ASTM C1600/C1600M-19

Standard Specification for Rapid Hardening Hydraulic Cement

ABSTRACT
This specification covers performance requirements for rapid hardening hydraulic cements. There are no restrictions on the compositions of the cement or its constituents. The specification classifies cements by type based on specific requirements for very early compressive strength development. The following are the four types of rapid hardening cement: (1) Type URH, ultra rapid hardening for use where high early strength is desired; (2) Type VRH, very rapid hardening for use where very high early strength is desired; (3) Type MRH, medium rapid hardening for use where mid-range hardening high early strength is desired; and (4) Type GRH, general rapid hardening for use when the higher strength properties of a Type VRH or a Type MRH cement is not required. Cement of the type specified shall conform to all of the applicable standard physical requirements for compressive strength and drying shrinkage. Cement shall be tested using the following methods: autoclave expansion; time of setting; compressive strength; drying shrinkage of mortar; heat of hydration; surface resistance; alkali silica resistivity; and expansion in water.
SCOPE
1.1 This specification is for rapid hardening hydraulic cements. This is a specification giving performance requirements. There are no restrictions on the composition of the cement or its constituents.  
1.2 The specification classifies cements by type based on specific requirements for very early compressive strength development.  
1.3 The values stated in either SI units or inch-pound units shall be regarded separately as standard. The values stated in each system are not exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.4 The text of this standard refers to notes and footnotes that provide explanatory material. These notes and footnotes (excluding those in tables and figures) are not requirements of the standard.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. (Warning—Fresh hydraulic cementitious mixtures are caustic and may cause chemical burns to skin and tissue upon prolonged exposure.2)  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

General Information

• Status: Historical
• Publication Date: 14-Dec-2019
• ICS: 91.100.10 - Cement. Gypsum. Lime. Mortar
• Technical Committee: C01 - Cement
• Drafting Committee: C01.13 - Special Cements

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation: C1600/C1600M − 19
Standard Specification for
1
Rapid Hardening Hydraulic Cement
This standard is issued under the fixed designation C1600/C1600M; the number immediately following the designation indicates the
year of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last
reapproval. A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope* 2. Referenced Documents
3
2.1 ASTM Standards:
1.1 This specification is for rapid hardening hydraulic ce-
ments. This is a specification giving performance requirements. C109/C109M Test Method for Compressive Strength of
Hydraulic Cement Mortars (Using 2-in. or [50-mm] Cube
There are no restrictions on the composition of the cement or
its constituents. Specimens)
C114 Test Methods for Chemical Analysis of Hydraulic
1.2 The specification classifies cements by type based on
Cement
specific requirements for very early compressive strength
C151/C151M Test Method for Autoclave Expansion of Hy-
development.
draulic Cement
1.3 The values stated in either SI units or inch-pound units
C183/C183M Practice for Sampling and the Amount of
shall be regarded separately as standard. The values stated in
Testing of Hydraulic Cement
each system are not exact equivalents; therefore, each system
C186 Test Method for Heat of Hydration of Hydraulic
4
shall be used independently of the other. Combining values
Cement (Withdrawn 2019)
from the two systems may result in nonconformance with the
C191 Test Methods for Time of Setting of Hydraulic Cement
standard.
by Vicat Needle
C219 Terminology Relating to Hydraulic and Other Inor-
1.4 The text of this standard refers to notes and footnotes
ganic Cements
that provide explanatory material. These notes and footnotes
C441/C441M Test Method for Effectiveness of Pozzolans or
(excluding those in tables and figures) are not requirements of
Ground Blast-Furnace Slag in Preventing Excessive Ex-
the standard.
pansion of Concrete Due to the Alkali-Silica Reaction
1.5 This standard does not purport to address all of the
C596 Test Method for Drying Shrinkage of Mortar Contain-
safety concerns, if any, associated with its use. It is the
ing Hydraulic Cement
responsibility of the user of this standard to establish appro-
C1012/C1012M Test Method for Length Change of
priate safety and health practices and determine the applica-
Hydraulic-Cement Mortars Exposed to a Sulfate Solution
bility of regulatory limitations prior to use. (Warning—Fresh
C1038/C1038M Test Method for Expansion of Hydraulic
hydraulic cementitious mixtures are caustic and may cause
Cement Mortar Bars Stored in Water
2
chemical burns to skin and tissue upon prolonged exposure. )
C1107/C1107M Specification for Packaged Dry, Hydraulic-
1.6 This international standard was developed in accor-
Cement Grout (Nonshrink)
dance with internationally recognized principles on standard-
C1437 Test Method for Flow of Hydraulic Cement Mortar
ization established in the Decision on Principles for the
2.2 Other Standards
Development of International Standards, Guides and Recom-
EN 14647 Calcium Aluminate Cement - Composition, speci-
mendations issued by the World Trade Organization Technical
fications and conformity criteria
Barriers to Trade (TBT) Committee.
3. Terminology
3.1 Definitions:
1
This test method is under the jurisdiction of ASTM Committee C01 on Cement
3
and is the direct responsibility of Subcommittee C01.13 on Special Cements. For referenced ASTM standards, visit the ASTM website, www.astm.org, or
Current edition approved Dec. 15, 2019. Published January 2020. Originally contact ASTM Customer Service at [e-mail]. For Annual Book of ASTM
approved in 2007. Last previous edition approved in 2018 as C1600/C1600M – 18. Standards volume information, refer to the standard’s Document Summary page on
DOI: 10.1520/C1600_C1600M-19. the ASTM website.
2 4
See the section on Safety, Manual of Cement Testing, Annual Book of ASTM The last approved version of this historical standard is referenced on
Standards, Vol 04.01. www.astm.org.
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
C1600/C1600M − 19
3.1.1 For definitions of terms used in this specification, see 6. Chemical Composition
Terminology C219.
6.1 The chemical composition for the cement is not speci-
3.2 Definitions of Terms Specific to This Standard: fied. However, the purchaser shall have the option to request
3.2.1 Rapid Hardening Hydraulic Cement, n—a hydraulic the cement composition from the producer. If analyzed, the
or blended hydraulic cement which exhibits rapid
...

This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation: C1600/C1600M − 18 C1600/C1600M − 19
Standard Specification for
1
Rapid Hardening Hydraulic Cement
This standard is issued under the fixed designation C1600/C1600M; the number immediately following the designation indicates the
year of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last
reapproval. A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope*
1.1 This specification is for rapid hardening hydraulic cements. This is a specification giving performance requirements. There
are no restrictions on the composition of the cement or its constituents.
1.2 The specification classifies cements by type based on specific requirements for very early compressive strength
development.
1.3 The values stated in either SI units or inch-pound units shall be regarded separately as standard. The values stated in each
system are not exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two
systems may result in nonconformance with the standard.
1.4 The text of this standard refers to notes and footnotes that provide explanatory material. These notes and footnotes
(excluding those in tables and figures) are not requirements of the standard.
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility
of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory
limitations prior to use. (Warning—Fresh hydraulic cementitious mixtures are caustic and may cause chemical burns to skin and
2
tissue upon prolonged exposure. )
1.6 This international standard was developed in accordance with internationally recognized principles on standardization
established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued
by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
2. Referenced Documents
3
2.1 ASTM Standards:
C109/C109M Test Method for Compressive Strength of Hydraulic Cement Mortars (Using 2-in. or [50-mm] Cube Specimens)
C114 Test Methods for Chemical Analysis of Hydraulic Cement
C151/C151M Test Method for Autoclave Expansion of Hydraulic Cement
C183/C183M Practice for Sampling and the Amount of Testing of Hydraulic Cement
4
C186 Test Method for Heat of Hydration of Hydraulic Cement (Withdrawn 2019)
C191 Test Methods for Time of Setting of Hydraulic Cement by Vicat Needle
C219 Terminology Relating to Hydraulic and Other Inorganic Cements
C441/C441M Test Method for Effectiveness of Pozzolans or Ground Blast-Furnace Slag in Preventing Excessive Expansion of
Concrete Due to the Alkali-Silica Reaction
C596 Test Method for Drying Shrinkage of Mortar Containing Hydraulic Cement
C1012/C1012M Test Method for Length Change of Hydraulic-Cement Mortars Exposed to a Sulfate Solution
C1038/C1038M Test Method for Expansion of Hydraulic Cement Mortar Bars Stored in Water
C1107/C1107M Specification for Packaged Dry, Hydraulic-Cement Grout (Nonshrink)
C1437 Test Method for Flow of Hydraulic Cement Mortar
2.2 Other Standards
EN 14647 Calcium Aluminate Cement - Composition, specifications and conformity criteria
1
This test method is under the jurisdiction of ASTM Committee C01 on Cement and is the direct responsibility of Subcommittee C01.13 on Special Cements.
Current edition approved Dec. 15, 2018Dec. 15, 2019. Published January 2019January 2020. Originally approved in 2007. Last previous edition approved in 20172018
as C1600/C1600M – 17.C1600/C1600M – 18. DOI: 10.1520/C1600_C1600M-18. 10.1520/C1600_C1600M-19.
2
See the section on Safety, Manual of Cement Testing, Annual Book of ASTM Standards, Vol 04.01.
3
For referenced ASTM standards, visit the ASTM website, www.astm.org, or contact ASTM Customer Service at [e-mail]. For Annual Book of ASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
4
The last approved version of this historical standard is referenced on www.astm.org.
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
C1600/C1600M − 19
3. Terminology
3.1 Definitions:
3.1.1 For definitions of terms used in this specification, see Terminology C219.
3.2 Definitions of Terms
...