Standard Specification for General Requirements for Nickel and Nickel Alloy Welded Tube

Standard Specification for General Requirements for Nickel and Nickel Alloy Welded Tube

SCOPE
1.1 This specification contains various requirements that, with the exception of Sections 6 and 7, are mandatory requirements to the following ASTM nickel and nickel alloy, longitudinally welded tubular product specifications:Title of SpecificationASTM DesignationWelded UNS N08020, N08024, and UNS N08026 Alloy TubesB 468Welded UNS N08120, UNS N08800, UNS N08810, UNS N08811 Alloy TubesB 515Welded Nickel-Chromium-Iron Alloy (UNS N06600, UNS N06603, UNS N06025, and UNS N06045) TubesB 516Welded Nickel and Nickel-Cobalt Alloy TubeB 626UNS N08904, UNS N08925, and UNS N08926 Welded TubeB 674UNS N08366 and UNS N08367 Welded TubeB 676Welded UNS N06625, N06219, and N08825 Alloy TubesB 704Ni-Cr-Mo-Co-W-Fe-Si Alloy (UNS N06333) Welded TubeB 726Welded Nickel (UNS N02200/UNS N02201) and Nickel Copper Alloy (UNS N04400) Tube B 730
1.2 One or more of the test requirements of Section 6 apply only if specifically stated in the product specification or in the purchase order.
1.3 In case of conflict between a requirement of the product specification and a requirement of this general specification, only the requirement of the product specification need be satisfied.
1.4 The values stated in inch-pound units are to be regarded as the standard. The values given in parentheses are for information only.
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Material Safety Data Sheet for this product/material as provided by the manufacturer, to establish appropriate safety and health practices, and determine the applicability of regulatory limitations prior to use.

General Information

Status
Historical
Publication Date
09-Oct-2002
ICS
77.150.40 - Nickel and chromium products
Technical Committee
B02 - Nonferrous Metals and Alloys
Drafting Committee
B02.07 - Refined Nickel and Cobalt and Their Alloys
Current Stage
Ref Project

Relations

Replaces
ASTM B751-01 - Standard Specification for General Requirements for Nickel and Nickel Alloy Welded Tube
Effective Date
10-Oct-2002
Replaced By
ASTM B751-03 - Standard Specification for General Requirements for Nickel and Nickel Alloy Welded Tube
Effective Date
10-Jun-2003
Referred By
ASTM B726-02(2021) - Standard Specification for Nickel-Chromium-Molybdenum-Cobalt-Tungsten-Iron-Silicon Alloy (UNS N06333) Welded Tube
Effective Date
10-Oct-2002
Referred By
ASTM B468-10(2020) - Standard Specification for Welded UNS N08020 Alloy Tubes
Effective Date
10-Oct-2002
Referred By
ASTM B674-21 - Standard Specification for Nickel-Iron-Chromium-Molybdenum and Iron-Nickel-Chromium-Molybdenum-Copper Welded Tube
Effective Date
10-Oct-2002
Referred By
ASTM B739-03(2023) - Standard Specification for Nickel-Iron-Chromium-Silicon Alloy Welded Tube
Effective Date
10-Oct-2002
Referred By
ASTM B515-22 - Standard Specification for Welded Nickel-Iron-Chromium Alloy Tubes
Effective Date
10-Oct-2002
Referred By
ASTM B676-19 - Standard Specification for UNS N08367 Welded Tube
Effective Date
10-Oct-2002
Referred By
ASTM B626-19 - Standard Specification for Welded Nickel and Nickel-Cobalt Alloy Tube
Effective Date
10-Oct-2002
Referred By
ASTM B924-02(2022) - Standard Specification for Seamless and Welded Nickel Alloy Condenser and Heat Exchanger Tubes With Integral Fins
Effective Date
10-Oct-2002
Referred By
ASTM B730-08(2018) - Standard Specification for Welded Nickel (UNS N02200/UNS N02201) and Nickel Copper Alloy (UNS N04400) Tube
Effective Date
10-Oct-2002
Referred By
ASTM B516-18 - Standard Specification for Welded Nickel-Chromium-Aluminum Alloy (UNS N06699) and Nickel-Chromium-Iron Alloy (UNS N06600, UNS N06601, UNS N06603, UNS N06025, UNS N06045, UNS N06690, and UNS N06693) Tubes
Effective Date
10-Oct-2002
Referred By
ASTM B704-19 - Standard Specification for Welded Nickel Alloy Tubes
Effective Date
10-Oct-2002

Buy Standard

ASTM B751-02 - Standard Specification for General Requirements for Nickel and Nickel Alloy Welded TubeASTM B751-02 - Standard Specification for General Requirements for Nickel and Nickel Alloy Welded Tube
PreviousNext
Technical specification
ASTM B751-02 - Standard Specification for General Requirements for Nickel and Nickel Alloy Welded Tube
English language
6 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)

NOTICE: This standard has either been superceded and replaced by a new version or discontinued.
Contact ASTM International (www.astm.org) for the latest information.
Designation: B 751 – 02
Standard Specification for
General Requirements for Nickel and Nickel Alloy Welded
1
Tube
This standard is issued under the fixed designation B 751; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (e) indicates an editorial change since the last revision or reapproval.
1. Scope 2. Referenced Documents
1.1 This specification contains various requirements that, 2.1 ASTM Standards:
with the exception of Sections 6 and 7, are mandatory B 880 Specification for General Requirements for Chemical
requirements to the following ASTM nickel and nickel alloy, Check Analysis Limits for Nickel, Nickel Alloys and
2
longitudinally welded tubular product specifications: Cobalt Alloys
4
E 8 Test Methods for Tension Testing of Metallic Materials
ASTM
Title of Specification
2,3
Designation
E 18 Test Methods for Rockwell Hardness and Rockwell
Welded UNS N08020, N08024, and UNS N08026 Alloy Tubes B 468
4
Superficial Hardness of Metallic Materials
Welded UNS N08120, UNS N08800, UNS N08810, UNS B 515
E 29 Practice for Using Significant Digits in Test Data to
N08811 Alloy Tubes
5
Welded Nickel-Chromium-Iron Alloy (UNS N06600, UNS B 516
Determine Conformance with Specifications
N06603, UNS N06025, and UNS N06045) Tubes
6
E 39 Test Methods for Chemical Analysis of Nickel
Welded Nickel and Nickel-Cobalt Alloy Tube B 626
UNS N08904, UNS N08925, and UNS N08926 Welded Tube B 674 E 76 Test Methods for Chemical Analysis of Nickel-Copper
7
UNS N08366 and UNS N08367 Welded Tube B 676
Alloys
Welded UNS N06625, N06219, and N08825 Alloy Tubes B 704
E 112 Test Methods for Determining the Average Grain
Ni-Cr-Mo-Co-W-Fe-Si Alloy (UNS N06333) Welded Tube B 726
4
Welded Nickel (UNS N02200/UNS N02201) and Nickel Cop- B 730 Size
per Alloy (UNS N04400) Tube
E 213 Practice for Ultrasonic Examination of Metal Pipe
8
and Tubing
1.2 One or more of the test requirements of Section 6 apply
E 273 Practice for Ultrasonic Examination of the Weld
only if specifically stated in the product specification or in the
8
Zone of Welded Pipe and Tubing
purchase order.
E 309 Practice for Eddy-Current Examination of Steel Tu-
1.3 In case of conflict between a requirement of the product
8
bular Products Using Magnetic Saturation
specification and a requirement of this general specification,
E 426 Practice for Electromagnetic (Eddy-Current) Exami-
only the requirement of the product specification need be
nation of Seamless and Welded Tubular Products, Austen-
satisfied.
8
itic Stainless Steel and Similar Alloys
1.4 The values stated in inch-pound units are to be regarded
E 571 Practice for Electromagnetic (Eddy-Current) Exami-
as the standard. The values given in parentheses are for
8
nation of Nickel and Nickel Alloy Tubular Products
information only.
E 1473 Test Methods for Chemical Analysis of Nickel,
1.5 This standard does not purport to address all of the
7
Cobalt, and High-Temperature Alloys
safety concerns, if any, associated with its use. It is the
2.2 Other Documents:
responsibility of the user of this standard to become familiar
SNT-TC-1A Recommended Practice for Nondestructive
with all hazards including those identified in the appropriate
9
Personnel Qualification and Certification
Material Safety Data Sheet for this product/material as pro-
vided by the manufacturer, to establish appropriate safety and
3. Terminology
health practices, and determine the applicability of regulatory
3.1 Definitions:
limitations prior to use.
1 4
This specification is under the jurisdiction of ASTM Committee B02 on Annual Book of ASTM Standards, Vol 03.01.
5
Nonferrous Metals and Alloys and is the direct responsibility of Subcommittee Annual Book of ASTM Standards, Vol 14.02.
6
B02.07 on Refined Nickel and Cobalt and Their Alloys. Discontinued; See Annual Book of ASTM Standards, Vol 03.05.
7
Current edition approved Oct. 10, 2002. Published December 2002. Originally Annual Book of ASTM Standards, Vol 03.05.
8
published as B 751 – 85. Last previous edition B 751 – 01. Annual Book of ASTM Standards, Vol 03.03.
2 9
Annual Book of ASTM Standards, Vol 02.04. Available from The American Society for Nondestructive Testing (ASNT), P.O.
3
Annual Book of ASTM Standards, Vol 02.01. Box 28518, 1711 Arlingate Ln., Columbus, OH 43228-0518.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
1

---------------------- Page: 1 ----------------------
NOTICE: This standard has either been superceded and replaced by a new version or discontinued.
Contact ASTM International (www.astm.org) for the latest information.
B751–02
A
TABLE 2 Permissible Variations in Length
3.1.1 average diameter
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

ASTM
ASTM B472-23(Specification)
Standard Specification for Nickel Alloy Billets and Bars for Reforging

ABSTRACT
This specification covers UNS N06002, UNS N06030, UNS N06035, UNS N06022, UNS N06200, UNS N06230, UNS N06600, UNS N06617, UNS N06625, UNS N08020, UNS N08026, UNS N08024, UNS N08120, UNS N08926, UNS N08367, UNS N10242, UNS N10276, UNS N10665, UNS N10675, UNS N12160, UNS R20033, UNS N06059, UNS N06686, UNS N10629, UNS N08031, UNS N06045, UNS N06025, and UNS R30556 nickel alloy billets and bars for reforging. The products shall be hot worked from ingots by rolling, forging, extruding, hammering, or pressing. The material shall conform to the chemical composition requirements prescribed by the reference material. The chemical composition of the material shall be determined by chemical analysis in accordance with test method E1473.
SCOPE
1.1 This specification covers UNS N06002, UNS N06030, UNS N06035, UNS N06022, UNS N06200, UNS N10362, UNS N06230, UNS N06600, UNS N06617, UNS N06625, UNS N08020, UNS N08026, UNS N08024, UNS N08120, UNS N08926, UNS N08367, UNS N10242, UNS N10276, UNS N10665, UNS N10675, UNS N12160, UNS R20033, UNS N06059, UNS N06686, UNS N10629, UNS N08031, UNS N06045, UNS N06025, UNS N06699, and UNS R305562 billets and bars for reforging.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Safety Data Sheet (SDS) for this product/material as provided by the manufacturer, to establish appropriate safety, health, and environmental practices, and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    5 pages
    English language
    sale 15% off
  • Technical specification
    5 pages
    English language
    sale 15% off
ASTM
ASTM B637-23(Specification)
Standard Specification for Precipitation-Hardening and Cold Worked Nickel Alloy Bars, Forgings, and Forging Stock for Moderate or High Temperature Service

ABSTRACT
This specification covers hot- and cold-worked precipitation-hardenable nickel alloy rod, bar, forgings, and forging stock for high-temperature service. Chemical analysis shall be performed on the alloy and shall conform to the chemical composition requirement in carbon, manganese, silicon, phosphorus, sulfur, chromium, cobalt, molybdenum, columbium, tantalum, titanium, aluminum, zirconium, boron, iron, copper, and nickel. The material shall follow recommended annealing treatment, solution treatment, stabilizing treatment, and precipitation hardening treatment. Tension testing, hardness testing and stress-rupture testing shall be performed on the material and shall comply to the required tensile strength, yield strength, elongation, reduction in area, and Brinell hardness.
SCOPE
1.1 This specification2 covers hot- and cold-worked precipitation-hardenable nickel alloy rod, bar, forgings, and forging stock for moderate or high temperature service (Table 1).  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Safety Data Sheet (SDS) for this product/material as provided by the manufacturer, to establish appropriate safety, health, and environmental practices, and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    7 pages
    English language
    sale 15% off
  • Technical specification
    7 pages
    English language
    sale 15% off
ASTM
ASTM B446-23(Specification)
Standard Specification for Nickel-Chromium-Molybdenum-Niobium Alloy, Nickel-Chromium-Molybdenum-Silicon Alloy, and Nickel-Chromium-Molybdenum-Tungsten Alloy Rod and Bar

ABSTRACT
This specification covers nickel-chromium-molybdenum-columbium (UNS N06625), nickel-chromium-molybdenum-silicon alloy (UNS N06219), and nickel-chromium-molybdenum-tungsten alloy (UNS N06650) in the form of hot-worked rod and bar and cold-worked rod. The matreial shall conform to the required chemical composition for carbon, manganese, silicon, phosphorus, sulfur, chromium, columbium, tantalum, cobalt, molybdenum, iorn, aluminum, titanium, copper, nickel, tungsten, and nitrogen. The materials shall conform to the the heat treatment and room temperature tensile properties such as tensile strength, yield strength, and elongation. Dimensions of the alloys such as diameter, thickness, or width, length and straightness shall also be determined.
SCOPE
1.1 This specification covers nickel-chromium-molybdenum-niobium alloy (UNS N06625), nickel-chromium-molybdenum-silicon alloy (UNS N06219), and Nickel-Chromium-Molybdenum-Tungsten Alloy (UNS N06650)2 in the form of both hot-worked and cold-worked rod and bar in the conditions shown in Table 1.  
1.1.1 UNS N06625 products are furnished in three grades of different heat-treated conditions:
1.1.1.1 Grade 1 (Annealed)—Material is normally employed in service temperatures up to 1100 °F (593 °C).
1.1.1.2 Grade 2 (Solution Annealed)—Material is normally employed in service temperatures above 1100 °F (593 °C) when resistance to creep and rupture is required.  
Note 1: Hot-working or reannealing may change properties significantly, depending on working history and temperatures.
1.1.1.3 Grade 3 (Solution Annealed and Cold Worked)—Material is normally employed in services where higher strengths are needed.  
1.1.2 Alloys UNS N06219 and UNS N06650 are supplied in solution annealed condition only.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 The following precautionary caveat pertains only to the test methods portion, Section 12, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Safety Data Sheet (SDS) for this product/material as provided by the manufacturer, to establish appropriate safety, health, and environmental practices, and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    6 pages
    English language
    sale 15% off
  • Technical specification
    6 pages
    English language
    sale 15% off
ASTM
ASTM B474/B474M-19(2023)(Specification)
Standard Specification for Electric Fusion Welded Nickel and Nickel Alloy Pipe

ABSTRACT
This specification covers electric fusion welded pipe suitable for high-temperature or corrosive service. The pipes are designated into five classes namely Class 1, Class 2, Class 3, Class 4 and Class 5, according to how they are to be welded. The joints shall be full penetration double-welded or single-welded butt joints employing fusion welding processes. The furnished pipe shall undergo heat treatment and a chemical analysis shall be employed for both plate and weld. Each pipe shall be subjected to transverse tension test, transverse guided weld bend test and hydrostatic pressure test.
SCOPE
1.1 This specification covers electric fusion welded pipe suitable for high-temperature or corrosive service as listed in Table 1. (Although no restrictions are placed on the sizes of pipe that may be furnished under this specification, commercial practice is commonly limited to sizes not less than 8 in. [203 mm] nominal diameter.)  
1.2 Five classes of pipe are covered as follows:  
1.2.1 Class 1—Pipe shall be double welded by processes employing filler metal in all passes and shall be completely radiographed.  
1.2.2 Class 2—Pipe shall be double welded by processes employing filler metal in all passes. No radiography is required.  
1.2.3 Class 3—Pipe shall be single welded by processes employing filler metal in all passes and shall be completely radiographed.  
1.2.4 Class 4—Same as Class 3 except that the weld pass exposed to the inside pipe surface may be made without the addition of filler metal.  
1.2.5 Class 5—Pipe shall be double welded by processes employing filler metal in all passes and shall be spot radiographed.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Safety Data Sheet (SDS) for this product/material as provided by the manufacturer, to establish appropriate safety, health, and environmental practices, and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    6 pages
    English language
    sale 15% off
ASTM
ASTM B574-23(Specification)
Standard Specification for Low-Carbon Nickel-Chromium-Molybdenum, Low-Carbon Nickel-Molybdenum-Chromium, Low-Carbon Nickel-Molybdenum-Chromium-Tantalum, Low-Carbon Nickel-Chromium-Molybdenum-Copper, and Low-Carbon Nickel-Chromium-Molybdenum-Tungsten Alloy Rod and Bar

ABSTRACT
This specification2 covers rod of low-carbon nickel-chromium- molybdenum alloys (UNS N10276, N06022, N06035, N06455, N06058, and N06059), low-carbon nickel-molybdenum- chromium-tantalum (UNS N06210), low-carbon nickel-chromium-molybdenum-copper alloy (UNS N06200), and low-carbon nickel-chromium-molybdenum-tungsten (UNS N06686), for use in general corrosive service. Product and chemical analyses shall be performed on the materials and shall conform to the required chemical composition in molybdenum, chromium, iron, tungsten, cobalt, carbon, silicon, manganese, vanadium, phosphorus, sulfur, titanium, nickel, aluminum, copper, and tantalum. Tension test shall be performed and shall comply to required mechanical properties for hot or cold finished, solution annealed rods such as tensile strength, yield strength, and elongation.
SCOPE
1.1 This specification2 covers rod and bar of low-carbon nickel-chromium-molybdenum alloys (UNS N10276, N06022, N06035, N06044, N06455, N06058, and N06059), low-carbon nickel-molybdenum-chromium (USN N10362), low-carbon nickel-molybdenum-chromium-tantalum (UNS N06210), low-carbon nickel-chromium-molybdenum-copper alloy (UNS N06200), and low-carbon nickel-chromium-molybdenum-tungsten (UNS N06686) as shown in Table 1, for use in general corrosive service.      
1.2 The following products are covered under this specification:  
1.2.1 Rods and Bars 5/16 in. to 3/4 in. (7.94 mm to 19.05 mm), exclusive, in dimension3, solution annealed and pickled, or mechanically descaled.  
1.2.2 Rods and Bars 3/4 in. to 31/2 in. (19.05 mm to 88.9 mm), inclusive, in dimension3, solution annealed, ground or turned.  
1.2.3 Rods and Bars 1/4 in. to 3 1/2 in. (6.35 mm to 88.9 mm), inclusive, in dimension3, solution annealed, cold worked, ground or turned (N06022, N06059, N06686, and N10276, see Table 2 and Table 3).  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Safety Data Sheet (SDS) for this product/material as provided by the manufacturer, to establish appropriate safety, health, and environmental practices, and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    6 pages
    English language
    sale 15% off
  • Technical specification
    6 pages
    English language
    sale 15% off
ASTM
ASTM B167-23(Specification)
Standard Specification for Nickel-Chromium-Aluminum Alloys, Nickel-Chromium-Iron Alloys, Nickel-Chromium-Cobalt-Molybdenum Alloy, Nickel-Iron-Chromium-Tungsten Alloy, and Nickel-Chromium-Molybdenum-Copper Alloy Seamless Pipe and Tube

ABSTRACT
This specification covers nickel-chromium-iron alloys (UNS N06600, N06601, N06603, N06690, N06693, N06025, N06045, and N06696) and nickel-chromium-cobalt molybdenum alloy (UNS N06617) in cold-worked annealed, hot-worked annealed, and hot-finished seamless pipe and tube intended for general corrosion resistant and heat resistant applications. The material shall conform to the required chemical composition for nickel, chromium, iron, manganese, molybdenum, cobalt, aluminum, carbon, copper, boron, silicon, sulfur, titanium, niobium, phosphorous, zirconium, yttrium, and cerium. The following test methods shall be performed on the alloys, namely: chemical analysis, tension test, and hydrostatic or nondestructive electric test. The material shall conform to the required mechanical properties such as tensile strength, yield strength, elongation, nondestructive electric test, and rounding method.
SCOPE
1.1 This specification2 covers nickel-chromium-aluminum alloys (UNS N06699), nickel-chromium-iron alloys (UNS N06600, N06601, N06603, N06690, N06693, N06025, N06045, and N06696),3 nickel-chromium-cobalt-molybdenum alloy (UNS N06617), nickel-iron-chromium-tungsten alloy (UNS N06674), and nickel-chromium-molybdenum-copper alloy (UNS N06235) in cold-worked annealed, hot-worked annealed, and hot-finished seamless pipe and tube intended for general corrosion resistant and heat resistant applications.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 The following safety hazards caveat pertains only to the test methods portion, Section 13, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Safety Data Sheet (SDS) for this product/material as provided by the manufacturer, to establish appropriate safety, health, and environmental practices, and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    9 pages
    English language
    sale 15% off
  • Technical specification
    9 pages
    English language
    sale 15% off
ASTM
ASTM B668-23(Specification)
Standard Specification for Iron-Nickel-Chromium-Molybdenum Alloy Seamless Pipe and Tube

ABSTRACT
This specification covers the standard requirements for UNS N08028 seamless cold-finished or hot-finished pipe and tube intended for general corrosive services. The pipe and tube shall be furnished in the solution-annealed condition and heat treated at a certain range of temperature by subsequent quenching in water or rapidly cooling by other means. Chemical and product analysis shall be conducted on each lot of material as described in a referenced ASTM document and shall conform to the required chemical composition for carbon, silicon, manganese, phosphorus, sulfur, chromium, nickel, molybdenum, copper, and iron. The material shall also be subjected to tension test, flaring test, and hydrostatic or nondestructive test to determine its mechanical properties which shall be in conformity with the tensile strength, yield strength, and elongation requirements.
SCOPE
1.1 This specification covers UNS N08028 and N08029 seamless cold-finished or hot-finished pipe and tube intended for general corrosive service.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    2 pages
    English language
    sale 15% off
  • Technical specification
    2 pages
    English language
    sale 15% off
ASTM
ASTM B444-23(Specification)
Standard Specification for Nickel-Chromium-Molybdenum-Niobium Alloys and Nickel-Chromium-Molybdenum-Silicon Alloy Pipe and Tube

ABSTRACT
This specification covers UNS N06625 and UNS N06852 nickel-chromium-molybdenum-columbium alloys and UNS N06219 nickel-chromium-molybdenum-silicon alloy in the form of cold-worked seamless pipe and tube. UNS N06625 products are furnished in annealed Grade 1 and solution annealed Grade 2 while UNS N06219 and UNS N06852 are in solution annealed condition only. Chemical testing shall be performed on each type of material and shall conform to the chemical composition limits specified for carbon, manganese, silicon, phosphorus, sulfur, chromium, tantalum, columbium, cobalt, molybdenum, iron, aluminum, titanium, copper, and nickel. The material shall undergo tensile testing and shall conform to the required room temperature tensile properties like tensile strength, yield strength, and elongation depending on the heat treatment used and including small diameter and light-walled tubing. Each pipe or tube shall undergo hydrostatic testing and shall conform to the allowable fiber stress and also be examined with a nondestructive electric test as prescribed.
SCOPE
1.1 This specification2 covers nickel-chromium-molybdenum-niobium alloys (UNS N06625 and UNS N06852) and nickel-chromium-molybdenum-silicon alloy (UNS N06219)3 in the form of cold-worked seamless pipe and tube. The general requirements for pipe and tube are covered by Specification B829.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 The following precautionary caveat pertains only to the test methods portion, Section 8, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Safety Data Sheet (SDS) for this product/material as provided by the manufacturer, to establish appropriate safety, health, and environmental practices, and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    5 pages
    English language
    sale 15% off
  • Technical specification
    5 pages
    English language
    sale 15% off
ASTM
ASTM B581-17(2023)(Specification)
Standard Specification for Nickel-Chromium-Iron-Molybdenum-Copper Alloy Rod

ABSTRACT
This specification covers nickel-chromium-iron-molybdenum-copper alloy rods (UNS N06007, N06975, N06985, N06030, and N08031), hot- or cold-finished, solution annealed, ground, or turned, for use in general corrosive service. Heat and product (check) analysis of the alloy shall conform to the chemical composition requirements prescribed for nickel, chromium, iron, molybdenum, copper, manganese, cobalt, carbon, tungsten, silicon, phosphorus, sulfur, columbium and tantalum, titanium, and nitrogen. The material shall conform to the specified straightness criteria and to the mechanical property requirements including tensile strength, yield strength, and elongation, as determined by tension test.
SCOPE
1.1 This specification2 covers rod of Ni-Cr-Fe-Mo-Cu alloys (UNS N06007, N06975, N06985, N06030, N08031, and N08034)3 as shown in Tables 1-3, for use in general corrosive service.    
1.2 The following products are covered under this specification:  
1.2.1 Rods 5/16 in. to 3/4 in. (7.94 mm to 19.05 mm) excl in diameter, hot- or cold-finished, solution annealed and pickled or mechanically descaled.  
1.2.2 Rods 3/4 in. to 31/2 in. (19.05 mm to 88.9 mm) incl in diameter, hot- or cold-finished, solution annealed, ground or turned.  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    4 pages
    English language
    sale 15% off
ASTM
ASTM B805-23(Specification)
Standard Specification for Precipitation Hardening Nickel Alloys Bar and Wire

ABSTRACT
This specification covers UNS N07716, N07725, N07773, N07776, N09777, and N09925 nickel alloy hot or cold finished rounds, squares, hexagons, rectangles, and cold finished wires. Bars should be supplied in solution treated conditions while wires should be in both solution-treated and cold-finished conditions. The recommended solution treatment should consist of heating the material to a certain temperature followed by rapid cooling. Solution-treated materials should at least conform to the minimum room temperature mechanical properties and should be suitable for subsequent age hardening.
SCOPE
1.1 This specification covers nickel alloys UNS N07716, N07725, N07773, N07776, N09777, and N09925 in the form of hot or cold finished rounds, squares, hexagons, rectangles, and cold finished wire.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 The following precautionary caveat pertains only to the test methods, portion, Section 13, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Safety Data Sheet (SDS) for this product/material as provided by the manufacturer, to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    7 pages
    English language
    sale 15% off
  • Technical specification
    7 pages
    English language
    sale 15% off