Standard Guide for Testing Polymer Matrix Composite Materials

Standard Guide for Testing Polymer Matrix Composite Materials

SIGNIFICANCE AND USE
This guide is intended to aid in the selection of standards for polymer matrix composite materials. It specifically summarizes the application of standards from ASTM Committee D30 on Composite Materials that apply to continuous-fiber reinforced polymer matrix composite materials. For reference and comparison, many commonly used or applicable ASTM standards from other ASTM Committees are also included.
SCOPE
1.1 This guide summarizes the application of ASTM standard test methods (and other supporting standards) to continuous-fiber reinforced polymer matrix composite materials. The most commonly used or most applicable ASTM standards are included, emphasizing use of standards of Committee D30 on Composite Materials.
1.2 This guide does not cover all possible standards that could apply to polymer matrix composites and restricts discussion to the documented scope. Commonly used but non-standard industry extensions of test method scopes, such as application of static test methods to fatigue testing, are not discussed. A more complete summary of general composite testing standards, including non-ASTM test methods, is included in the Composite Materials Handbook (MIL-HDBK-17). Additional specific recommendations for testing textile (fabric, braided) composites are contained in Guide D6856.
1.3 This guide does not specify a system of measurement; the systems specified within each of the referenced standards shall apply as appropriate. Note that the referenced standards of ASTM Committee D30 are either SI-only or combined-unit standards with SI units listed first.
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

General Information

Status
Historical
Publication Date
31-Jul-2011
ICS
83.140.20 - Laminated sheets
Technical Committee
D30 - Composite Materials
Drafting Committee
D30.01 - Editorial and Resource Standards
Current Stage
Ref Project

Relations

Replaces
ASTM D4762-11 - Standard Guide for Testing Polymer Matrix Composite Materials
Effective Date
01-Aug-2011
Replaced By
ASTM D4762-16 - Standard Guide for Testing Polymer Matrix Composite Materials
Effective Date
15-Aug-2016
Referred By
ASTM E2533-21 - Standard Guide for Nondestructive Examination of Polymer Matrix Composites Used in Aerospace Applications
Effective Date
01-Aug-2011
Referred By
ASTM D8509/D8509M-23 - Standard Guide for Test Method Selection and Test Specimen Design for Bolted Joint Related Properties
Effective Date
01-Aug-2011
Referred By
ASTM D8069-17a - Standard Test Method for Determining Flexural Modulus of Full Section Pultruded Fiber Reinforced Polymer (FRP) Composite Members with Doubly Symmetric Cross Sections under Bending
Effective Date
01-Aug-2011

Buy Standard

ASTM D4762-11a - Standard Guide for Testing Polymer Matrix Composite MaterialsASTM D4762-11a - Standard Guide for Testing Polymer Matrix Composite Materials
PreviousNext
Guide
ASTM D4762-11a - Standard Guide for Testing Polymer Matrix Composite Materials
English language
21 pages
sale 15% off
Preview
sale 15% off
Preview
REDLINE ASTM D4762-11a - Standard Guide for Testing Polymer Matrix Composite MaterialsREDLINE ASTM D4762-11a - Standard Guide for Testing Polymer Matrix Composite Materials
PreviousNext
Guide
REDLINE ASTM D4762-11a - Standard Guide for Testing Polymer Matrix Composite Materials
English language
21 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation: D4762 − 11a
StandardGuide for
1
Testing Polymer Matrix Composite Materials
This standard is issued under the fixed designation D4762; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision.Anumber in parentheses indicates the year of last reapproval.A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope C271/C271MTest Method for Density of Sandwich Core
Materials
1.1 This guide summarizes the application of ASTM stan-
C272Test Method for Water Absorption of Core Materials
dard test methods (and other supporting standards) to
for Structural Sandwich Constructions
continuous-fiber reinforced polymer matrix composite materi-
C273/C273MTestMethodforShearPropertiesofSandwich
als. The most commonly used or most applicable ASTM
Core Materials
standards are included, emphasizing use of standards of Com-
C297/C297MTest Method for Flatwise Tensile Strength of
mittee D30 on Composite Materials.
Sandwich Constructions
1.2 This guide does not cover all possible standards that
C363/C363MTest Method for Node Tensile Strength of
could apply to polymer matrix composites and restricts discus-
Honeycomb Core Materials
sion to the documented scope. Commonly used but non-
C364/C364M Test Method for Edgewise Compressive
standard industry extensions of test method scopes, such as
Strength of Sandwich Constructions
application of static test methods to fatigue testing, are not
C365/C365MTest Method for Flatwise Compressive Prop-
discussed. A more complete summary of general composite
erties of Sandwich Cores
testing standards, including non-ASTM test methods, is in-
C366/C366MTest Methods for Measurement of Thickness
cluded in the Composite Materials Handbook (MIL-HDBK-
of Sandwich Cores
2
17). Additional specific recommendations for testing textile
C393/C393MTest Method for Core Shear Properties of
(fabric, braided) composites are contained in Guide D6856.
Sandwich Constructions by Beam Flexure
1.3 This guide does not specify a system of measurement;
C394Test Method for Shear Fatigue of Sandwich Core
the systems specified within each of the referenced standards
Materials
shall apply as appropriate. Note that the referenced standards
C480/C480MTest Method for Flexure Creep of Sandwich
ofASTM Committee D30 are either SI-only or combined-unit
Constructions
standards with SI units listed first.
C481Test Method for Laboratory Aging of Sandwich Con-
structions
1.4 This standard does not purport to address all of the
C613/C613MTest Method for Constituent Content of Com-
safety concerns, if any, associated with its use. It is the
posite Prepreg by Soxhlet Extraction
responsibility of the user of this standard to establish appro-
D2344/D2344MTest Method for Short-Beam Strength of
priate safety and health practices and determine the applica-
bility of regulatory limitations prior to use. PolymerMatrixCompositeMaterialsandTheirLaminates
D3039/D3039MTest Method forTensile Properties of Poly-
2. Referenced Documents
mer Matrix Composite Materials
3
D3171Test Methods for Constituent Content of Composite
2.1 ASTM Standards:
Materials
2.1.1 StandardsofCommitteeD30onCompositeMaterials
D3410/D3410MTest Method for Compressive Properties of
Polymer Matrix Composite Materials with Unsupported
1
This guide is under the jurisdiction of ASTM Committee D30 on Composite
Gage Section by Shear Loading
Materialsand is the direct responsibility of Subcommittee D30.01 on Editorial and
D3479/D3479MTest Method for Tension-Tension Fatigue
Resource Standards.
Current edition approved Aug. 1, 2011. Published September 2011. Originally
of Polymer Matrix Composite Materials
approved in 1988. Last previous edition approved in 2011 as D4762–11. DOI:
D3518/D3518MTest Method for In-Plane Shear Response
10.1520/D4762-11A.
ofPolymerMatrixCompositeMaterialsbyTensileTestof
2
Available from Standardization Documents Order Desk, DODSSP, Bldg. 4,
a 645° Laminate
Section D, 700 Robbins Ave., Philadelphia, PA 19111-5098, http://
dodssp.daps.dla.mil.
D3529/D3529MTest Method for Matrix Solids Content and
3
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
Matrix Content of Composite Prepreg
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
D3530/D3530MTest Method for Volatiles Content of Com-
Standards volume information, refer to the standard’s Document Summary page on
the ASTM website. posite Material Prepreg
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
D4762 − 11a
D3531Test Method for Resin Flow of Carbon Fiber-Epoxy D6671/D6671MTest Method for Mixed Mode I-Mode II
Prepreg Interlaminar Fracture Toughn
...

This document is not anASTM standard and is intended only to provide the user of anASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation:D4762–11 Designation:D4762–11a
Standard Guide for
1
Testing Polymer Matrix Composite Materials
This standard is issued under the fixed designation D4762; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope
1.1 This guide summarizes the application ofASTM standard test methods (and other supporting standards) to continuous-fiber
reinforced polymer matrix composite materials. The most commonly used or most applicable ASTM standards are included,
emphasizing use of standards of Committee D30 on Composite Materials.
1.2 This guide does not cover all possible standards that could apply to polymer matrix composites and restricts discussion to
the documented scope. Commonly used but non-standard industry extensions of test method scopes, such as application of static
test methods to fatigue testing, are not discussed. A more complete summary of general composite testing standards, including
2
non-ASTM test methods, is included in the Composite Materials Handbook (MIL-HDBK-17). Additional specific recommen-
dations for testing textile (fabric, braided) composites are contained in Guide D6856.
1.3 This guide does not specify a system of measurement; the systems specified within each of the referenced standards shall
apply as appropriate. Note that the referenced standards of ASTM Committee D30 are either SI-only or combined-unit standards
with SI units listed first.
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility
of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory
limitations prior to use.
2. Referenced Documents
3
2.1 ASTM Standards:
2.1.1 Standards of Committee D30 on Composite Materials
C271/C271M Test Method for Density of Sandwich Core Materials
C272 Test Method for Water Absorption of Core Materials for Structural Sandwich Constructions
C273/C273M Test Method for Shear Properties of Sandwich Core Materials
C297/C297M Test Method for Flatwise Tensile Strength of Sandwich Constructions
C363/C363M Test Method for Node Tensile Strength of Honeycomb Core Materials
C364/C364M Test Method for Edgewise Compressive Strength of Sandwich Constructions
C365/C365M Test Method for Flatwise Compressive Properties of Sandwich Cores
C366/C366M Test Methods for Measurement of Thickness of Sandwich Cores
C393/C393M Test Method for Core Shear Properties of Sandwich Constructions by Beam Flexure
C394 Test Method for Shear Fatigue of Sandwich Core Materials
C480/C480M Test Method for Flexure Creep of Sandwich Constructions
C481 Test Method for Laboratory Aging of Sandwich Constructions
C613/C613M Test Method for Constituent Content of Composite Prepreg by Soxhlet Extraction
D2344/D2344M Test Method for Short-Beam Strength of Polymer Matrix Composite Materials and Their Laminates
D3039/D3039M Test Method for Tensile Properties of Polymer Matrix Composite Materials
D3171 Test Methods for Constituent Content of Composite Materials
D3410/D3410M Test Method for Compressive Properties of Polymer Matrix Composite Materials with Unsupported Gage
Section by Shear Loading
D3479/D3479M Test Method for Tension-Tension Fatigue of Polymer Matrix Composite Materials
1
ThisguideisunderthejurisdictionofASTMCommitteeD30onCompositeMaterials andisthedirectresponsibilityofSubcommitteeD30.01onEditorialandResource
Standards.
Current edition approved Jan. 15,Aug. 1, 2011. Published FebruarySeptember 2011. Originally approved in 1988. Last previous edition approved in 20082011 as
D4762–08.D4762 – 11. DOI: 10.1520/D4762-11A.
2
Available from Standardization Documents Order Desk, DODSSP, Bldg. 4, Section D, 700 Robbins Ave., Philadelphia, PA 19111-5098, http://dodssp.daps.dla.mil.
3
For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at service@astm.org. For Annual Book ofASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
1

---------------------- Page: 1 ----------------------
D4762–11a
D3518/D3518M Test Method for In-Plane Shear Response of Polymer Matrix Composite Materials by Tensile Test o
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

ASTM
ASTM D3479/D3479M-19(2023)(Test Method)
Standard Test Method for Tension-Tension Fatigue of Polymer Matrix Composite Materials

SIGNIFICANCE AND USE
5.1 This test method is designed to yield tensile fatigue data for material specifications, research and development, quality assurance, and structural design and analysis. The primary test result is the fatigue life of the test specimen under a specific loading and environmental condition. Replicate tests may be used to obtain a distribution of fatigue life for specific material types, laminate stacking sequences, environments, and loading conditions. Guidance in statistical analysis of fatigue life data, such as determination of linearized stress life (S-N) or strain-life (ε-N) curves, can be found in Practice E739.  
5.2 This test method can be utilized in the study of fatigue damage in a polymer matrix composite such as the occurrence of microscopic cracks, fiber fractures, or delaminations.3 The specimen's residual strength or stiffness, or both, may change due to these damage mechanisms. The loss in stiffness may be quantified by discontinuing cyclic loading at selected cycle intervals to obtain the quasi-static axial stress-strain curve using modulus determination procedures found in Test Method D3039/D3039M. The loss in strength associated with fatigue damage may be determined by discontinuing cyclic loading to obtain the static strength using Test Method D3039/D3039M.  
Note 1: This test method may be used as a guide to conduct tension-tension variable amplitude loading. This information can be useful in the understanding of fatigue behavior of composite structures under spectrum loading conditions, but is not covered in this test method.
SCOPE
1.1 This test method determines the fatigue behavior of polymer matrix composite materials subjected to tensile cyclic loading. The composite material forms are limited to continuous-fiber or discontinuous-fiber reinforced composites for which the elastic properties are specially orthotropic with respect to the test direction. This test method is limited to unnotched test specimens subjected to constant amplitude uniaxial in-plane loading where the loading is defined in terms of a test control parameter.  
1.2 This test method presents two procedures where each defines a different test control parameter.  
1.2.1 Procedure A—A system in which the test control parameter is the load (stress) and the machine is controlled so that the test specimen is subjected to repetitive constant amplitude load cycles. In this procedure, the test control parameter may be described using either engineering stress or applied load as a constant amplitude fatigue variable.  
1.2.2 Procedure B—A system in which the test control parameter is the strain in the loading direction and the machine is controlled so that the test specimen is subjected to repetitive constant amplitude strain cycles. In this procedure, the test control parameter may be described using engineering strain in the loading direction as a constant amplitude fatigue variable.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.3.1 Within the text the inch-pound units are shown in brackets.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    6 pages
    English language
    sale 15% off
ASTM
ASTM D4762-23(Guide)
Standard Guide for Testing Polymer Matrix Composite Materials

SIGNIFICANCE AND USE
4.1 This guide is intended to aid in the selection of standards for polymer matrix composite materials. It specifically summarizes the application of standards from ASTM Committee D30 on Composite Materials that apply to continuous-fiber reinforced polymer matrix composite materials. For reference and comparison, many commonly used or applicable ASTM standards from other ASTM Committees are also included.
SCOPE
1.1 This guide summarizes the application of ASTM standard test methods (and other supporting standards) to continuous-fiber reinforced polymer matrix composite materials. The most commonly used or most applicable ASTM standards are included, emphasizing use of standards of Committee D30 on Composite Materials.  
1.2 This guide does not cover all possible standards that could apply to polymer matrix composites and restricts discussion to the documented scope. Commonly used but non-standard industry extensions of test method scopes, such as application of static test methods to fatigue testing, are not discussed. A more complete summary of general composite testing standards, including non-ASTM test methods, is included in the Composite Materials Handbook (CMH-17).2 Additional specific recommendations for testing textile (fabric, braided) composites are contained in Guide D6856.  
1.3 This guide does not specify a system of measurement; the systems specified within each of the referenced standards shall apply as appropriate. Note that the referenced standards of ASTM Committee D30 are either SI-only or combined-unit standards with SI units listed first.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Guide
    27 pages
    English language
    sale 15% off
  • Guide
    27 pages
    English language
    sale 15% off
ASTM
ASTM D8387/D8387M-23(Test Method)
Standard Test Method for High Bypass – Low Bearing Interaction Response of Polymer Matrix Composite Laminates

SIGNIFICANCE AND USE
5.1 Refer to Guide D8509.
SCOPE
1.1 This test method determines the uniaxial high bypass - low bearing interaction response of multi-directional polymer matrix composite laminates reinforced by high-modulus fibers using a two-fastener hard point joint specimen. The scope of this test method is limited to net section (bypass) failure modes. Standard specimen configurations using fixed values of test parameters are described for this procedure. A number of test parameters may be varied within the scope of the standard, provided that the parameters are fully documented in the test report. The composite material forms are limited to continuous-fiber or discontinuous-fiber (tape or fabric, or both) reinforced composites for which the laminate is balanced and symmetric with respect to the test direction. The range of acceptable test laminates and thicknesses are described in 8.2.1. This test method was previously published under Test Method D7248/D7248M-17 Procedure C.  
1.2 This test method is consistent with the recommendations of Composite Materials Handbook, CMH-17, which describes the desirable attributes of a bearing/bypass interaction response test method.  
1.3 The two-fastener test configurations described in this test method are intended to provide data in the relatively high bypass, low bearing part of the composite bolted joint bearing-bypass interaction diagram. This data complements the data from filled hole tension and compression (Practice D6742/D6742M), bearing (Test Method D5961/D5961M), and low bypass/high bearing interaction (Test Method D7248/D7248M) tests.  
1.4 This test method requires careful specimen design, instrumentation, data measurement, and data analysis. The use of this test method requires close coordination between the test requestor and the test lab personnel. Test requestors need to be familiar with the data analysis procedures of this test method and should not expect test labs who are unfamiliar with this test method to be able to produce acceptable results without close coordination.  
1.5 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.5.1 Within the text, the inch-pound units are shown in brackets.  
1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    27 pages
    English language
    sale 15% off
  • Standard
    27 pages
    English language
    sale 15% off
ASTM
ASTM D6873/D6873M-23(Practice)
Standard Practice for Bearing Fatigue Response of Polymer Matrix Composite Laminates

SIGNIFICANCE AND USE
5.1 Refer to Guide D8509.
SCOPE
1.1 This practice provides instructions for modifying static bearing test methods to determine the fatigue behavior of composite materials subjected to cyclic bearing forces. The composite material forms are limited to continuous-fiber reinforced polymer matrix composites in which the laminate is both symmetric and balanced with respect to the test direction. The range of acceptable test laminates and thicknesses are described in 8.2.  
1.2 This practice supplements Test Method D5961/D5961M with provisions for testing specimens under cyclic loading. Several important test specimen parameters (for example, fastener selection, fastener installation method, and fatigue force/stress ratio) are not mandated by this practice; however, repeatable results require that these parameters be specified and reported.  
1.3 This practice is limited to test specimens subjected to constant amplitude uniaxial loading, where the machine is controlled so that the test specimen is subjected to repetitive constant amplitude force (stress) cycles. Either engineering stress or applied force may be used as a constant amplitude fatigue variable. The repetitive loadings may be tensile, compressive, or reversed, depending upon the test specimen and procedure utilized.  
1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.4.1 Within the text the inch-pound units are shown in brackets.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    8 pages
    English language
    sale 15% off
  • Standard
    8 pages
    English language
    sale 15% off
ASTM
ASTM D8066/D8066M-23(Practice)
Standard Practice Unnotched Compression Testing of Polymer Matrix Composite Laminates

SIGNIFICANCE AND USE
5.1 This practice provides supplemental instructions for the use of Test Method D6484/D6484M to determine unnotched compressive strength data for material specifications, research and development, material design allowables, and quality assurance. Factors that influence compressive strengths and shall therefore be reported include the following: material, methods of material fabrication, accuracy of lay-up, laminate stacking sequence and overall thickness, specimen preparation, specimen conditioning, environment of testing, specimen alignment and gripping, speed of testing, time at temperature, void content, and volume percent reinforcement. Composite properties in the test direction that may be obtained from this test method include:  
5.1.1 Unnotched compressive (UNC) strength, Fxunc,  
5.1.2 Ultimate compressive strain,  
5.1.3 Compressive (linear or chord) modulus of elasticity, Ec, and  
5.1.4 Poisson's ratio in compression.  
5.2 This practice provides a compression test method for laminates containing fibers in multiple fiber directions, particularly those combining axial (0 degree) fibers and off-axis (± θ degree) fibers. Other compression strength test methods include SACMA SRM-1 (also known as the modified D695), D3410/D3410M, D5467/D5467M, D6641/D6641M, and D7249/D7249M. The SRM-1 test uses 12.6 mm [0.50 in.] wide specimens, which is only appropriate for unidirectional tape, cross-ply [0/90]ns tape, or small unit-cell-size fabrics (e.g. 3K-70-P). Larger cell-size fabrics (for example, spread-tow 12K fabrics) should be tested with wider specimens. The standard D3410/D3410M and D6641/D6641M test fixtures do permit the use of wider specimens, for example, 25.4 mm [1.0 in.] wide, and thus can be used to test laminates containing both axial and off-axis fibers; however their gage lengths are relatively short. Test Method D5467/D5467M is intended to obtain the compressive strength of unidirectional laminates, but is expensive due to the sandwich beam confi...
SCOPE
1.1 This practice provides instructions for using the Test Method D6484/D6484M open hole compression test fixture to determine unnotched compressive strength of multi-directional laminates. The composite material forms are limited to continuous-fiber reinforced polymer matrix composites in which the laminate is both symmetric and balanced with respect to the test direction. The range of acceptable test laminates and thicknesses are described in 8.2.1.  
1.2 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.2.1 Within the text the inch-pound units are shown in brackets.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    6 pages
    English language
    sale 15% off
  • Standard
    6 pages
    English language
    sale 15% off
ASTM
ASTM D8131/D8131M-23(Practice)
Standard Practice for Tensile Properties of Tapered and Stepped Joints of Polymer Matrix Composite Laminates

SIGNIFICANCE AND USE
5.1 This test practice is designed to produce tensile property data for material specifications, research and development, quality assurance, and structural design and analysis. Factors that influence the tensile response and should therefore be reported include the following: materials (laminates and adhesive), methods of material preparation including surface preparation prior to bonding, lay-ups, specimen stacking sequence, joint taper ratio or step length, ply overlap length, material relative thicknesses and stiffness of the parent and repair laminates, adhesive bond stiffness, specimen preparation, specimen conditioning, environment of testing, specimen alignment and gripping, speed of testing, time at temperature, void content, and volume percent reinforcement. Properties in the test direction, which may be obtained from this test practice, include the following:  
5.1.1 Ultimate tensile strength (based on the nominal parent material thickness), (Fptu).  
5.1.2 Ultimate tensile strength (based on the nominal repair material thickness), (Frtu).  
5.1.3 Ultimate running force per repair ply, (Nj).
SCOPE
1.1 This test practice defines the procedure for determination of the tensile strength of a tapered or stepped joint of polymer matrix composite materials. It is applicable to secondary bonded or co-bonded laminates with either unidirectional plies or woven fabric reinforcements. The materials to be bonded may be different material systems. In the bondline, a separate adhesive material may or may not be used (example: adhesives may be used with a prepreg system or may not be used with a wet lay-up repair system). The range of acceptable test laminates and thicknesses is described in 8.2.1.  
1.2 This practice supplements Test Method D3039/D3039M for tensile loading. Several important test specimen parameters (for example, joint length, ply overlaps, step depth, and taper ratio) are not mandated by this practice, however, these parameters are required to be specified and reported to support repeatable results.  
1.3 Unidirectional (0° ply orientation) tape composites, textile composites, as well as multidirectional composite laminates, can be tested.  
1.4 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.4.1 Within the text the inch-pound units are shown in brackets.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    9 pages
    English language
    sale 15% off
  • Standard
    9 pages
    English language
    sale 15% off
ASTM
ASTM D2344/D2344M-22(Test Method)
Standard Test Method for Short-Beam Strength of Polymer Matrix Composite Materials and Their Laminates

SIGNIFICANCE AND USE
5.1 In most cases, because of the complexity of internal stresses and the variety of failure modes that can occur in this specimen, it is not generally possible to relate the short-beam strength to any one material property. However, failures are normally dominated by resin and interlaminar properties, and the test results have been found to be repeatable for a given specimen geometry, material system, and stacking sequence  (4).  
5.2 Short-beam strength determined by this test method can be used for quality control and process specification purposes. It can also be used for comparative testing of composite materials, provided that failures occur consistently in the same mode (5) .  
5.3 This test method is not limited to specimens within the range specified in Section 8, but is limited to the use of a loading span length-to-specimen thickness ratio of 4.0 and a minimum specimen thickness of 2.0 mm [0.08 in.].
SCOPE
1.1 This test method determines the short-beam strength of high-modulus fiber-reinforced composite materials. The specimen is a short beam machined from a curved or a flat laminate up to 6.00 mm [0.25 in.] thick. The beam is loaded in three-point bending.  
1.2 Application of this test method is limited to continuous- or discontinuous-fiber-reinforced polymer matrix composites, for which the elastic properties are balanced and symmetric with respect to the longitudinal axis of the beam.  
1.3 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.3.1 Within the text, the inch-pound units are shown in brackets.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    10 pages
    English language
    sale 15% off
  • Standard
    10 pages
    English language
    sale 15% off
ASTM
ASTM D5449/D5449M-22(Test Method)
Standard Test Method for Transverse Compressive Properties of Hoop Wound Polymer Matrix Composite Cylinders

SIGNIFICANCE AND USE
5.1 This test method is designed to produce transverse compressive property data for material specifications, research and development, quality assurance, and structural design and analysis. Factors that influence the transverse compressive response and should therefore be reported are: material, method of material preparation, specimen preparation, specimen conditioning, environment of testing, specimen alignment and gripping, speed of testing, void content, and fiber volume fraction. Properties in the test direction that may be obtained from this test method are:  
5.1.1 Transverse compressive strength, σ22uc,  
5.1.2 Transverse compressive strain at failure, ε22uc,  
5.1.3 Transverse compressive modulus of elasticity, E22, and  
5.1.4 Poisson's ratio, γ21.
SCOPE
1.1 This test method determines the transverse compressive properties of wound polymer matrix composites reinforced by high-modulus continuous fibers. It describes testing of hoop wound (90°) cylinders in axial compression for determination of transverse compressive properties.  
1.2 The technical content of this test method has been stable since 1993 without significant objection from its stakeholders. As there is limited technical support for the maintenance of this test method, changes since that date have been limited to items required to retain consistency with other ASTM D30 Committee standards, including editorial changes and incorporation of updated guidance on specimen preconditioning and environmental testing. The test method, therefore, should not be considered to include any significant changes in approach and practice since 1993. Future maintenance of the test method will only be in response to specific requests and performed only as technical support allows.  
1.3 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.3.1 Within the text, the inch-pound units are shown in brackets.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    10 pages
    English language
    sale 15% off
  • Standard
    10 pages
    English language
    sale 15% off
ASTM
ASTM D5450/D5450M-22(Test Method)
Standard Test Method for Transverse Tensile Properties of Hoop Wound Polymer Matrix Composite Cylinders

SIGNIFICANCE AND USE
5.1 This test method is used to produce transverse tensile property data for material specifications, research and development, quality assurance, and structural design and analysis. Factors which influence the transverse tensile response and should, therefore, be reported are: material, methods of material preparation, specimen preparation, specimen conditioning, environment of testing, specimen alignment and gripping, speed of testing, void content, and fiber volume fraction. Properties, in the test direction, which may be obtained from this test method include:  
5.1.1 Transverse Tensile Strength,    
5.1.2 Transverse Tensile Strain at Failure,    
5.1.3 Transverse Tensile Modulus of Elasticity,  E22, and  
5.1.4 Poisson's Ratio,  υ21.
SCOPE
1.1 This test method determines the transverse tensile properties of wound polymer matrix composites reinforced by high-modulus continuous fibers. It describes testing of hoop wound (90°) cylinders in axial tension for determination of transverse tensile properties.  
1.2 The technical content of this test method has been stable since 1993 without significant objection from its stakeholders. As there is limited technical support for the maintenance of this test method, changes since that date have been limited to items required to retain consistency with other ASTM D30 Committee standards, including editorial changes and incorporation of updated guidance on specimen preconditioning and environmental testing. The test method, therefore, should not be considered to include any significant changes in approach and practice since 1993. Future maintenance of the test method will only be in response to specific requests and performed only as technical support allows.  
1.3 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.3.1 Within the text, the inch-pound units are shown in brackets.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    9 pages
    English language
    sale 15% off
  • Standard
    9 pages
    English language
    sale 15% off
ASTM
ASTM E1922/E1922M-22(Test Method)
Standard Test Method for Translaminar Fracture Toughness of Laminated and Pultruded Polymer Matrix Composite Materials

SIGNIFICANCE AND USE
5.1 The parameter KTL  determined by this test method is a measure of the resistance of a polymer matrix composite laminate to notch-tip damage and effective translaminar crack growth under opening mode loading. The result is valid only for conditions in which the damage zone at the notch tip is small compared with the notch length and the in-plane specimen dimensions. Alternately, for materials exhibiting distributed damage in a larger volume, observed force-displacement and discrete damage events are still valid structural responses for certain specific engineering applications.  
5.2 This test method can serve the following purposes. In research and development, (a) KTL data can quantitatively establish the effects of fiber and matrix variables and stacking sequence of the laminate on the translaminar fracture resistance of composite laminates; and (b) quantified distributed damage measurements can be used to validate progressive composite damage models. In structural design, KTL data can, within the constraints of the specimen geometry and loading, be used to assess composite laminate resistance to damage growth from edge flaws and notches.  
5.3 The translaminar fracture toughness,  KTL, as well as distributed damage observations, determined by this test method may be a function of the testing speed and temperature. This test method is intended for room temperature and quasi-static conditions, but it can apply to other test conditions provided that the requirements of 13.2 and 13.3 are met. Application of KTL in the design of service components should be made with awareness that the test parameters specified by this test may differ from service conditions, possibly resulting in a different material response than that seen in service. Distributed damage observations are also limited to the material and geometry tested, but may be more generally applied to a variety of structural analysis validation applications.  
5.4 Not all types of laminated polymer matrix...
SCOPE
1.1 This test method covers the determination of translaminar fracture toughness, KTL, for laminated, molded, or pultruded polymer matrix composite materials of various fiber orientations using test results from monotonically loaded notched specimens. If the material response is such that the KTL calculation is not valid, alternate reporting methods are provided.  
1.2 This test method is applicable to room temperature laboratory air environments.  
1.3 Composite materials that can be tested by this test method are not limited by thickness or by type of polymer matrix or fiber, provided that the specimen sizes and the test results meet the requirements of this test method. This test method was developed primarily from test results of various carbon fiber – epoxy matrix laminates and from additional results of glass fiber – epoxy matrix, glass fiber-polyester matrix pultrusions and carbon fiber – bismaleimide matrix laminates (1-4, 5, 6).2  
1.4 A range of eccentrically loaded, single-edge-notch tension, ESE(T), specimen sizes with proportional planar dimensions is provided, but planar size may be variable and adjusted, with associated changes in the applied test load. Specimen thickness is a variable, independent of planar size.  
1.5 Specimen configurations other than those contained in this test method may be used. It is particularly important that the requirements discussed in 5.1 and 5.4 regarding contained notch-tip damage be met when using alternative specimen configurations in conjunction with the KTL calculation.  
1.6 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.6.1 Within the text, the inch-pound units are shown ...

  • Standard
    8 pages
    English language
    sale 15% off
  • Standard
    8 pages
    English language
    sale 15% off