ASTM C639-01

(Test Method)

Standard Test Method for Rheological (Flow) Properties of Elastomeric Sealants

Standard Test Method for Rheological (Flow) Properties of Elastomeric Sealants

SCOPE
1.1 This test method describes a laboratory procedure for the determination of rheological (flow) properties of single- and multicomponent chemically curing sealants for use in building construction.
1.2 Other suitable flow characteristics may be agreed upon between the seller and purchaser or specifier. Special nonsag properties and lower flow characteristics may be required for use in sloping joints where absolute leveling is not desired.
Note 1--The sealants are supplied in various rheological properties ranging from pourable fluids to stiff nonsagging pastes. Multicomponent sealants are supplied as a base component with an activator or curing agent separately packaged. After mixing the multiple parts, the sealant is ready for application. Single-component sealants are supplied ready for use upon opening of the package and usually depend on the external environment for cure.
1.3 This test method describes four types of joint sealants:
1.3.1 Type I--Single-component flowable or self-leveling,
1.3.2 Type II--Single-component nonsag,
1.3.3 Type III--Multicomponent flowable or self-leveling, and
1.3.4 Type IV--Multicomponent nonsag.
1.4 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.
1.5 This standard does not purport to address the safety problems associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

General Information

Status
Historical
Publication Date
09-Jun-2001
ICS
91.100.50 - Binders. Sealing materials
Technical Committee
C24 - Building Seals and Sealants
Drafting Committee
C24.20 - General Test Methods
Current Stage
Ref Project

Relations

Replaces
ASTM C639-95 - Standard Test Method for Rheological (Flow) Properties of Elastomeric Sealants
Effective Date
10-Jun-2001
Replaced By
ASTM C639-01(2007) - Standard Test Method for Rheological (Flow) Properties of Elastomeric Sealants
Effective Date
01-Jun-2007
Referred By
ASTM C920-18 - Standard Specification for Elastomeric Joint Sealants
Effective Date
10-Jun-2001
Referred By
ASTM C1249-18(2023) - Standard Guide for Secondary Seal for Sealed Insulating Glass Units for Structural Sealant Glazing Applications
Effective Date
10-Jun-2001
Referred By
ASTM C1184-23 - Standard Specification for Structural Silicone Sealants
Effective Date
10-Jun-2001
Referred By
ASTM C1021-08(2023) - Standard Practice for Laboratories Engaged in Testing of Building Sealants
Effective Date
10-Jun-2001
Referred By
ASTM D5893/D5893M-16(2021) - Standard Specification for Cold-Applied, Single-Component, Chemically Curing Silicone Joint Sealant for Portland Cement Concrete Pavements
Effective Date
10-Jun-2001
Referred By
ASTM D8138-23 - Standard Specification for Preformed Silicone Joint Sealing System for Bridges
Effective Date
10-Jun-2001
Referred By
ASTM C1369-19 - Standard Specification for Secondary Edge Sealants for Structurally Glazed Insulating Glass Units
Effective Date
10-Jun-2001

Buy Standard

ASTM C639-01 - Standard Test Method for Rheological (Flow) Properties of Elastomeric SealantsASTM C639-01 - Standard Test Method for Rheological (Flow) Properties of Elastomeric Sealants
PreviousNext
Standard
ASTM C639-01 - Standard Test Method for Rheological (Flow) Properties of Elastomeric Sealants
English language
3 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation:C639–01
Standard Test Method for
1
Rheological (Flow) Properties of Elastomeric Sealants
This standard is issued under the fixed designation C 639; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (e) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the Department of Defense.
1. Scope 3. Terminology
1.1 This test method describes a laboratory procedure for 3.1 Definitions—Refer to Terminology C 717, Section 4.1,
the determination of rheological (flow) properties of single- for definitions of the following terms used in this standard:
and multicomponent chemically curing sealants for use in chemically curing sealants, compound, elastomeric, flow
building construction. (slump), non-sag sealant (non-slump), sealant, self-leveling
1.2 Other suitable flow characteristics may be agreed upon sealant (flowable).
between the seller and purchaser or specifier. Special nonsag
4. Comparison to Other Standards
properties and lower flow characteristics may be required for
4.1 ISO 7390:1987 Building Construction-Jointing
use in sloping joints where absolute leveling is not desired.
Products-Determination of Resistance to Flow
NOTE 1—The sealants are supplied in various rheological properties
ranging from pourable fluids to stiff nonsagging pastes. Multicomponent
5. Significance and Use
sealants are supplied as a base component with an activator or curing
5.1 The results obtained from this test method are simply a
agent separately packaged. After mixing the multiple parts, the sealant is
ready for application. Single-component sealants are supplied ready for measure of the degree of horizontal or vertical flow of
use upon opening of the package and usually depend on the external
single-component or multi-component sealants when applied
environment for cure.
to a set joint configuration at two pre-determined temperatures.
1.3 This test method describes four types of joint sealants: Only samples conditioned at the same temperature may be
directly compared.
1.3.1 Type I—Single-component flowable or self-leveling,
1.3.2 Type II—Single-component nonsag,
6. Apparatus
1.3.3 Type III—Multicomponent flowable or self-leveling,
6.1 Refrigerator, controlled at 4.4 6 2°C (40 6 3.6°F).
and
6.2 Oven, convention-type, controlled at 50 6 2°C (1226
1.3.4 Type IV—Multicomponent nonsag.
3.6°F).
1.4 The values stated in SI units are to be regarded as the
6.3 Channel, one, stainless steel (Type 304, No. 2-B finish,
standard. The values given in parentheses are for information
No. 16 gage), inside dimensions 19 mm wide, 13 mm deep,
only.
3 1
152 mm long ( ⁄4 by ⁄2 by 6 in.), and closed at both ends (see
1.5 This standard does not purport to address the safety
Fig. 1a).
problems associated with its use. It is the responsibility of the
6.4 Channels, two, stainless steel (Type 304, No. 2-B finish,
user of this standard to establish appropriate safety and health
No. 16 gage), inside dimensions 19 mm wide, 13 mm deep,
practices and determine the applicability of regulatory limita-
3 1
152 mm long ( ⁄4 by ⁄2 by 6 in.) with both ends open and the
tions prior to use.
back surface extended 51 mm (2 in.) (see Fig. 1b).
2. Referenced Documents
7. Standard Test Conditions
2.1 ASTM Standards:
2
7.1 Unless otherwise specified, standard conditions shall be
C 717 Terminology of Building Seals and Sealants
23 6 2°C (73.4 6 3.6°F) and 50 6 5 % relative humidity.
1
8. Procedures
ThistestmethodisunderthejurisdictionofASTMCommitteeC24onBuilding
Seals and Sealants and is the direct responsibility of Subcommittee C24.20 on
8.1 Test for Type I Sealants:
General Test Methods.
Current edition approved June 10, 2001. Published July 2001. Originally
published as C 639 – 69. Last previous edition C 639 – 95.
2
Annual Book of ASTM Standards, Vol 04.07.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
1

---------------------- Page: 1 ----------------------
C639–01
end of the exposure period, remove the channels from the
chambers and note any change in the configuration of the
compound in the channels.
8.3 Test for Type III Sealants—The test procedure shall be
the same as that described in 8.1 with the following exception:
After conditioning the base and curing agent separately for 16
to 24 h and the channel for2hinthe refrigerator, remove and
hand mix them for at least 5 min. Return the mixed compound
to the cold box for an additional 30 min. Then pour the
compoundintothehorizontalchannelandproceedasdescribed
in 8.1.2. Examine the compound for flow properties.
8.4 Tests for Type IV Sealants:
8.4.1 Vert
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

ASTM
ASTM C1737-23(Guide)
Standard Guide for Evaluating Temperature Effects to Aerosol Foam Sealant During and After Dispensing

SIGNIFICANCE AND USE
5.1 This guide is not intended to measure the precise temperature range for dispensing and curing product under all the possible substrate and environmental factors but to provide a basis for benchmarking a foam sealant product under specific laboratory conditions.  
5.2 The product user is encouraged to evaluate each application and determine suitability for actual use.
SCOPE
1.1 This guide covers the general effects of temperature from the aerosol foam sealant (either polyurethane or latex types) under the use temperatures.  
1.2 The guide is intended to estimate the observed product dispensing characteristics and foam quality of aerosol foam dispensed or cured, or both, at specific temperatures and standard conditions.  
1.3 Such foam sealants are primarily intended to reduce air movement in and out of building enclosures.  
1.4 Currently two main foam sealant types are applicable to this standard: single component polyurethane and latex.  
1.5 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.6 There are no other known test methods specific for measuring the product temperature range for aerosol foam sealant.  
1.7 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.8 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Guide
    3 pages
    English language
    sale 15% off
  • Guide
    3 pages
    English language
    sale 15% off
ASTM
ASTM C1257-15(2023)(Test Method)
Standard Test Method for Accelerated Weathering of Solvent-Release-Type Sealants

SIGNIFICANCE AND USE
5.1 It is difficult to establish a precise correlation between laboratory accelerated and natural weathering because of  (1) geographical climatic variations, local weather variation from normal, and local pollutants and (2) the fact that the acceleration factor is material dependent, varying with the type of material as well as its formulation. This test method is used to determine the resistance of a sealant to laboratory accelerated weathering and, if a control material with known outdoor weathering performance is used, the relative weathering performance of the sealant against that of the control material.  
5.2 This test method is conducted using aluminum channels. Other substrate materials may show different results.
SCOPE
1.1 This test method includes two laboratory accelerated exposure procedures for predicting the effects of ultraviolet or ultraviolet/visible radiation, heat, and moisture on color, chalking, cracking, and adhesion of solvent-release sealants.  
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.3 The committee with jurisdiction over this standard is not aware of any comparable standards published by other organizations.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    4 pages
    English language
    sale 15% off
ASTM
ASTM D2202-00(2023)(Test Method)
Standard Test Method for Slump of Sealants

SIGNIFICANCE AND USE
4.1 Excessive sealant slump or sag in a vertical joint may cause improper bead shape or inadequate sealant thickness in the completed joint. Slump measurements, as described in this test method, serve to evaluate only this application characteristic; they do not predict the performance capability of the sealant after installation.
SCOPE
1.1 This test method covers a laboratory procedure for the determination of the degree of slump of a sealant when used in a vertical joint in a structure.  
1.2 The values stated in either inch-pound or SI (metric) units are to be separately regarded as the standard. Within the text, the inch-pound units are shown in parentheses.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
Note 1: A related ISO standard is ISO 7390. The user should compare to determine how it differs from this test method.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    4 pages
    English language
    sale 15% off
ASTM
ASTM C1401-23(Guide)
Standard Guide for Structural Sealant Glazing

SIGNIFICANCE AND USE
5.1 The old saying “A chain is only as strong as its weakest link” is very applicable to a SSG system. In reality, a SSG system, to be successful, must establish and maintain a chain of adhesion. For example, a factory applied finish must adhere adequately to a metal framing member, a structural glazing sealant to that metal finish, that structural glazing sealant to a reflective coating on a glass lite, and lastly, that reflective coating to a glass surface. This guide will assist in the identification and development of, among others, performance criteria, test methods, and industry practices that should be implemented to obtain the required structural glazing sealant adhesion and compatibility with other system components.  
5.2 Although this guide has been arranged to permit easy access to specific areas of interest, it is highly recommended that the entire guide is read and understood before establishing the requirements for a particular SSG system.  
5.3 This guide should not be the only criteria upon which the design and installation of a SSG system is based. The information herein is provided to assist in the development of a specific program with a goal of achieving a successful SSG system installation. Information and guidelines are provided for the evaluation, design, installation, and maintenance of a SSG system and many of its various components. Considering the range of properties of structural glazing silicone sealants, as well as the many types of framing system designs, material combinations that can be used, various material finishes, and the many types and varieties of accessories, the information contained herein is general in nature.  
5.4 Generally, the design, fabrication, and installation of a SSG system requires more technical knowledge and experience then is required for a conventionally glazed window or curtain wall system. To ensure the success of a SSG system, it is important that suppliers, fabricators, and installers of materials an...
SCOPE
1.1 Structural sealant glazing, hereinafter referred to as SSG, is an application where a sealant not only can function as a barrier against the passage of air and water through a building envelope, but also primarily provides structural support and attachment of glazing or other components to a window, curtain wall, or other framing system.  
1.2 This guide provides information useful to design professionals, manufacturers, contractors, and others for the design and installation of a SSG system. This information is applicable only to this glazing method when used for a building wall that is not more than 15° from vertical; however, limited information is included concerning a sloped SSG application.  
1.3 Only a silicone chemically curing sealant specifically formulated, tested, and marketed for structural sealant glazing is acceptable for a SSG system application.  
1.4 The committee with jurisdiction for this standard is not aware of any comparable standard published by other organizations.  
1.5 The values stated in SI units are to be regarded as standard. The values given in parentheses after SI units are provided for information only and are not considered standard. SI units in this guide are in conformance with IEEE/ASTM SI 10.  
1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Guide
    56 pages
    English language
    sale 15% off
  • Guide
    56 pages
    English language
    sale 15% off
ASTM
ASTM C792-23(Test Method)
Standard Test Method for Effects of Heat Aging on Weight Loss, Cracking, and Chalking of Elastomeric Sealants

SIGNIFICANCE AND USE
5.1 Weight loss through volatilization of components of a sealant in a building joint may affect sealant appearance because of shrinkage, and sealant performance because of the loss of functional sealant components. Exposure to high-temperature environments will accelerate the loss of volatiles.  
5.2 This test method measures weight loss. It can be used in combination with a knowledge of sealant density to estimate shrinkage. In addition, when compared to sealant theoretical weight solids, it provides an estimate of the extent to which functional sealant components can be volatilized when exposed to high service temperatures. Substantial losses of this type may help predict early failures in durability. Also, development of cracks or chalking, or both, lessens sealant service life. However, a sealant that develops no cracks or chalking, or low weight loss in this test method, does not necessarily assure good durability.
SCOPE
1.1 This test method covers a laboratory procedure for determining the effects of heat aging on weight loss, cracking, and chalking of cured-in-place elastomeric joint sealants (single- and multi-component) for use in building construction.  
1.2 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.3 There is no known ISO equivalent to this test method.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    3 pages
    English language
    sale 15% off
  • Standard
    3 pages
    English language
    sale 15% off
ASTM
ASTM C1330-23(Specification)
Standard Specification for Cylindrical Sealant Backing for Use with Cold Liquid-Applied Sealants

ABSTRACT
This standard specification covers the basic requirements for cylindrical sealant backing for use with cold liquid-applied sealants. Cylindrical sealant backings are classified into three types: type C, type O, and type B, composed predominantly of closed cell material, open cell material, and bi-cellular material, respectively. Test methods for cylindrical sealant backing include water absorption, density, outgassing, compression deflection and recovery, and tensile strength. The sealant shall be clean, free of scale, foreign matter, oil, or water.
SIGNIFICANCE AND USE
5.1 This specification is designed to give some indication as to the differences in performance for various cylindrical sealant backings.  
5.2 Although this specification qualifies a cylindrical sealant backing for use, it does not address the compatibility of the backing with the sealants with which it will make contact. Sealant compatibility should be confirmed by the sealant manufacturer. Compatibility characteristics of sealants in contact with cylindrical sealant backings can be determined by Test Method C1087.
SCOPE
1.1 This specification covers the basic requirements for cylindrical sealant backing to be used with cold liquid applied sealants for use in building seals.  
1.2 Cylindrical sealant backing serves one or more of the following functions:  
1.2.1 Limits the amount and depth of sealant applied into a joint,  
1.2.2 Acts as a bond breaker to allow joint movement without undue stress to the sealant,  
1.2.3 Provides a form to assist the sealant in developing the proper shape factor, and  
1.2.4 Acts as a barrier to the flow of sealant through the joint.  
1.3 The committee with jurisdiction over this standard is not aware of any comparable standards published by other ASTM committees or other organizations.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    2 pages
    English language
    sale 15% off
  • Technical specification
    2 pages
    English language
    sale 15% off
ASTM
ASTM C1087-23(Test Method)
Standard Test Method for Determining Compatibility of Liquid-Applied Sealants with Accessories Used in Structural Glazing Systems

SIGNIFICANCE AND USE
5.1 In structural sealant glazing systems, the sealant functions as the structural adhesive and may also function as the primary weather seal. As the structural adhesive, the integrity of the adhesive bond is critical.  
5.2 Changes in color and adhesion after exposure are two of the criteria that can be used to determine the compatibility of the system. Experience has shown that accessories that cause loss of adhesion or discoloration in this test method may also cause these occurrences in actual use.
SCOPE
1.1 This test method covers a laboratory screening procedure for determining the compatibility of liquid-applied structural sealant glazing sealants when in contact with accessories such as dry glazing gaskets, spacers, shims, and setting blocks after exposure to heat and ultraviolet light.  
1.2 This test method includes the observation of three parameters as follows:  
1.2.1 Changes in the color of the sealant,  
1.2.2 Changes in the adhesion of the sealant to glass, and  
1.2.3 Changes in the adhesion of the sealant to the accessory being tested.  
1.3 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
Note 1: At this time, no comparable ISO standard exists.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    4 pages
    English language
    sale 15% off
  • Standard
    4 pages
    English language
    sale 15% off
ASTM
ASTM C1193-16(2023)(Guide)
Standard Guide for Use of Joint Sealants

SIGNIFICANCE AND USE
4.1 This guide provides information and guidelines for consideration by the designer or applicator of a joint seal. It explains the properties and functions of various materials, such as sealant, sealant backing, and primer, among others; and, procedures such as, substrate cleaning and priming, and installation of the components of a sealed joint. It presents guidelines for the use and application of the various materials, design of a sealant joint for a specific application, and environmental conditions and effects that are known to detrimentally affect a sealant joint. The information and guidelines are also useful for those that supply accessories to the sealant industry and for those that install sealants and accessory materials associated with sealant use.  
4.2 In addition to the design and installation data in this guide, consult the sealant manufacturer about applications for its products and their proper use and installation. Considering the range of properties of commercially available sealants, the variety of joint designs possible, and the many conditions of use, the information contained herein is general in nature.  
4.3 It should be realized that a sealant and sealant joint are expected to have a design life during which they remain functional. However, a sealant and sealant joint will also have a service life. The intent is for service life to meet or exceed design life. There are many factors that can affect service life including type of sealant polymer, sealant formulation, compatibility with adjacent materials, installation techniques or deficiencies, sealant joint design (or lack thereof), proper maintenance (or lack thereof), and environmental exposure, among others. The designer of a joint seal should take the above into consideration when designing and specifying sealants for certain applications.  
4.4 The design life of a sealant or sealant joint should be considered in conjunction with the design life of the structure for which it is us...
SCOPE
1.1 This guide describes the use of a cold liquid-applied sealant for joint sealing applications. Including joints on buildings and related adjacent areas, such as plazas, decks, and pavements for vehicular or pedestrian use, and types of construction other than highways and airfield pavements and bridges. Information in this guide is primarily applicable to a single and multi-component, cold liquid-applied joint sealant and secondarily to a precured sealant when used with a properly prepared joint opening and substrate surfaces.  
1.2 An elastomeric or non-elastomeric sealant described by this guide should meet the requirements of Specification C834, C920, or C1311.  
1.3 This guide does not provide information or guidelines for the use of a sealant in a structural sealant glazing application. Guide C1401 should be consulted for this information. Additionally, it also does not provide information or guidelines for the use of a sealant in an insulating glass unit edge seal used in a structural sealant glazing application. Guide C1249 should be consulted for this information.  
1.4 Practice C919 should be consulted for information and guidelines for the use of a sealant in an application where an acoustic joint seal is required.  
1.5 This guide also does not provide information relative to the numerous types of sealant that are available nor specific generic sealant properties, such as hardness, tack-free time, or curing process, among others.  
1.6 The values stated in SI units are to be regarded as the standard. The values given in parenthesis are provided for information only.  
1.7 The Committee with jurisdiction for this standard is not aware of any comparable standards published by other organizations.  
1.8 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and e...

  • Guide
    33 pages
    English language
    sale 15% off
ASTM
ASTM C793-23(Test Method)
Standard Test Method for Effects of Laboratory Accelerated Weathering on Elastomeric Joint Sealants

SIGNIFICANCE AND USE
5.1 It is known that solar radiation contributes to the degradation of sealants in exterior building joints. The use of a laboratory accelerated weathering machine with actinic radiation, moisture and heat appears to be a feasible means to give indications of early degradation by the appearance of sealant cracking. However, simulated weather factors in combination with extension may produce more severe degradation than weather factors only. Therefore, the effect of the weathering test is made more sensitive by the addition of the bending of the specimen at cold temperature.
SCOPE
1.1 This test method covers a laboratory procedure for determining the effects of accelerated weathering on cured-in-place elastomeric joint sealants (single- and multicomponent) for use in building construction.  
1.2 The values stated in SI units are to be regarded as the standard. The values in parentheses are for information only.  
1.3 The committee with jurisdiction over this standard is not aware of any comparable standards published by other ASTM committees or other organizations.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    4 pages
    English language
    sale 15% off
  • Standard
    4 pages
    English language
    sale 15% off
ASTM
ASTM C782-13(2023)(Test Method)
Standard Test Method for Softness of Preformed Tape Sealants

SIGNIFICANCE AND USE
5.1 Preformed tape sealants are tacky, deformable solids that are used under compression between two substrates in a variety of sealing applications. This procedure measures the softness of a preformed tape sealant and gives an indication of the preformed tape sealant's ease of compression during installation. The resistance to penetration may also give an indication of the toughness of the preformed tape sealant.
SCOPE
1.1 This test method describes a laboratory procedure for determining the softness of preformed tape sealants.  
Note 1: Cone penetration methods applicable to greases and to petrolatum are described in Test Methods D217 and D937. Test Method D2451 also uses a penetration technique for determining the degree of set in sash glazing compounds.  
1.2 The values stated in SI units are to be regarded as standard. Temperature values are also provided (in parentheses) in degrees Fahrenheit.  
1.3 The subcommittee with jurisdiction is not aware of any similar ISO standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    2 pages
    English language
    sale 15% off