ASTM C141-97(2005)

Standard Specification for Hydraulic Hydrated Lime for Structural Purposes

ABSTRACT
This specification covers hydraulic hydrated lime for structural purposes. Hydraulic hydrated lime may be used in the scratch or brown coat of plaster, stucco, mortar, or in Portland-cement concrete either as blend, amendment, or admixture. The hydraulic hydrated lime shall conform to the chemical composition requirements for calcium oxide, magnesium oxide, silica, iron oxide, aluminum oxide, and carbon dioxide. The sample shall be subjected to the following test methods: chemical analysis; fineness; normal consistency; time of setting; autoclave expansion; and compressive strength.
SCOPE
1.1 This specification covers hydraulic hydrated lime for structural purposes.  
1.2 Hydraulic hydrated lime may be used in the scratch or brown coat of plaster, stucco, mortar, or in portland-cement concrete either as blend, amendment, or admixture.  
1.3 The values stated in inch-pound units are to be regarded as the standard.  
1.4 The following precautionary caveat pertains only to the test method portion, Section 10 of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

General Information

• Status: Historical
• Publication Date: 30-Jun-2005
• ICS: 91.100.10 - Cement. Gypsum. Lime. Mortar
• Technical Committee: C07 - Lime and Limestone
• Drafting Committee: C07.02 - Specifications and Guidelines

Relations

• Replaces: ASTM C141-97 - Standard Specification for Hydraulic Hydrated Lime for Structural Purposes
• Effective Date: 01-Jul-2005
• Replaced By: ASTM C141/C141M-09 - Standard Specification for Hydrated Hydraulic Lime for Structural Purposes
• Effective Date: 01-Oct-2009
• Referred By: ASTM C1164-22 - Standard Practice for Evaluation of Limestone or Lime Uniformity From a Single Source
• Effective Date: 01-Jul-2005
• Referred By: ASTM C1722-23 - Standard Guide for Repair and Restoration of Dimension Stone
• Effective Date: 01-Jul-2005

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation: C141 – 97 (Reapproved 2005)
Standard Specification for
1
Hydraulic Hydrated Lime for Structural Purposes
This standard is issued under the fixed designation C141; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the Department of Defense.
1. Scope C187 Test Method for Normal Consistency of Hydraulic
Cement
1.1 This specification covers hydraulic hydrated lime for
C230/C230M Specification for Flow Table for Use in Tests
structural purposes.
of Hydraulic Cement
1.2 Hydraulic hydrated lime may be used in the scratch or
C266 TestMethodforTimeofSettingofHydraulic-Cement
brown coat of plaster, stucco, mortar, or in portland-cement
Paste by Gillmore Needles
concrete either as blend, amendment, or admixture.
C305 Practice for Mechanical Mixing of Hydraulic Cement
1.3 The values stated in inch-pound units are to be regarded
Pastes and Mortars of Plastic Consistency
as the standard.
C778 Specification for Standard Sand
1.4 The following precautionary caveat pertains only to the
E11 SpecificationforWovenWireTestSieveClothandTest
test method portion, Section 10 of this specification: This
Sieves
standard does not purport to address all of the safety concerns,
if any, associated with its use. It is the responsibility of the user
3. Terminology
of this standard to establish appropriate safety and health
3.1 Definitions:
practices and determine the applicability of regulatory limita-
3.1.1 hydraulic hydrated lime—the hydrated dry cementi-
tions prior to use.
tious product obtained by calcining a limestone containing
2. Referenced Documents silica and alumina, or a synthetic mixture of similar composi-
2
tion, to a temperature short of incipient fusion so as to form
2.1 ASTM Standards:
sufficient free lime (CaO) to permit hydration and at the same
C25 Test Methods for Chemical Analysis of Limestone,
time leaving unhydrated sufficient calcium silicates to give the
Quicklime, and Hydrated Lime
dry powder, meeting the requirements herein prescribed, its
C109/C109M Test Method for Compressive Strength of
hydraulic properties.
Hydraulic Cement Mortars (Using 2-in. or [50-mm] Cube
Specimens)
NOTE 1—The purchaser may increase the hydraulicity by the addition
C150 Specification for Portland Cement
of pulverized portland cement clinker, or a pulverized pozzolan, either
natural or artificial.
C151 Test Method for Autoclave Expansion of Hydraulic
3
Cement
3.1.1.1 high calcium hydraulic hydrated lime—a lime that
C184 Test Method for Fineness of Hydraulic Cement by the
contains not more than 5 % magnesium oxide (of the nonvola-
4
150-µm (No. 100) and 75-µm (No. 200) Sieves
tile portion).
3.1.1.2 magnesium hydraulic hydrated lime— a lime con-
taining more than 5 % magnesium oxide (of the nonvolatile
1
This specification is under the jurisdiction of ASTM Committee C07 on Lime
portion).
and is the direct responsibility of Subcommittee C07.02 on Structural Lime.
Current edition approved July 1, 2005. Published August 2005. Originally
4. Chemical Composition
approved in 1938. Last previous edition approved in 1997 as C141 – 97. DOI:
4.1 The hydraulic hydrated lime shall conform to the
10.1520/C0141-97R05.
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
following requirements as to chemical composition, calculated
contact ASTM Customer Service at [e-mail]. For Annual Book of ASTM
to the nonvolatile basis:
Standards volume information, refer to the standard’s Document Summary page on
Min Max
the ASTM website.
3
Calcium and magnesium oxides (CaO and MgO calcu- 65 75
Withdrawn.
4
lated to the nonvolatile basis), %
Withdrawn. The last approved version of this historical standard is referenced
Silica (SiO calculated to the nonvolatile basis), % 16 26
2
on www.astm.org.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
1

---------------------- Page: 1 ----------------------
C141 – 97 (2005)
NOTE 2—A piece of rubber tubing attached to a water faucet may be
Iron and aluminum oxides (Fe O and Al O . 12
2 3 2 3
used for the washing. The velocity of the water, which may be increased
caculated to the nonvolatile basis), %
Carbon dioxide (CO on an as received basis), % . 8
bypinchingthetubing,shallnotbesufficienttocauseanysplashingofthe
2
sample over the sides of the sieve.
5. Fineness
NOTE 3—CareshallbetakennottoletwateraccumulateontheNo.200
5.1 The sample shall leave a residue of not more than 0.5 %
(75-µm) sieve, because the openings will become clogged and the
on a No. 30 (600-µ
...