ASTM E279-97(2001)
(Test Method)Standard Test Method for Determination of Abrasion Resistance of Iron Ore Pellets and Sinter by the Tumbler Test
Standard Test Method for Determination of Abrasion Resistance of Iron Ore Pellets and Sinter by the Tumbler Test
SCOPE
1.1 This test method provides a relative measure of the resistance of iron ore pellets and sinter to degradation by impact and by abrasion.
1.2 The values as stated in SI units are to be regarded as the standard. The values in parentheses are given for information only.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
General Information
Relations
Standards Content (Sample)
NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation:E279–97 (Reapproved 2001)
Standard Test Method for
Determination of Abrasion Resistance of Iron Ore Pellets
and Sinter by the Tumbler Test
This standard is issued under the fixed designation E 279; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (e) indicates an editorial change since the last revision or reapproval.
1. Scope 4. Summary of Test Method
1.1 This test method provides a relative measure of the 4.1 Thesampleisplacedinatumblerdrumwhichisrotated.
resistance of iron ore pellets and sinter to degradation by Thetumbledmaterialisremovedandscreenedtodeterminethe
impact and by abrasion. degradation.
1.2 The values as stated in SI units are to be regarded as the
5. Significance and Use
standard. The values in parentheses are given for information
5.1 This test method is a comparative method intended
only.
1.3 This standard does not purport to address all of the primarily to test materials for compliance with compositional
specifications or for monitoring. It is assumed that all who use
safety concerns, if any, associated with its use. It is the
responsibility of the user of this standard to establish appro- these procedures will be trained analysts capable of performing
common laboratory procedures skillfully and safely. It is
priate safety and health practices and determine the applica-
bility of regulatory limitations prior to use. expected that work will be performed in a properly equipped
laboratory and that proper waste disposal procedures will be
2. Referenced Documents
followed. Appropriate quality control practices must be fol-
2.1 ASTM Standards: lowed such as those described in Guide E 882.
E 135 Terminology Relating to Analytical Chemistry for 5.2 This test method is used to monitor the feed to blast
Metals, Ores, and Related Materials furnaces for process control.
E 276 Test Method for Particle Size or Screen Analysis at
6. Apparatus
No. 4 (4.75-mm) Sieve and Finer for Metal-Bearing Ores
and Related Materials 6.1 Tumbler Apparatus, as shown in Fig. 1, shall be a
circular drum 914 mm (36 in.) in inside diameter and 457 mm
E 389 Test Method for Particle Size or Screen Analysis at
No. 4 (4.75-mm) Sieve and Coarser for Metal-Bearing (18 in.) in inside length constructed of steel plate at least 6.3
mm ( ⁄4in.) in thickness. The drum shall be replaced whenever
Ores and Related Materials
E 877 PracticeforSamplingandSamplePreparationofIron the thickness of the plate is reduced by wear to 3.18 mm ( ⁄8in.)
in any area.Two equally spaced steel angle lifters, 50.8 by 50.8
Ores and Related Materials
E 882 Guide for Accountability and Quality Control in the by 6.35 mm (2 by 2 by ⁄4 in.) shall be solidly attached
longitudinally inside the drum by riveting in such a manner as
Chemical Analysis Laboratory
to prevent accumulation of material between the lifter and
3. Terminology
drum. Preferably, one of the lifters shall be attached to the door
3.1 Definitions—For definitions of terms used in this test for ease of sample removal.The lifters shall be fastened so that
method, refer to Terminology E 135. theattachedlegspointawayfromthedirectionofrotation,thus
giving a clear unobstructed shelf for lifting the sample. The
lifters shall be replaced when the wear is such that the shelf
measures less than 47.6 mm (1 ⁄8in.). The door shall be so
This test method is under the jurisdiction of ASTM Committee E01 on
constructed as to fit into the drum to form a smooth inner
Analytical Chemistry for Metals, Ores, and Related Materials and is the direct
surface and during the test shall be rigidly fastened to prevent
responsibility of Subcommittee E01.02 on Ores, Concentrates, and Related Metal-
lurgical Materials.
any loss of the sample. The drum shall be rotated on stub axles
Current edition approved April 10, 1997. Published June 1997. Originally
about 38.1 mm (1 ⁄2 in.) in diameter attached to the ends of the
published as E 279 – 65 T. Last previous edition E 279 – 92.
2 drum by means of flanges welded or bolted so as to provide
Annual Book of ASTM Standards, Vol 03.05.
Annual Book of ASTM Standards, Vol 03.06. smooth inner surfaces. The apparatus shall be fitted with a
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
E279
FIG. 1 Tumbler Test Apparatus
revolution counter and, preferably, with an automatic device to sample retained on the ⁄4-in. (6.3-mm) sieve, the amount
stop the drum after 200 revolutions. retained on the No. 30 (600-µm) sieve, and the amount passing
6.2 Sieves—Square-mesh sieves having the following des- the No. 30 (600-µm) sieve in accordance with Test Methods
1 3
ignations are needed
...