Standard Test Method for Freeze-thaw and De-icing Salt Durability of Solid Concrete Interlocking Paving Units

Standard Test Method for Freeze-thaw and De-icing Salt Durability of Solid Concrete Interlocking Paving Units

SCOPE
1.1 This test method covers the resistance to freezing and thawing of solid interlocking concrete paving units conforming to the dimensional requirements of Specification C 936. Units are tested in a test solution that is either water or 3 % saline solution, depending on the intended use of the units in actual service.
1.2 The values stated in SI units are to be regarded as the standard.
This standard does not purport to address all of the safety concerns, in any, associated with its use. It is the responsibility of the use of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitation prior to use.

General Information

Status
Historical
Publication Date
31-May-2006
ICS
91.080.40 - Concrete structures
Technical Committee
C15 - Manufactured Masonry Units
Drafting Committee
C15.03 - Concrete Masonry Units and Related Units
Current Stage
Ref Project

Relations

Replaced By
ASTM C1645/C1645M-09 - Standard Test Method for Freeze-thaw and De-icing Salt Durability of Solid Concrete Interlocking Paving Units
Effective Date
15-Jul-2009
Referred By
ASTM C936/C936M-23 - Standard Specification for Solid Concrete Interlocking Paving Units
Effective Date
01-Jun-2006
Referred By
ASTM C1790-21 - Standard Specification for Fly Ash Facing Brick
Effective Date
01-Jun-2006
Referred By
ASTM C1782/C1782M-23 - Standard Specification for Segmental Concrete Paving Slabs
Effective Date
01-Jun-2006

Buy Standard

ASTM C1645-06 - Standard Test Method for Freeze-thaw and De-icing Salt Durability of Solid Concrete Interlocking Paving UnitsASTM C1645-06 - Standard Test Method for Freeze-thaw and De-icing Salt Durability of Solid Concrete Interlocking Paving Units
PreviousNext
Standard
ASTM C1645-06 - Standard Test Method for Freeze-thaw and De-icing Salt Durability of Solid Concrete Interlocking Paving Units
English language
2 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation:C1645–06
Standard Test Method for
Freeze-thaw and De-icing Salt Durability of Solid Concrete
1
Interlocking Paving Units
This standard is issued under the fixed designation C1645; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (e) indicates an editorial change since the last revision or reapproval.
1. Scope 4. Apparatus
1.1 This test method covers the resistance to freezing and 4.1 Freezing-and-Thawing Apparatus—The freezing appa-
thawingofsolidinterlockingconcretepavingunitsconforming ratus shall consist of suitable cabinet or cold room with
to the dimensional requirements of Specification C936. Units controls to reach and maintain an air temperature of −5 6 3°C
are tested in a test solution that is either water or 3% saline (23 6 5°F) within1hof introduction of specimens. The
solution, depending on the intended use of the units in actual thawing chamber shall maintain a controlled air temperature.
service. This temperature shall never be greater than + 30°C (86°F).
1.2 The values stated in SI units are to be regarded as the 4.2 Balance—Abalance capable of weighing 500 g with an
standard. accuracyof 60.1gshallbeusedformeasuringthemassofthe
1.3 This standard does not purport to address all of the fine spalled material.
safety concerns, in any, associated with its use. It is the 4.3 Oven—The oven shall be vented and capable of being
responsibility of the use of this standard to establish appropri- maintained at 60 6 2°C (140 6 4°F).
ate safety and health practices and determine the applicability 4.4 Specimen Container—The specimen container shall be
of regulatory limitation prior to use. made of non-corroding flexible material and have dimensions
that allow complete submersion of the specimen in the test
2. Referenced Documents
solution.The size of the container shall be less than or equal to
2
2.1 ASTM Standards:
three times the volume of the unit that is being tested. The
C936 Specification for Solid Concrete Interlocking Paving container shall prevent evaporation of the test solution.
Units
5. Sampling
3. Significance and Use
5.1 Selection of Test Specimens—Select whole units repre-
3.1 This test method is intended to determine the effects of sentative of the lot from which they are selected. The units
freezing and thawing on units conforming to the dimensional
shall be free from visible cracks, chipped edges, and structural
requirements of Specification C936 while immersed in a test defects.
solution. Other types of segmental concrete paving units that
5.2 Number of Test Specimens—Sample according to the
do not conform to the dimensional requirements of Specifica- requirements of Specification C936.
tion C936 may be tested using this method.
5.3 Identification—Mark each test specimen so that it is
3.2 The results from this test method are not intended to identifiable at any time.
provide a quantitative measure of the length of service from
6. Preparation of Test Specimens
paving units conforming to the dimensional requirements of
Specification C936. 6.1 Curing and Conditioning—Test specimens shall consist
offullsizeunits,aminimumof28daysold.Aftersampling,all
test specimens shall be cured for 14 days in a moist chamber
1
ThisspecificationisunderthejurisdictionofASTMCommitteeC27onPrecast
(cabinetorroom)atanairtemperatureof23 62°C(73 64°F)
Concrete Products and is the direct responsibility of Subcommittee C27.20 on
and a relative humidity of at least 90%. Moist curing shall be
Architectural and Structural Products.
Current edition approved on June 1, 2006. Published June 2006.
followed by air curing for a minimum of 14 days at 23 6 5°C
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
(73 6 9°F) at a minimum 40% relative humidity.
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
6.1.1 After air curing, specimens then shall be oven condi-
Standards volume information, refer to the standard’s Document Summary page on
the ASTM website. tioned for 48 h 62hat60° 6 2°C (140 6 4°F).
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
1

---------------------- Page: 1 ----------------------
C1645–06
6.1.2 Before testing begins, the specimens shall be brushed material collected at the bottom of the containers shall be
clean with a stiff bristled brush and all loose burrs and edge washed, filtered using an 80 µm filter paper, and dried to a
shards shall be removed with a carborundum stone. constant mass. This residue shall be defined as mass loss
expressedingrams.Theresidueshallbecumulativelyweighed
after 10, 25, and 50 (if necessary) cycles.
7. Procedure
7.5.1 If t
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

ASTM
ASTM C1645-22a(Test Method)
Standard Test Method for Freeze-thaw and De-icing Salt Durability of Solid Concrete Interlocking Paving Units

SIGNIFICANCE AND USE
3.1 This test method is intended to determine the effects of freezing and thawing on units conforming to the dimensional requirements of Specification C936/C936M while immersed in a test solution. Other types of segmental concrete paving units that do not conform to the dimensional requirements of Specification C936/C936M may be tested using this test method.  
3.2 The results from this test method are not intended to provide a quantitative measure of the length of service from concrete paving units conforming to the dimensional requirements of Specification C936/C936M.
SCOPE
1.1 This test method evaluates the resistance to freezing and thawing of solid interlocking concrete paving units conforming to the dimensional requirements of Specification C936/C936M. Units are tested in a test solution that is either tap water or 3 % saline solution, depending on the intended use of the units in actual service.  
1.2 The values stated in SI units are to be regarded as standard. The values given in parentheses after SI units are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    4 pages
    English language
    sale 15% off
  • Standard
    4 pages
    English language
    sale 15% off
ASTM
ASTM C1262/C1262M-18(Test Method)
Standard Test Method for Evaluating the Freeze-Thaw Durability of Dry-Cast Segmental Retaining Wall Units and Related Concrete Units

SIGNIFICANCE AND USE
4.1 The procedure described in this test method is intended to determine the effects of freezing and thawing on SRW and related units in the presence of potable tap water or saline solution.  
4.2 The procedure is not intended to provide a quantitative measure to determine an expected length of service for a specific type of concrete unit.
Note 2: The testing laboratory performing this test method should be evaluated in accordance with Practice C1093.
SCOPE
1.1 This test method covers the resistance to freezing and thawing of dry-cast segmental retaining wall (SRW) units (see Specification C1372) and related concrete units. Units are tested in a test solution that is either potable tap water or 3 % saline solution depending on the intended use of the units in actual service.  
Note 1: Related concrete units include units such as hollow and solid concrete masonry units, concrete brick, and concrete roof pavers.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with this standard. Some values have only SI units because the inch-pound equivalents are not used in practice.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    5 pages
    English language
    sale 15% off
  • Standard
    5 pages
    English language
    sale 15% off
ASTM
ASTM D7088-17(2023)(Practice)
Standard Practice for Resistance to Hydrostatic Pressure for Coatings Used in Below Grade Applications Applied to Masonry

SIGNIFICANCE AND USE
4.1 This test is meant to simulate the ability of a coating applied to a basement or other below grade masonry walls to prevent the intrusion of water through the coating caused by hydrostatic pressure from water on the outside of the structure.
SCOPE
1.1 This practice is for the evaluation of coatings used in below grade applications to resist the passage of water through concrete block.  
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    3 pages
    English language
    sale 15% off
ASTM
ASTM G109-23(Test Method)
Standard Test Methods for Determining Effects of Chemical Admixtures on Corrosion of Embedded Steel Reinforcement in Concrete Exposed to Chloride Environments

SIGNIFICANCE AND USE
3.1 These test methods provide a reliable means for predicting the inhibiting or corrosive properties of admixtures to be used in concrete.  
3.2 The total integrated (coulombs) current is calculated to provide an indication of the corrosion that occurs due to the macrocell corrosion.  
3.3 These test methods are useful for development studies of corrosion inhibitors to be used in concrete.  
3.4 These test methods have been used elsewhere with good agreement between corrosion as measured by these test methods and corrosion damage on the embedded steel (1-4).4 These test methods might not properly rank the performance of different corrosion inhibitors, especially at concrete covers over the steel less than 40 mm (1.5 in.) or water-to-cement ratios above 0.45. The concrete mixture proportions and cover over the steel are chosen to accelerate chloride ingress. Some inhibitors might have an effect on this process, which could lead to results that would differ from what would be expected in actual use (5).
SCOPE
1.1 These test methods cover a procedure for determining the effects of chemical admixtures on the corrosion of metals in concrete. These test methods can be used to evaluate materials intended to inhibit chloride-induced corrosion of steel in concrete. It can also be used to evaluate the corrosivity of admixtures in a chloride environment.  
1.2 The values stated in SI units are to be regarded as standard. The values given in parentheses after SI units are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    6 pages
    English language
    sale 15% off
  • Standard
    6 pages
    English language
    sale 15% off
ASTM
ASTM D4258-23(Practice)
Standard Practice for Surface Cleaning Concrete for Coating

SIGNIFICANCE AND USE
4.1 Surface cleaning is used to prepare concrete surfaces for applying coatings intended for light-duty service.  
4.2 Use of this practice alone is not intended where protective systems will be used for continuous or intermittent immersion, mechanical loading, or for protective systems needing optimum bond for satisfactory performance (see Practices D4259 and D4260).
SCOPE
1.1 This practice includes surface cleaning of concrete to remove grease, dirt, and loose material prior to the application of coatings. Procedures include broom cleaning, vacuum cleaning, air blast cleaning, water cleaning, detergent water cleaning, and steam cleaning.  
1.2 This practice is not intended to alter the surface profile of the concrete but to clean the surface.  
1.3 The values stated in inch-pound units are to be regarded as standard. No other units of measurement are included in this standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    3 pages
    English language
    sale 15% off
  • Standard
    3 pages
    English language
    sale 15% off
ASTM
ASTM D4260-23(Practice)
Standard Practice for Liquid and Gelled Acid Etching of Concrete

SIGNIFICANCE AND USE
5.1 This practice is used to prepare concrete for coatings where optimum bond is desired for service conditions such as continuous or intermittent immersion, temperature cycling, or mechanical loading.
SCOPE
1.1 This practice covers surface preparation of concrete to prepare the surface prior to the application of coatings.  
1.2 This practice is intended to alter the surface profile of the concrete and to remove foreign materials and weak surface laitance.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. For specific hazard statements, see Section 6.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    3 pages
    English language
    sale 15% off
  • Standard
    3 pages
    English language
    sale 15% off
ASTM
ASTM C1603-23(Test Method)
Standard Test Method for Measurement of Solids in Water

SIGNIFICANCE AND USE
4.1 This test method is used to determine the solids content of mixing water used to produce concrete when one or more of the water sources is wash water from concrete production operations or water that contains solids when batched as mixing water in concrete.  
4.2 The test method provides a means to determine the relationship between the density and solids content of water for compliance with solids content limits of mixing water such as in Specification C1602/C1602M.  
4.3 During production of concrete, the water property measured is its density, which can then be used to estimate the solids content from procedures described in this test method.  
4.4 To develop a correlation between the density and solids content of water, water samples should be tested that cover the range of solids concentrations anticipated during production.
SCOPE
1.1 This test method covers the measurement of the solids content in water for use as mixing water in ready-mixed concrete and the measurement of its density. Solids content is expressed in terms of parts per million (ppm) or in terms of percent by mass of the water sample.  
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.3 The text of this standard references notes and footnotes that provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    4 pages
    English language
    sale 15% off
  • Standard
    4 pages
    English language
    sale 15% off
ASTM
ASTM D7234-22(Test Method)
Standard Test Method for Pull-Off Strength of Coatings on Concrete Using Portable Pull-Off Adhesion Testers

SIGNIFICANCE AND USE
5.1 The pull-off strength and mode of failure of a coating from a concrete substrate are important performance properties that are used in specifications. This test method serves as a means for uniformly preparing and testing coated surfaces, and evaluating and reporting the results.  
5.2 Variations in strength results obtained using different instruments, different substrates, or different loading fixtures with the same coating are possible. Therefore, it is recommended that the specific test instrument and loading fixture be mutually agreed upon between the interested parties.  
5.3 It is recommended that the coating be sufficiently cured to ensure cohesive strength and adhesion. This required minimum cure time before testing should be provided by the coating manufacturer, and may require an extension due to atmospheric conditions on site (for example, low temperature, and low or high humidity).  
5.4 This test method may be adapted to determine surface strength of uncoated concrete (see X2.1). Test Method C1583 is also suitable for that determination.  
5.5 The objective of this method is to determine the adhesion of a coating to concrete (or adapted for surface strength as stated in 5.4) and will result in failure in the coating or near the substrate surface. If evaluating the cohesive strength of the substrate or cementitious surfacers is the purpose of the testing, or if the substrate or cementitious surfacers have low strength, then Test Method C1583 may be more suitable.
SCOPE
1.1 This test method covers procedures for evaluating the pull-off strength of a coating on concrete. Pull-Off strength of coatings for other rigid substrates is described in Test Method D4541. The test determines the greatest perpendicular force (in tension) that a surface area can bear before a plug of material is detached. Failure will occur along the weakest plane within the system comprised of the loading fixture, glue, coating system, and substrate, and will be exposed by the fracture surface.  
1.2 This test method uses a class of apparatus known as portable pull-off adhesion testers.2 They are capable of applying a concentric load and counter load to a single surface so that coatings can be tested even though only one side is accessible. Measurements are limited by the strength of adhesion bonds between the loading fixture, coating system and the substrate or the cohesive strengths of the glue, coating layers, and substrate.  
1.3 This test method is suitable for both laboratory and field testing.  
1.4 Pull-off strength measurements depend upon both material and instrumental parameters. There are different instruments used that comply with this test method. The specific instrument used should be identified when reporting results. This test is destructive and spot repairs may be necessary.  
1.5 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    9 pages
    English language
    sale 15% off
  • Standard
    9 pages
    English language
    sale 15% off
ASTM
ASTM C1645-22a(Test Method)
Standard Test Method for Freeze-thaw and De-icing Salt Durability of Solid Concrete Interlocking Paving Units

SIGNIFICANCE AND USE
3.1 This test method is intended to determine the effects of freezing and thawing on units conforming to the dimensional requirements of Specification C936/C936M while immersed in a test solution. Other types of segmental concrete paving units that do not conform to the dimensional requirements of Specification C936/C936M may be tested using this test method.  
3.2 The results from this test method are not intended to provide a quantitative measure of the length of service from concrete paving units conforming to the dimensional requirements of Specification C936/C936M.
SCOPE
1.1 This test method evaluates the resistance to freezing and thawing of solid interlocking concrete paving units conforming to the dimensional requirements of Specification C936/C936M. Units are tested in a test solution that is either tap water or 3 % saline solution, depending on the intended use of the units in actual service.  
1.2 The values stated in SI units are to be regarded as standard. The values given in parentheses after SI units are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    4 pages
    English language
    sale 15% off
  • Standard
    4 pages
    English language
    sale 15% off
ASTM
ASTM A1044/A1044M-22a(Specification)
Standard Specification for Steel Stud Assemblies for Shear Reinforcement of Concrete

SCOPE
1.1 This specification covers steel stud assemblies for shear reinforcement of concrete. Stud assemblies consist of either single-headed studs (Type 1) attached to a structural steel base rail by structural welding or stud welding, or double-headed studs (Type 2) mechanically crimped into a non-structural steel shape or attached to a steel plate by spot welding or tack welding. These stud assemblies are not intended for use as shear connectors in steel-concrete composite construction.
Note 1: The configuration of the studs for stud assemblies is much different than the configuration of the headed-type studs prescribed in Clause 9, Figure 9.1 of AWS D1.1/D1.1M. Ratios of the cross-sectional areas of the head-to-shank of the AWS D1.1/D1.1M studs range from about 2.5 to 4. In contrast, this specification requires the area of the head of the studs for stud assemblies to be at least 10 times the area of the shank. Thus, the standard headed-type studs in Clause 9, Figure 9.1 of AWS D1.1/D1.1M do not conform to the requirements of this specification for use as stud assemblies for shear reinforcement.  
1.2 This specification is applicable for orders in either inch-pound units or in SI units.  
1.3 The values stated either in inch-pound or SI units are to be regarded as standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with this specification.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    5 pages
    English language
    sale 15% off
  • Technical specification
    5 pages
    English language
    sale 15% off