Standard Test Method for Change of Resistance With Temperature of Metallic Materials for Electrical Heating

Standard Test Method for Change of Resistance With Temperature of Metallic Materials for Electrical Heating

SIGNIFICANCE AND USE
2.1 The change in resistance with temperature for heating element materials is a major design factor and may influence material selection. The measurement of this change is essential to ensure that heating elements perform as designed. This test method was designed to minimize the effect different manufacturing processes have on resistance change, thereby yielding results that are reproducible.
SCOPE
1.1 This test method covers the determination of the change of resistance with temperature of metallic materials for electrical heating, and is applicable over the range of service temperatures.  
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Material Safety Data Sheet (MSDS) for this product/material as provided by the manufacturer, to establish appropriate safety and health practices, and determine the applicability of regulatory limitations prior to use.

General Information

Status
Historical
Publication Date
30-Apr-2013
ICS
77.040.01 - Testing of metals in general
Technical Committee
B02 - Nonferrous Metals and Alloys
Drafting Committee
B02.10 - Thermostat Metals and Electrical Resistance Heating Materials
Current Stage
Ref Project

Relations

Replaces
ASTM B70-90(2007) - Standard Test Method for Change of Resistance With Temperature of Metallic Materials for Electrical Heating
Effective Date
01-May-2013
Replaced By
ASTM B70-90(2019) - Standard Test Method for Change of Resistance With Temperature of Metallic Materials for Electrical Heating
Effective Date
01-Apr-2019
Referred By
ASTM B603-07(2018) - Standard Specification for Drawn or Rolled Iron-Chromium-Aluminum Alloys for Electrical Heating Elements
Effective Date
01-May-2013
Referred By
ASTM B344-20 - Standard Specification for Drawn or Rolled Nickel-Chromium and Nickel-Chromium-Iron Alloys for Electrical Heating Elements
Effective Date
01-May-2013

Buy Standard

ASTM B70-90(2013) - Standard Test Method for Change of Resistance With Temperature of Metallic Materials for Electrical HeatingASTM B70-90(2013) - Standard Test Method for Change of Resistance With Temperature of Metallic Materials for Electrical Heating
PreviousNext
Standard
ASTM B70-90(2013) - Standard Test Method for Change of Resistance With Temperature of Metallic Materials for Electrical Heating
English language
2 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)


NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation: B70 − 90 (Reapproved 2013)
Standard Test Method for
Change of Resistance With Temperature of Metallic
Materials for Electrical Heating
This standard is issued under the fixed designation B70; the number immediately following the designation indicates the year of original
adoption or, in the case of revision, the year of last revision.Anumber in parentheses indicates the year of last reapproval.Asuperscript
epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope end, shall be attached by welding, at a distance from the
corresponding current lead not less than one tenth of the length
1.1 This test method covers the determination of the change
of the specimen between the potential leads.
of resistance with temperature of metallic materials for elec-
trical heating, and is applicable over the range of service 3.2 When the resistance is to be measured with a Wheat-
temperatures. stone bridge, only the current leads are required.The resistance
of the leads in this case shall not exceed 1 % of the resistance
1.2 The values stated in SI units are to be regarded as
of the specimen and the leads shall be made of the same type
standard. No other units of measurement are included in this
of alloy as the test specimen. For both methods of
standard.
measurement, the leads shall have a length within the heated
1.3 This standard does not purport to address all of the
zone of the furnace of at least 50 times their minimum
safety concerns, if any, associated with its use. It is the
transverse dimension, in order to avoid disturbance of the
responsibility of the user of this standard to become familiar
temperature of the specimen by conduction of heat to the
with all hazards including those identified in the appropriate
colder parts of the furnace.
Material Safety Data Sheet (MSDS) for this product/material
as provided by the manufacturer, to establish appropriate
4. Electric Furnace
safety and health practices, and determine the applicability of
4.1 The furnace for heating the specimen shall be of such a
regulatory limitations prior to use.
type that the temperature can be controlled over the range from
room temperature to the maximum desired. It shall be so
2. Significance and Use
constructed that the specimens and the thermocouples can be
2.1 The change in resistance with temperature for heating
maintained at a uniform and constant temperature at desired
element materials is a major design factor and may influence
points within the working range. The specimen and thermo-
material selection. The measurement of this change is essential
couples shall be so shielded as to prevent direct radiation from
to ensure that heating elements perform as designed. This test
hotter, or to colder, parts of the furnace.
method was designed to minimize the effect different manu-
4.2 In order to test the uniformity of the temperature in the
facturingprocesseshaveonresistancechange,therebyyielding
region to be occupied by the test specimen, a typical specimen
results that are reproducible.
and thermocouple shall be prepared and mounted in the center
of this region.The furnace shall then be heated to its maximum
3. Test Specimen and Leads
temperature and maintained at this temperature until equilib-
3.1 Thetestspecimenshallbepreparedfrommaterialasleft
rium is reached. The specimen shall then be moved in the
by the manufacturing process, and in a form suitable for
furnace in the direction of the maximum temperature gradient
measuring its resistance in an electric furnace. When the
through a distance equal to the maximum dimension of the
resistance is to be measured with a Kelvin bridge,
largest specimen and thermocouple assembly which is to be
potentiometer, digital ohmmeter, or equivalent, a current lead
usedinthisfurnace.Thetemperatureofthetypicalspecimenin
shall be welded to each end of the specimen in such a manner
this position shall not differ from that in the normal position by
that there will be no change of current distribution in the
more than 10°C.
specimen during measurements. Potential leads, one at each
5. Resistance Measurements
5.1 A Kelvin bridge, potentiometer, digital ohmmeter, or
This test method is under the jurisdiction of ASTM Committee B02 on
Nonferrous Metals and Alloys and is the direct responsibility of Subcommittee
equivalent shall be used when measuring specimens having
B02.10 on Thermostat Metals and Electrical Resistance Heating Materials.
resistances less than 10Ω. A Wheatstone bridge may be used
Current edition approved May 1, 2013. Published May 2013. Originally
with specimens having resistances greater than 10 Ω. The
approved in 1927. Last previous edition approved in 2007 as B70 – 90 (2007). DOI:
10.1520/B0070-90R13. resistance of the specimen shall be measured with an accuracy
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
B70 − 90 (2013)
of 0.1 %. The measuring current shall be so small that the ture of test for the alloy in question, and hold at this value until
resistance of a specimen is not changed thereby as much as the resistance of the specimen remains constant except for the
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

ASTM
ASTM B70-90(2019)(Test Method)
Standard Test Method for Change of Resistance With Temperature of Metallic Materials for Electrical Heating

SIGNIFICANCE AND USE
2.1 The change in resistance with temperature for heating element materials is a major design factor and may influence material selection. The measurement of this change is essential to ensure that heating elements perform as designed. This test method was designed to minimize the effect different manufacturing processes have on resistance change, thereby yielding results that are reproducible.
SCOPE
1.1 This test method covers the determination of the change of resistance with temperature of metallic materials for electrical heating, and is applicable over the range of service temperatures.  
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    2 pages
    English language
    sale 15% off
ASTM
ASTM E531-23(Practice)
Standard Practice for Surveillance Testing of High-Temperature Nuclear Component Materials

SIGNIFICANCE AND USE
4.1 The practice contained herein can be used as a basis for establishing conditions for the safe operation of critical structural components. The practices provide for general plant assessment and verification that materials continue meet design criteria and may in addition be of use for asset protection or life extension. The test specimens and procedures presented in this practice are for guidance when establishing a surveillance program.  
4.2 This practice for high-temperature materials surveillance programs is used when nuclear reactor component materials are monitored by specimen testing. Periodic testing is performed through the service life of the components to assess changes in selected material properties that are caused by neutron irradiation, thermal effects, chemical reactions, and mechanical stress. The properties of interest are those used as design criteria for the respective nuclear components or well correlated to said criteria (see 5.1.6). The need for surveillance arises from the need to assess predictions of aging material performance to ensure adequate component performance.  
4.3 This practice describes specimens and procedures required for the surveillance of multiple components. A surveillance program for a particular component will not necessarily require all test types described herein.
SCOPE
1.1 This practice covers procedures for surveillance program design and specimen testing to establish changes occurring in the mechanical properties of ferrous and nickel-based materials due to irradiation and thermal effects of nuclear component metallic materials used for high-temperature structural applications above 370 °C (700 °F). This should include consideration of gamma heating. This practice currently only applies to an initial program based on initial estimates of design life of components.  
1.2 This practice was developed for non-light-water moderated nuclear power reactors.  
1.3 This practice does not provide specific procedures for extending surveillance programs beyond their original design lifetimes.  
1.4 This practice does not consider in-situ monitoring techniques but may provide insights into the proper periodicity and design of such.  
1.5 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    6 pages
    English language
    sale 15% off
ASTM
ASTM E112-13(2021)(Test Method)
Standard Test Methods for Determining Average Grain Size

SIGNIFICANCE AND USE
4.1 These test methods cover procedures for estimating and rules for expressing the average grain size of all metals consisting entirely, or principally, of a single phase. The grain size of specimens with two phases, or a phase and a constituent, can be measured using a combination of two methods, a measurement of the volume fraction of the phase and an intercept or planimetric count (see Section 17). The test methods may also be used for any structures having appearances similar to those of the metallic structures shown in the comparison charts. The three basic procedures for grain size estimation are:  
4.1.1 Comparison Procedure—The comparison procedure does not require counting of either grains, intercepts, or intersections but, as the name suggests, involves comparison of the grain structure to a series of graded images, either in the form of a wall chart, clear plastic overlays, or an eyepiece reticle. There appears to be a general bias in that comparison grain size ratings claim that the grain size is somewhat coarser (1/2 to 1 G number lower) than it actually is (see X1.3.5). Repeatability and reproducibility of comparison chart ratings are generally ±1 grain size number.  
4.1.2 Planimetric Procedure—The planimetric method involves an actual count of the number of grains within a known area. The number of grains per unit area, NA , is used to determine the ASTM grain size number, G. The precision of the method is a function of the number of grains counted. A precision of ±0.25 grain size units can be attained with a reasonable amount of effort. Results are free of bias and repeatability and reproducibility are less than ±0.5 grain size units. An accurate count does require marking off of the grains as they are counted.  
4.1.3 Intercept Procedure—The intercept method involves an actual count of the number of grains intercepted by a test line or the number of grain boundary intersections with a test line, per unit length of test line, used to calculate t...
SCOPE
1.1 These test methods cover the measurement of average grain size and include the comparison procedure, the planimetric (or Jeffries) procedure, and the intercept procedures. These test methods may also be applied to nonmetallic materials with structures having appearances similar to those of the metallic structures shown in the comparison charts. These test methods apply chiefly to single phase grain structures but they can be applied to determine the average size of a particular type of grain structure in a multiphase or multiconstituent specimen.  
1.2 These test methods are used to determine the average grain size of specimens with a unimodal distribution of grain areas, diameters, or intercept lengths. These distributions are approximately log normal. These test methods do not cover methods to characterize the nature of these distributions. Characterization of grain size in specimens with duplex grain size distributions is described in Test Methods E1181. Measurement of individual, very coarse grains in a fine grained matrix is described in Test Methods E930.  
1.3 These test methods deal only with determination of planar grain size, that is, characterization of the two-dimensional grain sections revealed by the sectioning plane. Determination of spatial grain size, that is, measurement of the size of the three-dimensional grains in the specimen volume, is beyond the scope of these test methods.  
1.4 These test methods describe techniques performed manually using either a standard series of graded chart images for the comparison method or simple templates for the manual counting methods. Utilization of semi-automatic digitizing tablets or automatic image analyzers to measure grain size is described in Test Methods E1382.  
1.5 These test methods deal only with the recommended test methods and nothing in them should be construed as defining or establishing limits of acceptability or fitness of purpose of the ma...

  • Standard
    28 pages
    English language
    sale 15% off
ASTM
ASTM E3315-21(Specification)
Standard Specification for Certification of Metallic Materials

ABSTRACT
This specification covers the requirements for material certifications, specifically including materials under the jurisdiction of Committee E29. It defines terminology related thereto, including melt mill, traceability, heat number vs. lot number, certificate of compliance, and specifies the information to be included on material certifications. Hence the document is an authoritative reference to dispel the incorrect interpretations put forth by unknowledgeable segments of the metals industry.
SCOPE
1.1 This specification covers the requirements for material certifications, specifically including materials under the jurisdiction of Committee E29, as well as defining terminology related thereto.  
1.2 The values stated in inch-pound units are to be regarded as standard. No other units of measurement are included in this standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    3 pages
    English language
    sale 15% off
ASTM
ASTM D8075-16(2021)(Guide)
Standard Guide for Categorization of Microstructural and Microtextural Features Observed in Optical Micrographs of Graphite

SIGNIFICANCE AND USE
4.1 The purpose of this guide is to provide a framework for consistent description of microstructural and microtextural features visible in optical micrographs of graphite. It also provides some guidance on sample preparation and image processing.
SCOPE
1.1 This guide covers the identification and the assignment of microstructural and microtextural features observed in optical micrographs of graphite. The objective of this guide is to establish a consistent approach to the categorization of such features to aid unambiguous discussion of optical micrographs in the scientific literature. It also provides guidance on specimen preparation and the compilation of micrographs.  
1.2 The values stated in SI units are to be regarded as the standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Guide
    12 pages
    English language
    sale 15% off
ASTM
ASTM E127-20(Practice)
Standard Practice for Fabrication and Control of Flat Bottomed Hole Ultrasonic Standard Reference Blocks

SIGNIFICANCE AND USE
5.1 Standard reference block sets per 4.1 fabricated in accordance with this practice will exhibit specific area-amplitude and distance amplitude relationships only with an immersion test at 5 MHz using the search unit, test instrument, and test parameters described in this practice. Comparison tests at other frequencies or with uncalibrated instruments will not necessarily give the same relationships shown in this practice. See Ref (1)5 for area-amplitude limitations at other frequencies and transducer diameters. Also see Ref (2) for cautions regarding use of standard blocks for test standardizations.  
5.2 Reference standards fabricated per 4.2 may utilize the fabrication and verification techniques herein. Due to the variable nature of non-standard blocks, the details should be agreed upon in the ordering documents.
SCOPE
1.1 This practice covers a procedure for fabrication and control of metal alloy reference blocks used in ultrasonic examinations that contain flat bottom holes (FBH).  
1.2 These blocks may be used for checking the performance of ultrasonic examination instrumentation and search units and for standardization and control of ultrasonic examination of metal alloy products.  
1.3 The reference blocks described are suitable for use with either the direct-contact method or immersion pulse-echo ultrasonic methods.  
1.4 Standard sets are described for flat surface sound entry; the Basic set, Area-Amplitude set, and Distance Amplitude set.  
1.5 The requirements for FBH fabrication may be applied to round bar/billet reference standards and reference standards fabricated from other product forms.  
1.6 This practice does not specify reference reflector sizes or product rejection limits. It does describe fabrication practices and applied tolerances. In all cases of conflict between this practice and customer specifications, the customer specification shall prevail.  
1.7 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.8 This practice has incorporated the requirements of Practice E428 and Guide E1158. Reference standards that were manufactured under Practice E428 and Guide E1158 comply with the requirements of this practice.  
1.9 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.10 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    16 pages
    English language
    sale 15% off
  • Standard
    16 pages
    English language
    sale 15% off
ASTM
ASTM B70-90(2019)(Test Method)
Standard Test Method for Change of Resistance With Temperature of Metallic Materials for Electrical Heating

SIGNIFICANCE AND USE
2.1 The change in resistance with temperature for heating element materials is a major design factor and may influence material selection. The measurement of this change is essential to ensure that heating elements perform as designed. This test method was designed to minimize the effect different manufacturing processes have on resistance change, thereby yielding results that are reproducible.
SCOPE
1.1 This test method covers the determination of the change of resistance with temperature of metallic materials for electrical heating, and is applicable over the range of service temperatures.  
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    2 pages
    English language
    sale 15% off
ASTM
ASTM E768-99(2018)(Guide)
Standard Guide for Preparing and Evaluating Specimens for Automatic Inclusion Assessment of Steel

SIGNIFICANCE AND USE
4.1 Inclusion ratings done either manually using Test Methods E45 or automatically using Practice E1122 or E1245 are influenced by the quality of specimen preparation. This guide provides examples of proven specimen preparation methods that retain inclusions in polished steel specimens.  
4.2 This guide provides a procedure to determine if the prepared specimens are of suitable quality for subsequent rating of inclusions. None of these methods should be construed as defining or establishing specific procedures or limits of acceptability for any steel grade.
SCOPE
1.1 This guide2 covers two preparation methods for steel metallographic specimens that will be analyzed for nonmetallic inclusions with automatic image analysis (AIA) equipment. The two methods of preparation are offered as accepted methods used to retain nonmetallic inclusions in steel. This guide does not limit the user to these methods.  
1.2 A procedure to test the suitability of the prepared specimen for AIA inclusion work, using differential interference contrast (DIC), is presented.  
1.3 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Guide
    5 pages
    English language
    sale 15% off
ASTM
ASTM G148-97(2018)(Practice)
Standard Practice for Evaluation of Hydrogen Uptake, Permeation, and Transport in Metals by an Electrochemical Technique

SIGNIFICANCE AND USE
5.1 The procedures described, herein, can be used to evaluate the severity of hydrogen charging of a material produced by exposure to corrosive environments or by cathodic polarization. It can also be used to determine fundamental properties of materials in terms of hydrogen diffusion (for example, diffusivity of hydrogen) and the effects of metallurgical, processing, and environmental variables on diffusion of hydrogen in metals.  
5.2 The data obtained from hydrogen permeation tests can be combined with other tests related to hydrogen embrittlement or hydrogen induced cracking to ascertain critical levels of hydrogen flux or hydrogen content in the material for cracking to occur.
SCOPE
1.1 This practice gives a procedure for the evaluation of hydrogen uptake, permeation, and transport in metals using an electrochemical technique which was developed by Devanathan and Stachurski.2 While this practice is primarily intended for laboratory use, such measurements have been conducted in field or plant applications. Therefore, with proper adaptations, this practice can also be applied to such situations.  
1.2 This practice describes calculation of an effective diffusivity of hydrogen atoms in a metal and for distinguishing reversible and irreversible trapping.  
1.3 This practice specifies the method for evaluating hydrogen uptake in metals based on the steady-state hydrogen flux.  
1.4 This practice gives guidance on preparation of specimens, control and monitoring of the environmental variables, test procedures, and possible analyses of results.  
1.5 This practice can be applied in principle to all metals and alloys which have a high solubility for hydrogen, and for which the hydrogen permeation is measurable. This method can be used to rank the relative aggressivity of different environments in terms of the hydrogen uptake of the exposed metal.  
1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    10 pages
    English language
    sale 15% off
ASTM
ASTM D6152/D6152M-12(2024)(Specification)
Standard Specification for SEBS-Modified Mopping Asphalt Used in Roofing

ABSTRACT
This specification covers SEBS (styrene-ethylenebutylene-styrene)-modified mopping asphalt intended for use in built-up roof construction, construction of some modified bitumen systems, construction of bituminous vapor retarder systems, and for adhering insulation boards used in various types of roofing systems. This specification is intended as a material specification and issues regarding the suitability of specific roof constructions or application techniques are beyond its scope. The specified tests and property values are intended to establish minimum properties. In place system design criteria or performance attributes are factors beyond the scope of this specification. The base asphalt shall be prepared from crude petroleum and the SEBS-modified asphalt shall incorporate sufficient SEBS as the primary polymeric modifier. The SEBS modified asphalt shall be homogeneous and free of water and shall conform to the prescribed physical properties including (1) softening point before and after heat exposure, (2) softening point change, (3) flash point, (4) penetration before and after heat exposure, (5) penetration change, (6) solubility in trichloroethylene, (7) tensile elongation, (8) elastic recovery, and (9) low temperature flexibility. The sampling and test methods to determine compliance with the specified physical properties, as well as the evaluation for stability during heat exposure are detailed.
SCOPE
1.1 This specification covers SEBS (styrene-ethylene-butylene-styrene)-modified asphalt intended for use in built-up roof construction, construction of some modified bitumen systems, construction of bituminous vapor retarder systems, and for adhering insulation boards used in various types of roof systems.  
1.2 This specification is intended as a material specification. Issues regarding the suitability of specific roof constructions or application techniques are beyond its scope.  
1.3 The specified tests and property values used to characterize SEBS-modified asphalt are intended to establish minimum properties. In-place system design criteria or performance attributes are factors beyond the scope of this specification.  
1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.5 This standard does not purport to address the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    3 pages
    English language
    sale 15% off