ASTM B517-98

Standard Specification for Welded Nickel-Chromium-Iron-Alloy (UNS N06600, UNS N06603, UNS N06025, and UNS N06045) Pipe

SCOPE
1.1 This specification  covers welded, cold-worked, and annealed nickel-chromium-iron alloy (UNS N06600),* N06025, and N06045 pipe for general corrosive service and heat-resisting applications.  
1.2 This specification covers outside diameter and nominal wall pipe shown in ANSI B36.19. Pipe having other dimensions may be furnished provided such pipe complies with all other requirements of this specification.  
1.3 The values stated in inch-pound units are to be regarded as the standard.

General Information

• Status: Historical
• Publication Date: 09-Dec-1998
• ICS: 23.040.15 - Non-ferrous metal pipes
• Technical Committee: B02 - Nonferrous Metals and Alloys
• Drafting Committee: B02.07 - Refined Nickel and Cobalt and Their Alloys

Relations

• Replaced By: ASTM B517-03 - Standard Specification for Welded Nickel-Chromium-Iron-Alloy (UNS N06600, UNS N06603, UNS N06025, and UNS N06045) Pipe
• Effective Date: 10-Jul-2003
• Referred By: ASTM B775/B775M-22 - Standard Specification for General Requirements for Nickel and Nickel Alloy Welded Pipe
• Effective Date: 10-Dec-1998
• Referred By: ASTM B366/B366M-23 - Standard Specification for Factory-Made Wrought Nickel and Nickel Alloy Fittings
• Effective Date: 10-Dec-1998

Standards Content (Sample)

NOTICE: This standard has either been superceded and replaced by a new version or discontinued.
Contact ASTM International (www.astm.org) for the latest information.
Designation: B 517 – 98
Standard Specification for
Welded Nickel-Chromium-Iron-Alloy (UNS N06600, UNS
N06603, UNS N06025, and UNS N06045) Pipe
This standard is issued under the fixed designation B 517; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (e) indicates an editorial change since the last revision or reapproval.
1. Scope 4.1.2 ASTM designation and year of issue.
4.1.3 Condition (temper).
1.1 This specification covers welded, cold-worked, and
4.1.4 Dimensions:
annealed nickel-chromium-iron alloy (UNS N06600,*
4.1.4.1 Nominal pipe size or outside diameter and schedule
N06603, N06025, and N06045) pipe for general corrosive
number or nominal wall thickness.
service and heat-resisting applications.
4.1.4.2 Length (specific or random).
1.2 This specification covers outside diameter and nominal
4.1.5 Quantity (feet or metres, or number of pieces).
wall pipe shown in ANSI B36.19. Pipe having other dimen-
4.1.6 Certification—State if certification or a report of test
sions may be furnished provided such pipe complies with all
results is required.
other requirements of this specification.
4.1.7 Samples for Product (Check) Analysis—State whether
1.3 The values stated in inch-pound units are to be regarded
samples for product (check) analysis should be furnished.
as the standard.
4.1.8 Purchaser Inspection—If the purchaser wishes to
2. Referenced Documents witness tests or inspection of material at the place of manu-
facture, the purchase order must so state indicating which tests
2.1 ASTM Standards:
or inspections are to be witnessed.
B 775 Specification for General Requirements for Nickel
and Nickel Alloy Welded Pipe
5. Materials and Manufacture
2.2 ANSI Standard:
5.1 Pipe shall be made from flat-rolled alloy by an auto-
B36.19 Stainless Steel Pipe
matic welding process with no addition of filler metal. Subse-
3. General Requirement quent to welding and prior to final heat treatment, the material
shall be cold worked either in both weld and base metal or in
3.1 Material furnished in accordance with this specification
weld metal only.
shall conform to the applicable requirements of the current
5.2 Pipe shall be furnished with a scale-free finish. When
edition of Specification B 775 unless otherwise provided
bright annealing is used, descaling is not necessary.
herein.
6. Chemical Composition
4. Ordering Information
6.1 The material shall conform to the requirements as to
4.1 It is the responsibility of the purchaser to specify all
chemical composition prescribed in Table 1.
requirements that are necessary for the safe and satisfactory
6.2 If a product (check) analysis is performed by the
performance of material ordered under this specification.
purchaser, the material shall conform to the product (check)
Examples of such requirements include, but are not limited to,
analysis variations in Table 1 of Specification B 775.
the following:
4.1.1 Alloy name or UNS number.
7. Mechanical and Other Requirements
7.1 Mechanical Properties—The material shall conform to
This specification is under the jurisdiction of ASTM Committee B-2 on
the requirements for mechanical properties prescribed in Table
Nonferrous Metals and Alloys and is the direct responsibility of Subcommittee
2.
B02.07 on Refined Nickel and Cobalt and Their Alloys.
Current edition approved Dec. 10, 1998. Published January 1999. Originally
7.2 Flattening Test—Pipe shall be capable of withstanding,
published as B 517 – 70. Last previous edition B 517 – 95.
without cracking, flattening under a load applied gradually at
For ASME Boiler and Pressure Code applications see related Specification
room temperature until the distance between the platens is five
SB-517 in Section II of that Code.
* New designation establ
...