscopic method for determining the inclusion content, or combinations of the two methods, may be found most satisfactory.  
1.4 These test methods deal only with recommended test methods and nothing in them should be construed as defining or establishing limits of acceptability for any grade of steel.  
1.5 The values stated in SI units are to be regarded as standard. The values given in parentheses after SI units are provided for information only and are not considered standard.  
1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory...

  • Standard
    20 pages
    English language
    sale 15% off
ASTM
ASTM E1181-02(2023)(Test Method)
Standard Test Methods for Characterizing Duplex Grain Sizes

SIGNIFICANCE AND USE
5.1 Duplex grain size may occur in some metals and alloys as a result of their thermomechanical processing history. For comparison of mechanical properties with metallurgical features, or for specification purposes, it may be important to be able to characterize grain size in such materials. Assigning an average grain size value to a duplex grain size specimen does not adequately characterize the appearance of that specimen, and may even misrepresent its appearance. For example, averaging two distinctly different grain sizes may result in reporting a size that does not actually exist anywhere in the specimen.  
5.2 These test methods may be applied to specimens or products containing randomly intermingled grains of two or more significantly different sizes (henceforth referred to as random duplex grain size). Examples of random duplex grain sizes include: isolated coarse grains in a matrix of much finer grains, extremely wide distributions of grain sizes, and bimodal distributions of grain size.  
5.3 These test methods may also be applied to specimens or products containing grains of two or more significantly different sizes, but distributed in topologically varying patterns (henceforth referred to as topological duplex grain sizes). Examples of topological duplex grain sizes include: systematic variation of grain size across the section of a product, necklace structures, banded structures, and germinative grain growth in selected areas of critical strain.  
5.4 These test methods may be applied to specimens or products regardless of their state of recrystallization.  
5.5 Because these test methods describe deviations from a single, log-normal distribution of grain sizes, and characterize patterns of variation in grain size, the total specimen cross-section must be evaluated.  
5.6 These test methods are limited to duplex grain sizes as identifiable within a single polished and etched metallurgical specimen. If duplex grain size is suspected in a product too ...
SCOPE
1.1 These test methods provide simple guidelines for deciding whether a duplex grain size exists. The test methods separate duplex grain sizes into one of two distinct classes, then into specific types within those classes, and provide systems for grain size characterization of each type.  
1.2 Units—The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.3 This standard may involve hazardous materials, operations, and equipment. This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    15 pages
    English language
    sale 15% off
ASTM
ASTM E1245-03(2023)(Practice)
Standard Practice for Determining the Inclusion or Second-Phase Constituent Content of Metals by Automatic Image Analysis

SIGNIFICANCE AND USE
5.1 This practice is used to assess the indigenous inclusions or second-phase constituents of metals using basic stereological procedures performed by automatic image analyzers.  
5.2 This practice is not suitable for assessing the exogenous inclusions in steels and other metals. Because of the sporadic, unpredictable nature of the distribution of exogenous inclusions, other methods involving complete inspection, for example, ultrasonics, must be used to locate their presence. The exact nature of the exogenous material can then be determined by sectioning into the suspect region followed by serial, step-wise grinding to expose the exogenous matter for identification and individual measurement. Direct size measurement rather than application of stereological methods is employed.  
5.3 Because the characteristics of the indigenous inclusion population vary within a given lot of material due to the influence of compositional fluctuations, solidification conditions and processing, the lot must be sampled statistically to assess its inclusion content. The largest lot sampled is the heat lot but smaller lots, for example, the product of an ingot, within the heat may be sampled as a separate lot. The sampling of a given lot must be adequate for the lot size and characteristics.  
5.4 The practice is suitable for assessment of the indigenous inclusions in any steel (or other metal) product regardless of its size or shape as long as enough different fields can be measured to obtain reasonable statistical confidence in the data. Because the specifics of the manufacture of the product do influence the morphological characteristics of the inclusions, the report should state the relevant manufacturing details, that is, data regarding the deformation history of the product.  
5.5 To compare the inclusion measurement results from different lots of the same or similar types of steels, or other metals, a standard sampling scheme should be adopted such as described in Test Method...
SCOPE
1.1 This practice describes a procedure for obtaining stereological measurements that describe basic characteristics of the morphology of indigenous inclusions in steels and other metals using automatic image analysis. The practice can be applied to provide such data for any discrete second phase.  
Note 1: Stereological measurement methods are used in this practice to assess the average characteristics of inclusions or other second-phase particles on a longitudinal plane-of-polish. This information, by itself, does not produce a three-dimensional description of these constituents in space as deformation processes cause rotation and alignment of these constituents in a preferred manner. Development of such information requires measurements on three orthogonal planes and is beyond the scope of this practice.  
1.2 This practice specifically addresses the problem of producing stereological data when the features of the constituents to be measured make attainment of statistically reliable data difficult.  
1.3 This practice deals only with the recommended test methods and nothing in it should be construed as defining or establishing limits of acceptability.  
1.4 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    8 pages
    English language
    sale 15% off
ASTM
ASTM E975-22(Test Method)
Standard Test Method for X-Ray Determination of Retained Austenite in Steel with Near Random Crystallographic Orientation

SIGNIFICANCE AND USE
2.1 Significance—Retained austenite with a near random crystallographic orientation is found in the microstructure of heat-treated low-alloy, high-strength steels that have medium (0.40 weight %) or higher carbon contents. Although the presence of retained austenite may not be evident in the microstructure, and may not affect the bulk mechanical properties such as hardness of the steel, the transformation of retained austenite to martensite during service can affect the performance of the steel.  
2.2 Use—The measurement of retained austenite can be included in low-alloy steel development programs to determine its effect on mechanical properties. Retained austenite can be measured on a companion specimen or test section that is included in a heat-treated lot of steel as part of a quality control practice. The measurement of retained austenite in steels from service can be included in studies of material performance.
SCOPE
1.1 This test method covers the determination of retained austenite phase in steel using integrated intensities (area under peak above background) of X-ray diffraction peaks using chromium  Kα  or molybdenum Kα  X-radiation.  
1.2 The method applies to carbon and alloy steels with near random crystallographic orientations of both ferrite and austenite phases.  
1.3 This test method is valid for retained austenite contents from 1 % by volume and above.  
1.4 If possible, X-ray diffraction peak interference from other crystalline phases such as carbides should be eliminated from the ferrite and austenite peak intensities.  
1.5 Substantial alloy contents in steel cause some change in peak intensities which have not been considered in this method. Application of this method to steels with total alloy contents exceeding 15 weight % should be done with care. If necessary, the users can calculate the theoretical correction factors to account for changes in volume of the unit cells for austenite and ferrite resulting from variations in chemical composition.  
1.6 Units—The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.7 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.8 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    7 pages
    English language
    sale 15% off
ASTM
ASTM E7-22(Terminology)
Standard Terminology Relating to Metallography

SIGNIFICANCE AND USE
3.1 Standards of Committee E04 consist of test methods, practices, and guides developed to ensure proper and uniform testing in the field of metallography. In order for one to properly use and interpret these standards, the terminology used in these standards must be understood.  
3.2 The terms used in the field of metallography have precise definitions. The terminology and its proper usage must be completely understood in order to adequately communicate in this field. In this respect, this standard is also a general source of terminology relating to the field of metallography facilitating the transfer of information within the field.

  • Standard
    35 pages
    English language
    sale 15% off
  • Standard
    35 pages
    English language
    sale 15% off
ASTM
ASTM E1351-01(2020)(Practice)
Standard Practice for Production and Evaluation of Field Metallographic Replicas

SIGNIFICANCE AND USE
4.1 Replication is a nondestructive sampling procedure that records and preserves the topography of a metallographically prepared surface as a negative relief on a plastic film (replica). The replica permits the examination and analysis of the metallographically prepared surface on the LM or SEM.  
4.2 Enhancement procedures for improving replica contrast for microscopic examination are utilized and sometimes necessary (see 8.1).
Note 1: It is recommended that the purchaser of a field replication service specify that each replicator demonstrate proficiency by providing field prepared replica metallography and direct LM and SEM comparison to laboratory prepared samples of an identical material by grade and service exposure.
SCOPE
1.1 This practice covers recognized methods for the preparation and evaluation of cellulose acetate or plastic film replicas which have been obtained from metallographically prepared surfaces. It is designed for the evaluation of replicas to ensure that all significant features of a metallographically prepared surface have been duplicated and preserved on the replica with sufficient detail to permit both LM and SEM examination with optimum resolution and sensitivity.  
1.2 This practice may be used as a controlling document in commercial situations.  
1.3 The values stated in SI units are to be regarded as the standard. Inch-pound units given in parentheses are for information only.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    6 pages
    English language
    sale 15% off
ASTM
ASTM E2283-08(2019)(Practice)
Standard Practice for Extreme Value Analysis of Nonmetallic Inclusions in Steel and Other Microstructural Features

ABSTRACT
This practice describes a methodology to statistically characterize the distribution of the largest indigenous non-metallic inclusions in steel specimens based upon quantitative metallographic measurements. This practice enables the experimenter to estimate the extreme value distribution of inclusions in steels. The procedures in determining non-metallic inclusions in steel are presented and discussed in details.
SIGNIFICANCE AND USE
5.1 This practice is used to assess the indigenous inclusions or second-phase constituents in metals using extreme value statistics.  
5.2 It is well known that failures of mechanical components, such as gears and bearings, are often caused by the presence of large nonmetallic oxide inclusions. Failure of a component can often be traced to the presence of a large inclusion. Predictions related to component fatigue life are not possible with the evaluations provided by standards such as Test Methods E45, Practice E1122, or Practice E1245. The use of extreme value statistics has been related to component life and inclusion size distributions by several different investigators (3-8). The purpose of this practice is to create a standardized method of performing this analysis.  
5.3 This practice is not suitable for assessing the exogenous inclusions in steels and other metals because of the unpredictable nature of the distribution of exogenous inclusions. Other methods involving complete inspection such as ultrasonics must be used to locate their presence.
SCOPE
1.1 This practice describes a methodology to statistically characterize the distribution of the largest indigenous nonmetallic inclusions in steel specimens based upon quantitative metallographic measurements. The practice is not suitable for assessing exogenous inclusions.  
1.2 Based upon the statistical analysis, the nonmetallic content of different lots of steels can be compared.  
1.3 This practice deals only with the recommended test methods and nothing in it should be construed as defining or establishing limits of acceptability.  
1.4 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.4.1 For measurements obtained from light microscopy, linear feature parameters shall be reported as micrometers, and feature areas shall be reported as micrometers.  
1.5 The methodology can be extended to other materials and to other microstructural features.  
1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    11 pages
    English language
    sale 15% off
ASTM
ASTM E82/E82M-14(2019)(Test Method)
Standard Test Method for Determining the Orientation of a Metal Crystal

SIGNIFICANCE AND USE
4.1 The physical properties of metals and other materials are often anisotropic (for example: Young's modulus will typically vary in different crystallographic directions). As such, it is often desirable or necessary to determine the orientation of a single crystal to ascertain the relation of any pertinent physical properties with respect to different directions in the material.  
4.2 This test method can be used commercially as a quality control test in production situations in which a desired orientation, within prescribed limits, is required.  
4.3 With the use of an adjustable, fixed holder that can later be mounted on a saw, lathe, or other machine, a single crystal material can be moved to a preferred orientation and subsequently sectioned, ground, or processed otherwise.  
4.4 If the grains in a polycrystalline material are large enough, this test method can also be used to determine their orientations and differences in orientation can be documented or mapped or both.
SCOPE
1.1 This test method covers the back-reflection Laue procedure for determining the orientation of a metal crystal. The back-reflection Laue method for determining crystal orientation may be applied to macrograins and micrograins depending on the beam size within polycrystalline aggregates, as well as to single crystals of any size. This test method is described with reference to cubic crystals and other structures such as: hexagonal, tetragonal, or orthorhombic crystals.  
1.2 Most natural crystals have well developed external faces, and the orientation of such crystals can usually be determined from inspection. The orientation of a crystal having poorly developed faces or no faces at all (for example, a metal crystal prepared in the laboratory) shall be determined by more elaborate methods. The most convenient and accurate of these involves the use of X-ray diffraction. The “orientation of a metal crystal” is known when the positions in space of the crystallographic axes of the unit cell have been located with reference to the surface geometry of the crystal specimen. This relation between unit cell position and surface geometry is most conveniently expressed by stereographic or gnomonic projection.  
1.3 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    8 pages
    English language
    sale 15% off