ASTM B533-85(2013)

(Test Method)

Standard Test Method for Peel Strength of Metal Electroplated Plastics

Standard Test Method for Peel Strength of Metal Electroplated Plastics

SIGNIFICANCE AND USE
4.1 The force required to separate a metallic coating from its plastic substrate is determined by the interaction of several factors: the generic type and quality of the plastic molding compound, the molding process, the process used to prepare the substrate for electroplating, and the thickness and mechanical properties of the metallic coating. By holding all others constant, the effect on the peel strength by a change in any one of the above listed factors may be noted. Routine use of the test in a production operation can detect changes in any of the above listed factors.  
4.2 The peel test values do not directly correlate to the adhesion of metallic coatings on the actual product.  
4.3 When the peel test is used to monitor the coating process, a large number of plaques should be molded at one time from a same batch of molding compound used in the production moldings to minimize the effects on the measurements of variations in the plastic and the molding process.
SCOPE
1.1 This test method gives two procedures for measuring the force required to peel a metallic coating from a plastic substrate.2 One procedure (Procedure A) utilizes a universal testing machine and yields reproducible measurements that can be used in research and development, in quality control and product acceptance, in the description of material and process characteristics, and in communications. The other procedure (Procedure B) utilizes an indicating force instrument that is less accurate and that is sensitive to operator technique. It is suitable for process control use.  
1.2 The tests are performed on standard molded plaques. This method does not cover the testing of production electroplated parts.  
1.3 The tests do not necessarily measure the adhesion of a metallic coating to a plastic substrate because in properly prepared test specimens, separation usually occurs in the plastic just beneath the coating-substrate interface rather than at the interface. It does, however, reflect the degree that the process is controlled.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

General Information

Status
Historical
Publication Date
30-Nov-2013
ICS
25.220.40 - Metallic coatings
Technical Committee
B08 - Metallic and Inorganic Coatings
Drafting Committee
B08.05 - Decorative Coatings
Current Stage
Ref Project

Relations

Replaces
ASTM B533-85(2009) - Standard Test Method for Peel Strength of Metal Electroplated Plastics
Effective Date
01-Dec-2013
Replaced By
ASTM B533-85(2019) - Standard Test Method for Peel Strength of Metal Electroplated Plastics
Effective Date
01-Oct-2019
Referred By
ASTM B904-00(2021) - Standard Specification for Autocatalytic Nickel over Autocatalytic Copper for Electromagnetic Interference Shielding
Effective Date
01-Dec-2013
Referred By
ASTM B727-04(2020) - Standard Practice for Preparation of Plastics Materials for Electroplating
Effective Date
01-Dec-2013
Referred By
ASTM B604-91(2019) - Standard Specification for Decorative Electroplated Coatings of Copper Plus Nickel Plus Chromium on Plastics
Effective Date
01-Dec-2013

Buy Standard

ASTM B533-85(2013) - Standard Test Method for Peel Strength of Metal Electroplated PlasticsASTM B533-85(2013) - Standard Test Method for Peel Strength of Metal Electroplated Plastics
PreviousNext
Standard
ASTM B533-85(2013) - Standard Test Method for Peel Strength of Metal Electroplated Plastics
English language
4 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)


NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation: B533 − 85 (Reapproved 2013) Endorsed by American
Electroplaters’ Society
Endorsed by National
Association of Metal Finishers
Standard Test Method for
Peel Strength of Metal Electroplated Plastics
This standard is issued under the fixed designation B533; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope 3. Summary of Test Method
1.1 Thistestmethodgivestwoproceduresformeasuringthe 3.1 A properly prepared standard test specimen, called a
force required to peel a metallic coating from a plastic plaque, is copper electroplated, with no additional metal
substrate. One procedure (Procedure A) utilizes a universal coating. The coated plaque is either tested as is, or it is
testingmachineandyieldsreproduciblemeasurementsthatcan conditioned by a low-temperature bake and then tested. The
be used in research and development, in quality control and coating is cut through to the plastic substrate in a way that
product acceptance, in the description of material and process forms two strips of coating (see Fig. 1). Each strip is peeled
characteristics, and in communications. The other procedure from the substrate at a right angle using an instrument that
(ProcedureB)utilizesanindicatingforceinstrumentthatisless indicates the force required to separate it from its substrate.
accurate and that is sensitive to operator technique. It is
4. Significance and Use
suitable for process control use.
4.1 Theforcerequiredtoseparateametalliccoatingfromits
1.2 The tests are performed on standard molded plaques.
plastic substrate is determined by the interaction of several
This method does not cover the testing of production electro-
factors: the generic type and quality of the plastic molding
plated parts.
compound, the molding process, the process used to prepare
1.3 The tests do not necessarily measure the adhesion of a
the substrate for electroplating, and the thickness and mechani-
metallic coating to a plastic substrate because in properly
cal properties of the metallic coating. By holding all others
prepared test specimens, separation usually occurs in the
constant, the effect on the peel strength by a change in any one
plastic just beneath the coating-substrate interface rather than
oftheabovelistedfactorsmaybenoted.Routineuseofthetest
at the interface. It does, however, reflect the degree that the
in a production operation can detect changes in any of the
process is controlled.
above listed factors.
1.4 This standard does not purport to address all of the
4.2 The peel test values do not directly correlate to the
safety concerns, if any, associated with its use. It is the
adhesion of metallic coatings on the actual product.
responsibility of the user of this standard to establish appro-
4.3 When the peel test is used to monitor the coating
priate safety and health practices and determine the applica-
process, a large number of plaques should be molded at one
bility of regulatory limitations prior to use.
time from a same batch of molding compound used in the
production moldings to minimize the effects on the measure-
2. Referenced Document
ments of variations in the plastic and the molding process.
2.1 ASTM Standards:
E4 Practices for Force Verification of Testing Machines
5. Apparatus
5.1 Procedure A—A tension testing machine that has self-
aligning grips and that has a loading range that includes the
ThistestmethodisunderthejurisdictionofASTMCommitteeB08onMetallic
forces to be measured, 5 to 200 N, shall be used to separate the
and Inorganic Coatingsand is the direct responsibility of Subcommittee B08.05 on
coatingfromthesubstrate,andmeasuretheforcerequired.The
Decorative Coatings.
Current edition approved Dec. 1, 2013. Published December 2013. Originally
machine shall meet the verification requirements of Practices
approvedin1970.Lastpreviouseditionapprovedin2009asB533 – 85(2009).DOI: 4,5
E4. The speed of separation of the crossarms of the machine
10.1520/B0533-85R13.
shall be adjusted to give a separation rate of 25 6 3 mm/min.
This test is also known as the Jacquet Test.Adetailed treatment of the test has
been published by Saubestre et al in Plating, Vol 52, 1965, p. 982. The machine shall automatically and continuously record on a
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
Standards volume information, refer to the standard’s Document Summary page on The sole source of supply of the Instron universal testing machine known to the
the ASTM website. committee at this time is Instron Corp., Canton, MA.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
B533 − 85 (2013)
FIG. 1 Plaque
change with time after conditioning.
chart the load on one coordinate and the amount of peel on the
other coordinate. The amount of peel may be obtained from
9. Procedure
calculation, using a known chart speed.
5.2 Procedure B—A spring-loaded, force-indicating instru- 9.1 Moldtherequirednumberofplaquesusingthespecified
ment with a measurement range that includes the force to be molding compound and molding procedure.
measured, 5 to 200 N, shall be used to measure the force
NOTE 2—When the test is used as a control of the coating process,
required to separate the coating. The indicated force shall be
commercially prepared plaques can be used.
accurate to 610 %.
9.2 Clean, activate, and electroplate the plaques as speci-
6. Sampling fied. The thickness of the metallic coating in the test area (see
Fig. 1) shall be 40 6 4 µm.
6.1 A sampling procedure is not applicable to this test
method.
NOTE 3—It is necessary to have a ductile copper coating to perform this
test. The thickness and uniformity of thickness of the metallic coating
7. Test Specimen
directly influence the peel strength; therefore, in order to standardize this
test, the coating thickness is specified. If a different coating thickness is
7.1 Perform the test using a flat, molded plastic plaque such
used, the results will not be comparable to other test results. It may be
as shown in Fig. 1. Plaque dimensions may vary up to 610 %
necessary to use shielding during plating to obtain the required coating
provided that the edges of slit peel strips are not closer than 11
thickness uniformity.
mm from any plaque edge.
9.3 Cut through the coating along the dashed lines shown in
Fig. 1, and also along the centerline so as to produce two
8. Conditioning
parallel strips of coating that are 25.00 6 0.25 mm wide and
8.1 Condition the electroplated plaques requiring condition-
approximately 75 mm long.
ing by baking for1hinanair-circulating oven operated at
70 6 3°C. Place the plaques in the oven in a way that permits NOTE 4—Following are methods that can be used to cut the coating:
(a) Slit the coating with a milling machine equipped with a slitting
free circulation of air around all surfaces of the plaques.Allow
5,7
saw. Operate the saw at a peripheral speed of 300 mm/s and a feed of
the conditioned plaques to cool to room temperature and then
5 mm/s.
test them within 1 h. Test the plaques that
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

ASTM
ASTM B651-83(2024)(Test Method)
Standard Test Method for Measurement of Corrosion Sites in Nickel Plus Chromium or Copper Plus Nickel Plus Chromium Electroplated Surfaces with Double-Beam Interference Microscope

SIGNIFICANCE AND USE
4.1 Different electroplating systems can be corroded under the same conditions for the same length of time. Differences in the average values of the radius or half-width or of penetration into an underlying metal layer are significant measures of the relative corrosion resistance of the systems. Thus, if the pit radii are substantially higher on samples with a given electroplating system, when compared to other systems, a tendency for earlier failure of the former by formation of visible pits is indicated. If penetration into the semi-bright nickel layer is substantially higher, a tendency for earlier failure by corrosion of basis metal is evident.
SCOPE
1.1 This test method provides a means for measuring the average dimensions and number of corrosion sites in an electroplated decorative nickel plus chromium or copper plus nickel plus chromium coating on steel after the coating has been subjected to corrosion tests. This test method is useful for comparing the relative corrosion resistances of different electroplating systems and for comparing the relative corrosivities of different corrosive environments. The numbers and sizes of corrosion sites are related to deterioration of appearance. Penetration of the electroplated coatings leads to appearance of basis metal corrosion products.  
1.2 The values stated in SI units are to be regarded as the standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    3 pages
    English language
    sale 15% off
ASTM
ASTM B533-85(2024)(Test Method)
Standard Test Method for Peel Strength of Metal Electroplated Plastics

SIGNIFICANCE AND USE
4.1 The force required to separate a metallic coating from its plastic substrate is determined by the interaction of several factors: the generic type and quality of the plastic molding compound, the molding process, the process used to prepare the substrate for electroplating, and the thickness and mechanical properties of the metallic coating. By holding all others constant, the effect on the peel strength by a change in any one of the above listed factors may be noted. Routine use of the test in a production operation can detect changes in any of the above listed factors.  
4.2 The peel test values do not directly correlate to the adhesion of metallic coatings on the actual product.  
4.3 When the peel test is used to monitor the coating process, a large number of plaques should be molded at one time from a same batch of molding compound used in the production moldings to minimize the effects on the measurements of variations in the plastic and the molding process.
SCOPE
1.1 This test method gives two procedures for measuring the force required to peel a metallic coating from a plastic substrate.2 One procedure (Procedure A) utilizes a universal testing machine and yields reproducible measurements that can be used in research and development, in quality control and product acceptance, in the description of material and process characteristics, and in communications. The other procedure (Procedure B) utilizes an indicating force instrument that is less accurate and that is sensitive to operator technique. It is suitable for process control use.  
1.2 The tests are performed on standard molded plaques. This method does not cover the testing of production electroplated parts.  
1.3 The tests do not necessarily measure the adhesion of a metallic coating to a plastic substrate because in properly prepared test specimens, separation usually occurs in the plastic just beneath the coating-substrate interface rather than at the interface. It does, however, reflect the degree that the process is controlled.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    4 pages
    English language
    sale 15% off
ASTM
ASTM B765-03(2023)(Guide)
Standard Guide for Selection of Porosity and Gross Defect Tests for Electrodeposits and Related Metallic Coatings

SIGNIFICANCE AND USE
4.1 Porosity tests indicate the completeness of protection or coverage offered by the coating. When a given coating is known to be protective when properly deposited, the porosity serves as a measure of the control of the process. The effects of substrate finish and preparation, plating bath, coating process, and handling, may all affect the degree of imperfection that is measured.
Note 1: The substrate exposed by the pores may be the basis metal, an underplate, or both.  
4.2 The tests in this guide involve corrosion reactions in which the products delineate pores in coatings. Since the chemistry and properties of these products may not resemble those found in service environments, these tests are not recommended for prediction of product performance unless correlation is first established with service experience.
SCOPE
1.1 This guide describes some of the available standard methods for the detection, identification, and measurement of porosity and gross defects in electrodeposited and related metallic coatings and provides some laboratory-type evaluations and acceptances. Some applications of the test methods are tabulated in Table 1 and Table 2.    
1.2 This guide does not apply to coatings that are produced by thermal spraying, ion bombardment, sputtering, and other similar techniques where the coatings are applied in the form of discrete particles impacting on the substrate.  
1.3 This guide does not apply to beneficial or controlled porosity, such as that present in microdiscontinuous chromium coatings.  
1.4 Porosity test results (including those for gross defects) occur as chemical reaction end products. Some occur in situ, others on paper, or in a gel coating. Observations are made that are consistent with the test method, the items being tested, and the requirements of the purchaser. These may be visual inspection (unaided eye) or by 10× magnification (microscope). Other methods may involve enlarged photographs or photomicrographs.  
1.5 The test methods are only summarized. The individual standards must be referred to for the instructions on how to perform the tests.  
1.6 The values stated in SI units are to be regarded as standard. The values given in parentheses are for information only.  
1.7 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.8 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Guide
    4 pages
    English language
    sale 15% off
ASTM
ASTM B571-23(Practice)
Standard Practice for Qualitative Adhesion Testing of Metallic Coatings

SIGNIFICANCE AND USE
2.1 These tests are useful for production control and for acceptance testing of products.  
2.2 Interpreting the results of qualitative methods for determining the adhesion of metallic coatings is often a controversial subject. If more than one test is used, failure to pass any one test is considered unsatisfactory. In many instances, the end use of the coated article or its method of fabrication will suggest the technique that best represents functional requirements. For example, an article that is to be subsequently formed would suggest a draw or a bend test; an article that is to be soldered or otherwise exposed to heat would suggest a heat-quench test. If a part requires baking or heat treating after plating, adhesion tests should be carried out after such posttreatment as well.  
2.3 Several of the tests are limited to specific types of coatings, thickness ranges, ductility, or compositions of the substrate. These limitations are noted generally in the test descriptions and are summarized in Table 1 for certain metallic coatings. (A) + Appropriate; − not appropriate.    
2.4 “Perfect” adhesion exists if the bonding between the coating and the substrate is greater than the cohesive strength of either. Such adhesion is usually obtained if good electroplating practices are followed.  
2.5 For many purposes, the adhesion test has the objective of detecting any adhesion less than “perfect.” For such a test, one uses any means available to attempt to separate the coating from the substrate. This may be prying, hammering, bending, beating, heating, sawing, grinding, pulling, scribing, chiseling, or a combination of such treatments. If the coating peels, flakes, or lifts from the substrate, the adhesion is less than perfect.  
2.6 If evaluation of adhesion is required, it may be desirable to use one or more of the following tests. These tests have varying degrees of severity; and one might serve to distinguish between satisfactory and unsatisfactory adhesion in a ...
SCOPE
1.1 This practice covers simple, qualitative tests for evaluating the adhesion of metallic coatings on various substances.  
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    4 pages
    English language
    sale 15% off
  • Standard
    4 pages
    English language
    sale 15% off
ASTM
ASTM B832-93(2023)(Guide)
Standard Guide for Electroforming with Nickel and Copper

SIGNIFICANCE AND USE
4.1 The specialized use of the electroplating process for electroforming results in the manufacture of tools and products that are unique and often impossible to make economically by traditional methods of fabrication. Current applications of nickel electroforming include: textile printing screens; components of rocket thrust chambers, nozzles, and motor cases; molds and dies for making automotive arm-rests and instrument panels; stampers for making phonograph records, video-discs, and audio compact discs; mesh products for making porous battery electrodes, filters, and razor screens; and optical parts, bellows, and radar wave guides (1-3).3  
4.2 Copper is extensively used for electroforming thin foil for the printed circuit industry. Copper foil is formed continuously by electrodeposition onto rotating drums. Copper is often used as a backing material for electroformed nickel shells and in other applications where its high thermal and electrical conductivities are required. Other metals including gold are electroformed on a smaller scale.  
4.3 Electroforming is used whenever the difficulty and cost of producing the object by mechanical means is unusually high; unusual mechanical and physical properties are required in the finished piece; extremely close dimensional tolerances must be held on internal dimensions and on surfaces of irregular contour; very fine reproduction of detail and complex combinations of surface finish are required; and the part cannot be made by other available methods.
SCOPE
1.1 This guide covers electroforming practice and describes the processing of mandrels, the design of electroformed articles, and the use of copper and nickel electroplating solutions for electroforming.  
1.2 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Guide
    9 pages
    English language
    sale 15% off
ASTM
ASTM B874-96(2023)(Specification)
Standard Specification for Chromium Diffusion Coating Applied by Pack Cementation Process

ABSTRACT
This specification covers the requirements for chromium diffusion of metals applied by pack cementation process. The four classes of chromium diffusion coating, defined by the type of base metal, are as follows: Class I (carbon steels); Class II (low-alloy steels); Class III (stainless steels); and Class IV (nickel-based alloys). Specimens shall adhere to processing requirements such as substrate preparation, materials (masteralloys, activators, and inert fillers), loading, furnace cycle, post cleaning, post straightening, visual inspection, and marking and packaging. Specimens shall also adhere to coating requirements such as diffusion thickness, decarburization, chromium content, appearance, and mechanical properties (tensile strength, and macro- and micro-hardness).
SCOPE
1.1 This specification covers the requirements for chromium diffusion of metals by the pack cementation method. Pack diffusion employs the chemical vapor deposition of a metal which is subsequently diffused into the surface of a substrate at high temperature. The material to be coated (substrate) is immersed or suspended in a powder containing chromium (source), a halide salt (activator), and an inert diluent such as alumina (filler). When the mixture is heated, the activator reacts to produce an atmosphere of chromium halides which transfers chromium to the substrate for subsequent diffusion. The chromium-rich surface enhances corrosion, thermal stability, and wear-resistant properties.  
1.2 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    3 pages
    English language
    sale 15% off
ASTM
ASTM B556-90(2023)(Guide)
Standard Guide for Measurement of Thin Chromium Coatings by Spot Test

SIGNIFICANCE AND USE
4.1 The thickness of a decorative chromium coating is often critical to its performance.  
4.2 This procedure is useful for an approximate determination when the best possible accuracy is not required. For more reliable determinations, the following methods are available: Methods B504, B568, and B588.  
4.3 This test assumes that the rate of dissolution of the chromium by the hydrochloric acid under the specified conditions is always the same.
SCOPE
1.1 This guide covers the use of the spot test for the measurement of thicknesses of electrodeposited chromium coatings over nickel and stainless steel with an accuracy of about ±20 % (Section 9). It is applicable to thicknesses up to 1.2 μm.2
Note 1: Although this test can be used for coating thicknesses up to 1.2 μm, there is evidence that the results obtained by this method are high at thicknesses greater than 0.5 μm.3 In addition, for coating thicknesses above 0.5 μm, it is advisable to use a double drop of acid to prevent depletion of the test solution before completion of the test.  
1.2 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Guide
    3 pages
    English language
    sale 15% off
ASTM
ASTM B867-95(2023)(Specification)
Standard Specification for Electrodeposited Coatings of Palladium-Nickel for Engineering Use

ABSTRACT
This specification establishes the requirements for electrodeposited palladium-nickel (Pd-Ni) coatings for engineering applications. Composite coatings consisting of palladium-nickel and a thin gold over-plate for applications involving electrical contacts are also covered. The classification system for the coatings covered here shall be specified by the basis metal, the thickness of the underplating, the composition type and thickness class of the palladium-nickel coating, and the grade of the gold overplating. Coatings should be sampled, tested, and conform to specified requirements as to purity, appearance, thickness, composition, adhesion, ductility, and integrity (including gross defects, mechanical damage, porosity, and microcracks). Alloy composition shall be examined either by wet method, X-ray fluorescence (XRF), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), Auger or electron probe X-ray microanalysis (EPMA), or wavelength dispersive spectroscopy (WDS). Coating adhesion shall be analyzed either by bend, heat, or cutting test.
SCOPE
1.1 Composition—This specification covers requirements for electrodeposited palladium-nickel coatings containing between 70 and 95 mass % of palladium metal. Composite coatings consisting of palladium-nickel and a thin gold overplate for applications involving electrical contacts are also covered.  
1.2 Properties—Palladium is the lightest and least noble of the platinum group metals. Palladium-nickel is a solid solution alloy of palladium and nickel. Electroplated palladium-nickel alloys have a density between 10 and 11.5, which is substantially less than electroplated gold (17.0 to 19.3) and comparable to electroplated pure palladium (10.5 to 11.8). This yields a greater volume or thickness of coating per unit mass and, consequently, some saving of metal weight. The hardness range of electrodeposited palladium-nickel compares favorably with electroplated noble metals and their alloys (1, 2).2  
Note 1: Electroplated deposits generally have a lower density than their wrought metal counterparts.
Approximate Hardness (HK25)  
Gold  
50–250  
Palladium  
75–600  
Platinum  
150–550  
Palladium-Nickel  
300–650  
Rhodium  
750–1100  
Ruthenium  
600–1300  
1.3 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.4  This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    10 pages
    English language
    sale 15% off
ASTM
ASTM B555-86(2023)(Guide)
Standard Guide for Measurement of Electrodeposited Metallic Coating Thicknesses by Dropping Test

SIGNIFICANCE AND USE
4.1 The thickness of a metal coating is often critical to its performance.  
4.2 This procedure is useful for an approximate determination when the best possible accuracy is not required. For more reliable determinations, the following methods are available: Test Methods B487, B499, B504, and B568.  
4.3 This test assumes that the rate of dissolution of the coating by the corrosive reagent under the specified conditions is always the same.
SCOPE
1.1 This guide covers the use of the dropping test to measure the thickness of electrodeposited zinc, cadmium, copper, and tin coatings.  
Note 1: Under most circumstances this method of measuring coating thicknesses is not as reliable or as convenient to use as an appropriate coating thickness gauge (see Test Methods B499, B504, and B568).  
1.2 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Guide
    5 pages
    English language
    sale 15% off
ASTM
ASTM B734-97(2023)(Specification)
Standard Specification for Electrodeposited Copper for Engineering Uses

ABSTRACT
This specification establishes the requirements for electrodeposited copper coatings used for engineering purposes including surface hardening, heat treatment stop-off, as an underplate for other engineering coatings, for electromagnetic interference shielding in electronic circuitry, and in certain joining operations. This specification does not cover electrodeposited copper used as a decorative finish, as an undercoat for other decorative finishes, or for electroforming. Coatings shall be classified according to thickness. Metal parts shall undergo pre- and post-coating treatment for reducing the risk of hydrogen embrittlement, and peening. Coatings shall be sampled, tested, and shall conform to specified requirements as to appearance, thickness, porosity, solderability, adhesion, embrittlement relief, and packaging.
SCOPE
1.1 This specification covers requirements for electrodeposited coatings of copper used for engineering purposes. Examples include surface hardening, heat treatment stop-off, as an underplate for other engineering coatings, for electromagnetic interferences (EMI) shielding in electronic circuitry, and in certain joining operations.  
1.2 This specification is not intended for electrodeposited copper when used as a decorative finish, or as an undercoat for other decorative finishes.  
1.3 This specification is not intended for electrodeposited copper when used for electroforming.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    4 pages
    English language
    sale 15% off