ASTM B135-10
(Specification)Standard Specification for Seamless Brass Tube
Standard Specification for Seamless Brass Tube
ABSTRACT
This specification covers seamless round and rectangular including square copper alloy tube in straight lengths. The tempers of drawn tube shall be designated as light-drawn, drawn, and hard-drawn. Light-drawn temper shall be used only when a tube of some stiffness but yet capable of being bent is needed. Drawn temper, which is most commonly used where there is no specific requirement for high strength on the one hand, shall be utilized for general purposes and or for bending qualities on the other. Hard-drawn temper shall be used only where there is need for a tube as strong as is commercially feasible for the sizes indicated. For any combination of diameter and wall thickness not covered under hard-drawn temper, the values given for drawn temper shall be used. Expansion test shall be performed on the rounded tube and shall show no cracking or rupture visible to the unaided eye. Both annealed and drawn tempers shall withstand, after proper cleaning, an immersion in standard mercurous nitrate solution for a certain amount of time without cracking. Materials shall then be removed from the solution and shall be wiped free of excess mercury and shall then be examined for cracks. The specimen shall undergo the eddy-current testing which is the standard nondestructive test. The specimen shall undergo the pneumatic test which subjects the tube to an internal air pressure making sure that it must not show evidence of leakage. The test method used shall provide for easy visual detection of any leakage, such as by immersion of the tube under water or by the pressure differential method. Annealed tube shall be either bright annealed or acid cleaned after final annealing operations.
SCOPE
1.1 This specification covers seamless round and rectangular including square copper alloy tube in straight lengths. Ten alloys are specified having the following nominal compositions:
General Information
Relations
Buy Standard
Standards Content (Sample)
NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation:B135 −10
Standard Specification for
1
Seamless Brass Tube
This standard is issued under the fixed designation B135; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the Department of Defense.
1. Scope* containingproducts,orboth,inyourstatemaybeprohibitedby
2
state law. (See 10.1.)
1.1 This specification covers seamless round and rectangu-
1.4 This standard does not purport to address all of the
lar including square copper alloy tube in straight lengths. Ten
safety concerns, if any, associated with its use. It is the
alloys are specified having the following nominal composi-
responsibility of the user of this standard to establish appro-
tions:
priate safety and health practices and determine the applica-
Copper Previously Nominal Composition, %
Alloy Used bility of regulatory limitations prior to use.
UNS Designa-
2 A
No. tion Copper Zinc Lead Tin
2. Referenced Documents
3
C22000 7 90.0 10.0 . .
2.1 ASTM Standards:
C23000 1 85.0 15.0 . .
B153 Test Method for Expansion (Pin Test) of Copper and
C26000 2 70.0 30.0 . .
C27000 9 65.0 35.0 . . Copper-Alloy Pipe and Tubing
C27200 8 63.0 37.0 . .
B154 Test Method for Mercurous Nitrate Test for Copper
C27400 . 62.5 37.5 . .
Alloys
C28000 5 60.0 40.0 . .
C33000 3 66.0 33.5 0.5 . B251 Specification for General Requirements for Wrought
C33200 4 66.0 32.4 1.6 .
Seamless Copper and Copper-Alloy Tube
C37000 6 60.0 39.0 1.0 .
B601 Classification forTemper Designations for Copper and
C44300 . 71.5 27.5 . 1.00
Copper Alloys—Wrought and Cast
A
Alloy Designations of Specification B135 – 63, which was published in the 1966 E243 PracticeforElectromagnetic(Eddy-Current)Examina-
Book of ASTM Standards, Part 5.
tion of Copper and Copper-Alloy Tubes
1.2 This specification is the inch-pound companion to E527 Practice for Numbering Metals and Alloys in the
Specification B135M; therefore, no SI equivalents are pre- Unified Numbering System (UNS)
sented in the specification.
3. Terminology
1.3 Warning—Mercury has been designated by EPA and
3.1 Definitions of Terms Specific to This Standard:
many state agencies as a hazardous material that can cause
3.1.1 capable of—the test need not be performed by the
central nervous system, kidney, and liver damage. Mercury, or
producer of the material. However, if subsequent testing by the
its vapor, may be hazardous to health and corrosive to
purchaser establishes that the material does not meet these
materials. Caution should be taken when handling mercury and
requirements, the material shall be subject to rejection.
mercury-containing products. See the applicable product Ma-
terial Safety Data Sheet (MSDS) for details and EPA’s website
4. Ordering Information
(http://www.epa.gov/mercury/faq.htm) for additional informa-
tion. Users should be aware that selling mercury or mercury-
4.1 Orders for material under the specification shall include
the following information:
4.1.1 Alloy (Section 1),
1
4.1.2 Temper (Section 7),
ThisspecificationisunderthejurisdictionofASTMCommitteeB05onCopper
and CopperAlloys and is the direct responsibility of Subcommittee B05.04 on Pipe
4.1.3 Whether tension tests are required (for drawn tempers
and Tube.
only (see 8.1)),
Current edition approved Oct. 1, 2010. Published November 2010. Originally
approved in 1940. Last previous edition approved in 2008 as B135 – 08a. DOI:
10.1520/B0135-10.
2 3
The UNS system for copper and copper alloys (see Practice E527) is a simple For referenced ASTM standards, visit the ASTM website, www.astm.org, or
expansion of the former standard designation system accomplished by the addition contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
of a prefix “C” and a suffix “00.” The suffix can be used to accommodate Standards volume information, refer to the standard’s Document Summary page on
composition variations of the base alloy. the ASTM website.
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1
---------------------- Page: 1 ----------------------
B135−10
4.1.4 Dimensions: diameter or distance between parallel mostcommonlyusedwherethereisnospecificrequirementfor
surfaces and wall thickness (see 11.2 and 11.3), high strength on the one hand or for bending qualities on the
4.1.5 Length (see 12.4), other. Hard-drawn temper is used only where there is need for
4.1.6 Mercurous nitrate test, if required (Section 10), a tube as strong as is co
...
This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation:B135–08a Designation: B135 – 10
Standard Specification for
1
Seamless Brass Tube
This standard is issued under the fixed designation B135; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope*
1.1 This specification covers seamless round and rectangular including square copper alloy tube in straight lengths. Ten alloys
are specified having the following nominal compositions:
Copper Previously Nominal Composition, %
Alloy Used
UNS Designa-
2 A
No. tion Copper Zinc Lead Tin
C22000 7 90.0 10.0 . .
C23000 1 85.0 15.0 . .
C26000 2 70.0 30.0 . .
C27000 9 65.0 35.0 . .
C27200 8 63.0 37.0 . .
C27400 . 62.5 37.5 . .
C28000 5 60.0 40.0 . .
C33000 3 66.0 33.5 0.5 .
C33200 4 66.0 32.4 1.6 .
C37000 6 60.0 39.0 1.0 .
C44300 . 71.5 27.5 . 1.00
A
Alloy Designations of Specification B135 – 63, which was published in the 1966 Book of ASTM Standards, Part 5.
1.2This1.2 This specification is the inch-pound companion to Specification B135M; therefore, no SI equivalents are presented
in the specification.
1.3 Warning—Mercury has been designated by EPA and many state agencies as a hazardous material that can cause central
nervous system, kidney, and liver damage. Mercury, or its vapor, may be hazardous to health and corrosive to materials. Caution
should be taken when handling mercury and mercury-containing products. See the applicable product Material Safety Data Sheet
(MSDS) for details and EPA’s website (http://www.epa.gov/mercury/faq.htm) for additional information. Users should be aware
2
that selling mercury or mercury-containing products, or both, in your state may be prohibited by state law. (See 10.1.)
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility
of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory
limitations prior to use.
2. Referenced Documents
3
2.1 ASTM Standards:
B153 Test Method for Expansion (Pin Test) of Copper and Copper-Alloy Pipe and Tubing
B154 Test Method for Mercurous Nitrate Test for Copper Alloys
B251 Specification for General Requirements for Wrought Seamless Copper and Copper-Alloy Tube
B601 Classification for Temper Designations for Copper and Copper AlloysWrought and Cast
E243 Practice for Electromagnetic (Eddy-Current) Examination of Copper and Copper-Alloy Tubes
E527 Practice for Numbering Metals and Alloys in the Unified Numbering System (UNS)
3. Terminology
3.1 Definitions of Terms Specific to This Standard:
1
This specification is under the jurisdiction ofASTM Committee B05 on Copper and CopperAlloys and is the direct responsibility of Subcommittee B05.04 on Pipe and
Tube.
Current edition approved Oct. 1, 2008.2010. Published November 2008.2010. Originally approved in 1940. Last previous edition approved in 2008 as B135 – 08a. DOI:
10.1520/B0135-08A.10.1520/B0135-10.
2
The UNS system for copper and copper alloys (see Practice E527) is a simple expansion of the former standard designation system accomplished by the addition of a
prefix “C” and a suffix “00.” The suffix can be used to accommodate composition variations of the base alloy.
3
For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at service@astm.org. For Annual Book of ASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
*A Summary of Changes section appears at the end of this standard.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
1
---------------------- Page: 1 ----------------------
B135 – 10
3.1.1 capable of—the test need not be performed by the producer of the material. However, if subsequent testing by the
purchaser establishes that the material does not meet these requirements, the material shall be subject to rejection.
4. Ordering Information
4.1 Orders for material under the specification shall include the following information:
4.1.1 Alloy (Section 1),
4.1.2 Temper (Section 7),
4.1.3 Whether tension tests are required (for drawn tempers only (see 8.1)),
4.1.4 Dimensions: diameter or distance between parallel surfaces and wall thickness (see 11.2 and 11.3),
4.1.5 Length (see 1
...
This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation:B135–08a Designation: B135 – 10
Standard Specification for
1
Seamless Brass Tube
This standard is issued under the fixed designation B135; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope*
1.1 This specification covers seamless round and rectangular including square copper alloy tube in straight lengths. Ten alloys
are specified having the following nominal compositions:
Copper Previously Nominal Composition, %
Alloy Used
UNS Designa-
2 A
No. tion Copper Zinc Lead Tin
C22000 7 90.0 10.0 . .
C23000 1 85.0 15.0 . .
C26000 2 70.0 30.0 . .
C27000 9 65.0 35.0 . .
C27200 8 63.0 37.0 . .
C27400 . 62.5 37.5 . .
C28000 5 60.0 40.0 . .
C33000 3 66.0 33.5 0.5 .
C33200 4 66.0 32.4 1.6 .
C37000 6 60.0 39.0 1.0 .
C44300 . 71.5 27.5 . 1.00
A
Alloy Designations of Specification B135 – 63, which was published in the 1966 Book of ASTM Standards, Part 5.
1.2This1.2 This specification is the inch-pound companion to Specification B135M; therefore, no SI equivalents are presented
in the specification.
1.3 Warning—Mercury has been designated by EPA and many state agencies as a hazardous material that can cause central
nervous system, kidney, and liver damage. Mercury, or its vapor, may be hazardous to health and corrosive to materials. Caution
should be taken when handling mercury and mercury-containing products. See the applicable product Material Safety Data Sheet
(MSDS) for details and EPA’s website (http://www.epa.gov/mercury/faq.htm) for additional information. Users should be aware
2
that selling mercury or mercury-containing products, or both, in your state may be prohibited by state law. (See 10.1.)
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility
of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory
limitations prior to use.
2. Referenced Documents
3
2.1 ASTM Standards:
B153 Test Method for Expansion (Pin Test) of Copper and Copper-Alloy Pipe and Tubing
B154 Test Method for Mercurous Nitrate Test for Copper Alloys
B251 Specification for General Requirements for Wrought Seamless Copper and Copper-Alloy Tube
B601 Classification for Temper Designations for Copper and Copper AlloysWrought and Cast
E243 Practice for Electromagnetic (Eddy-Current) Examination of Copper and Copper-Alloy Tubes
E527 Practice for Numbering Metals and Alloys in the Unified Numbering System (UNS)
3. Terminology
3.1 Definitions of Terms Specific to This Standard:
1
This specification is under the jurisdiction ofASTM Committee B05 on Copper and CopperAlloys and is the direct responsibility of Subcommittee B05.04 on Pipe and
Tube.
Current edition approved Oct. 1, 2008.2010. Published November 2008.2010. Originally approved in 1940. Last previous edition approved in 2008 as B135 – 08a. DOI:
10.1520/B0135-08A.10.1520/B0135-10.
2
The UNS system for copper and copper alloys (see Practice E527) is a simple expansion of the former standard designation system accomplished by the addition of a
prefix “C” and a suffix “00.” The suffix can be used to accommodate composition variations of the base alloy.
3
For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at service@astm.org. For Annual Book of ASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
*A Summary of Changes section appears at the end of this standard.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
1
---------------------- Page: 1 ----------------------
B135 – 10
3.1.1 capable of—the test need not be performed by the producer of the material. However, if subsequent testing by the
purchaser establishes that the material does not meet these requirements, the material shall be subject to rejection.
4. Ordering Information
4.1 Orders for material under the specification shall include the following information:
4.1.1 Alloy (Section 1),
4.1.2 Temper (Section 7),
4.1.3 Whether tension tests are required (for drawn tempers only (see 8.1)),
4.1.4 Dimensions: diameter or distance between parallel surfaces and wall thickness (see 11.2 and 11.3),
4.1.5 Length (see 1
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.