ASTM D5961/D5961M-10
(Test Method)Standard Test Method for Bearing Response of Polymer Matrix Composite Laminates
Standard Test Method for Bearing Response of Polymer Matrix Composite Laminates
SIGNIFICANCE AND USE
This test method is designed to produce bearing response data for material specifications, research and development, quality assurance, and structural design and analysis. The standard configuration for each procedure is very specific and is intended primarily for development of quantitative double- and single-shear bearing response data for material comparison and structural design. Procedures A and D, the double-shear configurations, with a single fastener loaded in shear and reacted by laminate tension or compression, are particularly recommended for basic material evaluation and comparison. Procedures B and C, the single-shear, single- or double-fastener configurations are more useful in evaluation of specific joint configurations, including fastener failure modes. The Procedure B specimen may be tested in either an unstabilized (no support fixture) or stabilized configuration. The unstabilized configuration is intended for tensile loading and the stabilized configuration is intended for compressive loading (although tensile loading is permitted). The Procedure C specimen is particularly well-suited for development of countersunk-fastener bearing strength data where a near-double-shear fastener rotational stiffness is desired. These Procedure B and C configurations have been extensively used in the development of design allowables data.
It is important to note that these four procedures, using the standard test configurations, will generally result in bearing strength mean values that are not of the same statistical population, and thus not in any way a “basic material property.”
Note 2—Typically, Procedure D will yield slightly higher strengths than Procedure A (due to the finite edge distance, e, in Procedure A); while Procedure C will yield significantly higher strengths than Procedure B (due to the larger fastener rotation and higher peak bearing stress in Procedure B). For protruding head fasteners, Procedure D will typically yield somewhat higher resu...
SCOPE
1.1 This test method covers the bearing response of pinned or fastened joints using multi-directional polymer matrix composite laminates reinforced by high-modulus fibers by double-shear tensile loading (Procedure A), single-shear tensile or compressive loading of a two-piece specimen (Procedure B), single-shear tensile loading of a one-piece specimen (Procedure C), or double-shear compressive loading (Procedure D). Standard specimen configurations using fixed values of test parameters are described for each procedure. However, when fully documented in the test report, a number of test parameters may be optionally varied. The composite material forms are limited to continuous-fiber or discontinuous-fiber (tape or fabric, or both) reinforced composites for which the laminate is balanced and symmetric with respect to the test direction. The range of acceptable test laminates and thicknesses are described in 8.2.1.
1.2 This test method is consistent with the recommendations of MIL-HDBK-17, which describes the desirable attributes of a bearing response test method.
1.3 The multi-fastener test configurations described in this test method are similar to those used by industry to investigate the bypass portion of the bearing bypass interaction response for bolted joints, where the specimen may produce either a bearing failure mode or a bypass failure mode. Note that the scope of this test method is limited to bearing and fastener failure modes. Use Test Method D7248/D7248M for by-pass testing.
1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.
1.4.1 Within the text the inch-pound units are shown in brackets.
1.5 This standard does not purport to address a...
General Information
Relations
Buy Standard
Standards Content (Sample)
NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation: D5961/D5961M − 10
StandardTest Method for
1
Bearing Response of Polymer Matrix Composite Laminates
This standard is issued under the fixed designation D5961/D5961M; the number immediately following the designation indicates the
year of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last
reapproval. A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope 1.5 This standard does not purport to address all of the
safety concerns, if any, associated with its use. It is the
1.1 This test method covers the bearing response of pinned
responsibility of the user of this standard to establish appro-
or fastened joints using multi-directional polymer matrix
priate safety and health practices and determine the applica-
composite laminates reinforced by high-modulus fibers by
bility of regulatory limitations prior to use.
double-sheartensileloading(ProcedureA),single-sheartensile
or compressive loading of a two-piece specimen (Procedure
2. Referenced Documents
B), single-shear tensile loading of a one-piece specimen
2
2.1 ASTM Standards:
(Procedure C), or double-shear compressive loading (Proce-
D792 Test Methods for Density and Specific Gravity (Rela-
dure D). Standard specimen configurations using fixed values
tive Density) of Plastics by Displacement
of test parameters are described for each procedure. However,
D883 Terminology Relating to Plastics
when fully documented in the test report, a number of test
D953 Test Method for Bearing Strength of Plastics
parameters may be optionally varied. The composite material
D2584 Test Method for Ignition Loss of Cured Reinforced
forms are limited to continuous-fiber or discontinuous-fiber
Resins
(tape or fabric, or both) reinforced composites for which the
D2734 TestMethodsforVoidContentofReinforcedPlastics
laminate is balanced and symmetric with respect to the test
D3171 Test Methods for Constituent Content of Composite
direction. The range of acceptable test laminates and thick-
Materials
nesses are described in 8.2.1.
D3410/D3410M Test Method for Compressive Properties of
1.2 Thistestmethodisconsistentwiththerecommendations
Polymer Matrix Composite Materials with Unsupported
of MIL-HDBK-17, which describes the desirable attributes of
Gage Section by Shear Loading
a bearing response test method.
D3878 Terminology for Composite Materials
1.3 The multi-fastener test configurations described in this
D5229/D5229M TestMethodforMoistureAbsorptionProp-
test method are similar to those used by industry to investigate
erties and Equilibrium Conditioning of Polymer Matrix
the bypass portion of the bearing bypass interaction response
Composite Materials
for bolted joints, where the specimen may produce either a
D5687/D5687M Guide for Preparation of Flat Composite
bearing failure mode or a bypass failure mode. Note that the
Panels with Processing Guidelines for Specimen Prepara-
scope of this test method is limited to bearing and fastener
tion
failure modes. Use Test Method D7248/D7248M for by-pass
D7248/D7248M Test Method for Bearing/Bypass Interac-
testing.
tion Response of Polymer Matrix Composite Laminates
Using 2-Fastener Specimens
1.4 The values stated in either SI units or inch-pound units
E4 Practices for Force Verification of Testing Machines
are to be regarded separately as standard. The values stated in
E6 Terminology Relating to Methods of Mechanical Testing
each system may not be exact equivalents; therefore, each
E83 Practice for Verification and Classification of Exten-
system shall be used independently of the other. Combining
someter Systems
values from the two systems may result in non-conformance
E122 Practice for Calculating Sample Size to Estimate,With
with the standard.
Specified Precision, the Average for a Characteristic of a
1.4.1 Within the text the inch-pound units are shown in
Lot or Process
brackets.
E177 Practice for Use of the Terms Precision and Bias in
ASTM Test Methods
1
This test method is under the jurisdiction of ASTM Committee D30 on
Composite Materials and is the direct responsibility of Subcommittee D30.05 on
2
Structural Test Methods. For referenced ASTM standards, visit the ASTM website, www.astm.org, or
Current edition approved Oct. 1, 2010. Published November 2010. Originally contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
approved in 1996. Last previous edition approved in 2008 as D5961/D5961M – 08. Standards volume information, refer to the standard’s Document Summary page on
DOI: 10.1520/D5961_D5961M-10. the ASTM website.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1
---------------------- Page: 1 ----------------------
D5961/D5961M − 10
E238 Test Method for Pi
...
This document is not anASTM standard and is intended only to provide the user of anASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation:D5961/D5961M–08 Designation:D5961/D5961M–10
Standard Test Method for
1
Bearing Response of Polymer Matrix Composite Laminates
This standard is issued under the fixed designation D5961/D5961M; the number immediately following the designation indicates the
year of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last
reapproval. A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope
1.1 This test method covers the bearing response of pinned or fastened joints using multi-directional polymer matrix composite
laminates reinforced by high-modulus fibers by double-shear tensile loading (Procedure A), single-shear tensile or compressive
loading of a two-piece specimen (Procedure B), single-shear tensile loading of a one-piece specimen (Procedure C), or
double-shear compressive loading (Procedure D). Standard specimen configurations using fixed values of test parameters are
described for each procedure. However, when fully documented in the test report, a number of test parameters may be optionally
varied. The composite material forms are limited to continuous-fiber or discontinuous-fiber (tape or fabric, or both) reinforced
composites for which the laminate is balanced and symmetric with respect to the test direction. The range of acceptable test
laminates and thicknesses are described in 8.2.1.
1.2 This test method is consistent with the recommendations of MIL-HDBK-17, which describes the desirable attributes of a
bearing response test method.
1.3 The multi-fastener test configurations described in this test method are similar to those used by industry to investigate the
bypassportionofthebearingbypassinteractionresponseforboltedjoints,wherethespecimenmayproduceeitherabearingfailure
mode or a bypass failure mode. Note that the scope of this test method is limited to bearing and fastener failure modes. Use Test
Method D7248/D7248M for by-pass testing.
1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. Within the text the
inch-pound units are shown in brackets. The values stated in each system aremay not be exact equivalents; therefore, each system
mustshall be used independently of the other. Combining values from the two systems may result in non-conformance with the
standard.
1.4.1 Within the text the inch-pound units are shown in brackets.
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility
of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory
limitations prior to use.
2. Referenced Documents
2
2.1 ASTM Standards:
D792 Test Methods for Density and Specific Gravity (Relative Density) of Plastics by Displacement
D883 Terminology Relating to Plastics
D953 Test Method for Bearing Strength of Plastics
D2584 Test Method for Ignition Loss of Cured Reinforced Resins
D2734 Test Methods for Void Content of Reinforced Plastics
D3171 Test Methods for Constituent Content of Composite Materials
D3410/D3410M Test Method for Compressive Properties of Polymer Matrix Composite Materials with Unsupported Gage
Section by Shear Loading
D3878 Terminology for Composite Materials
D5229/D5229M Test Method for MoistureAbsorption Properties and Equilibrium Conditioning of Polymer Matrix Composite
Materials
D5687/D5687M Guide for Preparation of Flat Composite Panels with Processing Guidelines for Specimen Preparation
1
This test method is under the jurisdiction ofASTM Committee D30 on Composite Materials and is the direct responsibility of Subcommittee D30.05 on Structural Test
Methods.
´1
Current edition approved Sept. 15, 2008. Published November 2008. Originally approved in 1996. Last previous edition approved in 2005 as D5961/D5961M–05 . DOI:
10.1520/D5961_D5961M-08.
Current edition approved Oct. 1, 2010. Published November 2010. Originally approved in 1996. Last previous edition approved in 2008 as D5961/D5961M – 08. DOI:
10.1520/D5961_D5961M-10.
2
For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at service@astm.org. For Annual Book of ASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
1
---------------------- Page: 1 ----------------------
D5961/D5961M–10
D72
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.